US20060124283A1 - Fluid-handling apparatus with corrosion-erosion coating and method of making same - Google Patents
Fluid-handling apparatus with corrosion-erosion coating and method of making same Download PDFInfo
- Publication number
- US20060124283A1 US20060124283A1 US11/011,895 US1189504A US2006124283A1 US 20060124283 A1 US20060124283 A1 US 20060124283A1 US 1189504 A US1189504 A US 1189504A US 2006124283 A1 US2006124283 A1 US 2006124283A1
- Authority
- US
- United States
- Prior art keywords
- coating
- sea water
- corrosion
- wetted surfaces
- erosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Inlet surfaces of a fluid-handling apparatus, such as a heat exchanger, are often prone to corrosion and erosion due to the high velocities of incoming fluid. The present disclosure includes a fluid-handling apparatus with a plurality of wetted surfaces of which a first portion is corrosion-erosion prone and a second portion is non-corrosion-erosion prone. The first portion is coated with a corrosion-erosion coating that is harder than the first portion. Less than all of the wetted surfaces are coated.
Description
- The present invention relates generally to fluid-handling apparatuses, and more specifically to heat exchangers with a corrosive-erosion resistant coating and a method of making same.
- There are various uses for heat exchangers known in the art. For instance, heat exchangers, often referred to as charge air coolers, use a coolant to cool compressed air exiting a turbocharger before the air is injected into an engine. In commercial or pleasure marine crafts, sea water is often used as the coolant. The sea water will flow into a sea water inlet manifold before flowing into a plurality of sea water passages, and the air will flow into an air inlet manifold before flowing into a plurality of air passages. The sea water passages are generally oriented perpendicularly to the air passages such that the heat within the air can be exchanged with sea water through walls of the sea water and the air passages. The sea water passages and the air passages are defined by a core of the heat exchanger. The sea water will increase in temperature and the air will decrease in temperature as the sea water and air simultaneously pass through the core of heat exchanger.
- Using sea water as the coolant can present a challenge due to the sea water's corrosive nature and tendency to contain abrasives such as sand and silt and other forms of deposits including sea weeds, sea shell fragments, animal components, etc. As the sea water flows from the inlet manifold into the plurality of smaller sea water passages, the flow of the sea water is turbulent. Thus, the sea water will directly contact at a relatively high velocity inlet surfaces defining the sea water inlet manifold before flowing into the sea water passages. Due to the high velocity and the corrosive nature of the sea water, the sea water contacting the inlet surfaces will impinge the surfaces. The impingement can cause corrosion and erosion, and thus, damage the surfaces of the inlet manifold, including a core surface defining inlets of the sea water passages. Over time, the damage can lead to holes, causing leakage of the sea water and, thus, premature failure of the heat exchanger. For instance, the corrosion and erosion can create holes in the surfaces separating the hot air passages and the sea water inlet manifold or passages, causing leaking of the sea water into the air passages.
- One method known in the art of avoiding heat exchanger failure due to inlet surface corrosion-erosion and impingement is to use robust materials that offer corrosion-erosion resistance. For instance, a heat exchanger set forth in U.S. Pat. No. 5,323,849, issued to Korczynski, Jr. et. al., on Jun. 28, 1994, includes sea water wetted heat exchanger components that are made from corrosion and erosion-resistant materials. Although the Korczynksi heat exchanger includes corrosion and erosion-resistant sea water inlet surfaces, the heat exchanger also includes other components, such as the tubes defining the sea water passages, made from corrosion-erosion resistant materials. However, the tubes are less prone to corrosion and erosion than the inlet surfaces. The sea water contacting the inlet surfaces is turbulent; whereas, the sea water flow through the tubes is generally laminar. The turbulent flow causes more impingement which leads to corrosion and erosion than does the laminar flow.
- Manufacturing heat exchanger components from corrosion and erosion-resistant materials can be more costly than using traditional materials. Further, the corrosion-erosion resistant materials can introduce a heat transfer penalty due to their reduced thermal conductivity. Most of the heat transfer occurs through the material separating the air and sea water passages, which is also where there is the least amount of impingement and corrosion-erosion related problems due to the flow of the sea water. Thus, by manufacturing all of the sea water wetted components out of corrosion-erosion resistant materials, rather than just the corrosion-erosion prone sea water inlet surfaces, the cost of the heat exchanger and the heat transfer penalty is unnecessarily increased while potentially also reducing heat transfer performance.
- The present disclosure is directed at overcoming one or more of the problems set forth above.
- According to one aspect of the present disclosure, a fluid-handling apparatus includes a an apparatus body including a plurality of wetted surfaces of which a first portion is corrosion-erosion prone and a second portion is non-corrosion-erosion prone. The first portion of the wetted surfaces is coated with a corrosion-erosion resistant coating that is harder than the first portion. Less than all of the wetted surfaces are coated.
- In another aspect of the present disclosure, an engine system with marine applications includes an engine fluidly connected to a heat exchanger. The heat exchanger defines a sea water inlet that is fluidly connected to a plurality of wetted surfaces of which a first portion is corrosion-erosion prone and a second portion is non-corrosion-erosion prone. The first portion is coated with a corrosion-erosion resistant coating that is harder than the first portion. Less than all of the wetted surfaces are coated.
- In yet another aspect of the present disclosure, a heat exchanger is made by assembling a plurality of components to include a plurality of wetted surfaces. Corrosion-erosion prone wetted surfaces are distinguished from non-corrosion-erosion prone surfaces. The corrosion-erosion prone wetted surfaces are coated with a corrosion-erosion resistant coating that is harder than the corrosion-erosion prone wetted surfaces.
-
FIG. 1 is a schematic representation of an engine system, according to the present disclosure; -
FIG. 2 is a sectioned side diagrammatic representation of a heat exchanger within the engine system ofFIG. 1 ; -
FIG. 3 is an isometric view of a sectioned core of the heat exchanger ofFIG. 2 ; and -
FIG. 4 is a table of example corrosion-erosion resistant coatings applied to the heat exchanger within the engine system ofFIG. 1 . - Referring to
FIG. 1 , there is shown a schematic representation of anengine system 10 for marine applications, according to the present disclosure. Theengine system 10 includes anengine 11 that includes anengine housing 21 defining anair inlet 22. Theengine system 10 also includes aturbocharger 12 that includes anair outlet 23 fluidly connected to theair inlet 22 of theengine 11 via anair line 15. Theturbocharger 12 draws ambient air through anair filter 13 and into anair inlet 44 of theturbocharger 12. Within theturbocharger 12, the air is compressed and then delivered to theengine 10 via theair line 15. An upstream portion of theair line 15 fluidly connects a fluid-handling apparatus, being aheat exchanger 14, with theair outlet 23 of theturbocharger 12. A downstream portion of theair line 15 fluidly connects theheat exchanger 14 with theair inlet 22 of theengine 11. Theheat exchanger 14 is also in fluid communication with apump 18 that can supply sea water to theheat exchanger 14 via asea water line 19. Theheat exchanger 14 includes aheat exchanger body 24 that defines anair inlet 25, anair outlet 26, asea water inlet 27 and asea water outlet 28. - The temperature of the compressed air exiting the
turbocharger 12 is significantly increased due to the compression within theturbocharger 12. Thus, theheat exchanger 14, often referred to as a charge air cooler, will cool the compressed air, via heat exchange with the sea water, before it is injected into theengine 11. Sea water is preferably used as the coolant due to its accessibility, abundance and lower temperatures, but it should be appreciated that theheat exchanger 10 could use various other coolants. By cooling the compressed air, the density of the air is increased, allowing more air, and thus more oxygen, to occupy the volume of the cylinder. When the cooled compressed air is injected into theengine 11, the increased amount of oxygen within the cylinder can burn, resulting in increased engine power. The exhaust created by the combustion within theengine 11 will continue to power theturbocharger 12, and the process can repeat itself. Although the present disclosure is illustrated for theengine system 10 including theturbocharger 12, it should be appreciated that the heat exchanger could be used for other cooling applications in engine systems with or without turbochargers. For instance, the heat exchanger could be used to cool hot exhaust exiting the combustion chamber of the engine. - Referring to
FIG. 2 , there is shown a sectioned side diagrammatic representation of theheat exchanger 14. Acore 30 is positioned within a space defined by the heat exchanger body 24 (shown inFIG. 1 ). Although thecore 30 is preferably a “bar and plate”style core 30, it should be appreciated that the present invention also contemplates the heat exchanger including a “tube and fin” style core of the type known in the art, or any other suitable heat exchange structure. Thecore 30 includes acore body 42 that defines a plurality of air passages 34 (shown inFIG. 3 ) and a plurality ofsea water passages 36. Thecore body 42 and theheat exchanger body 24 define a seawater inlet manifold 16 and a seawater outlet manifold 17 that direct sea water streams into and out of the core 30, and a sea watermiddle manifold 20 that changes the direction of the sea water flow. The sea water inlet, outlet andmiddle manifolds housing surface core surface sea water passages 36 are in fluid communication with thesea water inlet 27 and thesea water outlet 28 via the seawater inlet manifold 16 and the seawater outlet manifold 17, respectively. As illustrated by the arrows, the sea water will flow through theinlet 27 into the seawater inlet manifold 16, through a first portion 36 a of thesea water passages 36 to themiddle manifold 20 in which the sea water changes direction, through a second portion 36 b ofsea water passages 36 and to theoutlet 28 via the seawater outlet manifold 17. Although the sea water makes two passes through the illustratedcore 30, the present disclosure contemplates use in heat exchangers through which the sea water makes any number of passes, including only one. It should also be appreciated that, although not shown, an air inlet manifold and air outlet manifolds are attached to opposite ends of the core 30 to which thesea water manifolds air passages 34. - Still referring to
FIG. 2 , theheat exchanger body 24, including thecore body 42, include a plurality of wetted surfaces 43. In the illustratedheat exchanger 14, the plurality of wettedsurfaces 43 include, but is not limited to, the core surfaces 16 b, 17 b and 20 b and thehousing surfaces sea water manifolds sea water passages 36. Afirst portion 43 a of the wetted surfaces 43 are corrosion-erosion prone 43 a and asecond portion 43 b of the wetted surfaces 43 are non-corrosion-erosion prone. Those skilled in the art will appreciate that, although all of the wetted surfaces 43 may be subjected to some corrosion and erosion due to the harsh environment caused by the sea water, thefirst portion 43 a of the wetted surfaces 43 subject to direct impingement from the high velocity flow of sea water is significantly more corrosion and erosion prone than thesecond portion 43 b subject to contact from less turbulent flow of the sea water. Thefirst portion 43 a includes at least one seawater inlet surface 39. Thesurfaces 39 include thesurfaces inlet manifold 16 and themiddle manifold 20 being that themanifolds sea passages 36. Preferably, the core surfaces 17 b and thehousing surfaces 17 a defining theoutlet manifold 17 are also included within thefirst portion 43 a. Because the sea water flowing through thesea water passages 36 has a laminar flow, the sea water is not directly impinging the surfaces defining thesea water passages 36. Thus, thesecond portion 43 b that is non-corrosion-erosion prone includes the surfaces of thesea water fins 35 defining thesea water passages 36. Only thefirst portion 43 a of the wetted surfaces 43 is coated with a corrosion-erosionresistant coating 40, and thus, less than all of the wetted surfaces 43 are coated. The corrosion-erosionresistant coating 40 is harder than the corrosion-erosionprone portion 43 a. From one point of view, the corrosion prone surfaces are flow direction changing surfaces, whereas the non-corrosion prone surfaces are generally parallel to the local flow direction. - Referring to
FIG. 3 , there is shown an isometric view of a sectionedcore 30 of theheat exchanger 14 inFIG. 2 . Thecore body 42 includesmultiple separator sheets 32,air fins 33 andsea water fins 35, although the present invention contemplates a heat exchanger including only one separator sheet positioned between an air fin and a sea water fin. Theseparator sheets 32 are preferably alternatively separated from one another by theair fins 33 and thesea water fins 35 in order to maintain the air flow separate from the sea water flow. Theair fins 33 separate theair passages 34 from one another, and thesea water fins 35 define and separate thesea water passages 36 from one another. Thus, thesea water fins 35 include the non-corrosion-erosionprone surfaces 43 b. Theair fins 33 are preferably oriented substantially perpendicularly to thesea water fins 35 such that the flow of the air transverses the flow of the sea water. Although it should be appreciated that some of the air passages and sea water passages can be oriented to one another at various angles, the air flow still transverses the sea water flow. - Further, the
core body 42 includes long enclosure bars 37 that act as end surfaces for eachsea water fin 35 and provide a surface for attaching themanifolds core body 42. Thecore body 42 also includes short enclosure bars 38 (shown inFIG. 2 ) that act as end surfaces for eachair fin 33 to protect theair fins 33 andair passages 34 from sea water.Side sheets 31 enclose ends of the core 30, and mountings, such as load stops 29, are attached to theside sheets 31 to provide a means of securing theheat exchanger 14 within theengine system 10. The separate components of the core 30 can be made into one unit by various methods known in the art, such as brazing the assembled core. Thus, the core surfaces 16 b, 17 b and 20 b (shown inFIG. 2 ) include surfaces of various components, including an outer surface of theshort bars 38 separating theair fins 33 from thesea water manifolds separator sheets 32, edge surfaces of thelong bars 37, and edge surfaces of thesea water fins 35. - Referring to
FIGS. 1-3 , in the illustratedheat exchanger 14, thesea water fins 35, theseparator sheets 32, thelong bars 37 and the short enclosure bars 38 are made from copper due to the heat transfer capability of the copper. Thus, thefirst portion 43 a being corrosion-erosion prone is generally made from copper. However, it should be appreciated that the present disclosure contemplates use with corrosion-erosion prone wetted surfaces made from metals other than copper. Thecoating 40 preferably includes a metal alloy that is similar to the metal of the corrosion-erosionprone surfaces 43 a, illustrated as copper. Thecoating 40 preferably is sufficiently similar to thesurfaces 43 a such that thecoating 40 and the corrosion-erosion prone wettedsurfaces 43 a are galvanic compatible. Those skilled in the art will appreciate that the galvanic compatibility of thecoating 40 and thesurfaces 43 a is dependent on various factors, including, but not limited to, the difference in the galvanic potentials of thecoating 40 and thesurfaces 43 a, whether thecoating 40 or thesurface 43 a acts as an anode, the area ofcoating 40 compared to the area of the electrolyte, and the type of electrolyte, being sea water. Although the copper-nickel alloys set forth inFIG. 4 are slightly more noble than the copper surface on which they are coated, the alloys are sufficiently galvanic compatible with thesurfaces 43 a. In each of the example coatings set forth in Table I, thecoating 40 includes a metal alloy principally comprised of copper. - Further, the
coating 40 preferably includes a metal alloy with a coefficient of thermal expansion sufficiently similar to a coefficient of thermal expansion of the corrosion-erosionprone portion 43 a of the wetted surfaces 43 so that thecoating 40 remains attached over a pre-determined temperature range. The predetermined temperature range is the range of temperatures to which the corrosion-erosionprone surfaces 43 a are subjected. For instance, in the illustrated heat exchanger, the compressed air is entering theair passages 34 at approximately 200° C. and exiting theair passages 34 at approximately 40° C. Because the air flowing through theair passages 34 transverses the core surfaces 16 b, 17 b and 20 b, the sea water core surfaces 16 b, 17 b and 20 b are subject to temperature range of 49-200° C. Thecoating 40 is principally comprised of the same material as thesurfaces 43 a, being copper. Those skilled in the art will appreciate that alloys other than copper alloys, such as certain stainless steel alloys, may be used within thecoating 40 applied to the copper surfaces 43 a as long as the alloy include a similar coefficient of thermal expansion as copper. - The
coating 40 is preferably 0.005 to 0.015 inches (127-381 micrometers), but can have a thickness between 0.003-0.02 inches (75-500 micrometers). Thecoating 40 should be sufficiently thick to withstand the impingement of the sea water, but not too thick to create a substantial heat transfer penalty, material waste and unnecessary expense. - Referring to
FIG. 4 , there is shown a table including five example compositions of thecoating 40 applied to theheat exchanger 14. Although thecoating 40 could include any type of material that is harder than the corrosion-erosion prone wettedsurfaces 43 a, is galvanic compatible with thesurfaces 43 a in the relevant cooling liquid (e.g. sea water) and has a similar coefficient of thermal expansion as thesurfaces 43 a, such as certain stainless steel alloys, preferably thecoating 40 includes a copper-based alloy. Preferably, the copper-based alloy includes a copper-nickel alloy with a nickel concentration between 9% and 40%. The copper can provide sufficient heat transfer between sea water and the air, and the nickel protects the corrosion-erosionprone surfaces 43 a from impingement that can lead to corrosion and erosion. Thecoating 40 with the nickel is harder than the corrosion-erosionprone surfaces 43 a upon which thecoating 40 is applied. For instance,example coating 1 includes the preferred version of thecoating 40 that includes a copper-nickel alloy with a nickel concentration of approximately 10%. Those skilled in the art will appreciate thatexample coating 1 is a commercially available alloy, specifically alloy 70600, often referred to as 90-10% copper nickel. In addition to the copper and nickel,example coating 1 includes other alloying metals, including iron and manganese. The iron contributes the corrosion resistance and the strength of the coating 40 a, and the manganese contributes to the stability of the coating 40 a. Moreover, because thecoating 40 includes almost 90% copper, the coating 40 a is sufficiently similar to the copper manifold surfaces 16 a, 16 b, 17 a, 17 b, 20 a and 20 b to which the coating 40 a is applied. Thus, thecoating 40 is galvanic compatible with thesurfaces 43 a, thereby providing a stable coating 40 a even in relatively highly polluted waters, and will not expand at a sufficiently different rate than thesurfaces 43 a despite the heat fluctuations within theheat exchanger 14. Also,example coating 1 is resistant to biological fowling in polluted waters. -
Example coating 2 includes a copper-nickel alloy that includes approximately 70% copper and approximately 30% nickel. Those skilled in the art will appreciate thatexample coating 2 is a commercially available alloy, specifically alloy 71600, often referred to as 70-30% copper-nickel. Similar toexample coating 1, in addition to the copper and nickel,example coating 2 includes other alloying metals, including iron and manganese.Example coating 2 is harder than the corrosion-erosionprone surfaces 43 a upon which thecoating 40 is applied.Example coating 3 includes a 60% copper—40% nickel alloy.Example coating 3 is not a standard copper alloy, but rather a powder commercially available for physical disposition spray applications. Although coating 3 could include other minor alloying metals like those used in example 1 and example 2,coating 3 is illustrated as including 60% copper and 40% nickel. Although the coatings in examples 2 and 3 will protect the corrosion-erosionprone surfaces 43 a, the 60-40% copper—nickel alloys are generally more expensive than the 90-10% copper nickel alloys, as used in example 1. Moreover,example coatings coating 40 of Example 1 in highly polluted waters. -
Example coating 4 includes a 85-15% copper nickel alloy. Similar to example coatings 1-3,example coating 4 includes copper to transfer the heat between the air and the sea water, and nickel to resist impingement, thereby, providing corrosion and erosion resistance. Moreover,example coating 4 includes minor alloying metals and is commercially available as alloy 72200. -
Example coating 5 includes an aluminum-bronze alloy that includes 14% or less aluminum, 2% or less manganese, 6% or less nickel, and 5% or less iron. The remaining concentration would include copper and/or other minor alloying elements. Those skilled in the art will appreciate that theexample coating 5 could includes standard aluminum-bronze alloys commercially available could be used.Example coating 5 is a commercially available aluminum bronze alloy, being alloy 63000. The aluminum aids in corrosion resistance while the iron and nickel aids in impingement resistance. As with theother coatings 40 a-c,example coating 5 preferably includes manganese and iron. - Referring to
FIGS. 1-3 , a method of making theheat exchanger 14 will be discussed. Although theheat exchanger 14 is part of theengine system 10 with marine application and is a “bar and plate” type heat exchanger, those skilled in the art should appreciate that the method of the present disclosure could apply to various types of heat exchangers, including the “tube and fin” and “tube and shell” type, used in various applications. A plurality ofcomponents air fins 33 are oriented perpendicularly to the plurality ofsea water fins 35, and theair fins 33 andsea fins 35 are alternatively stacked and separated from one another with theseparator sheets 32. The short bars 38 are positioned at the closed ends of theair fins 33 in order to protect theair fin 33 from the incoming sea water. Thecomponents - After the
core 30 is brazed, the corrosion-erosionresistant coating 40 is applied to less than all of the wetted surfaces 43. The corrosion-erosionprone surfaces 43 a are distinguished from the non-corrosion-erosionprone surfaces 43 b, and only the corrosion-erosionprone surfaces 43 a will be coated. Although the corrosion-erosionprone surfaces 43 a may differ between different types of heat exchangers, the corrosion-erosionprone surfaces 43 a includes the wettedsurface 43 that are subjected to direct impingement from the high velocity flow of the sea water. The non-corrosion-erosionprone surfaces 43 b includes the wetted surfaces 43 with which the sea water does not directly impinge. Thesurfaces manifolds sea water passages 36; whereas, the surfaces of thesea fins 35 defining thesea passages 36 are not directly impinged by the sea water due to the laminar flow of the sea-water through thepassages 36. In the illustratedheat exchanger 14, the sea water makes two passes through thecore 30. Not only will the turbulent flow of the sea water within the inlet and outlet manifolds 16 and 17 cause the sea water to directly impinge the manifold surfaces 16 a, 17 a, 16 b and 17 b before being directed into and out of thesea water passages 36, thehousing surface 20 a of themiddle manifold 20 directs the sea water flow from the first portion 36 a to the second portion 36 b of thepassages 36, and thus, is also subject to direct impingement. It should be appreciated that the present disclosure could apply to heat exchangers through which the sea water makes any number of passes, including only one pass. Regardless of the number of sea water manifolds, preferably the housing surfaces, along with the core surfaces, defining each manifold are coated. Thus, thecoating 40 will be applied to the core surfaces 16 b, 17 b and 20 b and thehousing surfaces sea water fins 35 defining thesea water passages 36. - Preferably before attaching the
heat exchanger body 24 to thecore 30 and thus creating themanifolds coating 40 is applied to the corrosion-erosion prone wettedsurfaces 43 a, being the core surfaces 16 b, 17 b and 20 b and thehousing surfaces core surface core 30 is assembled and brazed, thecoating 40 can be applied to thecore 30, after assembly and brazing. Thus, it is not necessary that thecoating 40 be able to withstand the brazing process. Moreover, thecoating 40 can be applied to thehousing surfaces housing 24 is attached to thecore 30. Although thecoating 40 can be applied by various methods, thecoating 40 is preferably applied by thermal spraying thecoating 40 on thesurfaces 43 a. Those skilled in the art will appreciate that there are various methods of thermal spraying. Although any one of the conventional methods of thermal spraying could be used to coat thesurfaces 43 a, preferably thecoating 40 is applied by High Velocity Oxy Fuel (HVOF). The HVOF method allows thecoating 40 to be applied with hand-held devices, including, but not limited to, spray guns, and does not require isolation in a chamber or vacuum environment. Further, thecoating 40 can be applied with a uniform thickness without the need for post treatments, such as grinding or polishing, to only the intended surfaces, being the corrosion-erosionprone surfaces 43 a. Thus, using proper thermal spray methods, thecoating 40 should not obstruct the assembledsea water passages 36. Those skilled in the art will appreciate that the corrosion-erosionprone surfaces 43 a must be prepared and cleaned in a conventional manner when using thermal spray coating methods. - Although the thickness of the
coating 40 will vary depending on the composition of thecoating 40 and the particular application of theheat exchanger 14, the thickness will generally be between 0.003-0.02 inches (75-500 micrometers) and preferably between 0.005-0.015 inches (127-381 micrometers). Thecoating 40 must be sufficiently thick to provide the needed impingement and corrosion-erosion resistance, but not too thick to adversely affect cost or heat transfer. - Once the
core 30 is assembled and the core surfaces 16 b, 17 b and 20 b and thehousing surfaces housing 24 in a conventional manner. The present disclosure contemplates various methods of attaching the core 30 to thehousing 24, including, but not limited to bolting and welding. In the illustrated embodiments, thehousing 24 is welded to thecore 30, and thus, thecoating 40 should be able to sufficiently withstand the heat from the welding process. However, it should be appreciated that the joint design style and type of the heat exchanger may be such that a welding resistant coating may not be needed. The attachedhousing 24 and the core 30 define themanifolds - The present disclosure is advantageous because it provides a relatively inexpensive, corrosion-erosion
resistant heat exchanger 14 that can be used in harsh environments, such as in sea water. Rather than making all of heat exchanger components that come into with sea water from an exotic relatively expensive corrosion-erosion resistant material, the present disclosure coats only theportion 43 a of theheat exchanger 14 that is most corrosion-erosion prone due to the sea water. Relatively inexpensive materials, such as copper, that transfer heat well can still be used in the non-corrosion-erosionprone portions 43 b, such as thesea water fins 35. Thus, the use of thecoating 40 does not adversely affect the efficiency of theheat exchanger 14. - The
coating 40 is sufficiently hard and corrosion-erosion resistant that the sea water will not interact or impinge thecoating 40. Thus, thecoating 40 can protect thesurfaces 43 a from impingement, corrosion and erosion that can lead to holes within thesurfaces 43 a, causing leakage of the sea water into theair passages 34 and premature failure. Thus, the life and durability of theheat exchanger 14 is increased by making theheat exchanger 14 corrosion-erosion resistant while not compromising the efficiency of theheat exchanger 14 or significantly increasing the cost of theheat exchanger 14. In fact, because of the increased durability, there is a significant decrease in heat exchanger down time and repair frequency, which reduces maintenance costs. - The present disclosure is further advantageous because the
preferred coating 40 is stable even in highly polluted waters. Because thecoating 40 is made out of a similar metal as thesurfaces 43 a, thecoating 40 is galvanic compatible with thesurfaces 43 a. Moreover, even if subjected to extreme temperature change, thecoating 40 will adhere to thesurfaces 43 a due to the similar coefficients of thermal expansion between thecoating 40 and thesurfaces 43 a. - Further, the
coating 40 can be applied with relative ease. Because the corrosion-erosionprone surfaces 43 a on which thecoating 40 is needed are accessible on the assembledcore 30, there is no need to apply thecoating 40 pre-assembly. Thus, there is no concern about the coating's ability to withstand the brazing of thecore 30. In addition, by thermal spraying thecoating 40 onto thesurfaces 43 a, thecoating 40 can have a uniform thickness without post-treatments, such as grinding or polishing, thereby decreasing manufacturing costs and material waste. - It should be appreciated that, although the
heat exchanger 14 is described as a heat exchanger to cool compressed air exiting theturbocharger 12, the present disclosure contemplates use with any heat exchanger used for various applications and with various coolants. Further, the present disclosure contemplates use with fluid-handling apparatuses, other than heat exchangers, that are subjected to high velocity fluid flow. - It should further be understood that the above description is intended for illustrative purposes only, and is not intended to limit the scope of the present invention in any way. Thus, those skilled in the art will appreciate that other aspects, objects, and advantages of the invention can be obtained from a study of the drawings, the disclosure and the appended claims.
Claims (20)
1. A fluid-handling apparatus comprising:
an apparatus body including a plurality of wetted surfaces characterized in that a first portion of the wetted surfaces is corrosion-erosion prone and a second portion of the wetted surfaces is non-corrosion-erosion prone;
a corrosion-erosion resistant coating coated on the first portion of the wetted surfaces, wherein the coating is harder than the apparatus body; and
wherein less than all of the wetted surfaces are coated.
2. The fluid-handling apparatus of claim 1 wherein the coating includes a metal alloy with a coefficient of thermal expansion sufficiently similar to a coefficient of thermal expansion of the first portion of the wetted surface so that the coating remains attached over a pre-determined temperature range.
3. The fluid-handling apparatus of claim 1 wherein the coating includes a metal alloy being galvanic compatible with the first portion of the wetted surfaces.
4. The fluid handling apparatus of claim 1 wherein the coating includes a copper-based alloy.
5. The fluid-handling apparatus of claim 4 wherein the coating includes copper-nickel alloys including a nickel concentration less than or equal to 40% and greater than or equal to 9%.
6. The fluid-handling apparatus of claim 5 wherein the coating includes a nickel concentration of 9-11%.
7. The fluid-handling apparatus of claim 4 wherein the coating includes an aluminum bronze alloy including an aluminum concentration equal to or less than 14%, a manganese concentration equal to or less than 2%, a nickel composition equal to or less than 6%, and an iron concentration equal to or less than 5%.
8. The fluid handling apparatus of claim 1 wherein the first portion of the wetted surfaces includes at least one liquid inlet surface.
9. The fluid-handling apparatus of claim 1 wherein the apparatus includes a heat exchanger.
10. The fluid-handling apparatus of claim 9 wherein the heat exchanger includes an air-sea water heat exchanger.
11. The fluid-handling apparatus of claim 10 wherein the apparatus body defines a plurality of sea water passages separated from one another by at least one sea water fin and a plurality of air passages separated from one another by at least one air fin oriented substantially perpendicular to the sea water fin, and the sea water passages being separated from the air passages by a plurality of separator plates; and
the sea water passages and air passages being fluidly connected to a sea water inlet manifold and a air inlet manifold, respectively.
12. The fluid-handling apparatus of claim 11 wherein the first portion of the wetted surfaces includes at least one sea water inlet surface within at least the sea water inlet manifold, and the second portion of the wetted surfaces includes a inner surface of the sea water passages; and
the coating includes a metal alloy being galvanic compatible with the first portion of the wetted surfaces and including a coefficient of thermal expansion sufficiently similar to a coefficient of thermal expansion of the first portion of the wetted surface so that the coating remains attached over a pre-determined temperature range, and the coating including either a copper-nickel alloy with 9-40% nickel and an aluminum bronze alloy.
13. An engine system using sea water as a coolant comprising:
an engine; and
a heat exchanger being in fluid communication with the engine, and defining a sea water inlet fluidly connected with a plurality of wetted surfaces, and a first portion of the wetted surfaces being corrosion-erosion prone and a second portion of the wetted surfaces being non-corrosion-erosion prone; a corrosion-erosion resistant coating being coated on the first portion of the wetted surfaces, and wherein the coating is harder than the first portion; and less than all the wetted surfaces are coated.
14. The engine system of claim 13 wherein the first portion includes at least one sea water inlet surface of the heat-exchanger.
15. The engine system of claim 14 wherein the coating includes a metal alloy being galvanic compatible with the first portion of the wetted surfaces and including a coefficient of thermal expansion sufficiently similar to a coefficient of thermal expansion of the first portion of the wetted surface so that the coating remains attached over a pre-determined temperature range.
16. The engine system of claim 15 wherein the coating includes a copper-based alloy.
17. The engine system of claim 16 wherein the coating includes a copper-nickel alloy including 9-40% nickel.
18. A method of making a heat exchanger, comprising the steps of:
assembling a plurality of components to include a plurality of wetted surfaces;
distinguishing between corrosion-erosion prone wetted surfaces and non-corrosion-erosion prone wetted surfaces; and
coating the corrosion-erosion prone wetted surfaces with a corrosion-erosion resistant coating being harder than the corrosion-erosion prone wetted surfaces.
19. The method of claim 18 wherein the step of coating includes the step of thermal spraying the coating onto the corrosion-erosion prone portion of the wetted surfaces.
20. The method of 18 wherein the step of coating being performed after the step of assembling.