US20080202644A1 - Quiescent transfer of melts - Google Patents

Quiescent transfer of melts Download PDF

Info

Publication number
US20080202644A1
US20080202644A1 US11/710,452 US71045207A US2008202644A1 US 20080202644 A1 US20080202644 A1 US 20080202644A1 US 71045207 A US71045207 A US 71045207A US 2008202644 A1 US2008202644 A1 US 2008202644A1
Authority
US
United States
Prior art keywords
melt
holding furnace
furnace
holding
pump
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US11/710,452
Other languages
English (en)
Inventor
John R. Grassi
John Campbell
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Alotech Ltd LLC
Original Assignee
Alotech Ltd LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Alotech Ltd LLC filed Critical Alotech Ltd LLC
Priority to US11/710,452 priority Critical patent/US20080202644A1/en
Assigned to ALOTECH LTD. LLC reassignment ALOTECH LTD. LLC ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: CAMPBELL, JOHN
Assigned to ALOTECH LTD. LLC reassignment ALOTECH LTD. LLC ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: GRASSI, JOHN R.
Priority to PCT/US2008/002279 priority patent/WO2008103402A2/fr
Publication of US20080202644A1 publication Critical patent/US20080202644A1/en
Priority to US12/578,195 priority patent/US8303890B2/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F27—FURNACES; KILNS; OVENS; RETORTS
    • F27B—FURNACES, KILNS, OVENS, OR RETORTS IN GENERAL; OPEN SINTERING OR LIKE APPARATUS
    • F27B3/00—Hearth-type furnaces, e.g. of reverberatory type; Tank furnaces
    • F27B3/04—Hearth-type furnaces, e.g. of reverberatory type; Tank furnaces of multiple-hearth type; of multiple-chamber type; Combinations of hearth-type furnaces
    • F27B3/045—Multiple chambers, e.g. one of which is used for charging
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22B—PRODUCTION AND REFINING OF METALS; PRETREATMENT OF RAW MATERIALS
    • C22B9/00—General processes of refining or remelting of metals; Apparatus for electroslag or arc remelting of metals
    • C22B9/006—General processes of refining or remelting of metals; Apparatus for electroslag or arc remelting of metals with use of an inert protective material including the use of an inert gas
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22B—PRODUCTION AND REFINING OF METALS; PRETREATMENT OF RAW MATERIALS
    • C22B9/00—General processes of refining or remelting of metals; Apparatus for electroslag or arc remelting of metals
    • C22B9/02—Refining by liquating, filtering, centrifuging, distilling, or supersonic wave action including acoustic waves
    • C22B9/023—By filtering
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F27—FURNACES; KILNS; OVENS; RETORTS
    • F27D—DETAILS OR ACCESSORIES OF FURNACES, KILNS, OVENS, OR RETORTS, IN SO FAR AS THEY ARE OF KINDS OCCURRING IN MORE THAN ONE KIND OF FURNACE
    • F27D3/00—Charging; Discharging; Manipulation of charge
    • F27D3/14—Charging or discharging liquid or molten material
    • F27D3/145—Runners therefor
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P10/00—Technologies related to metal processing
    • Y02P10/20—Recycling

Definitions

  • This disclosure relates to the melting, holding, degassing and casting of liquid metals, particularly light metals such as aluminum and magnesium, by a totally quiescent means. This encourages the detrainment of non-metallic inclusions from the melt, and avoids the re-entrainment of surface oxides into the metal during degassing and the transfer to the point of casting and during the casting process itself.
  • bifilms are not easily eliminated from liquid metals, particularly oxide bifilms in liquid aluminum and its alloys.
  • the reason for this is that the bifilm initially ravels into a compact ball, allowing it to pass through most filters. Later, in the casting, it can unravel, becoming a serious crack-like defect that reduces the properties of the casting.
  • Bifilms in Al and its alloys will also not sink or float in any reasonable time. The reason for this is that the aluminum oxide is slightly denser than liquid Al and so should sink.
  • the air entrained between the folded-over film giving it its name ‘bifilm’ to denote its doubled-over nature) causes it to float. This nearly neutral buoyancy together with its film-like aspect ratio confers an extremely low Stokes velocity. Thus any slight convection in the melt will cause the suspended oxide defects to circulate for hours or days.
  • the cleaning of the metal is usually nowadays carried out by the production of thousands or millions of minute bubbles of an inert gas introduced beneath the surface of the melt.
  • This can be achieved via porous plugs inserted into the walls or base of the holding vessel, or by rotary degassing, in which an immersed rotor is caused to spin in the liquid, releasing clouds of minute bubbles.
  • Such techniques use inert gas to flush out dissolved hydrogen and usually operate with impressive efficiency.
  • the bubbles attach to suspended oxides and carry them to the surface of the melt, from where they can be skimmed off.
  • the so-called cleaning process is one in which the few large double oxides are probably replaced by millions of small double oxides. For this reason, the total cleaning action is less than optimum. Even worse, it is not uncommon for rotary degassers to operate in such a way that a vortex is formed around the rotor shaft which carries air down into the melt, re-introducing oxides as fast as they can be removed. In addition to these problems, if the rotor assembly is not completely dry (the refractories are likely to have absorbed up to ten per cent water vapor over a weekend for instance) the first several minutes of operation of the rotary degasser will cause an increase in the gas content of the melt. Thus the melt will get worse before it gets better. For those systems working on an automatically-controlled (i.e. rather short) degassing time, the final result is likely to be a melt with increased rather than decreased hydrogen content.
  • U.S. Pat. No. 3,809,379 describes a succession of stations in which the metal is melted, held, degassed by vacuum, and the transfers between stations effected by electromagnetic pump.
  • electromagnetic pumps is considered less than ideal because of the problems cited above. More fundamentally, the active transfer of the melt is seen to be counter-productive in achieving a quiescent transfer system with minimal moving parts so as to avoid disturbance to the melt, and the consequent stirring-in of bifilm defects. The different levels of the melt in the various sections is again counter-productive because it is not easily achieved without the action of powerful forces, and the probable consequential eventual fall under gravity at some later stage.
  • U.S. Pat. No. 3,890,139 discloses a succession of treatment stations for the production of blister copper.
  • the stations are not required to be at the same height, but the process necessarily runs continuously, requiring the melts to run downhill between the various vessels.
  • the locally high velocities that will be generated by this downhill motion of the liquid are highly injurious to the aims discussed herein.
  • the proposed heating by arcs will also, of course, create Lorentz forces in the liquid, causing localized intense stirring, again to the severe detriment of the melt as envisioned herein.
  • U.S. Pat. No. 4,741,514 is typical of many modern systems for the holding and dosing of liquid aluminum.
  • the furnace body has to be filled by pouring in metal under gravity. This is a highly damaging action, creating and entraining much dross (i.e. macroscopic oxide defects in addition to copious amounts of microscopic oxide bifilms). Whilst filling a dispensing chamber, a stopper then allows the melt to fall a second time, thus further causing degradation of the quality of the melt. Finally, the melt is dosed by gravity into the mold, again damaging the melt.
  • U.S. Pat. No. 4,881,670 describes a connected succession of vessels of unspecified geometry as usual.
  • degassing by bubbles is disadvantageously introduced, together with a plunger displacement mechanism that transfers the melt out of the final vessel in some unspecified manner.
  • a plunger displacement mechanism that transfers the melt out of the final vessel in some unspecified manner.
  • U.S. Pat. No. 4,974,817 describes a holding vessel of unspecified geometry as usual, but heated by gas burner, and so both disturbing the surface and providing products of combustion so that the hydrogen content of the melt is not easily reduced. Subsequent efforts to reduce hydrogen are carried out by immersed porous lances to create bubbles, introducing more defects as we have discussed, and preventing settling of suspended debris under gravity by the creation of circulation currents in the liquid. Finally, the system is designed merely to provide a baling well, from which metal is baled out via a small ladle.
  • This technique introduces oxides back into the melt at this point of delivery, mainly as a result of oxide adhesion to the walls of the ladle, and because of the usual pouring action that is a consequence of the ladle adjusting the level of its contents prior to lifting clear of the well.
  • U.S. Pat. No. 5,662,859 is a complicated system involving the use of many moving parts, all of which are known to introduce severe practical problems for the reliable operation of systems for the handling of molten Al and its alloys. It includes no means of degassing the melt. Level control in the main body of the unit is achieved by a displacement plunger. The varying level of this body will create oxides by the wash of metal up and down its sides. Similar oxide creation on the walls of the containment vessel will damage the melt when the unit is used in the gas-pressurized delivery mode. When used with the electromagnetic pump (as a kind of linear motor) the strong internal turbulence expected in this device is again counter-productive. The movement of the whole unit on rails to effect contact with the casting machine is also seen to be disadvantageous because of the danger of slopping and surging of the melt, again raising sediment, and creating oxide wash on the internal walls of the various chambers.
  • U.S. Pat. No. 5,725,043 describes a variant of a conventional low pressure casting system. As such, it has the standard drawbacks of large, expensive pressure vessel, and large volumes of air or nitrogen gas to pressurize the melt to effect casting. Control is rather ‘spongy’ as a result of the large compressible volume of gas that is used to accelerate the large volume of heavy molten liquid (the system is equivalent to operating a heavy battering ram by holding it only by weak elastic bands).
  • the valve immersed in the melt is a source of concern regarding its reliability in production.
  • the filtering system comprising the deep bed effectively prevents any rapid change of alloy, and is a major task when the bed requires to be changed. There is effectively no holding furnace in this arrangement, and no opportunity to degass the melt.
  • the pressure in the vessel will have to be released. This will cause the metal in the riser tube to fall, equalizing levels with the melt. This washing of melt up and down the delivery tube will generate oxides at the very point where they are most in danger of entering the mold and thus degrading the casting.
  • the principle involved is that of quiescence.
  • the novel principle is the design for conditions of quiescence of both the surface of the melt, and the bulk liquid beneath the surface.
  • the surface of the melt is maintained at a substantially unvarying and horizontal level and is undisturbed, and the melt beneath the surface enjoys quiescent, non-convecting conditions.
  • the imposition of these conditions requires the elimination of conventional degassing and cleaning of the melt by techniques involving the passage of bubbles of inert gas through the melt.
  • Novel non-disturbing techniques are employed such as hydrogen diffusion out of the melt and its removal from the system by counter-current flow of a dry, hydrogen-free gas. Cleaning of the melt from inclusions is accomplished efficiently for the first time by sedimentation.
  • a quiescent melt handling system comprises a holding furnace for a molten metal, wherein the holding furnace comprises a relatively large surface area and a relatively shallow depth, having a width to depth ratio in the range of at least approximately 4 to 1, but which may be as high as 100 to 1, and a means for separating inclusions from the melt in the holding furnace.
  • a quiescent transfer casting method comprises the steps of melting a metal to form a melt.
  • the melt is then transferred into a holding furnace where the hydrogen in the melt is passively equilibrated with a dry atmosphere maintained in the holding furnace.
  • the melt is subsequently withdrawn from the holding furnace.
  • a quiescent melt handling system comprises a melting furnace, which transforms solid metal into a melt, and a holding furnace for the melt, wherein the holding furnace comprises a shallow bath having a relatively large surface area with a heater located above the surface of the melt.
  • the holding furnace has a width to depth ratio on the order of at least approximately 4-100 to 1 and a length to width ratio on the order of at least approximately 1-100 to 1.
  • a first channel communicates the holding furnace with the melting furnace ensuring that a melt level within both furnaces is substantially equal.
  • a means is provided for withdrawing the melt from the holding furnace.
  • FIG. 1 is a schematic side elevational view in cross-section of a quiescent transfer casting furnace system according to a first embodiment of the present disclosure
  • FIG. 2 is a schematic side elevational view in cross-section of a quiescent transfer casting furnace system according to a second embodiment of the present disclosure
  • FIG. 3 is a schematic side elevational view in cross-section of a quiescent transfer casting furnace according to a third embodiment of the present disclosure
  • FIG. 4 is a schematic side elevational view in cross-section of a holding furnace according to a fourth embodiment of the present disclosure
  • FIG. 5 is a schematic side elevational view in cross-section of a holding furnace according to a fifth embodiment of the present disclosure
  • FIG. 6 is a schematic plan view of another embodiment of a holding furnace according to the present disclosure.
  • FIG. 7 is a schematic plan view of a holding furnace according to still another embodiment of the present disclosure.
  • the holding furnace It is necessary for the holding furnace to operate at a substantially constant level of liquid metal. This is achieved by ensuring that the rate of supply to the unit and rate of delivery from it are, on average, sufficiently well matched so that the change of level on additions to or deliveries from the unit cause the surface level to change by only relatively few millimeters. This is easily achieved by monitoring the height of metal in the holding furnace, and adjusting the rate of melting from the melting furnace accordingly. The task of maintaining the constant height is facilitated if the area of the melt in the holder compared to the volume changes is sufficiently large.
  • this furnace is electrically heated by elements in the roof (although fuel-firing inside heater tubes is of course possible). This has the benefit of creating a positive vertical temperature gradient in the liquid bath that will assist to stabilize the melt against convection.
  • a dry atmosphere free from the water vapor characterizing fuel-fired furnaces
  • the key aspect of the furnace that is central to this patent is the aspect ratio of the width (or length) of the bath compared to its depth.
  • the holder width to depth ratio should be in the range 4 to 40 times as wide as it is deep, or preferably 5 to 50 or more preferably 10 to 100.
  • the holding furnace should be at least four times as wide as it is deep, or possibly up to one hundred times as wide as it is deep (It is assumed that in most cases the length of the furnace will exceed its width, otherwise, the ratio would logically apply to the furnace length).
  • the length to width ratio can be in the range of 1-100, or more, to 1.
  • the static nature of the main body of liquid now allows inclusions to sink and float even though their Stokes velocity (their natural sedimentation speed) is extremely low.
  • the dwell time is, of course, related to the weight of castings produced and the number cast per unit time. For instance considering a relatively large Al alloy automotive cylinder block casting weighing 25 kg, it is easily shown that a furnace with a bath only 1 m wide, 100 mm deep and 3 m long would experience an average forward movement of the melt by 100 mm per casting, leading to a drop in surface level of 3 mm per casting. A casting every minute would give a dwell time of only 30 minutes. This is rather minimal, and is easily extended by a wider or longer bath. Less advantageously, the depth of the bath might be increased to an extent limited by the allowed ratios for effective operation.
  • the degassing of the melt is achieved without disturbance of the liquid metal.
  • the limited depth of the melt and its large area ensures that gas can diffuse out of the metal within the dwell time, provided the atmosphere above the melt is maintained free from hydrogen, or sources of hydrogen such as water vapor or hydrocarbon gases.
  • dry nitrogen, or possibly even dry air can be introduced above the melt.
  • the volume of air or other gas present in the holding furnace above the melt is the same as in conventional holding furnaces of a given size.
  • the dry gas can be introduced near the exit from the furnace.
  • the dry atmosphere therefore would travel beneficially in a counter-current direction to the flow of the liquid metal, and would be allowed to exit via the numerous natural leaks at the far end of the furnace.
  • the additional natural leaks from the sides of the furnace will reduce the overall efficiency somewhat, but the effect is insignificant provided the lid is sitting down on the walls of the body of the furnace with a reasonable sealing face; the joint possibly additionally sealed with lengths of refractory blanket or rope.
  • the holes for the heating elements will also benefit from sealing in a ‘rough and ready’ manner with refractory wool or similar sealing material.
  • the counter-current system is advantageous because the gas which enters at the end of the furnace where the melt is about to exit is the purest. Thus, despite leakage and contamination of the gas, as it flows toward the melt entrance in the holding furnace, the melt exiting the holding furnace is expected to be excellent.
  • the rate of flow of the gas in the holding furnace varies with the size of the holding furnace.
  • the rate of gas flow can be between about 2 to 6 liters per minute for a furnace which is 1 m wide 3 m long and 0.5 m high on the inside, above the melt.
  • molten metal into the holder can be accomplished by a dry hearth type melting furnace.
  • a dry hearth type melting furnace Such a furnace is conveniently fuel-fired, and attains a high melting efficiency by either (i) the use of twin recuperating burners so that charging can be carried out at floor level; or (ii) the furnace is a tower variety in which high thermal efficiency is achieved by conveying the spent gases from the melting burners up the stack, counter-current to the charge which descends as melting takes place.
  • Such furnaces deliver a high quality metal because the main oxide skins on the charge material (and any iron inserts such as cylinder liners etc) remain on the sloping dry hearth, and can be removed at intervals as necessary via a side door. (This benefit contrasts with induction and other crucible type furnaces, where the oxides on the surface of the charge materials and all remaining inserts are necessarily incorporated into the melt).
  • the melt from such furnaces is, however, at rather a low superheat.
  • an additional function of the holding furnace is to bring the melt temperature up to a casting temperature, and stabilize the melt at this temperature. This is easily achieved because of the large area and small depth of the melt.
  • the rate of delivery of metal can be adjusted to maintain the melt level in the furnace between close limits by controlling the rate of burning of fuel by the burners.
  • the rate can therefore be turned up or down at will.
  • the system is a ‘just-in-time’ or an ‘on-tap’ melt delivery system.
  • Metal delivery from the holding furnace can be envisioned to occur in a number of ways in which disturbance is minimized to the main body of the melt.
  • FIG. 1 is an example of a 3-Element interpretation of the current disclosure.
  • a melting furnace, element 1 preferably of a dry hearth type, is connected to a second element, a holding furnace of shallow depth and relatively large surface area 2 , preferably of a radiant roof type, that is in turn connected to the third element, constituting a pump well furnace 3 .
  • a pneumatic pump 4 of the type described in U.S. Pat. No. 6,103,182 dated 15 Aug. 2000.
  • the simple channel connections 5 and 6 between the three elements (which may or may not be three separate furnaces) are arranged to convey the liquid metal 7 at constant surface level 8 .
  • the dry hearth furnace may be of a conventional tower design requiring a lifting device, often a type of skip hoist design, to raise and load the charge materials into the top of the furnace.
  • the furnace may be of a horizontal design, employing twin regenerative burners, using air for combustion heated by the spent gases, to raise melting efficiency.
  • Charging is then carried out conveniently at floor level by fork lift truck via a door 11 , opened to admit the metal charge 12 .
  • the charge is then melted by heat from fuel burners or electrical elements (not shown) under a radiant roof 13 .
  • the melted metal runs down the sloping hearth 14 into the well 15 of the dry hearth furnace, or, possibly via the connecting channel 5 , directly into the holding furnace.
  • the significance of the choice of melting unit as a dry hearth furnace is that the oxide skins of the ingots or foundry returns (runners, risers and castings etc) are designed to be left on the dry hearth. Only the melted metal runs down the hearth and into the furnace well. The skins, dross, or even steel insert parts from mixed scrap, can be separated by raking off from the hearth at intervals via a side door. Thus only relatively clean metal is provided to the start of the melt supply.
  • the dry hearth furnace has the further benefit that it provides liquid metal on demand, can operate continuously, and the rate of delivery can be adjusted by control of the burners. Moreover, a dry hearth furnace has practically no moving parts and requires relatively little attention or maintenance.
  • the dry hearth furnace may have a well, forming a reservoir in which gentle mixing under a tranquil surface is encouraged to provide a smoothing of chemical changes as charges to the furnace are changed, or as the melt rate changes.
  • the well region of the furnace allows a second burner or other heater to be sited to raise the temperature of the melt, since the metal drains from the dry hearth practically at its melting point.
  • a second burner or other heater to be sited to raise the temperature of the melt, since the metal drains from the dry hearth practically at its melting point.
  • at least 50 to 150 C superheat the temperature above the melting point
  • most of the superheat will require to be made up by the second burner or other heater in the melting furnace (the final adjustments to temperature can, of course, be made later in the holding furnace, or even in the pump well itself.
  • the quiescent transfer of molten metal from the melting furnace to the holding furnace is achieved if the two units are in good hydrostatic communication and so have substantially identical liquid levels. In such a situation the melt travels with extreme gentleness from one to the other.
  • any other conventional type of furnace could be used instead, such as the recently developed electrical resistance immersion heated furnaces, or even a crucible melter.
  • the liquid metal need not be melted in the foundry. It could be supplied direct from a smelter possibly many miles away and transported to the foundry by road or rail in a specially insulated container, as is well known in the industry.
  • the liquid metal can be off-loaded and stored at the foundry in the special container, or transferred into a second holding furnace. From such a container or second holding furnace, the molten metal could be subsequently transferred at a controlled rate to the holding furnace so as to substantially retain constant melt level, such as by a snorkel ladle.
  • a snorkel ladle such an embodiment will be described hereinbelow.
  • the melt 15 may exit the melting furnace via a filter 16 which may be of any suitable type such as the ceramic foam or bonded particle types. Alternatively, if used at all, a filter may be placed in the entrance to the holding furnace 2 .
  • the dry hearth furnace well and the holding furnace are connected via a simple ceramic channel 5 (although other connections such as a ceramic tube can be envisaged to work equally well). Such connections necessarily require the normal attention to detail including good thermal insulation, and reasonable exclusion of air by suitable heated or insulated cover. Alternatively, of course, the furnaces may be effectively integrated to avoid any necessity for a separate link.
  • the melt then enters the holding furnace.
  • That furnace is an important element of the melt handling concept.
  • This furnace comprises a base part 21 that contains a shallow bath of liquid metal, and a roof 22 that contains the heating elements.
  • the source of heating can be electrical resistance elements or tubular gas radiant elements and the mechanism of heat transfer to the melt is radiation, as is normal for a reverbatory type furnace.
  • the large area and shallow depth of the melt in this element acts beneficially in a number of ways:
  • the large area acts as a reservoir and buffer to smooth temporary imbalances between the melt supply and demand, maintaining a substantially constant level
  • inclusions are given the time to encourage separation by a sink or float process because the aspect ratio (width/depth) of the furnace effectively suppresses convective stirring driven mainly by the cooling from sidewalls since the effect of sidewalls is reduced to insignificance in this design of furnace;
  • iv. hydrogen is allowed to equilibrate with the dry atmosphere above the melt that is constantly replenished while the hydrogen-contaminated spent gas is constantly removed.
  • This degassing technique avoids the turbulent techniques commonly employed throughout the industry such as purging with bubbles from immersed lances or rotary degassing machines. Such turbulent degassing techniques can cause damage to the melt, leading to variable melt quality.
  • the shallow depth of the furnace is calculated to allow the majority of hydrogen time to diffuse to the surface, and so escape into the atmosphere that is being continuously replenished with a hydrogen-free and moisture-free atmosphere.
  • the shallow bath is easy to clean, and contrasts with deep baths that sometimes are found to be impossible to clean because of oxide material which can remain out of sight for long periods and becomes fused to the furnace lining.
  • liquid metal inventory is unusually low for a high production casting system.
  • Liquid metal inventories are often in the region of 10 to 50 tonnes of liquid metal, so that an alloy change can rarely if ever be contemplated.
  • Liquid metal inventories according to the current disclosure are expected to be in the region of 0.5 tonnes making maintenance or alloy changes easier.
  • the liquid metal in the holding furnace 2 can connect to a pump well in a separate casting unit via a launder channel 6 .
  • the pump well requires sufficient depth to accommodate the pump 4 , plus any box type filter unit 32 that may surround or be inserted under the pump.
  • the furnace usually includes a steel shell 33 with an insulating lining 34 , which, in turn, contains a conventional silicon carbide or graphite based crucible 31 .
  • the heating source surrounding the crucible may be gas or electric. However, electrical resistance heating is normally to be preferred at this point in the line because waste gas ducts above the furnace are thereby avoided, and would otherwise complicate the siting and operation of a casting station. Also, the permeability of the crucible to hydrogen means that the hydrogen in solution in the melt is probably kept lower by avoiding gas heating, with its accompanying load of water vapor as products of combustion.
  • the crucible is held in place on its ceramic stool 37 with a cover assembly 35 and the whole covered by a lid 36 to retain heat and exclude moist air.
  • the pump itself 4 can be of the type described in U.S. Pat. No. 6,103,182 which is incorporated by reference hereinto in its entirety.
  • This design of liquid metal pump has the capability of totally quiescent operation: it has an intake (not shown) for liquid metal beneath the surface of the liquid, transfers the liquid into the mold via a riser tube 41 , and at a rate which can be precisely controlled by the application of gas pressure into the body of the pump.
  • the small volumes of gas and liquid involved ensure that the precision of control is excellent.
  • Such pumps whether pneumatic or electromagnetic, work with better repeatability if the melt level is constant, so that in this case such devices have optimum working conditions.
  • the crucible furnace has its own source of heat, so that last minute adjustments to the casting temperature can be made.
  • the generous (more than adequate) heating facility is far preferable to the usual geometry of a charge well as an extension to a normal electrically heated reverbatory furnace as outlined above.
  • the liquid can be held close to the open top of the riser tube 41 .
  • the fall of liquid acts to stir the metal inside the pressure vessel, thus stirring up once again inclusions that have taken time to settle to the bottom of the vessel.
  • the fall of the liquid uncovers the inner surface of the riser tube, allowing the formation of a skin of oxide that can be incorporated into the melt during the next time the melt ascends the tube for the filling of the next mold.
  • maintaining the riser tube continuously full of liquid metal not only saves a second or so off the filling time, but more importantly retains the excellent defect-free quality of the melt for each casting.
  • connection between the elements of the melt line are made by simple known techniques, for instance by the use of proprietary preformed ceramic launder (channel) sections or ceramic tubes as has been mentioned above.
  • Good hydrostatic communication between the melting furnace, holding furnace, and casting station ensures substantially similar levels between the melter, holder and casting station, with the result that the transfer of the melt between the units occurs only with extreme gentleness, without turbulence.
  • Some difference in level is expected to build up as filters become blocked, but the essential feature of the gentle transfer of the liquid is not thereby threatened, as will be evident to any who have worked with in-line filtration as part of a melt supply system.
  • a filter possibly of a ceramic foam type, may be placed at the exit from the melting unit to keep back some of the larger inclusions. The filter will need to be replaced from time to time.
  • a box filter of well-known form may be placed around the pump, or a ceramic foam filter may be sited underneath, to provide a final filtering operation.
  • a melting furnace, element 110 preferably of a dry hearth type, is connected to a second element, a holding furnace of shallow depth and relatively large surface area 120 , preferably of a radiant roof type.
  • the simple channel connections 150 between the two elements are arranged to convey the liquid metal 170 at constant surface level 180 .
  • a door 111 is opened to admit a metal charge 112 that is then melted by heat from fuel burners or electrical heating elements (not shown) under a radiant roof 113 .
  • the melted metal runs down the sloping hearth 114 .
  • No well at the exit of the dry hearth is proposed for this system. This reduces the total inventory of liquid metal in the system, so facilitating alloy changes.
  • the dry hearth melting furnace therefore delivers metal direct, via the connecting launder or tube 150 if any, into the holding furnace 120 .
  • the melt enters the holding furnace.
  • this furnace comprises a base part 121 that contains a shallow bath of liquid metal, and a roof 122 which contains the heating elements.
  • the source of heating is some dry system such as electrical resistance and the mechanism of heat transfer to the melt is radiation, as is normal for a reverbatory type furnace.
  • a tip 218 of a conventional snorkel ladle 220 Close to the delivery end of the holding furnace the melt is extracted via a tip 218 of a conventional snorkel ladle 220 . Very little, if any, extra depth is required-for the melt at the point at which the tip of the ladle samples the melt.
  • a ladle is dry and preheated. It sucks up the liquid metal from the furnace, filling a reservoir 222 constituted by the upper part of the ladle. When full, a stopper (not visible) of the snorkel ladle is closed.
  • the ladle is withdrawn from the holding furnace and is transferred to a casting station 230 via a conventional mechanism 240 operating on an overhead rail 242 .
  • the snorkel ladle's delivery tube is lowered into the mold, the snorkel stopper is raised, and the contents of the snorkel ladle are transferred into the mold.
  • a load cell 244 may be provided on a support cable 246 of the ladle 220 to gauge the weight of molten metal held by the ladle.
  • two apertures 252 and 256 are shown as extending through the roof 122 of the holding furnace 120 .
  • the aperture 256 spaced further from the melting furnace 110 , is used to charge the snorkel ladle 220 .
  • the aperture 252 near the melting furnace 110 is used simply to return back into the holding furnace 120 any molten metal remaining in the snorkel ladle 220 after it has discharged the molten metal at the casting station 230 .
  • This is illustrated with the snorkel ladle in dashed outline in FIG. 2 . It should be appreciated that more than one snorkel may be needed for the embodiment of FIG. 2 .
  • the long snout of the snorkel can be lowered deeply into a mold, engaging with the base of the running system for the casting, so that the casting fills from the bottom upwards thus avoiding the falling of the metal with the danger of the entrainment of oxide defects inside the mold.
  • a snorkel 340 can be envisioned to be a permanent fixture to a delivery end of a holding furnace 320 connected to a melting furnace 310 .
  • molds can be brought to the holding furnace and offered up to the snorkel.
  • the snorkel can operate so as to deliver clean melt directly into the base of molds, so that the mold can fill in a counter-gravity mode.
  • FIG. 4 shows a further embodiment of the disclosure.
  • a snorkel ladle 450 is used to transport liquid metal from some outside source, and fill a quiescent transfer furnace 420 in a controlled manner.
  • the outside source could be at a location miles away from the holding furnace.
  • Another snorkel 440 can be a permanent fixture at a delivery end of the holding furnace. It can deliver clean melt directly into a base of a mold 470 .
  • the transport snorkel 450 is advantageous for adding new melt under the liquid surface and at a controlled rate so as to create minimal disturbance to the surface of the melt.
  • FIG. 5 illustrates an embodiment of the invention. Delivery from a holding furnace 520 is again via a snorkel 540 fixed in the base of the furnace. However, a heated refractory U tube arrangement 550 allows the counter-gravity filling of molds, similar to a known arrangement previously described in 1974 in U.S. Pat. No. 3,828,974. This patent provides a description of details of safety aspects of design that would be desirably included. The disclosure of this patent is incorporated herein, in its entirety
  • a known device a slide gate (not shown), affixed to the base of a mold 570 , operates at the junction between the orifice from the U tube and the mold.
  • a snorkel stopper 544 is opened to fill the mold. When the mold is full the slide gate is closed, and the snorkel stopper 544 is closed. The mold can then be lifted clear and a new mold with an open slide gate can be planted on the melt delivery point.
  • FIG. 6 shows a schematic plan view of a holding furnace 620 according to another embodiment of the present disclosure.
  • molten metal enters near the point marked with an arrow 630 .
  • the furnace is shown with a site 636 for a fixed snorkel.
  • Filters 650 in the form of ceramic filter blocks, are shown placed in the bath. Their purpose is not primarily filtration. In operation the holder will gradually fill with settled-out debris of nearly neutral buoyancy. Thus this effectively floatable material will travel with the melt rather than sitting firmly on the base of the furnace. It will build up to become a slurry of sundry debris. This porridge-like sludge will, if not restrained, travel as a body along the furnace. The purpose of the semi-circle of ceramic filter blocks 650 is to restrain this movement, holding the debris in place. Clearly, this role could easily be undertaken by a sintered ceramic particle box filter or other suitable device (or groups of such filters or devices) for holding back this slurry. In addition, of course, it may be found advantageous for the attainment of certain qualities of melt in certain alloys to introduce multiple such barriers.
  • FIG. 4 two such spaced barriers, or sets of barriers, 660 and 670 are shown.
  • FIG. 5 one such barrier or set of barriers 680 is shown.
  • the main inclusion separation mechanism is sedimentation.
  • the debris itself will build up its own filtration efficiency as it accumulates in depth, and only become too efficient when the melt cannot pass through it sufficiently quickly to re-fill the region of the furnace above the snorkel outlet prior to the next casting. At this point the rate of production will have to be slowed, forcing a cleaning operation for the holder.
  • the holder may benefit from additional barriers to the flow of debris.
  • additional arrays of heavy filter blocks (not shown) or other barriers to hold back the general flow of settled-out debris can be envisioned.
  • FIG. 7 another holding furnace 720 according to the present disclosure is there illustrated.
  • the holding furnace is provided with an inlet opening 722 on a first end thereof and an outlet opening 724 on a second end thereof.
  • the holding furnace includes a floor 730 and a set of upward steps 732 - 738 therein.
  • the melt 740 is at a level to cover all the upward steps.
  • the space in the holding furnace 720 above the melt is indicated by numeral 750 .
  • Each upward step perhaps only 10 mm high, would help to restrain the general movement of the whole mass.
  • the bifilms will have time to open in this quiescent environment, thus impinging and interlocking to form, macroscopically, a kind of fairly solid cake or gel.
  • relatively isolated points for pinning movement would tend to act on the whole mass because of its degree of integrity. It is believed that the up-steps would not interfere unduly with the raking out of the debris from the metal entrance end when the furnace will require its routine cleaning.
  • the holding furnace 720 is provided with a gas inlet 752 through which a dry gas atmosphere flows into the holding furnace, as illustrated by arrow 754 .
  • the dry atmosphere or gas allows hydrogen in the melt to equilibrate with the dry atmosphere being replenished into the holding furnace via inlet 752 .
  • An outlet for the dry atmosphere is shown at outlet port 756 through which the gas, which has now picked up hydrogen, flows outwardly as shown by arrow 758 .
  • a counter current flow of the dry atmosphere takes place such that the cleanest gas, i.e., a gas which has not yet picked up any hydrogen, flows into the holding furnace via the inlet port for gas 754 adjacent the outlet port 724 for liquid metal.
  • melt exiting the holding furnace This allows the melt exiting the holding furnace to be of the best quality.
  • Gas which has picked up hydrogen from the melt flows away from the outlet port 724 for metal, in the holding furnace, and towards the outlet port for gas 758 adjacent to the inlet port for metal 722 thereof.
  • the heaters can be radiant electric heaters of a conventional design.
  • any type of dry heating means i.e., any method of heating which does not involve burning a flame of combustible gas above the surface of the melt so that the products of combustion are exposed to the melt
  • any type of dry heating means i.e., any method of heating which does not involve burning a flame of combustible gas above the surface of the melt so that the products of combustion are exposed to the melt
  • the manufacturing technique and system combines a number of components in a novel manner to achieve the quiescent transfer of melts, leading to unique advantages in the properties of the cast product.
  • the method and apparatus employs a holding furnace from which all disturbances are designed to be suppressed, encouraging the sedimentation of inclusions, and achieving the simultaneous degassing of the melt, thus achieving liquid metal of high quality.
  • This high quality is maintained into the cast product only if the melting and holding system described above is linked to a suitably quiescent system for transferring melt out of the furnace directly into a mold or into a transfer system that delivers to a mold.
  • the usual manner of filling a holder is simply by pouring in fresh liquid metal.
  • Such trauma completely disturbs the whole melt, stirring sedimented inclusions back into suspension, and entraining new inclusions since all pouring actions involve much folding-in of the surface oxide.
  • the operation of the melt system proposed in the current application is with minimal stirring or upsetting of the molten material at any stage of the progress of the melt, during its melting, temperature adjustment, cleaning, degassing and casting.
  • a quiescent transfer casting line can include a melting furnace 1 , 110 which transforms solid metal into a melt. The melt is then transferred to a holding furnace 2 , 120 , 320 - 720 .
  • a first channel 5 , 150 can communicate the holding furnace with the melting furnace.
  • the holding furnace can be connected to a pump furnace 3 .
  • a second channel 6 can communicate the holding furnace with the pump furnace.
  • a snorkel ladle 220 can be used both to withdraw and to dispense melt from the holding furnace.
  • the holding furnace 2 , 120 , 320 - 720 has a relatively large surface area and a relatively shallow depth, having a width to depth ratio in the range of 4-100 to 1.
  • a method employing such a casting line encourages the cleaning of the melt by the detrainment of non-metallic inclusions and avoids the re-entrainment of surface oxides into the body of the melt, in addition to achieving a degassing action and adjusting the temperature of the casting as required.
  • the technique proposed herein is designed to achieve filling, transfers out or dosing to a casting unit or mold, degassing, and effective filtration. All this occurs without moving parts, except for one or more stoppers that move only relatively slowly through a relatively few millimeters vertically through the local melt surface, so as to disturb the surface only insignificantly.
US11/710,452 2007-02-23 2007-02-23 Quiescent transfer of melts Abandoned US20080202644A1 (en)

Priority Applications (3)

Application Number Priority Date Filing Date Title
US11/710,452 US20080202644A1 (en) 2007-02-23 2007-02-23 Quiescent transfer of melts
PCT/US2008/002279 WO2008103402A2 (fr) 2007-02-23 2008-02-21 Transfert de masses fondues au repos
US12/578,195 US8303890B2 (en) 2007-02-23 2009-10-13 Integrated quiescent processing of melts

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US11/710,452 US20080202644A1 (en) 2007-02-23 2007-02-23 Quiescent transfer of melts

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US12/578,195 Continuation-In-Part US8303890B2 (en) 2007-02-23 2009-10-13 Integrated quiescent processing of melts

Publications (1)

Publication Number Publication Date
US20080202644A1 true US20080202644A1 (en) 2008-08-28

Family

ID=39434275

Family Applications (1)

Application Number Title Priority Date Filing Date
US11/710,452 Abandoned US20080202644A1 (en) 2007-02-23 2007-02-23 Quiescent transfer of melts

Country Status (2)

Country Link
US (1) US20080202644A1 (fr)
WO (1) WO2008103402A2 (fr)

Cited By (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102010006229B3 (de) * 2010-01-28 2011-05-05 Sms Meer Gmbh Druckofen und Verfahren zum kontinuierlichen Betrieb eines Druckofens
US20120160092A1 (en) * 2010-12-22 2012-06-28 GM Global Technology Operations LLC Method of making a piston oil gallery using a hollow metallic core
US20130294901A1 (en) * 2012-05-01 2013-11-07 Sergey Mironets Metal powder casting
US9051623B2 (en) * 2012-05-29 2015-06-09 Gors Ltd. Apparatus for melting a solid metal
US20160320130A1 (en) * 2007-06-21 2016-11-03 Molten Metal Equipment Innovations, Llc Vessel transfer insert and system
CN107052303A (zh) * 2016-12-11 2017-08-18 贵阳煜兴车轮制造有限公司 一种铝合金熔炼大炉
CN107321961A (zh) * 2017-07-27 2017-11-07 福建省瑞奥麦特轻金属有限责任公司 一种坩埚炉式加压凝固铝合金薄壁铸件半固态成型机
CN107460342A (zh) * 2016-06-02 2017-12-12 百色学院 一种实验室用净化铝液熔炼炉
US9862026B2 (en) 2007-06-21 2018-01-09 Molten Metal Equipment Innovations, Llc Method of forming transfer well
US9903383B2 (en) 2013-03-13 2018-02-27 Molten Metal Equipment Innovations, Llc Molten metal rotor with hardened top
US9909808B2 (en) 2007-06-21 2018-03-06 Molten Metal Equipment Innovations, Llc System and method for degassing molten metal
US9982945B2 (en) 2007-06-21 2018-05-29 Molten Metal Equipment Innovations, Llc Molten metal transfer vessel and method of construction
US10052688B2 (en) 2013-03-15 2018-08-21 Molten Metal Equipment Innovations, Llc Transfer pump launder system
US10072891B2 (en) 2007-06-21 2018-09-11 Molten Metal Equipment Innovations, Llc Transferring molten metal using non-gravity assist launder
US10126059B2 (en) 2013-03-14 2018-11-13 Molten Metal Equipment Innovations, Llc Controlled molten metal flow from transfer vessel
US10138892B2 (en) 2014-07-02 2018-11-27 Molten Metal Equipment Innovations, Llc Rotor and rotor shaft for molten metal
US10195664B2 (en) 2007-06-21 2019-02-05 Molten Metal Equipment Innovations, Llc Multi-stage impeller for molten metal
US10267314B2 (en) 2016-01-13 2019-04-23 Molten Metal Equipment Innovations, Llc Tensioned support shaft and other molten metal devices
US10309725B2 (en) 2009-09-09 2019-06-04 Molten Metal Equipment Innovations, Llc Immersion heater for molten metal
US10428821B2 (en) 2009-08-07 2019-10-01 Molten Metal Equipment Innovations, Llc Quick submergence molten metal pump
US10570745B2 (en) 2009-08-07 2020-02-25 Molten Metal Equipment Innovations, Llc Rotary degassers and components therefor
WO2020254823A1 (fr) * 2019-06-20 2020-12-24 Sylatech Limited Appareil et procédé destinés à être utilisés pour la coulée de métaux et/ou d'alliages métalliques
US10947980B2 (en) 2015-02-02 2021-03-16 Molten Metal Equipment Innovations, Llc Molten metal rotor with hardened blade tips
US11149747B2 (en) 2017-11-17 2021-10-19 Molten Metal Equipment Innovations, Llc Tensioned support post and other molten metal devices
US11358217B2 (en) 2019-05-17 2022-06-14 Molten Metal Equipment Innovations, Llc Method for melting solid metal
CN114703410A (zh) * 2022-03-21 2022-07-05 江苏华企铝业科技股份有限公司 一种高强耐腐蚀铝锂合金型材及其制备方法
US11873845B2 (en) 2021-05-28 2024-01-16 Molten Metal Equipment Innovations, Llc Molten metal transfer device

Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2068924A (en) * 1932-12-02 1937-01-26 Hartford Empire Co Regenerator tank and method of operating the same
US3809379A (en) * 1970-04-21 1974-05-07 Alsacienne Atom Installation for the treatment and movement of liquid metals
US3890139A (en) * 1972-05-04 1975-06-17 Mitsubishi Kizoku Kabushiki Ka Continuous process for refining sulfide ores
US4002468A (en) * 1975-04-28 1977-01-11 Swiss Aluminium Ltd. Scrap smelting process
US4850577A (en) * 1988-06-15 1989-07-25 Kabushiki Kaisha Daiki Aluminum Kogyosho Melting and holding furnace
US4881670A (en) * 1988-07-01 1989-11-21 Kabushiki Kaisha Daiki Aluminium Kogyosho Automatic melt supplying method and holding furnace having automatic melt supplying system
US4967827A (en) * 1982-05-20 1990-11-06 Cosworth Research And Development Limited Method and apparatus for melting and casting metal
US4974817A (en) * 1989-05-29 1990-12-04 Meichuseiki Kabushiki Kaisha Metal melting and holding furnace
US4990059A (en) * 1988-12-19 1991-02-05 Aluminum Company Of America Method for filtering liquid-phase metals
US5662859A (en) * 1995-04-26 1997-09-02 Toshiba Kikai Kabushiki Kaisha Constant molten metal surface level retaining furnace integrally provided with melting unit
US5725043A (en) * 1993-07-02 1998-03-10 Frank W. Schaefer, Inc. Low pressure casting process and apparatus
US5741514A (en) * 1995-08-31 1998-04-21 Yissum Research Development Company Of The Hebrew University Of Jerusalem Method for reducing serum lipoprotein(a) concentration
US6103182A (en) * 1998-06-27 2000-08-15 Alotech, Inc. Dispensing apparatus and method

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE486525C (de) * 1929-11-22 Ver Aluminium Werke Akt Ges Verfahren zum Entgasen von Leichtmetallen, insbesondere von Aluminium und Aluminiumlegierungen
IT1204642B (it) * 1987-05-19 1989-03-10 Aluminia Spa Apparecchiatura per il trattamento di degasaggio e di filtrazione in linea dell'alluminio e sue leghe
US4861001A (en) * 1987-07-21 1989-08-29 Retech, Inc. Melting retort and method of melting materials
US5700422A (en) * 1995-04-14 1997-12-23 Ryobi Ltd. Molten metal supply device
ATE465379T1 (de) * 2005-08-11 2010-05-15 Aluar Aluminio Argentino S A I Übergabesystem für flüssige metalle

Patent Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2068924A (en) * 1932-12-02 1937-01-26 Hartford Empire Co Regenerator tank and method of operating the same
US3809379A (en) * 1970-04-21 1974-05-07 Alsacienne Atom Installation for the treatment and movement of liquid metals
US3890139A (en) * 1972-05-04 1975-06-17 Mitsubishi Kizoku Kabushiki Ka Continuous process for refining sulfide ores
US4002468A (en) * 1975-04-28 1977-01-11 Swiss Aluminium Ltd. Scrap smelting process
US4967827A (en) * 1982-05-20 1990-11-06 Cosworth Research And Development Limited Method and apparatus for melting and casting metal
US4850577A (en) * 1988-06-15 1989-07-25 Kabushiki Kaisha Daiki Aluminum Kogyosho Melting and holding furnace
US4881670A (en) * 1988-07-01 1989-11-21 Kabushiki Kaisha Daiki Aluminium Kogyosho Automatic melt supplying method and holding furnace having automatic melt supplying system
US4990059A (en) * 1988-12-19 1991-02-05 Aluminum Company Of America Method for filtering liquid-phase metals
US4974817A (en) * 1989-05-29 1990-12-04 Meichuseiki Kabushiki Kaisha Metal melting and holding furnace
US5725043A (en) * 1993-07-02 1998-03-10 Frank W. Schaefer, Inc. Low pressure casting process and apparatus
US5662859A (en) * 1995-04-26 1997-09-02 Toshiba Kikai Kabushiki Kaisha Constant molten metal surface level retaining furnace integrally provided with melting unit
US5741514A (en) * 1995-08-31 1998-04-21 Yissum Research Development Company Of The Hebrew University Of Jerusalem Method for reducing serum lipoprotein(a) concentration
US6103182A (en) * 1998-06-27 2000-08-15 Alotech, Inc. Dispensing apparatus and method

Cited By (63)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11167345B2 (en) 2007-06-21 2021-11-09 Molten Metal Equipment Innovations, Llc Transfer system with dual-flow rotor
US9982945B2 (en) 2007-06-21 2018-05-29 Molten Metal Equipment Innovations, Llc Molten metal transfer vessel and method of construction
US10458708B2 (en) 2007-06-21 2019-10-29 Molten Metal Equipment Innovations, Llc Transferring molten metal from one structure to another
US10562097B2 (en) 2007-06-21 2020-02-18 Molten Metal Equipment Innovations, Llc Molten metal transfer system and rotor
US10072891B2 (en) 2007-06-21 2018-09-11 Molten Metal Equipment Innovations, Llc Transferring molten metal using non-gravity assist launder
US10352620B2 (en) 2007-06-21 2019-07-16 Molten Metal Equipment Innovations, Llc Transferring molten metal from one structure to another
US20160320130A1 (en) * 2007-06-21 2016-11-03 Molten Metal Equipment Innovations, Llc Vessel transfer insert and system
US11759854B2 (en) 2007-06-21 2023-09-19 Molten Metal Equipment Innovations, Llc Molten metal transfer structure and method
US10274256B2 (en) 2007-06-21 2019-04-30 Molten Metal Equipment Innovations, Llc Vessel transfer systems and devices
US11185916B2 (en) 2007-06-21 2021-11-30 Molten Metal Equipment Innovations, Llc Molten metal transfer vessel with pump
US9862026B2 (en) 2007-06-21 2018-01-09 Molten Metal Equipment Innovations, Llc Method of forming transfer well
US11020798B2 (en) 2007-06-21 2021-06-01 Molten Metal Equipment Innovations, Llc Method of transferring molten metal
US9909808B2 (en) 2007-06-21 2018-03-06 Molten Metal Equipment Innovations, Llc System and method for degassing molten metal
US10345045B2 (en) 2007-06-21 2019-07-09 Molten Metal Equipment Innovations, Llc Vessel transfer insert and system
US10195664B2 (en) 2007-06-21 2019-02-05 Molten Metal Equipment Innovations, Llc Multi-stage impeller for molten metal
US11103920B2 (en) 2007-06-21 2021-08-31 Molten Metal Equipment Innovations, Llc Transfer structure with molten metal pump support
US11130173B2 (en) 2007-06-21 2021-09-28 Molten Metal Equipment Innovations, LLC. Transfer vessel with dividing wall
US10428821B2 (en) 2009-08-07 2019-10-01 Molten Metal Equipment Innovations, Llc Quick submergence molten metal pump
US10570745B2 (en) 2009-08-07 2020-02-25 Molten Metal Equipment Innovations, Llc Rotary degassers and components therefor
US10309725B2 (en) 2009-09-09 2019-06-04 Molten Metal Equipment Innovations, Llc Immersion heater for molten metal
DE102010006229B3 (de) * 2010-01-28 2011-05-05 Sms Meer Gmbh Druckofen und Verfahren zum kontinuierlichen Betrieb eines Druckofens
US20120160092A1 (en) * 2010-12-22 2012-06-28 GM Global Technology Operations LLC Method of making a piston oil gallery using a hollow metallic core
US8863381B2 (en) * 2010-12-22 2014-10-21 GM Global Technology Operations LLC Method of making a piston oil gallery using a hollow metallic core
US20130294901A1 (en) * 2012-05-01 2013-11-07 Sergey Mironets Metal powder casting
US9475118B2 (en) * 2012-05-01 2016-10-25 United Technologies Corporation Metal powder casting
US9051623B2 (en) * 2012-05-29 2015-06-09 Gors Ltd. Apparatus for melting a solid metal
US11391293B2 (en) 2013-03-13 2022-07-19 Molten Metal Equipment Innovations, Llc Molten metal rotor with hardened top
US10641279B2 (en) 2013-03-13 2020-05-05 Molten Metal Equipment Innovations, Llc Molten metal rotor with hardened tip
US9903383B2 (en) 2013-03-13 2018-02-27 Molten Metal Equipment Innovations, Llc Molten metal rotor with hardened top
US10126059B2 (en) 2013-03-14 2018-11-13 Molten Metal Equipment Innovations, Llc Controlled molten metal flow from transfer vessel
US10126058B2 (en) 2013-03-14 2018-11-13 Molten Metal Equipment Innovations, Llc Molten metal transferring vessel
US10302361B2 (en) 2013-03-14 2019-05-28 Molten Metal Equipment Innovations, Llc Transfer vessel for molten metal pumping device
US10322451B2 (en) 2013-03-15 2019-06-18 Molten Metal Equipment Innovations, Llc Transfer pump launder system
US10307821B2 (en) 2013-03-15 2019-06-04 Molten Metal Equipment Innovations, Llc Transfer pump launder system
US10052688B2 (en) 2013-03-15 2018-08-21 Molten Metal Equipment Innovations, Llc Transfer pump launder system
US11286939B2 (en) 2014-07-02 2022-03-29 Molten Metal Equipment Innovations, Llc Rotor and rotor shaft for molten metal
US11939994B2 (en) 2014-07-02 2024-03-26 Molten Metal Equipment Innovations, Llc Rotor and rotor shaft for molten metal
US10465688B2 (en) 2014-07-02 2019-11-05 Molten Metal Equipment Innovations, Llc Coupling and rotor shaft for molten metal devices
US10138892B2 (en) 2014-07-02 2018-11-27 Molten Metal Equipment Innovations, Llc Rotor and rotor shaft for molten metal
US10947980B2 (en) 2015-02-02 2021-03-16 Molten Metal Equipment Innovations, Llc Molten metal rotor with hardened blade tips
US11933324B2 (en) 2015-02-02 2024-03-19 Molten Metal Equipment Innovations, Llc Molten metal rotor with hardened blade tips
US11519414B2 (en) 2016-01-13 2022-12-06 Molten Metal Equipment Innovations, Llc Tensioned rotor shaft for molten metal
US10641270B2 (en) 2016-01-13 2020-05-05 Molten Metal Equipment Innovations, Llc Tensioned support shaft and other molten metal devices
US11098720B2 (en) 2016-01-13 2021-08-24 Molten Metal Equipment Innovations, Llc Tensioned rotor shaft for molten metal
US11098719B2 (en) 2016-01-13 2021-08-24 Molten Metal Equipment Innovations, Llc Tensioned support shaft and other molten metal devices
US10267314B2 (en) 2016-01-13 2019-04-23 Molten Metal Equipment Innovations, Llc Tensioned support shaft and other molten metal devices
CN107460342A (zh) * 2016-06-02 2017-12-12 百色学院 一种实验室用净化铝液熔炼炉
CN107052303A (zh) * 2016-12-11 2017-08-18 贵阳煜兴车轮制造有限公司 一种铝合金熔炼大炉
CN107321961A (zh) * 2017-07-27 2017-11-07 福建省瑞奥麦特轻金属有限责任公司 一种坩埚炉式加压凝固铝合金薄壁铸件半固态成型机
US11149747B2 (en) 2017-11-17 2021-10-19 Molten Metal Equipment Innovations, Llc Tensioned support post and other molten metal devices
US11976672B2 (en) 2017-11-17 2024-05-07 Molten Metal Equipment Innovations, Llc Tensioned support post and other molten metal devices
US11358217B2 (en) 2019-05-17 2022-06-14 Molten Metal Equipment Innovations, Llc Method for melting solid metal
US11759853B2 (en) 2019-05-17 2023-09-19 Molten Metal Equipment Innovations, Llc Melting metal on a raised surface
US11471938B2 (en) 2019-05-17 2022-10-18 Molten Metal Equipment Innovations, Llc Smart molten metal pump
US11850657B2 (en) 2019-05-17 2023-12-26 Molten Metal Equipment Innovations, Llc System for melting solid metal
US11858037B2 (en) 2019-05-17 2024-01-02 Molten Metal Equipment Innovations, Llc Smart molten metal pump
US11858036B2 (en) 2019-05-17 2024-01-02 Molten Metal Equipment Innovations, Llc System and method to feed mold with molten metal
US11931803B2 (en) 2019-05-17 2024-03-19 Molten Metal Equipment Innovations, Llc Molten metal transfer system and method
US11931802B2 (en) 2019-05-17 2024-03-19 Molten Metal Equipment Innovations, Llc Molten metal controlled flow launder
US11358216B2 (en) 2019-05-17 2022-06-14 Molten Metal Equipment Innovations, Llc System for melting solid metal
WO2020254823A1 (fr) * 2019-06-20 2020-12-24 Sylatech Limited Appareil et procédé destinés à être utilisés pour la coulée de métaux et/ou d'alliages métalliques
US11873845B2 (en) 2021-05-28 2024-01-16 Molten Metal Equipment Innovations, Llc Molten metal transfer device
CN114703410A (zh) * 2022-03-21 2022-07-05 江苏华企铝业科技股份有限公司 一种高强耐腐蚀铝锂合金型材及其制备方法

Also Published As

Publication number Publication date
WO2008103402A3 (fr) 2008-10-16
WO2008103402A2 (fr) 2008-08-28

Similar Documents

Publication Publication Date Title
US20080202644A1 (en) Quiescent transfer of melts
EP0095645B1 (fr) Procédé et dispositif de fusion et coulée de métal
US6503292B2 (en) Molten metal treatment furnace with level control and method
US9724753B2 (en) System and method for injecting semisolid aluminum into a mould
US6500228B1 (en) Molten metal dosing furnace with metal treatment and level control and method
KR101279447B1 (ko) 강철 제품의 제조를 위한 융통성이 있는 최소 에너지 이용 전기 아크 시스템 및 방법
CN201239793Y (zh) 改进的铁水浇注包
CN105149552A (zh) 分体式熔铸一体化设备
US8303890B2 (en) Integrated quiescent processing of melts
US20220305548A1 (en) Apparatus And Method For Use In Casting Of Metals And/Or Metal Alloys
CN104249149B (zh) 一种通道式感应加热中间包及其浇铸方法
US3610600A (en) Continuously operable plant for degassing and pouring metal melts
CN112828264A (zh) 一种带螺旋磁场的铸造装置和铸造方法
MXPA04012573A (es) Aparato y metodo de surtido.
US5996677A (en) Method and apparatus for supplying molten metal
JP2019162648A (ja) 溶湯補給装置及び溶湯補給方法
US3145095A (en) Method and apparatus for continuously tapping and degassing molten metal into ingot molds
GB2103132A (en) A method and apparatus for low pressure casting of metals
US5620043A (en) Transferring molten metal for low pressure casting
KR101385008B1 (ko) 주조 장치, 및 용융 물질을 주조 몰드로의 이송 방법
JPS58125358A (ja) 溶湯鍛造装置
US4014529A (en) Device for vacuum-refining of molten metal
CN104117662A (zh) 镍及镍合金真空熔炼水平连铸封闭式中间包
RU2728142C1 (ru) Плавильно-заливочный тигель с автоматическим выпуском расплава через канал сифонного типа
JPH0350619B2 (fr)

Legal Events

Date Code Title Description
AS Assignment

Owner name: ALOTECH LTD. LLC, GEORGIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:CAMPBELL, JOHN;REEL/FRAME:019043/0390

Effective date: 20070216

Owner name: ALOTECH LTD. LLC,GEORGIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:CAMPBELL, JOHN;REEL/FRAME:019043/0390

Effective date: 20070216

AS Assignment

Owner name: ALOTECH LTD. LLC, GEORGIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:GRASSI, JOHN R.;REEL/FRAME:019418/0399

Effective date: 20070601

Owner name: ALOTECH LTD. LLC,GEORGIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:GRASSI, JOHN R.;REEL/FRAME:019418/0399

Effective date: 20070601

STCB Information on status: application discontinuation

Free format text: EXPRESSLY ABANDONED -- DURING EXAMINATION