US20120100425A1 - Lead alkaline battery - Google Patents

Lead alkaline battery Download PDF

Info

Publication number
US20120100425A1
US20120100425A1 US13/299,482 US201113299482A US2012100425A1 US 20120100425 A1 US20120100425 A1 US 20120100425A1 US 201113299482 A US201113299482 A US 201113299482A US 2012100425 A1 US2012100425 A1 US 2012100425A1
Authority
US
United States
Prior art keywords
lead
electrolyte
cell
metal
battery
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/299,482
Inventor
John E. Stauffer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US10/758,015 external-priority patent/US6982428B2/en
Priority claimed from US11/167,535 external-priority patent/US7947391B2/en
Priority claimed from US12/410,500 external-priority patent/US20090181312A1/en
Application filed by Individual filed Critical Individual
Priority to US13/299,482 priority Critical patent/US20120100425A1/en
Publication of US20120100425A1 publication Critical patent/US20120100425A1/en
Priority to US14/032,540 priority patent/US8932753B2/en
Abandoned legal-status Critical Current

Abstract

A rechargeable battery is provided such that the positive electrode comprises lead dioxide, the negative electrode comprises a metal selected from the group consisting of iron, zinc, cadmium, lanthanum/nickel alloys and titanium/zirconium alloys, and the electrolyte is an aqueous alkali-metal acetate. Upon discharge, the lead dioxide is reduced to lead oxide, and the electrolyte remains unchanged. The reactions are reversed when the battery is charged.

Description

    CROSS-REFERENCE TO RELATED APPLICATION
  • This application is a continuation-in-part of application Ser. No. 12/410,500 which is a continuation-in-part of application Ser. No. 11/167,535, filed on Jun. 27, 2005, which is a continuation-in-part of application Ser. No. 10/756,015, filed on Jan. 13, 2004.
  • FIELD OF THE INVENTION
  • The present invention relates to a novel type of storage battery which is distinguished by its unique electrochemistry. In the changed condition, the positive electrode comprises lead dioxide and the negative electrode comprises a metal or a metal alloy.
  • BACKGROUND OF THE INVENTION
  • The most common storage battery, found in almost every vehicle, is the lead-acid battery. This battery comprises a lead dioxide positive electrode, a lead metal negative electrode, and sulfuric acid for the electrolyte. Its chief advantage is low cost. Nevertheless, it has a limited energy density and the electrolyte is extremely corrosive. Furthermore, sufficient acid is required to react with the electrodes during discharge. Maintenance-free types avoid the loss of evolved gases, as disclosed in U.S. Pat. No. 3,862,861, but their cycle-life is still restricted.
  • The search for alternatives to the lead-acid battery has been ongoing. As far back as 1934, Drumm disclosed the nickel-oxide zinc battery and the silver oxide-zinc battery (U.S. Pat. No. 1,955,115). Both of these batteries employ zinc as the negative electrode and caustic potash as the electrolyte. Nickel oxide or silver oxide serves as the positive electrode. These batteries have improved energy densities and for many uses are a good compromise.
  • The ideal storage battery would combine the best features of existing batteries with none of the drawbacks. The need for such a battery is apparent for backup systems and in mobile applications. Therefore, it is an object of the present invention to provide an improved storage battery, one that is both economical and highly efficient. These and other objects, features, and advantages of the invention will be recognized from the following description and accompanying figure.
  • SUMMARY OF THE DISCLOSURE
  • A rechargeable battery has been developed in which the positive electrode comprises lead dioxide in the charged condition, a negative electrode of metal or an alloy of metals, and an aqueous electrolyte comprising an alkali metal acetate. Upon discharge, the lead dioxide is reduced to lead oxide and the metal is oxidized to an oxide. These reactions are reversed when the battery is charged.
  • The negative electrode can be a metal selected from the group consisting of iron, zinc, cadmium, lanthanum/nickel and titanium/zirconium alloys.
  • The electrolyte of the cell is alkaline. Aqueous solutions of bases provide the alkalinity. The preferred buffer is an alkali metal acetate prepared from a weak acid and a strong base such as an alkali metal hydroxide. These compounds readily dissolve in water to form solutions with superior electrical conductivities.
  • Other solutions can be considered for the electrolyte as well. These include carbonates, borates, silicates, phosphates and sulfates. They may be introduced by the corresponding acids or their respective salts.
  • The electrodes of a practical embodiment of the invention may be configured as sheets, fibers, or particles thereby to maximize electrode surface area. Interspersed particles of a carbonaceous material may be used to improve the electrical conductivity. A gelling agent may be added to immobilize the electrolyte. As required, a separator may be employed between the positive and negative electrodes to prevent a short circuit.
  • WRITTEN DESCRIPTION
  • The chemistry of the lead-alkaline battery is important in order to gain an understanding of its operation. A positive electrode initially made of lead becomes lead dioxide when changed which is reduced to lead oxide during discharge. In the case where the negative electrode comprises, for example, zinc, this metal is oxidized to zinc oxide when the cell is discharged. The electrolyte is alkaline such that the solution contains an excess of hydroxyl ions. The electrode reactions during discharge can be represented by the following equations:
  • Positive Electrode:

  • PbO2+H2O+2e→PbO+2OH  (1)
  • Negative Electrode

  • Zn+2OH→ZnO+H2O+2e  (2)
  • In the above reaction, zinc hydroxide may be an intermediate in the formation of zinc oxide. When these equations are combined, the reaction for the cell is:

  • PbO2+Zn→PbO+ZnO   (3)
  • In the overall reaction, there is no change in the average composition of the electrolyte during discharge although there may be concentration gradients.
  • During recharging of the cell, the reactions are reversed. Thus, lead oxide is oxidized to lead dioxide and zinc oxide is reduced to zinc metal. The emf necessary for charging is supplied by an external power source. The discharge-recharge cycle can be repeated endlessly, thus fulfilling the function of a storage battery.
  • A particularly difficult challenge in designing new batteries is identifying electrode materials that will undergo electrochemical reactions and still withstand corrosion by the electrolyte. Although theory is helpful in this respect, empirical data are required to prove the effectiveness of materials—both for the electrodes and the electrolyte. One measure of the relative performance of a cell is its open-circuit voltage. Another consideration is cycle life.
  • Zinc is used as an example of a negative electrode that can be used with the lead positive electrode and the electrolyte described herein. However, other materials can be used for the negative electrode, including but not limited to iron, lead, cadmium and metal hydrides. Metal hydrides are materials that comprise certain alloys that on charging absorb atomic hydrogen to form the metal hydride. At least two classes of alloys are suitable to form metal hydrides. One group of alloys is based on rare earths and generally consists of a lanthanum-nickel blend. A second group of alloys is made of a titanium-zirconium composition. The negative electrodes herein are provided by way of example and are not meant to be limiting. It is contemplated that other alloys can be used as a negative electrode in the battery embodiments disclosed herein.
  • The use of lead in an alkaline cell may seem questionable because lead in the +2 oxidation state commonly forms plumbous salts containing the positive divalent ion Pb++. However, by the action of hydroxides on plumbous compounds it is possible to form the negative ion HPbO2 which is soluble in aqueous solutions. Accordingly, Pb(OH)2 is regarded as an amphoteric hydroxide. In a similar manner, concentrated solutions of alkali hydroxides act upon the dioxide PbO2 to form plumbate ions, PbO4 −4 and PbO3 −2, which are likewise soluble.
  • In view of these considerations, one goal of the research on new cells was to control the concentration hydroxides in the electrolyte. This result was made possible by employing solutions of sodium carbonate which react as follows:

  • Na2CO3+H2O
    Figure US20120100425A1-20120426-P00001
    NaOH+NaHCO3   (4)
  • From this equation it is seen that such solutions are strongly alkaline. The carbonic acid set free on hydrolysis does not escape when the base is strong but forms the bicarbonate. However, hydrolysis can be reduced by increasing the concentration of the sodium carbonate, thus permitting a degree of control over the formation of hydroxide.
  • In place of carbonates, borates can be employed to similar advantage. Boric acid is a weak acid, much more mild than carbonic acid. Thus, its salts tend to hydrolyze in solution. The following equation shows the reaction of potassium meta borate in solution to form potassium hydroxide and potassium tetra borate.

  • 2K2B2O4+H2O
    Figure US20120100425A1-20120426-P00001
    2KOH+K2B4O7   (5)
  • Again the hydroxyl concentration can be controlled by adjusting the concentration of the potassium borate.
  • Carbonates and borates are effective not only in controlling the alkalinity of the electrolyte, but they also form insoluble salts with lead. In this manner the corrosion of the positive electrode can be minimized. Not only are carbonates and borates helpful in this regard, but other salts are likewise effective. Silicates, phosphates and sulfates form insoluble salts with lead.
  • Alkalinity can be provided by compounds of the alkali metals including lithium, sodium, potassium, and cesium. Lithium has certain limitations inasmuch as its carbonate and phosphate are almost insoluble in water. Cesium provides a very strong base but the cost of this material limits its potential applications. While ammonium hydroxide is basic in solution, its volatility restricts its use. Finally, tetramethyl ammonium hydroxide is known to be strongly alkaline, approaching that of sodium hydroxide and potassium hydroxide.
  • The present invention covers the use of aqueous solutions for the electrolyte. These solutions have the advantage of superior electrical conductivities. Although use of organic solvents including alcohols and glycols is feasible, their performance is inferior.
  • The configuration of a lead-alkaline cell is not restricted. For purposes of testing various combinations of electrodes and electrolytes, a simple cell was assembled from a glass jar and strips of metal separated, as need be, by a polypropylene sheet. A workable battery, however, would necessarily be designed with the maximum surface areas for the electrodes and minimum volume of electrolyte. Such geometric designs as parallel plates, either flat or spirally wound, are appropriate. Alternatively, particles of lead and metal either alone or interspersed with graphite may be employed. In this manner, the capacity of the cell can be increased and its internal resistance minimized.
  • To gain a greater appreciation of the present invention, FIG. 1 illustrates its distinctive features. The cut-away perspective shows a lead-zinc battery comprising a single cell with its electrodes arranged as flat parallel plates. The lead dioxide positive electrodes 1 and the zinc negative electrodes 2 are kept apart by separators 3. These parts are immersed in the alkaline electrolyte 4, which is contained in casing 5. This sectional view also shows the electrical leads attached to the electrodes. An advantage of this design is that by placing the positive and negative electrodes in close proximity to each other the quantity of electrolyte is reduced.
  • Applications of a secondary battery as provided by the present invention are almost limitless. The largest application is in vehicles including automobiles powered by new hybrid motors. Other uses include portable electronic devices such as cell phones and laptop computers.
  • Example No. 1
  • The electrolyte was prepared by heating 100.0 gm. of potassium bicarbonate in an oven to convert it to potassium carbonate, which was then dissolved in 185 ml. of water. The positive electrode was formed from a 1½ in. wide strip of lead and the negative electrode was a 1½ in. wide strip of steel. The cell comprised a glass jar about 2¾ in. diameter by 2½ in. high. After charging the cell at 2.5 volts for 21 minutes an open circuit potential of 1.7 volts was observed. At the end of the run both electrodes were in good condition and the electrolyte was water-white.
  • Example No. 2
  • The electrolyte was prepared by heading 106.3 gm. of sodium bicarbonate in an oven to convert it to sodium carbonate, which was dissolved in 250 ml. of water and 10 ml. of concentrated sulfuric acid. Two strips of lead 2 in. wide were used for the positive and negative electrodes. The cell comprised a glass jar 2½ in. diameter by 4 in. high. After charging the cell at 2.4 volts for 9 minutes an open circuit potential of 1.5 volts was observed. Both electrodes were dimensionally stable.
  • Example No. 3
  • The same cell was used as in Example 2, but 3.7 gm. of sodium hydroxide pellets were added to the electrolyte. Also, a zinc electrode was substituted for the negative lead electrode. After charging the cell at 2.5 volts for 3 minutes an open circuit of 2.1 volts was obtained. The electrodes remained in excellent condition after repeat cycling.
  • Example No. 4
  • A cell fashioned from a glass jar 1.75 in. in diameter by 3.5 in. high. The positive electrode was a strip of lead 1.5 in. wide by 4 in. long. The negative electrode was a sheet of zinc 1.5 in. wide by 4 in. long. The electrolyte was prepared by neutralizing sodium bicarbonate (baking soda) with white vinegar of 5% acidity (acetic acid). Vinegar was added to 78.8 gm. of sodium bicarbonate until foaming stopped and the solution was clear. The resulting solution was boiled down to 350 ml. After charging the cell for 15 minutes at 3.0 volts, a cell potential of 2.1 volts was realized. Upon discharging the cell, a flashlight bulb was lit brightly with a current of 85 milliamps. The cell was repeatedly cycled. At the end of the run, both electrodes were in excellent condition.
  • In summary, the present invention provides for the use of a buffer in the electrolyte of a storage battery. As noted in the prior applications, the use of a buffer helps to control the pH of the electrolyte thereby minimizing the corrosion of the electrodes.
  • Alkali metal acetates are known to be effective buffers (The Merck Index, 11th Ed., p. 1355). They are prepared from a weak acid (acetic acid) and a strong base (alkali metal hydroxide). These compounds readily dissolve in water to form solutions that have superior electrical conductivities.
  • A cell per Example No. 3 can be constructed using cadmium as the negative electrode.

Claims (3)

1. A storage battery comprising:
a. a positive electrode which exists as lead dioxide in the charged condition,
b. a negative electrode of metal, and
c. an aqueous electrolyte comprising an alkali metal acetate.
2. A storage battery of claim 1 in which the metal is selected from the group consisting of iron, zinc, cadmium, lanthanum/nickel, and titanium/zirconium alloy.
3. A storage battery of claim 1 in which the alkali metal is selected from the group lithium, sodium, potassium, rubidium, and cesium.
US13/299,482 2004-01-13 2011-11-18 Lead alkaline battery Abandoned US20120100425A1 (en)