US20070015043A1 - Fuel cell having metalized gas diffusion layer - Google Patents
Fuel cell having metalized gas diffusion layer Download PDFInfo
- Publication number
- US20070015043A1 US20070015043A1 US11/191,223 US19122305A US2007015043A1 US 20070015043 A1 US20070015043 A1 US 20070015043A1 US 19122305 A US19122305 A US 19122305A US 2007015043 A1 US2007015043 A1 US 2007015043A1
- Authority
- US
- United States
- Prior art keywords
- diffusion layer
- fuel cell
- gas diffusion
- current collector
- porous metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A fuel cell is described and which includes an ion exchange membrane; an electrode positioned in ion exchanging relation relative to the ion exchange membrane; a gas diffusion layer borne by the electrode and having an outwardly facing surface; a porous metal coating comprising one or more elements selected from the periodic table of elements and which has an atomic number of less than 75, and which is positioned at least in partial covering relation relative to the outwardly facing surface of the gas diffusion layer; and a current collector forcibly disposed in ohmic electrical contact with the porous metal coating.
Description
- Field of the invention: The present invention relates to a fuel cell, and more specifically to a fuel cell incorporating a metalized gas diffusion layer which is disposed in ohmic electrical contact with an adjoining current collector, and wherein a substantially force independent contact resistance is established between the current collector and the gas diffusion layer during fuel cell operation.
- A fuel cell is a device which can readily convert chemical energy to electrical energy by the reaction of a fuel gas with a suitable oxidant supply. In a proton exchange membrane fuel cell, for example, the fuel gas is typically hydrogen, and the oxidant supply comprises oxygen (or more typically ambient air). In fuel cells of this type, a membrane electrode diffusion layer assembly is provided and which includes a solid polymer electrolyte with opposite anode and cathode sides. Appropriate electrodes are provided on the opposite anode and cathode sides. During operation, a fuel gas reacts with a catalyst present in the electrode on the anode side to produce hydrogen ions which migrate through the solid polymer electrolyte to the opposite cathode side. Meanwhile, an oxidant supply introduced to the cathode side is present to react with the hydrogen ions in the presence of catalyst which is incorporated into the electrode on that side, to produce water and a resulting electrical output.
- Many fuel cell designs have been provided through the years, and much research and development activity has been conducted to develop a fuel cell which meets the perceived performance and cost per watt requirements of various users. Despite decades of research, fuel cells have not been widely embraced except for narrow commercial applications. While many designs have emerged, and which have operated with various degrees of success, shortcomings in some peculiar aspect of their individual designs have resulted in difficulties which have detracted from their widespread commercial acceptance and perceived usefulness. For example, one of the perceived challenges for fuel cell designers is the reduction of contact resistance between the current collector and an adjacent gas diffusion layer and which is borne by the membrane electrode diffusion layer assembly. This contact resistance is generally speaking inversely related to the current output of the fuel cell. Consequently, lowering the contact resistance increases the overall current output of the fuel cell.
- Heretofore, the conventional prior art means of minimizing this contact resistance has been to apply relatively large amounts of direct pressure or force to the current collector which lies in immediate, ohmic electrical contact with the gas diffusion layer. The designers and manufacturers of both fuel cell stacks, and fuel cell modular power systems include in their respective fuel cell designs, various force application assemblies to transmit force directly to the current collectors to minimize contact resistance. These force application assemblies have included various mechanical schemes and other arrangements to apply force or pressure substantially evenly across the surface area of the membrane electrode diffusion layer assembly enclosed within the fuel cell. While these several schemes have operated with some degree of success, there have been inherent shortcomings which have continued to detract from their usefulness.
- As a first matter, these above mentioned mechanical arrangements for applying force provide an additional level of complexity, and thus cost to the design and manufacture of such fuel cell devices. Secondly, such force application assemblies increase the perceived difficulty in repairing, maintaining and modifying such devices. For example, if an individual membrane electrode diffusion layer assembly in a fuel cell stack begins to decline in performance, or fails, the fuel cell stack must often be taken out of service, and off-line. Subsequently, the fuel cell stack must be completely disassembled in order to replace the failed component. This disassembly includes the removal of several long tie or compression bolts; disassembly of the fuel cell stack and then the reassembly of the fuel cell stack followed by the precise application of torque to each of the same tie bolts to reestablish the appropriate amount of force applied by the stack to the plurality of membrane electrode diffusion assemblies. Further, in fuel cell stack arrangements, the pressure applied by these same tie bolts is also necessary in order to establish an appropriate amount of sealing force throughout the stack and thus prevent the escape of hydrogen; coolant; oxygen; or the by-product, water.
- In a modular fuel cell power system such as what has been shown and described in U.S. Pat. No. 6,030,718, and in our pending application Ser. Nos. 09/873,139; 09/577,407 and that application filed Nov. 13, 2001, assorted fuel cell modules have been described and claimed and which utilize individual membrane electrode diffusion layer assemblies which are oriented in predetermined arrangements such that the respective modules can be readily removed from a subrack, for example, while the remaining modules continue to operate. In each of these fuel cell designs, the load which is electrically coupled to the power system continues to be substantially electrically served, and the failed fuel cell module can be readily replaced and/or serviced without the inconvenience of taking the entire fuel cell power system out of service, and off-line, as is the current prior art practice.
- In addition to the shortcomings noted above, if force or pressure is not evenly applied across the face of a membrane electrode diffusion layer assembly, the fuel cell will not reach it's full potential for producing electrical power. As will be recognized, all of the foregoing have detracted from the widespread acceptance of fuel cells for use in various commercial applications.
- These and other perceived shortcomings are addressed by means of the present invention.
- Therefore, one aspect of the present invention is to provide a fuel cell which includes an ion exchange membrane; an electrode positioned in ion exchanging relation relative to the ion exchange membrane; a gas diffusion layer borne by the electrode and having an outwardly facing surface; a porous metal coating comprising one or more elements selected from the periodic table of elements and which has an atomic number of less than 75, and which is positioned at least in partial covering relation relative to the outwardly facing surface of the gas diffusion layer; and a current collector forcibly disposed in ohmic electrical contact with the porous metal coating.
- Another aspect of the present invention is to provide a fuel cell which includes an ion exchange membrane; an electrode borne by the ion exchange membrane; a gas diffusion layer borne by the electrode and having an outwardly facing surface area; and a current collector forcibly juxtaposed relative to the gas diffusion layer, and wherein, during fuel cell operation, a contact resistance is created between the gas diffusion layer and the current collector, and which is expressed in milliohms per square centimeter of surface area, and wherein pressure applied by the current collector is expressed in pounds per square inch of surface area, and wherein the contact resistance, and the pressure applied by the current collector can be individually mathematically expressed as a logarithm, and wherein the relationship of the logarithm of the contact resistance and the logarithm of the pressure applied by the current collector is defined by a line having a slope of about 0 to about a negative 0.8.
- Still another aspect of the present invention relates to a fuel cell which includes an ion exchange membrane; an electrode disposed in at least partial covering relation relative to the ion exchange membrane; a gas diffusion layer borne by the electrode, and which has an outwardly facing surface area, and which further has a porous metal coating applied thereto; and a current collector juxtaposed relative to the metal coating, and wherein a pressure of less than about 300 pounds per square inch is applied by the current collector to the juxtaposed gas diffusion layer and which creates a contact resistance, during fuel cell operation, of less than about 20 milliohms per square centimeter between the porous metal coating and the current collector, and wherein the fuel cell, during operation, generates a substantially constant electrical current when exposed to a pressure of less than about 300 pounds per square inch by the current collector at operating temperatures of less than about 300° C.
- These and other aspects of the invention will be discussed in further detail hereinafter.
- Preferred embodiments of the invention are described below with reference to the following accompanying drawings.
-
FIG. 1 is a greatly enlarged, fragmentary, vertical sectional view of a membrane electrode diffusion layer assembly, and accompanying current collector, and which illustrates the teachings of the present invention. -
FIG. 2 is a perspective view of a modular fuel cell power system which may utilize the present invention. -
FIG. 3 is a perspective view of a fuel cell stack which may utilize the present invention. -
FIG. 4 is a graphic depiction of the performance characteristics of the present invention as compared to several prior art examples. -
FIG. 5 is a second, logarithmic, graphic depiction of the performance of the present invention as compared to the prior art. - This disclosure of the invention is submitted in furtherance of the constitutional purposes of the U.S. Patent Laws “to promote the progress of science and useful arts” (
Article 1, Section 8). - A fuel cell having a metalized gas diffusion layer in accordance with the teachings of the present invention is generally indicated by the
numeral 10 inFIG. 1 . As should be understood,FIG. 1 is a greatly enlarged, fragmentary, vertical sectional view taken through a portion of a membrane electrode diffusion layer assembly which is generally indicated by thenumeral 11. The membrane electrode diffusion layer assembly (MEDLA) is received within or made integral with a fuel cell device such as what is seen in FIGS. 2 or 3 and which will be discussed in greater detail, hereinafter. For purposes of the present discussion, however, the membrane electrode diffusion layer assembly, as will be disclosed below, is useful in fuel cell devices which operate at temperatures of less than about 300 degrees C. Consequently, this invention is not useful in solid oxide fuel cell designs or other fuel cells which generally operate at temperatures greater than about 300 degrees C. As wil be appreciated by a study ofFIG. 1 , aspects of the construction of the MEDLA can be expressed in terms of dimensions as measured along x, y and z axes. In this regard the x and y axis relate to length and width dimensions of an object, and the z axis relates to thickness of the same object. - As seen in
FIG. 1 , a fuel cell employing the present invention will typically utilize anion exchange membrane 12, such as may be purchased under the trade name “NAFION”. This ion exchange membrane is a thin, flexible and sheet-like material which is made from a fluor-polymer. This ion exchange membrane is available from the Dupont™ Company. Theion exchange membrane 12 has opposite anode andcathode sides - As will be seen from a study of
FIG. 1 , anelectrode layer 20 is disposed in ionic exchanging relation relative to the respective anode andcathode sides electrode layer 20 is of conventional design and which, during fuel cell operation, facilitates the creation and movement of ions across theion exchange membrane 12. Eachelectrode layer 20 has an outwardly facingsurface 21. As seen inFIG. 1 , a micro-diffusion layer orfirst portion 30 having a given degree of porosity is juxtaposed relative to the outwardly facingsurface 21 of theelectrode layer 20. Themicro-diffusion layer 30 comprises a carbon based slurry which may be modified, as needed, to provide different levels of porosity for theanode side 13, and thecathode side 14. Still further, the porosity of themicro-diffusion layer 30 may be manipulated in various ways to achieve various desired performance characteristics such as effective hydration of the fuel cell. Yet further, while themicro-diffusion layer 30 is shown as a single layer, the micro-diffusion layer may comprise individually discreet layers each having a different porosity. Moreover, while the porosity of themicro-diffusion layer 30 may vary across its thickness dimension (z axis), it is also possible that the micro-diffusion layer may vary in porosity in the X and Y axes, that is, across the outwardly facingsurface area 31. - Continuing still with
FIG. 1 , it will be seen that a macro-diffusion layer or second portion is generally indicated by thenumeral 40, and is immediately juxtaposed relative to the outwardly facingsurface area 31 of themicro-diffusion layer 30. The macro-diffusion layer comprises, in one form, a carbon fiber based sheet having a porosity, which is, as general matter, greater than the porosity of themicro-diffusion layer 30. This macro-diffusion layer can be commercially purchased under the trade name “TORAY” or from various other commercial sources. Themicro-diffusion layer 30 and themacro-diffusion layer 40 in combination define a gas diffusion layer (GDL) which is generally indicated by the numeral 50. Thegas diffusion layer 50 has an outwardly facingsurface area 51 which has a surface texture or topology. It should be understood that the gas diffusion layer, while described herein, as including both themacro-diffusion layer 40 and amicro-diffusion layer 30, may in some forms include only one of these two previously described diffusion layers. It being understood thatFIG. 1 shows a preferred form of practicing the invention. The porosity of themacro diffusion layer 40 may be varied utilizing various prior art practices. Similarly, as discussed with respect to the micro diffusion layer the porosity of the macro diffusion layer may be varied in the x, y, and z axes. - Referring still to
FIG. 1 , it will be seen that aporous metal coating 60 comprising one or more elements selected from the periodic table of elements and which has an atomic number of 13 through 75 is positioned at least in partial covering relation relative to the outwardly facingsurface area 51, of thegas diffusion layer 50. This metal material forms a resulting metalizedgas diffusion layer 50. Theporous metal coating 60 may comprise an alloy; oxide; nitride; or carbide. In the attached drawings, thegas diffusion layer 50, and theporous metal coating 60, are disposed on both the anode andcathode sides ion exchange membrane 12. However, it will be appreciated that thegas diffusion layer 50, and theporous metal layer 60 may be disposed on only one of the anode orcathode sides diffusion layer assembly 11 wherein thegas diffusion layer 50 is located on both the anode andcathode sides porous metal coating 60 is positioned on only one of the anode or cathode sides. - As discussed above, the
gas diffusion layer 50 has an outwardly facingsurface area 51 having a topology. Further, theporous metal coating 60 is applied in a fashion to the outwardly facing surface such that it substantially conforms to the topology. In this regard, the porous metal coating is applied in an amount of about 8 to about 150 milligrams of porous metal per square centimeter of the outwardly facingsurface area 51. Moreover, theporous metal coating 60 is applied in an amount, and in a fashion which causes the resultinggas diffusion layer 50 to have an air impedance of about 23 to about 300 seconds Gurley. Gurley is defined in this application by the use of a Gurley Model 4118 (low pressure) 0.1 square inch orifice at a flow rate of about 100 cubic centimeters. As will be appreciated from studyingFIG. 1 , theporous metal coating 60 may be continuous as depicted in the drawing; or may be discontinuous based upon other design concerns and desired fuel cell performance parameters. - The
porous metal coating 60, may include a substantially homogeneous metal or their respective alloys, oxides, nitrides, and carbides. The porous metal coating has a density of about 2.0 to about 19.0 grams per cubic centimeter. Further, theporous metal coating 60 is selected from the group of metals consisting essentially of aluminum, titanium, nickel, iron, stainless steel, manganese, zinc, chromium, copper, zirconium, silver, and tungsten, and their alloys, nitrides, oxides and carbides. For example, when theporous metal coating 60 is formed of nickel, this metal is deposited in an amount of about 28 to about 150 milligrams per square centimeter of surface area. On the other hand, when a porous metal coating of aluminum is employed, it is deposited in an amount of about 8 to about 40 milligrams per square centimeter of surface area. As a general matter, theporous metal coating 60 has an average thickness of about 25 to about 400 micrometers. Theporous metal coating 60 is applied by conventional metal spraying techniques which are well known in the art and further elaboration regarding these techniques is neither warranted nor required in this application. - Referring still to
FIG. 1 , a fuel cell employing thepresent invention 10 will include a current collector which is generally designated by the numeral 80, and which is forcibly disposed into ohmic electrical contact with theporous metal coating 60. Thecurrent collector 80 is of traditional design having amain body 81 which hasopen areas 82 formed therein and which allows a fuel gas, such as hydrogen (on the anode side 13), and an oxidant supply, such as oxygen (on the cathode side 14) to reach the underlyingporous metal coating 60 and associatedgas diffusion layer 50. Thecurrent collector 80 is typically a metal, or metal alloy, or has a metal coating, cladding, or plating formed of nickel or similar metals. As noted above, the current collector transmits force orpressure 83 which is applied thereto and which maintains the current collector in an appropriate ohmic electrical contact with the underlyingporous metal coating 60. During subsequent fuel cell operation, contactresistance 84 is established between themain body 81 of thecurrent collector 80 and theporous metal coating 60. - Referring now to
FIG. 2 , a modular fuelcell power system 100 is shown, and which can utilize thepresent invention 10. As seen inFIG. 2 , the modular fuelcell power system 100 includes a number offuel cell modules 101 which may be selectively released from the modular fuelcell power system 100 while the remaining modules continue to operate and serve a load. This particular modular fuel cell power system avoids many of the shortcomings in the prior art practice by providing ease of service and repair for failed or failingfuel cell modules 101. The fuelcell power system 100 is provided with a source of fuel gas, herein shown as a bottle ofhydrogen 102. Still further, a suitable source of hydrogen for use in the modular fuel cell power system may also be acquired from achemical reformer 103. Both the reformer, and the bottled supply of hydrogen are coupled in fluid flowing relation to the modular fuelcell power system 100 by means of a suitable conduit or fuel line which is generally indicated by the numeral 104. - Referring now to
FIG. 3 , another fuel cell arrangement is illustrated, that being afuel cell stack 110 which can utilize thepresent invention 10. Thefuel cell stack 110 which is shown inFIG. 3 , includesopposite end plates 111 which are operable to apply compression, by way of a plurality of tie orcompression bolts 112, to a plurality of membrane electrodediffusion layer assemblies 113. Still further,fluid couplers 114 are provided, and which supply a suitable fuel gas and oxidant supply to the fuel cell for its operation. - Fuel cells, such as illustrated in
FIGS. 2 and 3 , are often modeled as a current source in series with a capacitance, and an accompanying electrical resistance. This electrical resistance is referred to as equivalent series resistance, or ESR. The ESR for a typical fuel cell comprises, as a general matter, the electrical resistance of the membrane electrodediffusion layer assembly 11 plus the contact resistance which is established between that membrane electrode diffusion layer assembly and the adjacentcurrent collector 80. In the present invention, the ESR of the membrane electrodediffusion layer assembly 11 is substantially independent of the force or pressure applied; whereas on the other hand the contact resistance which exists between this assembly and the adjacent current collector, in prior art assemblies, is typically a function of pressure or force applied by the current collector. - Referring now to
FIG. 4 , the current produced and the fuel cell ESR is graphically shown with respect to two different fuel cells each having a 16 square centimeter active electrode surface area, and utilizing a stainless steelcurrent collector 80. In this graphic depiction, the earlier prior art relationships are clearly seen. In this regard, the line labeled 120 shows the operational response of a prior art fuel cell which has a membrane electrodediffusion layer assembly 11, with no accompanyingporous metal coating 60. As would be expected, as pressure, in terms of pounds per square inch is applied to thecurrent collector 80, the resulting electrical current output as expressed in milliamps per square centimeter of surface area of the activeelectrode surface area 21 is shown to rise proportionately. Conversely, and referring to the line labeled 121, for the same prior art fuel cell which does not have aporous metal layer 60, it will be seen that the application of increasing pressure or force by way of the current collector results in a decrease in the fuel cell ESR. Since the ESR of the membrane electrode diffusion assembly is a constant and substantially independent of pressure or force, the change in fuel cell ESR is almost entirely due to a change in contact resistance. This ESR is expressed in milliohms per centimeter square of surface area. The relationship between current output, and pressure applied is quite clear relative to using a prior art, non-metalized,gas diffusion layer 50, that is, the application of increasing amounts of pressure results, on the one hand, with decreasing contact resistance, and on the other hand, a corresponding increase in the current output of the prior art fuel cell. - Referring still to
FIG. 4 , the performance of thepresent invention 10 is graphically depicted with respect to the lines labeled 130 and 131, respectively for a second fuel cell of identical structure as described above. As seen inFIG. 4 ,line 130 depicts the same fuel cell with a stainless steelcurrent collector 80, and wherein thegas diffusion layer 50 of the membrane electrodediffusion layer assembly 11 has aporous metal coating 60 applied thereto.Line 130 illustrates that current output, as expressed in milliamps per square centimeter of surface area, is substantially constant when exposed to increasing amounts of pressure applied by, or to, the current collector. This is, of course, in stark contrast toline 120 which shows the relationship of pressure and current output in a fuel cell not having ametal coating 60 applied to the gas diffusion layer. Still further,line 131 shows the same fuel cell having aporous metal layer 60 applied to thegas diffusion layer 50, and wherein it will be seen that the fuel cell ESR, as expressed in milliohms per square centimeter of surface area, and thus contact resistance, remains substantially constant at pressures of less than about 300 pounds per square inch as applied by thecurrent collector 80. Still further,line invention 10 will operate at pressures which would render a prior art fuel cell arrangement nearly inoperable or commercially unfeasible in view of the relatively low current output. - As will be recognized the use of the
present invention 10 results in substantial performance improvements and potentially significant cost savings. In this regard, significant manufacturing costs can be effectively eliminated from fuel cell fabrication inasmuch as many of the design features which are employed to exert the pressure necessary to render a prior art fuel cell operational are substantially reduced, or eliminated. Still further, less expensive materials can be used in the fabrication of a fuel cell inasmuch as relatively low pressures are needed to effectuate maximum current density and minimum contact resistance. In this regard, for example, in the assembly of suitablefuel cell modules 101, mere sealing pressure need only be applied to achieve maximum current output and minimum contact resistance within the same fuel cell module. - Referring now to
FIG. 5 , several logarithmic relationships are shown and which demonstrate the relationship between the amount of pressure or force applied by, or to thecurrent collector 80, expressed in pounds per square inch, and the contact resistance, as established between the current collector and the underlyingporous metal coating 60 during fuel cell operation. As seen inFIG. 5 ,line 140 shows a prior art fuel cell arrangement and the logarithmic relationship which is established for acurrent collector 80 having a nickel coating, and agas diffusion layer 40 without aporous metal coating 60. The contact resistance established between the current collector and the adjacentgas diffusion layer 40 is expressed in milliohms per square centimeter of surface area.Line 140 which shows the relationship of the logarithm of the contact resistance and the logarithm of the pressure applied by the current collector is characterized by a slope of about negative 0.962. - Referring still to
FIG. 5 ,line 141 shows the same logarithmic relationship noted above, except as it now relates to a porousgas diffusion layer 40, which hasporous metal coating 60 of nickel applied thereto. As should be understood, the relationship of the logarithm of the contact resistance, and the logarithm of the pressure applied by the current collector, is characterized, inline 141 as having a slope of about negative 0.751. - Finally,
line 142 inFIG. 5 shows the logarithmic relationship of contact resistance and pressure in a fuel cell employing agas diffusion layer 40 having aporous metal layer 60 comprising nickel. Further, acurrent collector 80 having a nickel coating which has been roughened in a predetermined amount is also employed. The logarithmic relationship of the contact resistance and the pressure applied by the current collector is characterized by a line (142) having a slope of about 0.366. For thepresent invention 10, therefore, the relationship of the logarithm of the contact resistance and the logarithm of the pressure applied by the current collector is characterized by a line having a slope of about 0 to about negative 0.8. - The operation of the described embodiment of the
present invention 10 is believed to be readily apparent and is briefly summarized at this point. Thepresent invention 10 includes anion exchange membrane 12; anelectrode 20 which is borne by the ion exchange membrane; agas diffusion layer 50 having an outwardly facingsurface 51 and which is borne by the electrode; and acurrent collector 80 forcibly disposed in ohmic electrical contact with the gas diffusion layer, and wherein a substantially forceindependent contact resistance 84 is established between thecurrent collector 80 and thegas diffusion layer 50 during fuel cell operation. - As seen in
FIGS. 1, 4 and 5, theelectrode 20;ion exchange membrane 12; and thegas diffusion layer 50 form a membrane electrodediffusion layer assembly 11 and which has aporous metal coating 60; and wherein the membrane electrode diffusion layer assembly, during fuel cell operation produces substantially constant electrical current when exposed to a pressure of greater than about 3 pounds per square inch and less than about 300 pounds per square inch of surface area, at fuel cell operating temperatures of less than about 300 degrees C. - As earlier disclosed, the
porous metal coating 60 is applied to the outwardly facingsurface area 51, and is disposed in ohmic electrical contact with thecurrent collector 80. The current collector may have anopen area 82 in an amount of about 10% to about 80%. Further, theporous metal coating 60 comprises one or more elements selected from the periodic table and which have an atomic number of 13 to 74. Thegas diffusion layer 50 which is employed with the present invention and combined with theporous metal coating 60 has a combined air impedance of about 23 to 300 seconds Gurley. Yet further, and as seen inlines FIG. 5 , the logarithm of the pressure applied by thecurrent collector 80 to thegas diffusion layer 50; and the logarithm of the contact resistance as measured between thegas diffusion layer 50, and thecurrent collector 80, is characterized by a line having a slope of about 0 to about negative 0.8. - Therefore, it will be seen that a fuel cell having a
porous metal coating 60, as described above, forms a metalized gas diffusion layer which provides many advantages over the prior art devices and practices employed heretofore. Thepresent invention 10 effectively reduces contact resistance and resulting equivalent series resistance in a fuel cell and causes a resulting substantially constant current output. Thepresent fuel cell 10 operates at temperatures of less than 300 degrees, and provides substantially constant electrical current and constant contact resistance across a wide range of pressures including pressures which would merely be characterized as sealing pressure. In view of the many advantages provided by theinvention 10, substantial cost savings can be realized in designing and manufacturing fuel cells. This will, in turn, reduces the relative cost per watt to produce electrical power, and makes fuel cells a better option for various commercial applications. - In compliance with the statute, the invention has been described in language more or less specific as to structural and methodical features. It is to be understood, however, that the invention is not limited to the specific features shown and described, since the means herein disclosed comprise preferred forms of putting the invention into effect. The invention is, therefore, claimed in any of its forms or modifications within the proper scope of the appended claims appropriately interpreted in accordance with the doctrine of equivalents.
Claims (50)
1. A fuel cell comprising:
an ion exchange membrane;
an electrode positioned in ion exchanging relation relative to the ion exchange membrane;
a gas diffusion layer borne by the electrode and having an outwardly facing surface;
a porous metal coating comprising one or more elements selected from the periodic table of elements and which has an atomic number less than 75, and which is positioned at least in partial covering relation relative to the outwardly facing surface of the gas diffusion layer; and
a current collector forcibly disposed in ohmic electrical contact with the porous metal coating.
2. A fuel cell as claimed in claim 1 , and wherein the fuel cell is operational at temperatures of less than about 300 degrees C.
3. A fuel cell as claimed in claim 1 , and wherein the porous metal coating comprises an alloy, oxide, nitride or carbide.
4. A fuel cell as claimed in claim 1 , and wherein the porous metal coating is selected from the group of metals in the periodic table of elements having atomic numbers from 13 to 74.
5. A fuel cell as claimed in claim 1 , and wherein the ion exchange membrane has opposite anode and cathode sides, and wherein the gas diffusion layer and the porous metal coating are disposed on only one of the anode or cathode sides.
6. A fuel cell as claimed in claim 1 , and wherein the ion exchange membrane has opposite anode and cathode sides, and wherein the gas diffusion layer and the porous metal coating are disposed on both the anode and cathode sides.
7. A fuel cell as claimed in claim 1 , and wherein the ion exchange membrane has opposite anode and cathode sides, and wherein the gas diffusion layer is located on both the anode and cathode sides, and wherein the porous metal coating is positioned on only one of the anode or cathode sides.
8. A fuel cell as claimed in claim 1 , and wherein the gas diffusion layer has first and second portions, and where the first portion has a porosity and the second portion has a porosity which is greater than the first portion.
9. A fuel cell as claimed in claim 1 , and wherein the gas diffusion layer comprises:
a carbon fiber based sheet having a porosity, and wherein the outwardly facing surface has a topology, and wherein the porous metal coating substantially conforms to the topology.
10. A fuel cell as claimed in claim 1 , and wherein the gas diffusion layer comprises:
a carbon fiber based sheet having a porosity, and wherein the outwardly facing surface has a topology, and wherein the porous metal coating substantially conforms to the topology and is deposited in an amount of about 8 to about 150 milligrams of the porous metal per square centimeter of surface area.
11. A fuel cell as claimed in claim 1 , and wherein the outwardly facing surface of the gas diffusion layer has a topology, and wherein the porous metal coating substantially conforms to the topology and is deposited in an amount which causes the resulting gas diffusion layer to have an air impedance of about 23 to about 300 seconds Gurley.
12. A fuel cell as claimed in claim 1 , and wherein the outwardly facing surface of the gas diffusion layer has a topology, and wherein the porous metal coating substantially conforms to the topology, and is deposited in an amount of about 8 to about 150 milligrams of the porous metal per square centimeter of surface area.
13. A fuel cell as claimed in claim 1 , and wherein the porous metal coating is continuous.
14. A fuel cell as claimed in claim 1 , and wherein the porous metal coating is discontinuous.
15. A fuel cell as claimed in claim 1 , and wherein the porous metal coating is selected from the group of metals and their alloys, oxides, nitrides, and carbides which have a density of about 2.0 to about 19.0 grams per cubic centimeter.
16. A fuel cell as claimed in claim 1 , wherein the porous metal coating is selected from the group of metals consisting essentially of aluminum, titanium, nickel, iron, stainless steel, manganese, zinc, chromium, copper, zirconium, silver, and tungsten, and their alloys, nitrides, oxides and carbides.
17. A fuel cell as claimed in claim 1 , and wherein the outwardly facing surface of the gas diffusion layer has a surface area, and wherein the porous metal coating comprises nickel which is deposited in an amount of about 28 to about 150 milligrams per square centimeter of surface area.
18. A fuel cell as claimed in claim 1 , and wherein the outwardly facing surface of the gas diffusion layer has a surface area, and wherein the porous metal coating comprises aluminum which is deposited in an amount of about 8 to about 40 milligrams per square centimeter of surface area.
19. A fuel cell as claimed in claim 1 , and wherein the outwardly facing surface of the gas diffusion layer has a surface area, and wherein the porous metal coating has an average thickness of about 25 to about 400 micrometers.
20. A fuel cell as claimed in claim 1 , and wherein the outwardly facing surface of the gas diffusion layer has a surface area which defines a topology, and wherein the porous metal coating substantially conforms to the topology; and has an average thickness of about 25 to about 400 micrometers on the surface area of the gas diffusion layer; and wherein the gas diffusion layer and the metal coating have a combined air impedance of about 23 to about 300 seconds Gurley.
21. A fuel cell as claimed in claim 1 , and wherein the outwardly facing surface of the gas diffusion layer has a surface area, and wherein a contact resistance is established between the current collector and the adjacent porous metal coating, and wherein the contact resistance is expressed in milliohms per square centimeter of surface area, and the pressure applied by the current collector is expressed in pounds per square inch, and wherein the contact resistance and the pressure can each be mathematically expressed as a logarithm, and wherein the relationship of the logarithm of the contact resistance, and the logarithm of the pressure applied by the current collector is characterized by a line having a slope of about 0 to about negative 0.8.
22. A fuel cell as claimed in claim 1 , and wherein a contact resistance is established between the current collector and the adjacent porous metal coating, and wherein the contact resistance is substantially constant and independent of the force applied by way of the current collector.
23. A fuel cell as claimed in claim 1 , and wherein the outwardly facing surface of the gas diffusion layer has a surface area, and wherein a contact resistance is established between the current collector and the adjacent porous metal coating, and wherein the contact resistance is substantially constant when exposed to a pressure of about 3 to about 300 pounds per square inch by way of the current collector.
24. A fuel cell as claimed in claim 1 , and wherein the electrode, ion exchange membrane, and the gas diffusion layer, form a resulting membrane electrode diffusion layer assembly, and wherein, during fuel cell operation, the membrane electrode diffusion layer assembly produces a substantially constant electrical current when exposed to a pressure of about 3 to about 300 pounds per square inch by way of the current collector.
25. A fuel cell as claimed in claim 1 , and wherein the electrode, ion exchange membrane, and the gas diffusion layer form a resulting membrane electrode diffusion layer assembly, and wherein, during fuel cell operation, the membrane electrode diffusion layer assembly generates electrical current, and a contact resistance is established between the porous metal coating and the juxtaposed current collector, and wherein the current produced, and the contact resistance experienced, is substantially constant, and independent of the force applied by the current collector.
26. A fuel cell as claimed in claim 1 , and wherein the electrode, ion exchange membrane, and the gas diffusion layer, form a resulting membrane electrode diffusion layer assembly, and wherein the outwardly facing surface of the gas diffusion layer has a surface area having a topology and wherein the porous metal coating substantially conforms to the topology, and wherein during fuel cell operation, the membrane electrode diffusion layer assembly generates electrical current, and a contact resistance is established between the porous metal coating and the juxtaposed current collector, and wherein the current produced is substantially constant, and independent of the pressure applied by the current collector, and wherein the contact resistance is expressed in milliohms per square centimeter of surface area, and the pressure applied by the current collector is expressed in pounds per square inch of surface area, and wherein both the contact resistance and the pressure applied by the current collector can each be mathematically expressed as a logarithm, and wherein the relationship between the logarithm of the contact resistance and the logarithm of the pressure applied by the current collector is characterized by a line having a slope of about 0 to about negative 0.8.
27. A fuel cell as claimed in claim 1 , and wherein the electrode, ion exchange membrane, and gas diffusion layer form a resulting membrane electrode diffusion layer assembly, and wherein the outwardly facing surface of the gas diffusion layer has a surface area having a topology: and wherein the porous metal coating substantially conforms to the topology, and wherein the fuel cell is operational at temperatures of less than about 300 degrees C.; and wherein the porous metal coating has an average thickness across the outwardly facing surface area of the gas diffusion layer of about 25 to about 400 micrometers, and wherein the gas diffusion layer and the porous metal coating have a combined air impedance of about 23 to about 300 seconds Gurley, and wherein during fuel cell operation, the membrane electrode diffusion layer assembly generates electrical current, and a contact resistance is established between the porous metal coating and the juxtaposed current collector, and wherein the current produced is substantially constant and substantially independent of the pressure applied by the current collector, and wherein the contact resistance is expressed in milliohms per square centimeter of surface area, and the pressure applied by the current collector is expressed in pounds per square inch of surface area, and wherein both the contact resistance, and the pressure applied by the current collector can each be mathematically expressed as a logarithm, and wherein the relationship between the logarithm of the contact resistance, and the logarithm of the pressure applied by the current collector is characterized by a line having a slope of 0 to about negative 0.8.
28. A fuel cell comprising:
an ion exchange membrane;
an electrode borne by the ion exchange membrane;
a gas diffusion layer having an outwardly facing surface area and which is borne by the electrode; and
a current collector forcibly disposed in ohmic electrical contact with the gas diffusion layer, and wherein a substantially force independent contact resistance is established between the current collector and the gas diffusion layer during fuel cell operation.
29. A fuel cell as claimed in claim 28 , and wherein the electrode, ion exchange membrane, and the gas diffusion layer, form a membrane electrode diffusion layer assembly, and wherein the membrane electrode diffusion layer assembly, during fuel cell operation, produces a substantially constant electrical current when exposed to a pressure of greater than about 3 pounds per square inch and less than about 300 pounds per square inch of surface area by way of the current collector.
30. A fuel cell as claimed in claim 28 , and wherein the contact resistance is substantially constant when exposed to a pressure of less than about 300 pounds per square inch of surface area by way of the current collector.
31. A fuel cell as claimed in claim 28 , and wherein the contact resistance is substantially constant when exposed to a pressure of greater than about 3 pounds per square inch, and less than about 300 pounds per square inch of surface area by way of the current collector.
32. A fuel cell as claimed in claim 28 , and wherein the ion exchange membrane and the gas diffusion layer are operational at fuel cell operating temperatures of less than about 300 degrees C.
33. A fuel cell as claimed in claim 28 , and wherein a porous metal coating is applied to the outwardly facing surface area, and which is disposed in ohmic electrical contact with the current collector.
34. A fuel cell as claimed in claim 28 , and wherein a porous metal coating is applied to the outwardly facing surface, and is further disposed in ohmic electrical contact with the current collector, and wherein the porous metal coating comprises one or more elements selected from the periodic table of elements and which has an atomic number of 13 to 74.
35. A fuel cell as claimed in claim 28 , and wherein a porous metal coating is applied to the gas diffusion layer, and wherein the porous metal coating lies in ohmic electrical contact with the current collector, and wherein the contact resistance is expressed in milliohms per square centimeter of surface area, and the pressure is expressed in pounds per square inch of surface area, and wherein the contact resistance, and the pressure applied by the current collector can each be mathematically expressed as a logarithm, and wherein the relationship of the logarithm of the contact resistance, and the logarithm of the pressure applied by the current collector, is represented by a line having a slope of about 0 to about negative 0.8.
36. A fuel cell as claimed in claim 28 , and wherein the gas diffusion layer is a porous substrate which has a porous metal coating applied thereto.
37. A fuel cell as claimed in claim 36 , and wherein the porous substrate is a carbon fiber based sheet, and wherein the gas diffusion layer has an air impedance of less than about 300 seconds Gurley.
38. A fuel cell as claimed in claim 28 , and wherein the gas diffusion layer is a carbon fiber based sheet which has a topology, and wherein a porous metal layer substantially conforms to the topology.
39. A fuel cell as claimed in claim 28 , and wherein the gas diffusion layer is a carbon fiber based sheet having a topology, and wherein a porous metal layer substantially conforms to the topology, and wherein the gas diffusion layer and the porous metal layer have a combined air impedance of about 23 to about 300 seconds Gurley.
40. A fuel cell as claimed in claim 28 , and wherein the gas diffusion layer is a carbon fiber based sheet, and wherein a metal layer is deposited on the outwardly facing surface in an amount of about 8 to about 150 milligrams per square centimeter of surface area, and wherein the contact resistance is expressed in milliohms per square centimeter of surface area, and the pressure is expressed in pounds per square inch of surface area, and wherein the contact resistance and the pressure applied by the current collector, can each be mathematically expressed by a logarithm, and wherein the relationship between the logarithm of the contact resistance measured between the gas diffusion layer and the current collector, and the logarithm of the pressure applied by the current collector to the gas diffusion layer is characterized by a line having a slope of 0 to about negative 0.8.
41. A fuel cell as claimed in claim 28 , and wherein a porous metal layer is borne by the gas diffusion layer and positioned in ohmic electrical contact with the current collector, and wherein the current collector applies a pressure of about 3 to about 300 pounds per square inch of surface area, and further has a predetermined open area of about 10 to about 85 percent, and wherein the contact resistance established between the current collector and the adjacent metal layer is expressed in milliohms per square centimeter of surface area, and wherein the contact resistance, and the pressure applied by the current collector can each be mathematically expressed as a logarithm, and wherein the relationship of the logarithm of the contact resistance, and the logarithm of the pressure applied by the current collector is characterized by a line having a slope of about 0 to about negative 0.8.
42. A fuel cell as claimed in claim 28 , and wherein a metal layer is borne by the gas diffusion layer and disposed in ohmic electrical contact with the current collector, and wherein the metal layer is selected from the group of metals consisting essentially of aluminum, titanium, nickel, iron, stainless steel, manganese, zinc, chromium, copper, zirconium, silver, tungsten, and their respective nitrides, oxides, carbides and alloys.
43. A fuel cell as claimed in claim 28 , and wherein a porous metal layer is borne by the gas diffusion layer and oriented in ohmic electrical contact with the current collector, and wherein the porous metal layer is selected from the group of metals and their respective nitrides, oxides carbides and alloys which have a density of about 2.0 to about 19.0 grams per cubic centimeter.
44. A fuel cell as claimed in claim 28 , and wherein a nickel layer is borne by the gas diffusion layer and is oriented in ohmic electrical contact with the current collector, and wherein the nickel layer is deposited in an average amount equal to about 28 to about 150 milligrams per square centimeter of surface area of the gas diffusion layer.
45. A fuel cell as claimed in claim 28 , and wherein an aluminum layer is borne by the gas diffusion layer and is oriented in ohmic electrical contact with the current collector, and wherein the aluminum layer is deposited in an average amount of about 8 to about 40 milligrams per square centimeter of surface area of the gas diffusion layer.
46. A fuel cell as claimed in claim 28 , and wherein a metal layer is borne by the gas diffusion layer and disposed in ohmic electrical contact with the current collector, and wherein the metal layer has an average thickness of about 25 to about 400 micrometers.
47. A fuel cell comprising:
an ion exchange membrane;
an electrode borne by the ion exchange membrane;
a gas diffusion layer borne by the ion exchange membrane; and
a current collector forcibly juxtaposed into ohmic electrical contact with the gas diffusion layer, and wherein a pressure independent contact resistance is established between the gas diffusion layer and the current collector, and wherein the fuel cell is operational at fuel cell operating temperatures of less than about 300 degrees C.
48. A fuel cell comprising:
an ion exchange membrane;
an electrode borne by the ion exchange membrane;
a gas diffusion layer borne by the ion exchange membrane; and
a current collector forcibly juxtaposed relative to the gas diffusion layer, and wherein, during fuel cell operation, the gas diffusion layer, electrode, and the ion exchange membrane produce an electrical current which is substantially constant relative to the pressure applied by the current collector.
49. A fuel cell comprising:
an ion exchange membrane;
an electrode borne by the ion exchange membrane;
a gas diffusion layer borne by the electrode and which has an outwardly facing surface area; and
a current collector forcibly juxtaposed relative to the gas diffusion layer, and wherein, during fuel cell operation, a contact resistance is created between the gas diffusion layer and the current collector and which is expressed in milliohms per square centimeter of surface area, and wherein pressure applied by the current collector is expressed in pounds per square inch of surface area, and wherein the contact resistance, and the pressure applied by the current collector can each be individually mathematically expressed as a logarithm, and wherein the relationship of the logarithm of the contact resistance, and the logarithm of the pressure applied by the current collector is defined by a line having a slope of about 0 to about a negative 0.8.
50. A fuel cell comprising:
an ion exchange membrane;
an electrode disposed in at least partial covering relation relative to the ion exchange membrane;
a gas diffusion layer borne by the electrode and which has an outwardly facing surface area;
a porous metal coating applied on the outwardly facing surface area of the gas diffusion layer; and
a current collector juxtaposed relative to the porous metal coating, and wherein a pressure of less than about 300 pounds per square inch is applied by the current collector to the juxtaposed gas diffusion layer and porous metal coating, and which creates a substantially constant contact resistance, during fuel cell operation, between the porous metal coating and the current collector, and wherein the fuel cell, during operation, generates a substantially constant electrical current when exposed to a pressure of less than about 300 pounds per square inch by the current collector at operating temperatures of less than about 300 degrees C.