US20020009609A1 - Roughened bond coats for a thermal barrier coating system and method for producing - Google Patents
Roughened bond coats for a thermal barrier coating system and method for producing Download PDFInfo
- Publication number
- US20020009609A1 US20020009609A1 US09/872,272 US87227201A US2002009609A1 US 20020009609 A1 US20020009609 A1 US 20020009609A1 US 87227201 A US87227201 A US 87227201A US 2002009609 A1 US2002009609 A1 US 2002009609A1
- Authority
- US
- United States
- Prior art keywords
- screen
- metallic material
- bond coat
- range
- disposing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A roughened bond coat comprises a screen that includes interwoven wires defining openings and a metallic material disposed on the screen. The screen and metallic material form a roughened bond coat possessing an uneven, undulated, and irregular surface. The metallic material may be one of a slurry and a powder, and applied by coating and spraying, respectively. A thermal barrier coating system, which is formed with and incorporates the roughened bond coat, exhibits greater adhesion of a thermal barrier coating and bond coat due to an increased interfacial surface area provided by the uneven, undulated, and irregular surface.
Description
- The invention relates to bond coats. In particular, the invention relates to roughened bond coats for thermal barrier coating systems.
- Thermal barrier coating systems are used in hot-section components in turbines, for example jet engine and gas turbines. The thermal barrier coating system insulates the turbines from high temperatures during thermal cycling. Thermal barrier coating systems include a thermal barrier coating (TBC) disposed on a bond coat, which in turn is disposed on a substrate. The thermal barrier coating normally comprises zirconia, such as example at least one of a stabilized zirconia and a partially-stabilized zirconia (PSZ). The bond coat typically comprises an oxidation-resistant metallic layer disposed between the TBC and substrate turbine component. The TBC is adhered to the bond coat typically by mechanical interlocking, so the bond coat provides oxidation resistant to the substrate and a relatively rough surface. The bond coat surface generally has Ra (Arithmetic Average Roughness (Ra) as determined from ANSI/ASME Standard B461-1985) values over about 350 mainly by mechanical interlocking. So the function of the bond coat is to provide oxidation resistant to the substrate and a relatively rough surface, preferably with Ra values over about 350 microinches, for the TBC to adhere to the substrate. Thus, the TBC is disposed over the turbine component can provide thermal insulation.
- FIG. 1 is a schematic representation of a known thermal barrier coating system1. A
substrate 10 comprises an underlying part of a component, for example a turbine component. Abond coat 12 is disposed on thesubstrate 10. The bond coat is disposed on thesubstrate 10 by any appropriate method, for example, but riot limited to, thermal spray processes, such as vacuum plasma spray (VPS), air plasma spray (APS) and hyper-velocity oxy-fuel (HVOF) spray processes. - The structure and roughness of
bond coat surface 13 are dependent on the spray process. Bond coats deposited by a VPS process are typically dense and free of oxides. Therefore, VPS—applied bond coats provide protection at high temperatures against oxidation. The VPS application process disposes fine powders, and thus, VPS—applied bond coats are typically dense, for example having a density greater than about 90% of its theoretical density, but have relatively smooth surfaces. Consequently, a TBC does not adhere well to a VPS bond coat. - An air plasma spray (APS) process produces rough bond coats because of large powders used in APS. The large powders possess a relatively high heat capacity; however, the APS—applied bond coats contain high amounts of oxides. Also, APS—applied bond coats possess a relatively low porosity due to the oxidation environment and low momentum of the powders. Although APS—applied bond coats provide better TBC adhesion due to their roughness, they are more prone to oxidation because of their relatively high oxide levels and relatively low porosity.
- Bond coats deposited by HVOF are sensitive to particle size distributions. Dense and oxide-free bond coats can be deposited by HVOF using very lean conditions (low oxygen amounts) and finer particles, for example particles with a size about −325+10 μm. The surface roughness of HVOF—applied bond coats is relatively smooth. Rough bond coats can be deposited by HVOF using coarser powders, for example particles with a size about −230+325, however a low HVOF flame temperature is needed. The low flame temperatures result in the bond coat comprising unmelted powders, therefore the coating is porous and less dense.
- A
TBC 14 is disposed on thebond coat 12 and forms asurface 15 against thesurface 13. TheTBC 14 is disposed on thebond coat 12 by any appropriate process to adhere (bond) to the bond coat. TheTBC surface 15 andbond coat surface 13 define aninterfacial area 16 at their adjoining surfaces. - Effectiveness of a thermal barrier coating system during thermal cycling is compromised by de-bonding of the TBC and bond coat, for example at the TBC and bond coat interfacial area. De-bonding can be caused by at least one of a poor TBC and bond coat adhesion, and lack of accommodation of thermal expansion mismatch between the TBC and bond coat. The lack of adhesion is characteristic of smooth adjoining surfaces where a total surface area is minimal. The thermal expansion mismatch between the TBC and bond coat results from different coefficients of thermal expansion of the materials used for these features. If the difference in coefficients of thermal expansion of the adhered elements is large, one element expands much more than the other, and separation and de-bonding occur at the interfacial areas. De-bonding of the TBC and bond coat is undesirable as the insulation effect of the thermal barrier coating system will be lost at TBC separation.
- Therefore, it is desirable to increase adhesion between the TBC and the bond coat to prevent de-bonding. The adhesion between the bond coat and TBC can be increased by roughening a bond coat, thus increasing an area at an interfacial area mating surface of adhered elements and enhancing mechanical interlocking adhesion between the bond coat and TBC. Increasing a bond coat's roughness provides an enhanced interfacial surface area for accommodation of any thermal mismatch, with respect to non-roughened bond coats.
- The invention overcomes the above noted deficiencies of known thermal barrier coating systems. The invention sets forth a method of forming a bond coat that comprises providing a screen, where the screen comprises interwoven wires defining openings; providing a metal material; and disposing the metal material onto the screen to form an uneven, undulated, and irregular surface.
- The invention also sets forth a method of forming a roughened bond coat that comprises providing a screen, where the screen comprises interwoven wires defining openings; providing a powder; and plasma spraying the powder on the screen to form an uneven, undulated, and irregular surface.
- The invention also sets forth a further method of forming a roughened bond coat that comprises providing a screen, where the screen comprises interwoven wires defining openings; providing a slurry; and disposing the slurry on the screen to form an uneven, undulated, and irregular surface.
- A roughened bond coat is set forth embodied by the invention, and comprises a screen, where the screen includes interwoven wires defining openings; and a metal material disposed on the screen. The metal material on the screen forms an uneven, undulated, and irregular surface.
- An embodiment of the invention provides a method of forming a thermal barrier coating system, where the thermal barrier coating system comprises a roughened bond coat disposed on a substrate and a thermal barrier coating disposed on the bond coat. The method comprises disposing a roughened bond coat on the substrate and disposing a thermal barrier coating on the roughened bond coat. The roughened bond coat comprises a screen having interwoven wires defining openings and a metal material disposed on the screen lo form the roughened bond coat. The roughened bond coat possessing an uneven undulated surface adjacent to the thermal barrier coating.
- A further embodiment of the invention provides a thermal barrier coating system. The thermal barrier coating system comprises a roughened bond coat and a thermal barrier coating disposed on a substrate. The roughened bond coat comprises a screen with interwoven wires defining openings and a metal material disposed on the screen to form a roughened bond coat. The roughened bond coat possessing an uneven undulated surface adjacent to the thermal barrier coating.
- These and other aspects, advantages and salient features of the invention will become apparent from the following detailed description, which, when taken in conjunction with the annexed drawings, where like parts are designated by like reference characters throughout the drawings, disclose embodiments of the invention.
- FIG. 1 is a schematic representation of a known thermal barrier coating system;
- FIG. 2 is a schematic representation of a thermal barrier coating system including a roughened bond coat;
- FIG. 3 is a plan illustration of a screen for use in a roughened bond coat;
- FIG. 4 is a plan illustration of a roughened bond coat;
- FIG. 5 is a side, part sectional illustration of a roughened bond coat;
- FIG. 6 is a micro-photograph of a roughened bond coat; and
- FIG. 7 is a flow chart of one method for forming a thermal barrier coating system.
- Roughened bond coats enhance adhesion between a thermal barrier coating (TBC) and a bond coat in a thermal barrier coating system. Roughened bond coats prevent de-bonding and separation between the TBC and bond coat of the thermal barrier coating system. A roughened bond coat increases interfacial mating surface areas of adhered elements, enhances mechanical interlocking between the bond coat and TBC, and provides for accommodation of thermal mismatches between the TBC and bond coat. Accordingly, expansion of elements in a thermal barrier coating system with a roughened bond coat does not lend to separation and de-bonding therebetween. An effect of the roughened bond coat includes an enhanced life of the TBC in the thermal barrier coating system.
- In the following description, material compositions of mixtures are provided in approximate weight percent unless otherwise expressed. Further, individual compositions are provided in weight percent, unless otherwise provided. For example, if a mixture comprises about 70% of Constituent A and about 30% of constituent B, the percents are in weight percents. Nomenclature used for compositions is as follows. If Composition A comprises Ni—23Cr—6Al—0.4Y, yttrium is provided at 0.4 weight percent, aluminum is provided at 6 weight percent, chromium is provided at 23 weight percent, and nickel is provided as the balance weight percent.
- A thermal
barrier coating system 100 including a roughened bond coat, as embodied by the invention, is schematically illustrated in FIG. 2. The thermalbarrier coating system 100 comprises asubstrate 10, a roughenedbond coat 22 and aTBC 14. Aninterfacial surface area 28 is located at adjacent, adjoiningsurfaces bond coat 22 and theTBC 14, respectively. The roughenedbond coat 22 is attached to thesubstrate 10, by at least oneconnection 110. Theconnection 110, comprises a physical attachment, for example a weld, such as at least one of a tack weld, laser weld, and ultrasonic weld. The number of connections varies dependent on factors such as, but not limited to, a screen's wire and mesh opening sizes. - A thermal
barrier coating system 100 including a roughened bond coat, as embodied by the invention, is schematically illustrated in FIG. 2. The thermalbarrier coating system 100 comprises asubstrate 10, a roughenedbond coat 22 and aTBC 14. Aninterfacial surface area 28 is located at adjacent, adjoiningsurfaces bond coat 22 and theTBC 14, respectively. The roughenedbond coat 22 is attached to thesubstrate 10, by at least oneconnection 110. Theconnection 110 comprises a physical attachment, for example a weld, such as at least one of a tack weld, laser weld, and ultrasonic weld. The number of connections varies dependent on factors such as, but not limited to, a screen's wire and mesh opening sizes. - The roughened
bond coat 22 comprises ascreen 24 provided with ametallic material 26 disposed thereon. FIG. 3 illustrates ascreen 24, such as a metal screen, used to form a roughenedbond coat 22. Themetal screen 24 comprises a material that is metallurgically similar to the material of thesubstrate 12. For example, if the substrate is a turbine formed of a nickel-based superalloy composition, thescreen 24 is formed from a nickel-based material. This material is merely exemplary of screen materials, and is not meant to limit the scope of the invention. - The
screen 24 comprises interwovenwires 30 that definemesh openings 34. The size of thewires 30 andopenings 34 varies, dependent on the ultimate desired roughness of thebond coat 22. For example, thewires 30 of thescreen 24 are provided with an average diameter in a range between about 5 μm to about 240 μm. Theopenings 34 of thescreen 24 are substantially rectangular, such as square openings. The size of theopenings 34 are provided in a range from about 190 μm2 to about 420 μm2. For example and in no way limiting of the invention, a “fine”screen 24 provides an opening of about 200 μm2 with about 50 μm average diameter wire; a “medium”screen 24 provides anopening 34 of about 190 μm2 with about 130 μm average diameter wire; and a “coarse”screen 24 provides an opening of about 420 μm2 with about 240 μm average diameter wire. - FIG. 4 is a schematic illustration of a roughened
bond coat 22 with ametallic material 26 disposed onwires 30 ofscreen 24. Themetallic material 26 is disposed on thescreen 24 by a method appropriate for themetallic material 26. These methods include, but are not limited to; spraying, such as, but not limited to, plasma spraying; coating, such as by directly applying (painting); and deposition, such as chemical vapor deposition and physical vapor deposition. FIG. 4 illustrates one possible configuration of themetallic material 26 on thewires 30 and in theopenings 34 of thescreen 22, however this is merely exemplary and not meant to limit the invention. An exact configuration of themetallic material 26 on thescreen 22 is dependent on various factors, including, but not limited to, process variables used in applying themetal material 26, the size of thewires 30 andopenings 34, and material characteristics of themetal material 26, such as density and viscosity. - The
metallic material 26 covers portions of thewires 30 and extends into and at least partially fills theopenings 34, as illustrated in FIG. 4. For example, and in no way limiting of the invention, themetallic material 26 totally covers thewires 30, as atportion 33. Themetallic material 26 also partially covers thewires 30, as atportion 35. Further, themetallic material 26 totally covers thewires 30, while exposing other parts of thewires 30. Themetallic material 26 completely fillsopenings 34 in thescreen 22, as atportion 36. Themetallic material 26 also at least partially fills theopenings 34, as at portion 37. Further, themetallic material 26 completely fills some of theopenings 34, and partially fillsother openings 34, as atportion 38. In other words, themetallic material 26 covers at least part ofwires 30 and fills parts of theopenings 34. - The
metallic material 26 possesses a thermal expansion coefficient that is close to the thermal expansion coefficient of theTBC 14. Close thermal expansions for themetallic material 26 andTBC 14 avoid one of these expanding much more than the other, thus avoiding de-bonding. - The
metallic material 26 is also an oxidation resistant material. Oxidation of the thermal barrier coating system is undesirable since it causes spalling, separation, de-bonding, and possible failure of the thermal barrier coating system, and oxidation is reduced by the addition of themetallic material 26. Themetallic material 26 comprises at least one oxidation resistant material selected from NiCrAlY, where M is at least one of nickel (Ni), iron (Fe), and cobalt (Co), AlSi (hereinafter “AlSi”), and Ni—60Al—1B. The invention describes MCrAlY as NiCrAlY, however this description is merely exemplary and is not meant to limit the invention in any way. - The physical characteristics of the
metallic material 26 facilitates its application on thescreen 24. Themetallic material 26 flows over and around thewires 30 to adhere to thewires 30. Themetallic material 26 also possesses a viscosity that enables themetallic material 26 to fill theopenings 34 in thescreen 24. Thus, themetallic material 26 comprises materials, such as but not limited to slurries and powders. - A slurry as a
metallic material 26 that is applied to thescreen 24 comprises a mixture of at least one oxidation resistant material, such as a metal powder, plus a binder. The mixture comprises about 70% by weight metal powder, and about 30% by weight of a binder. The binder is selected from appropriate binders for slurries, that are used to hold powders and similar materials together. - One metal powder portion of a slurry mixture, as embodied by the invention, comprises about 90% of NiCrAlY (Ni-23Cr—6Al—0.4Y) by weight and about 10% of AlSi by weight. NiCrAlY is an oxidation-resistant composition possessing a high melting point (approximately 1350° C.). AlSi is an oxidation-resistant composition, and possesses a low melting point (approximately 577° C.). Therefore, if the bond coat is subjected to a heat treatment, AlSi melts prior to NiCrAlY melting, for example during subsequent heat treatments of the thermal
barrier coating system 100. Melted AlSi fuses and re-acts together elements of the roughened bond coat. If the heat treatment is conducted at temperatures higher than the melting point of AlSi, but lower that the melting point of NiCrAlY, the AlSi melts before the NiCrAlY. The melted AlSi joins (fuses) the un-melted NiCrAlY and structural elements of the roughened bond together. NiCrAlY in the slurry mixture is merely exemplary of the metal powders within the scope of the invention, and other compositions, such as, but not limited to Ni—20Cr (melting point about 1400° C.) and Ni—60Al—1B (melting point about 850° C.), are within the scope of the invention. The combination of different melting point powders results in a higher density, for example a density of at least about 95% of its theoretical density. - FIG. 5 is a side part-sectional schematic illustration of a roughened
bond coat 22 with thescreen 24 having themetallic material 26 disposed thereto. As illustrated, asurface 46 of themetallic material 26 on the screen defines aninterfacial surface area 28. Thesurface 46 is uneven, undulated, and irregular, rather than smooth as in known bond coat surfaces. Accordingly, thesurface 46 provides a larger surface area compared to known smooth bond coat surfaces. For example, theinterfacial surface area 28 is greater than a known bond coat's surface area by at least about 25%. - The roughness of the
bond coat 24 is sufficient to increase interfacial surface areas at the interface, thus reducing de-bonding and increasing accommodation of thermal expansion mismatches. Thebond coat 24, as embodied by the invention, possesses a roughness in a range of about 100 microinches (about 2.5×10−4 cm) Ra (Arithmetic Average Roughness (Ra) as determined from ANSI/ASME Standard B461-1985) to about 2000 microinches (about 5.0×10−3 cm) Ra. Alternatively, thebond coat 24 possesses a roughness in a range of about 100 microinches (about 2.5×10−4 m) Ra to about 400 microinches (about 1.0×10−3 cm) Ra. Further, thebond coat 24 possesses a roughness in a range of about 100 microinches (about 2.5×10−4 cm) Ra to about 300 microinches (about 7.5×10−4 cm) Ra. - FIG. 6 is a micro-photograph of a roughened
bond coat 22, where themetallic material 26 is applied as a slurry. In FIG. 6, some particles, such as NiCrAlY, that have a melting point higher that another component of the slurry, such as AlSi, of the metal powder portion of the slurry mixture remain un-melted after heat treatments (as discussed above). These un-melted powder particles sit on top of the screen and increase the localized roughness of thebond coat 22, which, of course, is desirable. - Melting of the AlSi enhances adherence the metal powder portion lo the
screen 24. A larger volume fraction of a low-melting point powder, such as AlSi, in the slurry mixture increases adhesion of the slurry to thescreen 24. Further, a larger volume fraction of a low-melt powder, such as AlSi, decreases slurry porosity, as more material is melted and less gaps between powder particles remain. This reduced porosity enhances operation of the resultant thermalbarrier coating system 100, as there are fewer gaps between powder particles for oxidation to initiate. Also, metallic material comprising AlSi may be applied to reduce porosity of the thermal barrier coating system at the screen, by applying AlSi to thescreen 24 prior to applying themetallic material 26. Thus, the AlSi on thescreen 24 will melt and reduce gaps at thescreen 24, further reducing porosity. - The
metal material 26, which is disposed on thescreen 24, alternatively comprises a powder material. The powder material is disposed on thescreen 24 by an appropriate powder spraying process, such as, but not limited to, plasma spraying, for example air-plasma spraying. Therefore, a roughenedbond coat 22, as embodied by the invention, comprises ascreen 24 with a powderedmetallic material 26 applied thereto, for example by spraying. This process forms a metal material spray-formed overlayer, which comprises the powderedmetallic material 26 on thescreen 24. - The spray-formed overlayer is provided in a range from about 5×10−3 cm to about 2.5×10−2 cm. One exemplary overlay has an average thickness of about 1.27×10−2 cm (0.005 inches). The powder for the
metal material 26, in this embodiment of the invention, comprises at least one powder selected from: Al—11.6Si; NiCrAlY (Ni—23Cr—6Al—0.4Y); and a mixture of about 25% AlSi by weight and about 75% Ni—20Cr by weight. NiCrAlY is a known oxidation-resistant material. Thus, the mixture of AlSi and Ni—20Cr provides the metal material with desirable oxidation-resistant characteristics, especially after heat-treatment. - FIG. 7 is a flow chart illustrating an exemplary process for preparing a roughened
bond coat 22 and thermalbarrier coating system 100, as embodied by the invention. In steps S1 and S1.1, ascreen 24 andsubstrate 10, respectively, are provided. Thescreen 24 is attached to thesubstrate 10 in step S2. Thescreen 24 is attached to thesubstrate 10 at selected areas 110 (FIG. 2) by an appropriate method, for example welding, such as tack welding, ultrasonic welding, and laser welding. -
Metallic material 26 is applied to thescreen 24 in step S3. If themetallic material 26 is a slurry, it is applied to thescreen 24 by a slurry liquid application process. If themetallic material 26 is provided as a powder, themetallic material 26 is sprayed onto thescreen 24. Each of these processes results in a roughenedbond coat 22 on asubstrate 10. - Once the roughened
bond coat 22 is provided, aTBC 14 is applied to the roughenedbond coat 22 in step S4 to form a thermalbarrier coating system 100. The TBC is disposed on the roughenedbond coat 22 by an appropriate method, such as, but not limited to spraying, deposition, and coating. - The roughened
bond coat 22 andsubstrate 10, prior to the TBC being disposed thereon, undergoes optional heat treatment, at step S3.1. Further, the entire thermalbarrier coating system 100 undergoes optional heat treatment at step S7. The heat treatment of the thermalbarrier coating system 100 comprises heat-treating at about 1200° C./1 hr in a vacuum and would generally be performed only if optional heat treatment step S3.1 is performed at a heat treatment temperature sufficient to melt the AlSi but not NiCrAlY or Ni—20Cr, if provided, wherein upon re-solidification the AlSi fuses the bond coat to the screen and its elements with the roughenedbond coat 22. - As discussed above, some
metallic material 26 can be applied to thescreen 22 to reduce porosity of the roughened bond coat. The application of themetallic material 26 to thescreen 22 occurs at step S1.2, which is prior to the attachment of thescreen 22 to thesubstrate 10. - While various embodiments are described herein, it will be appreciated from the specification that various combinations of elements, variations or improvements therein may be made by those skilled in the art, and are within the scope of the invention.
Claims (81)
1. A method of forming a bond coat, the method comprising:
providing a screen, the screen comprises interwoven wires defining openings;
providing a metallic material; and
disposing the metallic material on the screen to form an uneven, undulated, and irregular surface.
2. A method according to claim 1 , wherein said providing a screen comprises selecting a screen with the openings having a size in a range from about 190 μm2 to about 420 μm2.
3. A method according to claim 1 , wherein said providing a screen comprises selecting a screen with the wires having a diameter in a range from about 50 μm to about 240 μm.
4. A method according to claim 3 , wherein said providing a screen comprises selecting a screen with the openings having a size in a range from about 190 μm2 to about 420 μm2.
5. A method according to claim 1 , wherein said disposing comprises plasma spraying a layer of powder on the screen.
6. A method according to claim 5 , wherein said plasma spraying comprises providing a layer with a thickness in a range from about 5.0×10−3 cm to about 2.5×10−2 cm.
7. A method according to claim 1 , wherein said disposing comprises disposing a slurry on the screen.
8. A method according to claim 1 , wherein said providing a metallic material comprises selecting at least one of a slurry and a powder, the metallic material comprises at least one of:
MCrAlY; where M is at least one of nickel (Ni), iron (Fe), and cobalt (Co); Al—11.6Si; and Ni—20Cr.
9. A method according to claim 8 , wherein the metallic material comprises about 25% Al—11.6Si by weight and about 75% Ni—20Cr by weight.
10. A method according to claim 1 , wherein the metallic material comprises a slurry comprising about 70% by weight of a metal powder and about 30% by weight of a binder, and the metal powder comprises about 90% NiCrAlY by weight and about 10% Al—11.6Si by weight.
11. A method according to claim 1 , wherein the disposing the metallic material forms the uneven, undulated, and irregular surface with roughness in a range from about 2.5×10−4 cm Ra to about 5.0×10−3 cm Ra.
12. A method according to claim 1 , wherein the disposing the metallic material forms the uneven, undulated, and irregular surface) with roughness in a range from about 2.5×10−4 cm Ra to about 10−3 cm Ra.
13. A method according to claim 1 , wherein the disposing the metallic material forms the uneven, undulated, and irregular surface with roughness in a range from about 2.5×10−4 cm Ra to about 7.5×10−4 cm Ra.
14. A method of forming a bond coat, the method comprising:
providing a screen, the screen comprises interwoven wires defining openings;
providing a powder; and
plasma spraying the powder on the screen to form an uneven, undulated, and irregular surface.
15. A method according to claim 14 , wherein the providing a screen comprises selecting a screen with the openings having a size in a range from about 190 μm2 to about 420 μm2.
16. A method according to claim 14 , wherein the providing a screen comprises selecting a screen with the wire having a diameter in a range from about 50 μm to about 240 μm.
17. A method according to claim 16 , wherein the providing a screen comprises selecting a screen with the openings having a diameter in a range from about 190 μm2 to about 420 μm2.
18. A method according to claim 14 , wherein said plasma spraying comprises providing a layer of powder on the screen.
19. A method according to claim 18 , wherein said providing a layer comprises providing a layer with a thickness in a range from about 5.0×10−3 cm to about 12.5×10−2 cm.
20. A method according to claim 14 , wherein said providing a powder comprises selecting a powder that comprises at least one of: NICrAlY, where M is at least one of nickel (Ni), iron (Fe), and cobalt (Co); Al—11.6Si; and Ni—20Cr.
21. A method according to claim 20 , wherein the metallic material comprises about 25% Al—11.6Si by weight and about 75% Ni—20Cr by weight.
22. A method according to claim 14 , wherein the disposing the metallic material forms the uneven, undulated, and irregular surface with roughness in a range from about 2.5×10−4 cm Ra to about 5.0×10−3 cm Ra.
23. A method according to claim 14 , wherein the disposing the metallic material forms the uneven, undulated, and irregular surface with roughness in a range from about 2.5×10−4 cm Ra to about 10−3 cm Ra.
24. A method according to claim 14 , wherein the disposing the metallic material forms the uneven, undulated, and irregular surface, with roughness in a range from about 2.5×10−4 cm Ra to about 7.5×10−4 cm Ra.
25. A method of forming a bond coat, the method comprising:
providing a screen, the screen comprises interwoven wires defining openings;
providing a slurry; and
disposing the slurry on the screen to form an uneven, undulated, and irregular surface.
26. A method according to claim 25 , wherein said providing a screen comprises selecting a screen with the openings having a size in a range from about 190 μm2 to about 420 μm2.
27. A method according to claim 25 , wherein said providing a screen comprises selecting a screen with the wires having a diameter in a range from about 50 μm to about 240 μm.
28. A method according to claim 27 , wherein said providing a screen comprises selecting a screen with the openings having a size in a range from about 190 μm2 to about 420 μm2.
29. A method according to claim 25 , wherein said providing a slurry comprises selecting a slurry that comprises about 70% by weight of a metal powder and about 30% by weight of a binder.
30. A method according to claim 29 , wherein the metal powder comprises about 90% MCrAlY, where M is at least one of nickel (Ni), iron (Fe), and cobalt (Co), by weight and about 10% Al—11.6Si by weight.
31. A roughened bond coat comprising:
a screen comprising interwoven wires defining openings; and
a metallic material disposed on the screen, wherein the metallic material on the screen forms the uneven, undulated, and irregular surface.
32. A bond coat according to claim 31 , wherein the openings comprise a size in a range from about 190 μm2 to about 420 μm2.
33. A bond coat according to claim 31 , wherein the wires comprise a diameter in a range from about 50 μm to about 240 μm.
34. A bond coat according to claim 33 , wherein the openings comprise a size in a range from about 190 μm2 to about 420 μm2.
35. A bond coat according to claim 31 , wherein the metallic material comprises a powder disposed on the screen.
36. A bond coat according to claim 35 , wherein the powder comprises a layer of powder plasma sprayed on the screen.
37. A bond coat according to claim 36 , wherein the layer with a thickness in a range from about 5.0×10−3 cm to about 12.5×10−2 cm.
38. A bond coat according to claim 31 , wherein the metallic material comprises a slurry disposed on the screen.
39. A bond coat according to claim 31 , wherein the metallic material comprises at least one of a slurry and a powder, the metallic material comprises at least one of:
MCrAlY, where M is at least one of nickel (Ni), iron (Fe), and cobalt (Co); Al—11.6Si; and Ni—20Cr.
40. A bond coat according to claim 39 , wherein the metallic material comprises about 25% Al—11.6Si by weight and about 75% Ni—20Cr by weight.
41. A bond coat according to claim 31 , wherein the metallic material comprises a slurry comprising about 70% by weight of a metal powder and about 30% by weight of a binder, and the metal powder comprises about 90% MCrAlY, where M is at least one of nickel (Ni), iron (Fe), and cobalt (Co), by weight and about 10% Al—11.6Si by weight.
42. The bond coat according to claim 31 , wherein the bond coat is applied to a substrate comprising a turbine component.
43. A bond coat according to claim 31 , wherein the disposing the metallic material forms the uneven, undulated, and irregular surface with roughness in a range from about 2.5×10−4 cm Ra to about 5.0×10−3 cm Ra.
44. A bond coat according to claim 31 , wherein the disposing the metallic material forms the uneven, undulated, and irregular surface with roughness in a range from about 2.5×10−4 cm Ra to about 10−3 cm Ra.
45. A bond coat according to claim 31 , wherein the disposing the metallic material forms the uneven, undulated, and irregular surface with roughness in a range from about 2.5×10−4 cm Ra to about 7.5×10−4 cm Ra.
46. A method of providing a thermal barrier coating system, the thermal barrier coating system comprises a roughened bond coat disposed on a substrate, and a thermal barrier coating disposed on the bond coat the method comprising:
disposing a roughened bond coat on the substrate;
disposing a thermal barrier coating on the roughened bond coat;
wherein said disposing a roughened bond coat comprises:
providing a screen, the screen comprises interwoven wires defining openings;
providing a metallic material; and
disposing the metallic material on the screen to form a roughened bond coat,
wherein the roughened bond coat provides an uneven undulated surface adjacent to the thermal barrier coating.
47. A method according to claim 46 , wherein said providing a screen comprises selecting a screen with the openings having a size in a range from about 190 μm2 to about 420 μm2.
48. A method according to claim 46 , wherein said providing a screen comprises selecting a screen with the wires having a diameter in a range from about 50 μm to about 240 μm.
49. A method according to claim 48 , wherein said providing a screen comprises selecting a screen with the openings having a size in a range from about 190 μm2 to about 420 μm2.
50. A method according to claim 46 , wherein said disposing comprises plasma spraying a layer of powder on the screen.
51. A method according to claim 50 , wherein said plasma spraying comprises providing a layer with a thickness in a range from about 5.0×10−3 cm to about 12.5×10−2 cm.
52. A method according to claim 46 , wherein said disposing comprises disposing a slurry on the screen.
53. A method according to claim 46 , wherein said providing a metallic material comprises selecting at least one of a slurry and a powder, the metallic material comprises at least one of:
MCrAlY, where M is at least one of nickel (Ni), iron (Fe), and cobalt (Co); Al—11.6Si; and Ni—20Cr.
54. A method according to claim 53 , wherein the metallic material comprises about 25% Al—11.6Si by weight and about 75% Ni—20Cr by weight.
55. A method according to claim 46 , wherein the metallic material comprises a slurry comprising about 70% by weight of a metal powder and about 30% by weight of a binder and the metal powder comprises about 90% MCrAlY, where M is at least one of nickel (Ni), iron (Fe), and cobalt (Co), by weight and about 10% Al—11.6Si by weight.
56. A method according to claim 46 , the method further comprising heat treating, wherein a portion of the metallic material melts and, upon re-solidification, joins the roughened bond coat to the substrate.
57. A method according to claim 46 , the method further comprises connecting the screen to the substrate prior to disposing the metallic material to the screen.
58. A method according to claim 57 , wherein said connecting comprises welding the screen to the substrate.
59. A method according to claim 46 , the method further comprises disposing metallic material on the screen prior to disposing the screen on the substrate.
60. A method according to claim 46 , wherein the substrate comprises a turbine component.
61. A turbine component according to claim 46 , wherein the disposing the metallic material forms the uneven, undulated, and irregular surface with roughness in a range from about 2.5×10−4 cm Ra to about 5.0×10−3 cm Ra.
62. A turbine component according to claim 46 , wherein the disposing the metallic material forms the uneven, undulated, and irregular surface with roughness in a range from about 2.5×10−4 cm Ra to about 10−3 cm Ra.
63. A turbine component according to claim 46 , wherein the disposing the metallic material forms the uneven, undulated, and irregular surface with roughness in a range from about 2.5×10−4 cm Ra to about 7.5×10−4 cm Ra.
64. A thermal barrier coating system comprising:
a roughened bond coat disposed on a substrate; and
a thermal barrier coating disposed on the roughened bond coat, wherein the roughened bond coat comprises:
a screen comprising interwoven wires defining openings;
a metallic material disposed on the screen to form a roughened bond coat possessing an uneven, undulated, and irregular surface adjacent to the thermal barrier coating.
65. A system according to claim 64 , wherein the openings have a size in a range from about 190 μm2 to about 420 μm2.
66. A system according to claim 64 , wherein the wire have a diameter in a range from about 50 μm to about 240 μm.
67. A system according to claim 66 , wherein the openings have a size in a range from about 190 μm2 to about 420 μm2.
68. A system according to claim 64 , wherein the metallic material comprises a layer of metallic material that is plasma sprayed on the screen.
69. A system according to claim 68 , wherein said layer comprises a layer with a thickness in a range from about 5.0×10−3 cm to about 12.5×10−2 cm.
70. A system according to claim 64 , wherein said metallic material comprises a slurry disposed on the screen.
71. A system according to claim 64 , wherein said metallic material comprises at least one of a slurry and a powder, the metallic material comprises at least one of:
MCrAlY, where M is at least one of nickel (Ni), iron (Fe), and cobalt (Co); Al—11.6Si; and Ni—20Cr.
72. A system according to claim 71 , wherein the metallic material comprises about 25% Al—11.6Si by weight and about 75% Ni—20Cr by weight.
73. A system according to claim 64 , wherein the metallic material comprises a slurry comprising about 70% by weight of a metal powder and about 30% by weight of a binder and the metal powder comprises about 90% MCrAlY, where M is at least one of nickel (Ni), iron (Fe), and cobalt (Co), by weight and about 10% Al—11.6Si by weight.
74. A system according to claim 64 , wherein the system undergoes heat treatment and a portion of the metallic material melts and re-solidifies joining the roughened bond coat to the substrate.
75. A system according to claim 64 , the system further comprises connections that connect the screen to the substrate.
76. A system according to claim 75 , wherein said connections comprise welds.
77. A system according to claim 64 , the system further comprises the metallic material disposed on the screen prior to the screen being disposed on the substrate.
78. A system according to claim 64 , wherein the substrate comprises a turbine component.
79. A system according to claim 64 , wherein the disposing the metallic material forms the uneven, undulated, and irregular surfacer with roughness in a range from about 2.5×10−4 cm Ra to about 5.0×10−3 cm Ra.
80. A system according to claim 64 , wherein the disposing the metallic material forms the uneven, undulated, and irregular surface with roughness in a range from about 2.5×10−4 cm Ra to about 10−3 cm Ra.
81. A system according to claim 64 , wherein the disposing the metallic material forms the uneven, undulated, and irregular surface with roughness in a range from about 2.5×10−4 cm Ra to about 7.5×10−4 cm Ra.