US20020000178A1 - Systems and methods for producing and using fine particle materials - Google Patents
Systems and methods for producing and using fine particle materials Download PDFInfo
- Publication number
- US20020000178A1 US20020000178A1 US09/858,432 US85843201A US2002000178A1 US 20020000178 A1 US20020000178 A1 US 20020000178A1 US 85843201 A US85843201 A US 85843201A US 2002000178 A1 US2002000178 A1 US 2002000178A1
- Authority
- US
- United States
- Prior art keywords
- glass
- processing chamber
- solid material
- shaft
- impellers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Systems and methods of making and using fine particle materials in pigment blends and for using the aforementioned pigment blends in paint, coating, or coloring compositions are provided. This invention further provides systems and methods of enhancing the visual appearance of a variety of substrates by introducing a paint, coating, or coloring composition to the substrate. The fine particle materials of the present invention have a substantially random geometric shape, a particle size less than about 100 microns, and help provide both functional and visual enhancing properties to compositions and substrates containing these fine particle materials.
Description
- This application claims the benefit of U.S. provisional patent application Ser. No. 60/142,087, filed Jul. 2, 1999.
- The present invention relates to systems and methods for producing and using fine particle materials. More particularly, the present invention relates to systems and methods for taking raw materials, pulverizing those raw materials, and incorporating the pulverized materials into products to enhance the visual appearance of the products.
- In numerous commercial products, pigment blends are used to create color and visual effects that aesthetically appeal to consumers. Because different consumers have different preferences to various visual effects, a designer's ability to create and control these effects is often important to the marketability of a product. Often, additives such as coated mica flakes, metal flakes, and glass flakes have been used in pigment blends to enhance the visual appeal of items such as automobiles, boats, planes, appliances, signs, painted surfaces, fabrics, and other consumer goods.
- Depending on the nature of the substrate to which the pigment blend is introduced, there are certain visual effects that often have strong aesthetic appeal to consumers. Coated mica flakes, for example, is one of the more common additives used to improve luster and depth of color of paint compositions on cars. Metal flakes, such as aluminum flakes, are another common additive used to improve the sparkle of paint and coatings.
- While the aforementioned additives offer some of the visual effects that typically appeal to consumers, a need remains for an economical pigment blend that enables a designer to create and control a broader range of visual effects. Moreover, a need always exists for improved ways to enhance the functional properties of paint and coating compositions, such as increased durability, increased travel, improved pattern control, UV screening, and reduced settling problems from particulates in unapplied paint or coatings.
- These and other needs are satisfied in accordance with the present invention by providing systems and methods for making and using fine particle materials in pigment blends and for using the aforementioned pigment blends in paint, coating, or coloring compositions. The invention further provides systems and methods for enhancing the visual appearance of a variety of substrates by introducing such a paint, coating, or coloring composition to the substrate. The fine particle materials of the present invention have a substantially random geometric shape, a particle size less than about100 microns, and help provide both functional and visual enhancing properties to compositions and substrates containing these fine particle materials.
- The fine particle materials of the present invention may be made generally from any pulverizable material. Initially, solid raw pulverizable material may be sorted according to type and subsequently cleaned of any impurities. Depending on the original size of the solid raw material, it may be sent, either before or after cleaning, to a crusher to reduce the size of the raw material into pieces suitable for efficient pulverizing. Once the raw material has been separated, crushed, and cleaned, it is conveyed to a first feed hopper that then feeds the raw material to a first pulverizer. The pulverized particles made by pulverizing the raw material may then be sent to a screen classifier to remove any remaining impurities, such as particle metal waste resulting from wear and tear of the innards of the pulverizer, if necessary. Next, the pulverized particle material is classified according to size. Pulverized particle materials that do not meet the desired size limitation may be sent to be either pulverized again or milled to further reduce the particle material to a size suitable for the desired application. Alternatively, the pulverized material produced by the first pulverizer may be sent immediately to a ball mill to help reduce the particle material to a desired particle size.
- The fine particle materials of the present invention may be used in pigment blends to enhance the visual and functional properties of a substrate. One or more coloring agents may be optionally added to the pigment to assist with enhancing the visual appearance of the substrate to be treated. The visual appearance of the substrate may be enhanced by introducing a coating, coloring, or paint composition containing the pigment blend with the fine particle material to the substrate by either applying the composition to the surface of the substrate or by incorporating the composition into the substrate itself.
- Further features of the invention, its nature and various advantages will be more apparent from the following detailed description of the preferred embodiments, taken in conjunction with the accompanying drawing, in which like reference characters refer to like parts throughout, and in which:
- FIGS.1A-1C illustrate one embodiment of a system for producing fine particle materials in accordance with the present invention.
- FIG. 2 illustrates an alternative embodiment of a system for producing fine particle materials that uses a ball mill in conjunction with a pulverizer in accordance with the present invention.
- FIG. 3 illustrates a partially schematic and partially cut-away view of an embodiment of a pulverizer suitable for use in accordance with the present invention.
- FIG. 4 illustrates an enlarged, partially schematic and partially cut-away view of one bearing assembly for the pulverizer of FIG. 3.
- FIG. 5 illustrates an enlarged, partially schematic and partially cut-away view of another bearing assembly for the pulverizer of FIG. 3.
- FIG. 6 illustrates an enlarged, partially schematic and partially cut-away view of yet another bearing assembly for the pulverizer of FIG. 3.
- FIG. 7 illustrates an enlarged, partially schematic and partially cut-away view of still another bearing assembly for the pulverizer of FIG. 3.
- FIG. 8 illustrates a plan view of a preferred embodiment of a top ring for the pulverizer of FIG. 3.
- FIG. 9 illustrates a cross-sectional view of the ring of FIG. 8, taken along the line7--7 thereof.
- FIG. 10 illustrates a cross-sectional view of the ring of FIG. 8, taken along the line8--8 thereof.
- FIG. 11 illustrates a partially schematic plan view of a preferred embodiment of an impact ring of the pulverizer of FIG. 3.
- FIG. 12 illustrates a cross section of the ring of FIG. 11, taken along the
line 10--10 thereof. - FIG. 13 illustrates an enlarged fragment of the ring of FIG. 11 showing a preferred ridged and grooved inner surface.
- FIGS.14A-B illustrate alternate shafts that are split into two or more portions and connected by torque transferring couplings for the pulverizer of FIG. 3.
- FIG. 15 illustrates a schematic for additionally or alternatively cooling the shaft of the pulverizer of FIG. 3 to prevent expansion of the shaft.
- FIG. 16 illustrates yet another shaft for the pulverizer of FIG. 3 that includes a threaded section enabling a user to adjust the gaps between the vanes of impellers and baffles plates.
- FIG. 17 illustrates an alternative embodiment of the pulverizer of FIG. 3 incorporating additional vanes along the bottom of one or more of the impellers.
- FIGS.18A-D show scanning-electron-microscope micrographs of mirrorized glass chips produced in accordance with the present invention.
- FIG. 19 shows a particle size distribution of fine particle glass produced in accordance with the present invention.
- Turning to FIGS.1A-1C, one embodiment of a
system 100 for producing fine particle materials in accordance with the present invention is shown. As illustrated,system 100 is directed toward the production of fine particle glass. However, it should be noted that with minor modification,system 100 could be used to produce other types of fine particle materials, including rubber, oyster shell, rock minerals, coal, aluminum, and other similar crushable materials. - Initially raw material glass is stored in
storage bins 102. As illustrated in FIG. 1A,system 100 may contain sixstorage bins 102 or any suitable number ofstorage bins 102. Withinstorage bins 102, the raw material glass may be sorted by type. For example, the raw material glass may be separated by type and color so that clear glass, green glass, amber glass, aluminum-coated mirror, gold-coated mirror, and mixed glass are each stored in a different one ofstorage bins 102. Most commonly the mirrors will be silver-copper coated with a paint backing. In addition to using mirrors with different types of backing, mirrors of varying thickness may also be employed. For example, other raw material products, such as one-quarter inch or one-half inch mirror may also be used. The one-quarter inch and one-half inch mirrors may be mixed together or treated separately to yield fine glass particles. Depending on the application and visual effect sought, one or more classes of mirrors may be combined to yield a combination of fine particle materials that provide sought after visual enhancing properties. - Using
conveyer 104, glass may be removed from any one or more ofstorage bins 102 and transported tomagnetic separator 106.Magnetic separator 106 may be used to remove any metal waste that may be mixed in with the raw glass.Conveyer 104 then carries the glass tocrusher 108.Crusher 108 is used to crush the raw material glass down into a size suitable for further processing. The crushed glass is then conveyed to washer/dryer 110. In washer/dryer 110, the crushed glass is then removed of paper, glue, and any other impurities that may be present in the crushed glass. In an alternative embodiment, the glass may be first cleaned by washer/dryer 110 before it is crushed bycrusher 108. Alternatively, as part of the cleaning process, the combustible impurities that may accompany the glass (e.g., labels from recycled glass) may be burned off of the raw glass material either before or after the glass is crushed bycrusher 108. - Once the glass has been crushed, washed and dried, the glass is then conveyed by
conveyer 112 to afirst feed hopper 114.First feed hopper 114 then feeds the crushed and cleaned glass to afirst pulverizer 116 by way of a screw conveyer. First pulverizer 116 performs an initial pass on the crushed glass and provides first-stage pulverized glass throughpipe 118 todust collector 120.Dust collector 120 releases air pressure from the output offirst pulverizer 116. Attached todust collector 120 is amaterial transport system 122 that restabilizes the air pressure in the output ofdust collector 120 and then drives the first-stage pulverized glass throughpipe 124 toscreen classifier 202 as shown in FIG. 1B. - Once the
screen classifier 202 receives the pulverized glass, it removes any remaining impurities, including any particle metal waste resulting from wear and tear of the innards ofpulverizer screen classifier 202 then flows throughpipe 204 tofirst air classifier 206.First air classifier 206 then classifies the pulverized glass into three groups. The first group is the pulverized glass less than 5 microns in size. This glass is output throughpipe 208. The second group is the pulverized glass between 5 and 15 microns. This glass is output throughpipe 210. The third group is the pulverized glass larger than 15 microns. This glass is output throughpipe 212 and passed tosecond air classifier 213.Second air classifier 213 then also classifies the glass into three groups. The first group is the glass less than 5 microns in size that managed to pass through tosecond classifier 213. This glass is output throughpipe 208. The second group is the glass that is between 15 and 30 microns in size. This glass is output throughpipe 214. Finally the glass that is larger than 30 microns in size is output as the third group throughpipe 216 back tosecond feed hopper 126 as shown in FIG. 1A. - Once the first-stage pulverized glass that is greater than 30 microns in size has been sent to
second feed hopper 126, the glass is then repulverized bysecond pulverizer 128 which provides second-stage pulverized glass throughpipe 130 todust collector 132.Dust collector 132 releases air pressure from the output ofsecond pulverizer 128. Attached todust collector 132 is amaterial transport system 134 that restabilizes the air pressure in the output ofdust collector 132 and then drives the second-stage pulverized glass back throughpipe 124 toscreen classifier 202 as shown in FIG. 1B. This second-stage pulverized glass then repeats the processing atair classifiers - Finally, as shown in FIG. 1C, the less than 5 micron pulverized glass in
pipe 208 is then passed todust collector 302 which releases air pressure inpipe 208. Attached todust collector 302 is amaterial transport system 304 that restabilizes the air pressure and then passes the glass to group ofsilos 306 viapipe 305. Similarly, the 5 to 15 micron glass inpipe 210 is passed to group ofsilos 308 and the 15 to 30 micron glass inpipe 214 is passed to group ofsilos 310. Each of the silos ingroups storage bins 102. - In an alternative embodiment, as shown in FIG. 2, solid raw glass material is sent to feed
hopper 312 and pulverized bypulverizer 314. The first-stage pulverized particle material made bypulverizer 314 may be further reduced in size by aball mill 316 before it is classified according to particle size byair classifier 320. Particles that need to be further reduced in size may be sent back topulverizer 314 byreturn pipe 318. Particles that have the desired particle size are output todust collector 322. - In a second alternative embodiment, a ball mill may be substituted in place of
second pulverizer 128 to help further reduce the particle size of the pulverized material. Depending on the particle size of the pulverized material, the ball mill may be a more efficient method of reducing the pulverized material to a particle size less than 30 microns. In particular, pulverized material between about 50 and 100 microns in size is well suited for use with a ball mill to obtain fine particle materials having a particle size less than about 30 microns. In contrast, pulverized materials that are greater than 100 microns may be more efficiently reduced in size by a pulverizer. - Alternative classification sizes may be used, if necessary, to suit the particular application for which the pulverized material will be used.
-
System 100 may additionally include a soft-start regulator for producing controlled delivery of power to the pulverizers and a computer control system for controlling and synchronizing the operation of the other components ofsystem 100. -
Storage bins 102,conveyer 104,crusher 108, washer/dryer 110,conveyer 112,feed hoppers dust collectors material transport systems screen classifier 202,air classifiers silos system 100 may be any suitable components for use in the production of the particular fine particle material desired. Also, one or more of these components may be omitted fromsystem 100 and additional components may be added tosystem 100, without departing from the spirit and scope of the invention. - For example, a glass tempering system could be incorporated into the flow of glass between
storage bins 102 and groups ofsilos system 100. By tempering the glass, added benefits can be realized in the product in which the fine particle glass is used. Alternatively, a tempering process could be implemented in one of the existing components ofsystem 100 such as washer/dryer 110 orpulverizers - An example of a pulverizer suitable for use as
pulverizers system 100 is described in Greco U.S. Pat. No. 5,820,044 (hereinafter “the '044 patent”) issued Oct. 13, 1998, which is hereby incorporated by reference herein in its entirety. As explained in the '044 patent, and shown in FIG. 3, solid material to be pulverized enters an inlet 11 to aprocessing chamber 12 withincontainer 13.Chamber 12 is divided into four compartments bybaffle plates 14, and each compartment contains arotor 15.Rotors 15 are fixed toshaft 50 for rapid rotation within processingchamber 12. - Each
rotor 15 hasperipheral vanes 16 that impel solid material radially outward against inside surfaces ofrings 20 that are arranged around eachimpeller 15.Rings 20 preferably have multi-sided internal surfaces surrounding and confronting eachrespective impeller 15. Solid material flung radially outward byvanes 16 onrotors 15 impacts against the internal surfaces ofrings 20 for breaking the solid material down into finer particles. - As the particles become smaller, they move downward through successive stages within processing
chamber 12. The particles pass through spaces that are available betweenvanes 16 ofimpellers 15 and the inside surfaces ofrings 20. The material then flows through central openings ofsuccessive baffle plates 14 to enter lower stages where it encounterssuccessive impellers 15. - The pulverized material outlet from the lowermost stage below the
lowermost impeller 15 proceeds downward through anoutput chute 18. The rotation ofvanes 16 onimpellers 15 pumps air throughprocessing chamber 12 along with solid material, and this helps force pulverized particles throughoutput chute 18, along with an air stream. - Considerable power is input to
shaft 50 viapulley 51, for violently hurling solid material outward against rings 20. In a working prototype, for example, a 300 horsepowermotor drives shaft 50 by a toothed belt (not shown) mating with teeth onpulley 51. The power expended in processingchamber 12 produces considerable heat. Theshaft 50 lengthens about 3 mm from the heat generated during operation. The exact lengthening ofshaft 50 will depend on materials used in construction, materials being processed, power input, and other variables; but however much shaft lengthening actually occurs must be accounted for. - As shown in FIGS.4-7, the shaft lengthening may be accommodated for by a floating bearing system. Turning to FIG. 4, beginning at the bottom,
shaft 50 is supported bybottom bearing 30, as best shown in FIG. 4. A pair ofball bearings shaft 50 between bottom collars 33 and atop collar 34.Ball bearings housing 35 so that outer bearing races fit within the inside ofhousing 35 and inner bearing races fit on and rotate withshaft 50. Aspacer 36 extends between an outer race of bearing 31 and acover plate 37 that is secured tohousing 35.Cover plate 37 contains aseal 38 bearing againstshaft 50 to keep dirt out of the inside ofhousing 35. Bore holes 39 inhousing 35 form passageways to admit lubricating grease and provide pressure relief overflow. - A
fan 40 is secured toshaft 50 above bearinghousing 35 to direct cooling air flow overhousing 35 andcover plate 37, for removing heat fromball bearings fan 40 ispulley 51, which is preferably keyed toshaft 50 for transmitting driving torque from a motor-driven belt (not shown).Shaft 50 has support bearings both above and belowpulley 51. - Above
pulley 51 and belowdischarge chute 18 is abearing 60 that is best shown in FIG. 5. A fixedsupport plate 59 holds abearing mount housing 61 in a fixedposition surrounding shaft 50. Withinhousing 61 is aball bearing 62 having aninner race 63 fitted on and movable withshaft 50 and anouter race 69 that has a sliding fit allowing vertical movement withinmount 61. Aseal 64 is arranged betweenhousing 61 andshaft 50, and anotherseal 66 is arranged betweencover plate 65 andshaft 50.Seals mount 61. -
Shaft 50 moves a small amount vertically from thermal expansion and contraction; andinner bearing race 63, while rotating withshaft 50, also moves axially withshaft 50 during thermal elongation.Outer bearing race 69 has a sliding fit withinhousing 61 that allows vertical movement ofouter race 69, even at elevated temperatures. An array of compression springs 68 arranged withinmount 61 presses downward onouter race 69 to resist upward movement and prevent rotation ofouter race 69. Six compression springs equally spaced apart in a ring aroundshaft 50 are adequate for this purpose, and other spring arrangements can also be used. - When
shaft 50 elongates from thermal expansion andball bearing 62 rises withshaft 50,outer race 69 compresses springs 68 and rises along withinner race 63 to keepball bearing 62 in working alignment. Whenshaft 50 later cools and contracts, loweringball bearing 62, springs 68 extend somewhat and pushouter race 69 downward in alignment withinner race 63. A reasonably light pressure fromsprings 68 is adequate to preventouter race 69 from rotating and keepouter race 69 in vertical alignment withinner race 63. - A
fan 55 fixed toshaft 50 below bearing 60 directs cooling air over bearing 60 to remove heat fromball bearing 62.Fan 55 works in an opposite direction fromfan 40. - The
plate 59 that supports bearing 60 also supports apipe 58 that extends upward aroundshaft 50 intodischarge passageway 18. At the top ofpipe 58 is a bearingassembly 70 holding anotherball bearing 75 for supportingshaft 50, as shown in FIG. 6. Alower shaft seal 56 is arranged between amount housing 71 andshaft 50, and anupper shaft seal 54 is arranged between amount cover plate 73 andshaft 50. An array of compression springs 78 retained incover plate 73 presses down against anouter race 74 ofball bearing 75. As previously described for bearing 60, springs 78 allowouter bearing race 74 to rise withinner bearing race 76 whenshaft 50 elongates thermally. This is possible becauseouter race 74 has a sliding fit withinmount housing 71 against the resistance ofsprings 78. - The arrangement of bearing75 and bearing mount 71 within
discharge passageway 18 subjects bearing 75 to the risk of pulverized material inchute 18 enteringhousing 71. To reduce this risk,plate 79 is fixed onshaft 50 abovecover plate 73 formount 71.Plate 79 spins withshaft 50 and thereby throws pulverized material radially outward to divert such material away from bearinghousing 71. This helps keepball bearing 75 clean. -
Plate 79, being fixed toshaft 50, rises withshaft 50 when thermal elongation occurs. Rising ofplate 79 opens a gap between the underside ofplate 79 and the top ofhousing cover 73. To inhibit entry of pulverized material into such a gap,plate 79 has a ring 77 extending downward into a correspondinggroove 67 formed incover plate 73. Ring 77 andgroove 67 are concentric withshaft 50 so that ring 77 spins withingroove 67 and provides a material barrier across a gap betweencover plate 73 and the underside ofplate 79. These measures, in conjunction withshaft seals 71 and 72, assure that bearing 75 remains clean. Many different configurations of rings and grooves can be used for such a purpose. - An
upper bearing assembly 80 is arranged on asupport plate 57 above processingchamber 12 at an upper region ofshaft 50, as best shown in FIG. 7.Mount housing 86 ofassembly 80 contains a pair ofball bearings housing 86. An array of compression springs 88 presses downward on the outer race of bearing 82 so that bothbearings shaft 50 against the pressure of springs 88. Shaft seals 83 and 84 are arranged respectively inmount housing 86 and inhousing cover plate 85. Afan 87 arranged abovecover plate 85 directs cooling air overhousing 86 for coolingbearings - The
bearing assemblies lower bearing 30, all have housing and spring arrangements that allow outer bearing races to rise with thermal elongation ofshaft 50. This ensures that all bearings run in alignment and give proper support toshaft 50 under operating conditions. Without such provisions for axial movement of bearings withshaft 50, bearings are destroyed as heat is generated from the work done inprocessing chamber 12. Many different spring arrangements and configurations of bearings and mount housings are possible, providing the bearings are given freedom of vertical movement. - Within processing
chamber 12, the throughflow of material being pulverized has been improved and the aggressiveness of the pulverizing action has been enhanced by several improvements. At an upper region of processingchamber 12 is arranged aring 52 that has a multi-sidedinside surface 53 that is beveled to face downward towarduppermost impeller 15, as best shown in FIGS. 8-10. Downwardly beveled faces 53 are wider at corners where faces meet, as shown in FIG. 9, and are narrower in central face regions, as shown in FIG. 10.Ring 52 directs material downward into contact withvanes 16 onuppermost impeller 15 so that any material bouncing upward into contact withring 52 is deflected back downward to encounter pulverizing force. -
Rings 20 that surroundimpellers 15 are also improved, as shown in FIGS. 11-13.Rings 20 can have different numbers of inward facing surfaces 21, and these are preferably inclined inward from bottom to top, as shown in FIG. 10. A 10 degree inclination for ring surfaces 21 is preferred, but other angles of inclination may also work. The inward slope ofsurfaces 21 makes their upper regions extend further intoprocessing chamber 12 than their lower regions, which tends to deflect material downward intoimpellers 15 andvanes 16. The inward inclination ofsurfaces 21 of a succession ofrings 20 enhances the throughflow of material being pulverized and also helps direct pulverizable material into contact withvanes 16 ofimpellers 15. - Inward facing surfaces21 of
rings 20 are also preferably provided with ridges and grooves, as shown in FIG. 13. Preferably evenly spacedridges 22 separated bygrooves 23 provide a jagged or zigzag contour forsurfaces 21 for scattering material impacting on surfaces 21. Slopingsides 24 ofridges 23 deflect impacting material in various directions, depending on angle of incidence. Sloping ridge sides 24 can also lead to double impacts of material glancing off of one ridge side and impacting against another. The result is to deflect or rebound material in different directions, adding randomness to the pulverizing process and making pulverization more aggressive. - In preferred embodiments of the present invention, modifications to the pulverizer described in the '044 patent and herein in connection with FIGS.3-13 may be implemented as part of
pulverizers shaft 50 of the pulverizer of the '044 patent and FIGS. 3-13 may be split into two or more portions and connected by atorque transferring coupling coupling 400 is a spline shaft that connects the two halves ofshaft 50 andcoupling 402 is a compressible coupling that connects the two halves ofshaft 50, however, any suitable type ofcoupling 400 could be used. As illustrated in FIG. 15,shaft 50 of the pulverizer of the '044 patent and FIGS. 3-13 could additionally or alternatively be cooled to prevent expansion. The approach shown uses a cooling liquid 508 that is pumped throughshaft 50 to keep it from expanding. Cooling liquid 508 may be stored in areservoir 506, then pumped by apump 502 through arotary coupler 510 intorotating shaft 50 back out anotherrotary coupler 510 into a radiator orheat exchanger 504 and back intoreservoir 506. - Other examples of modifications that could be made to the pulverizer of the '044 patent and FIGS.3-13 are shown in FIGS. 16 and 17. As illustrated in FIG. 16,
shaft 50 of the pulverizer could include a threadedsection 602 and a pair ofnuts gaps 608 betweenvanes 16 ofimpellers 15 and bafflesplates 14.Gaps 608 are adjusted by turningnut 604 to adjust the height ofimpeller 15 resting thereon. Once the height is set,nut 606 is made snug againstnut 604 to lock in the setting. Because the remainingimpellers 15 rest on the bottom impeller (and thus axially slide onshaft 50 while remaining rotationally fixed with respect to shaft 50), adjustingnut 604 causes all of thegaps 608 to be adjusted. By properly tuninggaps 608, the pulverizer can be made to operate most efficiently. The preferred gap spacing is about 0.062 inches for waste glass, although other gap spacings may be used with glass or other types of materials. - Turning to FIG. 17, still another modification to the pulverizer of the '044 patent and FIGS.3-13 is shown. As can be seen, this modification includes incorporating
additional vanes 702 along the bottom of one or more ofimpellers 15. Preferably,vanes 702 are only used on the bottom of thelowest impeller 15 in the pulverizer andvanes 702 are smaller thanvanes 16.Vanes 702 provide a restriction on the flow of the material being passed out of the pulverizer. This restriction then causes the material to become further pulverized. Preferably, fifteenvanes 16 and threevanes 702 are used on thebottom impeller 15, fifteenvanes 16 and novanes 702 are used on themiddle impellers 15, and eighteenvanes 16 and novanes 702 are used on thetop impeller 15. Furthermore, preferably, thespacing vanes plates 14 are tuned identically to about 0.062 inches (e.g., using the mechanism shown in FIG. 16), although any suitable spacing or combination of spacings could alternatively be used. - Also shown in FIG. 17 are a variation of
rings 20 of the pulverizer. Rather than being constructed with an inside radius that decreases from bottom to top (as can best be seen in FIG. 3), rings 708 shown in FIG. 17 decrease in radius symmetrically from the middle height of the rings toward both the bottom and the top of the rings. In this way, the rings can be flipped over during maintenance of the pulverizer in order to compensate for the wear that typically occurs at near the inside-top of the rings without rebuilding or replacing the rings. - In accordance with the present invention, fine particle materials, such as those produced using
system 100 of FIGS. 1A-1C, may be used to provide pigment blends containing randomly geometrically shaped particles suitable for use with one or more coloring agents such as pigments, metal flakes, coated mica, holographic flakes, colored or coated microbeads, colored or coated glass chips and other similar coloring agents. Alternatively, the coloring agents may be present in a colored base coating or substrate over which a transparent paint or coating composition containing the pigment blends of this invention can be applied. Most preferably, the fine particle chips are made of glass. - While the pigment blend may contain coated fine glass particle chips that have an opaque, mirrorized, and/or reflectorized coating, the glass chip mixture preferably includes glass chips that are transparent to allow light transmission. The transparent glass chips may include colorless and/or colored glass chips.
- If the fine glass particle chips are colored, they may be used either alone or in combination with other colored glass chips to provide coloration to the pigment blend. The colored glass chips may have the same color as the coloring agents included in the pigment blend to enrich and deepen the apparent color of the other included coloring agents. Alternatively, the fine colored glass particles may have a different color to create secondary colors when viewed in combination with one or more coloring agents.
- Because the fine colored glass particles may themselves act as a coloring agent, they may be used to replace pigments that are traditionally added to pigment blends. Because the color in colored glass are fused into the glass, colored glass chips may be a good coloring agent because the color will not leach out with time or exposure to various external elements such as high temperature and weather. Different colored glass chips may be mixed together to form secondary colors when the colored glass chips are viewed in combination. Secondary colors created by mixing two different colored glasses may also be subsequently mixed with primary colors available in other types of colored glass and/or other coloring agents to create apparent tertiary colors. Other color combinations necessary to achieve the desired color through the use of colored glass and/or other coloring agents will be evident to those skilled in the art.
- The fine glass particle materials may be formed from virgin or recycled glass. Recycled glass is preferred because of its very low cost and because it helps preserve the environment by conserving natural resources and by reducing the amount of waste that must ultimately be stored in landfills. Recycled glass may be readily obtained from a variety of sources, such as a local recycling center, and may include clear glass (e.g., from jars), green glass (e.g., from certain beer bottles), amber glass (e.g., from certain soda bottles and other beer bottles), and mirrored glass (e.g., from recycled automobiles, home and office construction waste, and architectural glass).
- Because recycled glass often already contains additives such as coloration or coatings that make the material colored, opaque, reflective, mirrorized, etc., the cost to produce useful pigment blends from recycled glass is even more inexpensive than attempting to use virgin glass to which coloration and/or coating must often be added.
- The fine particle chips preferably are under 100 μm in the largest dimension. Because paint and coatings on substrates commonly are less than about 70 μm thick, the largest dimension of the chips must typically be less than 70 μm so that the paint or coating containing the chips appears and feels smooth on the substrate. However, because individual layers of the paint or coating on a substrate may be as thin as 20-30 μm, the chips preferably are smaller than 30 μm in the largest dimension. Particle sizes larger than 30 μm may be tolerated, however, if the particle lies flat in the paint or coating composition such that the particle height extends not more than a few microns above the surface of the paint or coating on the substrate. Plastics, such as injection molded plastics and the like, may have surfaces that are rougher in texture, and consequently may include glass chips with larger particle size for visual and functional enhancing purposes without degrading or detracting from the apparent smoothness of the article. Preferably, the chips should be no larger than 40 μm in those circumstances.
- To ensure the paint or coating containing the fine particle chips appears and feels smooth on a substrate while preserving the enhanced visual effects that the chips provide, at least 95% of the chips most preferably are between 5 to 15 μm in the largest dimension. The chips will typically contain a distribution of particle sizes. The leading edge of the curve most preferably should not exceed 30 μm. The particle size may be determined by a
Malvern MasterSizer 2000, or any other suitable particle size characterizer known to those skilled in the art. FIG. 19 illustrates aparticle size distribution 1900 of particles made in accordance with the present invention and which are suitable for use in the pigment blend of the present invention. FIGS. 18A-18D show scanning-electron-microscope micrographs 1801-1804 of mirrorized glass chips produced in accordance with the present invention. FIGS. 18A-18D illustrate the randomly geometric shapes suitable for use in the present invention. - Although the chips may be formed in using
system 100, it should be noted that the glass chips may also be formed by any other method, provided that method produces random shaped particles having the aforementioned characteristics. - The glass chips may be made from any variety of glass compositions including silica glass, quartz, soda lime glass, electroconductive glass, sol-gel glass, organically modified sol-gel glass etc. The glass is preferably inorganic, inert, and does not react with other components of the pigment blend. Although the glass chips may be non-tempered, they preferably are tempered to provide greater durability. Because tempered glass chips are tougher, they are more durable and are better able to preserve their geometric shape, which is important to obtaining enhanced visual effects from the glass chips.
- The transparent glass chips preferably have an index of refraction between 1.5 to 2.5, more preferably between 1.9 to 2.1, or mixtures thereof. The transparent glass chips preferably transmit light in the ultraviolet (UV) spectrum (between 200 to 400 nm), visible spectrum (between 400 to 800 nm), infrared (IR) spectrum (between 800 nm to 10 μm), or combinations thereof. More preferably, the transparent glass chips transmit visible and IR light while inhibiting UV transmission. By limiting UV transmission, the chips can reduce the damaging effect that UV light may have on paint, a coating, and/or a substrate beneath the glass chips. Most preferably, the transparent glass chips transmits only visible light. For specific applications, the glass chips may also selectively transmit and/or inhibit one or more wavelengths in one or more of the aforementioned spectral regions.
- The reflective fine particle chips may be optically opaque, mirrorized, or reflectorized, such that the reflective chips reflect or emit light from the surface of the chips into and through the transparent glass chips present, or against coloring agents. These reflective chips in combination with one or more coloring agents give added depth and intensity to the visual appearance and color of the composition or substrate containing the pigment blend of this invention. The pigment blends containing the reflectorized chips may contain suitable additives, known to those skilled in the art, to create a variety of colors.
- Alternatively, the reflective chips may be luminescent, electroluminescent, or phosphorescent. Each of those properties may be obtained by coating the chips with conventional luminescent, electroluminescent, or phosphorescent compositions known to those skilled in the art. Where necessary, the coating may also be electroconductive.
- The pigment blends containing the glass chips are suitable for use with multi-layer paint systems, such as those used on automobiles. Automobile paint systems typically comprise a base color coating having a 20 to 24 micron thick film build and a 42 to 48 micron thick clear coat. Until now, pigment blends of the present invention could not be produced on a commercial scale and used without the difficulties of film protrusion or other undesirable appearance factors.
- In another embodiment, pigment blends containing the glass chips may be used in a mono-layer coating (non-clear coat) for exterior and interior paint applications. The pigment blends of this invention add a very satiny appearance to the surface while also creating a scattered reflective and luminescent appearance.
- In another embodiment, particulate solids, such as oyster shells, clam shells, rubber, rock minerals, coal, aluminum, etc., that have randomly geometric shapes and sizes, may also be used for visual enhancement purposes in pigment blends in accordance with the present invention.
- The presence of particulate solids in pigment blends offers the added advantage of reducing the amount of volatile organic compounds that commonly are used in paint and coating compositions. In alternative embodiments, lighter density particles may be used to reduce settling problems that can arise with heavier density particles.
- Paint or coating compositions containing pigment blends of the present invention may be applied by any suitable method known to those skilled in the art, including calendering, spraying, brush painting, or any other standard method of applying paint or coating compositions.
- The pigment blends of the present invention may be used on a variety of substrates, including metal, ceramic, glass, asbestos, human skin, leather, vinyl, plastic, polyester, epoxies, fabrics, wood, rubber, etc., for visual and functional enhancement. For example, a clear coating for wood may be enhanced with a pigment blend containing colorless glass chips and/or colored glass chips. The glass chips can increase the visual dimensionality of the wood by enhancing the tone and expanding the apparent definition of the ticking or grain in the wood, while also providing functional enhancement such as improved color travel.
- In addition, substrates containing the pigment blend of the present invention can show improved abrasion resistance, which may be particularly useful in items such as articles of clothing, including leather goods. Substrates containing pigment blends with the fine particle can also show improved light fastness if the chips contain suitable UV screening. The fine particle chips may also be used as a component of a pigment blend in cosmetics to provide enhanced visual and functional properties. For example, cosmetics containing the fine particle materials may be used to help provide UV screening for the skin, camouflage blemishes, cellulite, wrinkles, varicose veins or other skin imperfections, and enhance the visual effect of the coloring agents contained within the pigment blend of the cosmetics.
- Surface visibility of articles may be improved with pigment blends containing mirrorized and/or reflectorized fine particle chips. In particular, pigment blends containing mirrorized glass chips provide superior reflectivity and visibility compared to blends containing metal flakes. Such pigment blends can improve safety while also providing an aesthetically pleasing appearance. Because mirrorized or reflectorized glass chips display scattered reflectivity, enhanced night and day time surface visibility can be achieved from both multi-angle light sources and light sources close to the viewing angle of an observer.
- It will be understood that the foregoing is only illustrative of the principles of the invention, and that various modifications can be made by those skilled in the art without departing from the scope and spirit of the invention, which is limited only by the claims that follow.
Claims (24)
1. A pigment blend comprising:
a plurality of particle materials made by pulverizing a solid material; wherein said particles materials have a substantially random geometrical shape and a particle size less than about 100 microns.
2. The pigment blend according to claim 1 , further comprising at least one coloring agent.
3. The pigment blend according to claim 1 , wherein said particle size is less than about 30 microns.
4. The pigment blend according to claim 1 , and wherein said solid material is selected from the group consisting of glass, oyster shells, clam shells, rubber, rock minerals, coal, and metal.
5. A particle material made by pulverizing a solid material, wherein said particle material has a substantially random geometrical shape and a particle size less than about 100 microns, and wherein said solid material is a brittle material.
6. The particle material according to claim 5 , wherein said solid material is selected from the group consisting of glass, oyster shells, clam shells, rubber, rock minerals, coal, and metal.
7. The particle material according to claim 5 , wherein said solid material has an ultraviolet light screening property.
8. A method of manufacturing a plurality of particle materials, having a substantially random geometrical shape and a particle size less than about 100 microns, comprising pulverizing a solid material into particle materials, and classifying said particle materials according to size.
9. The method of manufacturing a plurality of particle materials according to claim 8 , further comprising the step of milling said particle materials.
10. A method of manufacturing a pigment blend comprising:
pulverizing a solid material into a particle material having a substantially random geometrical shape;
classifying said particle material according to size; and
mixing said particle material, having a random geometric shape and a particle size less than about 100 microns, with a binder material suitable for use in a composition selected from the group consisting of paint, coloring, and coating.
11. The method of manufacturing a pigment blend according to claim 10 , wherein said solid material is selected from the group consisting of glass, oyster shells, clam shells, rubber, rock minerals, coal, and metal.
12. A method of enhancing a visual appearance of a substrate comprising:
making a pigment blend comprising a plurality of particle materials having a substantially random geometrical shape, and a particle size less than about 100 microns; and
mixing a binder material, suitable for use in a composition selected from the group consisting of paint, coloring, and coating, with said pigment blend; and
adding said composition to said substrate.
13. The method according to claim 12 , wherein said particle size is less than about 30 micron.
14. The method according to claim 12 , wherein said solid material is selected from the group consisting of glass, oyster shells, rubber, rock minerals, coal, and metal.
15. The method according to claim 12 , wherein said substrate is selected from the group consisting of metal, ceramic, glass, asbestos, human skin, leather, vinyl, plastic, polyester, epoxies, fabrics, wood, and rubber.
16. A solid material pulverizer, comprising:
a processing chamber with an inlet and an outlet;
a plurality of impellers positioned in said processing chamber; and
a shaft extending through said processing chamber and said plurality of impellers, wherein said shaft comprises a plurality of shaft portions that are coupled by at least one coupling.
17. The solid material pulverizer of claim 16 , wherein said at least one coupling comprises a split shaft.
18. The solid material pulverizer of claim 16 , wherein said at least one coupling is a compressible coupling.
19. A solid material pulverizer, comprising:
a processing chamber with an inlet and an outlet;
a plurality of impellers positioned in said processing chamber;
a shaft extending through said processing chamber and said plurality of impellers; and
a cooling liquid that is used to cool said shaft.
20. The solid material pulverizer of claim 19 , further comprising:
a reservoir for containing said cooling liquid; and
a pump for pumping said cooling liquid between said reservoir and said shaft.
21. The solid material pulverizer of claim 19 , wherein said shaft comprising a passage that permits said cooling liquid to pass through said shaft.
22. A solid material pulverizer, comprising:
a processing chamber with an inlet and an outlet;
a plurality of baffle plates positioned in said processing chamber;
a plurality of impellers positioned in said processing chamber; and
a shaft extending through said processing chamber and said plurality of impellers, wherein said shaft comprises a threaded portion that enables said plurality of impellers to be repositioned with respect to said baffle plates.
23. A solid material pulverizer, comprising:
a processing chamber with an inlet and an outlet;
a plurality of impellers positioned in said processing chamber, wherein at least one of the plurality of impellers comprises vanes on both sides of said at least one of the plurality of impellers; and
a shaft extending through said processing chamber and said plurality of impellers.
24. A solid material pulverizer, comprising:
a processing chamber with an inlet and an outlet;
a plurality of impellers positioned in said processing chamber;
a plurality of rings positioned in said processing chamber at which said plurality of impellers project material to be pulverized, wherein at least one of said plurality of rings has an inside diameter that decreases substantially semetrically when measured from the middle toward both the top and the bottom of said at least one of said plurality of rings; and
a shaft extending through said processing chamber and said plurality of impellers.