TWI811376B - Cosmetics - Google Patents
Cosmetics Download PDFInfo
- Publication number
- TWI811376B TWI811376B TW108119671A TW108119671A TWI811376B TW I811376 B TWI811376 B TW I811376B TW 108119671 A TW108119671 A TW 108119671A TW 108119671 A TW108119671 A TW 108119671A TW I811376 B TWI811376 B TW I811376B
- Authority
- TW
- Taiwan
- Prior art keywords
- starch
- metal salt
- succinate
- zinc oxide
- mass
- Prior art date
Abstract
本發明提供一種包含相對於烯基丁二酸澱粉酯金屬鹽1質量份,以0.05~2質量份被覆氧化鋅之複合粒子的化妝料。烯基丁二酸澱粉酯金屬鹽可為選自由辛烯基丁二酸澱粉酯金屬鹽、癸烯基丁二酸澱粉酯金屬鹽、十二碳烯基丁二酸澱粉酯金屬鹽、十四碳烯基丁二酸澱粉酯金屬鹽、十六碳烯基丁二酸澱粉酯金屬鹽、及十八碳烯基丁二酸澱粉酯金屬鹽所組成之群中之1種以上。The present invention provides a cosmetic containing composite particles coated with zinc oxide in an amount of 0.05 to 2 parts by mass relative to 1 part by mass of alkenyl starch succinate metal salt. The alkenyl starch succinate metal salt may be selected from the group consisting of octenyl starch succinate metal salt, decenyl starch succinate metal salt, dodecenyl starch succinate metal salt, tetradecane starch ester metal salt, One or more species from the group consisting of carbenyl starch succinate metal salt, hexadecenyl starch succinate metal salt, and octadecenyl starch succinate metal salt.
Description
本發明係關於一種化妝料。The present invention relates to a cosmetic.
化妝料係塗抹於人的肌膚上而使用者,因此要求自皮膚出汗或對皮脂之耐性,一般而言,要求不浮油或脫妝。為滿足此種要求,藉由對化妝料使用之粉體施加各種改良,而進行防止脫妝之研究。Cosmetics are applied to human skin before use, so they require resistance to sweating or sebum from the skin. Generally speaking, they are required not to become oily or make up. In order to meet such demands, research is being conducted to prevent makeup from coming off by applying various improvements to powders used in cosmetics.
例如,可列舉將多孔質二氧化矽或多孔質球狀碳酸鎂等無機多孔質粉體調配於化妝料之方法,存在該等粉體吸收肌膚上之水分,肌膚之潤膚成分不足,引起肌膚乾燥或瘙癢之問題(專利文獻1、專利文獻2)。又,此外丙烯酸聚合物等有機粉體亦用作皮脂吸附劑,期待較該等皮脂吸附劑具有更優異之皮脂吸附能之素材的開發。For example, there is a method of blending inorganic porous powders such as porous silica or porous spherical magnesium carbonate into cosmetics. If these powders absorb moisture from the skin, the skin will not have enough emollient ingredients, causing skin problems. Problems with dryness or itching (Patent Document 1, Patent Document 2). In addition, organic powders such as acrylic polymers are also used as sebum adsorbents, and the development of materials with better sebum adsorption capacity than these sebum adsorbents is expected.
另一方面,氧化鋅於化妝料領域根據其粒子尺寸用作白色顏料或紫外線遮蔽材料。例如,已知微粒子氧化鋅與皮脂中之脂肪酸反應,使皮脂固定化,抑制皮脂擴張,藉此提高化妝持久性(專利文獻3)。然而,此種微粒子氧化鋅有若調配於化妝料,則存在出現乾澀感,觸感較差之缺點。因此,只要可獲得觸感優異且具有較高之皮脂固化能之氧化鋅粒子,則於化妝品領域成為非常有用之素材。Zinc oxide, on the other hand, is used in the cosmetic field as a white pigment or UV shielding material depending on its particle size. For example, it is known that fine particles of zinc oxide react with fatty acids in sebum to immobilize the sebum and inhibit the expansion of the sebum, thereby improving the durability of makeup (Patent Document 3). However, this kind of fine particle zinc oxide has the disadvantage of being dry and astringent and having poor touch when blended into cosmetics. Therefore, as long as zinc oxide particles with excellent touch feel and high sebum curing ability can be obtained, it will become a very useful material in the field of cosmetics.
又,亦已知相對於(丙烯酸酯/丙烯酸乙基己基酯)交聯聚合物1質量份被覆氧化鋅0.2~2質量份之複合粉體(專利文獻4),進而要求發揮較高之皮脂固化能之粉體及化妝料。 [先前技術文獻] [專利文獻]In addition, it is also known that a composite powder coated with 0.2 to 2 parts by mass of zinc oxide based on 1 part by mass of (acrylate/ethylhexyl acrylate) cross-linked polymer (Patent Document 4) is required to exhibit higher sebum curing Powerful powders and cosmetics. [Prior technical literature] [Patent Document]
[專利文獻1]日本專利特開2009-137806號公報 [專利文獻2]日本專利特開2006-096706號公報 [專利文獻3]日本專利特開平8-41379號公報 [專利文獻4]日本專利第6467100號公報[Patent Document 1] Japanese Patent Application Laid-Open No. 2009-137806 [Patent Document 2] Japanese Patent Application Publication No. 2006-096706 [Patent Document 3] Japanese Patent Application Laid-Open No. 8-41379 [Patent Document 4] Japanese Patent No. 6467100
[發明所欲解決之問題][Problem to be solved by the invention]
本發明之一目的在於提供一種包含發揮較高之皮脂固化能之複合粒子的化妝料。 [解決問題之技術手段]An object of the present invention is to provide a cosmetic containing composite particles exhibiting high sebum solidification ability. [Technical means to solve problems]
本發明係以下為要旨。 [1]一種化妝料,其包含相對於烯基丁二酸澱粉酯金屬鹽1質量份被覆氧化鋅0.05~2質量份之複合粒子。 [2]如[1]之化妝料,其中上述複合粒子相對於烯基丁二酸澱粉酯金屬鹽1質量份,以0.1~1.5質量份被覆氧化鋅。 [3]如[1]或[2]之化妝料,其中上述烯基丁二酸澱粉酯金屬鹽包含選自由辛烯基丁二酸澱粉酯金屬鹽、癸烯基丁二酸澱粉酯金屬鹽、十二碳烯基丁二酸澱粉酯金屬鹽、十四碳烯基丁二酸澱粉酯金屬鹽、十六碳烯基丁二酸澱粉酯金屬鹽、及十八碳烯基丁二酸澱粉酯金屬鹽所組成之群中之1種以上。 [4]如[3]之化妝料,其中上述烯基丁二酸澱粉酯金屬鹽包含辛烯基丁二酸澱粉酯金屬鹽。The present invention has the following gist. [1] A cosmetic containing 0.05 to 2 parts by mass of zinc oxide-coated composite particles based on 1 part by mass of alkenyl starch succinate metal salt. [2] The cosmetic according to [1], wherein the composite particles are coated with zinc oxide in an amount of 0.1 to 1.5 parts by mass based on 1 part by mass of alkenyl starch succinate metal salt. [3] The cosmetic of [1] or [2], wherein the alkenyl starch succinate metal salt includes a metal salt selected from the group consisting of octenyl starch succinate metal salt and decene starch succinate metal salt. , dodecenyl starch succinate metal salt, tetradecenyl starch succinate metal salt, hexadecenyl starch succinate metal salt, and octadecenyl starch succinate One or more of the group consisting of ester metal salts. [4] The cosmetic according to [3], wherein the alkenyl starch succinate metal salt includes an octenyl starch succinate metal salt.
[5]如[1]至[4]中任一項之化妝料,其中上述烯基丁二酸澱粉酯金屬鹽包含選自由烯基丁二酸澱粉酯鈉、烯基丁二酸澱粉酯鉀、烯基丁二酸澱粉酯鎂、烯基丁二酸澱粉酯鈣、烯基丁二酸澱粉酯鋇、烯基丁二酸澱粉酯銅、烯基丁二酸澱粉酯鋁、烯基丁二酸澱粉酯鐵、及烯基丁二酸澱粉酯鋯所組成之群中之1種以上。 [6]如[5]之化妝料,其中上述烯基丁二酸澱粉酯金屬鹽包含烯基丁二酸澱粉酯鋁。 [7]如[1]至[6]中任一項之化妝料,其中上述烯基丁二酸澱粉酯金屬鹽包含辛烯基丁二酸澱粉酯鋁。[5] The cosmetic according to any one of [1] to [4], wherein the metal salt of alkenyl starch succinate is selected from the group consisting of sodium alkenyl starch succinate and potassium alkenyl starch succinate. , magnesium alkenyl starch succinate, calcium alkenyl starch succinate, barium alkenyl starch succinate, copper alkenyl starch succinate, aluminum alkenyl starch succinate, alkenyl butadiene One or more of the group consisting of iron starch ester and zirconium alkenyl starch succinate. [6] The cosmetic according to [5], wherein the metal salt of alkenyl starch succinate contains aluminum alkenyl starch succinate. [7] The cosmetic according to any one of [1] to [6], wherein the metal salt of alkenyl starch succinate contains aluminum octenyl starch succinate.
[8]如[1]至[7]中任一項之化妝料,其中上述烯基丁二酸澱粉酯金屬鹽之平均粒徑為1~30 μm。 [9]如[1]至[8]中任一項之化妝料,其中上述氧化鋅之平均粒徑為10~200 nm。 [10]如[1]至[9]中任一項之化妝料,其中上述氧化鋅包含經疏水化處理之氧化鋅。 [發明之效果][8] The cosmetic according to any one of [1] to [7], wherein the average particle size of the alkenyl starch succinate metal salt is 1 to 30 μm. [9] The cosmetic according to any one of [1] to [8], wherein the zinc oxide has an average particle diameter of 10 to 200 nm. [10] The cosmetic according to any one of [1] to [9], wherein the zinc oxide includes hydrophobized zinc oxide. [Effects of the invention]
根據本發明,可提供一種包含發揮較高之皮脂固化能之複合粒子,難以溢出皮脂且發揮較高化妝持久性效果的化妝料。According to the present invention, it is possible to provide a cosmetic that contains composite particles exhibiting high sebum solidification ability, is less likely to overflow sebum, and exhibits a high makeup durability effect.
以下,對用以實施本發明之形態進行詳細說明。但是,本發明並不限定於以下實施形態。Hereinafter, the form for carrying out the present invention will be described in detail. However, the present invention is not limited to the following embodiments.
本發明之化妝料所含之複合粒子係包含烯基丁二酸澱粉酯金屬鹽、及被覆烯基丁二酸澱粉酯金屬鹽之氧化鋅的複合粒子,且較佳為相對於烯基丁二酸澱粉酯金屬鹽1質量份,以0.05~2質量份被覆氧化鋅。該複合粒子較佳為烯基丁二酸澱粉酯金屬鹽之粒子表面由氧化鋅被覆成為複合粒子之形態。The composite particles contained in the cosmetic of the present invention are composite particles containing alkenyl starch succinate metal salt and zinc oxide coating the alkenyl starch succinate metal salt, and are preferably smaller than alkenyl succinate. 1 part by mass of acid starch ester metal salt, and 0.05 to 2 parts by mass of zinc oxide. The composite particles are preferably in the form of composite particles in which the surface of the particles of alkenyl starch succinate metal salt is coated with zinc oxide.
本發明之烯基丁二酸澱粉酯金屬鹽係具有烯基之丁二酸之澱粉酯的金屬鹽。烯基丁二酸中,烯基之碳數較佳為5~22,更佳為10~20,進而較佳為8~18。作為烯基丁二酸,例如可列舉:辛烯基丁二酸、癸烯基丁二酸、十二碳烯基丁二酸、十四碳烯基丁二酸、十六碳烯基丁二酸、十八碳烯基丁二酸等。尤其可較佳使用辛烯基丁二酸澱粉酯之金屬鹽。作為金屬鹽,較佳為1價、2價或3價金屬鹽,例如可列舉:鈉、鉀、鎂、鈣、鋇、銅、鋁、鐵、鋯等。尤其,可較佳使用烯基丁二酸澱粉酯之鋁鹽、鈣鹽、鈉鹽,更佳為鋁鹽。其中,可較佳使用辛烯基丁二酸澱粉酯鋁。The alkenyl starch succinate metal salt of the present invention is a metal salt of starch succinate having an alkenyl group. In alkenyl succinic acid, the carbon number of the alkenyl group is preferably 5 to 22, more preferably 10 to 20, and still more preferably 8 to 18. Examples of alkenyl succinic acid include: octenyl succinic acid, decenyl succinic acid, dodecenyl succinic acid, tetradecenyl succinic acid, and hexadecenyl succinic acid. Acid, octadecenylsuccinic acid, etc. In particular, metal salts of starch octenyl succinate are preferably used. The metal salt is preferably a monovalent, divalent or trivalent metal salt, and examples thereof include sodium, potassium, magnesium, calcium, barium, copper, aluminum, iron, zirconium and the like. In particular, the aluminum salt, calcium salt, and sodium salt of alkenyl starch succinate can be preferably used, and the aluminum salt is more preferred. Among them, aluminum starch octenyl succinate is preferably used.
作為本發明可使用之澱粉,例如可列舉:玉米澱粉、木薯澱粉、米糠澱粉、莧澱粉等天然澱粉、區分小麥澱粉或馬鈴薯澱粉之小粒子者等。又,可使用該等加工澱粉,例如可列舉:酸分解澱粉、氧化澱粉、醚化、酯化、交聯等澱粉衍生物、濕熱處理澱粉等。Examples of starches that can be used in the present invention include natural starches such as corn starch, tapioca starch, rice bran starch, and amaranth starch, and small particles of wheat starch or potato starch. Moreover, such processed starch can be used, and examples thereof include acid-decomposed starch, oxidized starch, etherified, esterified, cross-linked and other starch derivatives, moist heat-treated starch, and the like.
本發明之複合粒子所使用之烯基丁二酸澱粉酯金屬鹽之平均粒徑較佳為1~30 μm,更佳為使用2~25 μm者於複合化方面較佳。此處,平均粒徑係藉由雷射繞射・散射式粒度分佈測定裝置之體積基準的平均粒徑。 烯基丁二酸澱粉酯金屬鹽之形狀並無特別限定,例如可為球狀、橢圓狀、多角形狀、破碎狀等粒子狀。 烯基丁二酸澱粉金屬鹽之製造方法可依據慣例而製造。The average particle diameter of the alkenyl starch succinate metal salt used in the composite particles of the present invention is preferably 1 to 30 μm, and more preferably 2 to 25 μm, in terms of composite formation. Here, the average particle diameter is a volume-based average particle diameter measured by a laser diffraction/scattering particle size distribution measuring device. The shape of the alkenyl starch succinate metal salt is not particularly limited, and may be, for example, spherical, elliptical, polygonal, broken, or other particle shapes. The production method of alkenyl succinic acid starch metal salt can be based on routine practice.
本發明之複合粒子使用之氧化鋅只要為可調配於化妝料者,則無特別限定。氧化鋅之形狀並無特別限定,平均粒徑就皮脂固化能之觀點而言,較佳為10~200 nm,更佳為15~100 nm,進而更佳為15~50 nm。此處,平均粒徑係藉由電子顯微鏡法之原理,測定1000個粒子之粒徑,設為個數平均之平均粒徑。The zinc oxide used in the composite particles of the present invention is not particularly limited as long as it can be blended into cosmetics. The shape of zinc oxide is not particularly limited, but from the viewpoint of sebum curing ability, the average particle diameter is preferably 10 to 200 nm, more preferably 15 to 100 nm, and still more preferably 15 to 50 nm. Here, the average particle diameter is based on the principle of electron microscopy, and the particle diameter of 1,000 particles is measured, and is regarded as the average particle diameter of the number average.
氧化鋅亦可直接使用未處理之氧化鋅,較佳使用實施疏水化處理之氧化鋅。作為疏水化處理劑,並無特別限定,可例示矽靈、甲基氫聚矽氧烷、金屬皂等。該等疏水化處理劑之中,較佳為使用矽靈、甲基氫聚矽氧烷、該等之共聚物、或該等之混合物。疏水化處理劑之被覆量只要為對氧化鋅進行疏水化處理而言充分之量即可。具體而言,氧化鋅與疏水化處理劑之質量比較佳為85:15~99:1,進而較佳為90:10~98:2。Untreated zinc oxide can also be used directly as zinc oxide. It is better to use zinc oxide that has undergone hydrophobic treatment. The hydrophobic treatment agent is not particularly limited, and examples thereof include silicone, methyl hydrogen polysiloxane, and metallic soap. Among these hydrophobic treatment agents, silicone, methyl hydrogen polysiloxane, copolymers thereof, or mixtures thereof are preferably used. The coating amount of the hydrophobizing treatment agent may be an amount sufficient to hydrophobize zinc oxide. Specifically, the mass ratio between zinc oxide and the hydrophobic treatment agent is preferably 85:15 to 99:1, and more preferably 90:10 to 98:2.
本發明之化妝料所使用之複合粒子中,相對於烯基丁二酸澱粉酯金屬鹽1質量份,氧化鋅之被覆量為0.05質量份以上,更佳為0.1質量份以上,進而較佳為0.2質量份以上。又,相對於烯基丁二酸澱粉酯金屬鹽1質量份,氧化鋅之被覆量為2質量份以下,更佳為1.5質量份以下。於該範圍,可更提高皮脂固化能且防止皮脂溢出。 相對於烯基丁二酸澱粉酯金屬鹽1質量份,氧化鋅之被覆量為0.05~2質量份,更佳為0.1~1.5質量份。In the composite particles used in the cosmetics of the present invention, the coating amount of zinc oxide is 0.05 parts by mass or more, more preferably 0.1 parts by mass or more, and still more preferably 1 part by mass of alkenyl starch succinate metal salt. 0.2 parts by mass or more. Furthermore, the coating amount of zinc oxide is 2 parts by mass or less, more preferably 1.5 parts by mass or less based on 1 part by mass of the alkenyl starch succinate metal salt. Within this range, sebum solidification performance can be further improved and sebum overflow can be prevented. The coating amount of zinc oxide is 0.05 to 2 parts by mass, more preferably 0.1 to 1.5 parts by mass relative to 1 part by mass of alkenyl starch succinate metal salt.
作為氧化鋅對於烯基丁二酸澱粉酯金屬鹽之被覆方法,可使用至今已知之各種方法,例如可選擇物理化學混合磨碎法(乾式、濕式)或化學沈積法等。就複合粒子之皮脂固化能之方面而言,可較佳使用乾式混合磨碎法。As a method for coating the alkenyl starch succinate metal salt with zinc oxide, various methods known so far can be used. For example, a physical and chemical mixing grinding method (dry method, wet method) or a chemical deposition method can be selected. In terms of the sebum solidification ability of the composite particles, the dry mixing and grinding method can be preferably used.
本發明之複合粒子可使用將選自上述烯基丁二酸澱粉酯金屬鹽中之1種或2種以上藉由氧化鋅而被覆者。氧化鋅可使用未處理之氧化鋅、經疏水化處理之氧化鋅、或該等之組合。又,本發明之化妝料中可將選自上述烯基丁二酸澱粉酯金屬鹽中之1種或2種以上與氧化鋅之組合即複合粒子單獨調配1種,或將2種以上組合調配。The composite particles of the present invention may be composed of one or two or more types selected from the above alkenyl starch succinate metal salts and coated with zinc oxide. As zinc oxide, untreated zinc oxide, hydrophobized zinc oxide, or a combination thereof can be used. Furthermore, in the cosmetic of the present invention, one type or a combination of two or more types selected from the above-mentioned alkenyl starch succinate metal salts and zinc oxide, that is, composite particles may be prepared individually or in combination of two or more types. .
本發明之化妝料可藉由包含上述複合粒子,而發揮具有皮脂固化能且發揮優異之化妝保持效果。By containing the above-mentioned composite particles, the cosmetic of the present invention can exhibit sebum-solidifying ability and an excellent makeup-maintaining effect.
作為複合粒子於化妝料之調配量,相對於化妝料總量,較佳為0.5~90質量%。該調配量未達0.5質量%時,有複合粒子之皮脂固化能於化妝料中難以有效發揮之傾向。另一方面,若化妝料中調配超過90質量%之複合粒子,則有難以製劑化之傾向。The compounding amount of the composite particles in the cosmetic is preferably 0.5 to 90% by mass relative to the total amount of the cosmetic. If the blending amount is less than 0.5% by mass, the sebum-curing ability of the composite particles tends to be difficult to effectively exert in cosmetics. On the other hand, if more than 90% by mass of the composite particles are blended into the cosmetic, it will tend to be difficult to formulate.
本發明之化妝料之用途並無特別限定,就其效果方面而言,可較佳用於粉餅等彩妝化妝料、或底妝化妝料、防曬化妝料等。The use of the cosmetics of the present invention is not particularly limited. In terms of its effects, it can be preferably used in color cosmetics such as pressed powder, base makeup, sunscreen cosmetics, etc.
本發明之化妝料之劑型並無特別限定,可例示粉體化妝料、乳化化妝料、2層化妝料等。The dosage form of the cosmetics of the present invention is not particularly limited, and examples thereof include powder cosmetics, emulsified cosmetics, and two-layer cosmetics.
本發明之化妝料除複合粒子外可適當調配視需要通常調配於化妝料之水性成分、保濕劑、油性成分、色素、界面活性劑、紫外線吸收劑、增黏劑、美容成分、香料、高分子物質、防菌防黴劑、醇類、粉體、清洗劑、源自活體成分等。 [實施例]In addition to the composite particles, the cosmetics of the present invention can be appropriately formulated with water-based ingredients, moisturizers, oily ingredients, pigments, surfactants, ultraviolet absorbers, thickeners, beauty ingredients, fragrances, and polymers that are usually formulated in cosmetics as needed. Substances, antibacterial and antifungal agents, alcohols, powders, cleaning agents, ingredients derived from living organisms, etc. [Example]
以下,藉由實施例具體說明本發明,但並非藉此限定本發明之範圍。再者,調配量只要無特別說明,為質量%。The present invention will be specifically described below through examples, but the scope of the present invention is not limited thereby. In addition, unless otherwise specified, the compounding quantity is mass %.
(複合粒子) 藉由將表1所示之核粒子與氧化鋅,使用攪拌機混合2小時,而獲得複合粒子。利用顯微鏡觀察該複合粒子,結果由氧化鋅被覆核粒子。再者,作為氧化鋅,使用以5%矽靈進行處理之平均粒徑25 nm之氧化鋅。 表1中,氧化鋅之被覆量係以相對於核粒子與氧化鋅之合計量的質量比率表示。 將氧化鋅被覆前之核粒子之平均粒徑示於表1。(composite particles) Composite particles were obtained by mixing the core particles shown in Table 1 with zinc oxide using a mixer for 2 hours. When the composite particles were observed with a microscope, it was found that the core particles were coated with zinc oxide. In addition, as zinc oxide, zinc oxide with an average particle diameter of 25 nm was used, which was treated with 5% silicone. In Table 1, the coating amount of zinc oxide is expressed as a mass ratio relative to the total amount of core particles and zinc oxide. Table 1 shows the average particle size of the core particles before zinc oxide coating.
(油酸固化試驗) (a)於20 mL之燒杯中測量油酸(PM810:Miyoshi油脂股份有限公司)5 g及離子交換水1 g,利用設定為40℃之加熱板加溫至35~40℃。 (b)於(a)中添加複合粒子0.5 g,使用刮勺,以成為均質之方式,攪拌30秒。 (c)攪拌後,立即投入攪拌子,利用攪拌器進行攪拌(200 rpm)。測量自攪拌開始時間進行油酸之凝膠化,直至停止攪拌子之旋轉的時間,設為固化時間。(Oleic acid curing test) (a) Measure 5 g of oleic acid (PM810: Miyoshi Oils and Fats Co., Ltd.) and 1 g of ion-exchange water in a 20 mL beaker, and heat it to 35 to 40°C using a hot plate set to 40°C. (b) Add 0.5 g of composite particles to (a), use a spatula, and stir for 30 seconds to achieve homogeneity. (c) After stirring, immediately put the stirrer in and stir with the stirrer (200 rpm). Measure the time from the start of stirring to the gelation of oleic acid until the rotation of the stirring bar is stopped, and set it as the solidification time.
[表1]
如表1所示,辛烯基丁二酸澱粉鋁與氧化鋅之複合粒子1~3顯示油酸固化時間非常快,發揮較高之皮脂固化能。又,辛烯基丁二酸澱粉鈣與氧化鋅之複合粒子5亦顯示油酸固化時間非常快,發揮較高之皮脂固化能。As shown in Table 1, the composite particles 1 to 3 of aluminum octenyl succinate starch and zinc oxide show that the oleic acid curing time is very fast and exhibit high sebum curing ability. In addition, the composite particles 5 of calcium octenyl succinate starch and zinc oxide also show that the oleic acid curing time is very fast and exhibits high sebum curing ability.
其次,使用表1所示之複合粒子1,以表2所示之配方,藉由慣例調製壓製型之粉餅。Next, use the composite particles 1 shown in Table 1 and the formula shown in Table 2 to prepare a compressed powder cake according to the usual practice.
(評價方法) 對彩妝化妝料之專門評價者3名,於半臉使用實施例1及比較例1,於高溫多濕下之室內分別評價3小時後之皮脂溢出,藉由合議以下述基準評價哪一種更優異。(evaluation method) Three expert evaluators of makeup and cosmetics used Example 1 and Comparative Example 1 on half of the face, and evaluated the seborrhea after 3 hours in a room under high temperature and humidity. Through consensus, they evaluated which one is more superior based on the following criteria. .
[皮脂溢出] 〇:不易皮脂溢出。 ×:容易皮脂溢出。[Seborrhea] 〇: Difficult to overflow sebum. ×: Easy to overflow sebum.
[表2]
如表2所示,調配複合粒子之實施例1顯示不易皮脂溢出。As shown in Table 2, Example 1, which formulated composite particles, showed that it was not prone to sebaceous overflow.
其次,使用表1所示之複合粒子1~3,依據下述順序,調製各種化妝料。
[實施例2]粉末粉餅
[表3]
製法:將1~10混合、均質化後,加熱熔解,添加設為75℃之11~13之成分進行混練。利用霧化器粉碎、篩過後,於金盤中壓製成型。Preparation method: After mixing and homogenizing 1 to 10, heat and melt, add ingredients 11 to 13 at 75°C and knead. After crushing and sieving using an atomizer, it is pressed and formed in a gold plate.
[實施例3]油性粉餅(精簡型)
[表4]
製法:將1~6混合、均質化後,添加加熱熔解之7~11的成分,利用輥磨機混練。將混練物再融解,充分攪拌,使泡浮起,繼而冷卻,於60℃流入容器中進行放冷、固化。Preparation method: After mixing and homogenizing 1 to 6, add ingredients 7 to 11 that have been heated and melted, and knead with a roller mill. Melt the kneaded product again, stir thoroughly to float the bubbles, then cool it, pour it into a container at 60°C, and let it cool and solidify.
[實施例4]遮斑用棒
[表5]
製法:將9~14於85℃下熔解、混合,一面將均質化之1~8的成分攪拌一面添加。利用膠體磨機使其磨碎分散,脫氣後於70℃下流入至容器使其冷卻。Preparation method: Melt 9 to 14 at 85°C and mix. Add the homogenized ingredients 1 to 8 while stirring. Grind and disperse it using a colloid mill, degas it, and then pour it into a container at 70° C. to cool it.
[實施例5]O/W乳化型粉餅
[表6]
製法:使6分散於9中,添加於10,於70℃下進行均質攪拌機處理之後,添加7及8充分攪拌。添加於其中混合、均質化之1~5,利用均質攪拌機進行均質混合。添加於75℃下加熱熔解、均質化之11~15之成分,利用均質攪拌機使其乳化後,進行冷卻。Preparation method: Disperse 6 in 9, add 10, perform homogenizer processing at 70°C, add 7 and 8 and stir thoroughly. Add to mix and homogenize steps 1 to 5, and homogenize with a homogenizer. Ingredients 11 to 15 melted and homogenized by heating at 75°C are added, emulsified using a homogenizer, and then cooled.
[實施例6]W/O乳化型粉餅
[表7]
製法:將8~10加熱熔解、均質化,添加1~5,利用均質攪拌機使其均質分散。添加均質熔解之6、7之成分,利用均質攪拌機使其乳化後,進行冷卻。Preparation method: Heat and melt 8 to 10, homogenize, add 1 to 5, and use a homogenizer to disperse homogeneously. Add the homogeneously melted ingredients 6 and 7, emulsify them using a homogenizer, and then cool them.
[實施例7]O/W乳化型防曬乳
[表8]
製法:混合9~13後,使用均質攪拌機,使其均質分散後,進行加熱熔解,添加設為75℃之1~8的成分,利用均質攪拌機使其乳化後,進行冷卻。Preparation method: After mixing 9 to 13, use a homomixer to homogeneously disperse, heat and melt, add ingredients 1 to 8 at 75°C, emulsify using a homomixer, and then cool.
[實施例8]W/O乳化型防曬乳液
[表9]
製法:將1~10加熱熔解、混合後,使用均質攪拌機,使其均質分散,添加均質熔解之11、12,利用均質攪拌機使其乳化後,進行冷卻。Preparation method: After heating, melting and mixing 1 to 10, use a homogeneous mixer to homogeneously disperse them, add the homogeneously melted 11 and 12, use a homogeneous mixer to emulsify, and then cool.
Claims (7)