US20050065303A1 - Coating compositions for plastic substrates - Google Patents

Coating compositions for plastic substrates Download PDF

Info

Publication number
US20050065303A1
US20050065303A1 US10/979,148 US97914804A US2005065303A1 US 20050065303 A1 US20050065303 A1 US 20050065303A1 US 97914804 A US97914804 A US 97914804A US 2005065303 A1 US2005065303 A1 US 2005065303A1
Authority
US
United States
Prior art keywords
composition
composition according
meth
compound
acrylate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/979,148
Inventor
Chander Chawla
Christopher Tronche
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JSR Corp
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to US10/979,148 priority Critical patent/US20050065303A1/en
Publication of US20050065303A1 publication Critical patent/US20050065303A1/en
Assigned to JSR CORPORATION reassignment JSR CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: DSM IP ASSETS B.V.
Abandoned legal-status Critical Current

Abstract

The present invention provides radiation-curable compositions for coating plastic substrates, wherein the compositions, after cure, have a combination of sufficient adhesion, flexibility, and hardness. The compositions include: (a) at least one component comprised of a metal oxide bonded to an organic compound, said organic compound having (i) a radiation curable group; and
(ii) a group represented by the following formula (1)
Figure US20050065303A1-20050324-C00001
wherein X represents an amine (NH), oxygen (O), or sulfur (S) radical; and Y represents an oxygen (O), or sulfur (S) radical; (b) a poly(meth)acrylate compound; and (c) an adhesion promoter.

Description

    CROSS-REFERENCE TO RELATED APPLICATIONS
  • This application is a continuation of U.S. patent application Ser. No. 09/951,777, filed Sep. 14, 2001, and further claims the benefit of priority to U.S. provisional application Ser. No. 60/232,427, filed Sep. 14, 2000, both of which are hereby incorporated in their entirety by reference.
  • FIELD OF THE INVENTION
  • The present invention relates to radiation curable compositions, to coatings formed by curing these compositions, and to articles comprising such coatings. An aspect of the invention concerns the use of the present compositions to form protective coatings on substrates including for example display monitors (like flat screen computer and/or television monitors such as those utilizing technology discussed in, for example, U.S. Pat. Nos. 6,091,184 and 6,087,730 which are both hereby incorporated by reference), optical discs, smart cards and the like.
  • BACKGROUND OF THE INVENTION
  • There is great interest in the development of plastic substrates for, for instance, LCD (liquid crystal display) and OLED (organic light emitting diode) display applications. Plastic substrates are light and tough, and comparatively easy to shape. However, plastics are typically relatively soft and, thus, there is the need to deposit a protective layer on the exposed surface of the plastic. Such protective layers are preferably relatively hard (to provide, e.g., scratch resistance) yet also substantially flexible. In addition, such layers should adhere well to the surface they are coated on.
  • SUMMARY OF THE INVENTION
  • The present invention provides compositions that, after cure, adhere well to plastic substrates and provide a flexible material having a hard, scratch resistant surface. The compositions comprise (i) a metal oxide bound to an organic compound having a radiation-curable group, (ii) a poly(meth)acrylate compound, and (iii) an adhesion promoter.
  • DESCRIPTION OF THE INVENTION
  • It is to be understood that the term polynorbornene herein refers to a polymer wherein at least 10 wt %, relative to the total weight of the polymer, results from the polymerization of norbornene monomers, more preferably at least 50 wt %, even more preferably at least 80 wt %, and most preferably at least 95 wt % results from the polymerization of norbornene monomers. Polynorborene may be a random copolymer, a block copolymer, a homopolymer or a polymer resulting from three or more monomers. Examples of polynorbornenes are, for instance, described in U.S. Pat. Nos. 5,468,819; 5,569,730; 5,571,881; 5,677,405; 5,741,869; and RE 34,638; which six patents are hereby incorporated in their entirety by reference. “(Meth)acrylate” refers in this application to “acrylate and/or methacrylate”.
  • The present invention concerns compositions for coating a plastic substrate, wherein the compositions comprise a component (A) comprised of a metal oxide bonded to an organic compound, wherein the organic compound has
      • (i) a radiation curable group; and
      • (ii) a group represented by the following formula (1)
        Figure US20050065303A1-20050324-C00002
      • wherein
      • X represents an amine (NH), oxygen (O), or sulfur (S) radical; and
      • Y represents an oxygen (O) or sulfur (S) radical;
      • wherein a coating formed by curing a 25 micron thick layer of said composition on a 0.1 mm thick polynorbornene substrate has
        • (a) sufficient adhesion to said plastic substrate;
        • (b) a pencil hardness of 1B or higher; and
        • (c) sufficient flexibility.
  • Suitable examples of the component comprised of a metal oxide bonded to an organic compound are, for instance, set forth in U.S. Pat. No. 6,160,067 to Eriyama et al, which is hereby incorporated in its entirety by reference. Preferably, the metal oxide comprises at least one metal selected from the group consisting of silicon, aluminum, zirconium, titanium, zinc, germanium, indium, tin, antimony, and cerium. The organic group preferably comprises a radiation-curable group that is ethylenically unsaturated, for instance a (meth)acrylate group, preferably an acrylate group.
  • The present compositions preferably comprise at least 20 wt/o, relative to the total weight of the composition, of the component comprised of a metal oxide bonded to an organic compound, more preferably at least 35 wt %, and most preferably at least 50 wt %. The present compositions preferably comprise less than 95 wt %, more preferably less than 85 wt %, of the component comprised of a metal oxide bonded to an organic compound.
  • Preferably, the present compositions comprise at least one poly(meth)acrylate monomer, i.e. a monomer comprising at least two acrylate or methacrylate groups, and more preferably at least two poly(meth)acrylate monomers. The poly(meth)acrylates may be alkoxylated, for instance ethoxylated or propoxylated. Preferably the composition comprises a tri(meth)acrylate, more preferably an alkoxylated tri(meth)acrylate, most preferably an ethoxylated tri(meth)acrylate. An example of a preferred ethoxylated tri(meth)acrylate is, for instance, ethoxylated trimethylolpropane triacrylate. Commercial examples of ethoxylated trimethylol propane triacrylate include SR 502 from Sartomer, which is an ethoxylated (9) trimethylol propane triacrylate. Examples of non-alkoxylated tri(meth)acrylates that can be used in the present invention include, for instance, tris(2-hydroxy ethyl)isocyanurate triacrylate, which is commercially available from, for instance, Sartomer as SR-368.
  • Examples of other preferred poly(meth)acrylate monomers include penta(meth)acrylates. Preferred penta(meth)acrylates include, for instance, dipentaerythritol monohydroxypenta acrylate. Commercial examples of such a pentacrylate include SR-399 from Sartomer. Preferably the compositions of the present invention comprise both a tri(meth)acrylate and a penta(meth)acrylate.
  • The present compositions may also comprise mono(meth)acrylate monomers as well as other radiation curable monomers such as N-vinyl functional monomers.
  • Preferably, the present compositions comprise monomers which not only comprise one or more (meth)acrylate groups, but also other functional groups such as one or more hydroxy groups and/or one or more carboxylic acid groups.
  • Preferably, the present compositions comprise, relative to the total weight of the composition, 5-50 wt % of (meth)acrylate-functional monomers (preferably poly[meth]acrylate monomers), more preferably 10-35 wt %, most preferably 15-25 wt %.
  • Preferably, the present compositions comprise 1-25 wt %, relative to the total weight of the composition, of monomers comprising 3 (meth)acrylate groups, more preferably 5-25 wt %. Preferably, the present compositions comprise, relative to the total weight of the composition, 5-25 wt % of monomers comprising 5 (meth)acrylate groups, more preferably 10-20 wt %.
  • If the composition comprises both a penta(meth)acrylate compound and a tri(meth)acrylate compound, the weight ratio of penta(meth)acrylate compounds in the composition to tri(meth)acrylate compounds in the composition is preferably below 5, more preferably below 3, and most preferably below 2.
  • The present compositions preferably comprise an adhesion promoter. Preferred adhesion promoters include silane adhesion promoters, for instance polyalkoxysilanes such as gamma-mercaptopropyltrimethoxysilane and methacryloxypropyl trimethoxy silane. Methacryloxypropyl trimethoxy silane is most preferred, for instance because it tends to have better shelf life than gamma-mercaptopropyl trimethoxy silane. Preferably the present compositions comprise, relative to the total weight of the composition, at least 1 wt % of adhesion promoter, more preferably at least 3 wt %, and most preferably at least 5 wt %. Generally, the present compositions will comprise less than 25 wt % of adhesion promoter.
  • Although generally not preferred, the present compositions may comprise any suitable epoxy-functional compound. Examples of suitable epoxy-functional compounds include bisphenol A diglycidyl ethers, epoxy novolaks, and cycloaliphatic epoxides. Preferred cycloaliphatic epoxides include those comprising one or more, preferably two, cyclohexene oxide structures, such as 3,4-epoxycyclohexyl-methyl-3,4-epoxycyclohexane carboxylate. Preferably, the present compositions comprise less than 30 wt % of epoxy-functional compounds, more preferably less than 15 wt %, and most preferably the present compositions are absent epoxy-functional compounds.
  • The present compositions may further comprise several additives, such as one or more photoinitiators (preferably at least two photoinitiators).
  • The coating thickness of the composition on the substrate, after cure of the composition, is preferably in the range of 1-100 microns, more preferably 5-50 microns.
  • Preferably, the pencil hardness of the compositions, after cure, is at least B, more preferably at least HB, and most preferably at least H.
  • Furthermore, a 5-10 micron thick cured layer of the present compositions preferably has a transparency of at least 65% for light having a wavelength of 400 run, more preferably at least 75%, and most preferably at least 90%.
  • The present compositions have, after cure, sufficient adhesion to plastic substrates. Preferably the compositions have an adhesion value of at least 1, more preferably at least 3, as measured according to ASTM D3359.
  • The present compositions are, after cure, sufficiently flexible. Preferably, the compositions exhibit a flexibility such that less than 10 cracks, more preferably less than 5 cracks, and most preferably no cracks, are visible in a 5-10 micron thick cured layer of the composition, wherein the composition is coated on a plastic substrate (length 20 cm, width 5 cm, and thickness 100 microns) and wound around a rod of 3.10 mm diameter with the plastic facing the surface of the rod and, consequently, the coating (cured composition) facing away from the rod.
  • The present compositions may be used as coating compositions. For instance, the present compositions may be used to coat substrates. Suitable substrates to be coated include organic substrates. Organic substrates are preferably polymeric (“plastic”) substrates, such as substrates comprising polynorbornene, polyethyleneterephtalate, polymethylmethacrylate, polycarbonate, polyethersulphone, polyimide, and/or polyethernaphtalene. Particularly preferred substrates include polynorbornene substrates and polyimide substrates.
  • The substrates may be pre-treated prior to coating with the present compositions. For instance, the substrates may be subjected to corona or high energy treatment. The substrates may also be chemically treated, such as by emulsion application.
  • Preferably, the substrate comprises functional groups such as hydroxy groups, carboxylic acid groups and/or trialkoxysilane groups such as trimethoxysilane. The presence of such functional groups may improve adhesion of the coating to the substrate.
  • There is no specific limitations to the method for preparing the crosslinkable particles (A) used in the present invention. Methods for preparing the particles are disclosed in, for instance WO 00/47666, which is hereby incorporated in its entirety by reference. A method of reacting the above-mentioned specific organic compound and oxide particles can be given as an example:
  • Oxide particles (A1) are known to have moisture on the surface of particles as adsorption water under usual storage conditions. In addition, components which react with a silanol group-forming compound such as a hydroxide, hydrate, or the like are presumed to be present at least on the surface of the oxide particles. Therefore, the crosslinkable particles (A) can be produced by mixing the silanol group-forming compound and oxide particles (A1), and heating the mixture while stirring. It is preferable that the reaction be carried out in the presence of water to efficiently bind the silanol group-forming site possessed by the specific organic compound (A2) and the oxide particle (A1). However, water is not required when the specific organic compound (A2) and (optionally) compound (A3) possess silanol groups. Therefore, the crosslinkable particles (A) can be prepared for example by a method which includes at least the operation to blend the oxide particles (A1), the specific organic compound (A2) and (optionally) compound (A3).
  • The crosslinkable particles may be prepared, for example, by a two step process. The first step involving hydrolyzing the compound (A2) and bonding the hydrolyzed compound to oxide particles (A1). And a second step of hydrolyzing the compound (A3) and bonding the particles obtained in the first step to the hydrolyzed compound obtained from compound (A3). Hydrolysis may be omitted, when the compound (A2) and compound (A3) are not silanol group-forming compounds, but silanol group-containing compounds.
  • First Step
  • The first step comprises reacting a mixture of oxide particles (A1) and a solvent or oxide particles (A1) dispersed in a solvent with the compound (A2) to bond oxide particles (A1) and the compound (A2) (such bonded particles may be hereinafter referred to as “intermediate particles”). Specifically, the oxide particles (A1), the compound (A2), and water are blended under the following conditions to produce the intermediate particles.
  • Here, p-methoxyphenol for example, may be added as a thermal polymerization inhibitor. The same solvent as used as a dispersion medium for the solvent dispersion sol of the oxide particles (A1) can be used as a solvent.
  • The temperature for the reaction may be between the temperature at which the solutes do not precipitates and the boiling point of the solvent, with the preferable temperature range being from 0 to 150° C.
  • There are no specific restrictions to the manner of stirring inasmuch as the mixture can be homogeneously mixed.
  • The reaction is carried out usually in an atmosphere of a dry gas such as nitrogen or air, with dry air being preferred. A reaction time within which the reaction is sufficiently completed, for example, from 5 minutes to 24 hours, and preferably from one hour to 8 hours, can be applied.
  • Second Step
  • The second step comprises reacting the intermediate particles produced in the first step and the compound (A3), thereby obtaining crosslinkable particles in which the intermediate particles are bonded with the compound (A3). Specifically, the intermediate particles, the compound (A3), and water are mixed under the following conditions to produce crosslinkable particles.
  • The temperature for the reaction may be between the temperature at which the solutes do not precipitates and the boiling point of the solvent, with the preferable temperature range being from 0 to 150° C.
  • There are no specific restrictions to the manner of stirring inasmuch as the mixture can be homogeneously mixed.
  • The reaction is carried out usually in an atmosphere of a dry gas such as nitrogen or air, with dry air being preferred. A reaction time within which the reaction is sufficiently completed, for example, from 5 minutes to 24 hours, and preferably from one hour to 8 hours, can be applied.
  • The crosslinkable particles can be obtained by bonding the oxide particles (A1), compound (A2), and compound (A3) through first and second steps in this manner.
  • As mentioned above, it is desirable to produce the crosslinkable particles by first treating with the compound (A2), followed by a treatment with the compound (A3).
  • Taking the case using silica particles as the oxide particles (A1) as an example, both impaired storage stability and inferior coating surfaces are associated with dispersion stability of the crosslinkable particles in the composition. Because the compound (A2) is relatively bulky, the treatment only with the compound (A2) cannot completely restrain the silanol group on the surface of particles from condensing after the treatment. However, successive treatment with the compound (A3) with a relatively small molecular size is presumed to effect a smooth bonding on the surface of the particles, whereby the remaining silanol groups can be reduced more efficiently, resulting in improved dispersion stability of particles.
  • If the treatment with the compound (A3) is carried out simultaneously with or prior to the treatment with the compound (A2), dispersion stability of particles may be impaired, which results in impaired storage stability of the coating material and an inferior coating film appearance.
  • The amount of each of the compound (A2) and the compound (A3) bonded to the oxide particles (A1) is 0.01 wt % or more, preferably 0.1 wt % or more, and particularly preferably 1 wt % or more, in the crosslinkable particles. If the amount of either the compound (A2) or the compound (A3) bonded with the oxide particles (A1) is less than 0.01 wt %, dispersibility of the crosslinkable particles in the composition may be insufficient, which may result in cured products with insufficient transparency and scratch resistance. The amount of the oxide particles (A1) used in the raw materials for preparing the crosslinkable particles is preferably from 5-99 wt %, and more preferably from 10-98 wt %.
  • The method for preparing the crosslinkable particles will now be described in more detail for the case where the alkoxysilane compound shown by the following formula (2) is used as a silanol group-forming compound.
    Figure US20050065303A1-20050324-C00003

    wherein
    • R1 and R2 individually represent a hydrogen atom or an alkyl group or aryl group having 1-8 carbon atoms;
    • m represents 1, 2, or 3;
    • R3 represents a divalent organic group having a C1-C12 aliphatic or aromatic structure which may include a linear, branched, or cyclic structure;
    • R4 represents a divalent organic group;
    • R5 represents an organic group of an (n+1) valence;
    • Z is a monovalent organic group having a polymerizable unsaturated group in the molecule which causes an inter-molecular cross-linking reaction in the presence of active radicals; and
    • n represents an integer from 1 to 20.
  • The amount of water consumed in the hydrolysis of the alkoxysilane compound in the preparation of the crosslinkable particles may be the amount sufficient to hydrolyze at least one alkoxy group on the silicon atom in one molecule. Preferably, the amount of water which is added or present during the hydrolysis reaction is one third (⅓) or more of the number of mols of the total alkoxy groups on the silicon atoms of the alkoxysilane compound, with particularly preferable amount being from ½ to 3 times of the number of mols of the total alkoxy groups. The product obtained by mixing the alkoxysilane compound and the oxide particles (A1) under the conditions where no moisture is present is a product wherein the alkoxysilane compound has physically absorbed on the surface of oxide particles (A1). The cured products made from the composition which includes such crosslinkable particles can exhibit only insufficient hardness and scratch resistance.
  • The methods which can be selected for the preparation of crosslinkable particles (A) include a method of separately hydrolyzing the above-mentioned alkoxysilane compound, and mixing the hydrolyzed product with a powder of oxide particles or a solvent dispersion sol of oxide particles with heating and stirring; a method of carrying out the hydrolysis of the alkoxysilane compound in the presence of the oxide particles; and a method of treating the surface of the oxide particles in the presence of, for example, (D) the polymerization initiator and the like. Among these, the method of hydrolyzing the alkoxysilane compound in the presence of oxide particles is preferable. The treatment for the preparation of the crosslinkable particles (A) is carried out at a temperature from 0 to 150° C., preferably from 20 to 100° C. The treating time is usually from 5 minutes to 24 hours.
  • When oxide particles in the form of a powder are used in the preparation of the crosslinkable particles (A), an organic solvent may be added to ensure a smooth and homogeneous reaction with the alkoxysilane compound. The same solvents as used as the above-mentioned dispersion medium for the solvent dispersion sol of oxide particles can be used as such an organic solvent. There are no specific limitations to the types of these solvents, in as much as a smooth and homogeneous reaction is ensured.
  • When a solvent dispersion sol is used as the raw material for the crosslinkable particles (A), the crosslinkable particles (A) can be prepared by a process comprising at least a step of mixing the solvent dispersion sol and the specific organic compound. Here, an organic solvent which is mutually soluble with water can be added to ensure homogeneity in the initial stage of the reaction and smooth reaction.
  • Moreover, an acid, salt, or base may be added as a catalyst to accelerate the reaction to produce the crosslinkable particles (A). Given as examples of the acid are inorganic acids such as hydrochloric acid, nitric acid, sulfuric acid, and phosphoric acid, organic acids such as methanesulfonic acid, toluenesulfonic acid, phthalic acid, malonic acid, formic acid, acetic acid, and oxalic acid, as well as unsaturated organic acids such as methacrylic acid, acrylic acid, and itaconic acid. As examples of the salt, ammonium salts such as tetramethylammonium chloride and tetrabutylammonium chloride can be given. Given as examples of the base, aqueous ammonia; primary, secondary, or tertiary aliphatic amines such as diethylamine, triethylamine, dibutylamine, and cyclohexylamine; aromatic amines such as pyridine; sodium hydroxide, potassium hydroxide; as well as tertiary ammonium hydroxides such as tetramethylammonium hydroxide, tetrabutylammonium hydroxide, and the like. Among these, preferable catalysts are acids such as organic acids and unsaturated organic acids, and bases such as tertiary amines and quaternary ammonium hydroxide. The amount of these acids, salts, or bases to be added is preferably from 0.001 to 1.0 part by weight, and more preferably from 0.01 to 0.1 part by weight, for 100 parts by weight of the alkoxysilane compounds.
  • Preferably, a dehydrating agent is added to promote the reaction. As a dehydrating agent, inorganic compounds such as zeolite, anhydrous silica, and anhydrous alumina, and organic compounds such as methyl orthoformate, ethyl orthoformate, tetraethoxymethane, and tetrabutoxymethane can be used. Of these, the organic compounds are preferred, with ortho esters such as methyl orthoformate, ethyl orthoformate being particular preferred. The amount of alkoxysilane compound bonded with the crosslinkable particles (A) can be determined as a weight loss (%) when a dry powder is burnt completely in air in a thermogravimetric analysis from 110 to 800° C.
  • The following examples are given as particular embodiments of the invention and to demonstrate the practice and advantages thereof. It is to be understood that the examples are given by way of illustration and are not intended to limit the specification or the claims that follow in any manner.
  • EXAMPLES
  • Several compositions were prepared by admixing components as set forth in Table 1 below. The amounts in Table 1 are in weight percentages relative to the total weight of the compositions.
  • The compositions in Table 1 were coated on a polynorbornene substrate sample (Arton®, JSR-Tokyo-Japan) as a 25 micron thick layer and, after evaporation of solvent during 3 minutes at room temperature, cured under air at 1.0 J/cm2 using a Fusion unit equipped with a D lamp. The dimensions of the polynorbornene substrate, before applying the composition, was: length 20 cm, width 5 cm, and thickness 100 microns.
  • Adhesion was tested according to testing method ASTM D3359, which is herewith incorporated by reference, which uses a rating scale from 0-5, with 5 being the highest adhesion and 0 the lowest.
  • Flexibility of the coatings was measured by winding the coated polynorbornene substrates around rods of different diameter, with the polynorbornene substrate facing the surface of the rod and, consequently, the coating facing away from the rod, and by subsequently determining the degree of cracking. The results are given in Table 2. The severity of cracks, as determined with the naked eye, is indicated with numerals 0-5, with 0 meaning no cracks were observed and 5 meaning very severe cracking was observed. For instance, the indication 3 means that approximately 10 cracks were observed in the outer coating layer of the fully wound substrate. The indication “--” means that the coating was no longer coherent.
    TABLE 1
    Comparative Examples 1-3 and Examples 1
    Comparative Comparative Comparative
    Ingredients Example 1 Example 2 Example 3 Example 1
    Acrylated MEK-ST (acrylated silica particles 75.00 75.00
    in methyl ethyl ketone [30 wt % particles
    relative to the combined weight of particles
    and methyl ethyl ketone])
    Acrylated MT-ST (acrylated silica particles 75.00 72.00
    in methanol [30 wt % particles relative to the
    combined weight of particles and methanol])
    Dipentaerythritol monohydroxy penta 14.30 13.60
    acrylate (SR-399)
    Tris (2-hydroxyethyl) isocyanurate triacrylate 9.50 22.00
    (SR-368)
    Ethoxylated (9) trimethylolpropane 22.00 9.00
    triacrylate (SR-502)
    Irgacure 184 photoinitiator (Ciba Geigy) 1.50 1.50 1.50 1.50
    Irgacure 907 photoinitiator (Ciba Geigy) 0.90 1.50 1.50 0.90
    A-189 silane adhesion promoter (gamma- 3.00
    mercaptopropyltrimethoxysilane, Union
    Carbide)
    Properties after cure:
    Adhesion to polynorbornene (ASTM D3359) 0 0 1 1
    Pencil hardness of coated polynorbornene HB HB 3B HB
    substrate
  • TABLE 2
    Flexibility of coatings according to Comparative Example 1-3
    and Examples 1
    Rod Diameter (mm)
    Polynorbornene Substrate 6.25 5.00 3.75 3.10 2.50 1.25
    Comparative Example 1 5
    Comparative Example 2 0 0 0 0 0 2
    Comparative Example 3 0 0 0 0 0 0
    Example 1 0 0 0 0 3
  • TABLE 3
    Table 3 shows another formulation according
    to the present invention.
    Ingredients Example 2
    Acrylated MT-ST (acrylated silica particles in methanol 70.00
    [30 wt % particles relative to the combined weight of
    particles and methanol])
    Dipentaerythritol monohydroxy penta acrylate (SR-399) 13.60
    Ethoxylated (9) trimethylolpropane triacrylate (SR-502) 9.00
    Irgacure 184 photoinitiator (Ciba Geigy) 1.50
    Irgacure 907 photoinitiator (Ciba Geigy) 0.90
    Methacryloxypropyl trimethoxy silane 5.00
  • Having described specific embodiments of the present invention, it will be understood that many modifications thereof will readily be apparent to those skilled in the art, and it is intended therefore that this invention is limited only by the spirit and scope of the following claims.

Claims (30)

1. A curable composition for coating a plastic substrate, said composition comprising:
(a) at least one component comprised of a metal oxide bonded to an organic compound, said organic compound having
(i) a radiation curable group; and
(ii) a group represented by the following formula (1)
Figure US20050065303A1-20050324-C00004
wherein
X represents an amine (NH), oxygen (O), or sulfur (S) radical; and
Y represents an oxygen (O), or sulfur (S) radical;
(b) a poly(meth)acrylate compound; and
(c) an adhesion promoter;
wherein said composition, after cure, has
(a) sufficient adhesion to said plastic substrate;
(b) a pencil hardness of B or higher; and
(c) sufficient flexibility.
2. The composition of claim 1, wherein said plastic substrate comprises at least one plastic selected from the group consisting of polynorbornene, polyethyleneterephtalate, polymethylmethacrylate, polycarbonate, polyethersulphone, polyimide, and polyethernaphtalene.
3. The composition according to claim 1, wherein said plastic substrate comprises polynorbornene.
4. The composition according to claim 1, wherein said metal oxide comprises at least one metal selected from the group consisting of silicon, aluminum, zirconium, titanium, zinc, germanium, indium, tin, antimony, and cerium.
5. The composition according to claim 1, wherein said metal oxide is a silicon oxide.
6. The composition according to claim 1, wherein said composition comprises, relative to the total weight of the composition, 20-95 wt % of said at least one component.
7. The composition according to claim 1, wherein said composition comprises, relative to the total weight of the composition, at least 50 wt % of said at least one component.
8. The composition according to claim 1, wherein said poly(meth)acrylate compound comprises at least three (meth)acrylate groups.
9. The composition according to claim 1, wherein said composition comprises 5-25 wt %, relative to the total weight of the composition, of a poly(meth)acrylate comprising three (meth)acrylate groups.
10. The composition according to claim 1, wherein said composition comprises at least two compounds having at least three (meth)acrylate groups.
11. The composition according to claim 1, wherein said composition comprises an ethoxylated triacrylate.
12. The composition according to claim 1, wherein said composition comprises a pentacrylate.
13. The composition of claim 12, wherein said composition comprises 5-25 wt %, relative to the total weight of the composition, of said pentacrylate.
14. The composition according to claim 1, wherein said adhesion promoter is selected from the group consisting of gamma-mercaptopropyl trimethoxysilane and methacryloxypropyl trimethoxy silane.
15. The composition according to claim 1, wherein said composition comprises at least 3 wt %, relative to the total weight of the composition, of said adhesion promoter.
16. The composition according to claim 1, wherein said composition comprises at least 5 wt %, relative to the total weight of the composition, of said adhesion promoter.
17. The composition according to claim 1, wherein said poly(meth)acrylate compound comprises hydroxy groups and/or carboxylic groups.
18. The composition according to claim 1, wherein said composition is absent epoxy-functional compounds.
19. The composition according to claim 1, wherein the pencil hardness of the composition, after cure, is at least HB.
20. The composition according to claim 1, wherein a 5-10 micron thick cured layer of said composition has a transparency of at least 65% for light having a wavelength of 400 mm.
21. The composition according to claim 1, wherein the composition exhibits a flexibility such that less than 10 cracks are visible in a 5-10 micron thick cured layer of the composition when the composition is coated on said plastic substrate (length 20 cm, width 5 cm, and thickness 100 microns) and wound around a rod of 3.10 mm diameter with the plastic facing the surface of the rod and, consequently, the cured layer facing away from the rod.
22. The composition according to claim 1, wherein the composition, after cure, has an adhesion value of at least 1 as measured according to ASTM D3359.
23. An article comprising
(a) a substrate comprising at least one plastic selected from the group consisting of polynorbornene, polyethyleneterephtalate, polymethylmethacrylate, polycarbonate, polyethersulphone, polyimide, and polyethernaphtalene; and
(b) a coating on said substrate, said coating being obtained by curing the composition according to claim 1.
24. The article of claim 23, wherein said substrate is corona treated.
25. The article according to claim 23, wherein said article includes an optical display.
26. The article according to claim 23, wherein said article includes a liquid crystal display or an organic light emitting diode display.
27. The article according to claim 23, wherein said article includes an optical disc.
28. A process for preparing a substantially flexible coating, said process comprising curing a composition according to claim 1.
29. A display monitor comprising a plastic substrate coated at least in part with a coating formed by curing the composition according to claim 1.
30. The display monitor of claim 29 wherein an image is viewed through said coating.
US10/979,148 2000-09-14 2004-11-03 Coating compositions for plastic substrates Abandoned US20050065303A1 (en)