US20030116307A1 - Insulating preform - Google Patents

Insulating preform Download PDF

Info

Publication number
US20030116307A1
US20030116307A1 US10/258,996 US25899602A US2003116307A1 US 20030116307 A1 US20030116307 A1 US 20030116307A1 US 25899602 A US25899602 A US 25899602A US 2003116307 A1 US2003116307 A1 US 2003116307A1
Authority
US
United States
Prior art keywords
glass
preform
wool
support
net
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/258,996
Inventor
Filippo Amadio
Original Assignee
Filippo Amadio
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to ITBO20000265 priority Critical patent/IT1321250B1/en
Priority to PCT/IB2001/000766 priority patent/WO2001094353A1/en
Application filed by Filippo Amadio filed Critical Filippo Amadio
Publication of US20030116307A1 publication Critical patent/US20030116307A1/en
Application status is Abandoned legal-status Critical

Abstract

An insulating preform made of a mass of glass fiber resembling wool obtained by extreme bulking of glass fiber and by a support for the glass wool, the support including a net being of the same material of the glass wool and defined by a non bulked glass strand. The glass wool and the net are held together so as to make geometrical shapes without any glue and/or impregnating substance.

Description

    BACKGROUND OF THE INVENTION
  • The present invention relates to thermal and acoustic insulation obtained by means of continuous glass fiber. [0001]
  • DESRCIPTION OF THE PRIOR ART
  • It is known that continuous glass fiber can be used without any decay in a temperature range of 950° C. to 1150° C.; a “softening” phase begins only at about 1300° C. and continues until [0002] 1520° C.: after having reached this temperature, the glass begins to melt.
  • Thus, this material can be used in fields in which medium-low working temperatures are reached as e.g. electrical appliances (stoves, refrigerators or generally motor powered devices), boilers, mufflers for internal combustion engines, etc. [0003]
  • According to a known system for thermal insulation of a hot body (so as to prevent it from dispersing heat) or for keeping a body cold, or for sound insulation between adjacent walls, the body to be insulated is wrapped with a surrounding preform with thermal and sound insulating properties. [0004]
  • The preform is obtained by two processes: [0005]
  • according to a first process, countless filaments forming the glass fiber are oriented; then they are soaked with phenol starch, so as to maintain the desired volume (i.e. maintain the capability for keeping air, which is the actual thermal insulator) and density, and finally they are glued onto a paper or aluminium support (according to the intended use), so as to allow them to be handled and applied; [0006]
  • according to a second process, basaltic rock is melted to obtain many filaments. The so obtained filaments are excessively fragile and do not keep their own volume, so they are impregnated with phenolic resins to obtain either preformed blocks, which matches the cavities and fill them thus giving them insulating properties, or mats of various thickness and density, which are placed in a desired position. [0007]
  • The methods used so far do not allow to obtain filaments of exact and selected diameter neither from the glass wool nor from rock wool, actually filaments of 10, 6 and also 2 μm are obtained. [0008]
  • These filaments are not continuous, but they can break forming separated filaments resembling needles. [0009]
  • It is to be pointed out that EEC regulations have put these articles into the class II, because they can leave particles smaller than 2 μm, which are breathable, irritating and consequently cancerogenous. [0010]
  • Another disadvantage of the above methods results from the necessity to use phenolic resins for making the articles suitable for handling; the resins not only emit exhalations, which are sometimes toxic, but also increase the production costs, since they require annealing of the treated article. [0011]
  • From the publication WO-A-98/24615 a molded insulation product is known produced by means of a process for forming a thermal insulation layer which include advancing a multi-filament strand of continuous filaments through a nozzle, to separate the filaments from each other to form a continuous filament wool, applying a binder to the filaments, placing a charge comprising the wool in a mold and molding the charge to form the insulation layer. In a preferred embodiment, the charge comprises a container formed from a polymer film. [0012]
  • From another publication, EP-A-531767 it is known a device for adsorption of acoustic and/or hydrodynamic waves, in which a conical, wedge-shaped or pyramidal external circumferential surface, which is constructed as a network, knitted or knotted from a weatherproof material such as rubber or glass fibre, is filled with a fibrous material. The external surface takes the form of a wedge or a pyramid to provide an acoustic dampening effect. [0013]
  • SUMMARY OF THE INVENTION
  • The object of the present invention is to propose a heat and sound insulating preform, which can have different conformation in relation to its use. [0014]
  • Another object of the present invention is to propose a preform, which is not harmful to people. [0015]
  • A further object of the present invention is to propose a preform obtained by using only one component, i.e. glass. [0016]
  • The above objects are obtained, in accordance with the contents of the claims, by an insulating preform formed by a mass of glass fiber resembling wool, or glass wool, obtained by extreme bulking of glass fiber, that means increasing the volume of the glass fiber as much as possible, and a support for the glass wool, including a net, also of glass wool, and defined by a non-bulked thread of glass, said glass wool and the net being kept together, so as to compose geometrical figures without using glues and/or impregnating substances. [0017]
  • The characteristic particular to the invention are set forth in the following description of two preferred embodiments of the proposed shell[0018]
  • DESCRIPTION OF PREFERRED EMBODIMENTS
  • The used glass fiber is formed by various filaments having diameter in the range of 6 to 25 μm (in relation to the product used), put together to form one strand having weight in the range of 136 to 4800 Tex (grams×Km=Tex). [0019]
  • During the productive process, the glass fiber is covered with a silane starch to allow its workability as well as for shipment and storage needs. [0020]
  • A tool, obtained by the Applicant using the air-cushion generated by a suitable ejecting nozzle, manages to “inflate” the strand of glass fiber, thus forming a mass of glass fiber resembling wool with highly insulating properties. [0021]
  • It is to be pointed out that the so obtained glass wool is formed by innumerous continuous threads, having their own elasticity. These continuous threads do not release particles in the air and do not have any “needle” effect while being touched. [0022]
  • More precisely, more than 5000 continuous threads of diameter equal to 25 μm forming the strand, are separated. The separation is not regular, i.e. it does not form paired parallel threads but the threads are disposed in a curvilinear or straight way, so that they intersect each other producing maximum volume. Each thread keeps it own elasticity (though reduced because it is proportional to the cross-sectional area) thus giving the flock a particular softness because of the repeated elastic reaction movement following a compression exerted by any mechanical action thereon (either caused by a human hand or by the metallic structure of a machine). [0023]
  • Consequently, an extreme bulking of the continuos fiber glass, is obtained, that means that the volume of the glass fiber is increased as much as possible. [0024]
  • Excellent from the acoustic point of view, a vibrating wall is dampened by a more or less thick flock with any possible shape; handling a glass fiber flock does not require for the operator any safety care by means of particular anti-pollution devices. [0025]
  • The glass thread is continuous and therefore does not have any needle-like part. The thickness of the glass thread is 25 μM, does not spread in the ambient air and therefore is not inhaled, does not produce chemical vapors or exhalation of any type. [0026]
  • This softness property obtained with am homogeneous capillary fabric performs the task of keeping air within small spaces and prevents the underlying surface from scattering heat (in other words it prevents temperature drops and the necessity to spend energy to re-integrate it). [0027]
  • The melting temperature of the glass fiber is about 1,200° C., therefore it can be easily used at temperatures below this value thus allowing a large number of applications. [0028]
  • In order to give a support to the insulating glass wool, a net has been made from non-bulked glass strand to form a kind of container or false wall. In this way it is possible to form mats with the desired dimension using only glass. [0029]
  • Advantageously, some applications in the field of exhaust pipe mufflers production for motorcars would not allow to insert the insulating glass wool in accordance with the density requirements, since not all the insulating walls are available. [0030]
  • Actually, while producing compression molded mufflers, the operator necessarily has to gain access therein by keeping one of the shells raised. Any material introduced therein which has not been previously given a stable shape will tend to come out of the seat where it was placed. [0031]
  • Blowing in the glass wool through a glass net makes it possible to obtain any desired density and, at the same time, to create a false wall defined by that part of glass net which does not match any real wall. This false wall keeps the otherwise free-flowing material. [0032]
  • Consequently, the above mentioned net takes a selected spatial arrangement. [0033]
  • In case this arrangement is too complex, the net can be stiffened with a selected substance, starch for instance, at least in the external part forming the false wall. [0034]
  • The net can be compacted until it becomes like a woven material. [0035]
  • To optimize the insulating property of the proposed preform, a layer of material, preferably metallic such as aluminum, is applied at least to the surface of the shell which does not match with any wall, so as to avoid any air passage from inside the shell to outside, and vice versa. In this way, a shield is obtained which keeps the air within the preform. [0036]
  • In all those cases in which a glass wool preform was used, from now on the following will be used instead: [0037]
  • a preform which has not any needle-like parts, so that operators will not have to face any risk; [0038]
  • a preform which does not release any part smaller than 3 μm; an environment in which health is not endangered is thus obtained and the device provided with this new kind of filled insulation do not present any problem deriving from spreading particles in the ambient; [0039]
  • a preform is obtained which is not impregnated with chemical additives, which does not cause exhalations inside heated environments, with possible problems connected with the toxicologic characteristics of the product. [0040]
  • As far as other applications in which pre-molded blocks of rock wool are to be used, the advantages deriving from the presence of false walls and bulked glass are as follows: [0041]
  • recesses filled with glass only, no exhalations because of resins; [0042]
  • no more storage expenses due to hundreds of different pre-formed blocks; [0043]
  • an insulating product which, not only does not release hazardous particles, but it also does not release anything even after some time (the product includes continuous threads) thus obtaining a longer life of the silencer devices. [0044]
  • As a final consideration, the preform proposed includes glass wool and a net, made of the same material as the glass wool, which are held together to form geometrical shapes without the use of any glue and/or impregnating substances. [0045]
  • It should be understood that the above description is by way of unlimited example only, inasmuch as constructional and practical modifications remain decidedly within the scope of the protection afforded to the present invention as described above and as claimed below. [0046]

Claims (11)

1. A method for producing an insulating preform including a mass of mass of glass threads resembling wool, obtained by extreme bulking of glass fiber in form of increasing the volume of the glass fiber as much as possible, and a support for holding the glass wool, the method including the steps of:
inflating a strand of glass fiber by means of the air jet generated by a nozzle, thus forming a mass of glass fibers;
providing a support for the inflated glass fiber from non bulked strand of glass fibers, the support having a conformation corresponding to its use.
2. A method according to claim 1, wherein the support taking a form a kinnd of container or a false wall complementary to a wall raised or removed of the component into which the preform is to be inserted.
3. A method according to claim 1, wherein the support is obtained by blowing in the glass wool through a net made of fiber glass strands.
4. A method according to claim 2, wherein the net is stiffened by means of a starch.
5. An insulating preform as obtained by the method of claims 1 to 4, including a mass of mass of glass threads resembling wool, obtained by extreme bulking of glass fiber in form of increasing the volume of the glass fiber as much as possible, and a support for holding the glass wool, the support being formed by a net made of the same material as the glass wool and defined by a strand of non-bulked glass in the form of a strand of glass fiber, the glass threads resembling wool and the net being held together, due to elastic reaction of the bulked glass fiber, to form geometrical shapes without any help from glue and/or impregnating substances, these shapes corresponding to the use of the preform.
6. A preform as in claim 5, characterized in that the net is compacted to define a cloth.
7. A preform as in claim 5, characterized in that at least the part of the net that does not match any real wall is stiffened by means of a selected substance.
8. A preform as in claim 5, characterized in that at least the part of the net that does not match any real wall is coated with a layer of material such as to prevent air passage from inside the preform to outside and vice-versa.
9. A preform as in claim 8, characterized in that the layer of material is metallic.
10. A preform as in claim 5, characterized in that the support has shape of a container that defines a seat for receiving said glass wool.
11. A preform as in claim 5, characterized in that the support has a false wall co-operating with a real wall to define a seat for receiving said glass wool.
US10/258,996 2000-05-09 2001-05-08 Insulating preform Abandoned US20030116307A1 (en)