US20110075297A1 - Patterned magnetic media having an exchange bridge structure connecting islands - Google Patents
Patterned magnetic media having an exchange bridge structure connecting islands Download PDFInfo
- Publication number
- US20110075297A1 US20110075297A1 US12/959,692 US95969210A US2011075297A1 US 20110075297 A1 US20110075297 A1 US 20110075297A1 US 95969210 A US95969210 A US 95969210A US 2011075297 A1 US2011075297 A1 US 2011075297A1
- Authority
- US
- United States
- Prior art keywords
- magnetic recording
- islands
- exchange
- patterned
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This non-provisional patent application is a continuation of U.S. patent application Ser. No. 11/964,685 filed on Dec. 26, 2007, which is incorporated herein by reference.
- 1. Field of the Invention
- The invention is related to the field of magnetic disk drive systems and, in particular, to patterned magnetic media having an exchange bridge structure connecting the islands of a perpendicular magnetic recording layer.
- 2. Statement of the Problem
- Many computer systems use magnetic disk drives for mass storage of information. Magnetic disk drives typically include one or more magnetic recording heads (sometimes referred to as sliders) that include read elements and write elements. An actuator/suspension arm holds the recording head above a magnetic disk. When the magnetic disk rotates, an air flow generated by the rotation of the magnetic disk causes an air bearing surface (ABS) side of the recording head to ride a particular height above the magnetic disk. The height depends on the shape of the ABS. As the recording head rides on the air bearing, an actuator moves the actuator/suspension arm to position the read element and the write element over selected tracks of the magnetic disk.
- One type of magnetic disk presently used in magnetic disk drives provides for longitudinal recording. A magnetic disk for longitudinal recording includes a magnetic recording layer having an easy axis of magnetization parallel to the substrate. The easy axis of magnetization is the crystalline axis that is aligned along the lowest energy direction for the magnetic moment. Another type of magnetic disk provides for perpendicular recording. A magnetic disk for perpendicular recording includes a magnetic recording layer having an easy axis of magnetization oriented substantially perpendicular to the substrate.
- A perpendicular magnetic disk is generally formed with a soft magnetic underlayer (SUL), an interlayer, a perpendicular magnetic recording layer, and a protective layer or overcoat for protecting the surface of the perpendicular magnetic recording layer, which are formed on a substrate. The soft magnetic underlayer (SUL) serves to concentrate a magnetic flux emitted from a main pole of a write element and to serve as a flux return path back to a return pole of the write element during recording on the magnetic recording layer. The interlayer serves to control the size of magnetic crystal grains and the orientation of the magnetic crystal grains in the magnetic recording layer. The interlayer also serves to magnetically de-couple the SUL and the magnetic recording layer.
- On a longitudinal or perpendicular magnetic disk, the magnetic recording layer is divided into small magnetic regions, each of which is used to encode a single binary unit of information. The magnetic regions include multiple magnetic grains, possibly small in number (10 to 100), which generates a highly localized magnetic field. The write element magnetizes a magnetic region by generating a strong local magnetic field.
- As the areal density of magnetic disks increase, the super-paramagnetic effect causes problems for disk manufacturers. The super-paramagnetic effect occurs when the microscopic magnetic grains on the disk become so tiny that ambient temperature can reverse their magnetic orientations. The result is that the bit is erased and the data is lost.
- One solution to the problems posed by the super-paramagnetic effect is to pattern the magnetic disk (also referred to as bit patterned recording). A patterned disk is created as an ordered array of highly uniform islands, with each island capable of storing an individual bit. A patterned disk may allow ultra-high density recording to be achieved. Because each island represents an individual magnetic domain, the patterned disk is thermally stable and higher densities may be achieved.
- However, the magnetic stability of the islands as well as their switching field distribution may be adversely affected by magnetostatic interaction fields. The adverse effects of magnetostatic interaction fields are a problem especially when the media is patterned with high densities of islands. As the size of the islands decrease with increased density, the width of the write element (i.e., pole tip) also decreases. Smaller pole tips lead to reduced write fields. Thus, the switching field (Hs) of the islands needs to be decreased, which leads to decreased energy barriers against thermal reversal or demagnetization-induced reversal.
- The islands on a perpendicular magnetic disk are patterned as discrete magnetic islands, meaning that there is no magnetic material connecting the islands. Although there is no magnetic material connecting the islands, there is still magnetostatic coupling between the islands. Magnetostatic coupling tends to cause antiparallel (AP) coupling between neighboring islands. As the densities increase and the islands are patterned closer together, the magnetostatic coupling between the islands increases. The increase in magnetostatic coupling can de-stabilize the island magnetization.
- Embodiments of the invention solve the above and other related problems by connecting the islands of a patterned magnetic recording media with an exchange bridge structure formed from magnetic material. Connecting the islands with magnetic material increases exchange coupling between the islands. The exchange coupling tends to cause parallel coupling between neighboring islands, which counteracts or offsets the magnetostatic coupling between the islands. The result is that the islands are more magnetically stable against thermal reversal or demagnetization-induced reversal.
- One embodiment of the invention comprises a method of fabricating a patterned magnetic recording media. One step of the method includes fabricating a perpendicular magnetic recording layer that is patterned into a plurality of discrete magnetic islands. Another step of the method includes fabricating an exchange bridge structure formed from magnetic material that connects the islands of the perpendicular magnetic recording layer. These steps may be performed in either order. In one example, the exchange bridge structure may be fabricated first, with the perpendicular magnetic recording layer patterned on top of the exchange bridge structure. The exchange bridge structure thus connects the bottoms of the islands of the perpendicular magnetic recording layer. In another example, the perpendicular magnetic recording layer may be patterned first, with the exchange bridge structure fabricated on top of the islands of the perpendicular magnetic recording layer. The exchange bridge structure thus connects the tops of the islands of the perpendicular magnetic recording layer. In yet another example, the perpendicular magnetic recording layer may be patterned first, with the exchange bridge structure fabricated between the islands of the perpendicular magnetic recording layer. The exchange bridge structure thus connects the sides of the islands of the perpendicular magnetic recording layer.
- The invention may include other exemplary embodiments described below.
- The same reference number represents the same element or same type of element on all drawings.
-
FIG. 1 illustrates a magnetic disk drive system. -
FIG. 2 is a cross-sectional view of a typical patterned magnetic recording media for perpendicular recording. -
FIG. 3 is a flow chart illustrating a method of fabricating a patterned magnetic recording media in an exemplary embodiment of the invention. -
FIG. 4 is a cross-sectional view of a patterned magnetic recording media with an exchange bridge structure fabricated under islands in an exemplary embodiment of the invention. -
FIG. 5 is a cross-sectional view of a patterned magnetic recording media with an exchange bridge structure fabricated on top of islands in another exemplary embodiment of the invention. -
FIG. 6 is a cross-sectional view of a patterned magnetic recording media with an exchange bridge structure fabricated between islands in another exemplary embodiment of the invention. -
FIG. 7 is a cross-sectional view of a patterned magnetic recording media with an exchange bridge structure only partially filling the spaces between islands in an exemplary embodiment of the invention. -
FIG. 8 is a flow chart illustrating a method of fabricating a patterned magnetic recording media in an exemplary embodiment of the invention. -
FIG. 9 is a cross-sectional view of a patterned magnetic recording media with an SUL deposited in an exemplary embodiment of the invention. -
FIG. 10 is a cross-sectional view of patterned a magnetic recording media with an interlayer deposited in an exemplary embodiment of the invention. -
FIG. 11 is a cross-sectional view of a patterned magnetic recording media with an exchange bridge structure deposited in an exemplary embodiment of the invention. -
FIG. 12 is a cross-sectional view of a patterned magnetic recording media with a perpendicular magnetic recording layer deposited in an exemplary embodiment of the invention. -
FIG. 13 is a cross-sectional view of a patterned magnetic recording media with an etch mask patterned in an exemplary embodiment of the invention. -
FIG. 14 is a cross-sectional view of a patterned magnetic recording media after the etching process in an exemplary embodiment of the invention. -
FIG. 15 is a cross-sectional view of a patterned magnetic recording media with an etch mask removed in an exemplary embodiment of the invention. -
FIG. 16 is a flow chart illustrating another method of fabricating a patterned magnetic recording media in an exemplary embodiment of the invention. -
FIG. 17 is a cross-sectional view of a patterned magnetic recording media with an SUL deposited in an exemplary embodiment of the invention. -
FIG. 18 is a cross-sectional view of a patterned magnetic recording media with an interlayer deposited in an exemplary embodiment of the invention. -
FIG. 19 is a cross-sectional view of a patterned magnetic recording media with a perpendicular magnetic recording layer deposited in an exemplary embodiment of the invention. -
FIG. 20 is a cross-sectional view of a patterned magnetic recording media with an etch mask patterned in an exemplary embodiment of the invention. -
FIG. 21 is a cross-sectional view of a patterned magnetic recording media after an etching process in an exemplary embodiment of the invention. -
FIG. 22 is a cross-sectional view of a patterned magnetic recording media with a refill material deposited in an exemplary embodiment of the invention. -
FIG. 23 is a cross-sectional view of a patterned magnetic recording media with an etch mask removed in an exemplary embodiment of the invention. -
FIG. 24 is a cross-sectional view of a patterned magnetic recording media with an exchange bridge structure deposited in an exemplary embodiment of the invention. -
FIG. 25 is a flow chart illustrating another method of fabricating a patterned magnetic recording media in an exemplary embodiment of the invention. -
FIG. 26 is a cross-sectional view of a patterned magnetic recording media with an SUL deposited in an exemplary embodiment of the invention. -
FIG. 27 is a cross-sectional view of a patterned magnetic recording media with an interlayer deposited in an exemplary embodiment of the invention. -
FIG. 28 is a cross-sectional view of a patterned magnetic recording media with a perpendicular magnetic recording layer deposited in an exemplary embodiment of the invention. -
FIG. 29 is a cross-sectional view of a patterned magnetic recording media with an etch mask patterned in an exemplary embodiment of the invention. -
FIG. 30 is a cross-sectional view of a patterned magnetic recording media after an etching process in an exemplary embodiment of the invention. -
FIG. 31 is a cross-sectional view of a patterned magnetic recording media with an exchange bridge structure deposited in an exemplary embodiment of the invention. -
FIG. 32 is a cross-sectional view of a patterned magnetic recording media with an etch mask removed in an exemplary embodiment of the invention. -
FIG. 33 illustrates a patterned magnetic recording media with refill material deposited before an exchange bridge structure in an exemplary embodiment of the invention. -
FIG. 34 illustrates a patterned magnetic recording media with refill material deposited after an exchange bridge structure in an exemplary embodiment of the invention. -
FIG. 35 illustrates a multi-layer exchange bridge structure in an exemplary embodiment of the invention. -
FIG. 36 is a cross-sectional view of a patterned magnetic recording media with islands fabricated on a SUL in an exemplary embodiment of the invention. -
FIG. 37 is a cross-sectional view of a patterned magnetic recording media with islands fabricated on an exchange control layer in an exemplary embodiment of the invention. -
FIG. 1 illustrates a magneticdisk drive system 100. Magneticdisk drive system 100 includes aspindle 102, amagnetic recording disk 104, amotor controller 106, anactuator 108, an actuator/suspension arm 110, and arecording head 114.Spindle 102 supports and rotatesmagnetic recording disk 104 in the direction indicated by the arrow. A spindle motor (not shown) rotatesspindle 102 according to control signals frommotor controller 106.Recording head 114 is supported by actuator/suspension arm 110. Actuator/suspension arm 110 is connected to actuator 108 that is configured to rotate in order to positionrecording head 114 over a desired track ofmagnetic recording disk 104. Magneticdisk drive system 100 may include other devices, components, or systems not shown inFIG. 1 . For instance, a plurality of magnetic disks, actuators, actuator/suspension arms, and recording heads may be used. - When
magnetic recording disk 104 rotates, an air flow generated by the rotation ofmagnetic disk 104 causes an air bearing surface (ABS) ofrecording head 114 to ride on a cushion of air at a particular height abovemagnetic disk 104. The height depends on the shape of the ABS. Asrecording head 114 rides on the cushion of air,actuator 108 moves actuator/suspension arm 110 to position a read element (not shown) and a write element (not shown) inrecording head 114 over selected tracks ofmagnetic recording disk 104. -
FIG. 2 is a cross-sectional view of a typical patternedmagnetic recording media 200 for perpendicular recording, such asmagnetic disk 104. Patternedmagnetic recording media 200 includes a soft magnetic underlayer (SUL) 202, aninterlayer 204, and a perpendicularmagnetic recording layer 206 formed on asubstrate 201. Patternedmagnetic recording media 200 may include other layers not shown inFIG. 2 for the sake of brevity, such as one or more protective layers or an overcoat formed on perpendicularmagnetic recording layer 206, one or more seed layers, one or more layers betweenSUL 202 andinterlayer 204, or one or more layers betweeninterlayer 204 andmagnetic recording layer 206, etc. - Perpendicular
magnetic recording layer 206 is formed from one or more materials that have an easy axis of magnetization oriented substantially perpendicular tosubstrate 201. Perpendicularmagnetic recording layer 206 may be formed from a Co-alloy and may include elements such as Cr and Pt as well as oxides such as SiO2.Interlayer 204 controls the orientation and grain diameter of the perpendicularmagnetic recording layer 206.SUL 202 acts in conjunction with the write element to increase the perpendicular field magnitude and improve the field gradient generated by a recording head passing overmagnetic recording media 200.SUL 202 may be a single layer structure formed from materials such as CoFeTaZr.SUL 202 may alternatively have an antiparallel (AP) structure, where two SULs are antiparallel coupled across an AP coupling layer. - Perpendicular
magnetic recording layer 206 is patterned into a plurality of discretemagnetic islands 208.Islands 208 are separated from one another byrefill material 210, which is some type of non-magnetic material such as alumina. Although there is no magneticmaterial connecting islands 208, there is still magnetostatic coupling betweenislands 208. Magnetostatic coupling tends to cause AP coupling between neighboringislands 208. As densities increase andislands 208 are patterned closer together, the magnetostatic coupling betweenislands 208 increases. The increase in magnetostatic coupling leads to magnetic instability inislands 208. Improved patterned magnetic recording media and associated methods of fabrication are described below to overcome the problems of magnetostatic coupling. -
FIGS. 3-37 and the following description depict specific exemplary embodiments of the invention to teach those skilled in the art how to make and use the invention. For the purpose of teaching inventive principles, some conventional aspects of the invention have been simplified or omitted. Those skilled in the art will appreciate variations from these embodiments that fall within the scope of the invention. Those skilled in the art will appreciate that the features described below can be combined in various ways to form multiple variations of the invention. As a result, the invention is not limited to the specific embodiments described below, but only by the claims and their equivalents. - In the following embodiments of patterned magnetic recording media, a soft magnetic underlayer (SUL) is described as one of the layers used to form the media, as that is common in present technology. However, the patterned magnetic recording media in the following embodiments may include a SUL as described below, may include a substantially thinner SUL or a SUL with significantly less permeability than is presently implemented, or no SUL.
-
FIG. 3 is a flow chart illustrating amethod 300 of fabricating a patterned magnetic recording media in an exemplary embodiment of the invention.Method 300 may be used to fabricatemagnetic recording disk 104 as shown inFIG. 1 . - Step 302 comprises fabricating a soft magnetic underlayer (SUL) on a substrate. Step 304 comprises fabricating an interlayer on the SUL. Step 306 comprises fabricating a perpendicular magnetic recording layer. The perpendicular magnetic recording layer may be fabricated in a variety of ways. In one example, the material for the layer is deposited, and then is patterned. The perpendicular magnetic recording layer may be patterned by first patterning a master tool using electron beam lithography. An etch layer may then be deposited on the perpendicular magnetic recording layer, which is imprinted with the master tool. An etching process, such as ion beam etching, may then be performed to remove the portions of the perpendicular magnetic recording layer that are exposed by the etch layer. This patterns the perpendicular magnetic recording layer into a plurality of discrete magnetic islands.
- In another example, additional substrate material may be deposited before the perpendicular magnetic recording layer. An etch layer may then be deposited on the substrate material, which is imprinted with the master tool. An etching process may then be performed to remove the portions of the substrate material that are exposed by the etch layer. This patterns the substrate material into a plurality of discrete islands. The perpendicular magnetic recording layer is then deposited on top of the patterned substrate material. Those skilled in the art will appreciate that there may be additional ways of patterning a perpendicular magnetic recording layer.
- Step 308 comprises fabricating an exchange bridge structure. An exchange bridge structure comprises any structure that connects neighboring islands of a patterned perpendicular magnetic recording layer with magnetic material. The exchange bridge structure increases exchange coupling between the islands. The exchange coupling tends to cause the magnetizations of neighboring islands to align in parallel, which counteracts or offsets the magnetostatic coupling between the islands. As a result, the islands are more magnetically stable against thermal reversal or demagnetization-induced reversal.
- The steps of
method 300 are not provided in any particular order. As a result, the exchange bridge structure may be fabricated before the perpendicular magnetic recording layer, or after the perpendicular magnetic recording layer. Thus, the exchange bridge structure may be fabricated underneath the perpendicular magnetic recording layer in order to connect the bottoms of the islands. In one alternative, the exchange bridge structure may be fabricated on top of the perpendicular magnetic recording layer in order to connect the tops of the islands. In yet another alternative, the exchange bridge structure may be fabricated in between the islands. Examples of these structures are shown inFIGS. 4-6 . -
FIG. 4 is a cross-sectional view of a patternedmagnetic recording media 400 with an exchange bridge structure fabricated under the islands in an exemplary embodiment of the invention. Patternedmagnetic recording media 400 includes a soft magnetic underlayer (SUL) 402 formed on asubstrate 401, with aninterlayer 404 formed onSUL 402. Patternedmagnetic recording media 400 further includes anexchange bridge structure 406 formed oninterlayer 404. Patternedmagnetic recording media 400 further includes a perpendicularmagnetic recording layer 408 formed onexchange bridge structure 406. Patternedmagnetic recording media 400 may include other layers not shown inFIG. 4 for the sake of brevity, such as one or more protective layers formed on perpendicularmagnetic recording layer 408, one or more seed layers, one or more layers betweenSUL 402 andinterlayer 404, etc. - Patterned
magnetic recording layer 408 is patterned into a plurality ofislands 410. Becauseislands 410 are formed onexchange bridge structure 406, the bottom ofislands 410 are connected to one another with magnetic material.Exchange bridge structure 406 provides exchange coupling betweenislands 410, which counteracts the demagnetization fields from neighboringislands 410. The interaction field can decrease or increase the switching field of anisland 410 depending on relative orientation.Exchange bridge structure 406 filters out the switching field fluctuations that are due to magnetostatic coupling. Further,exchange bridge structure 406 connectsislands 410 with different intrinsic switching fields (e.g., due to anisotropy fluctuations, moment fluctuations, defects, etc), which helps to smooth these fluctuations.Exchange bridge structure 406 may also allow the use of an increased anisotropy ofislands 410 without raising the write field requirement. -
FIG. 5 is a cross-sectional view of a patternedmagnetic recording media 500 with an exchange bridge structure fabricated on top of the islands in another exemplary embodiment of the invention. Patternedmagnetic recording media 500 includes aSUL 502 formed on asubstrate 501, with aninterlayer 504 formed onSUL 502. Patternedmagnetic recording media 500 further includes a perpendicular magnetic recording layer 506 formed oninterlayer 504. Patterned magnetic recording layer 506 is patterned into a plurality ofislands 508.Refill material 510 is deposited betweenislands 508 in order to create a planarized surface. Patternedmagnetic recording media 500 further includes anexchange bridge structure 512 formed on patterned magnetic recording layer 506. Becauseexchange bridge structure 406 is formed on patterned magnetic recording layer 506, the top ofislands 508 are connected to one another with magnetic material. -
FIG. 6 is a cross-sectional view of a patternedmagnetic recording media 600 with an exchange bridge structure fabricated between the islands in another exemplary embodiment of the invention. Patternedmagnetic recording media 600 includes aSUL 602 formed on asubstrate 601, with aninterlayer 604 formed onSUL 602. Patternedmagnetic recording media 600 further includes a perpendicularmagnetic recording layer 606 formed oninterlayer 604. Patternedmagnetic recording layer 606 is patterned into a plurality ofislands 608. Patternedmagnetic recording media 600 further includes anexchange bridge structure 610 formed betweenislands 608 of patternedmagnetic recording layer 606. - Patterned
magnetic recording media 600 as illustrated inFIG. 6 showsexchange bridge structure 610 completely filling the spaces betweenislands 608. However,exchange bridge structure 610 may only partially fill the spaces betweenislands 608 in other embodiments.FIG. 7 is a cross-sectional view of a patternedmagnetic recording media 600 withexchange bridge structure 610 only partially filling the spaces betweenislands 608. Anon-magnetic material 702 is deposited betweenislands 608, andexchange bridge structure 610 is deposited on top ofnon-magnetic material 702. In other embodiments,exchange bridge structure 610 may be deposited first withnon-magnetic material 702 deposited on top ofexchange bridge structure 610. - Patterned magnetic recording media as described herein may be fabricated in a variety of ways. Three examples are shown in
FIGS. 8-34 , but those skilled in the art will appreciate that many variations of these fabrication methods may be employed. -
FIG. 8 is a flow chart illustrating amethod 800 of fabricating a patterned magnetic recording media in an exemplary embodiment of the invention.FIGS. 9-15 illustrate a patternedmagnetic recording media 900 being fabricated according tomethod 800. - Step 802 comprises depositing a
SUL 902 on a substrate 901 (seeFIG. 9 ).FIG. 9 is a cross-sectional view of patternedmagnetic recording media 900 withSUL 902 deposited according tostep 802. As previously mentioned,SUL 902 may comprise a single layer structure or an AP coupled structure. Step 804 comprises depositing aninterlayer 1002 on SUL 902 (seeFIG. 10 ).FIG. 10 is a cross-sectional view of patternedmagnetic recording media 900 withinterlayer 1002 deposited according tostep 804. The material forinterlayer 1002 may comprise NiCr, NiWCr, or a similar alloy. - Step 806 comprises depositing an
exchange bridge structure 1102 on interlayer 1002 (seeFIG. 11 ).FIG. 11 is a cross-sectional view of patternedmagnetic recording media 900 withexchange bridge structure 1102 deposited according tostep 806.Exchange bridge structure 1102 may be deposited in a variety of ways. In one example,exchange bridge structure 1102 may be deposited by depositing an exchange bridge layer of magnetic material, such as Permalloy, Co-alloys, or soft ferromagnetic materials. In another example,exchange bridge structure 1102 may be deposited by depositing an exchange bridge layer of magnetic material, and then depositing an exchange control layer of non-magnetic material, such as Ru, Pt, C, Pd, Si, SiOx, SiNx, Cu, Ta, Au, Ag, Mg, MgOx, Ti, TiOx, Cr, etc, or of attenuated magnetic materials by forming mixtures of aforementioned materials with addition of one or more of the magnetic elements such as Co, Fe, and Ni. The exchange control layer controls the amount of exchange coupling between subsequently-formed islands of a perpendicular magnetic recording layer and the exchange bridge layer. - Step 808 comprises depositing a perpendicular
magnetic recording layer 1202 on exchange bridge structure 1102 (seeFIG. 12 ).FIG. 12 is a cross-sectional view of patternedmagnetic recording media 900 with perpendicularmagnetic recording layer 1202 deposited according tostep 808. The material for the perpendicularmagnetic recording layer 1202 may comprise CoPtCr—SiOx or other similar materials or multilayers of Co, Fe, Pt, Pd, or similar materials. - Step 810 comprises patterning an
etch mask 1302 on perpendicular magnetic recording layer 1202 (seeFIG. 13 ).FIG. 13 is a cross-sectional view of patternedmagnetic recording media 900 withetch mask 1302 patterned according tostep 810. Step 812 comprises performing an etching process, such as ion beam etching, to remove the portions of perpendicularmagnetic recording layer 1202 exposed by etch mask 1302 (seeFIG. 14 ).FIG. 14 is a cross-sectional view of patternedmagnetic recording media 900 after the etching process according tostep 812. The etching process ofstep 812 defines discretemagnetic islands 1402 out of perpendicularmagnetic recording layer 1202. - Step 814 comprises removing etch mask 1302 (see
FIG. 15 ).FIG. 15 is a cross-sectional view of patternedmagnetic recording media 900 withetch mask 1302 removed according tostep 814. At this point, refill material may be deposited to fill in the spaces betweenislands 1402, and the top surface planarized to create a flat surface for the recording head to fly over. An overcoat layer may then be deposited to protectislands 1402.Method 800 fabricates a patternedmagnetic recording media 900 much as is illustrated inFIG. 4 , withexchange bridge structure 1102 fabricated underneathislands 1402.Exchange bridge structure 1102 thus creates exchange coupling betweenislands 1402. - One variation of
method 800 is to removeinterlayer 1002, and allowSUL 902 to act as the exchange bridge structure. TheSUL 902 may then serve as the magnetic layer that creates exchange coupling betweenislands 1402. These embodiments are described inFIGS. 36-37 . -
FIG. 16 is a flow chart illustrating anothermethod 1600 of fabricating a patterned magnetic recording media in an exemplary embodiment of the invention.FIGS. 17-24 illustrate a patternedmagnetic recording media 1700 being fabricated according tomethod 1600. -
Step 1602 comprises depositing aSUL 1702 on a substrate 1701 (seeFIG. 17 ).FIG. 17 is a cross-sectional view of patternedmagnetic recording media 1700 withSUL 1702 deposited according tostep 1602.Step 1604 comprises depositing aninterlayer 1802 on SUL 1702 (seeFIG. 18 ).FIG. 18 is a cross-sectional view of patternedmagnetic recording media 1700 withinterlayer 1802 deposited according tostep 1604. -
Step 1606 comprises depositing a perpendicularmagnetic recording layer 1902 on interlayer 1802 (seeFIG. 19 ).FIG. 19 is a cross-sectional view of patternedmagnetic recording media 1700 with perpendicularmagnetic recording layer 1902 deposited according tostep 1606.Step 1608 comprises patterning anetch mask 2002 on perpendicular magnetic recording layer 1902 (seeFIG. 20 ).FIG. 20 is a cross-sectional view of patternedmagnetic recording media 1700 withetch mask 2002 patterned according tostep 1608.Step 1610 comprises performing an etching process to remove the portions of perpendicularmagnetic recording layer 1902 exposed by etch mask 2002 (seeFIG. 21 ).FIG. 21 is a cross-sectional view of patternedmagnetic recording media 1700 after the etching process according tostep 1610. The etching process ofstep 1610 defines discretemagnetic islands 2102 out of perpendicularmagnetic recording layer 1902.Step 1612 comprises depositing refill material 2202 (seeFIG. 22 ).FIG. 22 is a cross-sectional view of patternedmagnetic recording media 1700 withrefill material 2202 deposited according tostep 1612.Refill material 2202 is used to fill the spaces betweenislands 2102.Refill material 2202 may comprise alumina or some other non-magnetic material.Step 1614 comprises removing etch mask 2002 (seeFIG. 23 ).FIG. 23 is a cross-sectional view of patternedmagnetic recording media 1700 withetch mask 2002 removed according tostep 1614. At this point, the top surface of patternedmagnetic recording media 1700 may be planarized, or may be left slightly uneven from the previous processes. -
Step 1616 comprises depositing anexchange bridge structure 2402 on the top surface of patterned magnetic recording media 1700 (seeFIG. 24 ).FIG. 24 is a cross-sectional view of patternedmagnetic recording media 1700 withexchange bridge structure 2402 deposited according tostep 1616.Exchange bridge structure 2402 is in contact with the top surfaces ofislands 2102. An overcoat layer may then be deposited to protectexchange bridge structure 2402. - In the embodiment described in
FIG. 16 , perpendicularmagnetic recording layer 1902 was etched to formislands 2102. However, those skilled in the art will appreciate that there are different ways of formingislands 2102. For example, substrate material may be deposited in the place of perpendicularmagnetic recording layer 1902, and then patterned as described above. A perpendicular magnetic recording layer may then be deposited on top of the islands formed out of the substrate material. After the perpendicular magnetic recording layer and therefill material 2202 is deposited,exchange bridge structure 2402 may then be deposited. -
FIG. 25 is a flow chart illustrating anothermethod 2500 of fabricating a patterned magnetic recording media in an exemplary embodiment of the invention.FIGS. 26-34 illustrate a patternedmagnetic recording media 2600 being fabricated according tomethod 2500. -
Step 2502 comprises depositing aSUL 2602 on a substrate 2601 (seeFIG. 26 ).FIG. 26 is a cross-sectional view of patternedmagnetic recording media 2600 withSUL 2602 deposited according tostep 2502.Step 2504 comprises depositing aninterlayer 2702 on SUL 2602 (seeFIG. 27 ).FIG. 27 is a cross-sectional view of patternedmagnetic recording media 2600 withinterlayer 2702 deposited according tostep 2504. -
Step 2506 comprises depositing a perpendicularmagnetic recording layer 2802 on interlayer 2702 (seeFIG. 28 ).FIG. 28 is a cross-sectional view of patternedmagnetic recording media 2600 with perpendicularmagnetic recording layer 2802 deposited according tostep 2506.Step 2508 comprises patterning anetch mask 2902 on perpendicular magnetic recording layer 2802 (seeFIG. 29 ).FIG. 29 is a cross-sectional view of patternedmagnetic recording media 2600 withetch mask 2902 patterned according tostep 2508.Step 2510 comprises performing an etching process to remove the portions of perpendicularmagnetic recording layer 2802 exposed by etch mask 2902 (seeFIG. 30 ).FIG. 30 is a cross-sectional view of patternedmagnetic recording media 2600 after the etching process according tostep 2510. The etching process ofstep 2510 defines discretemagnetic islands 3002 out of perpendicularmagnetic recording layer 2802. -
Step 2512 comprises depositing an exchange bridge structure 3102 (seeFIG. 31 ).FIG. 31 is a cross-sectional view of patternedmagnetic recording media 2600 withexchange bridge structure 3102 deposited according tostep 2512.Exchange bridge structure 3102 is deposited betweenislands 3002 and contacts the sides ofislands 3002. -
Step 2514 comprises removing etch mask 2902 (seeFIG. 32 ).FIG. 32 is a cross-sectional view of patternedmagnetic recording media 2600 withetch mask 2902 removed according tostep 2514. At this point, the top surface of patternedmagnetic recording media 2600 may be planarized, or may be left slightly uneven from the previous processes. An overcoat layer may then be deposited to protectislands 3002 andexchange bridge structure 3102. -
FIG. 32 illustrates theexchange bridge structure 3102 having a thickness equal toislands 3002. If exchange coupling betweenislands 3002 is too strong to allowislands 3002 to switch independently from one another, then a composite material forexchange bridge structure 3102 may be used. For instance, there may be microscopic regions of magnetic material interspersed among regions of non-magnetic material. Strong exchange coupling may alternatively be reduced by adjusting the thickness ofexchange bridge structure 3102 as shown inFIGS. 33-34 . The spaces betweenislands 3002 may be filled with refill material (i.e., a non-magnetic material) andexchange bridge structure 3102 to adjust the thickness ofexchange bridge structure 3102.FIG. 33 illustrates patternedmagnetic recording media 2600 with refill material 3302 deposited beforeexchange bridge structure 3102. In this example, theexchange bridge structure 3102 is thinner than inFIG. 32 and contacts the top portions ofislands 3002.FIG. 34 illustrates patternedmagnetic recording media 2600 withrefill material 3402 deposited afterexchange bridge structure 3102. In this example, theexchange bridge structure 3102 is again thinner than inFIG. 32 and contacts the bottom portions ofislands 3002. - The exchange bridge structure in the above embodiments may be fabricated in a variety of ways. In one example, the exchange bridge structure may be fabricated as a layer of magnetic material, such as Permalloy, Co-alloys, or soft ferromagnetic materials. In another example, the exchange bridge structure may be a multi-layer structure of non-magnetic material and magnetic material. In another example, the exchange bridge may include attenuated magnetic materials formed from mixtures of non-magnetic material, including Ru, Pt, C, Pd, Si, SiOx, SiNx, Cu, Ta, Au, Ag, Mg, MgOx, Ti, TiOx, Cr, etc, and one or more of the magnetic elements such as Co, Fe, and Ni.
-
FIG. 35 illustrates a multi-layerexchange bridge structure 3500 in an exemplary embodiment of the invention. Multi-layerexchange bridge structure 3500 includes anexchange bridge layer 3502 of magnetic material, such as Permalloy, Co-alloys, or soft ferromagnetic materials. The thickness of theexchange bridge layer 3502, in one example, is between about 0.3-12 nanometers, depending on the material used and what type of exchange control layer, if any, is used. A high thickness of theexchange bridge layer 3502 is achieved with attenuated magnetic materials where magnetic materials are attenuated by the addition of non-magnetic materials including Ru, Pt, C, Pd, Si, SiOx, SiNx, Cu, Ta, Au, Ag, Mg, MgOx, Ti, TiOx, Cr, etc. Thinner thickness of theexchange bridge layer 3502 is achieved by adding less, if any, of the non-magnetic materials to the magnetic materials. - Multi-layer
exchange bridge structure 3500 further includes anexchange control layer 3504 of non-magnetic material, such as Ru, Pt, C, Pd, Si, SiOx, SiNx, Cu, Ta, Au, Ag, Mg, MgOx, Ti, TiOx, Cr, etc, or of attenuated magnetic materials by forming mixtures of aforementioned materials with addition of one or more of the magnetic elements such as Co, Fe, and Ni.Islands 3506 of a perpendicular magnetic recording layer are illustrated as being patterned on top ofexchange control layer 3504.Exchange control layer 3504 controls the amount of exchange coupling betweenislands 3506 of a perpendicular magnetic recording layer andexchange bridge layer 3502.Exchange control layer 3504 is sufficiently thin to allow some exchange coupling to be mediated. An exemplary thickness ofexchange control layer 3504 is between about 0.5-2 nanometers, depending on the material used. A low thickness ofexchange control layer 3504 may be achieved with non-magnetic materials or highly-attenuated magnetic materials with small addition of the magnetic elements to the non-magnetic materials. Larger thickness ofexchange control layer 3504 may be achieved by adding more of the magnetic elements to the non-magnetic materials. - In
FIG. 35 ,exchange control layer 3504 is illustrated as deposited on top ofexchange bridge layer 3502. Such a configuration may be used in the method ofFIG. 8 .Exchange control layer 3504 is used to separateexchange bridge layer 3502 from theislands 3506 of the perpendicular magnetic recording layer. Thus,exchange bridge layer 3502 may be deposited on top ofexchange control layer 3504 in other embodiments ifexchange bridge structure 3500 is fabricated on top of the islands. - As previously mentioned, the SUL may act as the exchange bridge layer is some embodiments, which is illustrated in
FIGS. 36-37 .FIG. 36 is a cross-sectional view of a patternedmagnetic recording media 3600 with islands fabricated on a SUL in an exemplary embodiment of the invention. Patternedmagnetic recording media 3600 includes a soft magnetic underlayer (SUL) 3602 formed on asubstrate 3601, with a perpendicularmagnetic recording layer 3608 formed onSUL 3602. Patternedmagnetic recording layer 3608 is patterned into a plurality ofislands 3610. Becauseislands 3610 are formed onSUL 3602, the bottoms ofislands 3610 are connected to one another with magnetic material.SUL 3602 in this embodiment acts as an exchange bridge layer to provide exchange coupling betweenislands 3610. - In order to avoid excessive coupling between the
islands 3610 in this embodiment, athinner SUL 3602 or aSUL 3602 with a lower permeability is used. A typical SUL is between about 20-50 nanometers thick. A thinner or lower permeability SUL may be used when a write element, which is used to write to the media, is less reliant on flux conductance through the SUL. An example of a thinner SUL is about 2-5 nanometers. When athinner SUL 3602 or aSUL 3602 having a lower permeability is used in the media, theislands 3610 may be formed directly onSUL 3602, which then acts as the exchange bridge layer. - If a thicker SUL is used, then an exchange control layer may be implemented between the islands and the SUL.
FIG. 37 is a cross-sectional view of a patternedmagnetic recording media 3700 with islands fabricated on an exchange control layer in an exemplary embodiment of the invention. Patternedmagnetic recording media 3700 includes a soft magnetic underlayer (SUL) 3702 formed on asubstrate 3701, with anexchange control layer 3706 formed onSUL 3702. Patternedmagnetic recording media 3700 also includes a perpendicularmagnetic recording layer 3708 formed onexchange control layer 3706. Patternedmagnetic recording layer 3708 is patterned into a plurality ofislands 3710. Again,SUL 3702 in this embodiment acts as an exchange bridge layer to provide exchange coupling betweenislands 3710. -
Exchange control layer 3706 is formed from non-magnetic material, such as Ru, Pt, C, Pd, Si, SiOx, SiNx, Cu, Ta, Au, Ag, Mg, MgOx, Ti, TiOx, Cr, etc, or of attenuated magnetic materials by forming mixtures of aforementioned materials with addition of one or more of the magnetic elements such as Co, Fe, and Ni.Exchange control layer 3706 controls the amount of exchange coupling betweenislands 3710 andSUL 3702.Exchange control layer 3706 is sufficiently thin to allow some exchange coupling to be mediated. An exemplary thickness ofexchange control layer 3706 is between about 0.5-2 nanometers, depending on the material used. A low thickness ofexchange control layer 3706 may be achieved with non-magnetic materials or highly-attenuated magnetic materials with small addition of the magnetic elements to the non-magnetic materials. Larger thickness ofexchange control layer 3706 may be achieved by adding more of the magnetic elements to the non-magnetic materials. - Although specific embodiments were described herein, the scope of the invention is not limited to those specific embodiments. The scope of the invention is defined by the following claims and any equivalents thereof.
Claims (17)