US20130115479A1 - Porous ceramic coating system - Google Patents
Porous ceramic coating system Download PDFInfo
- Publication number
- US20130115479A1 US20130115479A1 US13/808,259 US201113808259A US2013115479A1 US 20130115479 A1 US20130115479 A1 US 20130115479A1 US 201113808259 A US201113808259 A US 201113808259A US 2013115479 A1 US2013115479 A1 US 2013115479A1
- Authority
- US
- United States
- Prior art keywords
- layer
- ceramic layer
- layer system
- zirconium oxide
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
- F01D—NON-POSITIVE DISPLACEMENT MACHINES OR ENGINES, e.g. STEAM TURBINES
- F01D5/00—Blades; Blade-carrying members; Heating, heat-insulating, cooling or antivibration means on the blades or the members
- F01D5/12—Blades
- F01D5/28—Selecting particular materials; Particular measures relating thereto; Measures against erosion or corrosion
- F01D5/288—Protective coatings for blades
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
- C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
- C23C28/32—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer
- C23C28/321—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer with at least one metal alloy layer
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
- C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
- C23C28/32—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer
- C23C28/321—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer with at least one metal alloy layer
- C23C28/3215—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer with at least one metal alloy layer at least one MCrAlX layer
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
- C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
- C23C28/32—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer
- C23C28/325—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer with layers graded in composition or in physical properties
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
- C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
- C23C28/34—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates
- C23C28/345—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates with at least one oxide layer
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
- C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
- C23C28/34—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates
- C23C28/345—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates with at least one oxide layer
- C23C28/3455—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates with at least one oxide layer with a refractory ceramic layer, e.g. refractory metal oxide, ZrO2, rare earth oxides or a thermal barrier system comprising at least one refractory oxide layer
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F05—INDEXING SCHEMES RELATING TO ENGINES OR PUMPS IN VARIOUS SUBCLASSES OF CLASSES F01-F04
- F05D—INDEXING SCHEME FOR ASPECTS RELATING TO NON-POSITIVE-DISPLACEMENT MACHINES OR ENGINES, GAS-TURBINES OR JET-PROPULSION PLANTS
- F05D2230/00—Manufacture
- F05D2230/80—Repairing, retrofitting or upgrading methods
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F05—INDEXING SCHEMES RELATING TO ENGINES OR PUMPS IN VARIOUS SUBCLASSES OF CLASSES F01-F04
- F05D—INDEXING SCHEME FOR ASPECTS RELATING TO NON-POSITIVE-DISPLACEMENT MACHINES OR ENGINES, GAS-TURBINES OR JET-PROPULSION PLANTS
- F05D2240/00—Components
- F05D2240/40—Use of a multiplicity of similar components
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F05—INDEXING SCHEMES RELATING TO ENGINES OR PUMPS IN VARIOUS SUBCLASSES OF CLASSES F01-F04
- F05D—INDEXING SCHEME FOR ASPECTS RELATING TO NON-POSITIVE-DISPLACEMENT MACHINES OR ENGINES, GAS-TURBINES OR JET-PROPULSION PLANTS
- F05D2300/00—Materials; Properties thereof
- F05D2300/20—Oxide or non-oxide ceramics
- F05D2300/21—Oxide ceramics
- F05D2300/2118—Zirconium oxides
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02T—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO TRANSPORTATION
- Y02T50/00—Aeronautics or air transport
- Y02T50/60—Efficient propulsion technologies, e.g. for aircraft
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12479—Porous [e.g., foamed, spongy, cracked, etc.]
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
- Y10T428/24942—Structurally defined web or sheet [e.g., overall dimension, etc.] including components having same physical characteristic in differing degree
- Y10T428/2495—Thickness [relative or absolute]
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/249921—Web or sheet containing structurally defined element or component
- Y10T428/249953—Composite having voids in a component [e.g., porous, cellular, etc.]
- Y10T428/249981—Plural void-containing components
Definitions
- the invention relates to a layer system having two different porous ceramic layers.
- Ceramic protective layers are often used for components used at high temperatures in order to protect the metallic substrate from relatively high temperatures.
- the ceramic layers have a certain porosity in order firstly to reduce the thermal conductivity and in order to set a certain ductility.
- FIG. 1 shows a layer system
- FIG. 2 shows a gas turbine
- FIG. 3 shows a turbine blade or vane
- FIG. 4 shows a combustion chamber
- FIG. 5 shows a list of superalloys.
- FIG. 1 schematically shows the layer system.
- the layer system 1 is preferably a turbine blade or vane 120 , 130 of a turbine, of a steam turbine, of a gas turbine 100 ( FIG. 2 ), for stationary operation or for aircraft.
- the substrate 4 prefferably comprises a nickel-based or cobalt-based superalloy made of an alloy shown in FIG. 5 .
- This is preferably a nickel-based superalloy.
- a metallic bonding layer in particular of the MCrAl or MCrAlX type (M ⁇ Ni, Co, Fe, preferably Ni, Co), is preferably present on the substrate 4 .
- a ceramic layer 16 there may be diffusion layers within the substrate 4 , to which a ceramic layer 16 can be applied.
- a ceramic layer 16 is applied to the metallic layer 7 or to the substrate 4 , wherein an oxide layer (TGO) is either produced deliberately on or applied to the interface, this forming during the ceramic coating or during operation of a layer system having the metallic layer 7 .
- TGO oxide layer
- the ceramic layer 16 has at least two, in particular only two, different ceramic layers 10 , 13 .
- the lower ceramic layer 10 has a lower porosity than the outer ceramic layer 13 .
- the porosity of the lower ceramic layer 10 is 8% to 14%, in particular 11% to 12% (preferably % by volume).
- the layer thickness of the inner ceramic layer 10 is at least 10%, in particular 20%, very particularly 50%, thinner than that of the outer ceramic layer 13 .
- the lower layer has a thickness of 100 ⁇ 25 ⁇ m, whereas the outer layer has a thickness of >100 ⁇ m.
- the outer ceramic layer 13 has a porosity of 14% to 18% and is preferably the outermost layer, which is exposed directly to the hot gas.
- the material of the lower ceramic layer 10 is partially stabilized, in particular by yttrium, zirconium oxide. This material is preferably also used for the outer ceramic layer 13 , although it is also possible to use a pyrochlore material.
- FIG. 2 shows, by way of example, a partial longitudinal section through a gas turbine 100 .
- the gas turbine 100 has a rotor 103 with a shaft which is mounted such that it can rotate about an axis of rotation 102 and is also referred to as the turbine rotor.
- the annular combustion chamber 110 is in communication with a, for example, annular hot-gas passage 111 , where, by way of example, four successive turbine stages 112 form the turbine 108 .
- Each turbine stage 112 is formed, for example, from two blade or vane rings. As seen in the direction of flow of a working medium 113 , in the hot-gas passage 111 a row of guide vanes 115 is followed by a row 125 formed from rotor blades 120 .
- the guide vanes 130 are secured to an inner housing 138 of a stator 143 , whereas the rotor blades 120 of a row 125 are fitted to the rotor 103 for example by means of a turbine disk 133 .
- a generator (not shown) is coupled to the rotor 103 .
- the compressor 105 While the gas turbine 100 is operating, the compressor 105 sucks in air 135 through the intake housing 104 and compresses it. The compressed air provided at the turbine-side end of the compressor 105 is passed to the burners 107 , where it is mixed with a fuel. The mix is then burnt in the combustion chamber 110 , forming the working medium 113 . From there, the working medium 113 flows along the hot-gas passage 111 past the guide vanes 130 and the rotor blades 120 . The working medium 113 is expanded at the rotor blades 120 , transferring its momentum, so that the rotor blades 120 drive the rotor 103 and the latter in turn drives the generator coupled to it.
- Substrates of the components may likewise have a directional structure, i.e. they are in single-crystal form (SX structure) or have only longitudinally oriented grains (DS structure).
- SX structure single-crystal form
- DS structure longitudinally oriented grains
- iron-based, nickel-based or cobalt-based superalloys are used as material for the components, in particular for the turbine blade or vane 120 , 130 and components of the combustion chamber 110 .
- the guide vane 130 has a guide vane root (not shown here), which faces the inner housing 138 of the turbine 108 , and a guide vane head which is at the opposite end from the guide vane root.
- the guide vane head faces the rotor 103 and is fixed to a securing ring 140 of the stator 143 .
- FIG. 3 shows a perspective view of a rotor blade 120 or guide vane 130 of a turbomachine, which extends along a longitudinal axis 121 .
- the turbomachine may be a gas turbine of an aircraft or of a power plant for generating electricity, a steam turbine or a compressor.
- the blade or vane 120 , 130 has, in succession along the longitudinal axis 121 , a securing region 400 , an adjoining blade or vane platform 403 and a main blade or vane part 406 and a blade or vane tip 415 .
- the vane 130 may have a further platform (not shown) at its vane tip 415 .
- a blade or vane root 183 which is used to secure the rotor blades 120 , 130 to a shaft or a disk (not shown), is formed in the securing region 400 .
- the blade or vane root 183 is designed, for example, in hammerhead form. Other configurations, such as a fir-tree or dovetail root, are possible.
- the blade or vane 120 , 130 has a leading edge 409 and a trailing edge 412 for a medium which flows past the main blade or vane part 406 .
- the blade or vane 120 , 130 may in this case be produced by a casting process, by means of directional solidification, by a forging process, by a milling process or combinations thereof.
- Workpieces with a single-crystal structure or structures are used as components for machines which, in operation, are exposed to high mechanical, thermal and/or chemical stresses.
- Single-crystal workpieces of this type are produced, for example, by directional solidification from the melt. This involves casting processes in which the liquid metallic alloy solidifies to form the single-crystal structure, i.e. the single-crystal workpiece, or solidifies directionally.
- dendritic crystals are oriented along the direction of heat flow and form either a columnar crystalline grain structure (i.e. grains which run over the entire length of the workpiece and are referred to here, in accordance with the language customarily used, as directionally solidified) or a single-crystal structure, i.e. the entire workpiece consists of one single crystal.
- a transition to globular (polycrystalline) solidification needs to be avoided, since non-directional growth inevitably forms transverse and longitudinal grain boundaries, which negate the favorable properties of the directionally solidified or single-crystal component.
- directionally solidified microstructures refers in general terms to directionally solidified microstructures, this is to be understood as meaning both single crystals, which do not have any grain boundaries or at most have small-angle grain boundaries, and columnar crystal structures, which do have grain boundaries running in the longitudinal direction but do not have any transverse grain boundaries.
- This second form of crystalline structures is also described as directionally solidified microstructures (directionally solidified structures).
- the blades or vanes 120 , 130 may likewise have coatings protecting against corrosion or oxidation e.g. (MCrAlX; M is at least one element selected from the group consisting of iron (Fe), cobalt (Co), nickel (Ni), X is an active element and stands for yttrium (Y) and/or silicon and/or at least one rare earth element, or hafnium (Hf)). Alloys of this type are known from EP 0 486 489 B1, EP 0 786 017 B1, EP 0 412 397 B1 or EP 1 306 454 A1.
- the density is preferably 95% of the theoretical density.
- the layer preferably has a composition Co-30Ni-28Cr-8Al-0.6Y-0.7Si or Co-28Ni-24Cr-10Al-0.6Y.
- nickel-based protective layers such as Ni-10Cr-12Al-0.6Y-3Re or Ni-12Co-21Cr-11Al-0.4Y-2Re or Ni-25Co-17Cr-10Al-0.4Y-1.5Re.
- thermal barrier coating which is preferably the outermost layer, to be present on the MCrAlX, consisting for example of ZrO 2 , Y 2 O 3 -ZrO 2 , i.e. unstabilized, partially stabilized or fully stabilized by yttrium oxide and/or calcium oxide and/or magnesium oxide.
- the thermal barrier coating covers the entire MCrAlX layer.
- Columnar grains are produced in the thermal barrier coating by suitable coating processes, such as for example electron beam physical vapor deposition (EB-PVD).
- EB-PVD electron beam physical vapor deposition
- the thermal barrier coating may include grains that are porous or have micro-cracks or macro-cracks, in order to improve the resistance to thermal shocks.
- the thermal barrier coating is therefore preferably more porous than the MCrAlX layer.
- the blade or vane 120 , 130 may be hollow or solid in form.
- the blade or vane 120 , 130 is hollow and may also have film-cooling holes 418 (indicated by dashed lines).
- FIG. 4 shows a combustion chamber 110 of the gas turbine 100 .
- the combustion chamber 110 is configured, for example, as what is known as an annular combustion chamber, in which a multiplicity of burners 107 , which generate flames 156 , arranged circumferentially around an axis of rotation 102 open out into a common combustion chamber space 154 .
- the combustion chamber 110 overall is of annular configuration positioned around the axis of rotation 102 .
- the combustion chamber 110 is designed for a relatively high temperature of the working medium M of approximately 1000° C. to 1600° C.
- the combustion chamber wall 153 is provided, on its side which faces the working medium M, with an inner lining formed from heat shield elements 155 .
- a cooling system may be provided for the heat shield elements 155 and/or their holding elements, on account of the high temperatures in the interior of the combustion chamber 110 .
- the heat shield elements 155 are then, for example, hollow and may also have cooling holes (not shown) opening out into the combustion chamber space 154 .
- each heat shield element 155 made from an alloy is equipped with a particularly heat-resistant protective layer (MCrAlX layer and/or ceramic coating) or is made from material that is able to withstand high temperatures (solid ceramic bricks).
- M is at least one element selected from the group consisting of iron (Fe), cobalt (Co), nickel (Ni), X is an active element and stands for yttrium (Y) and/or silicon and/or at least one rare earth element or hafnium (Hf). Alloys of this type are known from EP 0 486 489 B1, EP 0 786 017 B1, EP 0 412 397 B1 or EP 1 306 454 A1.
- a, for example ceramic, thermal barrier coating to be present on the MCrAlX, consisting for example of ZrO 2 , Y 2 O 3 —ZrO 2 , i.e. unstabilized, partially stabilized or fully stabilized by yttrium oxide and/or calcium oxide and/or magnesium oxide.
- Columnar grains are produced in the thermal barrier coating by suitable coating processes, such as for example electron beam physical vapor deposition (EB-PVD).
- EB-PVD electron beam physical vapor deposition
- the thermal barrier coating may include grains that are porous or have micro-cracks or macro-cracks, in order to improve the resistance to thermal shocks.
- Refurbishment means that after they have been used, protective layers may have to be removed from turbine blades or vanes 120 , 130 or heat shield elements 155 (e.g. by sand-blasting). Then, the corrosion and/or oxidation layers and products are removed. If appropriate, cracks in the turbine blade or vane 120 , 130 or the heat shield element 155 are also repaired. This is followed by recoating of the turbine blades or vanes 120 , 130 or heat shield elements 155 , after which the turbine blades or vanes 120 , 130 or the heat shield elements 155 can be reused.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Inorganic Chemistry (AREA)
- Mechanical Engineering (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Organic Chemistry (AREA)
- General Engineering & Computer Science (AREA)
- Ceramic Engineering (AREA)
- Turbine Rotor Nozzle Sealing (AREA)
- Other Surface Treatments For Metallic Materials (AREA)
- Physical Vapour Deposition (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP20100007240 EP2407579A1 (de) | 2010-07-14 | 2010-07-14 | Poröses keramisches Schichtsystem |
EP10007240.4 | 2010-07-14 | ||
PCT/EP2011/061320 WO2012007320A1 (de) | 2010-07-14 | 2011-07-05 | Poröses keramisches schichtsystem |
Publications (1)
Publication Number | Publication Date |
---|---|
US20130115479A1 true US20130115479A1 (en) | 2013-05-09 |
Family
ID=42727613
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US13/808,259 Abandoned US20130115479A1 (en) | 2010-07-14 | 2011-07-05 | Porous ceramic coating system |
Country Status (5)
Country | Link |
---|---|
US (1) | US20130115479A1 (zh) |
EP (2) | EP2407579A1 (zh) |
CN (2) | CN105177571A (zh) |
ES (1) | ES2496791T3 (zh) |
WO (1) | WO2012007320A1 (zh) |
Cited By (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20150159507A1 (en) * | 2013-12-06 | 2015-06-11 | General Electric Company | Article for high temperature service |
US20160024941A1 (en) * | 2013-09-10 | 2016-01-28 | Siemens Aktiengesellschaft | Porous ceramic layer system |
EP3385408A1 (en) * | 2017-04-07 | 2018-10-10 | General Electric Company | Thermal barrier system with thin dense columnar tbc layer and methods of forming the same |
US20180371599A1 (en) * | 2017-06-26 | 2018-12-27 | United Technologies Corporation | Alumina seal coating with interlayer |
US10215034B2 (en) | 2012-10-05 | 2019-02-26 | Siemens Aktiengesellschaft | Method for treating a gas turbine blade and gas turbine having said blade |
US11274560B2 (en) | 2017-04-28 | 2022-03-15 | Siemens Energy Global GmbH & Co. KG | Sealing system for a rotor blade and housing |
Families Citing this family (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN104605695B (zh) * | 2013-11-03 | 2017-09-15 | 邱莉 | 紫砂壶及其打磨方法 |
EP2881491A1 (en) * | 2013-12-06 | 2015-06-10 | Siemens Aktiengesellschaft | A coating system for a component of a turbomachine and a method for generating a coating system |
DE102014220359A1 (de) * | 2014-10-08 | 2016-04-14 | Siemens Aktiengesellschaft | Doppellagige Zirkonoxidschicht mit hochreinem Anteil |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20030138658A1 (en) * | 2002-01-22 | 2003-07-24 | Taylor Thomas Alan | Multilayer thermal barrier coating |
US20080187659A1 (en) * | 2004-07-26 | 2008-08-07 | Irene Spitsberg | Methods for preparing thermal barrier coatings with high fracture toughness inner layer for improved impact resistance |
US20100015401A1 (en) * | 2008-05-26 | 2010-01-21 | Andrea Bolz | Ceramic thermal barrier coating system with two ceramic layers |
Family Cites Families (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE3926479A1 (de) | 1989-08-10 | 1991-02-14 | Siemens Ag | Rheniumhaltige schutzbeschichtung, mit grosser korrosions- und/oder oxidationsbestaendigkeit |
WO1991002108A1 (de) | 1989-08-10 | 1991-02-21 | Siemens Aktiengesellschaft | Hochtemperaturfeste korrosionsschutzbeschichtung, insbesondere für gasturbinenbauteile |
KR100354411B1 (ko) | 1994-10-14 | 2002-11-18 | 지멘스 악티엔게젤샤프트 | 부식,산화및과도한열응력으로부터부품을보호하기위한보호층및그제조방법 |
EP0861927A1 (de) | 1997-02-24 | 1998-09-02 | Sulzer Innotec Ag | Verfahren zum Herstellen von einkristallinen Strukturen |
EP0892090B1 (de) | 1997-02-24 | 2008-04-23 | Sulzer Innotec Ag | Verfahren zum Herstellen von einkristallinen Strukturen |
WO1999067435A1 (en) | 1998-06-23 | 1999-12-29 | Siemens Aktiengesellschaft | Directionally solidified casting with improved transverse stress rupture strength |
US6231692B1 (en) | 1999-01-28 | 2001-05-15 | Howmet Research Corporation | Nickel base superalloy with improved machinability and method of making thereof |
JP2003529677A (ja) | 1999-07-29 | 2003-10-07 | シーメンス アクチエンゲゼルシヤフト | 耐熱性の構造部材及びその製造方法 |
US6444259B1 (en) * | 2001-01-30 | 2002-09-03 | Siemens Westinghouse Power Corporation | Thermal barrier coating applied with cold spray technique |
DE50104022D1 (de) | 2001-10-24 | 2004-11-11 | Siemens Ag | Rhenium enthaltende Schutzschicht zum Schutz eines Bauteils gegen Korrosion und Oxidation bei hohen Temperaturen |
DE50112339D1 (de) | 2001-12-13 | 2007-05-24 | Siemens Ag | Hochtemperaturbeständiges Bauteil aus einkristalliner oder polykristalliner Nickel-Basis-Superlegierung |
DE10225532C1 (de) * | 2002-06-10 | 2003-12-04 | Mtu Aero Engines Gmbh | Schichtsystem für die Rotor-/Statordichtung einer Strömungsmaschine |
WO2007112783A1 (en) * | 2006-04-06 | 2007-10-11 | Siemens Aktiengesellschaft | Layered thermal barrier coating with a high porosity, and a component |
EP2230329A1 (de) * | 2009-03-18 | 2010-09-22 | Siemens Aktiengesellschaft | Zweilagiges poröses Schichtsystem mit Pyrochlor-Phase |
EP2341166A1 (en) * | 2009-12-29 | 2011-07-06 | Siemens Aktiengesellschaft | Nano and micro structured ceramic thermal barrier coating |
-
2010
- 2010-07-14 EP EP20100007240 patent/EP2407579A1/de not_active Withdrawn
-
2011
- 2011-07-05 WO PCT/EP2011/061320 patent/WO2012007320A1/de active Application Filing
- 2011-07-05 ES ES11730287.7T patent/ES2496791T3/es active Active
- 2011-07-05 US US13/808,259 patent/US20130115479A1/en not_active Abandoned
- 2011-07-05 CN CN201510627939.5A patent/CN105177571A/zh active Pending
- 2011-07-05 CN CN2011800347308A patent/CN103003472A/zh active Pending
- 2011-07-05 EP EP20110730287 patent/EP2593582B1/de active Active
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20030138658A1 (en) * | 2002-01-22 | 2003-07-24 | Taylor Thomas Alan | Multilayer thermal barrier coating |
US20080187659A1 (en) * | 2004-07-26 | 2008-08-07 | Irene Spitsberg | Methods for preparing thermal barrier coatings with high fracture toughness inner layer for improved impact resistance |
US20100015401A1 (en) * | 2008-05-26 | 2010-01-21 | Andrea Bolz | Ceramic thermal barrier coating system with two ceramic layers |
Cited By (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US10215034B2 (en) | 2012-10-05 | 2019-02-26 | Siemens Aktiengesellschaft | Method for treating a gas turbine blade and gas turbine having said blade |
US10995625B2 (en) | 2012-10-05 | 2021-05-04 | Siemens Aktiengesellschaft | Method for treating a gas turbine blade and gas turbine having said blade |
US20160024941A1 (en) * | 2013-09-10 | 2016-01-28 | Siemens Aktiengesellschaft | Porous ceramic layer system |
US20150159507A1 (en) * | 2013-12-06 | 2015-06-11 | General Electric Company | Article for high temperature service |
EP3385408A1 (en) * | 2017-04-07 | 2018-10-10 | General Electric Company | Thermal barrier system with thin dense columnar tbc layer and methods of forming the same |
US11274560B2 (en) | 2017-04-28 | 2022-03-15 | Siemens Energy Global GmbH & Co. KG | Sealing system for a rotor blade and housing |
US20180371599A1 (en) * | 2017-06-26 | 2018-12-27 | United Technologies Corporation | Alumina seal coating with interlayer |
US11597991B2 (en) * | 2017-06-26 | 2023-03-07 | Raytheon Technologies Corporation | Alumina seal coating with interlayer |
Also Published As
Publication number | Publication date |
---|---|
CN103003472A (zh) | 2013-03-27 |
ES2496791T3 (es) | 2014-09-19 |
CN105177571A (zh) | 2015-12-23 |
WO2012007320A1 (de) | 2012-01-19 |
EP2593582B1 (de) | 2014-06-25 |
EP2593582A1 (de) | 2013-05-22 |
EP2407579A1 (de) | 2012-01-18 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US7935413B2 (en) | Layer system with layer having different grain sizes | |
US20130115479A1 (en) | Porous ceramic coating system | |
US10465535B2 (en) | Compressor blade or vane having an erosion-resistant hard material coating | |
WO2007112783A1 (en) | Layered thermal barrier coating with a high porosity, and a component | |
US9097127B2 (en) | Porous layer system having a porous inner layer | |
US20110031226A1 (en) | Method for Welding Depending on a Preferred Direction of the Substrate | |
US20110135947A1 (en) | Masking Material, Masking Layer, Process for Masking a Substrate and Process for Coating a Substrate | |
US20100143745A1 (en) | NiCoCrl layer for forming dense and solid oxide layers and metallic layer system | |
US10995625B2 (en) | Method for treating a gas turbine blade and gas turbine having said blade | |
US20100285415A1 (en) | Burner Element and Burner Having Aluminum Oxide Coating and Method for Coating a Burner Element | |
US20110268987A1 (en) | Mcralx Layer Having Differing Chromium and Aluminum Content | |
US20110143163A1 (en) | Method for the production of an optimized bonding agent layer by means of partial evaporation of the bonding agent layer, and a layer system | |
US9421639B2 (en) | Component having weld seam and method for producing a weld seam | |
US20160281511A1 (en) | Modified surface around a hole | |
US20160312622A1 (en) | Thermal barrier coating of a turbine blade | |
US20110293431A1 (en) | Component having varying structures and method for production | |
US20120263866A1 (en) | Method for measuring layer thickness by means of laser triangulation, and device | |
US20120088064A1 (en) | Method For Coating A Component With Film Cooling Holes And Component | |
US20140315006A1 (en) | Ceramic double layer based on zirconium oxide | |
US20120301624A1 (en) | Spray nozzle and method for atmospheric spraying, device for coating, and coated component | |
US20110020127A1 (en) | Component Comprising Overlapping Weld Seams and Method for the Production Thereof | |
US20100288823A1 (en) | Application of Solder to Holes, Coating Processes and Small Solder Rods | |
US8574671B2 (en) | Method for adjusting the coolant consumption within actively cooled components, and component | |
US20160024941A1 (en) | Porous ceramic layer system | |
US20100224600A1 (en) | Two-step welding process |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: SIEMENS AKTIENGESELLSCHAFT, GERMANY Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:STAMM, WERNER;REEL/FRAME:029564/0472 Effective date: 20121109 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |