US20030114014A1 - Photoresist stripping solution and a method of stripping photoresists using the same - Google Patents

Photoresist stripping solution and a method of stripping photoresists using the same Download PDF

Info

Publication number
US20030114014A1
US20030114014A1 US10/208,096 US20809602A US2003114014A1 US 20030114014 A1 US20030114014 A1 US 20030114014A1 US 20809602 A US20809602 A US 20809602A US 2003114014 A1 US2003114014 A1 US 2003114014A1
Authority
US
United States
Prior art keywords
photoresist
stripping
stripping solution
substrate
component
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/208,096
Inventor
Shigeru Yokoi
Kazumasa Wakiya
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tokyo Ohka Kogyo Co Ltd
University of California
Original Assignee
Tokyo Ohka Kogyo Co Ltd
University of California
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Assigned to REGENTS OF THE UNIVERSITY OF CALIFORNIA, THE reassignment REGENTS OF THE UNIVERSITY OF CALIFORNIA, THE ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: ASAY, BLAINE, BUSSE, JAMES, HISKEY, MICHAEL A., NAUD, DARREN, SON, STEVEN F.
Application filed by Tokyo Ohka Kogyo Co Ltd, University of California filed Critical Tokyo Ohka Kogyo Co Ltd
Assigned to TOKYO OHKA KOGYO CO., LTD. reassignment TOKYO OHKA KOGYO CO., LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: WAKIYA, KAZUMASA, YOKOI, SHIGERU
Publication of US20030114014A1 publication Critical patent/US20030114014A1/en
Priority to US10/973,302 priority Critical patent/US20050084792A1/en
Priority to US11/503,189 priority patent/US20070037087A1/en
Priority to US11/898,174 priority patent/US8192923B2/en
Abandoned legal-status Critical Current

Abstract

A photoresist stripping solution which comprises (a) a salt of hydrofluoric acid with a base free from metal ions, (b) a water-soluble organic solvent, (c) a mercapto group containing corrosion inhibitor, and (d) water, and a method of stripping photoresists with the use of the same are disclosed. In case of using ammonium fluoride as component (a), the photoresist stripping solution may further contain (e) a salt of hydrofluoric acid with a quaternary ammonium hydroxide, such as tetramethylammonium hydroxide, tetrapropylammonium hydroxide, etc., and/or an alkanolamine. The photoresist stripping solution of the present invention has an excellent effect of protecting both Al- and Cu-based metal wiring conductors from corrosion, of efficiently stripping photoresist films and post-ashing residues, and is free from the precipitation of the corrosion inhibitor.

Description

    BACKGROUND OF THE INVENTION
  • 1. Field of the Invention [0001]
  • This invention relates to a photoresist stripping solution and a method of stripping photoresists using the same. More particularly, it relates to a photoresist stripping solution which is excellent in protecting both Al- and Cu-based wiring conductors and other metal conductors from corrosion and in stripping photoresist films and post-ashing residues; and a method of photoresists using the same. The present invention is suitable for use in the fabrication of semiconductor devices such as ICs and LSIs, as well as liquid-crystal panel apparatus. [0002]
  • 2. Description of Relevant Art [0003]
  • The fabrication of semiconductor devices such as ICs and LSIs, as well as liquid-crystal panel apparatus, comprises forming a uniform photoresist coating over conductive metallic layers, insulation layers such as an SiO[0004] 2 film formed on a substrate (silicon wafer) by CVD; performing selective exposure and development to form a photoresist pattern; selectively etching the substrate having the conductive metallic layers, the insulation layers formed thereon using the photoresist pattern as a mask to thereby form a microcircuit; and then removing the unwanted photoresist layer with a stripping solution. For removal of such unwanted photoresist layers, various organic stripping solutions has been used from safety and strippability standpoints.
  • Examples of the conductive metallic layers formed by CVD as described above include those of aluminum (Al); aluminum alloys (Al alloys) such as aluminum-silicon (Al—Si), aluminum copper (Al—Cu) and aluminum-silicon-copper (Al—Si—Cu); titanium (Ti); titanium alloys (Ti alloys) such as titanium nitride (TiN) and titanium-tungsten (TiW); tantalum (Ta), tantalum nitride (TaN), tungsten (W), tungsten nitride (WN) and copper (Cu). These conductive metallic films are formed in one or more layers on the substrate. In recent years, both of devices having Al-based conductors (Al and Al alloy-based wirings) and devices having Cu-based conductors are coexisted. Accordingly, it has been required to protect both of these two types of devices from corrosion with the use of a single photoresist stripping solution. [0005]
  • Furthermore, with the recent tendency toward highly integrated, high-density circuits, dry etching enabling fine etching with a higher density has become the major means. Also, it has been a practice to employ plasma ashing to remove the unwanted photoresist layers remaining after etching. After these etching and ashing treatments, residues comprising modified photoresist films and other components that are referred to horn-like shaped “veil”, “fences” or “side-walls” remain on the bottom or side wall of patterned grooves. In case of forming a pattern on a substrate having an Si-based interlayer film, such as an Si-based insulation film (SiN film, SiO2 film, etc.) and a low dielectric film (SOG film, etc.), Si-based residues (Si-based depositions) are sometimes formed around pattern hole openings. In addition, etching of metallic layers and ashing treatment builds up metal depositions. Such post-ashing residues or depositions should be completely stripped away so as to keep good yields in the fabrication of semiconductors. [0006]
  • In recent years, further highly-density and highly-integrated substrates are needed, and thus the treating conditions in the etching and ashing steps become more and more strict. As a result, it is also urgently required to achieve improved corrosion resistance of metal wirings as well as improved residue-strippability of stripping solutions, compared with conventional ones. [0007]
  • Under these circumstances, there have been frequently employed stripping solutions for photoresists and post-ashing residues which contain amines or hydrofluoric acid as the main component. Among all, those containing hydrof luoric acid as the main component show excellent strippability especially for post-ashing residues. [0008]
  • Examples of stripping solutions containing hydrofluoric acid as the main component include: a resist stripping solution composition of pH 5-8 containing a salt of hydrofluoric acid with a base free from metal ions, a water-soluble organic solvent and water optionally together with a corrosion inhibitor (JP-A-9-197681); and a cleaner for semiconductor devices containing a quaternary ammonium salt and a fluorine compound, and further adding a water-soluble organic solvent (JP-A-7-201794). [0009]
  • The resist stripping solution composition in JP-A-9-197681 is to a certain extent effective in strippability and anti-corrosivity on semiconductor devices having Al wiring conductors, however, it fails to exert any satisfactory effect of protecting devices having Cu wiring conductors from corrosion. [0010]
  • In the cleaner in JP-A-7-201794, tetramethylammonium formate and trimethyl(2-hydroxyethyl)ammonium salt are used as the quaternary ammonium salt. Although the corrosion of Cu wiring conductors can be relieved to a certain extent by using these compounds, there arises another problem that strippability for Cu-based metallic depositions (residues) is still insufficient. [0011]
  • JP-A-2000-273666 teaches a cleaner solution containing a sulfur-based corrosion inhibitor for protecting Cu wiring conductors from corrosion. However, any satisfactory strippability for Cu-based metallic depositions (residues) also cannot be established by using this cleaner solution. [0012]
  • As discussed above, none of the conventional photoresist stripping solutions can satisfy both of the requirements for efficient strippability and effective inhibition of metal corrosion. This is because strippability offsets the performance of inhibiting corrosion in a photoresist stripping solution. That is to say, there is a problem that one of the above-described requirement cannot be fulfilled unless the other is sacrificed. In the ultrafine processing employed in these days, in particular, the strippability for photoresist films and post-ashing residues should be further improved and it is therefore needed to enhance the effect of protecting metal wirings from corrosion. Recent models of semiconductor devices can be divided into two type, one using Al wiring conductors (Al, Al alloy and other Al-based metal wiring) and the other using Cu wiring conductors (Cu-based metal wiring). In addition to the need to protect devices of these two types from corrosion with the use of a single stripping solution, it is also required to provide effective protection against corrosion of other metals on the devices. Further improvements are desired to achieve effective stripping away of photoresists and post-ashing residues and to protect metal conductors from corrosion. [0013]
  • SUMMARY OF THE INVENTION
  • The present invention has been accomplished under these circumstances and has as an object of providing a photoresist stripping solution that is suitable for use in the photolithographic technology to form today's semiconductor and liquid-crystal display devices having an ever decreasing feature size and an increasing number of interlevel films superposed on the substrate, and that can assure effective protection of Al, Cu and other wiring metal conductors against corrosion as well as efficient stripping of the photoresist film and post-ashing residues. [0014]
  • To attain the above-described objects, the present invention provides a photoresist stripping solution which comprises (a) a salt of hydrof luoric acid with a base free from metal ions, (b) a water-soluble organic solvent, (c) a mercapto group containing corrosion inhibitor, and (d) water. [0015]
  • The present invention also provides a photoresist stripping solution which further contains, in addition to components (a)-(d), with the proviso that component (a) is ammonium fluoride, (e) a salt of hydrofluoric acid with a quaternary ammonium hydroxide represented by the following general formula (I) and/or an alkanolamine: [0016]
    Figure US20030114014A1-20030619-C00001
  • wherein R[0017] 1, R2, R3 and R4 are each independently an alkyl group or a hydroxyalkyl group having 1 to 4 carbon atoms.
  • The present invention furthermore provides a method of stripping photoresists which comprises forming a photoresist pattern on a substrate, etching the substrate using the photoresist as a mask, and thereafter stripping away the photoresist pattern from the substrate using the photoresist stripping solution as described above. [0018]
  • The present invention still furthermore provides a method of stripping photoresists which comprises forming a photoresist pattern on a substrate, etching the substrate using the photoresist as a mask, then plasma ashing the photoresist pattern, and thereafter stripping away post-plasma ashing residues from the substrate using the photoresist stripping solution as described above. [0019]
  • DETAILED DESCRIPTION OF THE INVENTION
  • The present invention will be described below in detail. [0020]
  • In the present invention, component (a) is a salt of hydrofluoric acid with a base free from metal ions. Preferable examples of the base free from metal ions include hydroxylamines, organic amines such as primary, secondary or tertiary aliphatic amines, alicyclic amines, aromatic amines and heterocyclic amines, aqueous ammonia, and lower alkyl quaternary ammonium hydroxides. [0021]
  • Specific examples of the hydroxylamines include hydroxylamine (NH[0022] 2OH), N-methylhydroxylamine, N,N-dimethylhydroxylamine and N,N-diethylhydroxylamine.
  • Specific examples of the primary aliphatic amines include monoethanolamine, ethylenediamine and 2-(2-aminoethylamino)ethanol. [0023]
  • Specific examples of the secondary aliphatic amines include diethanolamine, N-methylaminoethanol, dipropylamine and 2-ethylaminoethanol. [0024]
  • Specific examples of the tertiary aliphatic amines include dimethylaminoethanol and ethyldiethanolamine. [0025]
  • Specific examples of the alicyclic amines include cyclohexylamine and dicyclohexylamine. [0026]
  • Specific examples of the aromatic amines include benzylamine, dibenzylamine and N-methylbenzylamine. [0027]
  • Specific examples of the heterocyclic amines include pyrrole, pyrrolidine, pyrrolidone, pyridine, morpholine, pyrazine, piperidine, N-hydroxyethylpiperidine, oxazole and thiazole. [0028]
  • Specific examples of the lower alkyl quaternary ammonium salts include tetramethylammonium hydroxide (TMAH), tetraethylammonium hydroxide, tetrapropylammonium hydroxide, trimethylethylammonium hydroxide, (2-hydroxyethyl)trimethylammonium hydroxide, (2-hydroxyethyl)triethylammonium hydroxide, (2-hydroxyethyl)tripropylammonium hydroxide and (1-hydroxypropyl)trimethylammonium hydroxide. [0029]
  • Among these bases, aqueous ammonia, monoethanolamine, N-methylaminoethanol, tetramethylammonium hydroxide and (2-hydroxyethyl)trimethylammonium hydroxide are preferable from availability and safety standpoints. [0030]
  • The bases free from metal ions may be used either alone or in combination with one another. [0031]
  • The salt of hydrofluoric acid with the base free from metal ions may be prepared using a commercially available hydrofluoric acid having a concentration of 50-60% and adding thereto the base free from metal ions. As the salt, ammonium fluoride (NH[0032] 4F) may be the most desirable. Either one or more salts may be used as component (a).
  • The content of component (a) preferably ranges 0.1-10 mass percent, still preferably 0.2-3 mass percent in the stripping solution of the invention. In case where the content of component (a) is too large, Cu wiring conductors tend to corrode. In case where its content is too small, on the other hand, the strippability is liable to be lowered. [0033]
  • As component (b) that is a water-soluble organic solvent, use may be made of those commonly employed in the art. Such a water-soluble organic solvent is not specifically restricted so long as it is miscible with water and other components employed in the present invention. Specific examples thereof include: sulfoxides, such as dimethyl sulfoxide; sulfones, such as dimethyl sulfone, diethyl sulfone, bis(2-hydroxyethyl)sulfone and tetramethylene sulfone; amides, such as N,N-dimethylformamide, N-methylformamide, N,N-dimethylacetamide, N-methylacetamide and N,N-diethylacetamide; lactams, such as N-methyl-2-pyrrolidone, N-ethyl-2-pyrrolidone, N-propyl-2-pyrrolidone, N-hydroxymethyl-2-pyrrolidone and N-hydroxyethyl-2-pyrrolidone; imidazolidinones, such as 1,3-dimethyl-2-imidazolidinone, 1,3-diethyl-2-imidazolidinone and 1,3-diisopropyl-2-imidazolidinone; and polyhydric alcohols and derivatives thereof, such as ethylene glycol, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monobutyl ether, ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, diethylene glycol, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether, propylene glycol monopropyl ether and propylene glycol monobutyl ether. Among these organic solvents, preferable ones are dimethylformamide, N-methyl-2-pyrrolidone and dimethyl sulfoxide. Dimethylformamide is the most desirable since it can be easily handled after stripping treatment. Either one or more solvents may be used as component (b). [0034]
  • The content of component (b) preferably ranges 30-80 mass percent, still preferably 40-75 mass percent in the stripping solution of the present invention. In case where the content of component (b) is too large, the strippability is liable to be lowered. In case where its content is too small, on the other hand, various metal wiring conductors tend to corrode. [0035]
  • Although the mercapto group containing corrosion inhibitor to be used as component (c) is not specifically restricted so long as it can protect metal atoms employed in wiring conductors (in particular, Al wiring or Cu wiring) from corrosion, it is preferable to use a compound having in its structure a hydroxyl group and/or a carboxyl group at least one of the α- and β-positions. Specific examples of such a compound include 1-thioglycerol, 3-(2-aminophenylthio)-2-hydroxypropylmercaptan, 3-(2-hydroxyethylthio)-2-hydroxypropylmercaptan, 2-mercaptopropionic acid and 3-mercaptopropionic acid. Among these compounds, 1-thioglycerol is particularly preferable. In the present invention, component (c) is used as a corrosion inhibitor to thereby achieve an excellent effect of protecting Al and Cu wiring conductors from corrosion as well as an effect of preventing precipitation of the corrosion inhibitor. [0036]
  • Either one or more compounds may be used as component (c). The content of component (c) preferably ranges 0.1-10 mass percent, still preferably 0.2-5 mass percent in the stripping solution of the invention. In case where the content of component (a) is too small, there is a fear that insufficient effect may be provided for protecting in particular Cu wiring conductors from corrosion. [0037]
  • Component (d) in the stripping solution of the invention is water. Although some water is contained inevitably in other components, water is intentionally added to adjust the content. The content of component (d) is the balance of the stripping solution of the present invention. [0038]
  • In addition to components (a)-(d), with the proviso that component (a) is ammonium fluoride, the stripping solution of the invention may further incorporate into the stripping solution (e) a salt of hydrof luoric acid with a quaternary ammonium hydroxide represented by the following general formula (I) and/or an alkanolamine: [0039]
    Figure US20030114014A1-20030619-C00002
  • wherein R[0040] 1, R2, R3 and R4 are each independently an alkyl group or a hydroxyalkyl group having 1 to 4 carbon atoms. Use of component (e) contributes to the improvement in the strippability without seriously damaging Cu.
  • Specific examples of the quaternary ammonium hydroxide represented by the general formula (I) include tetramethylammonium hydroxide (TMAH), tetraethylammonium hydroxide, tetrapropylammonium hydroxide, tetrabutylammonium hydroxide, monomethyltripleammonium hydroxide, trimethylethylammonium hydroxide, (2-hydroxyethyl)trimethylammonium hydroxide, (2-hydroxyethyl)triethylammonium hydroxide, (2-hydroxyethyl)tripropylammonium hydroxide and (1-hydroxypropyl)trimethylammonium hydroxide. Among these compounds, TMAH, tetraethylammonium hydroxide, tetrapropylammonium hydroxide, tetrabutylammonium hydroxide, monomethyltripleammonium hydroxide, (2-hydroxyethyl)trimethylammoniumhydroxide, etc. are preferable from availability and safety standpoints. [0041]
  • Examples of the above-described alkanolamines include monoethanolamine, diethanolamine, triethanolamine, 2-(2-aminoethoxy)ethanol, N,N-dimethylethanolamine, N,N-diethylethanolamine, N,N-dibutylethanolamine, N-methylethanolamine, N-ethylethanolamine, N-butylethanolamine, N-methyldiethanolamine, monoisopropanolamine, diisopropanolamine and triisopropanolamine. Among these compounds, N-methylethanolamine is particularly preferable in terms of protecting Cu wiring conductors from corrosion. [0042]
  • Either one or more compounds may be used as component (e). The content of component (e) preferably ranges 0.1-10 mass percent, still preferably 0.2-3 mass percent in the stripping solution of the invention. In case where the content of component (e) is too large, Al wiring conductors tend to corrode. [0043]
  • In case of using component (e) in the present invention, it is preferable to adjust the composition ratio of ammonium fluoride employed as component (a) to component (e) [ammonium fluoride: component (e)] to from 2:8 to 8:2 by mass, still preferably from 3:7 to 7:3. By regulating the composition ratio of fluoride ammonium to component (e) within the range as specified above, metal wiring conductors can be more efficiently protected from corrosion. In case where the content of ammonium fluoride exceeds the upper limit as specified above, Al-based wiring conductors are prone to corrode. In case where the content of component (e) exceeds the upper limit as specified above, on the other hand, Cu-based wiring conductors are prone to corrode. [0044]
  • In order to improve penetrating properties, the stripping solution of the invention may further contain, as an optional component, an acetylene alcohol/alkylene oxide adduct prepared by adding an alkylene oxide to an acetylene alcohol. [0045]
  • As the acetylene alcohol as described above, use may be preferably made of compounds represented by the following general formula (II): [0046]
    Figure US20030114014A1-20030619-C00003
  • wherein R[0047] 5 is a hydrogen atom or a group represented by the following formula (III);
    Figure US20030114014A1-20030619-C00004
  • and R[0048] 6, R7, R8 and R9 are each independently a hydrogen atom or an alkyl group having 1-6 carbon atoms.
  • These acetylene alcohols are commercially available under trade names of “Surfynol” and “Olfin” series (both are produced by Air Products and Chemicals Inc.). Among these commercial products, “Surfynol 104”, “Surfynol 82” or mixtures thereof are most preferred for the physical properties. Use can be also made of “Olfin B”, “Olfin P”, “Olfin Y” etc. [0049]
  • As the alkylene oxide to be added to the acetylene alcohol as described above, it is preferred to use ethylene oxide, propylene oxide or a mixture thereof. [0050]
  • In the present invention, it is preferable to use, as the acetylene alcohol/alkylene oxide adduct, compounds represented by the following general formula (IV): [0051]
    Figure US20030114014A1-20030619-C00005
  • wherein R[0052] 10 is a hydrogen atom or a group represented by the following formula (V):
    Figure US20030114014A1-20030619-C00006
  • and R[0053] 11, R12, R13 and R14 are each independently a hydrogen atom or an alkyl group having 1-6 carbon atoms; (n+m) is an integer of 1 to 30, which is the number of ethylene oxide molecules added. This number subtly affects the properties of the compound such as water solubility and surface tension.
  • The acetylene alcohol/alkylene oxide adducts per se are known as surfactants. These products are commercially available under the trade name “Surfynol” series (products of Air Product and Chemicals Inc.) and “Acetylenol” series (products of Kawaken Fine Chemicals Co., Ltd.) and have been appropriately utilized. Among these products, it is preferred to use “Surfynol 440” (n+m=3.5), “Surfynol 465” (n+m=10), “Surfynol 485” (n+m=30), “Acetylenol EL” (n+m=4), “Acetylenol EH” (n+m=10) or mixtures thereof, in view of the changes in their physical properties such as water solubility and surface tension depending on the number of ethylene oxide molecules added. A mixture of “Acetylenol EL” with “Acetylenol EH” in a mass ratio of 2:8 to 4:6 is particularly desirable. [0054]
  • Use of the acetylene alcohol/alkylene oxide adduct makes it possible to improve the penetrating properties and wetting properties of the stripping solution. [0055]
  • When the stripping solution of the invention contains the acetylene alcohol/alkylene oxide adduct, the content thereof is preferably 0.05-5 mass percent, more preferably 0.1-2 mass percent. When the content exceeds the upper limit as defined above, it tends to cause foaming but the wetting properties cannot be improved any more. When the content is less than the lower limit as defined above, on the other hand, the desired improvement in the wetting properties can be scarcely obtained. [0056]
  • To complete the stripping treatment in a short period of time, the stripping solution of the invention may further contain an acidic compound. Examples of the acidic compound include hydrof luoric acid, acetic acid and glycolic acid. In case of using such an acidic compound, its content is preferably 1 mass percent or less. When the stripping solution of the invention contains the acidic compound, the strippability of Si-based depositions can be particularly improved. Thus, the stripping time can be shortened and an excellent effect of stripping Si-based depositions can be established thereby. [0057]
  • The photoresist stripping solution of the invention can advantageously be used with all photoresists, whether negative- or positive-working, that can be developed with aqueous alkaline solutions. Such photoresists include, but are not limited to, (i) a positive-working photoresist containing a naphthoquinonediazide compound and a novolak resin, (ii) a positive-working photoresist containing a compound that generates an acid upon exposure, a compound that decomposes with an acid to have a higher solubility in aqueous alkali solutions, and an alkali-soluble resin, (iii) a positive-working photoresist containing a compound that generates an acid upon exposure and an alkali-soluble resin having a group that decomposes with an acid to have a higher solubility in aqueous alkali solutions, and (iv) a negative-working photoresist containing a compound that generates an acid upon illumination with light, a crosslinker and an alkali-soluble resin. [0058]
  • According to the invention, photoresists are stripped away by one of two methods which have the following steps in common: forming a photoresist pattern by lithography on a substrate having conductive metallic layers, insulation layers and low-dielectric layers thereon, and selectively etching the layers with the photoresist pattern used as a mask to form a fine-line circuit. After these steps, the photoresist pattern is immediately stripped away (method I), or the etched photoresist pattern is subjected to plasma ashing and thereby post-ashing residues, such as the modified photoresist film (photoresist film residue) and metal deposition, are stripped away (method II). [0059]
  • An example of method I in which the photoresist film is stripped away immediately after etching comprises: [0060]
  • (I) providing a photoresist layer on a substrate; [0061]
  • (II) selectively exposing said photoresist layer; [0062]
  • (III) developing the exposed photoresist layer to provide a photoresist pattern; [0063]
  • (IV) etching the substrate to form a pattern using said photoresist pattern as a mask; and [0064]
  • (V) stripping away the photoresist pattern from the etched substrate using the photoresist stripping solution of the present invention. [0065]
  • An example of method II in which the modified photoresist film and metal deposition resulting from plasma ashing are stripped away after etching comprises: [0066]
  • (I) providing a photoresist layer on a substrate; [0067]
  • (II) selectively exposing said photoresist layer; [0068]
  • (III) developing the exposed photoresist layer to provide a photoresist pattern; [0069]
  • (IV) etching the substrate to form a pattern using said photoresist pattern as a mask; [0070]
  • (V) plasma ashing the photoresist pattern; [0071]
  • (VI) stripping away the post-ashing residues using the photoresist stripping solution of the present invention. [0072]
  • The specific advantage of the present invention resides in that the photoresist stripping solution has excellent effects of stripping photoresist films and post-ashing residues (modified photoresist films, metal depositions, etc.) and protecting a substrate having metal conductors from corrosion both in stripping away photoresists formed on a substrate having Al wiring conductors and formed on a substrate having Cu wiring conductors. [0073]
  • Examples of the metal wiring conductors include, but are not limited to, those made of aluminum (Al); aluminum alloys such as aluminum copper (Al—Cu) and aluminum-silicon-copper (Al—Si—Cu); titanium (Ti); titanium alloys (Ti alloys) such as titanium nitride (TiN) and titanium-tungsten (TiW); and copper (Cu). [0074]
  • Using conventional photoresist stripping solutions, it is very difficult to satisfy both of the requirements for efficient strippability for photoresists and post-ashing residues and effective inhibition of metal corrosion in Al-based wiring devices and Cu-based wiring devices. According to the present invention, however, both of these requirements can be successfully satisfied by combining components (a)-(d) with each other. Using component (e) in addition to components (a)-(d), with the proviso that component (a) is ammonium fluoride, the strippability can be further improved without seriously damaging Cu. [0075]
  • In the second stripping method described above, residue adhere to the substrate surface after plasma ashing, such as photoresist residue (modified photoresist film) and metal deposition that formed during etching of the metal film. These residues are contacted by the stripping solution of the invention so that they are stripped away from the substrate surface. Plasma ashing is inherently a method for removing the photoresist pattern but it often occurs that part of the photoresist pattern remains as a modified film; the present invention is particularly effective for the purpose of completely stripping away such modified photoresist film. [0076]
  • In forming the photoresist layer, and exposing, developing and etching treatments, any conventional means may be employed without particular limitation. [0077]
  • After the development step (III) or the stripping step (V) or (VI), conventional rinsing may optionally be performed using pure water, lower alcohols, etc., followed by drying. [0078]
  • The photoresist is usually stripped by the dip, shower or paddle method. The stripping time is not limited to any duration as long as it is sufficient to achieve removal of the photoresist.[0079]
  • EXAMPLES
  • The following examples are provided for the purpose of further illustrating the present invention but are in no way to be taken as limiting. Unless otherwise noted, all compounding amounts are expressed by mass percent. [0080]
  • [Treatment 1][0081]
  • A silicon wafer having an SiO[0082] 2 layer formed thereon was used as a substrate. On this substrate, a TiN layer, an Al—Si—Cu layer and another TiN layer were successively formed thereon respectively as the first, second and third layers. The topmost layer was spin-coated with a positive-working photoresist (TDUR-P015 of Tokyo Ohka Kogyo Co., Ltd.), which was prebaked at 80° C. for 90 seconds to form a photoresist layer 0.7 μm thick.
  • The photoresist layer was exposed through a mask pattern using FPA 3000 EX3 (Canon Inc.), then subjected to post-exposure bake at 110° C. for 90 seconds and developed with an aqueous solution of 2.38 mass percent tetraammonium hydroxide (TMAH) to form a photoresist pattern of 400 nm in line-and-space. Subsequently it was subjected to dry etching and plasma ashing. [0083]
  • [Treatment II][0084]
  • A silicon wafer having Cu layer that is overlaid with an SiO[0085] 2 layer formed by plasma CVD was used as a substrate. The substrate was spin-coated with a positive-working photoresist (TDUR-P015 of Tokyo Ohka Kogyo Co., Ltd.), which was prebaked at 80° C. for 90 seconds to form a photoresist layer 0.7 μm thick.
  • The photoresist layer was exposed through a mask pattern using FPA 3000 EX3 (Canon Inc.), then subjected to post-exposure bake at 110° C. for 90 seconds and developed with an aqueous solution of 2.38 mass percent tetraammonium hydroxide (TMAH) to form a hole pattern of 200 nm in diameter. Subsequently it was subjected to dry etching and plasma ashing. [0086]
  • EXAMPLES 1-8 and COMPARATIVE EXAMPLES 1-5 [0087]
  • The thusly treated substrate in treatment I or II as described above was dipped (25° C., 5 minutes) in each photoresist stripping solution as indicated in Table 1 for stripping. In Example 8, dipping was carried out for 1 minute. After the completion of the stripping treatment, each substrate was rinsed with purified water. Then the substrate was observed under a scanning electron microscope (SEM) to evaluate strippability of the post-ashing residues, state of corrosion of metal wiring conductors and precipitation of the corrosion inhibitor. The results are shown in Table 2. [0088]
  • The strippability of the post-ashing residues, state of corrosion of metal wiring conductors and precipitation of the corrosion inhibitor were evaluated in accordance with the following criteria. [0089]
  • The strippability of the post-ashing residues was evaluated by using the substrate treated in treatment II. Regarding the protection of metals from corrosion, the substrate treated in treatment I was mainly used for Al wiring, and the one treated in treatment II was mainly used for Cu wiring. The precipitation of the corrosion inhibitor was evaluated by using the substrate treated in treatment II. [0090]
  • [Strippability of Post-ashing Residues (Cu-based Depositions and Si-based Depositions)][0091]
  • ⊚: Complete stripping [0092]
  • ◯: Almost complete stripping [0093]
  • Δ: Some residues remained [0094]
  • X: Much residues remained [0095]
  • [Protection of Metal Wiring Conductors (Al and Cu) from Corrosion][0096]
  • ⊚: No corrosion found [0097]
  • ◯: Little corrosion found [0098]
  • Δ: Suffered from somewhat corrosion [0099]
  • X: Suffered from corrosion [0100]
  • [State of Precipitation of Corrosion Inhibitor][0101]
  • ⊚: No precipitation of corrosion inhibitor found [0102]
  • ◯: Little precipitation of corrosion inhibitor found [0103]
  • Δ: Suffered from somewhat precipitation of corrosion inhibitor [0104]
  • X: Suffered from precipitation of corrosion inhibitor [0105]
    TABLE 1
    Photoresist stripping solution (mass %)
    Other
    Compo- Compo- Com- Compo- Compo- com-
    nent (a) nent (b) ponent (c) nent (d) nent (e) ponent
    Ex. 1 NH4F DMSO Cor. inhib. water
    (0.5) (70) A (2) (27.5)
    Ex. 2 NH4F DMSO Cor. inhib. water
    (2)   (50) B (1) (47)  
    Ex. 3 NH4F DMF Cor. inhib. water acetylene
    (1)   (60) C (1) (37.5) alcohol/
    alkylene
    oxide ad-
    duct (0.5)
    Ex. 4 NH4F DMSO Cor. inhib. water HF/TMAH
    (0.5) (70) D (1) (28)   (0.5)
    Ex. 5 NH4F DMSO Cor. inhib. water HF/TPAH acetylene
    (1.2) (50) E (0.5) (45.5) (1.8) alcohol/
    alkylene
    oxide ad-
    duct (0.5)
    Ex. 6 NH4F DMF Cor. inhib. water HF/TMAH
    (0.6) (70) A (1) (28)   (0.4)
    Ex. 7 NH4F NMP Cor. inhib. water HF/TMAH
    (0.4) (70) A (1) (28)   (0.6)
    Ex. 8 NH4F NMP Cor. inhib. water HF/TMAH acetic
    (0.5) (70) A (1) (27.7) (0.5) acid (0.3)
    Com. NH4F DMSO Cor. inhib. water
    Ex. 1 (2)   (60) X (2) (36)  
    Com. NH4F DMSO Cor. inhib. water
    Ex. 2 (1)   (50) Y (1) (48)  
    Com. NH4F DMSO Cor. inhib. water
    Ex. 3 (0.5) (75) Z (2) (22.5)
    Com. NH4F DMSO Cor. inhib. water HF/TMAH
    Ex. 4 (0.5) (70) X (1) (28)   (0.5)
    Com. NH4F DMSO Cor. inhib. water HF/TPAH
    Ex. 5 (2)   (50) X (0.5) (46.5) (1)  
  • [0106]
    TABLE 2
    Protection of
    Strippability of metal conductor
    post-ashing residues from corrosion Precipitation
    Cu-based Si-based Cu Al of corrosion
    deposition deposition wiring wiring inhibitor
    Ex. 1
    Ex. 2
    Ex. 3
    Ex. 4
    Ex. 5
    Ex. 6
    Ex. 7
    Ex. 8
    Com. Ex. 1 Δ x
    Com. Ex. 2 x
    Com. Ex. 3 x
    Com. Ex. 4 Δ x
    Com. Ex. 5 Δ x
  • As described above in detail, according to the present invention, there is provided an excellent photoresist stripping solution that causes no corrosion of Al and Cu wiring conductors or any other metals, has excellent strippability for photoresist films and post-ashing residues and is free from precipitation of a corrosion inhibitor. Use of the photoresist stripping solution of the present invention makes it possible to effectively protect both of devices having Al wiring conductors and devices having Cu wiring conductors from corrosion. [0107]

Claims (11)

What is claimed is:
1. A photoresist stripping solution which comprises (a) a salt of hydrofluoric acid with a base free from metal ions, (b) a water-soluble organic solvent, (c) a mercapto group containing corrosion inhibitor, and (d) water.
2. The photoresist stripping solution according to claim 1, wherein component (a) is ammonium fluoride.
3. The photoresist stripping solution according to claim 1, wherein component (b) is at least one member selected from among dimethylformamide, N-methyl-2-pyrrolidone and dimethyl sulfoxide.
4. The photoresist stripping solution according to claim 1, wherein component (c) is a compound having in its structure a hydroxyl group and/or a carboxyl group at least one of the α- and β-positions.
5. The photoresist stripping solution according to claim 1, wherein component (c) is at least one member selected from among 1-thioglycerol, 3-(2-aminophenylthio)-2-hydroxypropylmercaptan, 3-(2-hydroxyethylthio)-2-hydroxypropylmercaptan, 2-mercaptopropionic acid and 3-mercaptopropionic acid.
6. The photoresist stripping solution according to claim 1, which further contains, in addition to components (a)-(d), with the proviso that component (a) is ammonium fluoride, (e) a salt of hydrofluoric acid with a quaternary ammonium hydroxide represented by the following general formula (I) and/or an alkanolamine:
Figure US20030114014A1-20030619-C00007
wherein R1, R2, R3 and R4 are each independently an alkyl group or a hydroxyalkyl group having 1 to 4 carbon atoms.
7. The photoresist stripping solution according to claim 6, wherein the composition ratio of component (a) : component (e) ranges from 2:8 to 8:2 by mass.
8. A method of stripping photoresists which comprises forming a photoresist pattern on a substrate, etching the substrate using said photoresist as a mask, and thereafter stripping away the photoresist pattern from the substrate using the photoresist stripping solution according to any one of claims 1-7.
9. A method of stripping photoresists which comprises forming a photoresist pattern on a substrate, etching the substrate using said photoresist as a mask, then plasma ashing the photoresist pattern, and thereafter stripping away post-plasma ashing residues from the substrate using the photoresist stripping solution according to any one of claims 1-7.
10. The method of stripping photoresists according to claim 8 or 9, wherein the substrate has either Al wiring conductor or Cu wiring conductor or both thereon.
11. The method of stripping photoresists according to claim 8 or 9, wherein the substrate has at least an Si-based interlevel film thereon.
US10/208,096 2001-08-03 2002-07-31 Photoresist stripping solution and a method of stripping photoresists using the same Abandoned US20030114014A1 (en)