US20010039087A1 - Dram trench capacitor - Google Patents
Dram trench capacitor Download PDFInfo
- Publication number
- US20010039087A1 US20010039087A1 US09/764,656 US76465601A US2001039087A1 US 20010039087 A1 US20010039087 A1 US 20010039087A1 US 76465601 A US76465601 A US 76465601A US 2001039087 A1 US2001039087 A1 US 2001039087A1
- Authority
- US
- United States
- Prior art keywords
- trench
- region
- dielectric constant
- capacitor
- temperature sensitive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a process of fabricating semiconductor memory structures, particularly deep trench semiconductor memory devices wherein a temperature sensitive high dielectric constant material is incorporated into the storage node of the capacitor. Specifically, the present invention describes a process for forming deep trench storage capacitors after high temperature shallow trench isolation and gate conductor processing. This process allows for the incorporation of a temperature sensitive high dielectric constant material into the capacitor structure without causing decomposition of that material. Furthermore, the process of the present invention limits the extent of the buried-strap outdiffusion, thus improving the electrical characteristics of the array MOSFET.
Description
- The present invention relates to a semiconductor memory device, and in particular to a deep trench dynamic random access memory (DRAM) capacitor structure wherein a temperature sensitive high dielectric constant material is used and is incorporated into the storage node of the DRAM trench capacitor.
- In dynamic random access memory (DRAM) cell manufacturing, a key issue is the size of the overall cell. As the integration densities increase, it is desirable in the semiconductor industry to decrease the storage capacitor size while maintaining the charge storage capacity. One approach to this problem in the prior art is to utilize a deep trench capacitor. Such capacitor structures have reduced surface space while maintaining the charge storage capacity of the capacitor.
- One problem associated with the formation of deep trench capacitors for semiconductor memory cells such as DRAMs is how to incorporate temperature sensitive high dielectric constant materials such as barium strontium titanium oxide (BSTO) into the storage node of the DRAM capacitor device.
- Another problem associated with the formation of deep trench storage capacitors is the effect of the buried-strap outdiffusion on the array MOSFET electrical characteristics. Presently, DRAM technology falls into two main categories, use of stacked capacitor storage elements and use of deep trench storage capacitors. Each approach has certain advantages and disadvantages relative to each other. For example, deep trench technology results in improved planarization of the various layers of the structure which facilitates the ultra-fine lithographic and etching processes required for todays DRAMs.
- FIG. 1 is a cross-sectional diagram showing the structure of a prior
art DRAM cell 61 having atrench storage capacitor 60 and anarray MOSFET 62. TheDRAM cell 61 occupies an area of about 7F2 of the surface area of the DRAM IC, F being the minimum feature size which is photolithographically defined for features on the IC. TheDRAM cell 61 is characterized by adesign dimension 63 which is defined as the lateral distance between thenear edge 64 of thetrench storage capacitor 60 and thefar edge 66 of thegate conductor 68. In an existing 7F2 DRAM cell design, thisdimension 63 is designed to have a value of nominally 1.5 F, with the width of the gate conductor being 1.0 F and the nominal (designed) distance between the near edge of the gate conductor and thetrench storage capacitor 60 being 0.5 F. - The most widely used trench storage DRAM technology utilizes a buried-strap (see FIG. 1) to form the connection between the array MOSFET and the
storage capacitor 60. The buried-strap has a diffusion associated with it which extends vertically and laterally away from the interfacial opening between thetrench storage capacitor 60 and the silicon substrate (see FIG. 1). The diffusion is formed by the outdiffusion of dopants (i.e. arsenic) from the N+ polysilicon in the storage trench into the adjacent single crystal silicon substrate. The depth and lateral extent of this buried-strap outdiffusion is highly detrimental to the scalability of the array MOSFET. - In past DRAM generations, when the state of the art minimum feature size, F, was larger than approximately 0.5 μm, the presence of the buried-strap outdiffusion did not pose much of an electrical problem for the array MOSFET. However, with present day DRAM designs approaching minimum feature size equal to 0.15 μm, and the typical buried-strap outdiffusion distance being greater than 50 nm from the interface between the N+ polysilicon in the deep trench, it is likely that the buried-strap outdiffused junction may extend under the gate conductor (wordline). This is likely to occur since, in addition to the large outdiffusion relative to the
dimension 63, there is significant misalignment tolerance between the gate conductor and the deep storage trench. As shown in FIG. 1, the encroachment of the buried-strap outdiffusion upon the array MOSFET is characterized by the parameter δ, which is the distance between the bitline (BL) diffusion and the buried-strap (BS) outdiffusion, expressed as a percentage of the trench edge to gateconductor edge dimension 63. - FIG. 2 illustrates how the device off-current increases with decreasing δ. To assure that the off-current objective is met under all circumstances, the channel doping of the MOSFET must be raised. However, increased channel doping results in increased junction leakage and degraded device performance, thus degrading data retention time. Therefore, it is highly desirable to make the value of δ as large as possible to minimize these deleterious effects.
- The distance between the bitline diffusion and the buried-strap diffusion is determined by the layout groundules, process tolerances (overlay and feature size) and the amount of buried-strap outdiffusion from the trench storage capacitor. This critical distance is illustrated by the parameter δ in the prior art deep trench DRAM cell shown in FIG. 1. The amount of buried-strap outdiffusion is principally determined by the thermal budget that the buried-strap encounters in the course of the chip fabrication process. The thermal budget is a function of the square root of the sum of the products of the diffusivity, D, of the strap dopant impurity and the effective amount of time spent at each high temperature step which contributes significantly to the diffusion.
- For prior art deep trench storage capacitor DRAM cells, the high temperature processing steps which contribute to the strap outdiffusion from the storage capacitor polysilicon typically consist of STI oxidation, STI densification, gate sacrificial oxidation, transfer gate oxidation, gate conductor sidewall oxidation, and junction anneals. The combined thermal budget of these high-temperature processes results in an arsenic outdiffusion from the storage trench poly into the silicon substrate which typically ranges from 50 to 100 nm. This means that for high-density trench DRAM cell designs having a minimum feature size of 0.15 μm, the distance δ typically ranges from 0.08 to 0.13 μm; δ typically ranges from 35% to 60% of the design distance between the storage trench edge and the far edge of the gate conductor, for prior art DRAM cells having a layout area of 7 minimum features squared (7F2) per bit and a minimum feature size, F, equal to 0.15 μm. As seen from FIG. 2, the off-current can vary by more than 100× over this range of variation in δ.
- In a possible fabrication approach, a deep trench is first formed in a semiconductor substrate or wafer and then the deep trench is filled with a temperature sensitive high dielectric constant material. After filling the deep trench with the temperature sensitive high dielectric constant material, shallow trench isolation (STI) regions and gate conductor (GC) stacks are typically formed. A problem with such an approach is that the high temperatures used in fabricating the STI regions and the GC stacks adversely affect the temperature sensitive high dielectric constant material used in filling the deep trench and contribute to the buried-strap outdiffusion. Specifically, the length of time at the high processing temperatures employed in fabricating the STI regions and the GC stacks cause decomposition of the temperature sensitive high dielectric constant material and add to the thermal budget of the strap outdiffusion. The high dielectric material and its by-products thus formed may diffuse and interact with the underlying semiconductor material.
- To avoid this problem of capacitor insulator degradation, the prior art in stacked capacitor DRAM technology utilizes a thin electrically conductive barrier layer comprising a material such as TiN, TiAlN, TaSiN and CoSi between the temperature sensitive high dielectric constant material and the semiconductor material, e.g. silicon. The presence of such a barrier layer in semiconductor memory devices, while prohibiting oxygen diffusion from occurring, adds additional processing steps and costs to the overall semiconductor memory device manufacturing process.
- On top of this conductive barrier layer, the prior art in stacked capacitor DRAM technology typically deposits a thin layer of a conductive material so as to form a bottom electrode. This conducting layer, in the case of high dielectric constant capacitors, is composed of conductive oxides such as RuO2, SrRuO3, La—Sr—Co—O and IrO2, or by metals like Pt or Ir. One advantage of SrRuO3 is that it can be directly deposited on silicon with minimum or no oxidation underneath. A high dielectric constant material can then be deposited on top of the electrode layer to a desired thickness.
- Finally, for the top electrodes, material similar to the bottom electrode is typically selected. If it is desired to use a polysilicon or amorphous silicon overlayer, a thin layer of a barrier material, as discussed above, can be deposited to prevent undesirable reactions between silicon and the electrode material before chemical vapor deposition (LPCVD) of amorphous/polysilicon.
- In view of the drawbacks mentioned with prior DRAM stacked capacitor structures in using temperature sensitive high dielectric constant material, it would be beneficial if a new and improved process of fabricating a trench DRAM capacitor structure having a temperature sensitive high dielectric constant material incorporated into the storage node of the DRAM capacitor structure was developed which overcomes all of these drawbacks.
- It should also be mentioned that in the process embodiment of the present invention, the buried-strap outdiffusion from the trench storage capacitor does not encounter the STI liner oxidation, sacrificial oxidation and gate oxidation steps. This limits the thermal budget and the amount of buried-strap outdiffusion. In prior art processes, the buried-strap diffuses further due to the inclusion of the three oxidation steps mentioned above.
- One object of the present invention is to provide a process of fabricating a trench capacitor semiconductor memory device which allows for the easy incorporation of a temperature sensitive high dielectric constant material into the capacitor region of the device.
- Another object of the present invention is to provide a process of fabricating a trench capacitor semiconductor memory device wherein the storage node material, i.e. temperature sensitive high dielectric constant material, does not degrade during the course of providing the STI regions and the GC stack regions of the memory device.
- A still further aspect of the present invention is to provide a process of fabricating a trench capacitor semiconductor memory cell device wherein the temperature sensitive high dielectric constant material does not diffuse into the underlying semiconductor material.
- Yet another object of the present invention is to provide a process which results in a limited buried-strap outdiffusion, whose deleterious electrical effects on the array MOSFET are reduced from the prior art.
- These as well as other objects and advantages can be achieved in the present invention by forming the storage trench after formation of the STI regions in a semiconductor structure which contains preformed layers of a partial GC stack already on the surface of the structure. By fabricating the trench capacitor after STI formation, the temperature sensitive high dielectric constant material does not encounter the high temperatures associated with STI formation. Moreover, since the initial structure contains a partial GC stack already on the surface, the temperature sensitive high dielectric constant material does not encounter high temperatures that are associated with fabricating the GC stack; therefore substantially no degradation of the temperature sensitive material is caused to occur.
- Specifically, the process of the present invention comprises the steps of:
- (a) providing a semiconductor structure comprising a semiconductor substrate or wafer having at least one trench storage region and a raised shallow trench isolation (STI) region adjacent to said trench storage region, said structure having preformed layers of a partial gate conductor stack formed on said substrate or wafer which are spaced apart by said trench storage region and said raised STI region;
- (b) forming a bottom electrode in said trench storage region;
- (c) forming a temperature sensitive high dielectric constant material on said bottom electrode and lining sidewalls of said trench storage region;
- (d) forming a top electrode over said temperature sensitive high dielectric constant material;
- (e) filling said trench with polysilicon;
- (f) completing fabrication of a capacitor in said trench storage region;
- (g) forming a patterned gate conductor region from said preformed GC stack layers; and
- (h) forming subsequent device connections so as to complete fabrication of a trench capacitor semiconductor memory cell.
- In a highly preferred embodiment of the present invention, the trench storage region is formed after STI formation and formation of the partial GC stack layers. In another highly preferred embodiment of the present invention, a conducting barrier layer is formed over the top electrode prior to the polysilicon fill.
- In accordance with the present invention, the formation of the trench storage capacitor follows the formation of the STI. This means that the prior art high-temperature processing steps which include STI oxidation, STI densification, gate sacrificial oxidation, and transfer gate oxidation are not seen by the buried-strap outdiffusion. Elimination of these high temperature steps from the thermal budget of the strap outdiffusion typically results in a reduction of thermal budget-of greater than 50%. This reduction of thermal budget translates into a reduction of strap outdiffusion which is typically greater than 30% of the outdiffused distance which results from the prior art process. This reduction in strap outdiffusion, which is typically less than 50 nm, results in a substantial increase in the parameter δ, which results in reduced off-current for a given channel doping concentration. In the present invention δ is always greater than that of the prior art structures. For the inventive structure, δ is typically 50% to greater than 75% of the design distance between the storage trench edge and the far edge of the gate conductor, for a 7F2 cell with F=0.15 μm. Because of the high sensitivity of the MOSFET off-current to δ, the inventive structure represents a significant improvement over the prior art, whose δ ranges from 35% to 60% of the design distance.
- FIG. 1 is a cross-sectional view of a prior art trench storage DRAM structure.
- FIG. 2 is a graph of modeled sensitivity of device off-current to distance outdiffusion and bitline diffusion,
- FIGS.3(a)-(l) show various processing steps that are employed in the-present invention in fabricating a trench capacitor semiconductor memory device having a temperature sensitive high dielectric constant material incorporated into the storage node of the capacitor.
- FIGS.4(a)-(d) show various processing steps that are employed in fabricating the semiconductor structure illustrated in FIG. 3(a).
- The present invention, which provides a process of fabricating a trench capacitor semiconductor memory device having a temperature sensitive high dielectric material incorporated into the storage node of the capacitor, will now be described in greater detail by referring to the drawings that accompanying this application. It is noted that in the various drawings like elements or components are referred to be like and corresponding reference numerals.
- Before describing the process of the present invention it is again emphasized that the process of the present invention overcomes the drawbacks in prior art deep trench semiconductor memory cells by forming the trench storage region after the STI regions and preformed layers of a GC stack are formed. By forming the storage trench after high temperature STI and GC processing, the temperature sensitive high dielectric constant material formed in the storage trench of the memory cell does not degrade and thus it does not interact by diffusion with the underlying semiconductor material.
- Furthermore, in the present invention the buried-strap outdiffusion does not see several high temperature processing steps which contribute to large buried-strap outdiffusion in the prior art. Thus, the lateral outdiffusion of the buried-strap formed in the present invention is significantly reduced as compared with prior art memory cell structures.
- With this in mind, attention is directed to FIG. 3(a) which shows an initial semiconductor structure which is employed in step (a) of the present invention. Specifically, the semiconductor structure shown in FIG. 3 (a) comprises a semiconductor substrate or
wafer 10 having at least onestorage trench region 12 and a raised shallow trench isolation (STI)region 14 adjacent tostorage trench region 12 formed therein. The structure further comprises preformedlayers 16 of a partial gate conductor stack formed thereon which are spaced apart bystorage trench region 12 and raisedSTI region 14. - Semiconductor substrate or
wafer 10 is composed of any semiconducting material including, but not limited to: Si, Ge, SiGe, GaAs, InAs, InP and all other III/V compounds. Of these semiconducting material, it is preferred that semiconductor substrate orwafer 10 be composed of Si. The semiconductor substrate or wafer may be of the p-type or the n-type depending on the type of semiconductor memory device being manufactured. The preformed layers of the partial gate conductor shown in FIG. 3(a) are composed of a bottomgate oxide layer 16 a such as SiO2, a middle layer ofpolysilicon 16 b and a toppolish stop layer 16 c such as Si3N4. The layers are formed sequentially on the surface of the semiconductor substrate or wafer starting withlayer 16 a, then 16 b and finally 16 c. - The structure shown in FIG. 3(a) is fabricated using conventional techniques well known to those skilled in the art. For example, the structure shown in FIG. 3(a) can be fabricated as is shown in FIGS. 4(a)-(d). Specifically, as is shown in FIG. 4(a), a semiconductor substrate or
wafer 10 is first provided andgate oxide layer 16 a is grown on the surface of semiconductor substrate orwafer 10 using conventional thermal growing techniques well known to those skilled in the art. This includes heating the semiconductor substrate or wafer in an oxygen ambient at a temperature of from about 800° to about 1100° C. until a gate oxide having a thickness of from about 4 to about 10 nm is formed on the surface of the semiconductor substrate or wafer. - Next, a layer of
polysilicon 16 b is formed on the surface ofgate oxide 16 a using standard deposition techniques well known to those skilled in the art. Suitable deposition processes that may be employed in formingpolysilicon layer 16 b include, but are not limited to: chemical vapor deposition, plasma vapor deposition, low pressure chemical vapor deposition, high density chemical vapor deposition and other like deposition processes. The thickness of the polysilicon layer formed is typically in the range of from about 10 to about 500 nm. -
Polish stop 16 c is then formed onpolysilicon layer 16 b using standard deposition techniques, including those mentioned above, that are well known to those skilled in the art. The polish stop is composed of a conventional material such as Si3N4 which resists erosion during subsequent planarization and etching steps. The thickness of the polish stop layer formed is typically of from about 10 to about 500 nm. - The next step in forming the structure of FIG. 3(a) is illustrated in FIG. 4(b). Specifically, FIG. 4(b) shows a structure which contains a
trench 14 a which is formed inlayers wafer 10. It is noted thattrench 14 a is used in formingSTI region 14. The structure of FIG. 4(b) is fabricated using standard lithography, etching and planarization, all of which are well known to those skilled in the art. - Specifically, the structure shown in FIG. 4(b) is fabricated by providing a conventional resist having a preformed pattern on top of
layer 16 c of the structure shown in FIG. 4(a) using standard deposition techniques which include spin-on coating and dip coating. The pattern is then etched by standard etching techniques well known to those skilled in the art throughlayers wafer 10. Suitable etching techniques that can be employed include, but are not limited to: reactive ion etching (RIE), plasma etching and ion beam etching. The depth that etching is performed into the semiconductor substrate or wafer is typically of from about 100 to about 700 nm. It should be noted that the resist is removed at this time using conventional stripping techniques well known to those skilled in the art. - A thermal silicon dioxide layer, not shown in the drawings, is then grown in the trench of the raised STI region using conventional thermal growing techniques, including the use of an oxygen-containing ambient and heating to a temperature of from about 750° to about 1100° C. The thickness of the grown silicon dioxide layer in
trench 14 a is typically of from about 3 to about 30 nm. A STI dielectric, not shown in the drawings, is then formed over the thermal silicon dioxide layer using standard deposition techniques such as low pressure chemical vapor deposition or a plasma-assisted process. Suitable STI dielectrics include, but are not limited to: high density plasma tetraethylorthosilicate (HDP TEOS) oxide. It should be noted that in the drawings of the present invention, the above two components, i.e. thermal silicon dioxide layer and STI dielectric are not shown. Instead,STI region 14 is meant to include those two components as well as others that may be present in a conventional STI region. - To provide a planar structure, as is shown in FIG. 4(b), the structure is then planarized using standard planarization techniques well known to those skilled in the art, including, but not limited to: chemical mechanical polishing, RIE and grinding.
- FIG. 4(c) shows the next steps employed in fabricating the structure illustrated in FIG. 3(a). Specifically, to the planarized structure of FIG. 4(b) there is formed a hard
dielectric mask layer 18, e.g. boron doped silicon dioxide (BSG), which is then patterned utilizing standard lithography techniques and reactive ion etched to remove a portion of the hard dielectric mask. The patterned structure is shown in FIG. 4(c). - Next, a
storage trench 20 is formed in semiconductor substrate orwafer 10 using harddielectric layer 18 as a masking film. Specifically, RIE using reactive gases such as HBr, NF3, O2 or He is employed in fabricatingstorage trench 20. By “storage trench” it is meant that etching is performed to a depth of from about 1 to about 10 μm. The structure containingstorage trench 20 which forms the capacitor region of the device is shown in FIG. 4(d).Hard dielectric mask 18 is then removed by an HF-etching process to provide the structure shown in FIG. 3(a). - It is again emphasized that the above description provides one way of fabricating the structure shown in FIG. 3(a). Other ways of fabricating the structure shown in FIG. 3(a) are also known and are thus contemplated herein.
- In accordance with step (b) of the present invention, a
bottom electrode 22 is then formed in storage trench 20 (bottom wall, sidewalls as well as areas outside the deep trench) using conventional deposition techniques well known to those skilled in the art. For example,bottom electrode 22 can be formed by chemical vapor deposition, metallo-organic chemical vapor deposition, electroplating or electrodeless plating. The material employed in formingbottom electrode 22 includes any conductive oxide which is typically used as a bottom electrode of a capacitor. Exemplary conductive oxides include, but are not limited to: RuO2, SrRuO3, La—Sr—Co—O, IrO2 and other like conductive oxides. In addition to conductive oxides, metals such as Pt or Ir can also be used as the bottom electrode. The structure containingbottom electrode 22 is shown in FIG. 3(b). - In an optional embodiment of the present invention, a diffusion barrier layer is formed in
storage trench 20 prior to formingbottom electrode 22. Suitable diffusion barrier layers that can be optionally employed in the present invention include, but are not limited to: TiN, TiAlN, TaSiN, CoSi and other like materials which are capable of preventing the diffusion of oxygen into the semiconductor substrate or wafer. Chemical vapor deposition or physical vapor deposition are two deposition processes that can be employed in the present invention in forming the optional diffusion barrier layer. - After formation of
bottom electrode 22, a layer of a temperature sensitive high dielectricconstant material 24 is formed on the surface of the bottom electrode, see FIG. 3(c). The term “temperature sensitive” is used herein to denote a material which when in contact with silicon and heated to temperatures over 600° C. oxidizes the silicon and degrades by reacting with silicon or by breaking up into other compounds. The temperature sensitive high dielectric constant material utilized herein is however not in direct contact with silicon. It nevertheless becomes unstable by itself at temperatures of about 550° C. and above. On the other hand, the term “high dielectric constant material” denotes a material which has a dielectric constant relative to a vacuum higher than about 7. More preferably, the high dielectric constant material employed in the present invention has a dielectric constant of from about 20 to about 10,000. - Suitable temperature sensitive high dielectric constant materials that can be employed in the present invention include perovskite-type oxides such as barium strontium titanium oxide (BSTO), lead zirconium titanium oxide (PZTO), strontium bismuth tantalate (SBT) and Ta2O5. The temperature sensitive high dielectric constant material is formed on
bottom electrode 22 using standard deposition processes including chemical vapor deposition or sputtering. - A
top electrode 26 is then formed on top of temperaturesensitive material 24 utilizing standard deposition techniques such as chemical vapor deposition. The top electrode may be composed of the same or different conductive oxide as the bottom electrode. Thus,top electrode 26 may be composed of RuO2, SrRuO3, La—Sr—Co—O and IrO2. Alternatively, Pt or Ir can be employed. The structure containingtop electrode 26 is shown in FIG. 3(d). - In an optional, but highly preferred embodiment of the present invention, a conducting barrier layer is formed over
top electrode 26 prior to filling the trench withpolysilicon 28. This conducting barrier layer which is formed by conventional deposition processes serves to prevent interaction between the temperature sensitive high dielectric constant material and the polysilicon. TiN, TiAlN, CoSi and TaSiN are some examples of conducting barrier layers that may be employed in the present invention. For clarity, the conducting barrier layer is not shown in the drawings. - The remaining portion of
storage trench 20 is filled withpolysilicon 28, preferably n+-doped polysilicon, using standard deposition processes and then the polysilicon is recessed using a dry etch containing gas such as SF6, He, O2 or NF3 to a depth of from about 0.5 to about 1.5 μm. The structure obtained from these combined steps of the present invention is shown in FIG. 3(e). - It should be noted that the recess process mentioned above and the description that follows regarding FIGS.3(f)-(j) refers to processing steps that are employed in the present invention in fabricating the capacitor in the storage trench region.
- Next, as is shown in FIG. 3(f), a conformal insulating
collar oxide 30 is then formed over the semiconductor substrate orwafer 10 and the sidewalls ofstorage trench 20 which were again left exposed by the above recess process. The conformal insulating collar oxide is formed by conventional deposition processes such as low pressure chemical vapor deposition or plasma-assisted chemical vapor deposition to a thickness of from about 10 to about 30% of the storage trench diameter. Dry etching using an anisotropic removal processing gas such as C4F8, CH3F, CF4, C3F8, CO, O2 or Ar is then employed so as to etch material from the wafer plane and the bottom ofstorage trench 20, but leaving material along the sidewalls of the storage trench. The trench is then filled with low pressure chemical vapor depositedpolysilicon 32 which may or may not be doped and planarized utilizing a dry etch or chemical mechanical polishing process. - As shown in FIG. 3(g), the low pressure chemical vapor deposited polysilicon is then recessed to a predetermined depth, e.g. 20 to 50 nm, utilizing a dry etch process such as previously described hereinabove. The collar dielectric is then removed using a HF containing etch from upper regions of the storage trench, See FIG. 3(h).
- The next steps employed in the present invention in completing the fabrication of the capacitor in the storage trench, which is shown in FIG. 3(i), comprise depositing a low pressure chemical vapor
deposition polysilicon layer 34 which may or may not be doped over the structure and then recessing using an anisotropic dry etch process containing gases such as HBr, Cl2, HCl, SF6, He or O2 to a depth of from about 5 to about 30 nm below the surface of semiconductor substrate orwafer 10. -
Capacitor 36 is then completely fabricated in the storage trench by forming a trench top oxide (TTO)dielectric film 38 and planarizing to the top oflayer 16 c, See FIG. 3(j). The TTO dielectric film is formed by conventional deposition processes including low pressure chemical vapor deposition or plasma enhanced chemical vapor deposition and planarization is carried out using one of the previously mentioned planarization techniques, e.g. chemical mechanical polishing. - FIG. 3(k) shows a structure which includes a completely formed gate conductor stack which includes preformed gate conductor layers 16 a and 16 b, as well as a
polysilicon layer 16 d, a salicide layer, i.e. WSi, 16 e and cap layer, Si3N4, 16 f.Polysilicon layer 16 d is formed using the same deposition techniques as is described forpolysilicon layer 16 b.Layer 16 e is formed by chemical vapor deposition or sputtering and it has a thickness of from about 20 to about 200 nm. In regard to caplayer 16 f, that layer is formed by low pressure chemical vapor deposition and it has a final deposited thickness of from about 20 to about 300 nm. It should be noted thatbarrier layer 16 c is removed prior to depositinglayers 16 d, e and f. - The various gate stack layers are then patterned using conventional lithography and a RIE dry etch process stopping in
gate oxide layer 16 a and the TTO/STI oxide, See FIG. 3(l). A gate sidewall oxidation may be done by conventional process.Sidewall spacers 42, e.g. Si3N4, are formed over the patternedgate conductor stack 40 a using deposition techniques well known to those skilled in the art. - The semiconductor memory structure is then fully fabricated as follows: source/
drain diffusion regions 50 are formed in the semiconductor substrate orwafer 10 using conventional ion implantation followed by appropriate annealing steps. In FIG. 3(l), 50A represents a bitline diffusion region and the MOSFET region of the memory cell is defined as comprising patternedgate stack region 40 a,region 50 andregion 50A. The gate sidewall oxidation and junction anneal steps mentioned hereinabove drive the N+ dopant frompolysilicon region 28 throughpolysilicon regions strap outdiffusion region 44. The limited buried-strap outdiffusion region of the present invention has a lateral dimension 52 of less than 50 nm. More preferably the lateral dimension 52 of the buried-strap is from about 15 to about 30 nm. - An insulating
layer 46 such a boron-phosphorous doped glass is deposited over the structure covering patternedgate conductor regions 40 a, exposedgate oxide region 16 a, andcapacitor 36 using conventional deposition processes such as spin-on coating and chemical vapor deposition. Insulatinglayer 46 is then planarized using one of the aforementioned planarization techniques, andborderless diffusion contacts 48 are formed by standard lithography, dry etching, depositing a polysilicon layer and planarization. - It is noted that the memory cell of FIG. 3(l) is unlike prior art memory cells since the lateral outdiffusion of the buried-strap is significantly reduced as compared with prior art structures. More the distance, δ2, is greater for the inventive structure as compared with prior art structures, like the type shown in FIG. 1. This greater distance means that the off-current problem typically observed with prior art structures is significantly reduced herein.
- In a DRAM cell in which the designed
distance 43 between the near edge of the trench capacitor and the far edge of thegate conductor stack 40 a is about 1.5 times a minimum feature size F of 0.15 μm, thedistance 62 is nominally at least 50% of thedistance 43. A distance δ2, of nominally 75% or greater can be achieved with the process disclosed herein for a 7F2 DRAM cell with F equal to 0.15 micron. - While the present invention has been particularly shown and described with respect to preferred embodiments thereof, it will be understood by those skilled in the art that the foregoing and other changes in form and detail may be made without departing from the spirit and scope of the present invention.
Claims (33)
1. A process of fabricating a trench capacitor semiconductor memory structure comprising the steps of:
(a) providing a semiconductor structure comprising a semiconductor substrate or wafer having at least one storage trench region and a raised shallow trench isolation (STI) region adjacent to said storage trench, said structure having preformed layers of a partial gate conductor stack formed in said substrate or wafer which are spaced apart by said storage trench and raised STI regions;
(b) forming a bottom electrode layer in said storage trench region;
(c) forming a temperature sensitive high dielectric constant material on said bottom electrode layer and lining sidewalls of said storage trench region;
(d) forming a top electrode over said temperature sensitive high dielectric constant material;
(e) filling said storage trench region with polysilicon;
(f) completing fabrication of a capacitor in said storage trench region;
(g) forming a patterned gate conductor region from said preformed gate conductor stack layers; and
(h) forming subsequent device connections so as to complete fabrication of a trench capacitor semiconductor memory cell.
2. The process of wherein said STI region and said partial GC stack layers are formed prior to fabrication of said trench storage capacitor.
claim 1
3. The process of wherein said semiconductor substrate or wafer is composed of a semiconducting material selected from the group consisting of Si, Ge, SiGe, GaAs, InAs, InP and all other III/V compounds.
claim 1
4. The process of wherein said semiconductor substrate or wafer is composed of Si.
claim 1
5. The process of wherein said shallow trench isolation region includes a thermal silicon dioxide layer and a shallow trench isolation dielectric.
claim 1
6. The process of wherein said preformed partial gate conductor stack comprises a bottom gate oxide layer, a middle layer of polysilicon and a top barrier layer, wherein said layers are formed sequentially on the semiconductor substrate or wafer.
claim 1
7. The process of wherein said bottom and top electrodes are formed of the same or different conducting material selected from the group consisting of RuO2, SrRuO3, La—Sr—Co—O, IrO2, Pt and Ir.
claim 1
8. The process of wherein said bottom and top electrodes are formed by a deposition process selected from the group consisting of chemical vapor deposition, metallo-organic chemical vapor deposition, electroplating and electrodeless plating.
claim 1
9. The process of wherein prior to step (b), a diffusion barrier layer is formed in said storage trench.
claim 1
10. The process of wherein said diffusion barrier layer is formed by chemical vapor deposition or physical vapor deposition.
claim 9
11. The process of wherein said diffusion barrier layer is composed of TiN, TiAlN, CoSi or TaSiN.
claim 9
12. The process of wherein said temperature sensitive high dielectric material is a material which may become unstable and also oxidize silicon when exposed to temperatures over 550° C. and has a dielectric constant of about 7 or higher.
claim 1
13. The process of wherein said temperature sensitive high dielectric constant material has a dielectric constant of from about 20 to about10,000.
claim 12
14. The process of wherein said temperature sensitive high dielectric constant material is a material selected from the group consisting of barium strontium titanium oxide (BSTO), lead zirconium titanium oxide (PZTO), strontium bismuth tantalate (SBT) and Ta2O5.
claim 1
15. The process of wherein said temperature sensitive high dielectric constant material is BSTO.
claim 1
16. The process of wherein said temperature sensitive high dielectric constant material is formed by a deposition process selected from the group consisting of chemical vapor deposition and sputtering.
claim 1
17. The process of wherein said polysilicon in step (e) is doped with a dopant.
claim 1
18. The process of wherein said dopant is a N+dopant.
claim 17
19. The process of wherein said storage trench region has a depth of from about 1 to about 10 μm.
claim 1
20. The process of wherein after step (d), but prior to step (e), a conducting barrier is formed on said top electrode.
claim 1
21. The process of wherein said conducting barrier layer is TiN, TiAlN, CoSi or TiSiN.
claim 20
22. The process of further comprising subsequent gate sidewall oxidation and anneal steps which cause outdiffusion of the dopant from said polysilicon into said semiconductor substrate or wafer forming a buried-strap outdiffusion region whose lateral size is less than 50 nm.
claim 17
23. The process of wherein said lateral size of said outdiffusion region is between about 15 and about 30 nm.
claim 22
24. A memory cell comprising
a capacitor formed in a trench located in a semiconductor substrate or wafer;
a MOSFET formed in said semiconductor substrate or wafer, said MOSFET comprising at least a patterned gate conductor stack and source/drain regions, said capacitor and said MOSFET being connected by a buried-strap outdiffusion region whose lateral outdiffusion is less than 50 nm.
25. The memory cell of wherein said lateral outdiffusion is from about 15 to about 30 nm.
claim 24
26. The memory cell of wherein said buried-strap outdiffusion region is positioned adjacent to said capacitor.
claim 24
27. The memory cell of wherein said semiconductor substrate of wafer is composed of Si.
claim 24
28. The memory cell of wherein said capacitor comprises a temperature sensitive high dielectric constant material.
claim 24
29. The memory cell of wherein said temperature sensitive high dielectric material is a material which may become unstable and also oxidize silicon when exposed to temperatures over 550° C. and has a dielectric constant of about 7 or higher.
claim 28
30. The memory cell of wherein said temperature sensitive high dielectric constant material has a dielectric constant of from about 20 to about 10,000.
claim 29
31. The memory cell of wherein said temperature sensitive high dielectric constant material is a material selected from the group consisting of barium strontium titanium oxide (BSTO), lead zirconium titanium oxide (PZTO), strontium bismuth tantalate (SBT) and Ta2O5.
claim 28
32. The memory cell of wherein said temperature sensitive high dielectric constant material is BSTO.
claim 28
33. A memory cell comprising
a capacitor formed in a trench located in a semiconductor substrate or wafer;
a MOSFET formed in said semiconductor substrate or wafer, said MOSFET comprising at least a patterned gate conductor stack, a near source/drain region located between said gate conductor stack and said capacitor, a far source/drain region located on a side of said gate conductor stack opposite said near source/drain region said capacitor and said MOSFET being connected by a buried-strap outdiffusion region laterally extending from an edge of said trench toward said gate conductor stack;
said capacitor and said source/drain regions having lateral dimensions photolithographically patterned to a minimum feature size of about 0.15 micron or smaller;
said memory cell characterized by a distance parameter, said parameter being the lateral distance between a near edge of said far source/drain region and a near edge of said outdiffusion region, said parameter having a value of between about 50% to greater than 75% of a lateral distance between said far gate conductor edge and said trench edge.