US20100320630A1 - Method For Producing A Sintered Body - Google Patents
Method For Producing A Sintered Body Download PDFInfo
- Publication number
- US20100320630A1 US20100320630A1 US12/870,575 US87057510A US2010320630A1 US 20100320630 A1 US20100320630 A1 US 20100320630A1 US 87057510 A US87057510 A US 87057510A US 2010320630 A1 US2010320630 A1 US 2010320630A1
- Authority
- US
- United States
- Prior art keywords
- layer
- particles
- mould
- applying
- sintered body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
This invention relates to a method for forming a three dimensional sintered body comprising the steps of a) providing a basic mould having a configuration adapted to the sintered body that is to be produced, b) treating the surface of the basic mould to facilitate application of a first surface layer of the sintered body, c) applying powder particles onto the basic mould, to form said first surface layer, d) applying at least one more layer on top of said first surface layer, e) heat treating the basic mould and the particles to form a sintered body, wherein step b) is performed by providing an adhering layer to the basic mould arranged to adhere the particles of at least a portion of the surface layer.
Description
- The present invention relates to a method for forming a three dimensional sintered body comprising the steps of:
- a) providing a basic mould having a configuration adapted to the sintering body that is to be produced,
b) treating the surface of the basic mould to facilitate application of a first surface layer of the sintered body,
c) applying powder particles onto the basic mould, to form said first surface layer,
d) applying at least one more layer on top of said first surface layer,
e) heat treating the basic mould and the particles to form a sintered body. - Production of three dimensional sintered bodies is traditionally a complex and costly process, e.g. porous bodies. Porous bodies are used for many different technical applications in filtration of gases and liquids, fluidising processes, separation and catalysing. One important application is in filtration of pulps. The shape of the porous body or mould is in the latter case quite complicated. However, the shape of filters for gases and liquids is commonly quite simple due to the inherent manufacturing problems in producing porous bodies having a more complex configuration. Furthermore the production series may be of relative small size, why a low production cost of the mould is an advantage, as also fast and cost effective way of manufacturing it. Another aspect is the internal structure of such products, e.g. drainage properties.
- There are some key properties of a filter that have large importance on the requested functionality at the filtering operation. Two of these properties, i.e. high yield at the filtering operation and low pressure drop over the filter, are very often contradictory. High yield of the substance to be taken away by the filtering operation e.g. fibres in a pulp is achieved by using a filter with a fine porous structure. A fine porous structure means in this case that the channels formed by the pores are small in size. However, the pressure drop over the filter increases with decreasing size of the pore channels. On the other hand as mentioned above, a fine structure is often desired to obtain high yield and some times also to facilitate providing a body having a smooth surface structure.
- It is well known that a fine pore structure can be achieved by manufacturing the porous body from fine particles or fibres and obviously a coarse pore structure by using coarse particles or fibres in the manufacturing process of the filter.
- One rather recent method for producing three-dimensional objects, e.g. to provide filters with a graduated structure, is the WPS-process (Wet Powder Spraying Process). In this process a mixture containing sinter able powder is sprayed on to a supporting body, where after the binding agent of the mixture is decomposed in a first step and the actual sintering is performed in a second step. In US 2004/0050773 there is presented such a process intended for the production of at least two layers of different pore size.
- From US 2002/0195188 there is known a similar but somewhat modified process wherein the mixture contains pore forming material containing particles with predetermined size or size distribution. Further, there is also known a process wherein centrifugal forces are used to obtain a graduated structure of a three-dimensional sintered body. As is evident, all of these processes need sophisticated arrangements/apparatuses to achieve a desired result, which leads to a relatively high cost of the final product.
- From EP0559490 and EP0559491 there is known a further process for producing a three dimensional body, e.g. a pulp moulding die, preferably comprising glass beads to form a porous structure is presented, which also mentions that sintered particles can be used. The production technology described therein is however complicated.
- It is an object of the invention to provide a method for forming a three dimensional sintered body comprising the steps of:
- a) providing a basic mould having a configuration adapted to the sintering body that is to be produced,
b) treating the surface of the basic mould to facilitate application of a first surface layer of the sintered body,
c) applying powder particles onto the basic mould, to form said first surface layer,
d) applying at least one more layer on top of said first surface layer,
e) heat treating the basic mould and the particles to form a sintered body wherein step b) is performed by providing an adhering layer to the basic mould arranged to adhere the particles of the surface layer. - Thanks to the invention there is provided a method that substantially improves the efficiency for producing a three-dimensional sintered body. Further the present invention provides for the manufacture of a filter having a thin surface layer with fine pore structure and an inner core with coarse pore structure. Hereby is a filter obtained with efficient filtering capability and excellent drainage properties, primarily low pressure-drop during the filtering operations.
- According to further aspects of the invention:
-
- said adhering layer, is applied as a liquid, which preferably is applied to the basic mould by means of spraying, which provides for a surprisingly efficient process of performing a method according to the invention.
- said liquid substantially comprises water, which preferably is applied to the basic mould by means of spraying, which provides for an especially cost-effective and environmental friendly manner of performing a method according to the invention, and which not least advantageous provides a method where the binder may easily be removed (evaporation) without leaving any rest products.
- at least a portion of said adhering layer is arranged to melt by means of heat supplied from said powder particles, which provides for a surprisingly efficient process of performing a method according to the invention.
- prior to step b) the basic mould has been treated to obtain a temperature of between 0° C.-−100° C., preferably in the range of −10° C.-−30° C., which is an easy way of providing beneficial conditions for performing a method according to the invention.
- step c) is performed in a room having a temperature above +10° C. and below 60° C., preferably between 15-35° C., and more preferred at room temperature between 18-28° C., which for beneficial conditions for performing a method according to the invention and also for individuals involved in it.
- at least one layer and/or at least one portion comprises particles of different size than the particles in other parts of said body, wherein preferably at least one layer and/or one portion comprises particles of larger size than the particles in said surface layer, which provides for en efficient manner of tailoring different properties of a porous body.
- at least one further layer is applied in the same manner on top of said surface layer, which provides for the advantage that more exact tailoring may be achieved concerning properties of a porous body.
- at least one layer comprises powder particles.
- the basic mould is substantially filled prior to step e), which provides an efficient manner of producing a voluminous body, e.g. needing a flat supporting surface.
- at last one channel is provided in the body by applying a solid device that is removed from the body after step d), which is an efficient manner of producing bodies provided with customised properties concerning drainage, etc.
- step b) is also applied to surfaces of the basic mould adapted for substantially non-permeable areas of the body, which for some products provides a very cost-efficient manner of production.
- Further aspects and advantages of the method may be found in the description.
- In the following the invention will be described in relation to the appended figures, wherein:
-
FIG. 1 shows a cross sectional side view of the basic mould according to one embodiment of the invention, -
FIG. 2 shows a basic mould ofFIG. 1 in a subsequent step for the production of a product according to the invention, -
FIG. 3 shows a subsequent step in relation toFIG. 2 , -
FIG. 4 shows a subsequent step in relation toFIG. 3 , -
FIG. 5 shows a subsequent step in relation toFIG. 4 , -
FIG. 6 shows a subsequent step in relation toFIG. 5 , -
FIG. 6 a shows a modified manner of performing the step shown inFIG. 6 , -
FIG. 7 shows the final product, -
FIG. 8 shows a different kind of product produced along the same lines as described in relation toFIGS. 1-6 , -
FIG. 9 is a cross sectional zooming of the embodiment shown inFIG. 8 showing the internal porous structure, -
FIG. 10 shows an exemplary different kind of body produced in a similar mould as shown inFIGS. 1-6 , -
FIG. 11 is a cross sectional zooming of the embodiment shown inFIG. 10 , -
FIG. 12 shows an exemplary further embodiment of performing the method according to the invention, -
FIG. 13 is a subsequent step in relation toFIG. 12 , -
FIG. 14 shows a cross sectional view of a male part and complementary female part of another kind of porous body produced according to the invention, i.e. a pulp mould, -
FIG. 15 shows the same asFIG. 14 but in an a moulding position, and -
FIG. 16 shows a zooming of a part ofFIG. 15 , - In
FIG. 1 there is shown abasic mould half 400 for a producing a product 100 (seeFIG. 7 ) according to the invention, e.g. a filter body. Thebasic mould 400 comprises abody 401, having abottom wall 405,side wall 404 and atop surface 403, into which formedsurfaces - In the
basic mould 400 there is formed amoulding face 402 that corresponds to thesurface layer 130 of theproduct 100 to be sintered and alsonon-forming surfaces 406. Themoulding face 402 may be produced in many different ways known in the art, e.g. by the use of conventional machining techniques. For some products a very smooth surface is desired and then the finish of the surface of themoulding face 402 should preferably be of high quality. - However, the precision, i.e. exact measurement, must not always be extremely high, since an advantage with the invention is that high quality properties of some products may be achieved even if moderate tolerances are used for the configuration of the basic mould, e.g. filter bodies where e.g. drainage properties may be more or less independent of the surface or pulp moulds where heat pressing may improve the surfaces of the moulded object pulp moulds. For moulded pulp objects the first heat pressing action (when producing a moulded pulp product according to a preferred mode, see
FIGS. 8 and 9 ), creates a kind of impulse impact within the fibre material trapped in the void 300 between the twomould halves - In
FIGS. 2-6 the consecutive production of a product according to the invention is shown. - In
FIG. 2 it is shown that thebasic mould 400 is applied with a thin layer ofice 604. This is preferably achieved by first having the basic mould 4 in a freezer 5 (as schematically indicated inFIG. 1 ), e.g. at −18° C., to reduce the temperature of thebasic mould 400 to well below the freezing point of water. Once the desired temperature of thebasic mould 400 is obtained the production of the actual pulp mould may be started. Thebasic mould 400 is then taken out of thefreezer 5 and may thereafter be worked with. This may for instance be achieved by having thefreezer 5 positioned within the working area having room temperature, i.e. allowing workers having a comfortable temperature, e.g. ambient temperature of about 18-28° C. - Thereafter, as shown in
FIG. 2 , a thin layer of thewater 604 is sprayed onto thebasic mould 400. The water will freeze and form athin ice layer 604 on thebasic mould 400. Thewater 601 is (as shown schematically) is supplied to a spray means 600 having aspray head 602 provided with means for producing finely divideddroplets 603, e.g. a kind of shower head arranged with numerous small outlets. Thespray device 600 is directed to cover the formedsurface 402 of themould 400. Hence a thin layer ofice 604 will be formed on top of theproduct forming surface 402 of thebasic mould 400. - In the next step, as shown in
FIG. 3 , thefirst layer 130 ofparticles 131 will be formed. This is achieved by applying thefine particles 131, having room temperature into thebasic mould 400 onto the formed surfaces 402. Thereafter thebasic mould 400 is moved around to allow the excessive amount ofparticles 131 to come into contact with each part of thesurface 402 of themould 400, such that an even,thin layer 130 is applied. The mechanism behind this efficient method is that the warm particles 131 (having room temperature), coming in contact with thelayer 604, will melt some ice during its initial contact and thereafter quickly adopt the temperature of thebasic mould 400. The melted ice will then re-freeze and binds theparticles 131 to thethin ice layer 604. Accordingly this is a very efficient way of establishing an evenfirst layer 130 ofparticles 131 in thebasic mould 400. (It is evident for the skilled person that this principle may also be used in connection with other liquids having formed a thin layer in thebasic mould 400, e.g. wax but then of course a higher temperature of the particles may be needed to assure sufficient adhering). - Thereafter the
mould 400 may again be put into the freezer 5 (if necessary to re-cool it) and subsequently taken out thereof to apply a further layer ofice 605, as shown inFIG. 4 . Accordingly this second layer ofice 605 is applied in exactly the same way as described in connection withFIG. 2 , but on top on thesurface layer 130 offine particles 131. Once the desiredice layer 605 has established the procedure of applyingfine particles 121 is also repeated. Accordingly an excessive amount offurther particles 121 forming asecond layer 120 on top of thefirst layer 130 is supplied. As can be seen inFIG. 5 thebasic mould 400 after two subsequent steps will presentdouble layers fine particles inner surface 402 of thebasic mould 400 by means of ice. - In the next step a holding
device 700 is applied on top of the fixedlayers layers FIG. 6 theholding device 700 comprises some kind ofpowder material 702 that will not interact during the sintering process, e.g. sand or other inert particles. - In
FIG. 6A there is shown alternate method to hold the establishedlayers male mould 701 provided with a sufficient space for thelayers mould 400 and themale device 701. - Thereafter the final step when producing a
product 100 according to the invention is achieved by sintering (as known per se) thelayers - During the sintering process, at elevated temperature, the water in the ice layers 604, 605 will melt and evaporate, leaving no rest products and merely creating gases in the form of evaporated steam. Hence the use of water/ice provides a very environmental friendly method and also a method that eliminates possible problems related to rest products (as is known in connection with other methods where different kind of binders are used). As is evident the holding
device 700 during this process merely fixes the adheredlayers device 701 will not exert any pressure onto thelayers solid holding device 701 as shown inFIG. 6A . - After cooling, the
sintered body 100 is taken out of thebasic mould 400 and is now in principle ready for use, e.g. as a filter body. As can be seen inFIG. 7 theexemplary filter 100 produced may be made to be extremely thin, which in some instances can be desired. - However, as indicated by way of example in
FIG. 8 a filter body is rarely needed to be as extremely thin as shown inFIG. 5 , but normally the thickness is at least 2 mm. Considering the fact that particles in the range of between 0.2-200 μm may be used according to the invention, it is realised that normally at least onelayer 120 containing at least four levels of coarse particles is applied on top of afine surface layer 130. -
FIG. 9 is a cross sectional zooming ofFIG. 8 showing thesurface layer 130, afirst support layer 120, andbasic support structure 110. As can be seen from the figure thesurface layer 130 comprises sinteredparticles 131, having anaverage diameter 131 d, provided in one thin layer. The thickness of thesurface layer 130 is denoted by 133 and since it comprises one layer ofparticles 131 thethickness 133 of thesurface layer 130 is equal to theaverage diameter 131 d, e.g. powder particles with anaverage diameter 131 d between 0.09-0.18 mm. - As can be seen from
FIG. 9 thefirst support layer 120 comprises sinteredparticles 121, having anaverage diameter 121 d. The thickness of the support layer is denoted by 123 and since it comprises one layer of particles, thethickness 123 is equal to theaverage diameter 121 d, e.g. in the range 0.18-0.25 mm. Inother words 121 d is about twice 131 d Generally it is preferred that 3×131 d>121 d>1.5×131 d. Thefirst support layer 120 may of course be omitted, especially if the size difference between thesintered particles 111 of thebase structure 110 and thesintered particles 131 of thesurface layer 130, is small enough, i.e. the function of thefirst support layer 120 may sometimes merely be to increase the strength of the mould, i.e. to safeguard that thesurface layer 130 does not collapse intovoids sintered particles 111 of thebase structure 110 and thesintered particles 131 of thesurface layer 130 is very large, numerous support layers may be used where the size of the sintered particles gradually is increased in order to improve strength, i.e. to prevent structural collapse due to the voids between the layers. - The
base structure 110 of the embodiment shown inFIG. 9 , e.g. contains spherical metal powder with a particle size range between 0.71-1.00 mm, implying a theoretical pore size of about 200 μm and a filter threshold of about 100 μm. Thepores 112 of thebase structure 110 inFIG. 7 thus have atheoretical pore size 112 d of 200 μm, enabling liquid and/or gas/vapour to be evacuated through the pore structure. - As understood by the above and the following, the invention, e.g. by use of the same
basic mould 400 to form the same outer configuration, enables production ofporous bodies 100 having tailored properties in relation to different parameters, e.g. drainage by varying size and/or shape of the particles and/or temperature conductivity by varying the material of the particles and/or corrosion resistance by varying the material of the particles. - In
FIG. 10 there is shown a different kind of body that may be produced in abasic mould 400 shown and describe above. Here, as is understood when studying the cross sectional zooming ofFIG. 11 , there are positioned afirst surface layer 130 and asecond layer 120 as described above (InFIG. 10 these two layers have been schematically indicated as acommon layer 120/130). Contrary to what is shown in e.g.FIG. 5 theedge 120/130A of these twolayers 120/130 merely extends a limited distance of the entire height of thebasic mould 400. Hence once the twolayers 120/130 have been established there is formed a kind of trough shape void inside thereof. Within this trough shaped void a further amount ofparticles 111 are supplied, to form theupper portion 110 of thebody 100. As is evident theseparticles 111 may be chosen to have any kind of desired diameters/configuration in order to provide desired properties. Generally numerous layers of particles will be used to form thisportion 110 of thebody 100. An important advantage when producing abody 100 according to this embodiment is that there is no need for any holding device/body 700, since theparticles 111 will provide sufficient support to hold the establishedlayer - In
FIGS. 12 and 13 there is shown a further modification according to the invention, where abody 100 is formed having a similar outer configuration as shown inFIG. 10 , but with different properties within theupper portion 110 thereof, by forming a centre portion 110C comprising a first kind ofparticles 111A and aperipheral portion 110B comprising differentlysized particles 111B. Such a body may be achieved along the following lines. The first twolayers upper layer 120. In thenext step particles 111A are supplied into the void within thecylindrical body 408. Thereafter water is sprayed onto theparticles 111A and thebasic mould 400 put into thefreezer 5 thereby fixing theparticles 111A corresponding to the configuration of thecylindrical body 408. In a subsequent step thebasic mould 400 is taken out of thefreezer 5 and thecylindrical body 408 removed where after further particles (of different desired, shape/material) 111B are supplied into the existing void within the remaining part of the space defined by thelayers filter body 100. Hence it is evident that a method according to the invention may be used in a very flexible manner to achieveporous bodies 100 having very varying properties. - In the following it will be described that the invention in an efficient manner also enables manufacture of even more complex filter bodies, by describing a pulp mould produced in accordance with the invention.
-
FIG. 14 shows a cross-sectional view of more complex filter bodies (produced according to the invention), i.e. a male 100 and acomplementary female 200 part of a pulp mould, to high-light some further advantages for products manufactured according to the invention. By way of example the same kind of outer configuration is used as for the products described above, i.e. the samebasic mould 400 is used for producing themale pulp mould 100. - A major difference for a product according to
FIG. 14 , compared to the products shown inFIGS. 1-13 is that herechannels basic mould 400 is filled up in level with itsupper surface 403, prior to the sintering. (the female 200 and the male 100 part are constructed according to the same principles). A forming space 300 (seeFIG. 15 ) is arranged between the pulp moulds 100, 200, where the moulded pulp is formed during operation.) Abase structure bodies support layer base structure surface layer base structure - As is evident from
FIGS. 14-16 the drainage through a body produced according to the invention may be increased/adapted by introducing one ormore drainage channels FIG. 15 there is shown the position of the twomould halves FIG. 16 , which is a cross sectional zooming ofFIG. 15 , theupper drainage channel 150 ends where thesurface layer 130 meets the formingspace 300 and thelower drainage channel 250 ends betweensurface layer 230 and thefirst support layer 220. Thanks to the flexibility in accordance with the invention thedrainage channels body - Finally, as is evident from
FIGS. 14 and 15 that all the area forming thesurface layer fine particles 131, 231. However, all parts of that surface area are not needed to be permeable. As a consequence, some portions of thosesurfaces impermeable layer 161, 261 (e.g. paint) having appropriate properties or by workshop machining techniques. - As is evident for the skilled person in the field, the above examples show that the invention provides for production of a large variety of different three dimensional products in a flexible and cost-efficient manner.
- As mentioned above the process steps for forming the
first layers FIGS. 1-13 ) as for a pulp mould 100 (as shown inFIG. 14 ). However, when producing a pulp mould, having a homogeneous body withchannels outer layers first support layer 120. These objects will form theenlarged drainage passages 150 in thebasic body 100, to facilitate an enhanced drainage of fluid. Thereafter theparticles 111, forming thebase structure 110, are poured into thebasic mould 400 forming thebasic body 110 of the pulp mould, on the top of theother layers bottom surface 140 of the pulp mould, i.e. the surface that is directed upwardly inFIG. 11 , is evened out before the entirebasic mould 400 is introduced into the sintering furnace; wherein the sintering is accomplished in accordance with conventional know how. After cooling, thesintered body 100 is thereafter taken out of thebasic mould 400 and the sharp pointed objects taken out from the body, which is especially easy if these are conical. (It may be preferred to apply the “nails” to a plate, which allows for introduction and removal of the “nails” in an efficient manner). Finally therear surface 140 of thebody 100 may be machined in order to obtain a totally flat supporting surface. - The invention is not limited by what is described above but may be varied within the scope of the appended claims. For instance, it is evident that the
surface layer 130 applied within thebasic mould 400 may also be configured generally along the principles as shown inFIG. 12 , i.e. merely adhering particles to a limited surface area. Hence merely a portion of the formingsurface 402 of thebasic mould 400 may be applied with the adhering laying 604, e.g. by using a template to cover desired parts of thesurface 402 when applying the adhering layer/s 604. In this manner it is possible to tailor the outer surface layer 130 (and indeed of course any other layers) in any desired way. Moreover it is to be understood that the definition surface layer, or indeed the definition layer, must be interpreted broadly. It is evident that even though the figures show that thesurface layer 130 merely contains exactly one layer/level offine particles 131, this is a schematic view of how it possible may be done, but in reality there is rarely a need to have such exactness. Hence, normally there may exist some variation of how many “levels” there are in a layer, e.g. including some portions of a layer/s 130 includingparticles 131 positioned on top of each other. Moreover, in many situations there may be an advantage that the surface layer 130 (or indeed any other layer) includes a number of particles fixed on top of each other within that layer. Accordingly the invention has to be interpreted in sufficiently broad manner to also cover an embodiment where the further layer that is defined before step e) may include the same kind of particles as the particles in the surface layer, e.g. supplied in one batch into themould 400, which form both thesurface layer 130 and the further layer on top of that surface layer 130 (needed to establish a sintered body). Further it is evident that the invention is not restricted to the use of water containing liquids to adhere the particles, but that many different kind of liquids or indeed pastes may be used in accordance with the invention. This may for example be achieved by applying a thin sticky layer (e.g. wax, starch, organic glue, etc.) on to the basic mould, e.g. by means of spray or by applying it with a cloth or dipping the basic mould into it. Further it is realised that parameters of the environments (e.g. a different temp.) do have an influence on what kind of liquids/pastes may be most appropriate to use. - Of course the configuration of the
product 100 may vary within wide frames depending on desired needs and hence it is evident that the shapes of the shown embodiments are by means of example only. The shape of the particles may also vary within wide frames depending on desired needs, e.g. spherical, irregular and/or elongated. The material of the powder particles may also be chosen within a wide range, for example to be mainly ceramic, intermetallic or metallic, e.g. copper, bronze and other copper based alloys, nickel based alloys (e.g.Inconel 600,Monel 400, Hastelloy X, etc) titanium, stainless steel etc.
Claims (21)
1-13. (canceled)
14. A method for forming a sintered body comprising the steps of:
applying to a surface of a mould an adhering layer to facilitate application of a first layer of particles, the mould having a configuration adapted to the sintered body that is to be produced;
applying the first layer of particles onto the adhering layer on the surface of the mould, wherein at least a portion of the adhering layer melts from heat supplied by the particles when they are applied to the mould;
applying a second layer of particles on top of the first layer of particles; and
sintering the particles of the first layer and the second layer on the mould to form the sintered body.
15. The method of claim 14 , wherein the adhering layer is applied as a liquid and freezes after being applied to the surface of the mould.
16. The method of claim 14 , wherein the portion of the adhering layer that melts from heat supplied by the particles freezes again before the sintering step.
17. The method of claim 14 , wherein the particles of the first layer are adhered by means of freezing of the adhering layer.
18. The method of claim 14 , further comprising the step of treating the mould to obtain a temperature of the mould between 0° C. and −100° C. before applying the adhering layer.
19. The method of claim 14 , further comprising the step of treating the mould to obtain a temperature of the mould between −10° C. and −30° C. before applying the adhering layer.
20. The method of claim 14 , wherein the step of applying the first layer of particles is performed in a room having a temperature between 10° C. and 60° C.
21. The method of claim 14 , further comprising the step of treating the mould to obtain a temperature of the mould between 0° C. and −100° C. after applying the first layer of particles and before applying the second layer of particles.
22. The method of claim 14 , further comprising the step of applying a second adhering layer after applying the first layer of particles and before applying the second layer of particles.
23. The method of claim 14 , wherein the particles of the first layer have a different size than the particles in the second layer.
24. A sintered body formed by a process comprising the steps of:
applying to a surface of a mould an adhering layer to facilitate application of a first layer of particles, the mould having a configuration adapted to the sintered body that is to be produced;
applying the first layer of particles onto the adhering layer on the surface of the mould, wherein at least a portion of the adhering layer melts from heat supplied by the particles when they are applied to the mould;
applying a second layer of particles on top of the first layer of particles; and
sintering the particles of the first layer and the second layer on the mould to form the sintered body.
25. The sintered body of claim 24 , wherein the adhering layer is applied as a liquid and freezes after being applied to the surface of the mould.
26. The sintered body of claim 24 , wherein the portion of the adhering layer that melts from heat supplied by the particles freezes again before the sintering step.
27. The sintered body of claim 24 , wherein the particles of the first layer are adhered by means of freezing of the adhering layer.
28. The sintered body of claim 24 , wherein the process further comprises the step of treating the mould to obtain a temperature of the mould between 0° C. and −100° C. before applying the adhering layer.
29. The sintered body of claim 24 , wherein the process further comprises the step of treating the mould to obtain a temperature of the mould between −10° C. and −30° C. before applying the adhering layer.
30. The sintered body of claim 24 , wherein the step of applying the first layer of particles is performed in a room having a temperature between 10° C. and 60° C.
31. The sintered body of claim 24 , wherein the process further comprises the step of treating the mould to obtain a temperature of the mould between 0° C. and −100° C. after applying the first layer of particles and before applying the second layer of particles.
32. The sintered body of claim 24 , wherein the process further comprises the step of applying a second adhering layer after applying the first layer of particles and before applying the second layer of particles.
33. The sintered body of claim 24 , wherein the particles of the first layer have a different size than the particles in the second layer.