US20090025742A1 - Low ignition propensity cigarette paper - Google Patents
Low ignition propensity cigarette paper Download PDFInfo
- Publication number
- US20090025742A1 US20090025742A1 US12/238,247 US23824708A US2009025742A1 US 20090025742 A1 US20090025742 A1 US 20090025742A1 US 23824708 A US23824708 A US 23824708A US 2009025742 A1 US2009025742 A1 US 2009025742A1
- Authority
- US
- United States
- Prior art keywords
- cigarette paper
- tobacco rod
- burn
- cigarette
- base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H27/00—Special paper not otherwise provided for, e.g. made by multi-step processes
-
- A—HUMAN NECESSITIES
- A24—TOBACCO; CIGARS; CIGARETTES; SIMULATED SMOKING DEVICES; SMOKERS' REQUISITES
- A24D—CIGARS; CIGARETTES; TOBACCO SMOKE FILTERS; MOUTHPIECES FOR CIGARS OR CIGARETTES; MANUFACTURE OF TOBACCO SMOKE FILTERS OR MOUTHPIECES
- A24D1/00—Cigars; Cigarettes
- A24D1/10—Cigars; Cigarettes with extinguishers
-
- A—HUMAN NECESSITIES
- A24—TOBACCO; CIGARS; CIGARETTES; SIMULATED SMOKING DEVICES; SMOKERS' REQUISITES
- A24D—CIGARS; CIGARETTES; TOBACCO SMOKE FILTERS; MOUTHPIECES FOR CIGARS OR CIGARETTES; MANUFACTURE OF TOBACCO SMOKE FILTERS OR MOUTHPIECES
- A24D1/00—Cigars; Cigarettes
- A24D1/02—Cigars; Cigarettes with special covers
-
- A—HUMAN NECESSITIES
- A24—TOBACCO; CIGARS; CIGARETTES; SIMULATED SMOKING DEVICES; SMOKERS' REQUISITES
- A24D—CIGARS; CIGARETTES; TOBACCO SMOKE FILTERS; MOUTHPIECES FOR CIGARS OR CIGARETTES; MANUFACTURE OF TOBACCO SMOKE FILTERS OR MOUTHPIECES
- A24D1/00—Cigars; Cigarettes
- A24D1/02—Cigars; Cigarettes with special covers
- A24D1/025—Cigars; Cigarettes with special covers the covers having material applied to defined areas, e.g. bands for reducing the ignition propensity
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H1/00—Paper; Cardboard
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H19/00—Coated paper; Coating material
- D21H19/10—Coatings without pigments
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H19/00—Coated paper; Coating material
- D21H19/10—Coatings without pigments
- D21H19/14—Coatings without pigments applied in a form other than the aqueous solution defined in group D21H19/12
- D21H19/24—Coatings without pigments applied in a form other than the aqueous solution defined in group D21H19/12 comprising macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H19/00—Coated paper; Coating material
- D21H19/10—Coatings without pigments
- D21H19/12—Coatings without pigments applied as a solution using water as the only solvent, e.g. in the presence of acid or alkaline compounds
Definitions
- the present invention relates to a low ignition propensity cigarette paper.
- a cigarette paper has been proposed which is reduced in the air permeability of base cigarette paper by applying a salt of alginic acid to at least a part of the base cigarette paper such that a cigarette is restrained from causing, for example, a floor to catch fire from the burning butt when the cigarette falls on the floor because of, for example, carelessness by the smoker (see Jpn. Pat. Appln. KOKAI Publication No. 7-300795).
- the inventors of the present invention have made studies as to the effect of sodium alginate out of salts of alginic acid on the actual ignition propensities of cigarette paper, and as a result, have found that the coating required to exhibit the same ignition propensities differs depending on the degree of polymerization or viscosity of sodium alginate.
- a low ignition propensity cigarette paper comprising base cigarette paper having a basis weight exceeding 22 g/m 2 , and a plurality of burn limiting areas arranged apart from one another on one surface of the base cigarette paper, wherein the burn limiting areas are formed by applying sodium alginate having a degree of polymerization of about 500 to about 900.
- a low ignition propensity cigarette paper comprising base cigarette paper having a basis weight exceeding 22 g/m 2 , and a plurality of burn limiting areas arranged apart from one another on one surface of the base cigarette paper, wherein the burn limiting areas are each formed by applying sodium alginate whose 3% by weight aqueous solution exhibits a viscosity of 19000 cP or more as measured at 25° C.
- a low ignition propensity cigarette paper comprising base cigarette paper containing a filler in an amount of 2 g/m 2 or more, and having a basis weight exceeding 22 g/m 2 and an inherent air permeability of 30 to 60 CORESTA units, and a plurality of burn limiting areas arranged apart from one another on one surface of the base cigarette paper, wherein the burn limiting areas are each formed by applying sodium alginate in an amount less than 3 g/m 2 , and the cigarette paper provides a cigarette exhibiting a PFLB value of 0 to 10% when measured according to ASTM E-2187-04.
- the single FIGURE is a partially broken schematic perspective view illustrating an example of a cigarette wrapped with a cigarette paper according to one embodiment of the present invention.
- a cigarette paper of the present invention is a paper in which a plurality of burn limiting areas where a burn limiting agent constituted of sodium alginate is applied are provided apart from on another on a base cigarette paper.
- the base cigarette paper is ordinary cigarette paper using, as the base, ordinary pulp such as flax pulp.
- Such base cigarette paper may contain a generally used filler, including a carbonate such as calcium carbonate or potassium carbonate and a hydroxide such as calcium hydroxide or magnesium hydroxide in an amount of 2 g/m 2 or more.
- the filler may be contained in an amount of 2 to 8 g/m 2 in the base cigarette paper.
- the base cigarette paper usually has a basis weight exceeding 22 g/m 2 .
- the basis weight is usually 80 g/m 2 or less and preferably more than 20 g/m 2 but 28 g/m 2 or less.
- the inherent air permeability of the base cigarette paper is usually 30 to 60 CORESTA units.
- the base cigarette paper may be added with a burn adjusting agent such as citric acid or its salt (a sodium salt, potassium salt).
- a burn adjusting agent such as citric acid or its salt (a sodium salt, potassium salt).
- the burn adjusting agent if added, is used in an amount of 2% by weight or less in the base paper.
- a plurality of burn limiting areas which are respectively formed by application of a burn limiting agent (sodium alginate), are arranged apart from one another on one surface of the base cigarette paper.
- these burn limiting areas may extend in the longitudinal direction of the tobacco rod, so that they are arranged in the form of plural stripes apart from one another in the direction of the circumference of the tobacco rod.
- these burning areas may extend in the circumferential direction of the tobacco rod, so that they are arranged in the form of plural circular bands apart from one another in the longitudinal direction of the tobacco rod.
- sodium alginate is used as the burn limiting agent.
- Alginic acid is polyuronic acid consisting of two types of monomers, ⁇ -D-mannuronic acid and ⁇ -L-guluronic acid.
- a sodium salt of alginic acid having a degree of polymerization of 500 to 900 is used.
- sodium alginate whose 3% by weight aqueous 3% solution exhibits a viscosity of 19000 cP or more when measured at 25° C. is used. The degree of polymerization and viscosity of alginic acid are correlated with each other to some extent.
- the same level of reduced ignition propensities can be attained even in a smaller coating amount than in the case of using other sodium alginate.
- the above viscosity is usually 40000 cP or less.
- the total coating amount (dry basis) of the sodium alginate burn limiting agent is less than 3 g per m 2 of the coating area.
- a coating amount of as low as 0.2 to 2 g/m 2 can achieve sufficiently reduced ignition propensities.
- the cigarette paper according to the invention can provide a cigarette (cigarette in which a tobacco filler is wrapped by the cigarette paper) exhibiting a percent full-length burn (PFLB) of 0 to 10% when measured according to ASTM E-2187-04.
- a cigarette paper according to one embodiment of the invention includes base cigarette paper containing a filler in an amount of 2 g/m 2 or more and having a basis weight exceeding 22 g/m 2 and an inherent air permeability of 30 to 60 CORESTA units, and a plurality of burn limiting areas arranged apart from one another on one surface of the base cigarette paper.
- the burn limiting area is formed by applying sodium alginate in an amount less than 3 g/m 2 .
- a cigarette prepared by winding the cigarette paper around wrapping a tobacco filler rod with this cigarette paper exhibits a PFLB value of 0 to 10% when measured according to ASTM E-2187-04.
- the low ignition propensity cigarette paper of the invention is used to wrap a tobacco rod constituted of a tobacco filler such as shredded tobacco, and usually, the surface to which the burn limiting agent is applied is brought into contact with the tobacco rod.
- FIGURE illustrates a cigarette wrapped with a cigarette paper to which the burn limiting agent is applied in the form of a circular band.
- a cigarette 10 has a tobacco rod 11 constituted of a tobacco filler 13 wrapped with a base cigarette paper 12 in a columnar shape.
- the tobacco rod 11 usually has a circumferential length of 17 mm to 26 mm and a length of 49 mm to 90 mm.
- An ordinary filter 18 may be fitted to a proximal end (i.e., the downstream end in the smoking direction) 11 b of the tobacco rod 11 by using a tipping paper 17 according to an ordinary method.
- a plurality of circular band areas 14 to which burn limiting agents (sodium alginate) are applied are formed on the base cigarette paper 12 and respectively define burn limiting areas. These circular band burn limiting areas 14 are formed apart from one another in the longitudinal direction of the tobacco rod.
- a usual burn area 15 to which no burn adjusting agent is applied is defined between the adjacent band burn limiting areas 14 . Since this area 15 is constituted of the part of the base cigarette paper 12 , it can be burned in the usual smoking condition like the base cigarette paper 12 itself. Therefore, the area 15 acts as the usual burn area.
- the base cigarette paper 12 may be provided with, for example, two or three circular band burn limiting areas 14 . Also, the circular band burn limiting area 14 may have a width of 4 mm to 7 mm in the longitudinal direction and its thickness may usually be 0.1 to 5 ⁇ m. The spacing between the adjacent burn limiting areas 14 is preferably 18 mm to 25 mm.
- no burn limiting agent is applied to an area 16 at a distance d from the distal end of the cigarette.
- the end part where no burn limiting agent is applied constitutes a usual burn area 16 and can correspond to the area burned by one or two puffs of the usual cigarette.
- the distance d may be designed to be 10 mm to 25 mm from the distal end 11 a of the tobacco rod. It is not particularly necessary to form the burn limiting area 14 on the inside surface of the cigarette paper corresponding to the part of the cigarette paper 12 covered with the tipping paper 17 .
- the cigarette 10 when the cigarette 10 is ignited at the distal end 11 a of the cigarette rod 11 and smoked to burn the cigarette, the cigarette can be burned like a usual cigarette in the usual burn area 15 to be able to enjoy a smoking taste.
- inflammables such as a carpet, tatami, wood products, fabrics and clothes
- the fire is extinguished by the heat absorption of the burn limiting area 14 in a burning direction and inflammables in combination with tobacco shreds contained in the tobacco filler, which suppresses the inflammables to catch fire.
- ALG-1, ALG-2, ALG-3, ALG-4 and ALG-5 are available under the tradenames of ULV, IL-2, 1-1, I-5 and I-S, respectively.
- the viscosities shown in Table 1 are results when 200 g of a 3% by weight aqueous sodium alginate solution was placed in a 200 mL or 300 mL beaker, which was then placed in a constant-temperature water bath, the aqueous solution was kept at 25 ⁇ 0.5° C., the solution was stirred slowly with a glass rod for about one minute so as not to introduce air bubbles thereinto and was then allowed to stand for 10 minutes, followed by measuring the viscosity of the solution by a B-type viscometer.
- the 3% by weight aqueous sodium alginate solution was applied to (printed on) base cigarette paper (width: 27 mm, length: 1.500 m) having a specification as shown in Table 2 so as to have a fixed width of 7 mm in the longitudinal direction in a stripe form at fixed intervals of 20 mm by using a direct gravure system, thereby forming a total of 56 burn limiting agent coating areas.
- the total coating amount of sodium alginate was measured using the following method. The results are shown also in Table 2.
- the cigarette papers obtained in Examples 1 to 6 had the coating amount of the burn limiting agent per m 2 of the area to which the burn limiting agent (sodium alginate) was applied was 1.5 to 2 g.
- the coating amount of the burn limiting agent is calculated based on unit area of the cigarette paper, it is 0.39 to 0.52 g/m 2 because the coating amount should be multiplied by 7/27.
- the obtained cigarette paper was used to wrap a tobacco rod made of American blend shreds (amount of tar in the case of setting no filter: 19 to 20 mg) and the obtained tobacco rod was cut such that the first coating area was located with a band space of 5 mm from the burning tip end of the cigarette.
- the length of one cigarette was 59 mm and the cigarette had two burn limiting agent coating areas.
- the obtained cigarette was subjected to an ignition propensity test according to ASTM E-2187-04 to measure the PFLB value. The results are shown in Table 2.
- the coating amount of sodium alginate was measured in the following procedures according to “Quantitative analysis method for sodium alginate in foods” described in “Journal of Food Hygiene”, vol. 5, pp. 297-302 (1988) without performing defatting, dilute sulfuric acid treatment and deproteinization treatment.
- the cigarette paper (length: 1.500 m, width: 27 mm) (about 11.0 g) coated with the above burn limiting agent was cut into 5 mm square, added with 40 mL of a 1% by weight aqueous sodium bicarbonate solution, heated at 60° C. in a hot bath for 5 minutes and then sufficiently mixed and stirred, followed by centrifugation (3500 rpm, 10 minutes; the same as follows) to obtain a supernatant (extract).
- the extraction residue was extracted again in the same manner as above to obtain a supernatant (extract) and also, 20 mL of a 1% by weight aqueous sodium bicarbonate solution was added to the extraction residue, which was then sufficiently mixed and stirred to obtain a supernatant (extract).
- extract 20 mL of a 1% by weight aqueous sodium bicarbonate solution was added to the extraction residue, which was then sufficiently mixed and stirred to obtain a supernatant (extract).
- the obtained three extracts were combined and a 1% by weight aqueous sodium bicarbonate solution was added to the mixed extract to be 100 mL, which was used as a test solution.
- the present invention provides a cigarette paper exhibiting superior reduced ignition propensities.
Landscapes
- Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Paper (AREA)
- Cigarettes, Filters, And Manufacturing Of Filters (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2006-095825 | 2006-03-30 | ||
JP2006095825 | 2006-03-30 | ||
PCT/JP2007/055874 WO2007119484A1 (ja) | 2006-03-30 | 2007-03-22 | 低延焼性のシガレット用巻紙 |
Related Parent Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2007/055874 Continuation WO2007119484A1 (ja) | 2006-03-30 | 2007-03-22 | 低延焼性のシガレット用巻紙 |
Publications (1)
Publication Number | Publication Date |
---|---|
US20090025742A1 true US20090025742A1 (en) | 2009-01-29 |
Family
ID=38609269
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/238,247 Abandoned US20090025742A1 (en) | 2006-03-30 | 2008-09-25 | Low ignition propensity cigarette paper |
Country Status (13)
Country | Link |
---|---|
US (1) | US20090025742A1 (de) |
EP (1) | EP2000589B1 (de) |
JP (1) | JP4862041B2 (de) |
KR (1) | KR101059329B1 (de) |
CN (1) | CN101410571B (de) |
CA (1) | CA2645998C (de) |
ES (1) | ES2452320T3 (de) |
HK (1) | HK1126261A1 (de) |
MY (1) | MY153407A (de) |
RU (1) | RU2372820C1 (de) |
TW (1) | TWI354048B (de) |
UA (1) | UA91125C2 (de) |
WO (1) | WO2007119484A1 (de) |
Cited By (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20100297351A1 (en) * | 2008-02-08 | 2010-11-25 | Shinzo Kida | Production method of producing wrapper for cigarettes |
US20110033624A1 (en) * | 2008-05-16 | 2011-02-10 | Takeo Tsutsumi | Process for producing cigarette paper having low ignition propensity |
EP2404512A1 (de) | 2010-07-06 | 2012-01-11 | TEWS Elektronik GmbH & Co. KG | Vorrichtung zur Herstellung von Zigaretten in der tabakverarbeitenden Industrie sowie ein Verfahren hierzu |
US20150257438A1 (en) * | 2012-10-09 | 2015-09-17 | Kt & G Corporation | Low ignition propensity cigarette paper and cigarette including the same |
US9164218B2 (en) | 2008-07-10 | 2015-10-20 | Oree, Inc. | Slim waveguide coupling apparatus and method |
US9857519B2 (en) | 2012-07-03 | 2018-01-02 | Oree Advanced Illumination Solutions Ltd. | Planar remote phosphor illumination apparatus |
Families Citing this family (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2009191393A (ja) * | 2008-02-13 | 2009-08-27 | Rengo Co Ltd | たばこ用巻紙 |
RU2476128C1 (ru) * | 2009-07-07 | 2013-02-27 | Джапан Тобакко Инк. | Способ и устройство для изготовления оберточной бумаги для сигарет |
CA2781083C (en) * | 2009-11-25 | 2017-03-07 | Japan Tobacco Inc. | Low ignition propensity wrapping paper and method and machine of manufacturing same |
CN102174779B (zh) * | 2011-03-18 | 2012-06-27 | 云南烟草科学研究院 | 一种降低低引燃倾向卷烟纸阻燃胶粘度的方法 |
CN102493285B (zh) * | 2011-12-02 | 2013-10-30 | 牡丹江恒丰纸业股份有限公司 | 一种阻燃剂、具有阻燃带的卷烟纸及该卷烟纸的制备方法 |
DE102012106154B4 (de) * | 2012-07-09 | 2014-06-12 | Delfortgroup Ag | Zigarettenpapier mit verbesserter Luftdurchlässigkeit, Zigarette und Verfahren zum Herstellen eines Zigarettenpapiers |
PL3446573T3 (pl) * | 2017-08-24 | 2021-05-04 | Jt International S.A. | Papier owijający do wyrobu do palenia |
CN112385883B (zh) * | 2020-11-17 | 2022-11-04 | 云南中烟工业有限责任公司 | 一种用于电磁加热的加热不燃烧卷烟纸及其制备和用途 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4077414A (en) * | 1975-01-09 | 1978-03-07 | Brown & Williamson Tobacco Corporation | Smoking articles |
US5820998A (en) * | 1994-03-08 | 1998-10-13 | Schweitzer-Mauduit International, Inc. | Coated paper and process for making the same |
US20020139381A1 (en) * | 2000-11-13 | 2002-10-03 | Schweitzer-Mauduit International, Inc. | Process for producing smoking articles with reduced ignition proclivity characteristics and products made according to same |
US20030136420A1 (en) * | 2002-01-23 | 2003-07-24 | Schweitzer-Mauduit International, Inc. | Smoking articles with reduced ignition proclivity characteristics |
US20040123874A1 (en) * | 2001-03-28 | 2004-07-01 | Zawadzki Michael A. | Reduced ignition propensity smoking article with a polysaccharide treated wrapper |
Family Cites Families (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2000157245A (ja) * | 1998-11-24 | 2000-06-13 | Mishima Paper Co Ltd | 高燃焼性たばこ用巻紙 |
JP2003310232A (ja) * | 2002-04-24 | 2003-11-05 | Japan Tobacco Inc | 巻紙検査装置 |
-
2007
- 2007-03-22 WO PCT/JP2007/055874 patent/WO2007119484A1/ja active Application Filing
- 2007-03-22 JP JP2008510841A patent/JP4862041B2/ja not_active Expired - Fee Related
- 2007-03-22 EP EP07739317.1A patent/EP2000589B1/de not_active Not-in-force
- 2007-03-22 MY MYPI20083634A patent/MY153407A/en unknown
- 2007-03-22 UA UAA200811650A patent/UA91125C2/uk unknown
- 2007-03-22 ES ES07739317.1T patent/ES2452320T3/es active Active
- 2007-03-22 CN CN2007800114655A patent/CN101410571B/zh not_active Expired - Fee Related
- 2007-03-22 CA CA2645998A patent/CA2645998C/en not_active Expired - Fee Related
- 2007-03-22 KR KR1020087023240A patent/KR101059329B1/ko active IP Right Grant
- 2007-03-22 RU RU2008138704/12A patent/RU2372820C1/ru not_active IP Right Cessation
- 2007-03-28 TW TW096110703A patent/TWI354048B/zh not_active IP Right Cessation
-
2008
- 2008-09-25 US US12/238,247 patent/US20090025742A1/en not_active Abandoned
-
2009
- 2009-05-27 HK HK09104808.5A patent/HK1126261A1/xx not_active IP Right Cessation
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4077414A (en) * | 1975-01-09 | 1978-03-07 | Brown & Williamson Tobacco Corporation | Smoking articles |
US5820998A (en) * | 1994-03-08 | 1998-10-13 | Schweitzer-Mauduit International, Inc. | Coated paper and process for making the same |
US20020139381A1 (en) * | 2000-11-13 | 2002-10-03 | Schweitzer-Mauduit International, Inc. | Process for producing smoking articles with reduced ignition proclivity characteristics and products made according to same |
US20040182407A1 (en) * | 2000-11-13 | 2004-09-23 | Peterson Richard M. | Process for producing smoking articles with reduced ignition proclivity characteristics and products made according to same |
US20040123874A1 (en) * | 2001-03-28 | 2004-07-01 | Zawadzki Michael A. | Reduced ignition propensity smoking article with a polysaccharide treated wrapper |
US20030136420A1 (en) * | 2002-01-23 | 2003-07-24 | Schweitzer-Mauduit International, Inc. | Smoking articles with reduced ignition proclivity characteristics |
Non-Patent Citations (1)
Title |
---|
Kimica Corporation, "Product List: Sodium Alginate", Kimica Corporation, Cyuo-ku, Tokyo, Japan, www.kimica-alginate.com/products/ accessed 11/7/2011. * |
Cited By (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20100297351A1 (en) * | 2008-02-08 | 2010-11-25 | Shinzo Kida | Production method of producing wrapper for cigarettes |
US8420173B2 (en) | 2008-02-08 | 2013-04-16 | Japan Tobacco Inc. | Production method of producing wrapper for cigarettes |
US20110033624A1 (en) * | 2008-05-16 | 2011-02-10 | Takeo Tsutsumi | Process for producing cigarette paper having low ignition propensity |
US9164218B2 (en) | 2008-07-10 | 2015-10-20 | Oree, Inc. | Slim waveguide coupling apparatus and method |
EP2404512A1 (de) | 2010-07-06 | 2012-01-11 | TEWS Elektronik GmbH & Co. KG | Vorrichtung zur Herstellung von Zigaretten in der tabakverarbeitenden Industrie sowie ein Verfahren hierzu |
DE102010026178A1 (de) | 2010-07-06 | 2012-01-12 | Tews Elektronik Gmbh & Co. Kg | Vorrichtung zur Herstellung von Zigaretten in der tabakverarbeitenden Industrie sowie ein Verfahren hierzu |
US9277767B2 (en) | 2010-07-06 | 2016-03-08 | Tews Elektronik Gmbh & Co. Kg | Device for producing cigarettes in the tobacco processing industry and a method therefore |
US9857519B2 (en) | 2012-07-03 | 2018-01-02 | Oree Advanced Illumination Solutions Ltd. | Planar remote phosphor illumination apparatus |
US20150257438A1 (en) * | 2012-10-09 | 2015-09-17 | Kt & G Corporation | Low ignition propensity cigarette paper and cigarette including the same |
Also Published As
Publication number | Publication date |
---|---|
TWI354048B (en) | 2011-12-11 |
CN101410571B (zh) | 2012-05-30 |
EP2000589A2 (de) | 2008-12-10 |
CN101410571A (zh) | 2009-04-15 |
EP2000589A9 (de) | 2009-03-25 |
MY153407A (en) | 2015-02-13 |
KR101059329B1 (ko) | 2011-08-24 |
EP2000589A4 (de) | 2012-03-07 |
RU2372820C1 (ru) | 2009-11-20 |
HK1126261A1 (en) | 2009-08-28 |
WO2007119484A1 (ja) | 2007-10-25 |
CA2645998C (en) | 2012-05-15 |
ES2452320T3 (es) | 2014-03-31 |
KR20080095304A (ko) | 2008-10-28 |
TW200806853A (en) | 2008-02-01 |
EP2000589B1 (de) | 2013-12-18 |
UA91125C2 (uk) | 2010-06-25 |
JPWO2007119484A1 (ja) | 2009-08-27 |
CA2645998A1 (en) | 2007-10-25 |
JP4862041B2 (ja) | 2012-01-25 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20090025742A1 (en) | Low ignition propensity cigarette paper | |
EP1867782B1 (de) | Zigarettenpapier mit langsamer flammenvortriebsgeschwindigkeit | |
RU163981U1 (ru) | Обертки для курительных изделий, имеющие пониженную диффузию, обеспечивающие снижение способности к поджиганию | |
KR100904826B1 (ko) | 인화성 특성이 감소된 흡연 용품 | |
RU2652960C2 (ru) | Курительные изделия, имеющие пониженную способность к поджиганию | |
US20110033624A1 (en) | Process for producing cigarette paper having low ignition propensity | |
US9903071B2 (en) | Low flame-spreading cigarette paper | |
US8302612B2 (en) | Low ignition propensity cigarette paper |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: JAPAN TOBACCO INC., JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MATSUFUJI, TAKAAKI;KOMINAMI, TAKASHI;UYAMA, KEN;AND OTHERS;REEL/FRAME:021670/0113 Effective date: 20080905 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- AFTER EXAMINER'S ANSWER OR BOARD OF APPEALS DECISION |