TWI814628B - 用於製備得自於香蕉假莖的纖維材料之方法及其所製得的纖維材料 - Google Patents
用於製備得自於香蕉假莖的纖維材料之方法及其所製得的纖維材料 Download PDFInfo
- Publication number
- TWI814628B TWI814628B TW111141185A TW111141185A TWI814628B TW I814628 B TWI814628 B TW I814628B TW 111141185 A TW111141185 A TW 111141185A TW 111141185 A TW111141185 A TW 111141185A TW I814628 B TWI814628 B TW I814628B
- Authority
- TW
- Taiwan
- Prior art keywords
- fermentation
- banana
- obtaining
- treatment
- pseudostem
- Prior art date
Abstract
本發明揭示一種用於製備得自於香蕉假莖的纖維材料之方法，其包括：令一香蕉假莖進行一壓榨處理，藉此而得到一經壓榨的香蕉假莖；使用釀酒酵母菌(
Saccharomyces cerevisiae)來對該經壓榨的香蕉假莖進行一發酵反應，藉此而得到一發酵培養物；使用果膠酶來對該發酵培養物進行一發酵-水解處理，藉此而得到一發酵-水解產物；令該發酵-水解產物進行一固液分離處理，藉此而得到一固體部分；以及對該固體部分依序進行鹼處理、水洗處理、漂白處理、軟化處理以及乾燥處理，藉此而得到一纖維材料。
Description
本發明是有關於一種用於製備得自於香蕉假莖的纖維材料之方法及其所製得的纖維材料。
香蕉(學名：
Musa×
paradisiaca；中文俗名：甘蕉、芎蕉、芽蕉以及弓蕉)是芭蕉科(
Musaceae)的多年生草本植物，為目前世界上第四大糧食作物。然而，在採收香蕉果實後，會留下大量的香蕉假莖(pseudostem)農業廢棄物，且該香蕉假莖棄置時會導致相關的蟲害，例如螞蟻與象鼻蟲(weevil)，進而在腐化的過程中產生溫室氣體(如甲烷)的排放。因此，如何同時兼顧農業廢棄物的蟲害、糧食需求與環保問題，農業剩餘資源的有效利用已成為本領域的相關研究人員所致力的目標。
由於香蕉假莖所含有的纖維素(cellulose)、半纖維素(hemicellulose)以及木質素(lignin)會互相纏繞包覆而形成複雜且堅韌的網狀結構，因此通常需要先對香蕉假莖進行處理俾以促進去木質素作用(delignification)。目前處理香蕉假莖的方法包括：(i)物理性，藉由刮除(scrape)的方式；以及(ii)化學性，藉由酸處理(acid treatment)或鹼處理(alkaline treatment)。然而，這些方法皆存在有纖維萃取效率不佳、細纖維(例如類棉纖維)流失以及產量低等問題。
目前已有研究嘗試藉由微生物與酵素的處理方式而將農業廢棄物應用於纖維的開發。例如，CN 111996603 A揭示一種鳳梨葉纖維的生物萃取方法，其包括將鳳梨葉依序進行黑麴菌(
Aspergillus niger)以及酵素水解(enzymatic hydrolysis)的反應而萃取出鳳梨葉纖維，其中該酵素可以包括：漆酶(laccase)、木聚糖酶(xylanase)以及果膠酶(pectinase)。在該專利案的實施例中，鳳梨葉被處理以各種不同的酵素溶液，繼而對所製得的鳳梨葉纖維進行纖維殘膠量(residual sericin)、斷裂強度、粗細度、柔軟度以及色澤的分析，而結果發現：相較於單獨使用果膠酶，組合使用漆酶以及木聚糖酶來處理所得的鳳梨葉纖維才能產生優異的效用，這表示：並不是具有去木質素作用的酵素皆適用於鳳梨葉纖維的萃取。
雖然已存在有上述相關研究，目前仍需發展出一種能夠有效地利用農業廢棄物(特別是香蕉假莖)並能提高纖維產率的製程，以供產業界之所需。
發明概要
於本發明中，申請人發現對一香蕉假莖依序進行壓榨處理、發酵反應、發酵-水解處理以及固液分離處理，可以有效地提高得自於香蕉假莖的纖維材料之產率，且能進一步藉由蒸餾處理來獲得生質酒精以及可供作為有機肥料的蒸餾殘餘物。
於是，在第一個方面，本發明提供一種用於製備得自於香蕉假莖的纖維材料之方法，其包括：
(a) 令一香蕉假莖進行一壓榨處理，藉此而得到一經壓榨的香蕉假莖；
(b) 使用釀酒酵母菌(
Saccharomyces cerevisiae)來對該經壓榨的香蕉假莖進行一發酵反應，藉此而得到一發酵培養物；
(c) 使用果膠酶來對該發酵培養物進行一發酵-水解處理，藉此而得到一發酵-水解產物；
(d) 令該發酵-水解產物進行一固液分離處理，藉此而得到一固體部分；以及
(e) 對該固體部分依序進行鹼處理、水洗處理、漂白處理、軟化處理以及乾燥處理，藉此而得到一纖維材料。
在第二個方面，本發明提供一種得自於香蕉假莖的纖維材料，它是藉由一如上所述的方法而被製得。
發明的詳細說明
要被瞭解的是：若有任何一件前案刊物在此被引述，該前案刊物不構成一個下述承認：在台灣或任何其他國家之中，該前案刊物形成本技藝中的常見一般知識之一部分。
為了這本說明書之目的，將被清楚地瞭解的是：文字“包含有(comprising)”意指“包含但不限於”，以及文字“包括(comprises)”具有一對應的意義。
除非另外有所定義，在本文中所使用的所有技術性與科學術語具有熟悉本發明所屬技藝的人士所共同瞭解的意義。一熟悉本技藝者會認知到許多與那些被描述於本文中者相似或等效的方法和材料，它們可被用於實施本發明。當然，本發明決不受到所描述的方法和材料之限制。
本發明提供一種用於製備得自於香蕉假莖的纖維材料之方法，其包括：
(a) 令一香蕉假莖進行一壓榨處理，藉此而得到一經壓榨的香蕉假莖；
(b) 使用釀酒酵母菌(
Saccharomyces cerevisiae)來對該經壓榨的香蕉假莖進行一發酵反應，藉此而得到一發酵培養物；
(c) 使用果膠酶來對該發酵培養物進行一發酵-水解處理，藉此而得到一發酵-水解產物；
(d) 令該發酵-水解產物進行一固液分離處理，藉此而得到一固體部分；以及
(e) 對該固體部分依序進行鹼處理、水洗處理、漂白處理、軟化處理以及乾燥處理，藉此而得到一纖維材料。
適用於本發明的香蕉可包括，但不限於：華蕉屬物種(
Cavendishspp.)、芭蕉屬物種(
Musaspp.)、象腿蕉屬物種(
Ensetespp.)(又稱為衣蕉屬物種)，以及它們的組合。在本發明的一個較佳具體例中，該香蕉是華蕉屬物種。
如本文中所使用的，術語“假莖(pseudostem)”以及“殘莖(stubble)”可被交替地使用。
依據本發明，該壓榨處理、該發酵反應、該發酵-水解處理、該固液分離處理、該鹼處理、該水洗處理、該漂白處理、該軟化處理以及該乾燥處理可以採用熟習此項技藝者所詳知且慣用的技術來進行。可瞭解到的是，有關該等處理的操作條件會進一步隨著所使用的香蕉假莖的含水量以及用量等因素而被變動。而這些操作條件的選擇是熟習此項技藝者能例行性地自行決定的。
較佳地，在該方法的步驟(a)中，該壓榨處理是使用一油壓式壓榨機來進行，俾以將香蕉假莖的汁液移除約30-50%。
較佳地，在該方法的步驟(b)中，該發酵反應是在20-32℃下被進行。在本發明的一個較佳具體例中，該發酵反應是在28℃下被進行。
較佳地，在該方法的步驟(c)中，該發酵-水解處理是在15-55℃下被進行。在本發明的一個較佳具體例中，該發酵-水解處理是在50℃下被進行。
依據本發明，其進一步包括對在步驟(e)所得到的該纖維材料進行開纖(bale opening)，而得到束纖細度(tow fineness)分別約為0.9-5.0 decitex (dtex)以及40-60 dtex的纖維(fiber)。
較佳地，以所製得的纖維材料的總重量為計算基礎，該纖維材料包含有80 wt%的0.9-5.0 dtex之纖維以及20 wt%的40-60 dtex之纖維。
依據本發明，在進行該方法的步驟(a)之前，該香蕉假莖可先被進行一分段(segmenting)處理。在本發明的一個較佳具體例中，該香蕉假莖被分段成長度約為60-100 cm的大小。
依據本發明，在進行該方法的步驟(b)中的發酵培養的期間，可藉由添加一醣類來調整糖度(Brix)，較佳地，該糖度被維持在18至20 Brix。
較佳地，該醣類可選自於由下列所構成的群組：葡萄糖、果糖、蔗糖、以蔗糖為主要成分的食用糖，以及它們的組合。在本發明的一個較佳具體例中，該以蔗糖為主要成分的食用糖是砂糖。
較佳地，在該方法的步驟(b)中所得到的發酵培養物可進一步被進行一蒸餾處理，藉此而得到生質酒精以及可供作有機肥料的蒸餾殘餘物(distillation residue)。在本發明的一個較佳具體例中，該蒸餾處理是於78-100℃下被進行。
依據本發明，在該方法的步驟(c)中，果膠酶(pectinase)是商業上可購得的產品。在本發明的一個較佳具體例中，該果膠酶是購自於貝肯布自釀啤酒原料專賣(Bake n Brew Homebrew Supply)的Pectic Enzyme (廠牌：North Mountain Supply)。
如本文中所使用的，術語“發酵(fermentation)”、“培養(culturing)”以及“培育(cultivation)”可被交換地使用。有關發酵的操作程序與參數條件等是落在熟習此項技術之人士的專業素養與例行技術範疇內。
可瞭解到的是，有關發酵的操作條件會進一步隨著所使用的菌株以及該菌株與該香蕉假莖的用量比例等因素而被變動，以便達致最佳的發酵效果。而這些操作條件的選擇是熟習此項技藝者能例行性地自行決定的。
依據本發明，在該方法的步驟(e)中，該鹼處理是使用一鹼性溶液並在60-90℃下來進行歷時3小時。其中該鹼性溶液是選自於由下列所構成的群組：氫氧化鉀溶液、氫氧化鈉溶液、碳酸鈣溶液，以及它們的組合。較佳地，該鹼性溶液是2-4 wt%的氫氧化鉀溶液。更佳地，該鹼性溶液是2 wt%的氫氧化鉀溶液。
依據本發明，在該方法的步驟(e)中，該水洗處理是使用壓力被設定為100 bar的高壓水柱來沖洗以移除木質素(lignin)。
依據本發明，在該方法的步驟(e)中，該漂白處理是使用一漂白劑並在20-150℃下來進行歷時3小時。其中該漂白劑是選自於由下列所構成的群組：過氧化氫溶液、次氯酸鈉溶液、次氯酸鈣溶液、過硼酸鈉溶液，以及它們的組合。較佳地，該漂白劑是2-4 wt%的過氧化氫溶液。更佳地，該漂白劑是2 wt%的過氧化氫溶液。
依據本發明，在該方法的步驟(e)中，該軟化處理是使用一陰離子油脂來進行歷時90分鐘。在本發明的一個較佳具體例中，該陰離子油脂是購自於巨聖油脂化學股份有限公司的磷酸化合成油脂加脂劑(商品名稱：磷酸化合成油脂)。
依據本發明，在該方法的步驟(e)中，該乾燥處理是在40-100℃下被進行歷時90-120分鐘。較佳地，在100℃下被進行歷時120分鐘。
本發明亦提供一種得自於香蕉假莖的纖維材料，它是藉由使用一如上所述的方法而被製備。
依據本發明，該得自於香蕉假莖的纖維材料可進一步進行加工處理而被製造成紡織產品(textile products)，該紡織產品的種類包括，但不限於：紗線(yarn)、棉紗(cotton yarn)以及編織物(plaits)(例如，服飾、帆布、簾布、不織布、鞋帶等)。
依據本發明，該得自於香蕉假莖的纖維材料亦可進一步進行造紙工業(paper industry)或人造纖維工業(artificial fiber industry)所詳知且慣用的技術而被製造成纖維產品(fiber products)，該纖維產品的種類包括，但不限於：紙類、傢俱、餐具、鞋子、皮革以及過濾器材等。
較佳實施例之詳細說明
本發明將就下面的實施例來做進一步說明，但應瞭解的是，該等實施例僅是供例示說明用，而不應被解釋為本發明的實施上的限制。
實施例 一般實驗材料： 1. 在下面的實施例中所使用的香蕉假莖(
Musa×
paradisiacapseudostem)是採收自南投縣集集鎮、雲林縣莿桐鄉、高雄市大樹區以及屏東縣長治鄉。
2. 在下面的實施例中所使用的釀酒酵母菌菌粉(商品名稱：Fermentis SafAle
TMUS-05 Ale Yeast；廠牌：Lesaffre Yeast Corporation)以及果膠酶(pectinase)(商品名稱：Pectic Enzyme；廠牌：North Mountain Supply)皆是購自於貝肯布自釀啤酒原料專賣(Bake n Brew Homebrew Supply)。
實施例 1. 使用香蕉假莖來 製備纖維材料 實驗材料： 1. 製備釀酒酵母菌的接種源(inoculum of
Saccharomyces cerevisiae)：
將0.122 kg的釀酒酵母菌菌粉、6 kg的砂糖(購自於台糖)以及18 L逆滲透(reverse osmosis, RO)純水予以混合均勻以作為本實施例中的釀酒酵母菌的接種源。
實驗方法： A、 纖維材料的製備：
首先，使用一切割機來將30 kg的香蕉假莖切割分段成長度約為60-100 cm的大小(如圖1A所示)，繼而使用一油壓式壓榨機來進行壓榨處理(squeezing treatment)，而得到一經壓榨的香蕉假莖(如圖1B所示)。
接著，將該經壓榨的香蕉假莖置於一發酵槽中，繼而將上面“實驗材料”的第1項所述的釀酒酵母菌的接種源以一為0.5% (v/v)的接種量接種至該發酵槽中，繼而在28℃下進行發酵歷時120小時，俾以得到一發酵培養物。在進行發酵的過程中，藉由使用糖度計(saccharometer)來監控糖度(Brix)，並藉由補充砂糖來將糖度維持在18至20 Brix。
然後，取0.027 mL的0.005 wt%果膠酶溶液添加至該發酵培養物中並予以混合均勻，繼而在50℃下進行發酵-水解處理歷時120小時，俾以得到一發酵-水解產物(如圖2所示)。
之後，使用一濾網來對該發酵-水解產物進行固液分離處理(solid liquid separation treatment)歷時2小時而得到一固體部分。接著，在90℃下將該固體部分浸泡於2 wt%的氫氧化鉀溶液中來進行鹼處理(alkaline treatment)歷時3小時，繼而使用高壓水柱(壓力為100 bar)來進行水洗處理以移除木質素(lignin)，而得到一經水洗的固體物質。在100℃下將該經水洗的固體物質浸泡於2 wt%的過氧化氫溶液中來進行漂白處理歷時3小時，繼而浸泡於適量的磷酸化合成油脂加脂劑(商品名稱：磷酸化合成油脂；型號：SOFCON SWK；購自於巨聖油脂化學股份有限公司)來進行軟化處理歷時90分鐘，而得到一經軟化的固體物質。最後，藉由使用一熱風循環機於100℃下來對該經軟化的固體物質進行乾燥處理歷時120分鐘，藉此而製得束狀纖維(tow)。
之後，對束狀纖維進行開纖(bale opening)，而分別得到如圖3所示之兩種不同粗細的纖維(fiber)，它們的束纖細度(tow fineness)分別約為0.9-5.0 decitex (dtex)以及40-60 dtex。
B、 纖維產率 (fiber yield) 的測定：
對上面第A項所得到的所有纖維(下稱實驗組)進行秤重，並將所使用的香蕉假莖重量(亦即30 kg)代入下列公式(I)來計算纖維產率(%)：
公式 (1) ： A ＝ (B/C) × 100其中：A＝纖維產率(%)
B＝所得到的纖維的總重量(kg)
C＝所使用的香蕉假莖的重量(kg)
為供比較，申請人大體上依據上面第A項當中所述來製備比較組的纖維並計算纖維產率，不同之處在於：香蕉假莖未進行壓榨處理，而是依據習知慣用的方法來刮除(scrape)木質素以及半纖維素(hemicellulose)。
所得到的結果被顯示於下面的表1中。由表1可見，實驗組的纖維產率明顯高於比較組所具者。另外亦可觀察到的是，比較組沒有得到束纖細度小於4 dtex的纖維。這個實驗結果顯示：相較於習知方法，依據本發明的方法不僅能夠獲得較多的纖維含量，亦可獲得較多的纖維種類，而能較有效地再利用。
表1. 各組的纖維產率
實施例 2. 依據本發明方法所得到的副產物之再利用： A、 生質酒精以及蒸餾殘餘物 (distillation residue) 的製備：
| 組別 | 纖維產率(%) |
| 實驗組 | 8 |
| 比較組 | 2 |
將實施例1的第A項當中所得到的發酵培養物以濾網進行過濾並收取濾液。接著，將該濾液於78-100℃下使用蒸餾機進行蒸餾，藉此而得到生質酒精以及蒸餾殘餘物。
B、 胺基酸含量的測定：
上面第A項所得到的蒸餾殘餘物的胺基酸含量是委託捷生國際標準檢驗股份有限公司(JACKSON INTERNATIONAL STANDARD INSPECTION CO., LTD.)來進行測定。
所測得的結果被顯示於下面的表2中。從表2可見，依據本發明方法所得到的蒸餾殘餘物富含多種胺基酸。
表2. 胺基酸的種類與含量
C、 金屬含量的測定：
| 胺基酸 | 含量(mg/100 g) |
| 丙胺酸(alanine) | 156.02 |
| 精胺酸(arginine) | 55.68 |
| 天門冬醯胺(asparagine) | 651 |
| 胱胺酸(cystine) | 480.1 |
| 麩胺酸(glutamic acid) | 247.38 |
| 甘胺酸(glycine) | 81.78 |
| 組胺酸(histidine) | 20.15 |
| 異白胺酸(isoleucine) | 70.06 |
| 白胺酸(leucine) | 105.01 |
| 離胺酸(lysine) | 144.53 |
| 甲硫胺酸(methionine) | 8.03 |
| 苯丙胺酸(phenylalanine) | 60.08 |
| 脯胺酸(proline) | 55.06 |
| 蘇胺酸(threonine) | 71.11 |
| 酪胺酸(tyrosine) | 41.58 |
| 纈胺酸(valine) | 87.1 |
上面第A項所得到的蒸餾殘餘物的金屬含量是委託捷生國際標準檢驗股份有限公司來進行測定。
所測得的結果被顯示於下面的表3中。從表3可見，依據本發明方法所得到的蒸餾殘餘物之金屬含量符合行政院農業委員會農糧署(Agriculture and Food Agency, Council of Agriculture, Executive Yuan)訂定之「肥料種類品目及規格」中有機肥料的規定。
表3.金屬的種類與含量
註：「-」表示未測得。
| 金屬 | 含量 |
| 砷 | 0.12 ppm |
| 鎘 | - |
| 銅 | 0.67 ppm |
| 鉛 | 0.06 ppm |
| 汞 | - |
| 鉻 | 0.06 ppm |
| 鎳 | 0.14 ppm |
| 鈉 | 191 ppm |
| 鋅 | 12 ppm |
| 全氧化鉀 | 0.81% |
| 氯化鈉 | 0.035% |
綜合以上的實驗結果可知：依據本發明的方法不僅能夠有效地製備得自於香蕉假莖的纖維材料，亦能將其中所得的發酵培養物進一步藉由蒸餾處理來獲得生質酒精以及可供作為有機肥料的蒸餾殘餘物。
於本說明書中被引述之所有專利和文獻以其整體被併入本案作為參考資料。若有所衝突時，本案詳細說明(包含界定在內)將佔上風。
雖然本發明已參考上述特定的具體例被描述，明顯地在不背離本發明之範圍和精神之下可作出很多的修改和變化。因此意欲的是，本發明僅受如隨文檢附之申請專利範圍所示者之限制。
本發明的上述以及其它目的、特徵與優點，在參照以下的詳細說明與較佳實施例和隨文檢附的圖式後，將變得明顯，其中：
圖1A與1B分別顯示經切割分段的香蕉假莖與經壓榨的香蕉假莖；
圖2顯示所製得之發酵-水解產物；以及
圖3顯示所製得之纖維。
Claims (5)
- 一種用於製備得自於香蕉假莖的纖維材料之方法，其包括： (a) 令一香蕉假莖進行一壓榨處理，藉此而得到一經壓榨的香蕉假莖； (b) 使用釀酒酵母菌( Saccharomyces cerevisiae)來對該經壓榨的香蕉假莖進行一發酵反應，藉此而得到一發酵培養物； (c) 使用果膠酶來對該發酵培養物進行一發酵-水解處理，藉此而得到一發酵-水解產物； (d) 令該發酵-水解產物進行一固液分離處理，藉此而得到一固體部分；以及 (e) 對該固體部分依序進行鹼處理、水洗處理、漂白處理、軟化處理以及乾燥處理，藉此而得到一纖維材料。
- 如請求項1的方法，其中，在步驟(b)中，該發酵反應是在20-32℃下被進行。
- 如請求項1的方法，其中，在步驟(c)中，該發酵-水解處理是在15-55℃下被進行。
- 如請求項1的方法，其進一步包括對在步驟(e)所得到的該纖維材料進行開纖(bale opening)。
- 一種得自於香蕉假莖的纖維材料，它是藉由一如請求項1至4中任一項的方法而被製得。