US20060254761A1 - Brazed structure and method of manufacturing the same - Google Patents
Brazed structure and method of manufacturing the same Download PDFInfo
- Publication number
- US20060254761A1 US20060254761A1 US11/431,268 US43126806A US2006254761A1 US 20060254761 A1 US20060254761 A1 US 20060254761A1 US 43126806 A US43126806 A US 43126806A US 2006254761 A1 US2006254761 A1 US 2006254761A1
- Authority
- US
- United States
- Prior art keywords
- tube
- brazed
- brazing
- copper
- structure according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
In a brazed structure, a first member has a first portion defined by one of a recessed portion and a hole, and a second member has a second portion brazed to the first portion with a copper brazing material. The first member has a coefficient of thermal expansion that is smaller than that of the second member.
Description
- This application is based on Japanese Patent Applications No. 2005-139112 filed on May 11, 2005 and No. 2005-337626 filed on Nov. 22, 2005, the disclosures of which are incorporated herein by reference.
- The present invention relates to a brazed structure and a method of manufacturing the same, which is for example employed to connecting portions between a header tank and tubes of a heat exchanger.
- A heat exchanger in which longitudinal ends of tubes are connected to header tanks is for example known in Japanese Unexamined Patent Publication No. 2002-286395 (U.S. Pat. No. 6,736,197). In such a heat exchanger, the header tank is generally constructed of a tank body and a header plate formed with tube holes. The longitudinal ends of the tubes are inserted in the tube holes and brazed to the header plate. The tubes and the header tanks are for example made of aluminum.
- In general, the quality of brazing is determined based on how well a brazing material is drawn into a clearance of a joint between connecting portions by capillary action. As shown in
FIG. 7 and the following formula 1, it is known that the capillarity generally has an inverse proportion with respect to a density ρ of a brazing material BM and a clearance d of the joint. In the formula 1, h denotes a drawn height of the brazing material BM by capillary action, γ denotes a surface tension of the brazing material BM, and g denotes gravitational acceleration.
[Formula 1] h=2γ/dρg - To improve the quality of brazing, it is required to reduce the clearance as small as possible. If a material having high density is selected as a material of the heat exchanger, it is required to further reduce the clearance of the joint for an increase of the density of the brazing material. With this, it is required to improve dimensional accuracy of parts. However, there is a limitation to improve the dimensional accuracy while processing the parts.
- Further, it is for example proposed to mechanically expand the tube after the tube is inserted to the tube hole of the header plate so as to reduce the clearance between the tube end and the tube hole. However, if the tube is made of a material having a high coefficient of elasticity (e.g., copper), it does not easily deform and may cause a spring back. Accordingly, it is difficult to reduce the clearance.
- The present invention is made in view of the foregoing matter, and it is an object of the present invention to provide a brazed structure with an improved brazing quality and a method of manufacturing the same without precisely setting an initial clearance between brazing portions.
- According to an aspect of the present invention, a brazed structure has a first member having a first portion defined by one of a recessed portion and a hole, and a second member having a second portion brazed to the first portion of the first member with a copper brazing material. The first member has a coefficient of thermal expansion smaller than that of the second member.
- During brazing, the second member more expands than that the first member expands. Thus, the second portion relatively becomes close to the first portion of the first member during the brazing. Namely, the initial clearance defined between the first portion and the second portion is reduced by the difference of coefficient of thermal expansion between the first member and second members. Accordingly, the quality of brazing improves without requiring to precisely set the initial clearance between the brazing portions.
- Other objects, features and advantages of the present invention will become more apparent from the following detailed description made with reference to the accompanying drawings, in which like parts are designated by like reference numbers and in which:
-
FIG. 1 is a front view of an intercooler according to a first example embodiment of the present invention; -
FIG. 2 is a cross-sectional view of the intercooler taken along line II-II inFIG. 1 ; -
FIG. 3A is a cross-sectional view of a part of the intercooler denoted by an arrow III inFIG. 1 ; -
FIG. 3B is a cross-sectional view of the part of the intercooler for showing a coating on a header plate of the intercooler according to the first example embodiment; -
FIG. 4 is a cross-sectional view of the intercooler taken along line IV-IV inFIG. 3 ; -
FIG. 5 is a cross-sectional view of the intercooler as a modification of the first example embodiment shown inFIG. 1 ; -
FIG. 6 is a cross-sectional view of a tube of the intercooler according to a second example embodiment of the present invention; and -
FIG. 7 is an explanatory view of a model for explaining capillary action of a brazing material. - A first example embodiment of the present invention will now be described with reference to FIGS. 1 to 4. In the first example embodiment, a brazed structure of the present invention is for example employed to a base portion (connecting portion) 101 of an air
cooling type intercooler 100. - The
intercooler 100 is a heat exchanger for performing heat exchange between an intake air to be sucked in an engine of a vehicle for combustion and an external cooling air for cooling the intake air. Theintercooler 100 has acore portion 110 and a pair ofheader tanks 120. Theintercooler 100 is a large heat exchanger and is for example mounted on a large vehicle such as trucks. Respective parts of theintercooler 100, which will be described later, are made of materials such as copper, copper alloy, or iron to have sufficient thermal conduction and durability. - Further, connecting portions between respective parts are connected by brazing or welding. For example, a copper brazing material containing 75% copper, 15% tin, 5% nickel, and 5% phosphorous and having resolution at a low melting point is used as a brazing material.
- In the
core portion 110, tubes 11 andouter fins 112 are alternately layered andside plates 113 are provided at outermost ends of thecore portion 110 in a layering direction. Further,inner fins 114 are interposed in the inside of thetubes 111. - The tube (second member) 111 is a flat pipe member through which the intake air flows. The
tube 111 has a substantially rectangular cross-section so as to increase a flow area of the intake air as much as possible and reduce a flow resistance of the intake air. Thetube 111 is for example formed by joining two tube plates. - Here, the
tube 111 is made of copper alloy containing 15% zinc and 0.8% iron. The copper alloy has a coefficient of linear expansion (thermal expansion) of 19×10−6 m/K. - The
inner fin 114, which is interposed in thetube 111, is made of pure copper plate and is corrugated to disturb the flow of the intake air, to thereby improve thermal conduction of the intake air. Since thetube 111 has the rectangular cross-section, theinner fin 114 is housed in thetube 111 by effectively using the space inside of thetube 111. - Likewise, the
outer fin 112 is made of pure copper plate and is corrugated. Further, flat portions of the corrugatedouter fin 112 are cut to have slopingpieces 112 a as louver portions. Accordingly, a heat radiating area of the cooling air is increased by thelouver portions 112 a. Also, thelouver portions 112 a provide a turbulent effect to the cooling air to enhance heat exchange between the cooling air and the intake air. - The
side plates 113 is made of brass and provided as reinforcement members. Each of theside plates 113 extends in a longitudinal direction of thetubes 111. Theside plate 113 has a substantially U-shaped cross-section. Also, theside plate 113 has a rib that extends in the longitudinal direction of theside plate 113 at a substantially middle portion of the U-shape. - Each of the
tubes 111 is formed by brazing two tube plates. A paste brazing material, which is a mixture of the brazing material and binder, is applied to both surfaces of the tube plate before brazing. Further, theouter fins 112 and theinner fins 114 are brazed to thetubes 111 with the brazing material applied on the tube plates. - Likewise, the paste brazing material is applied to a surface of the
side plate 113, which faces theoutermost fin 112 before brazing. Thus, theside plates 113 are brazed to the outermostouter fins 112 with the brazing material. - Instead of the paste brazing material, a foil brazing material can be used. In this case, the foil brazing material is interposed between the respective connecting portions such as between the
tubes 111 and theouter fins 112, between the tubes and theinner fins 114, and between theside plates 113 and theouter fins 112. - The longitudinal ends 111 a of the
tubes 111 are connected toheader tanks 120 to have communication with cavities of theheader tanks 120. Each of theheader tanks 120 extends in a direction perpendicular to the longitudinal direction of thetubes 111. Theheader tank 120 is constructed of aheader plate 121, atank body 122 and apipe 123. - As shown in
FIG. 4 , the header plate (first member) 121 has a substantially U-shaped cross-section and includes a longitudinal plate portion andside portions 121 b extending from longitudinal edges of the plate portion. Also, the plate portion forms an expanding portion 1211 c that expands toward thetubes 111 in a domed shape. - Further, the plate portion of the
header plate 121forms tube holes 121 a at positions corresponding to the tube ends 111 a. Each of the tube holes 121 a has a hole size (inner dimension) that is slightly larger than a cross-sectional area (outer dimension) of thetube 111 and a perimeter of thetube hole 121 a on a side of thetube 111 is chamfered so that thetube 111 is easily inserted in thehole 121 a. - The
header plate 121 is made of an iron material, such as stainless steel or steel. Both surfaces of theheader plate 121, around the tube holes 121 a and except theside portions 121 b, are coated or covered with pure copper, as shown inFIG. 3B . The iron material of theheader plate 121 has a coefficient of linear expansion (thermal expansion) of 12×10−6 m/K. Namely, theheader plate 121 has the coefficient of linear expansion smaller than that of thetube 111. - In a condition that the tube ends 111 are inserted in the tube holes 121 a, a paste brazing material, which is a mixture of the brazing material, flux and binder, is applied to connecting portions between the tube ends 111 a and the tube holes 121 a. Accordingly, the
tubes 111 and theheader plate 121 are brazed atcontact portions 101 a between them through the brazing material. The brazedcontact portions 101 a correspond to thebase portions 101. Further, the longitudinal ends of theside plates 113 are brazed to theheader plates 121 by the brazing material applied to contact portions between theside plates 113 and theheader plates 121. - The
tank body 122 is made of the iron material, which is the same as the material of theheader plate 121. Thetank body 122 has a semi-tubular shape having an opening on one side. Theheader plate 121 is joined to the opening of thetank body 122. Theside portions 121 b of theheader plate 121 are welded to edges of the openings of thetank body 122. Accordingly, theheader tank 120 defining the cavity therein is formed. - The
pipe 123 is made of iron material. Thepipe 123 is welded to a longitudinal end of thetank body 122 so that a pipe space in thepipe 123 communicates with the cavity of theheader tank 120. - In
FIG. 1 , the intake air flowing in one header tank (right tank) 120 through thepipe 123 is distributed intotubes 111. The intake air passing through thetubes 111 is collected in the remaining header tank (left tank) 120, and then discharged to an external device through thepipe 123. - Next, a method of manufacturing the
intercooler 100 will be briefly described. First, tube plates for thetubes 111,side plates 113, and theheader plates 121 are formed by pressing. Also, theouter fins 112 and theinner fins 114 are shaped by using a roller. - Then, the paste brazing material is applied to the both surfaces of the tube plates, and one surface of each
side plate 113. Next, by using a layering jig (not shown) as a guide, thecore portion 110 is assembled. For example, one of theside plates 113 is laid at a bottom. On theside plate 113, predetermined numbers of theouter fin 112, thetube plate 111, theinner fin 114, and thetube plate 111 are repeatedly alternately layered in this order. Further, the remainingside plate 113 is placed on the uppermostouter fin 112. In this assembly, thetube 111 interposing theinner fin 114 therein is formed by layering theinner fin 114 between the tube plates. - Then, the tube ends 111 a are inserted to the tube holes 121 a of the
header plate 121 and the paste brazing material, containing the brazing material, flux and binder, is applied to the connecting portions between the tube ends 111 a and the tube holes 121 a. In a condition that the tube ends 111 a are inserted to the tube holes 121 b, a predetermined clearance D (initial clearance) is defined between an outer wall of the tube end 111 a and an inner wall of thetube hole 121 a. The predetermined clearance D is defined by initial dimensions of the tube ends 111 a and the tube holes 121 a. The initial clearance D is for example 0.15 mm. Also, another jig such as a wire can be used to hold the assembledcore portion 110, if necessary. - Next, grease or oil is removed from the assembled
core portion 110. Then, the assembledcore portion 110 is placed in a furnace. Thecore portion 110 is integrally brazed at a brazing temperature e.g., 625° C. - Then, the
pipe 123 is welded to thetank body 122, which is formed by pressing. Further, the edges of the opening of thetank body 122 is welded to theside portions 121 b of theheader plate 121. Thus, thetank body 122 and theheader plate 121 are connected. - Then, a predetermined check, such as a leak check for checking the quality of brazing and welding and a size check, is performed to the
intercooler 100. In this way, theintercooler 100 is manufactured. - In the first example embodiment, the
tubes 111 expands more than that theheader plate 121 expands during the brazing because of the difference of the coefficient of linear expansion between thetubes 111 and theheader plate 121. At thebase portion 101, particularly, thetube 111 expands in a direction to reduce the initial clearance D (e.g., 0.15 mm) between the tube end 111 a and thetube hole 121 a. - For example, the amount (ΔD) of change of the clearance D with the change of temperature from a normal temperature of 25° C. to the brazing temperature of 625° C. will be calculated as follows.
ΔD=0.15−(19−12)×10−6×56/2×(625−25)=0.03 - Here, value 56 is a width L of the
tube 111. - Accordingly, the initial clearance D is reduced by the difference of the coefficient of thermal expansion between the
tube 111 and theheader plate 121. Therefore, the quality of brazing is improved without precisely setting the initial clearance D. - The
intercooler 100, which is manufactured in the above condition, is cut at thebase portion 101 and the quality of brazing is checked in the cross-section of thebase portion 101. In the cross-section of thebase portion 101, the clearance D after brazing is 0.05 mm, and is sufficiently filled with the brazing material. - Further, the above quality of brazing is compared to that of a comparison heat exchanger, which is manufactured by using a tube made of copper alloy having a coefficient of linear expansion of 10×10−6 m/k and a header plate made of brass having a coefficient of linear expansion of 21×10−6 m/k. In the comparison heat exchanger, the header plate having tube holes expands more than the tube. Accordingly, the clearance D between the tube and the tube hole after brazing is 0.25 mm, and is not sufficiently filled with the brazing material.
- In the first example embodiment, the
tube 111 and theheader plate 121 are made of dissimilar materials (e.g., copper alloy and iron material), and theheader plate 121 is previously coated with the material (e.g., pure copper), similar to the material of thetube 111. Accordingly, flexibility for choosing the materials of thetubes 111 and theheader plate 121 so as to have the difference of the coefficient of linear expansion improves. Further, since the material that is similar to the material of thetube 111 is used as the brazing material, thetube 111 and theheader plate 121 are easily and sufficiently brazed according to diffusion of the brazing material into the coating. - In the heat exchanger such as the
intercooler 100, the quality of brazing at thebase portion 101 is important to maintain air-tightness. By employing the brazed structure of the present invention to thebase portions 101 of theintercooler 100, the quality of brazing at thebase portions 101 improves. - Also, the
inner fin 114 is interposed in thetube 111 without mechanically expanding thetube 111. If theinner fin 114 is inserted in thetube 111 by mechanically expanding thetube 111, it is likely to separate from an inner wall of thetube 111. In the first example embodiment, theinner fin 114 is sandwiched between the tube plates and integrally brazed. Accordingly, theinner fin 114 is sufficiently brazed to thetube 111. - As shown in
FIG. 5 , theheader plate 121 can have burringportions 121 d at the perimeters of the tube holes 121 a so that a brazing area between theheader plate 121 and thetube 111 increases. In this case, the expandingportion 121 c can be eliminated due to a matter of forming the burringportions 121 d. - A second example embodiment of the present invention will now be described with reference to
FIG. 6 . In the second embodiment, the brazed structure of the present invention is employed to thetubes 111 of theintercooler 100. - The
tube 111 is constructed of a first tube member (first member) 111A and a second tube member (second member) 111B, as shown inFIG. 6 Each of thetube members first tube member 111A forms a recessed portion inside of the U-shape. Thefirst tube member 111A and thesecond tube member 111B are brazed in a condition that the side portions of thesecond tube member 111B are arranged in the recessed portion defined by the side portions of thefirst tube member 111A, as shown inFIG. 6 . - The
first tube member 111A is made of the iron material, and both surfaces of thefirst tube member 111A are coated or covered with pure copper before brazed to thesecond tube member 111B. Thefirst tube member 111A has a coefficient of linear expansion (thermal expansion) of 12×10−6 m/K. Thesecond tube member 111B is made of copper alloy containing 15% zinc and 0.8% iron, similar to thetube 111 of the first example embodiment. Thesecond tube member 111B has a coefficient of linear expansion (thermal expansion) of 19 ×10−6 m/K. Thus, thefirst tube member 111A has the coefficient of thermal expansion smaller than that of thesecond tube member 111B. - In the second example embodiment, the connecting portion of the
tube 111 provides effects similar to those of the connecting portions between thetubes 111 and theheader plate 121 of the first example embodiment. Namely, during the brazing, thesecond tube member 111B expands more than thefirst tube member 111A because of the difference of the coefficient of the linear expansion between thefirst tube member 111A and thesecond tube member 111B. Thus, an initial clearance D1 (e.g., 0.15 mm) defined between thefirst tube member 111A and thesecond tube member 111B is reduced. - For example, the amount (ΔD1) of change of the clearance D1 when the temperature changes from the normal temperature (e.g., 25° C. ) to the brazing temperature (e.g., 625° C. ) during the brazing is calculated as follows.
ΔD1=0.15−(19−12)×10−6 ×60/2×(625−25)=0.024 - Here, value 60 is a width L1 of the
tube 111. - Accordingly, the clearance D1 between the
first side member 111A and thesecond side member 111B is reduced by the difference of the coefficient of thermal expansion between the first andsecond side members - In the second example embodiment, the
first tube member 111A and thesecond tube member 111B are made of different materials (e.g., iron material, and copper alloy), and thefirst tube member 111A is previously coated with the material (e.g., pure copper), which is similar to the material of thesecond tube member 111B. Accordingly, flexibility of choosing the materials of the first andsecond tube members - Further, since the brazing material (e.g., copper brazing material), which is similar to the material of the
second tube member 111B is used, thefirst tube member 111A and thesecond tube member 111B are easily brazed with diffusion of the brazing material into the coating on thefirst tube member 111A. Furthermore, theinner fin 114 is sufficiently brazed to the inner walls of thetube 111 by the difference of coefficient of thermal expansion between thefirst tube member 111A and thesecond tube member 111B. - The brazing structure of the present invention is employed to the connecting portions between the
tube plates intercooler 100. Accordingly, the quality of brazing, which is important to maintain air-tightness in the heat exchanger, improves. - The above first and second example embodiments can be modified as follows.
- In the first example embodiment, the header plate (first member) 121 has the coefficient of linear expansion smaller than that of the tube (second member) 111. In the second example embodiment, the first tube member (first member) 111A has the coefficient of liner expansion smaller than that of the second tube member (second member) 111B. As a modification of the first example embodiment, the
header plate 121 can be made of pure copper, instead of the iron material. Likewise, thefirst tube member 111A of the second example embodiment can be made of pure copper, instead of the iron material. In these cases, it is not necessary to coat the surfaces of theheader plate 121 and thefirst tube member 111A with copper, because themembers - In the above first and second example embodiments, the
intercooler 100 is mainly made of copper or copper alloy. Alternatively, the brazing structure of the present invention may be employed to another heat exchanger made of another material. - In the above first and second example embodiments, the brazed structure of the present invention is applied to the
base portion 101 between theheader plate 121 and thetube 111, and to the connecting portion between thetube plate members - Further, the brazed structure of the present invention can be employed to fix an additional member such as a fixing member (second member) to the header tank (first member) 120. In this case, a recessed portion is formed on the surface of the
header tank 120 and the fixing member is partly inserted in the recessed portion and brazed therein. Here, theheader tank 120 has a coefficient of linear expansion that is smaller than that of the fixing member. - Further, the brazed structure of the present invention can be employed in a body of a shell-and-tube heat exchanger. For example, ends of pipe members (second member) are inserted in a recessed portion defined by a rising edge formed at a periphery of a cover member (first member) and brazed thereto. In this case, the cover member has a coefficient of linear expansion smaller than that of the pipe member.
- Also, the heat exchanger to which the present invention is applied is not limited to the
intercooler 100. The brazed structure of the present invention can be employed to another heat exchanger such as a radiator or a condenser. - Furthermore, the use of the brazed structure of the present invention is not limited to the heat exchanger. The brazing structure can be employed to another device other than the heat exchanger as long as the first member having a recessed portion or a hole and the second member is inserted in the recessed portion or the hole and brazed therein.
- In the first example embodiment, the
tube 111 is made of copper alloy. Alternatively, thetube 111 can be made of pure copper. Likewise, thesecond tube member 111B of the second example embodiment can be made of pure copper, instead of copper alloy. - In the first example embodiment, the brazing portion of the
header plate 121, which is made of the iron material, is coated with pure copper before the brazing, so that it is brazed to thetube 111 with diffusion of the copper brazing material into the coating. Instead of pure copper, theheader plate 121 can be coated with nickel. Likewise, thefirst tube member 111A of the second example embodiment can be coated with nickel instead of pure copper. - The example embodiments of the present invention are described above. However, the present invention is not limited to the above example embodiment, but may be implemented in other ways without departing from the spirit of the invention.
Claims (12)
1. A brazed structure comprising:
a first member having a first portion that is defined by one of a recessed portion and a hole; and
a second member having a second portion brazed to the first portion with a copper brazing material, wherein the first member has a coefficient of thermal expansion smaller than that of the second member.
2. The brazed structure according to claim 1 , wherein
the first member and the second member are made of different materials,
one of the first member and the second member has a coating, and
the coating is made of a material that is brazed to the other one of the first and second member with diffusion of the copper brazing material.
3. The brazed structure according to claim 2 , wherein the material of the coating contains one of copper and nickel.
4. The brazed structure according to claim 1 , wherein
the first member and the second member are included in members of a heat exchanger that performs heat exchange between an internal fluid flowing therein and an external fluid flowing outside thereof.
5. The brazed structure according to claim 4 , wherein
the first member is included in a header tank of the heat exchanger in which the internal fluid flows, the header tank forms a hole as the first portion,
the second member is a tube of the heat exchanger in which the internal fluid flows, and the tube has a tube end brazed in the hole of the header tank as the second portion.
6. The brazed structure according to claim 5 , wherein the tube encloses an inner fin.
7. The brazed structure according to claim 4 , wherein
the first member and the second member are made of one of copper and copper alloy, respectively.
8. The brazed structure according to claim 4 , wherein
the first member is made of one of stainless steel and steel and has a coating containing one of copper and nickel, and
the second member is made of one of copper and copper alloy.
9. The brazed structure according to claim 4 , wherein
the first member forms a first tube member of a tube of the heat exchanger, the first tube member has a substantially U-shaped cross-section and includes a main portion and side portions extending from sides of the main portion, to define the recessed portion therein,
the second member forms a second tube member of the tube, the second tube member has a substantially U-shaped cross-section and includes a main portion and side portions extending from sides of the main portion, and
the side portions of the second tube member are brazed to the side portions of the first tube member in an inside of the recessed portion.
10. The brazed structure according to claim 9 , wherein the first tube member and the second tube member interpose an inner fin therebetween.
11. A method of manufacturing a brazed structure, the brazed structure having a first member having a first portion defined by one of a recessed portion and a hole and a second member having a second portion brazed in the first portion, the method comprising steps of:
arranging the second portion of the second member in the first portion of the first member; and
brazing the second portion of the second member to the first portion of the first member while thermally expanding the second member more than the first member.
12. The method according to claim 11 , wherein
in the arranging the first member and the second member define an initial clearance between the first portion and the second portion, and
in the brazing the initial clearance is reduced by a difference of coefficient of thermal expansion of the first member and the second member.