US20140116326A1 - Reactor designs for use in ammonothermal growth of group-iii nitride crystals - Google Patents
Reactor designs for use in ammonothermal growth of group-iii nitride crystals Download PDFInfo
- Publication number
- US20140116326A1 US20140116326A1 US14/149,121 US201414149121A US2014116326A1 US 20140116326 A1 US20140116326 A1 US 20140116326A1 US 201414149121 A US201414149121 A US 201414149121A US 2014116326 A1 US2014116326 A1 US 2014116326A1
- Authority
- US
- United States
- Prior art keywords
- baffle
- vessel
- fluid
- crystals
- source materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Reactor designs for use in ammonothermal growth of group-III nitride crystals. Internal heating is used to enhance and/or engineer fluid motion, gas mixing, and the ability to create solubility gradients within a vessel used for the ammonothermal growth of group-III nitride crystals. Novel baffle designs are used for control and improvement of continuous fluid motion within a vessel used for the ammonothermal growth of group-III nitride crystals.
Description
- This application is a continuation that claims the benefit under 35 U.S.C. Section 120 of:
- U.S. Utility patent application Ser. No. 13/128,083, filed on May 6, 2011, by Siddha Pimputkar, Derrick S. Kamber, James S. Speck and Shuji Nakamura, entitled “REACTOR DESIGNS FOR USE IN AMMONOTHERMAL GROWTH OF GROUP-III NITRIDE CRYSTALS,” attorneys' docket number 30794.296-US-WO (2009-283-2), which application claims the benefit under 35 U.S.C. Section 365(c) of:
- P.C.T. International Patent Application Serial No. US2009/063239, filed on Nov. 4, 2009, by Siddha Pimputkar, Derrick S. Kamber, James S. Speck and Shuji Nakamura, entitled “REACTOR DESIGNS FOR USE IN AMMONOTHERMAL GROWTH OF GROUP-III NITRIDE CRYSTALS,” attorneys' docket number 30794.296-WO-U1 (2009-283-2), which application claims the benefit under 35 U.S.C. Section 119(e) of:
- U.S. Provisional Patent Application Ser. No. 61/112,560, filed on Nov. 7, 2008, by Siddha Pimputkar, Derrick S. Kamber, James S. Speck and Shuji Nakamura, entitled “REACTOR DESIGNS FOR USE IN AMMONOTHERMAL GROWTH OF GROUP-III NITRIDE CRYSTALS,” attorneys' docket number 30794.296-US-P1 (2009-283/285-1),
- all of which applications are incorporated by reference herein.
- This application is related to the following co-pending and commonly-assigned U.S. patent applications:
- U.S. Utility patent application Ser. No. 11/921,396, filed on Nov. 30, 2007, by Kenji Fujito, Tadao Hashimoto and Shuji Nakamura, entitled “METHOD FOR GROWING GROUP-III NITRIDE CRYSTALS IN SUPERCRITICAL AMMONIA USING AN AUTOCLAVE,” attorneys' docket number 30794.129-US-WO (2005-339-2), which application claims the benefit under 35 U.S.C. Section 365(c) of P.C.T. International Patent Application Serial No. US2005/024239, filed on Jul. 8, 2005, by Kenji Fujito, Tadao Hashimoto and Shuji Nakamura, entitled “METHOD FOR GROWING GROUP III-NITRIDE CRYSTALS IN SUPERCRITICAL AMMONIA USING AN AUTOCLAVE,” attorneys' docket number 30794.129-WO-01 (2005-339-1);
- U.S. Utility patent application Ser. No. 11/784,339, filed on Apr. 6, 2007, by Tadao Hashimoto, Makoto Saito, and Shuji Nakamura, entitled “METHOD FOR GROWING LARGE SURFACE AREA GALLIUM NITRIDE CRYSTALS IN SUPERCRITICAL AMMONIA AND LARGE SURFACE AREA GALLIUM NITRIDE CRYSTALS,” attorneys' docket number 30794.179-US-U1 (2006-204), which application claims the benefit under 35 U.S.C. Section 119(e) of U.S. Provisional Patent Application Ser. No. 60/790,310, filed on Apr. 7, 2006, by Tadao Hashimoto, Makoto Saito, and Shuji Nakamura, entitled “A METHOD FOR GROWING LARGE SURFACE AREA GALLIUM NITRIDE CRYSTALS IN SUPERCRITICAL AMMONIA AND LARGE SURFACE AREA GALLIUM NITRIDE CRYSTALS,” attorneys' docket number 30794.179-US-P1 (2006-204);
- U.S. Utility patent application Ser. No. 11/765,629, filed on Jun. 20, 2007, by Tadao Hashimoto, Hitoshi Sato and Shuji Nakamura, entitled “OPTO-ELECTRONIC AND ELECTRONIC DEVICES USING N-FACE OR M-PLANE GaN SUBSTRATE PREPARED WITH AMMONOTHERMAL GROWTH,” attorneys' docket number 30794.184-US-U1 (2006-666), now U.S. Pat. No. 7,755,172, which application claims the benefit under 35 U.S.C. Section 119(e) of U.S. Provisional Patent Application Ser. No. 60/815,507, filed on Jun. 21, 2006, by Tadao Hashimoto, Hitoshi Sato, and Shuji Nakamura, entitled “OPTO-ELECTRONIC AND ELECTRONIC DEVICES USING N-FACE GaN SUBSTRATE PREPARED WITH AMMONOTHERMAL GROWTH,” attorneys' docket number 30794.184-US-P1 (2006-666);
- U.S. Utility patent application Ser. No. 12/234,244, filed on Sep. 19, 2008, by Tadao Hashimoto and Shuji Nakamura, entitled “GALLIUM NITRIDE BULK CRYSTALS AND THEIR GROWTH METHOD,” attorneys' docket number 30794.244-US-U1 (2007-809), now U.S. Pat. No. 8,253,221, which application claims the benefit under 35 U.S.C. Section 119(e) of U.S. Provisional Patent Application Ser. No. 60/973,662, filed on Sep. 19, 2007, by Tadao Hashimoto and Shuji Nakamura, entitled “GALLIUM NITRIDE BULK CRYSTALS AND THEIR GROWTH METHOD,” attorneys' docket number 30794.244-US-P1 (2007-809-1);
- U.S. Utility patent application Ser. No. 11/977,661, filed on Oct. 25, 2007, by Tadao Hashimoto, entitled “METHOD FOR GROWING GROUP III-NITRIDE CRYSTALS IN A MIXTURE OF SUPERCRITICAL AMMONIA AND NITROGEN, AND GROUP III-NITRIDE CRYSTALS GROWN THEREBY,” attorneys' docket number 30794.253-US-U1 (2007-774-2), now U.S. Pat. No. 7,803,344, which application claims the benefit under 35 U.S.C. Section 119(e) of U.S. Provisional Patent Application Ser. No. 60/854,567, filed on Oct. 25, 2006, by Tadao Hashimoto, entitled “METHOD FOR GROWING GROUP-III NITRIDE CRYSTALS IN MIXTURE OF SUPERCRITICAL AMMONIA AND NITROGEN AND GROUP-III NITRIDE CRYSTALS,” attorneys' docket number 30794.253-US-P1 (2007-774);
- U.S. Utility patent application Ser. No. 12/612,477, filed Nov. 4, 2009, by Siddha Pimputkar, Derrick S. Kamber, Makoto Saito, Steven P. DenBaars, James S. Speck and Shuji Nakamura, entitled “GROUP-III NITRIDE MONOCRYSTAL WITH IMPROVED CRYSTAL QUALITY GROWN ON AN ETCHED-BACK SEED CRYSTAL AND METHOD OF PRODUCING THE SAME,” attorneys' docket number 30794.288-US-U1 (2009-154-2), which application claims the benefit under 35 U.S.C. Section 119(e) of U.S. Provisional Patent Application Ser. No. 61/111,644, filed on Nov. 5, 2008, by Siddha Pimputkar, Derrick S. Kamber, Makoto Saito, Steven P. DenBaars, James S. Speck and Shuji Nakamura, entitled “GROUP-III NITRIDE MONOCRYSTAL WITH IMPROVED CRYSTAL QUALITY GROWN ON AN ETCHED-BACK SEED CRYSTAL AND METHOD OF PRODUCING THE SAME,” attorneys' docket number 30794.288-US-P1 (2009-154-1);
- P.C.T. International Patent Application Serial No. PCT/US2009/063240, filed on Nov. 4, 2009, by Derrick S. Kamber, Siddha Pimputkar, Makoto Saito, Steven P. DenBaars, James S. Speck and Shuji Nakamura, entitled “GROUP-III NITRIDE MONOCRYSTAL WITH IMPROVED PURITY AND METHOD OF PRODUCING THE SAME,” attorneys' docket number 30794.295-WO-U1 (2009-282-2), which application claims the benefit under 35 U.S.C. Section 119(e) of U.S. Provisional Patent Application Ser. No. 61/112,555, filed on Nov. 7, 2008, by Derrick S. Kamber, Siddha Pimputkar, Makoto Saito, Steven P. DenBaars, James S. Speck and Shuji Nakamura, entitled “GROUP-III NITRIDE MONOCRYSTAL WITH IMPROVED PURITY AND METHOD OF PRODUCING THE SAME,” attorneys' docket number 30794.295-US-P1 (2009-282-1);
- P.C.T. International Patent Application Serial No. PCT/US2009/063238, filed on Nov. 4, 2009, by Siddha Pimputkar, Derrick S. Kamber, James S. Speck and Shuji Nakamura, entitled “NOVEL VESSEL DESIGNS AND RELATIVE PLACEMENTS OF THE SOURCE MATERIAL AND SEED CRYSTALS WITH RESPECT TO THE VESSEL FOR THE AMMONOTHERMAL GROWTH OF GROUP-III NITRIDE CRYSTALS,” attorneys' docket number 30794.297-WO-U1 (2009-284-2), which application claims the benefit under 35 U.S.C. Section 119(e) of U.S. Provisional Patent Application Ser. No. 61/112,552, filed on Nov. 7, 2008, by Siddha Pimputkar, Derrick S. Kamber, James S. Speck and Shuji Nakamura, entitled “NOVEL VESSEL DESIGNS AND RELATIVE PLACEMENTS OF THE SOURCE MATERIAL AND SEED CRYSTALS WITH RESPECT TO THE VESSEL FOR THE AMMONOTHERMAL GROWTH OF GROUP-III NITRIDE CRYSTALS,” attorneys' docket number 30794.297-US-P1 (2009-284-1);
- P.C.T. International Patent Application Serial No. PCT/US2009/063287, filed on Nov. 4, 2009, by Siddha Pimputkar, Derrick S. Kamber, James S. Speck and Shuji Nakamura, entitled “ADDITION OF HYDROGEN AND/OR NITROGEN CONTAINING COMPOUNDS TO THE NITROGEN-CONTAINING SOLVENT USED DURING THE AMMONOTHERMAL GROWTH OF GROUP-III NITRIDE CRYSTALS,” attorneys' docket number 30794.298-WO-U1 (2009-286-2), which application claims the benefit under 35 U.S.C. Section 119(e) of U.S. Provisional Patent Application Ser. No. 61/112,558, filed on Nov. 7, 2008, by Siddha Pimputkar, Derrick S. Kamber, James S. Speck and Shuji Nakamura, entitled “ADDITION OF HYDROGEN AND/OR NITROGEN CONTAINING COMPOUNDS TO THE NITROGEN-CONTAINING SOLVENT USED DURING THE AMMONOTHERMAL GROWTH OF GROUP-III NITRIDE CRYSTALS TO OFFSET THE DECOMPOSITION OF THE NITROGEN-CONTAINING SOLVENT AND/OR MASS LOSS DUE TO DIFFUSION OF HYDROGEN OUT OF THE CLOSED VESSEL,” attorneys' docket number 30794.298-US-P1 (2009-286-1);
- P.C.T. International Patent Application Serial No. PCT/US2009/063236, filed on Nov. 4, 2009, by Siddha Pimputkar, Derrick S. Kamber, James S. Speck and Shuji Nakamura, entitled “CONTROLLING RELATIVE GROWTH RATES OF DIFFERENT EXPOSED CRYSTALLOGRAPHIC FACETS OF A GROUP-III NITRIDE CRYSTAL DURING THE AMMONOTHERMAL GROWTH OF A GROUP-III NITRIDE CRYSTAL,” attorneys' docket number 30794.299-WO-U1 (2009-287-2), which application claims the benefit under 35 U.S.C. Section 119(e) of U.S. Provisional Patent Application Ser. No. 61/112,545, filed on Nov. 7, 2008, by Siddha Pimputkar, Derrick S. Kamber, James S. Speck and Shuji Nakamura, entitled “CONTROLLING RELATIVE GROWTH RATES OF DIFFERENT EXPOSED CRYSTALLOGRAPHIC FACETS OF A GROUP-III NITRIDE CRYSTAL DURING THE AMMONOTHERMAL GROWTH OF A GROUP-III NITRIDE CRYSTAL,” attorneys' docket number 30794.299-US-P1(2009-287-1); and
- P.C.T. International Patent Application Serial No. PCT/US2009/063233, filed on Nov. 4, 2009, by Siddha Pimputkar, Derrick S. Kamber, James S. Speck and Shuji Nakamura, entitled “USING BORON-CONTAINING COMPOUNDS, GASSES AND FLUIDS DURING AMMONOTHERMAL GROWTH OF GROUP-III NITRIDE CRYSTALS,” attorneys' docket number 30794.300-WO-U1 (2009-288-2), which application claims the benefit under 35 U.S.C. Section 119(e) of U.S. Provisional Patent Application Ser. No. 61/112,550, filed on Nov. 7, 2008, by Siddha Pimputkar, Derrick S. Kamber, James S. Speck and Shuji Nakamura, entitled “USING BORON-CONTAINING COMPOUNDS, GASSES AND FLUIDS DURING AMMONOTHERMAL GROWTH OF GROUP-III NITRIDE CRYSTALS,” attorneys' docket number 30794.300-US-P1 (2009-288-1);
- all of which applications are incorporated by reference herein.
- 1. Field of the Invention
- This invention relates to ammonothermal growth of group-III nitrides.
- 2. Description of the Related Art
- Ammonothermal growth of group-III nitrides, for example, GaN, involves placing, within a reactor vessel, group-III containing source materials, group-III nitride seed crystals, and a nitrogen-containing solvent, such as ammonia, sealing the vessel and heating the vessel to conditions such that the vessel is at elevated temperatures (between 23° C. and 1000° C.) and high pressures (between 1 atm and, for example, 30,000 atm). Under these temperatures and pressures, the nitrogen-containing solvent may become a supercritical fluid which normally exhibits enhanced solubility of the group-III containing source materials into solution. The solubility of the group-III containing materials into the nitrogen-containing solvent is dependent on the temperature, pressure and density of the solvent, among other things. By creating two different zones within the vessel, it is possible to establish a solubility gradient where, in one zone, the solubility will be higher than in a second zone. The group-III containing source materials are then preferentially placed in the higher solubility zone and the seed crystals in the lower solubility zone. By establishing fluid motion of the solvent with the dissolved source materials between these two zones, for example, by making use of natural convection, it is possible to transport the group-III containing source materials from the higher solubility zone to the lower solubility zone where the group-III containing source materials are deposited onto the seed crystals.
- The current state of the art uses a device or vessel that contains the supercritical solvent and this vessel is heated to raise the entire vessel contents to elevated temperatures and pressures. The heating of the vessel is commonly performed by heating the outer walls of the vessel and, by virtue of heat transfer, heating the inner walls of the vessel, which, in turn, heats the solvent, group-III containing source materials, group-III nitride seed crystals and other material present within the vessel.
- For the ammonothermal growth of group-III nitride crystals, it is important to establish solubility gradients. One method of producing these gradients is to establish temperature gradients since the solubility is a function of temperature, among other variables. Therefore, it is crucial for the growth characteristics of the group-III nitride crystals to establish well defined and controllable temperature gradients across well defined and placed spatial zones within the reactor.
- In addition, many current reactor designs for the ammonothermal growth of group-III nitride crystals involve placing the group-III containing source materials and group-III nitride seed crystals within a vessel, where the vessel has a small ratio of inner diameter to length of vessel. By virtue of this design, the vessel has a long cylindrical shape wherein the group-III containing source materials or group-III nitride seed material are preferentially placed in different zones of the vessel, and the different zones are often separated by the use of baffle plates, which function as restriction devices for the fluid flow of the solvent, so it is possible to establish temperature gradients between the two zones.
- Thus, what is needed in the art are new reactor vessel designs for use in ammonothermal growth of group-III nitride crystals. Specifically, what is needed in the art are improved techniques for heating reactor vessels used in ammonothermal growth of group-III nitride crystals. In addition, what is needed in the art are improved baffle designs for reactor vessels used in ammonothermal growth of group-III nitride crystals. The present invention satisfies these needs.
- To overcome the limitations in the prior art described above, and to overcome other limitations that will become apparent upon reading and understanding the present invention, the present invention discloses improved reactor vessel designs for use in ammonothermal growth of group-III nitride crystals. The improvements include internal heating, which is used to enhance and/or engineer fluid motion, gas mixing, and the ability to create solubility gradients within the vessel, and novel baffle designs, which are used for control and improvement of continuous fluid motion within the vessel.
- Referring now to the drawings in which like reference numbers represent corresponding parts throughout:
-
FIG. 1 is a schematic of a high-pressure vessel according to an embodiment of the present invention. -
FIG. 2 is a flowchart illustrating the method according to an embodiment of the present invention. -
FIGS. 3( a) and 3(b) illustrate one possible embodiment of a baffle used in the high-pressure vessel of the present invention. -
FIG. 4 illustrates another possible embodiment of a baffle used in the high-pressure vessel of the present invention. - In the following description of the preferred embodiment, reference is made to a specific embodiment in which the invention may be practiced. It is to be understood that other embodiments may be utilized and structural changes may be made without departing from the scope of the present invention.
-
FIG. 1 is a schematic of an ammonothermal growth system comprising a high-pressure reaction vessel 10 according to one embodiment of the present invention. The vessel, which is an autoclave, may include alid 12,gasket 14, inlet andoutlet port 16, and external heaters/coolers baffle plate 20 divides the interior of thevessel 10 into twozones zones coolers upper zone 22 a may contain one or more group-IIInitride seed crystals 24 and alower zone 22 b may contain one or more group-III-containingsource materials 26, although these positions may be reversed in other embodiments. Both the group-IIInitride seed crystals 24 and group-III-containingsource materials 26 may be contained within baskets or other containment devices, which are typically comprised of a Ni—Cr alloy. Thevessel 10 andlid 12, as well as other components, may also be made of a Ni—Cr based alloy. Finally, the interior of thevessel 10 is filled with a nitrogen-containing solvent 28 to accomplish the ammonothermal growth. -
FIG. 2 is a flow chart illustrating a method for obtaining or growing a group-III nitride-containing crystal using the apparatus ofFIG. 1 according to one embodiment of the present invention. -
Block 30 represents placing one or more group-IIInitride seed crystals 24, one or more group-III containingsource materials 26, and a nitrogen-containing solvent 28 in thevessel 10, wherein theseed crystals 24 are placed in a seed crystals zone (i.e., either 22 a or 22 b, namely the opposite of thezone source materials 26, thesource materials 26 are placed in a source materials zone (i.e., either 22 b or 22 a, namely the opposite of thezone seed crystals 24 comprise a group-III containing crystal; thesource materials 26 comprise a group-III containing compound, a group-III element in its pure elemental form, or a mixture thereof, i.e., a group-III nitride monocrystal, a group-III nitride polycrystal, a group-III nitride powder, group-III nitride granules, or other group-III containing compound; and the nitrogen-containing solvent 28 is supercritical ammonia or one or more of its derivatives. An optional mineralizer may be placed in thevessel 10 as well, wherein the mineralizer increases the solubility of thesource materials 26 in the supercritical nitrogen-containing solvent 28 as compared to the supercritical nitrogen-containing solvent 28 without the mineralizer. -
Block 32 represents growing group-III nitride crystals on one or more surfaces of theseed crystals 24, wherein the conditions for growth include forming a temperature gradient between theseed crystals 24 and thesource materials 26 that causes a higher solubility of thesource materials 26 in the source materials zone and a lower solubility, as compared to the higher solubility, of thesource materials 26 in the seed crystals zone. Specifically, growing the group-III nitride crystals on one or more surfaces of theseed crystal 24 occurs by changing the source materials zone temperatures and the seed crystals zone temperatures to create a temperature gradient between the source materials zone and the seed crystals zone that produces a higher solubility of thematerials 26 in the solvent 28 in the source materials zone as compared to the seed crystals zone. For example, the source materials zone and seed crystals zone temperatures may range between 0° C. and 1000° C., and the temperature gradients may range between 0° C. and 1000° C. -
Block 34 comprises the resulting product created by the process, namely, a group-III nitride crystal grown by the method described above. A group-III nitride substrate may be created from the group-III nitride crystal, and a device may be created using the group-III nitride substrate. - According to the present invention, fluid motion within the
vessel 10 may be accomplished via a unique configuration of internal heaters and/or a unique baffle device design. These are described in more detail below. - The present invention intends the use of internal heater(s)/cooler(s), in combination with, or instead of, external heaters/
coolers vessel 10 containing theseed crystals 24, thesource materials 26, and the solvent 28, to different temperatures at different well defined spatial areas of thevessel 10. - In one embodiment, the
baffle 20 is the internal heater/cooler. However, any number of internal heaters/coolers may be placed within thevessel 10 in any number of spatial locations within thevessel 10. The temperature of each internal heater/cooler may be the same or different depending on the particular effect that one wishes to achieve. The internal heater/cooler may present itself in any shape, form, size or material, yet it may be preferable to use high purity metals, or high purity metal coated ceramics. The internal heaters/coolers may or may not have a protective coating surrounding the elements thereof to prevent corrosion or other detrimental effects from the surrounding environment on their operation. - Although the internal heaters/coolers may be integrated into or onto other components present within the vessel, such as, but not limited to, the
baffle 20, which are used to guide and/or restrict fluid flow within thevessel 10, the internal heaters/coolers may also be integrated into other components, such as a basket or containing device sometimes used to hold the seed crystals 24r source materials 26. - The internal heaters/coolers may also be designed to encompass the entire inner surface of the
vessel 10, thereby potentially eliminating the need for external heating or cooling of thevessel 10 to elevate or lower the temperatures within thevessel 10. This could potentially allow for the creation of higher pressure vessels, as the material barring the pressure is at a lower temperature, and enhance the mechanical characteristics of the current state of the art vessel designs used for the ammonothermal growth of group-III nitride crystals. - Some of the many possible purposes of the internal heaters/coolers are to establish a temperature gradient across a spatial zone surrounding the heaters/coolers and other spatial zones within the
vessel 10. By establishing this temperature gradient, it is possible to establish solubility gradients, which, in turn, may be used to enhance the growth of the group-III nitride crystals. The ability to engineer different solubility zones within thevessel 10, without the restriction and sole use of external heaters/coolers and devices which manage the fluid flow within thevessel 10, for example,baffle devices 20, is substantial and will allow for more efficient and more effective designs which, in turn, may allow for the increased growth rates and improved crystal quality of the group-III nitride crystals. - Other immediate benefits of the internal heaters/coolers may be the ability to establish a zone around each heater/cooler that is at a higher or lower density than the surrounding fluid due to the difference in temperature between the zone and the surrounding medium. This density difference may provide fluid dynamical forces within the
vessel 10, thereby enhancing fluid motion and hence mass transport of the solvent 28 with the dissolvedsource materials 26. One example of this particular aspect of the invention, although this should not be seen limiting in any way, would be a heater/cooler that is relatively long, held vertically and results in a temperature higher than the surrounding solvent 28. By heating the solvent 28, the solvent 28 will become a lower density material and will want to rise along the surface of the heater/cooler. The rising of the local, hotter supercritical solvent 28 is a demonstration of both a controlled convective flow within thevessel 10 and enhanced fluid motion. Not only does this example provide enhanced fluid motion, but the local hotter solvent 28 fluid may have a higher or lower solubility of thesource materials 26 and therefore it may be advantageous to place either thesource materials 26 orseed crystals 24 close to this zone within thevessel 10. - While the primary purpose of the internal heaters/coolers is to provide a controllable temperature gradient of any size between different spatial regions of the
vessel 10, the internal heaters/coolers may also simultaneously be used as structural units within thevessel 10 to control and/or engineer fluid patterns within thevessel 10 itself. For example, thebaffle 20 with an integrated heater/cooler can simultaneously heat or cool the solvent 28 and restrict solvent 28 flow. Alternatively, the internal heaters/coolers may be integrated into baskets or other devices used to hold theseed crystals 24 and/or contain thesource materials 26, as well as provide a local temperature that is different from the surrounding solvent 28 fluid. The internal heaters/coolers may also be used, for example, as a liner material for thevessel 10 in a lower solubility zone where the growth of the group-III nitride crystals occurs. By changing the local temperature near thevessel 10 wall, it may be possible to prevent nucleation and sequential growth of the material on thevessel 10 wall surfaces as the solubility may be increased just in the vicinity of the walls. - In order to improve on the mass transport within the
vessel 10, the present invention also usesnovel baffle devices 20 that enhance the mixing of fluids, e.g., the solvent 28 with the dissolvedsource materials 26, and additionally guide the fluid motion to circulate the fluid to a much greater degree, and furthermore, allow for greater penetration of the fluid into various areas of thevessel 10. This is achieved by thebaffle devices 20 enhancing circular fluid motion patterns and additionally redirecting the flow of the fluid within thebaffle device 20 itself. -
FIGS. 3( a) and 3(b) illustrate one possible embodiment of thebaffle device 20 according to the present invention. Specifically,FIG. 3( a) is a side view of anexemplary baffle device 20 wherein thearrows 36 show the motion of the fluid through thebaffle device 20, andFIG. 3( b) is a top view of thebaffle device 20 showing theopenings - The basic idea entails having the fluid enter the
baffle device 20, for example, on one side (e.g., the top surface), in theopenings 40 near the outer edge of thebaffle device 20 and exit through theopenings 38 that are in a region that is closer to the center of thebaffle device 20. Similarly, on the opposite side of the baffle device 20 (i.e., the bottom surface), the fluid may enter through theopenings 40 near the outer edge of thebaffle device 20 and exit through theopenings 38 that are in a region that is closer to the center of thebaffle device 20. - Alternative embodiments may reverse this fluid flow, namely the fluid may enter the
baffle 20 through the region that is closer to the center of thebaffle 20, and exit thebaffle 20 near the outer edge of thebaffle 20. - By virtue of this design for the
baffle device 20, it may be possible to establish a continual motion of fluid within thevessel 10. Theseed crystals 24 andsource materials 26 can then be placed in the appropriate areas of thevessel 10 to provide optimal conditions for growth on theseed crystals 24 and/or for dissolution of thesource materials 26 into the solvent 28. - Moreover, by incorporating internal heaters/coolers into the
baffle device 20 itself, or by adding other internal heaters/coolers into thevessel 10, or by applying or extracting heat from the outside the walls of thevessel 10 by use of other heating or cooling mechanisms or devices, specifically in the region of thebaffle 20, it is further possible to intentionally change the temperature, and hence, solubility, of the fluid exiting thebaffle device 20 as compared to the fluid entering thebaffle device 20. - This invention further includes the idea of designing the
baffle device 20 not only to improve on fluid motion within thevessel 10, but also to guide particular fluids into one or more specific zones within thevessel 10. One example of this idea, which should not be considered limiting in any way, would be for thebaffle device 20 to guide nutrient rich solvent 28, for example, solvent 28 coming from the source materials zone, towards the center of thevessel 10. By doing so, it may be possible to suppress nucleation and growth of group-III nitride material on undesired locations and/or surfaces within thevessel 10, for example, on the walls of thevessel 10, and further enhance growth of group-III nitride material on desired locations within thevessel 10, for example, on the group-IIInitride seed crystals 24. - This invention is not limited to the above schematic presentation of one
possible baffle device 20 design, but includes any possible design, which passively or actively redirects fluid motion and/or guides fluid motion without major redirection. This invention further includes the possibility and ability, depending on design of thebaffle device 20, to change the temperature, pressure and/or other properties of the fluid while flowing through the baffle device. For example, if one uses abaffle device 20 design in combination with a heating element, it may be possible to heat the fluid simultaneously while flowing through thebaffle device 20 itself. - Another possible example of a baffle device which guides fluid motion is schematically presented in
FIG. 4 , which shows thevessel 10 having a funnel-shapedbaffle device 42 that establishes a continual circular motion of the fluid within thevessel 10, wherein thearrows 44 indicate the fluid motion of the solvent 28 through thevessel 10. Note that thisbaffle device 42 may incorporate heating and/or cooling mechanisms that supplement or eliminate the need for other heating and/or cooling devices outside of thevessel 10 and/or inside thevessel 10. Further, while the fluid motion inFIG. 4 is fairly simple, other fluid motion could be engineered as well by means of the design of thebaffle device 42. Such design could create any number of difference zones within thevessel 10 having different characteristics, including but not limited to, solubility, fluid velocity, laminar or turbulent fluid flow patterns, and relative direction of fluid motion within the zones, temperature, pressure, and density of the various atoms, molecules, compounds and/or complexes. - This concludes the description of the preferred embodiment of the present invention. The foregoing description of one or more embodiments of the invention has been presented for the purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to the precise form disclosed. Many modifications and variations are possible in light of the above teaching. It is intended that the scope of the invention be limited not by this detailed description, but rather by the claims appended hereto.
Claims (18)
1. An apparatus for growing one or more crystals, comprising:
(a) a vessel including a first zone containing source materials and a second zone containing seed crystals, wherein the reaction vessel is filled with a solvent for dissolving the source materials in the first zone and transporting the dissolved source materials to the seed crystals in the second zone for growth of the crystals; and
(b) at least one baffle positioned within the vessel and having a plurality of openings configured to control a flow of a fluid comprised of the solvent and the dissolved source materials therein between the first and second zones, wherein the openings in the baffle control motion patterns for the fluid through the baffle.
2. The apparatus of claim 1 , wherein the source materials comprise group-III containing source materials, the seed crystals comprise group-III nitride seed crystals, the solvent comprises a nitrogen-containing solvent, and the crystals comprise group-III nitride crystals.
3. The apparatus of claim 1 , wherein the baffle establishes a circular motion of the fluid within the vessel.
4. The apparatus of claim 1 , wherein the fluid enters the baffle through one or more of the openings near an outer edge of the baffle and the fluid exits the baffle through one or more of the openings in a region that is closer to a center of the baffle.
5. The apparatus of claim 1 , wherein the fluid enters the baffle through one or more of the openings in a region that is closer to a center of the baffle and the fluid exits the baffle through one or more of the openings closer nearer to an outer edge of the baffle.
6. The apparatus of claim 1 , wherein the openings redirect the fluid through the baffle.
7. The apparatus of claim 1 , wherein the baffle suppresses nucleation and growth on undesired locations or surfaces within the vessel, and enhances growth on desired locations or surfaces within the vessel.
8. The apparatus of claim 1 , wherein the baffle changes a temperature, pressure or other properties of the fluid while the fluid flows through the baffle.
9. The apparatus of claim 1 , wherein the baffle incorporates one or more heaters or coolers for the fluid.
10. A method of growing one or more crystals, comprising:
(a) placing source materials into a first zone of a vessel;
(b) placing seed crystals into a second zone of a vessel;
(c) filling the vessel with a solvent for dissolving the source materials in the first zone and transporting the dissolved source materials to the seed crystals in the second zone for growth of the crystals; and
(d) using at least one baffle positioned within the vessel and having a plurality of openings to control a flow of a fluid comprised of the solvent and the dissolved source materials therein between the first and second zones, wherein the openings in the baffle control motion patterns for the fluid through the baffle.
11. The method of claim 10 , wherein the source materials comprise group-III containing source materials, the seed crystals comprise group-III nitride seed crystals, the solvent comprises a nitrogen-containing solvent, and the crystals comprise group-III nitride crystals.
12. The method of claim 10 , wherein the baffle establishes a circular motion of the fluid within the vessel.
13. The method of claim 10 , wherein the fluid enters the baffle through one or more of the openings near an outer edge of the baffle and the fluid exits the baffle through one or more of the openings in a region that is closer to a center of the baffle.
14. The method of claim 10 , wherein the fluid enters the baffle through one or more of the openings in a region that is closer to a center of the baffle and the fluid exits the baffle through one or more of the openings closer nearer to an outer edge of the baffle.
15. The method of claim 10 , wherein the openings redirect the fluid through the baffle.
16. The method of claim 10 , wherein the baffle suppresses nucleation and growth on undesired locations or surfaces within the vessel, and enhances growth on desired locations or surfaces within the vessel.
17. The method of claim 10 , wherein the baffle changes a temperature, pressure or other properties of the fluid while the fluid flows through the baffle.
18. The method of claim 10 , wherein the baffle incorporates one or more heaters or coolers for the fluid.