TWI818325B - 用於在模內電子(ime)組件之製造中使用的組成物、製造組成物之方法及製造模內電子組件之方法 - Google Patents
用於在模內電子(ime)組件之製造中使用的組成物、製造組成物之方法及製造模內電子組件之方法 Download PDFInfo
- Publication number
- TWI818325B TWI818325B TW110137306A TW110137306A TWI818325B TW I818325 B TWI818325 B TW I818325B TW 110137306 A TW110137306 A TW 110137306A TW 110137306 A TW110137306 A TW 110137306A TW I818325 B TWI818325 B TW I818325B
- Authority
- TW
- Taiwan
- Prior art keywords
- composition
- resin
- conductive
- particles
- ime
- Prior art date
Abstract
一種用於在模內電子(IME)組件之製造中使用的組成物,該組成物含有黏合劑,該黏合劑包含:交聯劑,其包含三聚氰胺甲醛;熱塑性樹脂,其包含羥基基團;及溶劑。
Description
本發明係關於用於在模內電子(IME)組件之製造中使用的組成物、製造組成物之方法、製造模內電子(IME)組件之方法、及模內電子(IME)組件。
高度可靠、強健、輕量、裝飾用、及經三維(3D)成形之人機介接電子裝置的發展係下一世代的汽車、白色家電、或消費性電子產品應用之發展高度所需者。
膜插物模製(FIM)係一種已知製程,其在模製程序期間將圖形、標示、及組件整合至塑膠部件。其係一種模內裝飾(IMD)或模內標示(IML)的形式。FIM程序能夠以二維(2D)將單一且經裝飾的塑膠部件建立成彎曲且經複雜成形的3D設計,該等設計係耐久且輕量的,可用於多種應用。在典型的FIM程序中,熱塑性膜之裝飾(顏色及透光率)以及表面功能(刮痕、抗反射、防眩光、光澤度、消光、抗指紋等)係按照應用需要設計,並經整合以製成強健、經複雜成形、及裝飾用的塑膠部件。此技術對於製成用於汽車、手持式電子裝置、及消費品的裝飾用部件而言係眾所周知,同時若干新近實例顯示與電子功能整合的努力。製備此類結構之方式中的一者係藉由射出模製網版印刷及/或熱成形之以導電及介電油墨印刷的電子電路系統。
有所欲的係製成能夠執行電子功能的3D射出模製、輕量塑膠結構。這些結構可藉由下列來製成:在可撓性聚合物基材(諸如,例如聚碳酸酯(PC)及聚對苯二甲酸乙二酯(PET))上網版印刷互連電路系統;附接/組裝電子組件至這些網版印刷電路系統;熱成形以製成此類電子裝置之3D結構,且隨後藉由射出模製將液體樹脂澆注至熱成形結構的背側,以製成強健而穩固的塑膠結構。此類結構可經設計以執行電容式及電阻式觸控開關應用,用於無線或藍牙連接、控制音量或光強度、及許多此類應用。這些射出模製電子結構係稱為模內電子(IME)、或射出模製結構電子(IMSE)、或Plastronics、或表面電子。
IME技術由整合若干電子及塑膠製造程序步驟組成:電子油墨(導電及介電油墨)的網版印刷、電子油墨的乾燥或固化、使用電子黏著劑的組件附接或電子總成、熱成形及修整以製成彎曲或3D結構、及藉由射出模製以熔融樹脂回填這些彎曲或3D結構。圖1描繪IME之通用製造程序步驟的示意圖。在圖1中,示意性地表示四個廣泛的製造處理步驟。在A(網版印刷及乾燥)處,顯示有2D網版印刷互連的示意圖:10表示可熱成形PC或PET基材、20表示網版印刷導電互連、30表示網版印刷電絕緣介電層。在B(電子組件總成(SMT組件、LED等))處,顯示有附接電子組件、LED等之2D電子電路系統的示意圖;40、50、及60表示不同的SMT組件或LED。在C(熱成形〔真空或高空氣壓力及溫度(140至210℃)〕)處,顯示有熱成形3D電子電路系統(70)的示意圖。在D(射出模製〔溫度(170至330℃)〕)處,顯示有射出模製(以射出模製樹脂填充)之熱成形3D電子電路系統(80)的示意圖。
電子功能可與FIM結構整合在兩膜中或在單一膜堆疊中。在兩膜堆疊中,以電子油墨印刷之塑膠層係藉由網版印刷導電或介電油墨而分開地製備,其等進一步係在射出模製步驟期間與以圖形油墨塗佈之經裝飾塑膠整合。單層膜結構中的裝飾用及電子功能兩者可以循序方式製造,首先始於網版印刷圖形油墨層,隨後網版印刷電子油墨(導電及介電油墨)以及使用導電或不導電黏著劑附接組件,且之後整體堆疊係進一步經熱成形及背向射出模製。塑膠基材一般係PC或PET,且射出模製樹脂一般係選自聚碳酸酯(PC)、聚對苯二甲酸乙二酯(PET)、丙烯腈丁二烯苯乙烯(ABS)、聚丙烯(PP)、聚酯、聚(甲基丙烯酸甲酯)(PMMA)、低密度聚乙烯(LDPE)、高密度聚乙烯(HDPE)、聚苯乙烯(PS)、及熱塑性聚胺甲酸酯(TPU)、及類似者。
典型的聚合物厚膜油墨(諸如,銀、碳等、及UV/熱固化介電油墨)及導電黏著劑係用於PC及PET基材上之可撓性電路構造。不過,這些油墨具高度可撓性,這些油墨無法經熱成形,因為其等在熱成形的同時顯示不連續性及裂開,且因此無法用於IME裝置製造。
欲發展全功能且可靠的IME結構,有若干挑戰需要解決,因為IME裝置的製造需要整合不同的處理條件、網版印刷、組件總成、熱成形、修整、及射出模製。這些步驟之各者的材料性質及處理條件與參數可進一步影響IME裝置在不同階段的性能。
例如,欲達成堆疊之優越的熱成形性能;所有油墨(圖形油墨層及電子油墨層)及基材需要高度的相互相容並具有類似的熱穩定性及模數性質。進一步地,油墨及基材之此類相互相容性及熱穩定性明顯有助於射出模製程序的成功,該程序主宰此類IME結構的總體穩定性及可靠度。
因此,下列問題與用於在IME組件之製造中使用的組成物有關:
網版印刷及乾燥:
電子油墨材料的關鍵要求之一係其等之網版印刷適性。例如,受良好定義的寬度、厚度、及多孔性控制的導電跡線之網版印刷對於構成用以建構電路系統、觸控開關、照明裝置、及其他類似裝置的高性能互連極為重要。類似地,均勻、無針孔、薄絕緣或包封膜的印刷對於構成常作為交越介電質的多層電路系統係重要的。沉積物結構的變動可顯著地影響IME的電氣功能及類似的結構性能,從而將增加製造期間的廢品率。類似地,導電及不導電黏著劑、封裝材料的精確施配、噴流、板印刷、澆鑄係將電子組件組裝至此類互連結構上所需者。
控制這些配方的流變性及黏度係最重要的特徵之一,並承擔沉積此類無缺陷導電跡線及不導電層的責任。這些網版印刷材料之有效率的乾燥及固化將係最小化熱成形及射出模製程序期間的缺陷之關鍵,從而將增加總體IME程序的產量。此外,任何印刷及乾燥缺陷亦可各別地影響3D結構電子或IME部件的電氣及可靠度性能。
具有適當且相容的化學性質之配方最佳化將係達成快速且完整的乾燥,且在印刷的同時具有較長的網版壽命,以及在射出模製期間提供其他功能要求(諸如導電性、拉伸性、及穩定性)之所欲。較長的網版壽命連同這些組成物的儲存穩定性對於產業適用性及可製造性係重要的。
相容性:
介電及導電材料的相互相容性連同與不同可撓性聚合物基材、裝飾用油墨、黏著劑、封裝材料、及射出模製樹脂的相容性係對於IME及類似結構之製造最重要的態樣之另一者。最大多數的情況下,這些材料的化學功能承擔相容性的責任,而完美匹配係用於製造強健且高績效的IME及類似結構的關鍵,然而,不相容的材料將得出有缺陷且不可靠的電子裝置。不相容的材料組合產生若干錯誤(諸如,在其上沉積另一新層之下方層的蝕刻、溶解、及脫層)。
電氣性質:
導電電子材料應具有所欲的導電性,以構成具備切換、照明、及觸控功能的電子裝置。進一步地,較高導電性對於結構的構成係所欲的,那些結構能夠運載高電流以用於執行無線信號處理、藍牙連接、及超高頻感測功能。按照用於製造IME及類似結構的首選可撓性基材之大多數的穩定性臨限,嚴格地要求於低於150℃下處理此類導電電子材料。此類導電材料亦需要在無顯著導電性變更的情況下於熱成形程序前後維持電氣路徑。亦將係重要的是針對高電流電氣裝置的有效絕緣控制介電性質。此外,此類導電體及介電質應具有足夠的熱穩定性以耐受射出模製處理條件。欲平衡電氣性質及其他功能要求(諸如熱成形性及射出模製穩定性),需要配製高性能導電及不導電聚合物複合物。
電子組件之總成:
組裝電子組件(諸如被動元件、LED)的典型選擇將係使用導電及不導電黏著劑,其等亦需要耐受熱成形及射出模製程序步驟。亦揭示導電及不導電黏著劑組成物,其等可經模板印刷或施配以用於組裝被動元件、LED、QFP、QFN、及類似的其他組件。
熱成形性:
欲構成IME及類似結構,電子材料必須沉積在可撓性聚合物基材上以藉由網版印刷建立2D印刷電子結構,並接著藉由熱成形程序轉化成3D形式。各種基材上之功能材料的熱成形程序經開放以便以3D形式建立新式設計、圖案,其在使用傳統印刷電路板技術的情況下將係不可行的。其係在其中利用熱以軟化基材達高於其玻璃轉移溫度/軟化溫度之程序,且此溫度隨不同基材而變化。在熱成形程序期間,亦在軟化的塑膠上施加高真空或壓力並給定特定大小及形狀。若干其他處理條件(諸如,熱成形程序的時間及溫度、工具設計(亦即,工具的深度或高度)、真空壓力等)需經最佳化以取得極良好的3D部件。挑戰將係設計可經網版印刷之高性能聚合物複合物,且網版印刷跡線的電氣性質(寬度及厚度)可依據熱成形應變及程序條件進行可預測性控制。
此外,熱成形前後的美感外觀、熱成形前後對上述基材之極良好的黏合性(亦即,在熱成形上不應發生油墨脫層)、尤其在熱成形期間與不同油墨(諸如,用於多層複雜結構的介電質)的相互相容性(亦即,堆疊相容性)、可撓性及伸長率使得其等在熱成形期間不顯示裂痕(亦即,熱成形期間的材料性質之行為)等。此外,若干其他美感缺陷(諸如,應可避免電子電路系統的印痕(鬼影))常會形成,導因於導電油墨及介電油墨連同基材或以圖形油墨塗佈的基材之不相容性,結合未適當選擇設計參數、熱成形處理條件、及模具選擇。
射出模製期間的穩定性:
經網版印刷及熱成形的可撓性電子結構係經射出模製以提供結構穩定性、剛性、及可靠度要求。各種樹脂(諸如,PC、ABS、ABS-PC摻合物、聚酯、PP、及TPU)係基於IME及類似結構之性能要求而使用。較高的處理溫度及射出壓力對於網版印刷電路系統非常嚴苛,該等電路系統需要直接面對熱射出模製樹脂的流動。所以,針對電子材料的關鍵要求之一,其等之熱穩定性,以及與進入的射出模製樹脂之相容性及對下方基材之高溫黏附性以對抗任何結構變形及損壞。很多情況下,射出模製期間之網版印刷特徵的此類變形及損壞係稱為「油墨洗落(ink wash-off)」。油墨洗落係可降低IME裝置之產出量的嚴重因素。此外,射出模製前後的電阻變化亦應係最小。電路系統連同材料組成物的設計係避免射出模製期間之油墨洗落的關鍵。
可靠度:
典型的IME裝置需要通過若干環境測試(諸如,85℃/85 RH、熱老化、熱循環、光照測試等)。IME及類似結構的可靠度最終取決於所有上述討論因素的準確度及所有材料、基材、及組件的相容性。需要淵博的知識及迭代來選擇不同的相容原料,以配製及最佳化高度相容的電子材料。適當的無機填料、聚合樹脂、溶劑、及功能添加劑之比率的選擇及最佳化對於最佳化用於製造IME及類似結構之此類電子組成物係重要的。
本發明試圖解決與先前技術相關聯的至少一些問題或至少為其提供商業上可接受的替代性解決方案。
在一第一態樣中,本發明提供一種用於在模內電子(IME)組件之製造中使用的組成物,該組成物含有黏合劑,該黏合劑包含:
交聯劑,其包含三聚氰胺甲醛;
熱塑性樹脂,其包含羥基基團;及
溶劑。
除非清楚指示相反情況,否則如本文中所定義的各態樣或實施例可與任何其他(多個)態樣組合。具體地,指示為較佳或有利的任何特徵可與指示為較佳或有利的任何其他特徵組合。
令人驚異地,本發明人發現,該組成物特別適於使用在IME組件的製造中(例如,作為導電油墨或介電油墨),並可導致所製造的IME組件與習知的IME組件相比具有用於電子應用之優越的強健性、環境耐久性/耐用性、機械可撓性、及改善的使用壽命。
如下文更詳細討論者,該組成物可包含固體粒子(諸如,導電粒子及不導電粒子)。該黏合劑用以將該組成物的這些成分「黏合(bind)」在一起。當該組成物包含固體粒子時,則該黏合劑可與任何無可避免的雜質一起形成該組成物的餘料。當該組成物不含固體粒子時,則該黏合劑與任何無可避免的雜質可一起構成整個組成物。
如本文中所使用,用語「三聚氰胺甲醛(melamine formaldehyde)」可含括具有三聚氰胺環之樹脂,該等三聚氰胺環係以衍生自兩單體、三聚氰胺、及甲醛的縮合產物之多個羥基基團封端。三聚氰胺甲醛有時係稱為「三聚氰胺甲醛樹脂」、「三聚氰胺樹脂」、或簡稱為「三聚氰胺」。
如本文中所使用,用語「熱塑性樹脂(thermoplastic resin)」可含括塑膠聚合物材料,其在一特定升高溫度下變為易彎或可模塑的,且一經冷卻即固化。
如本文中所使用,用語「組件(component)」可含括例如電子組件的一部分或整個電子組件。
在典型的IME製造方法期間,將組成物(例如,導電油墨或介電油墨)印刷在可熱成形基材上。在熱成形之前,一般接著在至多150℃(例如,從50至120℃)的升高溫度下使組成物持續乾燥一段時間,以從組成物移除溶劑。在不受理論束縛的情況下,咸認為一旦例如使用此類典型的乾燥溫度及時間加熱本發明的組成物,三聚氰胺樹脂可與熱塑性樹脂的羥基基團起反應以形成「氮-碳-氧」聯結聚合物網路。
有利地,一旦在此類條件下進行乾燥,本發明之黏合劑可展現兩個相牴觸的性質。在IME裝置的正規操作溫度(例如,從約-20℃至+50℃)下,黏合劑可表現如熱固物,其顯示非凡的強度、內聚力、及層間黏附性、以及合理的拉伸能力。然而,在熱成形期間所用的較高溫度下,黏合劑可轉換成熱塑性材料,其可輕易地熱成形為3D結構而不會頸縮、斷裂、或脫層。
在不受理論束縛的情況下,咸認為這些相牴觸的性質可歸因於使用包含具有含羥基基團樹脂之三聚氰胺甲醛的交聯劑。具體而言,咸認為此熱塑性質及熱固性質的有利平衡係藉由部分(亦即,不完全)交聯之發生而達成。推測此係因為與習知IME方法中所用的交聯劑相比,三聚氰胺甲醛係相對「慢」的交聯劑,且由於典型IME製造方法中所用的乾燥溫度及時間而導致僅部分交聯。
在典型的IME製造程序期間,使用多個可熱成形組成物以便形成最終組件(例如,導電油墨、介電油墨、導電黏著劑、不導電黏著劑、封裝材料、障壁層等)。有利地,當將本發明的組成物用作共用平台時,這些材料的相容性可獲得改善。雖然這些材料之各者可當然包括不同物種(例如,導電粒子、不導電粒子等),使用常見的黏合劑可確保材料之間(例如油墨之間)的相容性。結果,可減少例如不同材料層之脫層問題。
組成物可與習知以圖形油墨塗佈的基材相容,其係用於建構高功能IME結構及裝置的所欲準則。
使用該組成物建構之可撓性電子電路可顯示優越的電氣性能。
該等組成物可與一般用在IME製造方法中的射出模製樹脂高度相容。
與習知IME方法中所用的組成物相比,使用該組成物亦可減少油墨洗出的發生。
使用該等組成物製備的熱成形及射出模製結構顯示優越的環境可靠度特徵,且因此特別適於用於汽車、消費性電子產品、及白色家電應用的IME應用。
有利地,該組成物在正規儲存及環境溫度下可係穩定的。再次,在不受理論束縛的情況下,咸認為此係導因於在此類溫度下實質缺少三聚氰胺甲醛的任何交聯。
三聚氰胺甲醛較佳地包含六甲氧基甲基三聚氰胺。六甲氧基甲基三聚氰胺係特別合適的交聯劑。此外,六甲氧基甲基三聚氰胺可溶於除了脂族烴以外之大多數常見的有機溶劑中。
合適的市售三聚氰胺甲醛樹脂包括例如Maprenal BF 891/77SNB、Maprenal MF 600/55BIB、Maprenal MF 650/55IB、Maprenal MF 800/55IB、CYMEL 370、CYMEL 373、及CYMEL 380。Maprenal MF 600/55BIB係亞胺基型高度反應性異丁烯化三聚氰胺甲醛樹脂。
交聯劑有利地可進一步包含異氰酸酯、及/或聚異氰酸酯、及/或封閉型聚異氰酸酯。此類物種可增加習知IME製造方法中所用的乾燥條件下之交聯程度。當組成物必須具有增加的「熱固」性質時,此可係有利的。「封閉型(blocked)」或「掩蔽型(masked)」異氰酸酯可含括含有受保護之異氰酸酯的異氰酸酯。異氰酸酯官能基一般係透過使用封鎖劑來掩蔽,所製成的化合物在室溫下看來似乎呈惰性,但在升高溫度下產出反應性異氰酸酯官能性。
合適的異氰酸酯、聚異氰酸酯、及封閉型聚異氰酸酯包括例如甲苯二異氰酸酯(TDI)、伸己基二異氰酸酯(HDI)、異佛爾酮二異氰酸酯(IPDI)、Desmodur BL 3175A、Desmodur BL 3272 MPA、Desmodur BL 1100/1、及Vestanat B 1358A(來自Evonik)。這些可單獨使用或與三聚氰胺甲醛樹脂組合使用。VESTANAT B 1358A包含基於異佛爾酮二異氰酸酯(IPDI)之甲基-醚-酮-肟(MEKO)封閉型環脂族聚異氰酸酯。
熱塑性樹脂較佳地包含聚胺甲酸酯樹脂、聚酯樹脂、聚丙烯酸酯樹脂、聚乙烯酯樹脂、苯氧基樹脂、及酮樹脂中之一或多者(亦即,含有聚胺甲酸酯樹脂、聚酯樹脂、聚丙烯酸酯樹脂、聚乙烯酯樹脂、苯氧基樹脂、及/或酮樹脂的羥基基團)。此類樹脂特別適於使用在本發明中,並在典型IME製造方法的乾燥條件下與三聚氰胺甲醛起反應,以提供所欲的交聯程度。
這些熱塑性樹脂可單獨使用或與其他熱塑性樹脂組合使用。
聚胺甲酸酯樹脂可包含例如羥基封端多元醇、羥基封端聚(氧化乙烯)、羥基封端聚(二甲基矽氧烷)、或乙氧基化三羥甲基丙烷與甲基芐基異氰酸酯、(三甲基甲矽烷基)異氰酸酯、1-萘基異氰酸酯、3-(三乙氧基甲矽烷基)丙基異氰酸酯、苯基異氰酸酯、丙烯基異氰酸酯、異氰酸丁酯、異氰酸己酯、環己基異氰酸酯、異氰呋喃甲酯、異佛爾酮二異氰酸酯、六亞甲基二異氰酸酯、間苯二亞甲基二異氰酸酯、1,4-伸環己基二異氰酸酯、聚(丙二醇)、或甲伸苯基2,4-二異氰酸酯的反應產物。聚胺甲酸酯樹脂可包含熱塑性聚胺甲酸酯之一者或混合物(諸如,聚胺甲酸酯的Pearlstick系列,如Pearlstick 5701、Pearlstick 5703、Pearlstick 5707;聚胺甲酸酯的Estane系列,如ESTANE FS M92B4P;聚胺甲酸酯的Desmocoll系列,如Desmocoll 540/4、Desmocoll 400;聚胺甲酸酯的Desmomelt系列,如Desmomelt 540/3、Desmomelt 540/4)。苯氧基樹脂較佳地係熱塑性雙酚A基聚醚,其含有聚酯、或聚丙烯酸酯、或聚胺甲酸酯化合物。含有聚酯、或聚丙烯酸酯、或聚胺甲酸酯之合適的苯氧基樹脂之實例包括可以下列商標名稱購得之苯氧基樹脂:LEN-HB、PKHW-35、PKHH、PKHA、PKHM-301、及PKHS-40。聚酯樹脂、聚丙烯酸酯樹脂、及/或聚胺甲酸酯樹脂可含有多元醇、羥基、胺、羧酸、醯胺、及脂族鏈中之一或多者。苯氧基樹脂含有聚酯、或聚丙烯酸酯、或聚胺甲酸酯、或聚醚、或聚醯胺主鏈。
熱塑性樹脂較佳地包含聚胺甲酸酯樹脂、聚酯樹脂、及苯氧基樹脂。更佳地,熱塑性樹脂包含:
基於該熱塑性樹脂的總重量之從20至60 wt.%之聚胺甲酸酯樹脂,較佳地35至47 wt.%之聚胺甲酸酯樹脂;
從5至30 wt.%之聚酯樹脂,較佳地13至19 wt.%之聚酯樹脂;及
從20至60 wt.%之苯氧基樹脂,較佳地34至51 wt.%之苯氧基樹脂。
此類熱塑性樹脂(特別係以上文所列舉的量)係特別適於得到所欲之與三聚氰胺甲醛交聯的程度。(多個)聚胺甲酸酯樹脂的存在(特別係以所列舉的量)可提供具有所欲可撓性位準的乾燥組成物。(多個)聚酯樹脂的存在(特別係以所列舉的量)可提供具有所欲可撓性程度的乾燥組成物,且亦促進至基材之黏附性。(多個)苯氧基樹脂的存在(特別係以所列舉的量)可促進至基材之黏附性。這三種樹脂之組合(特別係以所列舉的量)可提供具有高度可撓性及至基材之高度黏附性的有利組合。
較佳地,熱塑性樹脂:
包含均聚物、及共聚物、及/或三聚物;及/或
具有小於100℃的玻璃轉移溫度;及/或
具有從1000至100000 g/莫耳之重量平均分子量;及/或
具有小於100℃的軟化點;及/或
具有大於20 mgKOH/g的羥基含量(OH數)。
在一較佳實施例中,組成物包含:
基於交聯劑及熱塑性樹脂之總量之從1至40 wt%的交聯劑,較佳地7至24 wt.%的交聯劑;及
從60至99 wt.%的該熱塑性樹脂,較佳地76至93 wt.%的該熱塑性樹脂
。此類量可幫助在習知IME製造方法的乾燥條件下提供所欲的交聯位準。
溶劑較佳地包含二醇醚乙酸酯、二醇醚、酯、酮、醇、及烴中之一或多者。此類溶劑可特別適於使用在本發明中。此類溶劑可單獨使用或組合使用。此類溶劑可特別適於溶解熱塑性樹脂及/或交聯劑,且特別可與基材及組成物中之任何功能填料及/或添加劑相容。此類溶劑可具有極性、溶解力性質(Hansen溶解度參數)、與基材之相容性、毒性、及其他物理性質(諸如沸點及閃點)的有利組合。此類溶劑可改善組成物之儲存穩定性、乾燥曲線、處理期間的乾燥穩定性(例如,在網版印刷期間於網版上)、及與基材及其他印刷油墨層(諸如圖形油墨或電子油墨層)的反應性。此類溶劑可得出均質組成物,其一經儲存即係穩定的,且亦滿足性能要求。溶劑之非限制性實例包括甲醇、乙醇、2-丙醇、苯甲醇、乙二醇、丙二醇、二丙二醇、1,3-丁二醇、2,5-二甲基-2,5-己二醇、乙二醇甲基醚、乙二醇單丁基醚、二乙二醇單正丁基醚、丙二醇正丙基醚、二丙二醇甲基醚、松脂醇、丁基卡必醇、丁基卡必醇乙酸酯、二醇醚乙酸酯、2-(2-乙氧乙氧)乙酸乙酯、二丙二醇甲基醚乙酸酯、丙二醇單甲基醚乙酸酯、2-丁氧基乙酸乙酯、卡必醇乙酸酯、碳酸丙烯酯丁基卡必醇、丁基賽路蘇、庚烷、己烷、環已烷、苯、二甲苯、基里尼、二元酯、異佛爾酮、C11-酮、及甲苯。
較佳地,溶劑包含:
基於該溶劑之總重量之至多95 wt%的二醇醚乙酸酯,較佳地至多85 wt.%的二醇醚乙酸酯;及/或
至多95 wt%的二醇醚,較佳地至多85 wt.%的二醇醚(例如1至85 wt.%);及/或
至多15%的酯,較佳地至多5 wt.%的酯(例如1至5 wt/%);及/或
至多40 wt%的酮,較佳地至多32 wt.%的酮(例如1至32 wt.%);及/或
至多80 wt%的醇,較佳地至多70 wt.%的醇(例如1至70 wt.%);及/或
至多30 wt%的烴,較佳地至多22 wt.%的烴(例如1至22 wt.%)。
此類量可特別適於提供上述優點。
黏合劑較佳地可進一步包含:
熱固性樹脂,其較佳地包含丙烯酸樹脂及環氧樹脂中之一或兩者;及
固化催化劑,其用於固化該熱固性樹脂,較佳地用於熱固化該熱固性樹脂及/或用於UV固化該熱固性樹脂。
熱固性樹脂及固化催化劑之存在可用以形成三維熱固性網路。當乾燥組成物必須具有更多「熱固」性質時,此可係有利的。熱固性樹脂較佳地包含丙烯酸樹脂及環氧樹脂中之一或兩者,並可使用熱固化劑及/或UV固化劑固化。
熱固性樹脂可含有例如聚酯、或聚丙烯酸酯、或聚醚、或聚胺甲酸酯、或聚醯胺主鏈。熱固性樹脂可含有具有環氧、聚胺甲酸酯、聚酯、聚醚、及丙烯酸主鏈之單體、二聚體、三聚體、四聚體、五聚體、或六聚體、及寡聚體的不同組合。
環氧樹脂的實例包括雙酚A環氧樹脂、4-乙烯基-1-環己烯、1,2-環氧化物、3,4-環氧環己基甲基-3',4'-環氧環己烯羧酸酯、1,4-丁二醇二縮水甘油醚、三羥甲丙烷三環氧丙醚、三環氧丙基異氰尿酸酯、環氧矽氧烷、環氧矽烷、及苯酚酚醛清漆環氧樹脂。環氧樹脂可包含環氧樹脂(諸如EPON 862、DYCK-CH、JER 828、1,4-丁二醇二縮水甘油醚、1,6-己二醇二縮水甘油醚(DER 731)、鄰甲苯酚縮水甘油醚(DER 723)、及C12至C14烷基縮水甘油醚(DER 721))之一者或混合物。一或多個硬化劑可存在,且此類硬化劑可係胺(諸如,丁胺、N,N-二乙基乙醇胺、或乙醇胺)、酸(諸如,油酸、己二酸、或戊二酸)、或酐(諸如,琥珀酸酐、鄰苯二甲酸酐、及馬來酐)。亦可使用環氧丙烯酸酯。(甲基)丙烯酸酯係藉由1,4-丁二醇二縮水甘油醚、雙酚A環氧樹脂、4-乙烯基-1-環己烯、1,2-環氧化物、3,4-環氧環己基甲基-3',4'-環氧環己烯羧酸酯、三羥甲丙烷三環氧丙醚、三環氧丙基異氰尿酸酯、環氧矽氧烷、環氧矽烷、苯酚酚醛清漆環氧樹脂與甲基丙烯酸的開環反應而製成。舉實例而言而非限制地,環氧丙烯酸酯可包含基於環氧主鏈之(甲基)丙烯酸酯中之一或多者(諸如,Ebecryl 3503、Ebecryl 3201、Photomer 3005、Photomer 3316、Ebecryl 3411、及Ebecryl 3500)。亦可使用聚胺甲酸酯丙烯酸酯(諸如,胺甲酸酯丙烯酸酯、甲基丙烯酸酯封端聚胺甲酸酯、及具有羥基甲基丙烯酸乙酯之改質異氰酸酯)。舉實例而言而非限制地,胺甲酸酯丙烯酸酯可包含基於胺甲酸酯主鏈之(甲基)丙烯酸酯中之一或多者(諸如,SUO2371、SUO-300、SUO-7620、Photomer 6891、SUO S3000、Ebecryl 8413、Ebecryl 230、Ebecryl 4833、Ebecryl 8411、Ebecryl 270、Ebecryl 8804、及Photomer-6628)。亦可使用聚酯丙烯酸酯(諸如,脂肪酸改質季戊四醇丙烯酸酯、三羥甲基丙烷三丙烯酸酯、及甲基丙烯酸酯化單醣)。亦可使用聚醚丙烯酸酯(諸如,聚(乙二醇)甲基醚丙烯酸酯、聚(乙二醇)甲基丙烯酸酯、聚(乙二醇)二甲基丙烯酸酯)。舉實例而言而非限制地,聚酯丙烯酸酯可包含基於聚酯主鏈之(甲基)丙烯酸酯中之一或多者(諸如,Photomer- 4006、Ebecryl 450、Photomer 5429、及Ebecryl 812)。單體丙烯酸酯之非限制性實例包括但不限於甲基丙烯酸、3-(三甲氧基矽烷)甲基丙烯酸丙酯、丙烯酸異冰片酯、丙烯酸四氫呋喃酯、聚(乙二醇)甲基醚丙烯酸酯、甲基丙烯酸羥丙酯、甲基丙烯酸二甲胺乙酯、丙烯酸2-乙基己酯、丙烯酸丁酯、異辛基丙烯酸酯、甲基丙烯酸甲酯、丙烯酸月桂酯、丙烯酸十二烷基酯、及丙烯酸四氫呋喃甲酯。二聚體丙烯酸酯之非限制性實例包括二聚體甲基丙烯酸酯(諸如,聚(乙二醇)二甲基丙烯酸酯、1,6-雙(丙烯醯氧基)己烷、雙酚A-乙氧基化二甲基丙烯酸酯、及季戊二醇二丙烯酸酯、1,3-二丙烯酸丁二醇酯)。
三聚體丙烯酸酯之非限制性實例包括三聚體甲基丙烯酸酯(諸如,三羥甲基丙烷三丙烯酸酯、季戊四醇三丙烯酸酯、及1,3,5-三丙烯醯基六氫-1,3,5-三嗪)。四聚體丙烯酸酯之非限制性實例包括季戊四醇四丙烯酸酯及二(三羥甲丙烷)四丙烯酸酯。
五聚體或六聚體丙烯酸酯之非限制性實例包括二季戊四醇五丙烯酸酯及二季戊四醇六丙烯酸酯。舉實例而言而非限制,矽氧烷丙烯酸酯可包含下列之一或多者:基於矽氧烷主鏈之(甲基)丙烯酸酯(諸如,BYK-UV3570、BYK-UV3575、BYK-UV3535、BYK-UV3530、BYK-UV3505、BYK-UV3500、Ebecryl 350、Ebecryl 1360、及SUO-S3000)。舉實例而言而非限制,脂族丙烯酸酯可包含下列之一或多者:基於烴主鏈之(甲基)丙烯酸酯(諸如,Ebecryl 1300、SAP-M3905、Ebecryl 525、及SAP-7700HT40)。
黏合劑較佳地進一步包含一或多個功能添加劑,其(等)較佳地選自界面活性劑、流變改質劑、分散劑、消泡劑、去膠黏劑、助滑添加劑、抗垂流劑、整平劑、表面活性劑、表面張力減少劑、助黏劑、抗結皮劑、消光劑、著色劑、染料、顏料、及濕潤劑中之一或多者。消泡劑可從黏合劑移除發泡體,且去膠黏劑可從黏合劑移除黏性。界面活性劑可包含陰離子性、陽離子性、或非離子性界面活性劑。非限制性實例包括可以下列商標名稱購得之界面活性劑:SPAN-80、SPAN-20、Tween-80、Triton-X-100、Sorbitan、IGEPAL-CA-630、Nonidet P-40、Cetyl alcohol、FS-3100、FS-2800、FS-2900。FS-230、FS-30、BYK-UV3500/UV3505/077/UV3530、FS-34、Modaflow 2100、Omnistab LS 292、Omnivad-1116、及Additol LED 01。流變改質劑係控制配方之流變特性的有機或無機添加劑。這些可單獨使用或在混合物中使用。合適的流變改質劑之實例包括但不限於可以下列商標名稱購得者:THIXIN-R、Crayvallac-Super、Brij 35、58、L4、O20、S100、93、C10、O10、L23、O10、S10、及S20。功能添加劑亦可係著色劑、染料、及顏料。著色劑、染料、及顏料之非限制性實例包括蒽醌染料、偶氮染料、吖啶染料、花青染料、重氮染料、硝基染料、亞硝基染料、苯醌染料、呫噸染料、茀染料、及玫瑰紅染料。抗氧化劑及抑制劑之非限制性實例包括2,6-二-三級丁-4-甲苯酚、2,6-二-三級丁-對甲苯酚、丁羥甲苯、3,5-二-三級-4-丁羥甲苯、Omnistab IC、Omnistab In 515/ 516、氫醌、及吩噻嗪。
除了本文中所述之元素以外,將理解組成物及黏合劑可包含無可避免的雜質。此類無可避免的雜質(若存在的話)一般係以下列量存在:組成物或黏合劑的至多1 wt.%、更一般地至多0.5 wt.%、甚至更一般地至多0.1 wt.%、甚至更一般地至多0.05 wt.%。
在一較佳實施例中,黏合劑包含:
從0.5至12 wt.%的該交聯劑,較佳地從1.5至7.7 wt.%的該交聯劑;
從10至40 wt.%的該熱塑性樹脂,較佳地從11至30.4 wt.%的該熱塑性樹脂;及
從40至85 wt.%的溶劑,較佳地從46.7至78.8 wt.%的溶劑;
可選地:
從0.1至30 wt.%的熱固性樹脂及從0.1至3 wt.%之用於固化該熱固性樹脂的固化催化劑,較佳地從1至10 wt.%的熱固性樹脂及從0.1至1 wt.%之用於固化該熱固性樹脂的固化催化劑;及/或
從0.1至20 wt%的功能添加劑,較佳地1.7至17 wt.%的功能添加劑。
此種黏合劑特別適於提供具有上述優點之組成物。
較佳地,黏合劑包含低位準的:
離子,更佳地實質上無離子;及/或
游離鹵素,更佳地實質上無游離鹵素;及/或
蓄意添加的鹵素,更佳地無蓄意添加的鹵素。
在一較佳實施例中,組成物進一步包含導電粒子(亦即,導電粒子)。此可能夠使組成物用作例如導電油墨或導電黏著劑。
導電粒子較佳地包含金屬粒子,更佳地包含選自銀粒子、銅粒子、黃銅粒子、鎳粒子、金粒子、鉑粒子、鈀粒子、金屬合金粒子、塗銀銅粒子、塗銀黃銅粒子、銀-鎳合金粒子、及銀-銅合金粒子中之一或多者。此類粒子特別適於使用在導電油墨或導電黏著劑中。
替代地或除此以外,導電粒子較佳地包含非金屬粒子,更佳地包含碳粒子,較佳地係選自石墨粒子、石墨片、碳黑粒子、石墨烯粒子、及奈米碳管中之一或多者。此類粒子特別適於使用在導電油墨或導電黏著劑中。使用石墨烯可改善組成物之機械、可撓性、及障壁性質。石墨烯之獨特的機械、可撓性、及障壁性質之組合可高度有利於可撓性、機械強健、耐磨、及抗腐蝕性碳層的製備,從而增強IME及類似結構的使用壽命。額外地,將石墨烯併入金屬油墨可實現具有適中導電性之高績效、低成本的金屬油墨之開發。
導電粒子較佳地具有從0.5至30 µm、更佳地從1至20 µm、甚至更佳地從1.25至7 µm的平均粒徑(d50)。粒徑可例如使用SEM、TEM、雷射散射粒徑分析儀、或動態光散射法來判定。此一粒徑分布可為目標黏度及電氣性質提供有利的填積密度、粒子間相互作用。特定的平均粒徑可取決於最終應用(例如,細線印刷、可熱成形應用、智慧型紡織品等),並取決於處理技術。
導電粒子較佳地具有從1至5 g/cc,更佳地從1.5至4 g/cc的敲緊密度。敲緊密度可使用習知的敲緊密度測試器來判定。敲緊密度越高,則用於導電性的展透閾值越高。較低的敲緊密度可使處理難度增加,並可不利地影響組成物的黏度及流變性。
導電粒子較佳地具有從0.3至2.1 m
2/g或從0.5至5 m
2/g的表面積。此可使該等導電粒子更適於電子應用。其亦可幫助提供具有有利的流變性及黏度之組成物。表面積越大,則黏度越大。因此,當將組成物用作導電黏著劑時,較大的表面積可更有利,而當將組成物用作導電油墨時,較小的表面積可更有利。表面積可例如使用氣體吸附BET法來判定。
導電粒子較佳地具有從0.06至1.3 wt.%或從0.01至3 wt.%的有機含量。有機物可充當有機塗層或封端劑。有機塗層可改變鏈長度,並可包含飽和或不飽和脂肪酸或酯、或甘油基衍生物、或胺、或醯胺、或磷酸酯、或硫醇。有機塗層可幫助導電粒子與聚合物相互作用,以便維持單相。有機含量可例如藉由重力測量法來判定。填料粒子(金屬或金屬氧化物)上之有機含量的量係藉由熱處理(200至700℃)後的重量損失來計算。
導電粒子較佳地呈片、球體、不規則形狀粒子、奈米粉末、及奈米線中之一或多者的形式。更佳地,導電粒子係呈片的形式。與球體相比,片可更傾向於與黏合劑及相鄰粒子相互作用。這些特徵可幫助達成至基材的較佳黏附性,並提供用於導電性的展透閾值。
較佳地,導電粒子包含低位準的:
離子,更佳地實質上無離子;及/或
游離鹵素,更佳地實質上無游離鹵素;及/或
蓄意添加的鹵素,更佳地無蓄意添加的鹵素。
除了上述導電填料以外,組成物較佳地可進一步包含奈米大小的銀粒子或有機銀化合物(AgMOC,諸如新癸酸銀及二乙基己酸銀)。這些可進一步增強組成物之導電性。
導電填料可包含:
導電金屬奈米線(諸如,例如銀、銅、金、鈀、鉑、銀-銅合金、鎳、銅-鎳、塗銀銅、塗鎳銅);及/或
導電奈米碳管及奈米碳纖維(諸如,例如導電或半導電單壁奈米碳管、導電或半導電多壁奈米碳管、導電或半導電奈米碳纖維等);及/或
導電聚合物(諸如,例如聚苯胺、PEDOT:PSS、聚噻吩等);及/或
導電石墨烯片。
此類導電填料可特別適於製成透明導電膜、印刷式電阻加熱器、透明加熱器、及透明可撓性及電路元件。本發明亦提供使用此類導電填料以製造此類物體。
組成物較佳地包含:
從30至85 wt%的黏合劑,較佳地從40.1至80.9 wt.%的黏合劑;及
從15至70 wt%的導電粒子,較佳地從19.1至59.9 wt.%的導電粒子。
此類量可提供有利的導電性位準連同上述黏合劑的優點。
在一較佳實施例中,組成物包含:
從30至85 wt%的黏合劑,較佳地從40.1至80.9 wt.%的黏合劑;及
從15至70 wt%的導電粒子,較佳地從19.1至59.9 wt.%的導電粒子,
且其中該黏合劑包含:
從0.2至6 wt.%的交聯劑,較佳地從0.7至3.3 wt.%的交聯劑;
從1至7.5 wt.%的聚胺甲酸酯樹脂,較佳地從1.7至4.5 wt.%的聚胺甲酸酯樹脂;
從0.1至5.5 wt.%的聚酯樹脂,較佳地從0.7至1.8 wt.%的聚酯樹脂;
從1至7.5 wt.%的苯氧基樹脂,較佳地從2.5至6.6 wt.%的苯氧基樹脂;
從0至10 wt.%的熱固性樹脂,較佳地從0至5.7 wt.%的熱固性樹脂(例如,0.1至5.7 wt.%);
從0至1 wt.%的固化催化劑,較佳地從0至0.6 wt.%的固化催化劑(例如,0.1至0.6 wt.%);
從0.2至10 wt%的功能添加劑,較佳地從2.6至7.4 wt.%的功能添加劑;
從0至60 wt%的二醇醚乙酸酯,較佳地從4.3至43.2的二醇醚乙酸酯;
從0至40 wt%的二醇醚,較佳地從0至24.1 wt.%的二醇醚(例如,1至24.1 wt.%);
從0至5 wt.%的酯,較佳地從0至1.7 wt.%的酯(例如,0.1至1.7 wt.%);及
從0至30 wt%的酮,較佳地從0至20.5 wt.%的酮(例如,1至20.5 wt.%)。
在一較佳實施例中,組成物係呈導電油墨的形式。換言之,本發明提供包含本文所述之組成物的導電油墨。導電油墨可有利地用以製作電氣可撓性及可成形電路、互連件、附接組件與部件、通孔填充等。導電油墨亦可用於熱連接。導電油墨可展現適於使用例如網版、模版、凹版、及柔版技術印刷的黏度及流變性,以在各種聚合基材(諸如PC及PET)上製成電子互連電路系統。一旦經熱乾燥及/或固化,使用此類油墨製成的互連線、圖案形狀、及/或特徵(例如,跡線寬度、墊寬度等)可控制在> 100 µm,並擁有優越的表面電阻(當各種碳粒子僅用作導電填料時< 100 Ω/□/密耳,或者當各種金屬粒子及/或片用作導電填料時<100 mΩ/□/密耳),並具有適於製造可撓性電子電路的黏附性(按照ASTM標準>3B)。使用此類油墨製成的這些互連電路可擁有優越的可熱成形性,且在射出模製油墨洗出下係穩定的,且因此適於IME製造。
在一較佳實施例中,組成物係呈導電黏著劑的形式。換言之,本發明提供包含本文所述之組成物的導電黏著劑。導電黏著劑可展現適於用於組裝各種組件、封裝、及LED之印刷(網版及模版)、施配、噴流、及微施配技術的黏度及流變特性,以在各種聚合基材(諸如PC及PET)上互連由較早之前所揭示之導電油墨製成的電路。一旦經熱乾燥及/或固化,這些互連線及圖案形狀與特徵可控制在> 50 µm,並擁有優越的表面電阻(當各種碳粒子僅用作導電填料時< 100 Ω/□/密耳,或者當各種金屬粒子及/或片用作導電填料時<100 mΩ/□/密耳),並具有適於製造可撓性電子電路的黏附性(按照ASTM標準>3B)。使用此類導電黏著劑製成之組裝組件及封裝可顯示高機械穩定性,如晶粒抗剪結果所證明者。使用此類導電黏著劑製成的電路可擁有優越的可熱成形性,且在射出模製油墨洗出下可係穩定的,且因此適於IME製造。
在一較佳實施例中,組成物進一步包含不導電粒子。此類組成物可用以製作例如電氣可撓性及可成形電路、互連件、附接組件與部件、及通孔填充。此類組成物可用於機械及熱連接。
不導電粒子較佳地包含有機不導電粒子,較佳地選自下列之一或多者:纖維素、蠟(例如,來自BYK的Ceraflour 991、Ceraflour 929、及Ceraflour 920)、聚合物微粒子、不導電碳粒子、及石墨烯氧化物。
替代地或除此以外,不導電粒子較佳地包含無機不導電粒子,較佳地選自雲母、矽石(SiO
2)、發煙矽石、滑石、二氧化鈦(TiO
2)、氧化鋁、鈦酸鋇(BaTiO
3)、氧化鋅(ZnO)、及氮化硼(BN) 中之一或多者,可選地其中該等無機不導電粒子係次微米至微米大小(例如,從5至50000 nm,較佳地從10至30000 nm)。
有機不導電粒子可增加組成物的均質性,但與無機不導電粒子相比可具有較低的介電強度。無機不導電粒子可增加介電強度,但與有機不導電粒子相比可導致均質性減小。因此,可係較佳的是以官能基(諸如,例如羧酸、胺、或醇)官能化不導電粒子,以使其等能較佳地透過與聚合物系統相互作用而極良好地分散。有機塗層可改變鏈長度,並可包含飽和或不飽和脂肪酸或酯、或甘油基衍生物、或胺、或醯胺、或磷酸酯、或硫醇。此亦可幫助改善組成物之長期儲存穩定性。
不導電粒子較佳地展現從1至30 µm或者小於或等於10 µm的平均粒徑(d50)。極小粒徑分布之較高比率使黏度增加並使處理困難,而極大粒徑分布之較高分布的存在使黏度降低,產生崩移問題。
不導電粒子可呈片、及/或球體、及/或不規則形狀粒子的形式。較佳地,不導電粒子係呈片及/或不規則形狀粒子的形式。此係因為與球體相比,片及不規則形狀粒子可具有至基材之改善的黏附性,並可在熱成形程序期間減少脫層的傾向。
不導電粒子較佳地具有低離子含量,較佳地實質上零。
較佳地,不導電粒子包含低位準的:
離子,更佳地實質上無離子;及/或
游離鹵素,更佳地實質上無游離鹵素;及/或
蓄意添加的鹵素,更佳地無蓄意添加的鹵素。
組成物較佳地包含:
從0至50 wt.%的不導電粒子,較佳地從2至45 wt.%的不導電粒子;及
從50至100 wt.%的黏合劑,較佳地從55至98 wt.%的黏合劑。
此類量可提供有利的介電性質位準連同上述黏合劑的優點。
在一較佳實施例中,組成物包含:
從40至100 wt.%的黏合劑,較佳地從50至98 wt.%的黏合劑;及
從0至60 wt.%的不導電粒子,較佳地從2至50 wt.%的不導電粒子,
且該黏合劑包含:
從0.5至10 wt%的交聯劑,較佳地從1.9至6.1 wt.%的交聯劑;
從2至12 wt%的聚胺甲酸酯樹脂,較佳地從4.8至8.4 wt.%的聚胺甲酸酯樹脂;
從0.5至10 wt.%的聚酯樹脂,較佳地從1.9至5.3 wt.%的聚酯樹脂;
從2至18 wt%之苯氧基樹脂,較佳地從4.5至12.4 wt.%之苯氧基樹脂;
從0至30 wt.%的熱固性樹脂,較佳地從0至19.6 wt.%的熱固性樹脂(例如,1至19.6 wt.%);
從0至3 wt.%的固化催化劑,較佳地從0至2 wt.%的固化催化劑(例如,0.1至2 wt.%);
從0.3至17 wt.%的功能添加劑,較佳地1.4至12.5 wt.%的功能添加劑;
從0至60 wt.%的二醇醚乙酸酯,較佳地從4.9至41.7 wt.%的二醇醚乙酸酯;
從0至60 wt.%的二醇醚,較佳地從0至43.8 wt.%的二醇醚(例如,1至43.8 wt.%);
從0至30 wt.%的酮,較佳地從0至19.9 wt.%的酮(例如,1至19.9 wt.%);
從0至50 wt.%的醇,較佳地從0至35.5 wt.%的醇(例如,1至35.5 wt.%);及
從0至20 wt%的烴,較佳地從0至13.3 wt.%的烴(例如,1至13.3 wt.%)。
在一較佳實施例中,組成物係呈介電油墨的形式。換言之,本發明提供包含本文所述之組成物的介電油墨。
在一較佳實施例中,組成物係呈不導電黏著劑的形式。換言之,本發明提供包含本文所述之組成物的不導電油墨。
在一較佳實施例中,組成物係呈封裝材料的形式。換言之,本發明提供包含本文所述之組成物的封裝材料。
一旦經乾燥/固化,介電油墨、不導電黏著劑、及封裝材料的黏合劑可擁有優越的介電性質,並可係高度可撓性及中度拉伸性,與其他油墨材料(例如銀及碳)及基材具有優異的黏附性及相容性,並具有優越的耐候性(濕氣、氣體、及化學品)。介電油墨、不導電黏著劑、及封裝材料可擁有優越的可熱成形性,且在射出模製油墨洗出下可係穩定的,因此適於IME製造。介電油墨、不導電黏著劑、及封裝材料的黏度及流變性可適於使用例如網版、模版、凹版、或柔版技術之印刷;噴塗;施配;及噴流技術,以製成用於保護各種聚合基材(諸如PC及PET)上之導電互連電路系統的絕緣層。一旦經熱乾燥或固化,介電塗層的厚度可控制在> 1 µm,並可擁有優越的介電崩潰電壓(>100 V),並可具有適於製造可撓性電子電路的黏附性(按照ASTM標準> 3B)。封裝塗層可為導電電路系統提供保護,使其等免受環境(諸如濕氣及氣體)影響。
組成物較佳地可進一步包含著色劑、及/或染料、及/或顏料,並可呈圖形油墨的形式。換言之,本發明提供包含本文所述之組成物的圖形油墨。染料及/或顏料可形成上文所討論之功能添加劑的部分。
在一進一步的態樣中,本發明提供一種製造本文所述之組成物之方法,該方法包含:提供溶劑;提供具有羥基基團之熱塑性樹脂;在從50至100℃、較佳地從70至100℃的溫度下於該溶劑中溶解該熱塑性樹脂;使該溶液冷卻至室溫;可選地將下列之一或多者添加至該經冷卻溶液:功能添加劑、熱固性樹脂、用於固化該熱固性樹脂之固化催化劑、導電粒子、及不導電粒子。
第一態樣的優點及較佳特徵同樣適用於此態樣。
在一進一步的態樣中,本發明提供一種製造模內電子(IME)組件之方法,該方法包含:製備一坯料;及熱成形該坯料,其中製備該坯料包含在一可熱成形基材上形成一或多個結構,各結構係藉由包含下列之一方法形成:將如本文所述之組成物設置在一可熱成形基材上;及在從20至150℃之一溫度下使該組成物乾燥從1至30分鐘。
如本文中所使用,用語「熱成形(thermoforming)」可含括一種製造程序,其中塑膠片材係經加熱達易彎的成形溫度,在模具中經成形為特定形狀,並經修整以創造出可用的產品。片材一般係在烘箱中加熱達足夠高的溫度,該溫度允許將片材拉伸至模具之中或之上並冷卻為成品形狀。其簡化版本係真空成形。熱成形期間可施加壓力。熱成形可包含高壓熱成形。
組成物的乾燥係在從20至150℃(較佳地從30至130℃)的溫度下實行從0.5至60分鐘(較佳地從1至30分鐘)。
較佳地,形成二或更多個結構。使用如本文所揭示之組成物確保一或多個結構(例如,多層堆疊中之一或多層)彼此相容。
一或多個結構較佳地選自導電層、導線、介電層、封裝材料層、圖形層、及障壁層。
一或多個結構較佳地包含多層堆疊。
一或多個結構較佳地包含印刷電路板。
設置組成物較佳地包含印刷組成物,更佳地包含網版印刷組成物。
基材較佳地包含聚碳酸酯(PC)及/或聚對苯二甲酸乙二酯(PET)。如本文所述之組成物與此類材料相容,並與此類材料形成強黏附性。此類材料亦展現有利的熱成形性質。
熱成形較佳地係在從140℃至210℃的溫度下實行。此一溫度特別適於熱成形,且本文所述之組成物在此一溫度下可係穩定的。熱成形可包含真空熱成形。在一較佳實施例中,真空熱成形係在從0.25 MPa至0.4 MPa的壓力下實行。在另一較佳實施例中,高壓熱成形係在範圍從6 MPa至12 MPa的壓力之一壓力下實行。
較佳地,該方法進一步包含使用導電黏著劑或不導電黏著劑將一或多個電子裝置附接至坯料,該導電黏著劑係本文所述之組成物,其中該附接在熱形成之前及/或之後發生。
較佳地,該方法進一步包含在熱成形之後,使用射出模製將樹脂層施加至基材,較佳地其中該樹脂包含聚碳酸酯(PC)、聚對苯二甲酸乙二酯(PET)、丙烯腈丁二烯苯乙烯(ABS)、聚丙烯(PP)、聚酯、聚(甲基丙烯酸甲酯)(PMMA)、低密度聚乙烯(LDPE)、高密度聚乙烯(HDPE)、聚苯乙烯(PS)、及熱塑性聚胺甲酸酯(TPU) 中之一或多者。亦可使用其他類似樹脂。此一樹脂層可為成品IME組件提供有利的機械及/或美感性質。
射出模製較佳地係在從170至330℃的溫度下實行。此一溫度特別適於射出模製,且本文所述之組成物在此一溫度下可係穩定的。
模內電子(IME)組件較佳地包含電容式觸控開關或電阻式觸控開關。與習知的電容式觸控開關及電阻式觸控開關相比,此一電容式觸控開關及電阻式觸控開關可展現改善的性能及/或可靠度。
模內電子(IME)組件較佳地包含顯示器、發光體/燈、感測器、指示器、及觸覺/觸控回饋裝置中之一或多者。
模內電子(IME)組件較佳地包含透明導電膜、印刷式電阻加熱器、透明電阻加熱器、透明電容式基於觸控裝置、及透明可撓性及電路元件中之一或多者。在此類情況下,較佳地,組成物包含導電填料,其等可包含導電、金屬奈米線、及/或導電奈米碳管及奈米碳纖維;及/或導電聚合物;及/或導電石墨烯片,如上述者。
在一進一步的態樣中,本發明提供根據本文所述之方法製造的模內電子(IME)組件。與習知的IME組件相比,該IME組件可展現改善的性能及/或可靠度。
在一進一步的態樣中,本發明提供一種模內電子(IME)組件,其包含本文所述之組成物。如將理解,該組成物將經受至少部分的交聯。與習知的IME組件相比,該IME組件可展現改善的性能及/或可靠度。
模內電子(IME)組件較佳地包含電容式觸控開關或電阻式觸控開關。與習知的電容式觸控開關及電阻式觸控開關相比,此一電容式觸控開關及電阻式觸控開關可展現改善的性能及/或可靠度。
模內電子(IME)組件較佳地包含顯示器、發光體/燈、感測器、指示器、及觸覺/觸控回饋裝置中之一或多者。與習知的顯示器、發光體/燈、感測器、指示器、及觸覺/觸控回饋裝置相比,此一顯示器、發光體/燈、感測器、指示器、及觸覺/觸控回饋裝置可展現改善的性能及/或可靠度。
模內電子(IME)組件較佳地包含透明導電膜、印刷式電阻加熱器、透明電阻加熱器、透明電容式基於觸控裝置、及透明可撓性及電路元件中之一或多者。在此類情況下,較佳地,組成物包含導電填料,其等可包含導電、金屬奈米線、及/或導電奈米碳管及奈米碳纖維;及/或導電聚合物;及/或導電石墨烯片,如上述者。
現將參照下列編號的條項進一步描述本發明:
1. 一種黏合劑組成物,其包含:
熱塑性樹脂,其包含羥基基團;
交聯劑;及
溶劑。
2. 如前述條項中任一項之黏合劑組成物,其係用於在用於電子總成之一組成物中使用。
3. 如條項1或條項2之黏合劑組成物,其包含:
從5至50 wt.%、較佳地從10至45 wt.%、更佳地從10至40 wt.%、甚至更佳地從15至30 wt.%的熱塑性樹脂;
從0.1至5 wt.%、較佳地從1至4 wt.%的交聯劑;及
從45至85 wt.%、較佳地從50至80 wt.%、更佳地從55至75 wt.%的溶劑。
4. 如前述條項中任一項之黏合劑組成物,其中該熱塑性樹脂展現下列之一或多者:
<100℃的一玻璃轉移溫度(較佳地使用DSC測量);
在1000至100000 g/莫耳之範圍內的一分子量(較佳地使用一黏度技術測量);
<100℃的一軟化點(較佳地根據ASTM-D1525測量);及
>20 mgKOH/g的羥基含量(OH數)(較佳地根據ASTM E222 – 17測量)。
5. 如前述條項中任一項之黏合劑組成物,其中該熱塑性樹脂包含聚胺甲酸酯樹脂、聚酯樹脂、聚丙烯酸酯樹脂、聚乙烯酯樹脂、苯氧基樹脂、及酮樹脂中之一或多者。
6. 如條項5之黏合劑組成物,其包含:
從1至50 wt.%的聚胺甲酸酯樹脂(較佳地從10至30 wt.%、更佳地從15至20 wt.%);及/或
從1至30 wt.%的聚酯樹脂(較佳地從10至30 wt.%、更佳地從15至20 wt.%);及/或
從1至30 wt.%的聚丙烯酸酯樹脂(較佳地從10至30 wt.%、更佳地從15至20 wt.%);及/或
從1至30 wt.%的聚乙烯酯樹脂(較佳地從10至30 wt.%、更佳地從15至20 wt.%);及/或
從1至30 wt.%的苯氧基樹脂(較佳地從10至30 wt.%、更佳地從15至20 wt.%);及/或
從1至30 wt.%的酮樹脂(較佳地從10至30 wt.%、更佳地從15至20 wt.%),
較佳地,其中該熱塑性樹脂的總量不超過50 wt.%、更佳地45 wt.%、又更佳地40 wt.%。
7. 如條項5之黏合劑組成物,其中該熱塑性樹脂包含:
從1至50 wt.%的聚胺甲酸酯樹脂(較佳地從10至30 wt.%、更佳地從15至20 wt.%);及/或
從1至30 wt.%的聚酯樹脂(較佳地從10至30 wt.%、更佳地從15至20 wt.%);及/或
從1至30 wt.%的聚丙烯酸酯樹脂(較佳地從10至30 wt.%、更佳地從15至20 wt.%);及/或
從1至30 wt.%的聚乙烯酯樹脂(較佳地從10至30 wt.%、更佳地從15至20 wt.%);及/或
從1至30 wt.%的苯氧基樹脂(較佳地從10至30 wt.%、更佳地從15至20 wt.%);及/或
從1至30 wt.%的酮樹脂(較佳地從10至30 wt.%、更佳地從15至20 wt.%)。
8. 如前述條項中任一項之黏合劑組成物,其包含至少二個熱塑性樹脂,該等熱塑性樹脂包含羥基基團。
9. 如前述條項中任一項之黏合劑組成物,其中該交聯劑係選自三聚氰胺樹脂、胺基樹脂、聚胺樹脂、異氰酸酯、及聚異氰酸酯中之一或多者,較佳地係三聚氰胺樹脂。
10. 如前述條項中任一項之黏合劑組成物,其中該溶劑係選自醇、二醇、二醇醚、二醇酯、酯、及/或酮溶劑、及/或烴中之一或多者。
11. 如條項8之黏合劑組成物,其包含:
從1至55 wt.%的醇溶劑;及/或
從1至50 wt.%的二醇溶劑;及/或
從1至15 wt.%的二醇醚溶劑;及/或
從1至60 wt.%的二醇酯溶劑;及/或
從1至75 wt.%的酯溶劑;及/或
從1至25 wt%的酮溶劑;及/或
從1至30 wt.%的烴溶劑,
較佳地,其中醇溶劑、二醇溶劑、二醇醚溶劑、二醇酯溶劑、酯溶劑、酮溶劑、及烴溶劑之總量不大於85 wt.%。
12. 如條項8之黏合劑組成物,其中該溶劑包含:
從1至55 wt.%的醇溶劑;及/或
從1至50 wt.%的二醇溶劑;及/或
從1至15 wt.%的二醇醚溶劑;及/或
從1至60 wt.%的二醇酯溶劑;及/或
從1至75 wt.%的酯溶劑;及/或
從1至25 wt%的酮溶劑;及/或
從1至30 wt.%的烴溶劑。
13. 如前述條項中任一項之黏合劑組成物,其進一步包含:
丙烯酸酯樹脂,其連同一或多個固化劑;及/或
環氧樹脂,其連同一或多個固化劑。
14. 如條項13之黏合劑組成物,其包含:從0.05至2 wt.%、較佳地0.1至1 wt.%的固化劑及下列之一或兩者:
從0.1至20 wt.%、較佳地從1至10 wt.%的丙烯酸酯樹脂;及
從0.1至20 wt.%、較佳地從1至10 wt.%的環氧樹脂。
15. 如前述條項中任一項之黏合劑組成物,其中該黏合劑組成物係可熱成形的。
16. 如前述條項中任一項之黏合劑組成物,其中該黏合劑組成物係熱可固化的。
17. 如前述條項中任一項之黏合劑組成物,其中該熱塑性樹脂能夠與該交聯劑形成一氮-碳鍵。
18. 一種用於電子總成之組成物,其包含:
如前述條項中任一項之黏合劑組成物;及
填料粒子。
19. 如條項18之用於電子總成之組成物,其包含:
從30至99 wt.%、較佳地從30至98 wt.%的黏合劑組成物(替代地從30至55 wt.%、較佳地30至50 wt.%的黏合劑組成物);及
從1至40 wt.%、較佳地從2至40 wt.%(替代地從45至70 wt.%、較佳地從50至70 wt.%的導電填料粒子,或從5至40 wt.%的填料粒子(一般係不導電填料粒子))。
20. 如條項18或條項19之用於電子總成之組成物,其中該等填料粒子包含諸如一金屬或一非金屬之一填料(一般係一導電填料)或者諸如金屬氧化物或非金屬或有機聚合材料之填料(一般係不導電填料)。
21. 如條項18至20中任一項之用於電子總成之組成物,其中該等填料粒子(一般係導電填料粒子)包含銀、銀合金、銅、銅合金(例如,CuNi、CuZn、及CuNiZn)、塗銀銅、塗銀銅合金、石墨烯、碳黑、奈米碳管、石墨、塗銀石墨烯、及塗銀石墨中之一或多者。
22. 如條項18至21中任一項之用於電子總成之組成物,其中該等填料粒子(一般係不導電填料粒子)包含下列之一或多者:纖維素、蠟、聚合物、雲母、矽石、滑石、氧化鋁、鈦酸鋇、碳粒子(一般係不導電碳粒子)、氧化石墨烯、及氮化硼。
23. 如條項18至22中任一項之用於電子總成之組成物,其中該等填料粒子具有從1至30 µm、較佳地從2至20 µm之一D50,較佳地使用SEM及/或一雷射散射粒徑分析儀測量。
24. 如條項18至23中任一項之用於電子總成之組成物,其中該等填料粒子之至少一些(較佳地實質上係該等填料粒子的全部)具有一片狀形狀,較佳地,其中該粒子的最長尺寸對該粒子的最短尺寸之一比率係大於1、更佳地大於2、甚至更佳地從2至10。
25. 如條項18至24中任一項之用於電子總成之組成物,其中該等填料粒子具有1至5之一敲緊密度。
26. 如條項18至25中任一項之用於電子總成之組成物,其中該等填料粒子係以一封端劑封端。
27. 如條項18至26中任一項之用於電子總成之組成物,其中該等填料粒子具有從0.5至5 m
2/g之一表面積。
28. 如條項18至27中任一項之用於電子總成之組成物,其呈金屬油墨、非金屬油墨、或導電黏著劑的形式。
29. 如條項18至28中任一項之用於電子總成之組成物,其呈介電油墨、不導電油墨、或不導電黏著劑、或封裝材料的形式。
30. 如條項18至29中任一項之用於電子總成之組成物,其經印刷在一聚合物基材(諸如,聚碳酸酯(PC)、聚對苯二甲酸乙二酯(PET))上及/或經熱成形以形成彎曲的2.5 D及3D結構。
31. 如條項18至30中任一項之用於電子總成之組成物,其經印刷在一合適的聚合物基材(諸如,聚碳酸酯(PC)、聚對苯二甲酸乙二酯(PET))上、經熱成形以形成彎曲的2.5 D及3D結構、經射出模製以形成模內電子(IME)及類似結構。
32. 如條項18至31中任一項之用於電子總成之組成物,其能夠經印刷在已施加至一聚合物基材(諸如,聚碳酸酯(PC)、聚對苯二甲酸乙二酯(PET))上之一合適的圖形油墨或裝飾用油墨上,並能夠經熱成形以形成彎曲的2.5 D及3D結構。
33. 如條項18至32中任一項之用於電子總成之組成物,其經印刷在已施加至一聚合物基材(諸如,聚碳酸酯(PC)、聚對苯二甲酸乙二酯(PET))上之一合適的圖形油墨或裝飾用油墨上、可經熱成形以形成彎曲的2.5 D及3D結構、經射出模製以形成模內電子(IME)及類似結構。
34. 如條項18至33中任一項之用於電子總成之組成物,其等係彼此相容,具有充分的黏附性,可熱成形,並在射出模製期間抗油墨洗出。
35. 一種如條項18至34中任一項之用於電子總成之組成物在模內電子結構(IME)的製造中之用途。
36. 一種製造模內電子結構(IME)之方法,該方法包含:
在一聚合物基材與一電子組件之間提供如條項18至34中任一項之用於電子總成之組成物以形成一電子結構;
熱成形該結構以形成一熱成形結構;及
射出模製該熱成形結構。
37. 如條項36之方法,其中該熱成形係在從140至180℃的一溫度下實行。
38. 如條項36或條項37之方法,其中該射出模製係在從200至330℃之一溫度下實行。
39. 如條項36至38中任一項之方法,其中該聚合物基材:
係可撓的;及/或
包含聚碳酸酯(PC)及/或聚對苯二甲酸乙二酯(PET);及/或
在其表面上具有圖形油墨。
40. 如條項36至39中任一項之方法,其中該聚合物基材係以下列之一或多者塗佈:
油墨(較佳地係圖形或裝飾用油墨);
不導電層(較佳地由不導電油墨形成);
介電層;及
外層,其呈以(或由)導電油墨形成之一電路的形式。
41. 如條項36至40中任一項之方法,其中在一聚合物基材與一電子組件之間提供該組成物以形成一結構包含網版印刷該組成物及/或乾燥或固化該組成物。
42. 如條項36至41中任一項之方法,其中該模內電子結構係彎曲的2.5 D或3D。
43. 一種黏合劑組成物,其包含:
熱塑性樹脂,其包含羥基基團;
交聯劑;及
溶劑;及/或
丙烯酸酯樹脂,其具有一或多個固化劑;及/或
環氧樹脂,其具有一或多個固化劑。
44. 如前述條項中任一項之黏合劑組成物,其係用於在用於電子總成之一組成物中使用。
45. 如條項43或條項44之黏合劑組成物,其包含:
從5至45 wt.%、較佳地從10至40 wt.%、更佳地從15至30 wt.%的熱塑性樹脂;
從0.1至5 wt.%、較佳地從1至4 wt.%的交聯劑;及
從0.1至20 wt.%、較佳地從1至10 wt.%的丙烯酸酯樹脂;及/或
從0.1至20 wt.%、較佳地從1至10 wt.%的環氧樹脂;及
從0.05至2 wt.%、較佳地0.1至1 wt.%的固化劑;及
從45至85 wt.%、較佳地從50至80 wt.%、更佳地從55至75 wt.%的溶劑。
46. 如前述條項中任一項之黏合劑組成物,其中該熱塑性樹脂展現下列之一或多者:
<100℃的一玻璃轉移溫度;
在1000至100000 g/莫耳之範圍內的一分子量;
<100℃的一軟化點;及
> 20 mgKOH/g的羥基含量(OH數)。
47. 如前述條項中任一項之黏合劑組成物,其中該熱塑性樹脂包含聚胺甲酸酯樹脂、聚酯樹脂、聚丙烯酸酯樹脂、聚乙烯酯樹脂、苯氧基樹脂、及酮樹脂中之一或多者。
48. 如條項43至47中任一項之黏合劑組成物,其包含:
從1至50 wt.%的聚胺甲酸酯樹脂;及/或
從1至30 wt.%的聚酯樹脂;及/或
從1至30 wt.%的聚丙烯酸酯樹脂;及/或
從1至30 wt.%的聚乙烯酯樹脂;及/或
從1至30 wt.%的苯氧基樹脂;及/或
從1至30 wt.%的酮樹脂;及/或
從1至75 wt.%的丙烯酸酯樹脂;及/或
從1至75 wt.%環氧樹脂。
49. 如前述條項中任一項之黏合劑組成物,其中該交聯劑係選自三聚氰胺樹脂、胺基樹脂、聚胺樹脂、異氰酸酯、及聚異氰酸酯中之一或多者,較佳地係三聚氰胺樹脂。
50. 如前述條項中任一項之黏合劑組成物,其中該固化劑係選自一熱固化起始劑及/或UV固化起始劑中之一或多者。
51. 如前述條項中任一項之黏合劑組成物,其中該溶劑係選自醇、二醇、二醇醚、二醇酯、酯、及/或酮溶劑、及/或烴中之一或多者。
52. 如條項51之黏合劑組成物,其包含:
從1至50 wt.%的醇溶劑;及/或
從1至50 wt.%的二醇溶劑;及/或
從1至15 wt.%的二醇醚溶劑;及/或
從1至60 wt.%的二醇酯溶劑;及/或
從1至75 wt.%的酯溶劑;及/或
從1至25 wt%的酮;及/或
從1至30 wt.%的烴溶劑。
53. 如前述條項中任一項之黏合劑組成物,其中該黏合劑組成物係熱可固化的。
54. 如前述條項中任一項之黏合劑組成物,其中該黏合劑組成物係UV可固化的。
55. 如前述條項中任一項之黏合劑組成物,其中該黏合劑組成物係可熱成形的。
56. 如前述條項中任一項之黏合劑組成物,其中該熱塑性樹脂能夠與該交聯劑形成一氮-碳鍵。
57. 一種用於電子總成之組成物,其包含:
如條項43至56中任一項之黏合劑組成物;及
填料粒子。
58. 如條項57之組成物,其包含:
從30至99 wt.%、較佳地從30至99 wt.%的黏合劑組成物;及
從45至70 wt.%、較佳地從50至70 wt.%的導電填料粒子、或者從1至40 wt.%、較佳地從2至40 wt.%、或從5至40 wt.%的不導電填料粒子。
59. 如條項57或條項58之組成物,其中該等填料粒子包含諸如金屬或一非金屬的一導電填料或者諸如金屬氧化物或非金屬或有機聚合材料之不導電填料。
60. 如條項57至59中任一項之組成物,其中該等導電填料粒子包含銀、銀合金、銅、銅合金(例如,CuNi、CuZn、及CuNiZn)、塗銀銅、塗銀銅合金、石墨烯、石墨、碳黑、奈米碳管、塗銀石墨烯、及塗銀石墨中之一或多者。
61. 如條項57至60中任一項之組成物,其中該等不導電填料粒子包含下列之一或多者:纖維素、蠟、聚合物、雲母、矽石、滑石、氧化鋁、鈦酸鋇、不導電碳粒子、氧化石墨烯、及氮化硼。
62. 如條項57至61中任一項之組成物,其中該等填料粒子具有從1至30 µm、較佳地從2至20 µm之一D50,較佳地使用SEM及/或雷射散射粒徑分析儀測量。
63. 如條項57至62中任一項之組成物,其中該等填料粒子之至少一些(較佳地實質上係該等填料粒子的全部)具有一片狀形狀,較佳地,其中該粒子的最長尺寸對該粒子的最短尺寸之一比率係大於1、更佳地大於2、甚至更佳地從2至10。
64. 如條項57至63中任一項之組成物,其中該等填料粒子具有1至5之一敲緊密度。
65. 如條項57至64中任一項之組成物,其中該等填料粒子係以封端劑封端。
66. 如條項57至65中任一項之組成物,其中該等填料粒子具有從0.5至5 m
2/g之一表面積。
67. 如條項57至66中任一項之組成物,其呈金屬油墨、非金屬油墨、或導電黏著劑的形式。
68. 如條項57至67中任一項之組成物,其呈介電油墨、不導電油墨、或不導電黏著劑、或封裝材料的形式。
69. 一種如條項57至67中任一項之組成物在模內電子結構(IME)的製造中之用途。
70. 一種製造模內電子結構(IME)之方法,該方法包含:
在一聚合物基材與一電子組件之間提供如條項57至68中任一項之組成物以形成一結構;
熱成形該結構以形成一熱成形結構;及
射出模製該熱成形結構。
71. 如條項70之方法,其中該熱成形係在從140至180℃的一溫度下實行。
72. 如條項70或條項71之方法,其中該射出模製係在從200至330℃之一溫度下實行。
73. 如條項70至72中任一項之方法,其中該聚合物基材:
係可撓的;及/或
包含聚碳酸酯(PC)及/或聚對苯二甲酸乙二酯(PET)。
74. 如條項70至73中任一項之方法,其中在一聚合物基材與一電子組件之間提供該組成物以形成一結構包含網版印刷該組成物及/或乾燥或固化該組成物。
75. 一種電子結構,其包含;一聚合物基材,其係以/不以圖形或裝飾用油墨塗佈,以一不導電或一介電層塗佈,隨後施加導電油墨以形成電路,其中在電子組件中係使用導電黏著劑附接;該結構係經熱成形;及/或結構係經射出模製以製成一部件。
76. 一種製造如條項75之電子結構之方法,該方法包含:
在以圖形或裝飾用油墨塗佈/未經塗佈之一聚合物基材上提供如條項13至23或44至54中任一項之不導電或介電油墨組成物;及
將如條項13至23或44至54中任一項之導電油墨組成物網版印刷在一以不導電油墨塗佈的聚合物基材上;
及放置使用如條項13至23或44至54中任一項之合適的導電及不導電黏著劑附接之一電子組件,以形成一電子結構;
熱成形該結構以形成一熱成形結構;及
射出模製該熱成形結構。
77. 如條項76之方法,其中該熱成形係在從140至180℃的一溫度下實行。
78. 如條項76或條項77之方法,其中該射出模製係在從200至330℃之一溫度下實行。
79. 如條項76至78中任一項之方法,其中該聚合物基材:
係可撓的;及/或
包含聚碳酸酯(PC)及/或聚對苯二甲酸乙二酯(PET)。
80. 如條項76至79中任一項之方法,其中該聚合物基材:
係可撓的;及/或
包含以圖形油墨塗佈之聚碳酸酯(PC)及/或聚對苯二甲酸乙二酯(PET)。
81. 如條項76至80中任一項之方法,其中在一聚合物基材與一電子組件之間提供該組成物以形成一結構包含網版印刷該組成物及/或乾燥或固化該組成物。
82. 一種模內電子結構(IME),其係根據如條項36至42或70至81中任一項之方法製造。
現將關於下列非限制性實例描述本發明。
在下文表1中定出實例中所用之各種(導電及不導電)填料的關鍵屬性。
[表1]:
導電油墨及組成物之實例:
填料類型 | 填料名稱 | 敲緊密度(g/cc) | 表面積(m 2/g) | 有機含量(wt%) | 平均粒徑(d50),µm |
導電填料 | 銀片1 | 3.5 | 1.01 | 0.57 | 4.4 |
銀片2 | 3.2 | 1 | 0.42 | 7 | |
銀片3 | 3.1 | 1.55 | 0.63 | 3.7 | |
銀片4 | 2 | 2.1 | 1.31 | 1.5 | |
銀片5 | 3.3 | 1.49 | 0.55 | 1.25 | |
塗Ag銅片 | 4 | 0.47 | 0.07 | 4.5 | |
塗Ag黃銅片 | 3.7 | 0.43 | 0.06 | 3.5 | |
奈米銀 | < 1 | 0.03至0.1 | |||
塗Ag銅片 | < 4 | 0.47 | < 0.1 | 4.5 | |
塗Ag黃銅片 | < 4 | 0.43 | < 0.1 | 3.5 | |
石墨片 | 11.25 | < 0.8 | 7.75 | ||
石墨烯粉末 | 30至50 | 5 | |||
不導電填料 | 滑石粉末 | 5.1 | |||
二氧化鈦粉末 | < 0.5 | 0.4 | |||
氮化硼粉末 | 0.35 | 10 | |||
鈦酸鋇粉末 | 2.1 | < 0.5 | 1.3 | ||
矽石粉末 | 5 | ||||
Ceraflour 920 | 5 | ||||
Ceraflour 929 | 8 | ||||
Ceraflour 991 | 5 |
若干組成物係藉由在70至100℃下於不同類別的溶劑之混合物中溶解熱塑性聚酯樹脂、聚胺甲酸酯樹脂、及具有羥基官能基的苯氧基樹脂之混合物來製備。反應混合物係冷卻至室溫,隨後添加功能添加劑包裝,該包裝含有界面活性劑、流變改質劑、分散劑、消泡劑、及濕潤劑。接著將反應性交聯劑及/或其他丙烯酸或環氧固化劑與上述聚合物樹脂混合物充分地混合。組成物係進一步與若干不同的導電粒子混合,以用於製備導電油墨、塗層、及黏著劑組成物。導電粒子係使用軌道式混合器混合(1000 rpm,持續1分鐘,進行3個循環)。某些組成物亦在三輥磨機中碾磨數分鐘以得到均質膏。
下文之實例1至實例14及實例19至實例26係在無熱固性樹脂的情況下製備的導電組成物。實例15至實例18係使用熱固性樹脂及對應的固化催化劑製備之導電組成物。
實例1
原料之類別 | 化學名稱 | 重量% |
交聯劑 | Maprenel MF650(異丁醇中55%) | 1.4 |
熱塑性聚酯樹脂 | Dynapol L-411 | 1.4 |
熱塑性聚胺甲酸酯樹脂 | Desmomelt 540/1 | 3.4 |
熱塑性苯氧基樹脂 | PKHH | 5.0 |
功能添加劑 | 功能添加劑 | 2.7 |
二醇醚乙酸酯 | Eastman DE乙酸酯 | 22.3 |
酮 | C11-酮 | 10.7 |
導電填料 | 銀片1 | 53.2 |
總計 | 100.0 |
使用軌道式混合器以1000 rpm持續1分鐘進行3個循環將53.2重量%之銀片與46.8重量%之聚合物溶液混合在一起,以得到均質膏。發現膏的黏度在4000至7000 cP的範圍內,且該膏適於網版印刷。
實例2至26
具有下文的表2至表6中所指定之組分的組成物係按照上文之實例1中所述的程序製備。
[表2]:實例1至實例5之化學組成物。
原料之類別 | 化學名稱 | 實例 1 | 實例 2 | 實例 3 | 實例 4 | 實例 5 |
交聯劑 | Maprenel MF650(異丁醇中55%) | 1.4 | 1.4 | 1.4 | 1.3 | 1.4 |
熱塑性聚酯樹脂 | Dynapol L-411 | 1.4 | 1.4 | 1.4 | 1.3 | 1.4 |
熱塑性聚胺甲酸酯樹脂 | Desmomelt 540/1 | 3.4 | 3.5 | 3.5 | 3.2 | 3.5 |
熱塑性苯氧基樹脂 | PKHH | 5.0 | 5.1 | 5.1 | 4.7 | 5.1 |
功能添加劑 | 功能添加劑 | 2.7 | 5.7 | 5.7 | 5.3 | 5.7 |
二醇醚乙酸酯 | Eastman DE乙酸酯 | 22.3 | 23.0 | 23.0 | 26.8 | 23.0 |
二醇醚 | Eastman DB溶劑 | - | 5.4 | 5.4 | 6.3 | 5.4 |
酮 | C11-酮 | 10.7 | - | - | - | - |
導電填料 | Ag片1 | 53.2 | 54.6 | - | - | - |
導電填料 | Ag片2 | - | - | 46.4 | - | - |
導電填料 | Ag片4 | - | - | 8.2 | 51.1 | - |
導電填料 | Ag片5 | - | - | - | - | 54.6 |
總計 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 |
[表3]:實例6至實例10之化學組成物。
原料之類別 | 化學名稱 | 實例 6 | 實例 7 | 實例 8 | 實例 9 | 實例 10 |
交聯劑 | Maprenel MF650(異丁醇中55%) | 1.8 | 1.5 | 1.4 | 1.4 | 1.4 |
熱塑性聚酯樹脂 | Dynapol L-411 | 1.8 | 1.5 | 1.4 | 1.4 | 1.4 |
熱塑性聚胺甲酸酯樹脂 | Desmomelt 540/1 | 4.5 | 3.8 | 3.5 | 3.5 | 3.4 |
熱塑性苯氧基樹脂 | PKHH | 6.6 | 5.5 | 5.1 | 5.1 | 5.0 |
功能添加劑 | 功能添加劑 | 7.4 | 6.2 | 5.7 | 5.7 | 5.6 |
二醇醚乙酸酯 | Eastman DE乙酸酯 | 16.5 | 17.4 | - | - | 2.8 |
二醇醚乙酸酯 | 丙二醇單甲基醚乙酸酯 | - | - | 8.5 | 4.3 | 4.2 |
二醇醚 | Downol PPH | - | - | - | 4.3 | 2.8 |
二醇醚 | Eastman DB溶劑 | 3.9 | 4.1 | 19.9 | 19.9 | 19.6 |
導電填料 | Ag片1 | - | - | 54.6 | 54.6 | 53.9 |
導電填料 | Ag片3 | 57.4 | 51.0 | - | - | - |
導電填料 | Ag片4 | - | 8.9 | - | - | - |
總計 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 |
[表4]:實例11至實例16之化學組成物。
原料之類別 | 化學名稱 | 實例 11 | 實例 12 | 實例 13 | 實例 14 | 實例 15 | 實例 16 |
交聯劑 | Maprenel MF650(異丁醇中55%) | 1.4 | 1.4 | 1.4 | 1.4 | 0.7 | 0.7 |
熱塑性聚酯樹脂 | Dynapol L-411 | 1.4 | 1.4 | 1.4 | 1.4 | 0.7 | 0.7 |
熱塑性聚胺甲酸酯樹脂 | Desmomelt 540/1 | 3.4 | 3.4 | 3.4 | 3.4 | 1.7 | 1.7 |
熱塑性苯氧基樹脂 | PKHH | 5.0 | 5.0 | 5.0 | 5.0 | 2.5 | 2.5 |
丙烯酸酯樹脂 | Ebecryl-8413 | - | - | - | - | 2.9 | 2.9 |
丙烯酸酯樹脂 | Ebecryl-1300 | - | - | - | - | 2.9 | 2.9 |
用於丙烯酸酯樹脂之固化催化劑(UV催化劑) | Omnirad-73 | - | - | - | - | - | 0.6 |
用於丙烯酸酯樹脂之固化催化劑(熱催化劑) | Luperex DI | - | - | - | - | 0.6 | - |
功能添加劑 | 功能添加劑 | 5.6 | 5.6 | 5.6 | 5.6 | 2.8 | 2.8 |
二醇醚乙酸酯 | Eastman DE乙酸酯 | 2.8 | 2.8 | 2.8 | 2.8 | 2.8 | 2.8 |
二醇醚乙酸酯 | 丙二醇單甲基醚乙酸酯 | 4.2 | 4.2 | 4.2 | 4.2 | 4.2 | 4.2 |
二醇醚 | Downol PPH | 2.8 | 2.8 | 2.8 | 2.8 | 2.8 | 2.8 |
二醇醚 | Eastman DB溶劑 | 19.6 | 19.6 | 19.6 | 19.6 | 19.6 | 19.6 |
導電填料 | Ag片1 | - | 16.2 | 37.7 | 8.1 | 56.0 | 56.0 |
導電填料 | Ag片2 | 45.8 | 37.7 | 16.2 | 45.8 | - | - |
導電填料 | Ag片4 | 8.1 | - | - | - | - | - |
總計 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 |
[表5]:實例17至實例21之化學組成物。
原料之類別 | 化學名稱 | 實例 17 | 實例 18 | 實例 19 | 實例 20 | 實例 21 |
交聯劑 | Maprenel MF650(異丁醇中55%) | 1.4 | 1.4 | 1.2 | 1.4 | 1.4 |
交聯劑(封閉型異氰酸酯) | Vestanat B 1358A | - | - | 2.0 | - | - |
熱塑性聚酯樹脂 | Dynapol L-411 | 1.4 | 1.4 | 1.2 | 1.4 | 1.4 |
熱塑性聚胺甲酸酯樹脂 | Desmomelt 540/1 | 3.4 | 3.4 | 3.0 | 3.5 | 3.5 |
熱塑性苯氧基樹脂 | PKHH | 2.5 | 2.5 | 4.4 | 5.1 | 5.1 |
環氧樹脂 | EPON 1001F (Hexion) | 2.5 | 2.5 | - | - | - |
用於環氧樹脂之固化催化劑 | 2E4MZ-CN | 0.3 | - | - | - | - |
用於環氧樹脂之固化催化劑(UV催化劑) | 二苯基錪鎓六氟磷酸鹽 | - | 0.3 | - | - | - |
功能添加劑 | 功能添加劑 | 5.7 | 5.7 | 4.9 | 5.7 | 5.7 |
二醇醚乙酸酯 | Eastman DE乙酸酯 | 2.8 | 2.8 | 2.5 | 23.0 | 23.0 |
二醇醚乙酸酯 | 丙二醇單甲基醚乙酸酯 | 4.2 | 4.2 | 3.7 | - | - |
二醇醚 | Downol PPH | 2.8 | 2.8 | 2.5 | - | - |
二醇醚 | Eastman DB溶劑 | 19.4 | 19.4 | 17.3 | 5.4 | 5.4 |
導電填料 | Ag片1 | 53.9 | 53.9 | 57.2 | - | - |
導電填料 | 塗銀銅片 | - | - | - | 54.6 | - |
導電填料 | 塗銀黃銅片 | - | - | - | - | 54.6 |
總計 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 |
[表6]:實例22至實例26之化學組成物。
實例不導電油墨及組成物:
原料之類別 | 化學名稱 | 實例 22 | 實例 23 | 實例 24 | 實例 25 | 實例 26 |
交聯劑 | Maprenel MF650(異丁醇中55%) | 1.7 | 1.7 | 1.3 | 1.4 | 1.4 |
熱塑性聚酯樹脂 | Dynapol L-411 | 1.7 | 1.7 | 1.3 | 1.4 | 1.4 |
熱塑性聚胺甲酸酯樹脂 | Desmomelt 540/1 | 4.2 | 4.2 | 3.8 | 3.5 | 3.5 |
熱塑性苯氧基樹脂 | PKHH | 6.2 | 6.2 | 4.7 | 5.1 | 5.1 |
功能添加劑 | 功能添加劑 | 3.4 | 3.4 | 2.6 | 5.7 | 5.7 |
二醇醚乙酸酯 | Eastman DE乙酸酯 | 43.2 | 43.2 | 21.2 | 23.0 | 23.0 |
二醇醚 | Eastman DB溶劑 | - | - | - | 5.4 | 5.4 |
酯 | 二元酯(DBE) | - | - | 1.7 | - | - |
酮 | C11-酮 | 20.5 | 20.5 | 10.1 | - | - |
導電填料 | Ag片1 | - | - | 53.2 | 51.9 | 46.5 |
導電填料 | 石墨片 | 16.8 | - | - | - | - |
導電填料 | 石墨烯粉末 | - | 16.8 | 0.1 | - | - |
導電填料 | 碳黑 | 2.3 | 2.3 | - | - | - |
導電填料 | Ag MoC(新癸酸銀) | - | - | - | 2.7 | - |
導電填料 | 奈米銀 | - | - | - | - | 8.2 |
總計 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 |
若干組成物係藉由在70至100℃下於不同類別的溶劑之混合物中溶解熱塑性聚酯樹脂、聚胺甲酸酯樹脂、及具有羥基官能基的苯氧基樹脂之混合物來製備。反應混合物係冷卻至室溫,隨後添加功能添加劑包裝,該包裝含有界面活性劑、流變改質劑、分散劑、消泡劑、及濕潤劑。接著將反應性交聯劑及/或其他丙烯酸或環氧固化劑與上述聚合物樹脂混合物充分地混合。組成物係進一步與若干不同的導電粒子混合,以用於製備導電油墨、塗層、及黏著劑組成物。導電粒子係使用軌道式混合器混合(1000 rpm,持續1分鐘,進行3個循環)。某些組成物亦在三輥磨機中碾磨數分鐘以得到均質膏。
下文之實例27至實例36及實例41至實例61係在無熱固性樹脂的情況下製備的導電組成物。實例37至實例40係使用熱固性樹脂及對應的固化催化劑製備之導電組成物。
實例27
原料類別 | 化學名稱 | 重量% |
交聯劑 | Maprenel MF650(異丁醇中55%) | 2.1 |
熱塑性聚酯樹脂 | Dynapol L-411 | 2.1 |
熱塑性聚胺甲酸酯樹脂 | Desmomelt 540/1 | 5.2 |
熱塑性苯氧基樹脂 | PKHH | 7.7 |
功能添加劑 | 功能添加劑 | 3.9 |
二醇乙酸酯 | Eastman DE乙酸酯 | 34.2 |
二醇醚 | Downol PPH | 7.3 |
二醇乙酸酯 | 丙二醇單甲基醚乙酸酯 | 7.3 |
不導電填料 | 滑石粉末 | 28.3 |
不導電填料 | Ceraflour 920 | 1.8 |
總計 | 100.0 |
使用軌道式混合器以1000 rpm持續1分鐘進行3個循環將30.1重量%之滑石與有機填料的混合物及69.9重量%的聚合物溶液混合在一起,以得到均質膏。發現膏的黏度在11000至15000 cP的範圍內,且該膏適於網版印刷。
實例28至61
具有下文的表7至表11中所指定之成分的組成物係按照上文之實例27中所述的程序製備。
[表7]:實例27至實例34之化學組成物。
原料之類別 | 化學名稱 | 實例 -27 | 實例 -28 | 實例 -29 | 實例 -30 | 實例 -31 | 實例 -32 | 實例 -33 | 實例 -34 |
交聯劑 | Maprenel MF650(異丁醇中55%) | 2.1 | 2.2 | 2.2 | 2.2 | 3.1 | 3.2 | 2.2 | 3.2 |
熱塑性聚酯樹脂 | Dynapol L-411 | 2.1 | 2.2 | 2.2 | 2.2 | 3.1 | 3.2 | 2.2 | 3.2 |
熱塑性聚胺甲酸酯樹脂 | Desmomelt 540/1 | 5.2 | 5.5 | 5.5 | 5.5 | 7.8 | 8.1 | 5.6 | 8.1 |
熱塑性苯氧基樹脂 | PKHH | 7.7 | 8.0 | 8.0 | 8.0 | 11.4 | 11.8 | 8.1 | 11.8 |
功能添加劑 | 功能添加劑 | 3.9 | 4.1 | 4.1 | 4.1 | 5.8 | 1.5 | 1.4 | 2.0 |
二醇醚乙酸酯 | Eastman DE乙酸酯 | 34.2 | - | - | - | 39.6 | 32.8 | 26.1 | 33.3 |
二醇醚乙酸酯 | 丁基卡必醇乙酸酯 | - | 5.1 | 5.1 | 5.1 | - | - | - | - |
二醇醚乙酸酯 | 丙二醇單甲基醚乙酸酯 | 7.3 | 10.2 | 10.2 | 5.1 | - | - | - | - |
酮 | C11-酮 | - | - | - | - | 17.0 | 15.6 | 12.5 | 15.9 |
二醇醚 | Downol PPH | 7.3 | - | - | - | - | - | - | - |
二醇醚 | 丁基卡必醇 | - | - | 35.5 | 5.1 | - | - | 10.6 | |
二醇醚 | 丙二醇單甲基醚 | - | - | - | - | - | - | 3.8 | 12.0 |
烴 | 芳族150流體 | - | - | - | - | - | 13.3 | - | - |
醇 | 萜品醇 | - | 35.5 | - | 35.5 | - | - | ||
不導電填料 | 滑石 | 28.3 | 26.8 | 26.8 | 26.8 | 11.6 | 10.4 | 27.6 | 10.4 |
不導電填料 | Ceraflour 920 | 1.8 | 0.5 | 0.5 | 0.5 | 0.6 | - | - | - |
總計 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 |
[表8]:實例35至實例40之化學組成物。
原料之類別 | 化學名稱 | 實例-35 | 實例-36 | 實例-37 | 實例-38 | 實例-39 | 實例-40 |
交聯劑 | Maprenel MF650(異丁醇中55%) | 2.5 | 2.7 | 1.9 | 1.9 | 2.5 | 2.5 |
熱塑性聚酯樹脂 | Dynapol L-411 | 2.5 | 2.7 | 1.9 | 1.9 | 2.5 | 2.5 |
熱塑性聚酯樹脂 | CAB 381-2 | - | 2.7 | - | - | - | - |
熱塑性聚胺甲酸酯樹脂 | Desmomelt 540/1 | 6.2 | 6.7 | 4.8 | 4.8 | 6.1 | 6.1 |
熱塑性苯氧基樹脂 | PKHH | 9.0 | 7.4 | 7.1 | 7.1 | 4.5 | 4.5 |
環氧樹脂 | EPON 1001F (Hexion)(基於雙酚A) | - | - | - | - | 4.5 | 4.5 |
丙烯酸酯樹脂 | Ebecryl 8413 | - | - | 9.8 | 9.8 | - | - |
丙烯酸酯樹脂 | Ebecryl 1300 | - | - | 9.8 | 9.8 | - | - |
用於環氧樹脂之固化催化劑 | 2E4MZ-CN | - | - | - | - | 0.4 | - |
用於環氧樹脂之固化催化劑(UV催化劑) | 二苯基錪鎓六氟磷酸鹽 | - | - | - | - | - | 0.4 |
用於丙烯酸酯樹脂之固化催化劑 | ACHN | - | - | 2.0 | - | - | |
用於丙烯酸酯樹脂之固化催化劑 | Omnirad-1173 | - | - | - | 2.0 | - | - |
功能添加劑 | 功能添加劑 | 10.1 | 9.0 | 7.9 | 7.9 | 10.0 | 10.0 |
二醇醚乙酸酯 | 丁基卡必醇乙酸酯 | 4.9 | |||||
二醇醚乙酸酯 | 丙二醇單甲基醚乙酸酯 | 15.2 | 11.9 | 11.9 | 15.1 | 15.1 | |
酮 | C11-酮 | - | 4.9 | - | |||
二醇醚 | 丁基卡必醇 | 35.5 | 27.8 | 27.8 | 35.2 | 35.2 | |
烴 | 芳族150流體 | - | 4.8 | - | - | - | - |
醇 | 萜品醇 | - | 33.9 | - | - | - | - |
不導電填料 | 滑石 | 19.0 | 19.9 | 14.9 | 14.9 | 19.3 | 19.3 |
不導電填料 | Ceraflour 920 | - | 0.6 | - | - | - | - |
總計 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 |
[表9]:實例41至實例48之化學組成物。
原料之類別 | 化學名稱 | 實例 -41 | 實例 -42 | 實例 -43 | 實例 -44 | 實例 -45 | 實例 -46 | 實例 -47 | 實例 -48 |
交聯劑 | Maprenel MF650(異丁醇中55%) | 2.3 | 2.4 | 3.4 | 3.4 | 3.4 | 2.5 | 2.9 | 3.2 |
用於多元醇之固化催化劑 | 來自Evonik之Vestanat B 1358A | 3.8 | - | - | - | - | - | - | - |
熱塑性聚酯樹脂 | Dynapol L-411 | 2.3 | 2.4 | 3.4 | 3.4 | 3.4 | 2.5 | 2.9 | 3.2 |
熱塑性聚胺甲酸酯樹脂 | Desmomelt 540/1 | 5.7 | 5.9 | 8.4 | 8.4 | 8.4 | 6.2 | 7.3 | 7.9 |
熱塑性苯氧基樹脂 | PKHH | 8.4 | 8.6 | 12.4 | 12.4 | 12.4 | 9.0 | 10.6 | 11.7 |
功能添加劑 | 功能添加劑 | 9.4 | 9.6 | 6.8 | 6.8 | 6.8 | 10.1 | 11.9 | 6.5 |
二醇醚乙酸酯 | Eastman DE乙酸酯 | - | - | 41.2 | 41.2 | 41.2 | - | - | 38.8 |
二醇醚乙酸酯 | 丙二醇單甲基醚乙酸酯 | 14.1 | 14.5 | - | - | - | 15.2 | 17.9 | - |
酮 | C11-酮 | - | - | 19.5 | 19.5 | 19.5 | 18.4 | ||
二醇醚 | 丁基卡必醇 | 32.9 | 33.7 | - | - | - | 35.5 | 41.7 | |
不導電填料 | 滑石 | 21.1 | 23.1 | - | - | - | 4.8 | 10.4 | |
不導電填料 | 矽石 | - | - | - | - | - | 19.0 | - | - |
不導電填料 | Ceraflour 991 | - | - | - | - | 5.0 | - | - | - |
不導電填料 | Ceraflour 929 | - | - | - | 5.0 | - | - | - | - |
不導電填料 | Ceraflour 920 | - | - | 5.0 | - | - | - | - | |
總計 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 |
[表10]:實例49至實例55之化學組成物。
原料之類別 | 化學名稱 | 實例 -49 | 實例 -50 | 實例 -51 | 實例 -52 | 實例 -53 | 實例 -54 | 實例 -55 |
交聯劑 | Maprenel MF650(異丁醇中55%) | 3.2 | 2.1 | 3.1 | 3.2 | 2.2 | 2.2 | 2.1 |
熱塑性聚酯樹脂 | Dynapol L-411 | 3.2 | 2.1 | 3.1 | 3.2 | 2.2 | 2.2 | 2.1 |
熱塑性聚胺甲酸酯樹脂 | Desmomelt 540/1 | 8.1 | 5.1 | 7.6 | 8.0 | 5.4 | 5.4 | 5.1 |
熱塑性苯氧基樹脂 | PKHH | 11.8 | 7.4 | 11.1 | 11.7 | 7.9 | 7.8 | 7.5 |
功能添加劑 | 功能添加劑 | 1.5 | 2.6 | 12.5 | 2.3 | 2.8 | 2.8 | 2.6 |
二醇醚乙酸酯 | Eastman DE乙酸酯 | 41.7 | - | - | 41.4 | - | - | - |
二醇醚乙酸酯 | 二丙二醇甲基醚乙酸酯 | - | 8.5 | - | - | 8.0 | 8.1 | 8.6 |
二醇醚乙酸酯 | 丙二醇單甲基醚乙酸酯 | - | 0.0 | 18.8 | - | - | - | - |
酮 | C11-酮 | 19.9 | - | - | 19.7 | - | - | - |
二醇醚 | 二丙二醇甲基醚 | - | 17.1 | - | - | 15.9 | 16.2 | 17.2 |
二醇醚 | 丁基卡必醇 | - | 17.1 | 43.8 | 0.0 | 15.9 | 16.2 | 17.2 |
不導電填料 | 滑石 | 10.4 | 1.1 | - | 10.4 | - | - | 1.1 |
不導電填料 | 二氧化鈦 | - | 36.1 | - | 0.0 | 39.6 | 39.3 | 36.4 |
不導電填料 | 矽石 | - | 0.8 | - | - | - | - | - |
總計 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 |
[表11]:實例56至實例61之化學組成物。
熱成形及射出模製性能:3D電子構造:
原料之類別 | 化學名稱 | 實例-56 | 實例-57 | 實例-58 | 實例-59 | 實例-60 | 實例-61 |
交聯劑 | Maprenel MF650(異丁醇中55%) | 2.1 | 2.3 | 2.2 | 2.5 | 2.1 | 2.1 |
熱塑性聚酯樹脂 | Dynapol L-411 | 2.1 | 2.3 | 2.2 | 2.5 | 2.1 | 2.1 |
熱塑性聚胺甲酸酯樹脂 | Desmomelt 540/1 | 5.1 | 5.7 | 5.4 | 6.2 | 5.2 | 5.1 |
熱塑性苯氧基樹脂 | PKHH | 7.5 | 8.3 | 7.8 | 9.0 | 7.6 | 7.5 |
功能添加劑 | 功能添加劑 | 2.6 | 3.0 | 2.8 | 10.5 | 2.7 | 2.6 |
二醇醚乙酸酯 | Eastman DE乙酸酯 | - | - | - | 4.8 | - | - |
二醇醚乙酸酯 | 二丙二醇甲基醚乙酸酯 | 8.6 | 25.5 | 8.1 | - | 8.3 | 8.6 |
二醇醚乙酸酯 | 丙二醇單甲基醚乙酸酯 | - | - | - | 14.8 | - | - |
二醇醚 | 二丙二醇甲基醚 | 17.1 | - | 16.2 | - | 16.5 | 17.2 |
二醇醚 | 丁基卡必醇 | 17.1 | 28.1 | 16.2 | 30.5 | 16.5 | 17.2 |
不導電填料 | 滑石 | 1.1 | - | - | 19.2 | 1.2 | 1.1 |
不導電填料 | 二氧化鈦 | 36.2 | - | 39.3 | - | 37.1 | |
不導電填料 | BN | - | - | - | - | - | 36.4 |
不導電填料 | 鈦酸鋇 | - | 24.8 | - | - | - | - |
不導電填料 | 發煙矽石 | 0.5 | - | - | - | - | |
不導電填料 | Ceraflour 991 | - | - | - | - | 0.7 | - |
總計 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 |
上文所揭示之導電及介電組成物係經徹底特徵化,並針對網版印刷、電氣性能、不同油墨與基材(PC及PET)之間的相容性進行測試,在不同的加速環境射條件下針對黏附性及穩定性進行測試。這些油墨進一步針對熱穩定性、熱成形、及射出模製穩定性進行測試。
例如,下文的表12總結如實例1至實例26中所述之導電組成物的各種特性及測試性能屬性。
[表12]:各種導電組成物之特性及測試性能測試結果(實例1至實例26)
實例 | 黏度@5 rpm,cP (錐狀體及板材) | 固體含量(Wt%) | 黏附性 (PC/PET) | 表面電阻;熱成形之前(mΩ/Sq/mil) | 按照用於PC的1000 µm線寬之「圓錐體可成形性測試程序」之在熱成形之後的電阻變化 | 射出模製洗出穩定性 | ||
@30%應變 | @37%應變 | @46%應變 | ||||||
實例1 | 4000至7000 | 62至68 | 5B | 40至45 | 2 | 3 | 6 | 良好 |
實例2 | 9000至13000 | 62至68 | 5B | 40至45 | 3 | 3 | 5 | 良好 |
實例3 | 8000至12000 | 62至68 | 5B | 30至35 | 2 | 3 | 7 | NM |
實例4 | 5000至8000 | 60至64 | 5B | 20至25 | 2 | 3 | 4 | NM |
實例5 | 8000至11000 | 62至68 | 5B | 40至45 | 1 | 2 | 3 | NM |
實例6 | 40000至60000 | 62至68 | NM | NM | NM | NM | NM | NM |
實例7 | 45000至55000 | 70至74 | 5B | 40至50 | 1 | 2 | 3 | NM |
實例8 | 9000至12000 | 62至68 | 5B | 30至35 | 2 | 2 | 3 | NM |
實例9 | 13000至17000 | 62至68 | 5B | 30至35 | 2 | 3 | 3 | NM |
實例10 | 8000至12000 | 62至68 | 5B | 30至35 | 1.5 | 2 | 3 | 優良 |
實例11 | 13000至16000 | 62至68 | 5B | 20至25 | 1 | 2 | 3 | 優良 |
實例12 | 8000至12000 | 62至68 | 5B | 20至25 | 2 | 3 | 4 | NM |
實例13 | 8000至12000 | 62至68 | 5B | 20至25 | 2 | 3 | 5 | NM |
實例14 | 8000至12000 | 62至68 | 5B | 20至25 | 2 | 3 | NM | |
實例15 | 13000至17000 | 62至68 | NM | NM | NM | NM | NM | NM |
實例16 | 10000至15000 | 62至68 | NM | NM | NM | NM | NM | NM |
實例17 | 3000至5000 | 62至68 | 5B | 30至35 | 2 | 3 | 5 | NM |
實例18 | 13000至17000 | 62至68 | NM | NM | NM | NM | NM | NM |
實例19 | 15000至20000 | 62至68 | NM | NM | NM | NM | NM | NM |
實例20 | 8000至12000 | 62至68 | NM | NM | NM | NM | NM | NM |
實例21 | 8000至12000 | 62至68 | NM | NM | NM | NM | NM | NM |
實例22 | 7000至11000 | 30至40 | NM | 26000 | 22 | NM | NM | NM |
實例23 | 7000至11000 | 30至40 | NM | 22000 | 20 | NM | NM | NM |
實例24 | 6000至10000 | 62至68 | 5B | 45 | 1.5 | 2.5 | 4 | NM |
實例25 | 15000至20000 | 50至65 | NM | NM | NM | NM | NM | NM |
實例26 | 20000至25000 | 50至65 | NM | NM | NM | NM | NM | NM |
進一步地,下文的表13總結如實例27至實例61中所述之不導電組成物的各種特性及測試性能屬性。
[表13]:各種不導電組成物之特性及測試性能測試結果(實例27至實例61)
實例編號 | 黏度@5 rpm,cP (錐狀體及板材) | 固體含量% | 黏附性 (PC/PET) | 射出模製洗出穩定性 |
實例27 | 11000至15000 | 45至50% | 3B至4B | NA |
實例28 | 16000至20000 | 45至50% | 3B | NA |
實例29 | 14000至17000 | 45至50% | 4B | NA |
實例30 | 16000至20000 | 45至50% | 4B | NA |
實例31 | 14000至17000 | 35至40% | 4B | NA |
實例32 | 16000至20000 | 35至40% | 5B | 優良 |
實例33 | 16000至20000 | 45至50% | 5B | 優良 |
實例34 | 11000至14000 | 35至40% | 5B | 優良 |
實例35 | 11000至15000 | 35至40% | 5B | 優良 |
實例36 | 14000至17000 | 43至48% | 3B | NA |
實例37 | 11000至14000 | 45至50% | 4B | NM |
實例38 | 11000至14000 | 45至50% | 4B | NM |
實例39 | 10000至14000 | 45至50% | NM | NM |
實例40 | 10000至14000 | 45至50% | NM | NM |
實例41 | 9000至14000 | 45至50% | NM | NM |
實例42 | 11000至14000 | 45至50% | 5B | 優良 |
實例43 | 16000至19000 | 30至35% | NM | NA |
實例44 | 11000至14000 | 30至35% | 4B | NA |
實例45 | 11000至14000 | 30至35% | NM | NA |
實例46 | 10000至14000 | 45至50% | NM | NM |
實例47 | 10000至16000 | 35至45% | 5B | NA |
實例48 | 12000至18000 | 35至40% | NM | NA |
實例49 | 14000至17000 | 35至40% | NM | NA |
實例50 | 9000至14000 | 55至58% | 5B | NA |
實例51 | 4000至7000 | 23至28% | 5B | NA |
實例52 | 16000至19000 | 35至40% | 5B | NA |
實例53 | 40000至44000 | 57至62% | 5B | NA |
實例54 | 36000至41000 | 57至62% | 5B | NA |
實例55 | 25000至30000 | 57至62% | 5B | NA |
實例56 | 25000至30000 | 57至62% | 5B | NA |
實例57 | 70000至130000 | 57至62% | 5B | NA |
實例58 | 50000至70000 | 57至62% | 5B | NA |
實例59 | 8000至14000 | 38至42% | 5B | 優良 |
實例60 | 15000至18000 | 55至59% | 5B | NA |
實例61 | 20000至27000 | 57至62% | NM | NA |
導電及不導電材料的相互相容性連同與不同可撓性聚合物基材、裝飾用油墨、黏著劑、封裝材料、及射出模製樹脂的相容性係對於IME及類似結構之製造的重要態樣。
濕潤銀墨組成物與各種PC基材之相容性
濕潤銀墨組成物與各種PC基材係高度相容。研究濕潤銀墨(實例1、17、23、及25)與PC膜基材(Makrafol DE1.4)的相容性,其中濕潤銀墨之網版印刷圖案(1000 µm線)的顯微影像係在使用噴射乾燥器乾燥之前於不同的時間間隔(立即(亦即,0分鐘)、1分鐘、2分鐘、3分鐘、5分鐘、及15分鐘)處擷取。這些結果描繪出銀墨與PC基材之極良好的相容性。
銀墨與介電油墨組成物的相互相容性,以及與各種初生及以圖形塗佈之PET及PC基材的相容性
所揭示的銀墨與介電油墨組成物係高度相互相容,並與各種初生及以圖形塗佈之PET及PC基材相容。實行黏附性測試(按照ASTM F1842-09進行測試)以展示乾燥銀與介電油墨與各種聚合物膜基材(PC、PET、及以圖形塗佈的PC膜基材)之相容性。下文之表14總結銀墨(實例2)與介電油墨(實例33及34)在各種初生PET(MacDermid Autotype AHU5、CT5、及HT5)、初生PC (Makrafol DE1.4)、及經列印在PC (MacDermid Autotype XFG2502L-HTR952)上的圖形油墨)膜基材上之黏附性測試的代表性結果。表4亦總結銀墨(實例2)在經塗佈於各種初生PET(MacDermid Autotype AhU5、CT5、及HT5)、初生PC (Makrafol DE1.4)、及經列印在PC (MacDermid Autotype XFG2502L-HTR952)上的圖形油墨)膜基材上之介電油墨(實例33及34)上之黏附性測試的代表性結果。
[表14]:
黏附性測試亦在下列上實行:
• 經印刷在初生PC (Makrafol DE1.4)上之銀墨(實例1);
• 經印刷在塗佈於初生PC (Makrafol DE1.4)上之介電油墨(實例32)上的銀墨(實例1);
• 經印刷在以圖形油墨印刷之PC (MacDermid Autotype XFG2502L-HTR952)上的銀墨(實例1);
• 經印刷在塗佈於以圖形油墨印刷之PC (MacDermid Autotype XFG2502L-HTR952)上之介電油墨(實例32)上的銀墨(實例1);
• 初生PC (Makrafol DE1.4)上之介電油墨(實例32);
• 經印刷在PC (MacDermid Autotype XFG2502L-HTR952)上的圖形油墨(實例32);
• 初生PC (Makrafol DE1.4)上之銀墨(實例10)/介電油墨(實例53)/銀墨(實例10)的多層堆疊;
• 初生PC (Makrafol DE1.4)上之銀墨(實例10)/介電油墨(實例54)/銀墨(實例10)的多層堆疊。
基材 類型 | 基材 塗層 | 銀墨 | 介電油墨 | 介電油墨 |
實例2 | 實例34 | 實例33 | ||
PET (AHU5) | 初生 | 5B | 5B | 5B |
實例33 | 5B | - - | - - | |
實例34 | 5B | - - | - - | |
PET (HT5) | 初生 | 5B | 5B | 56 |
實例33 | 5B | - - | - - | |
實例34 | 5B | - - | - - | |
PET (CT5) | 初生 | 58 | 58 | 5B |
實例33 | 5B | - - | - - | |
實例34 | 5B | - - | - - | |
PC (Makrafol DE1.4) | 初生 | 56 | 58 | 5B |
實例33 | 58 | - - | - - | |
實例34 | 5B | - - | - - | |
圖形印刷PC (XFG2502L-HTR952) | 初生 | 5B | 5B | 5B |
實例33 | 5B | - - | - - | |
實例34 | 5B | - - | - - |
所有這些樣本均顯示按照ASTM F1842-09之5B黏附性測試結果。
加速環境測試
當按照JEDEC 22-A101(環境測試,85℃/85 RH)及IEC 60068-2-2(熱老化測試/乾熱測試)在不同的加速環境測試條件下進行測試時,所揭露之銀墨及介電油墨組成物係高度強健且穩定的。典型的測試結構由藉由在初生PC上網版印刷及藉由噴射乾燥進行乾燥所製備的導電銀電路跡線之500 µm線組成。在暴露至85℃/85 RH或110℃之任一者持續100至1000小時之前及之後,測量這些線的電阻。同樣地,介電油墨//銀墨//介電油墨之堆疊樣本亦經製備,並測量電阻導電銀電路跡線。進一步地,在使這些樣本暴露至85℃/85 RH或110℃之任一者持續100至1000小時之後,這些油墨的黏附力係按照ASTM F1842-09進行測試。
表5總結在暴露至85℃/85 RH或110℃持續100小時之後,使用銀墨(實例10)及初生PC (Makrafol DE1.4)上之介電油墨(實例47)//銀墨(實例10)//介電油墨(實例47)堆疊製備之代表性測試結構的電阻變化百分率(% ΔR,按照方程式1計算)。
電阻變化百分率
(%ΔR)=[之後的電阻
-之前的電阻
/之前的電阻
](方程式1)
暴露至環境測試條件後之上述可靠度測試結構的黏附性測試係按照ASTM F1842-09實施,且結果係總結於表15中。
[表15]:在暴露至85℃/85 RH或110℃持續100小時之後,各種代表性測試結構之電阻變化百分率(% ΔR,按照方程式1計算)。
網版印刷銀層//介電層//以圖形層塗佈之可熱成形PC基材的堆疊
測試結構 | 乾燥條件 | 85℃/85 RH持續100小時 | 110℃持續100小時 | ||
(% ΔR) | 黏附性結果 | (% ΔR) | 黏附性結果 | ||
測試圖案由經印刷在初生PC (Makrafol DE1.4)上之銀墨(實例10)的500 µm線組成。 | 120℃持續6分鐘。 | -6.1 | 5B | -6.7 | 5B |
120℃持續6分鐘,隨後80℃爐烤5小時。 | -3.4 | 5B | -6.1 | 5B | |
在初生PC基材(Makrafol DE1.4)上製備的堆疊由下列組成: 介電油墨的矩形圖案(實例47,兩層)//銀墨的測試跡線(實例10,500 µm線寬,經印刷在第一介電油墨層上)//介電油墨的矩形圖案(實例47,兩層),以覆蓋銀測試跡線。 | 以120℃乾燥銀墨6分鐘,並以120℃乾燥介電油墨的兩層(第1層乾燥4分鐘且第2層乾燥8分鐘)。 | -1.9 | 5B | -1.1 | 5B |
以120℃乾燥銀墨6分鐘,並以120℃乾燥介電油墨(第1層乾燥4分鐘且第2層乾燥8分鐘)。總體堆疊在80℃下爐烤5小時。 | -0.6 | 5B | -0.2 | 5B |
圖2顯示網版印刷銀層//介電層//以圖形層塗佈之可熱成形PC基材(MacDermid Autotype Xtraform PC)的代表性堆疊(90);及使用在以黑色圖形油墨塗佈的可熱成形PC基材上之實例1(銀墨)、實例47(介電油墨)製備的影像樣本,其等一經熱成形即製成結構110、120、及130。這些結構中所印刷的互連線係電氣連接,且在熱成形之後不顯示顯著的電阻變化。針對熱成形程序,如圖2所示之網版印刷樣本100以及組件安裝樣本係暴露至170 ± 2℃的溫度30至35秒。印刷跡線在熱成形程序期間係面向加熱器。在暴露至熱時,印刷基材軟化,並在4巴的真空壓力下放置在成形工具上方10至15秒以得到如圖2所示之3D熱成形基材,如110、120、及130。圖2所示之影像100、110、120、及130對應於實例1。類似地,亦以PC及PET基材上的不同組合針對熱成形性能測試實例2、實例4、實例33、實例34、實例35、及實例42之印刷結構,並發現係可熱成形的。
導電及不導電組成物的關鍵屬性之一係可熱成形性。此對於IME及類似應用特別重要。欲評定2D電路跡線經成形為3D電路/裝置的可熱成形性,採用圓錐體結構測試載具。欲判定跡線的熱成形屬性,使用稱為「圓錐體可成形性測試程序(Cone Formability Test Procedure)」的內部開發程序。在此程序中,於平坦聚合基材上測量一系列電路跡線之導電性。在成形之後,使用電阻變化連同其他失效機制來評定可熱成形性的程度。此測試結構具有直線跡線,其具有150 µm、300 µm、500 µm、及1000 µm之線寬。這些平坦線結構係熱成形為可係正或負的柱狀圓錐形。在熱成形期間,各種跡線經歷可從0%變化至58%的拉伸。判定可熱成形性的關鍵性能度量係經拉伸而不斷裂或從基材脫層,且較佳地具有低電阻變化。
銀墨之熱成形屬性
銀墨之熱成形屬性係按照如先前所述之「圓錐體可成形性測試程序」進行評估。在一典型程序中,銀墨係印刷在可熱成形聚合物基材(例如PC或PET)上,且導電測試電路之電阻係在熱成形程序之前及之後測量,以記錄在各種%應變下的電阻變化。圖3a及圖3b分別顯示在可熱成形PC基材(Makrafol DE1.4)上於熱成形之前及之後的典型測試樣本之代表性影像。在成形之後,使用電阻變化連同其他失效機制來評定可熱成形性的程度。例如,圖3c及圖3d分別顯示在熱成形之前及之後的銀墨(實例1、實例2、實例10、及實例11)之1000 µm線寬的導電銀電路跡線之電阻變動。熱成形之前(圖3c)及之後(圖3d)的電阻係分別依據%應變位置及應變%繪製。在熱成形期間,電路線/跡線係形成為圓錐形。結果,電路線跡線經受拉伸。
銀墨與各種PC基材之相容性及熱成形屬性
銀墨與各種PC基材之相容性及熱成形屬性係按照如先前所述之「圓錐體可成形性測試程序」進行評估。在一典型程序中,銀墨係印刷在不同類型的可熱成形PC基材(DE作為Makrafol DE1.4,V3作為MacDermid Autotype XFG250 M HCL V3,且2L作為MacDermid Autotype XFG250 2L基材)以及以圖形油墨塗佈的PC基材(GCPC作為MacDermid Autotype XFG2502L-HTR952)上。由於發現以圖形油墨塗佈的PC基材(GCPC)輕度導電,欲避免短路,在印刷銀墨之前印刷一層介電油墨(實例33)。在熱成形程序之前及之後測量銀導電測試電路的電阻,以記錄各種%應變下的電阻變化。在成形之後,使用電阻變化連同其他失效機制來評定可熱成形性的程度。例如,圖4a及圖4b分別顯示在熱成形之前及之後,銀墨(實例10)在各種PC基材上之1000 µm線寬的導電銀電路跡線之電阻變動。熱成形之前(圖4a)及之後(圖4b)的電阻係分別依據%應變位置及應變%繪製。在熱成形期間,電路線/跡線係形成為圓錐形。結果,電路線跡線經受拉伸。圖4c顯示銀墨(實例10)在各種PC基材上於30%、37%、及46%應變下之1000 µm線寬的導電銀電路跡線的顯微影像,在低於40%應變下顯露出極小的變形。
雙堆疊介電及銀墨之相容性及熱成形屬性
雙堆疊介電及銀墨之相容性及熱成形屬性係按照如先前所述之「圓錐體可成形性測試程序」進行評估。典型雙堆疊電路總成係藉由首先在可熱成形聚合物基材(例如PC或PET)上印刷介電油墨層(障壁介電層),隨後印刷導電銀電路跡線而製備。在熱成形程序之前及之後測量銀導電測試電路的電阻,以記錄各種%應變下的電阻變化。圖5a及圖5b分別顯示在熱成形之前及之後的典型測試樣本之代表性影像。在成形之後,使用電阻變化連同其他失效機制來評定可熱成形性的程度。例如,圖5c及圖5d分別顯示在熱成形之前及之後,經印刷在介電油墨(實例33及35)上的銀墨(實例1)、經印刷在介電油墨(實例33及35)上的銀墨(實例10)、及經印刷在介電油墨(實例35)上的銀墨(實例11)之1000 µm線寬的導電銀電路跡線的電阻變動。熱成形之前(圖5c)及之後(圖5d)的電阻係分別依據%應變位置及應變%繪製。在熱成形期間,電路線/跡線係形成為圓錐形。結果,電路線跡線經受拉伸。
三堆疊介電及銀墨之相容性及熱成形屬性
三堆疊介電及銀墨之相容性及熱成形屬性係按照如先前所述之「圓錐體可成形性測試程序」進行評估。典型三堆疊電路總成係藉由首先在可熱成形聚合物基材(例如PC或PET)上印刷介電油墨層(障壁介電層),接下來印刷導電銀電路跡線,且隨後印刷另一介電油墨層(保護層)而製備。在熱成形程序之前及之後測量導電銀測試電路的電阻,以記錄各種%應變下的電阻變化。圖6a及圖6b分別顯示在熱成形之前及之後的典型測試樣本之代表性影像。在成形之後,使用電阻變化連同其他失效機制來評定可熱成形性的程度。例如,圖6c及圖6d顯示銀墨(實例10)之1000 µm線寬的導電電路跡線的電阻變動,其中障壁介電層及保護層係經選擇為實例35或實例47之任一者或其等之組合。熱成形之前(圖6c)及之後(圖6d)的電阻係分別依據%應變位置及應變%繪製。在熱成形期間,電路線/跡線係形成為圓錐形。結果,電路線跡線經受拉伸。
用作導電黏著劑以附接各種SMD組件之可熱成形導電組成物
實例1至實例26中所揭示的可熱成形導電組成物亦可用作導電黏著劑,以將各種SMD組件、LED等附接至可熱成形導電銀墨電路跡線。這些配方的黏度可經最佳化,以藉由施配或模版印刷之任一者來設置這些導電黏著劑。可熱成形導電黏著劑與銀墨及基材的相容性對於製造IME結構極為關鍵。圖7描繪用於將SMD組件附接在可成形導電銀電路跡線(實例10)上之可熱成形導電黏著劑組成物(實例7)的代表性應用。例如,圖7a顯示實例7之650至700 µm直徑之施配點(濕式沉積物)的顯微影像。圖7b及圖7c分別顯示可成形導電銀電路跡線(實例10)上之SMD 1206晶片及SMD 1206 LED之濕式總成的顯微影像。圖7d及圖7e分別顯示圖7b及圖7c的熱固化及乾燥成形。
代表性導電電路結構之熱成形屬性
按照如先前所述之「圓錐體可成形性測試程序」評估代表性導電電路結構之熱成形屬性,其中組件(諸如SMD 1206晶片或SMD 1206 LED)係使用導電黏著劑(實例7)附接在可熱成形PC基材(DE作為Makrafol DE1.4)上的銀墨(實例10)上。典型的總成係藉由首先在可熱成形聚合物基材(DE)上印刷銀墨(實例10)導電電路跡線,接下來施配實例7,且隨後附接組件SMD 1206晶片及SMD 1206 LED而製備。在熱成形之前及之後,藉由供應電流來檢查這些導電電路結構的電連續性。例如,圖8a及圖8b顯示施加電流之前及之後的印刷導電軌上之LED。具體地,發光LED指示電路結構的連續性,且對應的應變位置亦在圖8a及圖8b中指示。這些結果指示使用實例7作為用於可熱成形電路總成構造之導電黏著劑的合適性。
網版印刷銀層/可熱成形PC基材之代表性堆疊
圖9顯示網版印刷銀層//可熱成形PC基材(140)的代表性堆疊,其一經射出模製即製成結構150。使用中心閘在射出模製機上執行射出模製。腔穴尺寸係100 mm × 80 mm。射出模製係在厚度2至3 mm的平坦形狀中實行,且該部分的最大重量係大約的。實例10係用作銀墨及初生PC基材(Makrofol DE1.4)以製備結構140,而此結構經受以PC樹脂射出模製以製成結構150。類似地,亦以各種射出模製樹脂(諸如PC、ABS等)的不同組合針對射出模製性能測試實例1、實例2、實例4、實例33、實例34、實例35、及實例42之印刷結構,並發現在射出模製期間係穩定的。
代表性功能3D電子裝置
圖10顯示代表性功能3D電子裝置的設計及構造。此裝置係藉由網版印刷及乾燥實例1,隨後使用實例1附接LED,並接著熱成形整體堆疊來製成。圖10係能夠執行觸控開關應用之展示機的手持型(a及b)及控制台型(c及d)的影像。程序涉及首先印刷實例1,隨後乾燥。在第二步驟中涉及模版印刷實例7及LED放置,隨後乾燥。藉由透過鈕扣型電池提供電力而使LED發光。
代表性全功能IME裝置
圖11顯示代表性全功能IME裝置的構造,其可視為典型飛機控制盤的原型。圖11a及圖11b分別係處於關斷及接通條件下之IME裝置的光學影像。圖11b展示此類IME展示機的電容式觸控開關應用。這些裝置係藉由多步驟製程(諸如,網版印刷、熱乾燥、施配、SMT組件總成、高壓熱成形、雷射切割、射出模製(PC樹脂))來製成,並使用各種市售圖形油墨(諸如Proell)及銀墨(實例10)、介電油墨(實例47)、導電黏著劑(實例7)、及各種MacDermid Autotype Xtraform PC基材。這些IME裝置係構造為單一膜結構,其中首若干層的裝飾用圖形油墨(黑色及白色)係經印刷及乾燥。隨後係使用銀及介電油墨印刷導電電子電路層並乾燥,且使用導電黏著劑組裝LED。此整體堆疊進一步係經熱成形,經雷射切割以按照所欲形狀修整,並以PC樹脂背向射出模製。在圖11b中,藉由透過鈕扣型電池提供電力而使LED發光。
以上實施方式已藉由說明及繪示的方式提供,且不旨在限制隨附申請專利範圍之範疇。本文所繪示之目前較佳實施例中的許多變化對所屬技術領域中具有通常知識者而言將係顯而易見的,且仍在隨附申請專利範圍及其均等者之範疇內。
10:可熱成形PC或PET基材
20:網版印刷導電互連
30:網版印刷電絕緣介電層
40:SMT組件或LED
50:SMT組件或LED
60:SMT組件或LED
70:熱成形3D電子電路系統
80:熱成形3D電子電路系統
90:網版印刷銀層//介電層//以圖形層塗佈之可熱成形PC基材的堆疊
100:樣本
110:結構
120:結構
130:結構
現將涉及下列非限制性圖式描述本發明,其中:
[圖1]顯示膜內電子結構(IME)之通用製造程序步驟的示意圖。
[圖2]顯示具有不同材料之在可熱成形PC基材上之油墨堆疊的示意圖:網版印刷銀層//介電層//以圖形層塗佈之可熱成形PC基材的堆疊(90);及在以黑色圖形油墨塗佈的可熱成形PC基材上使用實例1(銀墨)及實例47(介電油墨)製備之實際樣本(100)的影像,其等一經熱成形即製成結構110、120、及130。
[圖3]顯示(a及b)按照「圓錐體可成形性測試程序」,分別在熱成形之前及之後,典型可熱成形測試樣本的代表性光學影像;(c及d)隨應變%改變,分別在熱成形之前及之後,使用銀墨(實例1、實例2、實例10、及實例11)製備之1000 µm線寬的導電銀電路跡線的電阻變動。
[圖4]顯示(a及b)按照「圓錐體可成形性測試」,隨應變%改變,分別在熱成形之前及之後之在各種PC基材上使用銀墨(實例10)製備之1000 µm線寬的導電銀電路跡線的電阻變動。圖4(c)顯示針對如圖4(b)所示之測試樣本,在0%、30%、37%、及46%應變下之1000 µm線寬的導電銀電路跡線的顯微影像。
[圖5]顯示(a及b)按照「圓錐體可成形性測試程序」,分別在熱成形之前及之後,使用介電油墨及銀墨製備的典型「雙堆疊」可熱成形測試樣本的代表性光學影像;(c及d)分別在熱成形之前及之後,經印刷在介電油墨(實例33及35)上的銀墨(實例1)、經印刷在介電油墨(實例33及35)上的銀墨(實例10)、及經印刷在介電油墨(實例35)上的銀墨(實例11)之1000 µm線寬的導電銀電路跡線的電阻變動。
[圖6]顯示(a及b)按照「圓錐體可成形性測試程序」,分別在熱成形之前及之後,使用介電油墨及銀墨製備的典型「三堆疊」可熱成形測試樣本的代表性光學影像;(c及d)銀墨(實例10)之1000 µm線寬的導電電路跡線的電阻變動,其中障壁介電層及保護層係經選擇為實例35或實例47之任一者或其等之組合。
[圖7]顯示用於將SMD組件附接在可成形導電銀電路跡線(實例10)上之可熱成形導電黏著劑組成物(實例7)的代表性應用;(a)施配點(濕式沉積物)的顯微影像;(b及c)分別係可成形導電銀電路跡線(實例10)上之SMD 1206晶片及SMD 1206 LED之濕式總成的顯微影像;(d及e)(b)及(c)的熱固化及乾燥成形。
[圖8]顯示按照「圓錐體可成形性測試程序」,分別在熱成形(a)之前及(b)之後,典型可熱成形測試樣本的代表性光學影像。可熱成形導電黏著劑(實例7)已用於SMD 1206晶片及SMD 1206 LED在可成形導電銀電路跡線(實例10)上的附接。熱成形實驗(a)之前及(b)之後在印刷導電跡線上的發光LED指示電路結構的連續性及對應的應變位置。
[圖9]顯示網版印刷銀層//可熱成形PC基材(140)的代表性堆疊,其一經射出模製即製成結構150。
[圖10]顯示功能3D電子裝置的代表性設計及構造;能夠執行觸控開關應用之展示機的手持型(a及b)及控制台型(c及d)的影像;藉由網版印刷及乾燥實例1,隨後使用實例1附接LED,並接著熱成形整體堆疊來製成。
[圖11]顯示(a)代表性全功能IME裝置,其可視為處於關斷條件下之典型飛機控制盤的原型;(b)展示此類IME展示機的電容式觸控開關應用。
10:可熱成形PC或PET基材
20:網版印刷導電互連
30:網版印刷電絕緣介電層
40:SMT組件或LED
50:SMT組件或LED
60:SMT組件或LED
70:熱成形3D電子電路系統
80:熱成形3D電子電路系統
Claims (43)
- 一種用於在模內電子(IME)組件之製造中使用的組成物,該組成物含有黏合劑,該黏合劑包含:交聯劑,其包含三聚氰胺甲醛;熱塑性樹脂,其包含羥基基團;及溶劑;其中該熱塑性樹脂包含:基於該熱塑性樹脂的總重量之從20至60wt%之聚胺甲酸酯樹脂;從5至30wt%之聚酯樹脂;及從20至60wt%之苯氧基樹脂。
- 如請求項1之組成物,其中該三聚氰胺甲醛包含六甲氧基甲基三聚氰胺。
- 如請求項1或2之組成物,其中該交聯劑進一步包含異氰酸酯、及/或聚異氰酸酯、及/或封閉型聚異氰酸酯。
- 如請求項1或2之組成物,其中該熱塑性樹脂包含聚胺甲酸酯樹脂、聚酯樹脂、聚丙烯酸酯樹脂、聚乙烯酯樹脂、苯氧基樹脂、及酮樹脂中之一或多者。
- 如請求項4之組成物,其中該熱塑性樹脂包含聚胺甲酸酯樹脂、聚酯樹脂、及苯氧基樹脂。
- 如請求項1或2之組成物,其中該熱塑性樹脂:包含均聚物、及共聚物、及/或三聚物;及/或具有小於100℃的玻璃轉移溫度;及/或具有從1000至100000g/莫耳之重量平均分子量;及/或具有小於100℃的軟化點;及/或具有大於20mgKOH/g的羥基含量(OH數)。
- 如請求項1或2之組成物,其包含:基於交聯劑及熱塑性樹脂之總量之從1至40wt%的該交聯劑;及從60至99wt%的該熱塑性樹脂。
- 如請求項1或2之組成物,其中該溶劑包含二醇醚乙酸酯、二醇醚、酯、酮、醇、及烴中之一或多者。
- 如請求項8之組成物,其中該溶劑包含:基於該溶劑之總重量之至多95wt%的二醇醚乙酸酯;及/或至多95wt%的二醇醚;及/或至多15%的酯;及/或至多40wt%的酮;及/或至多80wt%的醇;及/或至多30wt%的烴。
- 如請求項1或2之組成物,其中該黏合劑進一步包含:熱固性樹脂,其包含丙烯酸樹脂及環氧樹脂中之一或兩者;及固化催化劑,其用於固化該熱固性樹脂。
- 如請求項1或2之組成物,其中該黏合劑進一步包含一或多個功能添加劑,該一或多個功能添加劑選自界面活性劑、流變改質劑、分散劑、消泡劑、去膠黏劑、助滑添加劑、抗垂流劑、整平劑、表面活性劑、表面張力減少劑、助黏劑、抗結皮劑、消光劑、著色劑、染料、顏料、及濕潤劑中之一或多者。
- 如請求項1或2之組成物,其中該黏合劑包含:從0.5至12wt%的該交聯劑;從10至40wt%的該熱塑性樹脂;及從40至85wt%的溶劑;可選地:從0.1至30wt%的熱固性樹脂及從0.1至3wt%之用於固化該熱固性樹脂的固化催化劑;及/或從0.1至20wt%的功能添加劑。
- 如請求項1之組成物,其進一步包含導電粒子。
- 如請求項13之組成物,其中該等導電粒子:包含金屬粒子中之一或多者,其選自銀粒子、銅粒子、黃銅粒子、鎳粒子、金粒子、鉑粒子、鈀粒子、金屬合金粒子、塗銀銅粒子、塗銀黃銅粒子、銀-鎳合金粒子、及銀-銅合金粒子中之一或多者;及/或包含碳粒子,其選自石墨粒子、石墨片、碳黑粒子、石墨烯片、石墨烯粒子、及奈米碳管中之一或多者;及/或展現從1.25至7μm的一平均粒徑(d50)、從2至4g/cc的一敲緊密度、從0.3至2.1m2/g的一表面積、及從0.06至1.3wt%的一有機含量中之一或多者;及/或呈片、球體、不規則形狀粒子、奈米粉末、及奈米線中之一或多者的形式。
- 如請求項13或請求項14之組成物,其包含:從30至85wt%的黏合劑;及從15至70wt%的導電粒子。
- 如請求項13或14之組成物,其包含:從30至85wt%的黏合劑;及從15至70wt%的導電粒子,且其中該黏合劑包含:從0.2至6wt%的交聯劑;從1至7.5wt%的聚胺甲酸酯樹脂;從0.1至5.5wt%的聚酯樹脂;從1至7.5wt%的苯氧基樹脂;從0至10wt%的熱固性樹脂;從0至1wt%的固化催化劑;從0.2至10wt%的功能添加劑;從0至60wt%的二醇醚乙酸酯;從0至40wt%的二醇醚;從0至5wt%的酯;及從0至30wt%的酮。
- 如請求項13或14之組成物,其呈導電油墨的形式。
- 如請求項13或14之組成物,其呈導電黏著劑的形式。
- 如請求項1之組成物,其進一步包含不導電粒子。
- 如請求項19之組成物,其中該等不導電粒子:包含有機不導電粒子,其選自纖維素、蠟、聚合物微粒子、不導電碳粒子、及氧化石墨烯中之一或多者;及/或 包含無機不導電粒子,其選自雲母、矽石(SiO2)、發煙矽石、滑石、二氧化鈦(TiO2)、氧化鋁、鈦酸鋇(BaTiO3)、氧化鋅(ZnO)、及氮化硼(BN)中之一或多者,可選地其中該等無機不導電粒子係次微米及微米大小;及/或展現小於或等於10μm的一平均粒徑(d50)。
- 如請求項19或請求項20之組成物,其包含:從0至50wt%的不導電粒子;及從50至100wt%的黏合劑。
- 如請求項19或20之組成物,其包含:從40至100wt%的黏合劑;及從0至60wt%的不導電粒子,且其中該黏合劑包含:從0.5至10wt%的交聯劑;從2至12wt%的聚胺甲酸酯樹脂;從0.5至10wt%的聚酯樹脂;從2至18wt%之苯氧基樹脂;從0至30wt%的熱固性樹脂;從0至3wt%的固化催化劑;從0.3至17wt%的功能添加劑;從0至41.7wt%的二醇醚乙酸酯;從0至60wt%的二醇醚;從0至30wt%的酮;從0至50wt%的醇;及從0至20wt%的烴。
- 如請求項1、2、19、20中任一項之組成物,其呈介電油墨的形式。
- 如請求項1、2、19、20中任一項之組成物,其呈不導電黏著劑形式。
- 如請求項1、2、19、20中任一項之組成物,其呈封裝材料的形式。
- 如請求項1或2之組成物,其進一步包含著色劑、及/或染料、及/或顏料,該組成物呈圖形油墨的形式。
- 一種製造如請求項1至26中任一項之組成物之方法,該方法包含:提供溶劑;提供具有羥基基團之熱塑性樹脂;在從50至100℃的溫度下於該溶劑中溶解該熱塑性樹脂;使該溶液冷卻至室溫;可選地將下列之一或多者添加至該經冷卻溶液:功能添加劑、熱固性樹脂、用於固化該熱固性樹脂之固化催化劑、導電粒子、及不導電粒子。
- 一種製造模內電子(IME)組件之方法,該方法包含:製備一坯料;及熱成形該坯料,其中製備該坯料包含在一可熱成形基材上形成一或多個結構,各結構係藉由包含下列之一方法形成:將如請求項1至26中任一項之組成物設置在一可熱成形基材上;及 在從20至150℃之一溫度下使該組成物乾燥達從0.5至60分鐘。
- 如請求項28之方法,其中該一或多個結構係選自一導電層、一導電軌層、一黏著劑附接層、一介電層、一封裝材料層、一圖形層、及一障壁層。
- 如請求項28或請求項29之方法,其中該一或多個結構包含一多層堆疊。
- 如請求項28或29之方法,其中該一或多個結構包含一印刷電路板。
- 如請求項28或29之方法,其中設置該組成物包含印刷該組成物。
- 如請求項28或29之方法,其中該基材包含聚碳酸酯(PC)及/或聚對苯二甲酸乙二酯(PET)。
- 如請求項28或29之方法,其中該熱成形係在從140℃至210℃之一溫度下及/或在從0.25MPa至0.4MPa之一壓力下及/或在範圍從6MPa至12MPa之一壓力下實行。
- 如請求項28或29之方法,其進一步包含使用導電黏著劑或不導電黏著劑將一或多個電子裝置附接至該坯料,該導電黏著劑係如請求項18之組成物,且該不導電黏著劑係如請求項24之組成物,其中該附接在熱成形之前及/或之後發生。
- 如請求項28或29之方法,其進一步包含在熱成形之後,使用射出模製將一樹脂層施加至該基材,其中該樹脂包含聚碳酸酯(PC)、聚對苯二甲酸乙二酯(PET)、丙烯腈丁二烯苯乙烯(ABS)、聚丙烯(PP)、聚酯、聚(甲基丙烯酸甲酯)(PMMA)、低密度聚乙烯(LDPE)、高密度聚乙烯(HDPE)、聚苯乙烯(PS)、及熱塑性聚胺甲酸酯(TPU)中之一或多者。
- 如請求項36之方法,其中該射出模製係在從170至330℃之一溫度下實行。
- 如請求項28或29之方法,其中該模內電子(IME)組件包含一電容式觸控開關、一電阻式觸控開關、或一電容式觸控感測器。
- 如請求項28或29之方法,其中該模內電子(IME)組件包含一顯示器、一發光體/燈、一感測器、一指示器、及一觸覺/觸控回饋裝置中之一或多者。
- 一種模內電子(IME)組件,其係根據如請求項28至39中任一項之方法製造。
- 一種模內電子(IME)組件,其包含如請求項1至26中任一項之組成物。
- 如請求項40或請求項41之模內電子(IME)組件,其包含一電容式觸控開關或一電阻式觸控開關。
- 如請求項40或請求項41之模內電子(IME)組件,其包含一顯示器、一發光體/燈、一感測器、一指示器、及一觸覺/觸控回饋裝置中之一或多者。