US20060163078A1 - Single pass, dual thickness electroplating system for head suspension components - Google Patents
Single pass, dual thickness electroplating system for head suspension components Download PDFInfo
- Publication number
- US20060163078A1 US20060163078A1 US11/339,427 US33942706A US2006163078A1 US 20060163078 A1 US20060163078 A1 US 20060163078A1 US 33942706 A US33942706 A US 33942706A US 2006163078 A1 US2006163078 A1 US 2006163078A1
- Authority
- US
- United States
- Prior art keywords
- electroplating
- anodes
- anode
- plating
- current
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method for simultaneously electroplating exposed conductor regions on both sides of a disk drive suspension component by providing an electroplating system having a bath of electroplating solution with first and second anodes in the bath. The suspension component is positioned in the bath of electroplating solution between the first and second anodes. A first electroplating current is produced between the first anode and the exposed conductor regions on the first surface of the component. A second electroplating current is produced between the second anode and the exposed conductor regions on the second surface. Layers of conductive material are thereby plated onto the exposed conductor regions on both sides of the component. By controlling parameters of the first and second plating currents, such as time and magnitude, the layers of conductive material can be plated to the same or different thicknesses on the opposite sides of the conductors.
Description
- This application claims the benefit of U.S. Provisional Application Ser. No. 60/646,934 filed on Jan. 25, 2005 and entitled “Single Pass Dual Thickness Electroplating Method for Head Suspension Components,” which is incorporated herein by reference in its entirety.
- The invention is a system for electroplating portions of disk drive head suspension components. In particular, the invention is a system for simultaneously electroplating different portions of the suspension components to different plating thicknesses.
- BACKGROUND OF THE INVENTION
- Copper or copper alloy leads or conductors, terminal pads and other portions of so-called wireless or integrated lead disk drive head suspension components such as flexures are commonly electroplated with gold, nickel, silver, and/or other conductive materials to enhance electrical connectivity and reduce contamination. For example, one common plating configuration includes a layer of nickel under a layer of gold.
-
FIG. 1 is a schematic illustration of the components of a priorart plating system 10 located in a plating tank (not shown) of an electroplating system that can be used to plate conductive materials to portions of the suspension components. Equipment of the type shown inFIG. 1 is commercially available from suppliers such as PENC Chemicals and Machinery Co. of Hong Kong. As shown, a plurality ofanodes 118 are spaced around acircular rack 116.Panels 114 having suspension components with portions to be electroplated are mounted to therack 116. Thepanel 114 functions as a cathode. More particularly, the layer of conductive leads that are exposed to the plating solution in the plating tank and thereby intended to receive the conductive material function as the cathode. - Wireless flexures manufactured from laminated sheets of material using subtractive processes typically have most (e.g., about 95%) of the surface area to be electroplated on a
first side 120 of the panel, and the remainder of the surface area to be electroplated on a second side 122. Wireless flexures typically have a spring metal layer with conductors, terminal pads, and the like formed on one side of the spring metal layer. The flexures are therefore typically mounted on thepanel 114 so that the conductors formed onto the spring metal are on thefirst side 120 of thepanel 114. Portions of the spring metal layer attached to the conductors may be removed to create an access to the conductors from the second side 122 of the flexure. Some of these portions of the flexure with access to the conductors from both sides may be known as flying lead regions and the portions of the conductors in this region are known as flying leads. - Electroplating tends to be a very directional process. Current flowing between the
anodes 118 and the exposed conductive material (which acts as a cathode) tends to cause the plating material in the plating solution to plate onto the exposed conductive material on thefirst side 120 of the panel 114 (i.e., the side that is positioned to directly face the anodes 118). However, there is a relatively small amount of current leakage from the anode to the second side 122 of thepanel 114. Since the amount of surface area to be plated on the second side 122 of thepanel 114 is also relatively small, this leakage current is typically sufficient to produce suitable electroplating on the second side 122, even though the conductive material on the second side of thepanel 114 is not exposed to theanodes 118, (i.e., the second side does not directly face the anodes). - It is sometimes desirable to electroplate different portions of a suspension component with different thicknesses of plating material. For example, it is generally desirable to provide a relatively thin electroplated layer at terminals that will be solder ball bonded (SBB) to terminals of a read/write head mounted to the suspension. A thin plated layer is desirable at this location to reduce solder embrittlement that can sometimes occur if too much gold plating mixes with the solder. On the other hand, relatively thick plated layers are desirable on the back side of flying leads where they are ultrasonically bonded to other disk drive components. The relatively thick gold plating provides an enhanced bond in this application.
- Known approaches for plating different flexure portions to different thicknesses include using conventional photolithography resist processes to cover and shield portions of the flexure that are not to be plated when other portions of the suspension are being plated. For example, in a flexure having conductors that are to be plated to a first thickness and ground features that are to be plated to a second thickness, the ground feature locations can be masked by resist while the conductors are electroplated with relatively thin nickel and/or gold layers. After the conductors are electroplated, they can be masked with resist, the resist stripped from the ground feature locations, and the ground features electroplated.
- Still other known approaches include the use of additional process steps to increase the plating thickness at the locations of the flying leads. For example, following the thin nickel/gold layer plating described above, portions of the conductors other than the flying leads and the locations of the plated ground features can be masked by resist. An additional, and typically relatively thick, layer of gold or other material can then be electroplated onto the flying leads. The plated ground features can then be manufactured in the manner described above. These relatively thick gold flying leads can be manufactured in either encapsulated or non-encapsulated form.
FIG. 2 is a cross sectional illustration of aconductive lead 138 having acopper alloy portion 130 with a relatively thinnickel plating layer 132 and a relatively thingold plating layer 134 that are encapsulated by a relatively thick gold encapsulatinglayer 136.FIG. 3 is a cross sectional illustration of aconductive lead 148 having acopper alloy portion 140 with a relatively thinnickel plating layer 142 and a relatively thingold plating layer 144 that are not completely encapsulated by a relativelythick gold layer 146. An advantage of thenon-encapsulated lead 148 shown inFIG. 3 is that it requires lesser amounts of gold. But this advantage comes with the disadvantages of additional process steps needed in connection with the masking of the non-encapsulated surfaces, a seam, and associated manufacturing yield impacts. - So-called additive processes are also known and used to manufacture wireless suspensions. However, the plated ground feature manufacturing process described above is generally not suitable for effective use in connection with additive processes of these types.
- There remains a need for efficient processes for producing suspension components with electroplated portions or layers having different thicknesses. Such a process that can be incorporated into an additive wireless suspension component manufacturing process would be especially desirable.
- One embodiment of the invention is a method for electroplating a component for a disk drive suspension having first and second opposing surfaces with exposed conductor regions. The method includes providing an electroplating system having a bath of electroplating solution including a plating material and first and second anodes in the bath. The suspension component is positioned in the bath between the first and second anodes. A first electroplating current is applied between the first anode and the exposed conductor regions on the first surface to plate a layer of conductive plating material on the exposed conductor regions on the first surface. A second electroplating current is applied between the second anode and the exposed conductor regions on the second surface to plate a layer of conductive plating material on the exposed conductor regions on the second surface.
- Differing currents can be applied between the first anode and the component and the second anode and the component to achieve layers of plating material on the first and second surfaces having differing thicknesses. The currents can differ in magnitude or duration. Additional layers of material having the same or differing thicknesses can be plated onto the component during subsequent passes of the component through the system.
- Another embodiment of the invention is a system for simultaneously electroplating portions of opposing first and second surfaces of a disk drive suspension component. The system includes an electroplating container holding an amount of electroplating solution, first and second anodes and structure for supporting the component between the first and second anodes. Power supply means are in electrical communication with the anodes to cause the anodes to produce electrical currents between the anodes and the suspension component.
-
FIG. 1 is a schematic illustration of the components of a prior art plating system located in the plating tank. -
FIG. 2 illustrates a cross section of a prior art conductive lead plated with a plurality of conductive plating layers having differing thicknesses. -
FIG. 3 illustrates an alternative prior art conductive lead having an alternative pattern of conductive plating layers. -
FIG. 4 is a schematic representation of a major surface of a suspension component having conductive traces of the type to be plated according to one embodiment of the invention. -
FIG. 5 is a schematic representation of an opposing major surface of the suspension component ofFIG. 4 . -
FIG. 6 is a side elevation view of the suspension component taken along line 6-6 ofFIG. 4 . -
FIG. 7A is a schematic representation of the suspension component ofFIG. 6 having plating material formed onto opposing surfaces of the traces such that the plating material has differing thicknesses on the opposing surfaces in accordance with one embodiment of the invention. -
FIG. 7B is a detailed illustration of a portion of the suspension component ofFIG. 7A . -
FIG. 8A is a schematic representation of the suspension component ofFIG. 6 having plating material formed onto opposing surfaces of the traces such that the plating material has differing thicknesses on the opposing surfaces of the traces according to another embodiment of the invention. -
FIG. 8B is a detailed illustration of a portion of the suspension component ofFIG. 8A . -
FIG. 9 is a schematic representation of a single pass, dual thickness plating system in accordance with one embodiment of the invention, having anodes positioned on either side of a suspension component to simultaneously plate layers of conductive material of differing thicknesses onto two sides of the suspension component. -
FIG. 10 is a schematic representation of another embodiment of the plating system ofFIG. 9 . -
FIG. 11 is a schematic representation of still another embodiment of the plating system ofFIG. 9 having a plurality of anodes disposed on either side of the suspension component. -
FIG. 12 is a schematic representation of another alternative embodiment of the plating system ofFIG. 11 having a plurality of power sources attached to the anodes disposed on either side of the suspension component. - Referring to
FIG. 9 , a singlepass electroplating system 10 capable of providing dual sided, dual thickness plating according to one embodiment of the invention includes a plating container ortank 12 with platingsolution 14 located therein. Electroplatingsystem 10 is configured for use in connection with a reel-to-reel electroplating process for plating suspension components such as wireless flexures. Electroplatingsystem 10 includes an unwindmember 26, such as a dispensing reel which unwinds aweb 20 of material into thetank 12 so that it is in contact with the plating solution. Arewind member 28 such as a receiving reel rewinds theweb 20 of material after it has moved through thetank 12.Web 20 is a sheet of materials that includes a plurality ofsuspension components 40, previously prepared for the plating process of the current invention, as is described below. The web 20 (and suspension components 40) have a first surface orside 22 and second surface orside 24 opposing the first side. Theplating solution 14 can include gold for plating selected portions of the suspension components. Alternatively, theplating solution 14 can include other plating materials, such as nickel, silver, copper, palladium, solder materials, or alloys including any of these materials. - A pair of
anodes 30 are positioned in theplating solution 14 such that one of the anodes is positioned adjacent thefirst side 22 of theweb 20 and the other anode is positioned adjacent thesecond side 24 of theweb 20. Apower source 32, such as a rectifier or other suitable device, is in electrical communication with theanodes 30 viaelectrical conductors 34. Thepower source 32 provides electrical signals to each of theanodes 30. Thepower source 32 can provide the same or differing electrical signals (e.g., the same or different levels, magnitudes, types, and/or duration of signals) to theindividual anodes 30. When thepower source 32 provides an electrical signal to theanodes 30, the anodes produce an electric current in theplating solution 14. Thesuspension components 40 ofweb 20 include exposed conductive material accessible from each of theirfirst side 22 andsecond side 24, which is described in more detail below. The exposed conductive material functions as a cathode. When current is produced between theanodes 30 and the cathode, conductive material in theplating solution 14 is plated onto the exposed conductive material ofweb 20. - The thickness of the plating material applied onto the exposed conductive material of
suspension components 40 can be controlled by the amount of plating current that flows between theanodes 30 and the exposed conductive material of theweb 20 and the length of time that the current is applied to the suspension components. As described above, different portions of thesuspension component 40 may preferably include plating having differing thicknesses. Because the current produced by each anode can be applied at differing levels and lengths of time, the plating on exposed conductor surfaces accessible from thefirst side 22 can have a thicker layer of plating material than exposed conductor surfaces accessible from thesecond side 24, or vice versa, as desired. Therefore, by controlling the amount of current applied and/or the length of time that the current is applied between the first and second anodes and theweb 20, theelectroplating system 10 can providesuspension components 40 with varying thicknesses of conductive plating material on different surfaces in a single plating process. -
FIGS. 4-6 are schematic representations ofsuspension component 40 that can be plated by the plating process of the current invention. Conventional or otherwise known processes can be used to manufacture components such assuspension 40.Suspension component 40 can have any of a variety of conventional or otherwise known structures. By way of example, the illustrated embodiment ofsuspension component 40, prior to being plated, includes aspring metal layer 42 made of stainless steel or other similar materials. Adielectric layer 44 made of polyimide or other suitable materials extends over a portion of thespring metal layer 42 on thefirst side 22 and conductive leads 46 are formed onto the dielectric layer. Conductive leads 46 can be made of any suitable conductive material, including copper or a copper alloy. Conductive leads 46 have first and secondmajor surfaces dielectric layer 44 in one embodiment, and the secondmajor surface 47 of the conductive leads contact the dielectric layer. Acover layer 48 is disposed over portions the firstmajor surface 45 andsides 43 of the conductive leads 46 to protect the conductive leads. Those portions of the conductive leads 46 covered by thecover layer 48 are typically not plated.Cover layer 48 can be made of the same or similar materials asdielectric layer 44. -
Suspension component 40 can includeconductive pads 50, which are portions of conductive leads 46 that are supported bydielectric layer 44 andspring metal layer 42 and are exposed, that is, not covered bycover layer 48.Conductive pads 50 can be located in a variety of locations on the conductive leads 46 and an individual conductive lead can have any number of conductive pads. Theconductive pads 50, although shown as having the same width as other portions of the conductive leads 46, can have other widths, sizes, or shapes.Conductive pads 50 can be used to provide electrical communication between the conductive leads 46 and electrical components located either on or external to the suspension component. For example, aconductive lead 46 can be electrically connected to a magnetic head on a slider (not shown), electrical or electronic drive components (not shown) located on or external to thesuspension component 40, microactuators (not shown), or other conductive leads. - The illustrated embodiment of
suspension component 40 also includes flying leads 52. The flying leads 52 are a portion of the conductive leads 46 uncovered bycover layer 48 and unsupported by thedielectric layer 44 or thespring metal layer 42. The flying leads 52 can extend over anaperture 54 formed through thedielectric layer 44 and thespring metal layer 42. Thus, the secondmajor surface 47 of each of the flying leads 52 is exposed on thesecond side 24 of thesuspension component 40. Theportion 56 of theaperture 54 that extends through thedielectric layer 44, in one embodiment, is smaller than theportion 58 of the aperture that extends through thespring metal layer 42 so that the dielectric layer extends over the spring metal layer.Aperture 54 can be formed through a variety of known methods, including, for example, etching thespring metal layer 42 anddielectric layer 44. Thesuspension component 40 illustrated inFIGS. 4-6 is a schematic representation. Actual components can have other structures such as flexures, gimbals, and spring regions, and multiple features such asconductive pads 50 and flying leads 52. For example, a portion of the conductive lead can extend outside of the width of a component(not shown) and thereby be exposed on both the first side and second side of the component. - FIGS. 7A-B illustrate a
suspension component 40 after it is plated inelectroplating system 10 according-to one embodiment of the invention. Alayer 60 of plating material is applied to theconductive pads 50 and the flying leads 52 on thefirst side 22 of thesuspension component 40. In addition, alayer 70 of plating material is applied to that portion of the flying leads 52 accessible from thesecond side 24 of thesuspension component 40. Thelayer 70 on the flying leads 52 has athickness 72 that is greater than athickness 62 of thelayer 60. - Alternatively, the
thickness 62 of thelayer 60 can be the same or greater than thethickness 72 of thelayer 70. As described above, thelayers FIG. 9 , the type and duration of electrical signals supplied from thepower source 32 to theindividual anodes 30 positioned within theplating solution 14 will determine the thickness of the plating material oflayers FIG. 5 ) of theconductive pads 50 are effectively plated along withfirst layer 60. Thesides 43 of the flying leads 52 are effectively plated along withlayer 60 and/orlayer 70 as current leakage from each side will extend to the sides of the flying leads (not shown). As a result, the conductive leads are encapsulated, aslayers sides 43, thereby leaving no seams on the flying leads 52. - FIGS. 8A-B illustrate a
suspension component 240 after it is plated inelectroplating system 10 according to another embodiment of the invention.Suspension component 240 includesplating material 260 applied toconductive pads 250 and flying leads 252 on afirst side 222 of thesuspension component 240. In addition,suspension component 240 includesplating material 270 applied to thesecond side 247 of the flying leads 252, which are exposed to asecond side 224 of thesuspension component 240. Theplating material 260 includes afirst layer 264 and asecond layer 266 and theplating material 270 includes afirst layer 274 and asecond layer 276. Thefirst layers second layers first layers second layers first layers - The
first layers suspension component 240 by electroplating the layers as shown inFIG. 9 and described above. Theplating solution 14 includes the plating material that forms thefirst layers first layers second layers second layers system 10, with a different plating solution. Additional layers, applied in subsequent plating operations, can be similarly added without departing from the scope of the invention. With the exception of the differences discussed above, thesuspension component 240 is similar tosuspension component 40 and similar features are identified using reference numbers in the 2XX series. -
FIG. 10 illustrates a single pass, dual-sidedelectroplating system 310 in accordance with another embodiment of the invention.Electroplating system 310 includes aplating tank 312 with platingsolution 314. Afirst anode 330 is positioned in theplating solution 314 adjacent thefirst side 322 ofweb 320 and a second anode 331 is positioned in theplating solution 314 adjacent thesecond side 324 ofweb 320.First power source 332 is in electrical communication withfirst anode 330 andsecond power source 333 is in electrical communication with second anode 331. Separate power sources such as 332 and 333 can provide improved control of the amount and duration of current applied to the first and second sides, respectively, thereby more precisely determining the thicknesses of the layers of plating material applied to the opposing sides of components or portions of components such as described above in relation tocomponent 40. With the exception of the differences discussed above, theelectroplating system 310 can be the same as or similar to theelectroplating system 10 described above and similar features are identified using reference numbers in the 3XX series. -
FIG. 11 illustrates a single pass, dual-sidedelectroplating system 410 in accordance with still another embodiment of the invention.Electroplating system 410 includes aplating tank 412 with platingsolution 414. A plurality ofanodes 430 are positioned in theplating solution 414 adjacent thefirst side 422 ofweb 420 and a plurality ofsecond anodes 431 are positioned in theplating solution 414 adjacent thesecond side 424 ofweb 420.Power source 432 is in electrical communication with the plurality offirst anodes 430 andsecond anodes 431. The plurality offirst anodes 430 andsecond anodes 431 can improve the plating coverage by providing a more consistent current at the exposed conductive portions of theweb 420 as the web is dispensed between unwindmember 426, andrewind member 428. With the exception of the differences discussed above, theelectroplating system 410 can be the same as or similar to theelectroplating system 10 described above and similar features are identified using reference numbers in the 4XX series. -
FIG. 12 illustrates a single pass, dual-sidedelectroplating system 510 in accordance with still another embodiment of the invention.Electroplating system 510 includes aplating tank 512 with platingsolution 514. A plurality ofanodes 530 are positioned in theplating solution 514 adjacent thefirst side 522 ofweb 520 and a plurality ofsecond anodes 531 are positioned in theplating solution 514 adjacent thesecond side 524 ofweb 520.First power source 532 is in electrical communication with the plurality offirst anodes 530 and second power source 533 is in electrical communication with the plurality ofsecond anodes 531. The first andsecond power sources 532 and 533 can provide improved control of the current flowing from the plurality offirst anodes 530 andsecond anodes 531, thereby further refining the amount and duration of current applied to theweb 20. With the exception of the differences discussed above, theelectroplating system 510 can be the same or similar to theelectroplating system 410 and similar features are identified using reference numbers in the 5XX series. - The invention offers important advantages. It enables the simultaneous electroplating of different portions of suspension components, including portions on different sides of the components to different and independently controlled thicknesses. Fully encapsulated traces can be produced without additional consumption of gold or other plating material. The method is efficient, and can be used in connection with additive manufacturing processes.
- Although the present invention has been described with reference to preferred embodiments, those skilled in the art will recognize that changes can be made in form and detail without departing from the spirit and scope of the invention. For example, the several anodes can be spaced from one another along the length of the web of components rather than being opposite one another as shown in
FIGS. 9-12 .
Claims (20)
1. A method for electroplating a component for a disk drive suspension, comprising:
providing an electroplating system having a bath of electroplating solution including a plating material and first and second anodes in the bath;
providing a suspension component having first and second opposing surfaces with exposed conductor regions;
positioning the suspension component in the bath of electroplating solution between the first and second anodes;
applying a first electroplating current between the first anode and the exposed conductor regions on the first surface to plate a first layer of conductive plating material on the exposed conductor regions on the first surface; and
applying a second electroplating current between the second anode and the exposed conductor regions on the second surface to plate a first layer of conductive plating material on the exposed conductor regions on the second surface.
1. The method of claim 1 , wherein applying the first and second electroplating currents causes the first and second surfaces to be plated with first layers of plating material having differing thicknesses.
2. The method of claim 1 , wherein applying the first and second electroplating currents causes the first and second surfaces to be plated with first layers of plating material having about the same thickness.
3. The method of claim 1 , wherein applying the first and second electroplating currents includes applying a greater current between one of the first and second anodes and the exposed conductor regions than the current applied between the other of the first and second anodes and the exposed conductor regions.
5. The method of claim 1 , wherein applying the first and second electroplating currents includes applying current between one of the first and second anodes and the exposed conductor regions for a longer period of time than the current applied between the other of the first and second anodes and the exposed conductor regions.
6. The method of claim 1 , wherein applying the first electroplating current between the first anode and the exposed conductor regions is performed simultaneously with the application of the second electroplating current between the second anode and the exposed conductor regions.
7. The method of claim 1 , wherein applying the first and second electroplating currents includes applying the first and second electroplating currents at different times.
8. The method of claim 1 , wherein applying the second electroplating current includes applying the second electroplating current after applying the first electroplating current.
9. The method of claim 1 , further comprising plating a second layer of conductive plating material onto the first layer of conductive plating material on the first surface and plating a second layer of conductive plating material onto the first layer of conductive plating material on the second surface.
10. The method of claim 9 wherein the second conductive layer on the first surface has a different thickness than the first conductive layer on the first surface.
11. The method of claim 9 , wherein the second conductive layer on the first surface has a different thickness than the second conductive layer on the second surface.
12. A system for electroplating portions of opposing first and second surfaces of a disk drive suspension component, comprising:
an electroplating container holding an amount of electroplating solution;
a first anode;
a second anode;
structure for supporting the suspension component between the first and second anodes; and
power supply means in electrical communication with the first and second anodes to cause the first anode to produce a first electroplating current between the first anode and a first side of the suspension component and to cause the second anode to produce a second electrical current between the second anode and a second side of the suspension component.
13. The system of claim 12 further comprising a third anode spaced apart from first and second anodes, wherein the third anode is in electrical communication with power supply means to produce an electrical current between the third anode and one of the first and second sides of the suspension component.
14. The system of claim 12 and further comprising:
a web of material, including the suspension component;
an unwind member for dispensing the web of material into the plating solution; and
a rewind member for receiving the web of material dispensed through the plating solution;
wherein the first and second anodes are positioned between the unwind and rewind members.
15. The system of claim 12 wherein the electroplating solution comprises gold.
16. The system of claim 12 wherein the electroplating solution comprises nickel.
17. The system of claim 12 wherein the electroplating solution comprises silver.
18. The system of claim 12 wherein the electroplating solution comprises copper.
19. The system of claim 12 wherein the electroplating solution comprises palladium.
20. The system of claim 12 wherein the electroplating solution comprises a solder material.