TWI767078B - Eyelash cosmetic - Google Patents
Eyelash cosmetic Download PDFInfo
- Publication number
- TWI767078B TWI767078B TW107138029A TW107138029A TWI767078B TW I767078 B TWI767078 B TW I767078B TW 107138029 A TW107138029 A TW 107138029A TW 107138029 A TW107138029 A TW 107138029A TW I767078 B TWI767078 B TW I767078B
- Authority
- TW
- Taiwan
- Prior art keywords
- mass
- polar solvent
- eyelash cosmetic
- polyurethane
- eyelash
- Prior art date
Abstract
本發明之睫毛化妝料係含有聚胺基甲酸酯及極性溶劑。 The eyelash cosmetic of the present invention contains a polyurethane and a polar solvent.
Description
本發明係關於睫毛化妝料。 The present invention relates to eyelash cosmetics.
習知睫毛化妝料(睫毛膏、眼妝化妝料)係有如:重視耐水性、捲翹力之由油性材料構成的防水型(以下稱「WP型」)、不需要專用卸妝品等僅利用溫水便可卸妝的之重視簡便卸妝性的薄膜型(以下稱「FM型」)。但是,近年講求具備耐水性、捲翹力,且能簡便卸妝的需求,然尚無法能滿足此項需求。 Conventionally known eyelash cosmetics (mascara, eye makeup) are: waterproof type (hereinafter referred to as "WP type") composed of oily materials that attach importance to water resistance and curling power, do not require special makeup removers, etc. Only use warm A thin film type (hereinafter referred to as "FM type") that emphasizes easy makeup removal that can be easily removed with water. However, in recent years, the demand for water resistance, curling power, and easy makeup removal has not been able to meet this demand.
FM型係以水為基材,且使用胺基甲酸乙酯乳液進行皮膜形成(專利文獻1)等。其雖睫毛膏卸除簡便,但捲翹力較WP型大幅劣化,並無法滿足市場需求。特別因為聚胺基甲酸酯皮膜柔軟,因而必需如專利文獻1般較多地摻合蠟等油系成分、或如專利文獻2般與丙烯酸乳液混合而提升玻璃轉移點(Tg),藉此彌補捲翹力。專利文獻3與4所記載的睫毛化妝料,係含有:聚胺基甲酸酯、以及作為有機礦物增黏劑用活性劑之碳酸丙烯酯。專利文獻5所記載的睫毛化妝料,係含有高分子染料,該高分子染料係選自磺基聚酯(sulfopolyester)、聚醯胺、聚胺基甲酸酯及聚丙烯酸聚合物、或該等的混合物。 The FM type system uses water as a base material, and performs film formation using urethane emulsion (Patent Document 1) and the like. Although the mascara is easy to remove, its curling force is significantly worse than that of the WP type, and it cannot meet the market demand. In particular, since the polyurethane film is soft, it is necessary to mix a large amount of oil-based components such as wax as in Patent Document 1, or to increase the glass transition point (Tg) by mixing with an acrylic emulsion as in Patent Document 2. Compensate for curling force. The eyelash cosmetic materials described in Patent Documents 3 and 4 contain polyurethane and propylene carbonate as an activator for an organic mineral thickener. The eyelash cosmetic described in Patent Document 5 contains a polymer dye selected from the group consisting of sulfopolyester, polyamide, polyurethane, and polyacrylic acid polymer, or the like mixture.
[專利文獻1]日本專利特開2011-126884號公報 [Patent Document 1] Japanese Patent Laid-Open No. 2011-126884
[專利文獻2]日本專利特開2015-193551號公報 [Patent Document 2] Japanese Patent Laid-Open No. 2015-193551
[專利文獻3]日本專利特開2008-195732號公報 [Patent Document 3] Japanese Patent Laid-Open No. 2008-195732
[專利文獻4]日本專利特開2008-120805號公報 [Patent Document 4] Japanese Patent Laid-Open No. 2008-120805
[專利文獻5]日本專利特表2000-513002號公報 [Patent Document 5] Japanese Patent Publication No. 2000-513002
如上述,已知睫毛化妝料尚有改善空間,而期待新穎的睫毛化妝料。 As described above, the known eyelash cosmetic has room for improvement, and a novel eyelash cosmetic is expected.
為解決上述課題,本發明人經深入鑽研,結果發現藉由在聚胺基甲酸酯中添加極性溶劑,可大幅提升耐水性與伸縮性,遂完成本發明。 In order to solve the above-mentioned problems, the inventors of the present invention have conducted intensive studies, and as a result, they have found that by adding a polar solvent to polyurethane, the water resistance and stretchability can be greatly improved, and the present invention has been completed.
即,本發明係關於下述。 That is, the present invention relates to the following.
一種睫毛化妝料,係含有聚胺基甲酸酯與極性溶劑的睫毛化妝料,極性溶劑係含有從二醇之單或二烷基(C1~C4)醚或與C2~C6羧酸的酯化合物、碳酸烯(C2~C4)酯化合物及酮醇(C3~C6)所構成群組中選擇之至少1種。 An eyelash cosmetic, which is an eyelash cosmetic containing polyurethane and a polar solvent, wherein the polar solvent contains a mono- or dialkyl (C1-C4) ether from a glycol or an ester compound with a C2-C6 carboxylic acid , at least one selected from the group consisting of alkene carbonate (C2-C4) ester compounds and ketone alcohols (C3-C6).
如發明1之睫毛化妝料,其中,實質上不含有從磺基聚酯、聚醯 胺、聚胺基甲酸酯及聚丙烯酸聚合物、及該等混合物中選擇的高分子染料。 The eyelash cosmetic according to Invention 1 is substantially free of polymer dyes selected from sulfopolyester, polyamide, polyurethane, and polyacrylic acid polymers, and mixtures thereof.
如發明1或2所記載之睫毛化妝料,其中,極性溶劑係含有從甲甘醇、乙氧乙醇、丁氧乙醇、乙氧基二甘醇、丁氧基二甘醇、二甲氧基二甘醇、二乙氧基二甘醇、醋酸-2-乙氧基乙酯、羥丙酮及二丙酮醇所構成群組中選擇之至少1種。 The eyelash cosmetic according to Invention 1 or 2, wherein the polar solvent contains a group consisting of methyl glycol, ethoxyethanol, butoxyethanol, ethoxydiglycol, butoxydiglycol, and dimethoxydiethylene glycol. At least one selected from the group consisting of glycol, diethoxydiglycol, 2-ethoxyethyl acetate, hydroxyacetone and diacetone alcohol.
如發明3所記載之睫毛化妝料,其中,極性溶劑係含有從甲甘醇、乙氧乙醇、丁氧乙醇、乙氧基二甘醇、丁氧基二甘醇、二甲氧基二甘醇、二乙氧基二甘醇、羥丙酮及二丙酮醇所構成群組中選擇之至少1種。 The eyelash cosmetic according to Invention 3, wherein the polar solvent contains a group consisting of methyl glycol, ethoxyethanol, butoxyethanol, ethoxydiglycol, butoxydiglycol, and dimethoxydiglycol , at least one selected from the group consisting of diethoxydiglycol, hydroxyacetone and diacetone alcohol.
如發明4所記載之睫毛化妝料,其中,極性溶劑係含有從乙氧基二甘醇、碳酸丙烯酯及二丙酮醇所構成群組中選擇之至少1種。 The eyelash cosmetic according to Invention 4, wherein the polar solvent contains at least one selected from the group consisting of ethoxydiglycol, propylene carbonate, and diacetone alcohol.
如發明5所記載之睫毛化妝料,其中,極性溶劑係含有從乙氧基二甘醇及二丙酮醇所構成群組中選擇之至少1種。 The eyelash cosmetic according to Invention 5, wherein the polar solvent contains at least one selected from the group consisting of ethoxydiglycol and diacetone alcohol.
本發明之睫毛化妝料係對汗、皮脂等具有強力的化妝持久性,且利用溫水便可簡單卸除。較佳態樣係捲翹力高、完妝感優異。 The eyelash cosmetic of the present invention has strong makeup durability against sweat, sebum, etc., and can be easily removed with warm water. The preferred aspect is high curling force and excellent finish.
圖1係例1(僅BAYCUSAN C1010)之耐水性試驗結果。 Figure 1 shows the water resistance test results of Example 1 (BAYCUSAN C1010 only).
圖2係例2(BAYCUSAN C1010+乙氧基二甘醇)之耐水性試驗結果。 Figure 2 shows the water resistance test results of Example 2 (BAYCUSAN C1010+ethoxydiglycol).
圖3係例3(BAYCUSAN C1010+碳酸丙烯酯)之耐水性試驗結果。 Figure 3 shows the results of the water resistance test of Example 3 (BAYCUSAN C1010+propylene carbonate).
圖4係例4(BAYCUSAN C1010+二丙酮醇)之耐水性試驗結果。 Figure 4 shows the results of the water resistance test of Example 4 (BAYCUSAN C1010+diacetone alcohol).
圖5係例5(BAYCUSAN C1010+檸檬酸三乙酯)之耐水性試驗結果。 Figure 5 shows the water resistance test results of Example 5 (BAYCUSAN C1010+triethyl citrate).
圖6係例6(BAYCUSAN C1010+乙氧乙醇)之耐水性試驗結果。 Figure 6 shows the results of the water resistance test of Example 6 (BAYCUSAN C1010+ethoxyethanol).
圖7係例7(BAYCUSAN C1010+丁氧基二甘醇)之耐水性試驗結果。 Figure 7 shows the water resistance test results of Example 7 (BAYCUSAN C1010+butoxydiglycol).
圖8係例8(BAYCUSAN C1010+羥丙酮)之耐水性試驗結果。 Figure 8 shows the water resistance test results of Example 8 (BAYCUSAN C1010+Hydroxyacetone).
圖9係使用例9、例10、例11、例12及例13之處方的捲翹力評價試驗之照片。 FIG. 9 is a photograph of the curling force evaluation test of the prescriptions using Example 9, Example 10, Example 11, Example 12, and Example 13. FIG.
圖10係捲翹角度測量之示意圖。 Figure 10 is a schematic diagram of the measurement of the curling angle.
本發明中可有各種代替形態,本說明書係針對本發明之特定態樣進行詳述。然而,本說明書的特定態樣之詳述並非意在將本發明限定於特定態樣,本發明涵蓋申請專利範圍所規定本發明真意與範圍內的所有代替形態。 Various alternative forms are possible in the present invention, and this specification is intended to describe in detail specific aspects of the present invention. However, the detailed description of a specific aspect in this specification is not intended to limit the present invention to the specific aspect, and the present invention covers all alternative forms within the true meaning and scope of the present invention defined in the scope of the patent application.
睫毛(eyelash)化妝料或睫毛用化妝料亦稱睫毛膏、眼妝化妝料,係 使睫毛看起來變濃、變長及/或捲翹。 Eyelash cosmetic or cosmetic for eyelashes, also known as mascara, eye cosmetic, is used to make eyelashes appear thicker, longer and/or curled.
本發明之睫毛化妝料的形態並無特別的限定。可舉例如液狀、乳液狀、凝膠狀、乳霜狀、固態狀等。 The form of the eyelash cosmetic of the present invention is not particularly limited. For example, liquid form, emulsion form, gel form, cream form, solid form, etc. are mentioned.
本發明之睫毛化妝料係含有一種或二種以上的聚胺基甲酸酯(胺基甲酸乙酯樹脂)。聚胺基甲酸酯係只要為化妝品上容許者便可。例如:聚胺基甲酸酯-1~81、聚胺基甲酸酯交聯聚合物-1~2等(參照日本化妝品工業協會所發佈的化妝品成分標示名稱清單、美國個人護理產品協會(PCPC)所公佈的On-Line INFOBASE等)。更佳係含有:作為二異氰酸酯單體之六亞甲基二異氰酸酯或二環己基甲烷二異氰酸酯,以及作為二醇單體之1,4-丁二醇或1,6-己二醇。可舉例如聚胺基甲酸酯-32、聚胺基甲酸酯-34、聚胺基甲酸酯-35等。可為純度100%、亦可經稀釋。經稀釋者可為溶液、亦可為乳液、亦可為懸浮液。可任意選擇該等中之一種或二種以上,惟並不僅侷限於此,亦可為其衍生物。聚胺基甲酸酯的含有量係0.04質量%~20質量%、較佳係0.4質量%~16質量%、更佳係1.2質量%~12質量%。若未滿0.04質量%,則睫毛化妝料的皮膜無法利用溫水輕易卸除,若超過20質量%,將無法獲得良好的捲翹力。 The eyelash cosmetic of the present invention contains one or two or more types of polyurethanes (urethane resins). What is necessary is just the urethane type which is cosmetically acceptable. For example: polyurethane-1~81, polyurethane cross-linked polymer-1~2, etc. (refer to the list of cosmetic ingredients labeling names issued by the Japan Cosmetic ) published On-Line INFOBASE, etc.). More preferably, it contains hexamethylene diisocyanate or dicyclohexylmethane diisocyanate as diisocyanate monomers, and 1,4-butanediol or 1,6-hexanediol as diol monomers. For example, polyurethane-32, polyurethane-34, polyurethane-35, etc. are mentioned. It can be 100% pure or diluted. Diluted can be a solution, an emulsion, or a suspension. One or two or more of these can be arbitrarily selected, but it is not limited to this, and its derivatives can also be used. The content of the polyurethane is 0.04% by mass to 20% by mass, preferably 0.4% by mass to 16% by mass, and more preferably 1.2% by mass to 12% by mass. If it is less than 0.04 mass %, the film of the eyelash cosmetic cannot be easily removed with warm water, and if it exceeds 20 mass %, good curling force cannot be obtained.
本發明之睫毛化妝料係含有一種或二種以上的極性溶劑。極性溶劑係具有作為成膜助劑的機能。極性溶劑係在化妝品上所容許、且與 水及油二者具相溶性之前提下,其餘並無特別的限定。較佳係含有從乙二醇、二乙二醇等二醇之單或二烷基(C1~C4)醚或與C2~C6羧酸的酯化合物、屬於環狀碳酸酯之碳酸烯(C2~C4)酯化合物及酮醇(C3~C6)所構成群組中選擇之至少1種。可舉例如:甲甘醇、乙氧乙醇、丁氧乙醇、乙氧基二甘醇、丁氧基二甘醇、二甲氧基二甘醇、二乙氧基二甘醇、醋酸-2-乙氧基乙酯、碳酸乙烯酯、碳酸丙烯酯、碳酸丁烯酯、羥丙酮、二丙酮醇等(參照日本化妝品工業協會所發佈的化妝品成分標示名稱清單或化妝品原料製造廠之型錄等)。可任意選擇該等中之一種或二種以上,惟並不僅侷限於此,亦可為其衍生物。其含有量係0.1質量%~25質量%、較佳係0.5質量%~20質量%、更佳係1質量%~15質量%。若未滿0.1質量%,則無法獲得良好捲翹力,若超過25質量%,則無法獲得滑順使用感、使用感惡化。 The eyelash cosmetic of the present invention contains one or two or more polar solvents. The polar solvent system functions as a film-forming aid. The polar solvent is not particularly limited as long as it is cosmetically acceptable and has compatibility with both water and oil. Preferably, it contains mono- or dialkyl (C1~C4) ethers of diols such as ethylene glycol and diethylene glycol, or ester compounds with C2~C6 carboxylic acids, and alkene carbonates (C2~C6) belonging to cyclic carbonates. C4) At least one selected from the group consisting of ester compounds and ketone alcohols (C3-C6). For example, methyl glycol, ethoxyethanol, butoxyethanol, ethoxydiglycol, butoxydiglycol, dimethoxydiglycol, diethoxydiglycol, acetic acid-2- Ethoxyethyl ester, ethylene carbonate, propylene carbonate, butylene carbonate, hydroxyacetone, diacetone alcohol, etc. . One or two or more of these can be arbitrarily selected, but it is not limited to this, and its derivatives can also be used. The content thereof is 0.1% by mass to 25% by mass, preferably 0.5% by mass to 20% by mass, and more preferably 1% by mass to 15% by mass. If it is less than 0.1 mass %, a favorable curling force cannot be obtained, and if it exceeds 25 mass %, a smooth feeling in use cannot be obtained, and the feeling in use is deteriorated.
本發明之睫毛化妝料係在不致損及本發明效果之前提下,亦可更進一步含有一種或二種以上之熟習此技術者公認能摻合的公知化妝料原料。可舉例如:揮發性油劑、界面活性劑、凝膠化劑、抗結塊劑、乳化劑、分散劑、安定劑、保濕劑、增黏劑、固形化劑、結合劑、增量劑、不透明劑、潤滑劑、顏料、紫外線散射劑、紫外線吸收劑、pH調節劑、抗氧化劑、抗菌劑、防腐劑、護膚劑、潤滑劑、收斂劑、潤膚劑、發亮劑、光澤劑、消泡劑、撥水性被膜劑、保護劑等。亦可使用該等2種以上之用途/效果重複者。 The eyelash cosmetic of the present invention may further contain one or two or more known cosmetic raw materials that are known to be blended by those skilled in the art, without impairing the effect of the present invention. Examples include: volatile oils, surfactants, gelling agents, anti-caking agents, emulsifiers, dispersants, stabilizers, moisturizing agents, tackifiers, curing agents, binders, extenders, Opacifiers, lubricants, pigments, UV scattering agents, UV absorbers, pH adjusters, antioxidants, antibacterial agents, preservatives, skin care agents, lubricants, astringents, emollients, brighteners, glosses, antiseptics Foaming agent, water repellent coating agent, protective agent, etc. It is also possible to use two or more of these repeated uses/effects.
本發明一態樣中,本發明之睫毛化妝料係實質不含有硬蠟。另外,所謂「硬蠟」係在周圍溫度(25℃)下呈固態,且狀態具有可逆性之固態 /液態的狀態變化,並具有30℃以上熔解點的親油性化合物,且在20℃下顯示大於5MPa的硬度。此處所謂「實質不含有」係指本發明之睫毛化妝料不含有損及耐皮脂性及/或溫水洗淨容易性的量,例如不含有超過12質量%的量(或12質量%以上),更佳係不含有超過5質量%的量(或5質量%以上)。 In one aspect of the present invention, the eyelash cosmetic of the present invention does not substantially contain hard wax. In addition, the so-called "hard wax" is a solid at ambient temperature (25°C), and the state has a reversible solid/liquid state change, and a lipophilic compound with a melting point of 30°C or higher, and shows at 20°C Hardness greater than 5MPa. Here, "substantially not containing" means that the eyelash cosmetic of the present invention does not contain an amount that impairs sebum resistance and/or ease of washing with warm water, for example, does not contain an amount exceeding 12 mass % (or 12 mass % or more). ), more preferably not containing an amount exceeding 5 mass % (or 5 mass % or more).
本發明一態樣中,本發明之睫毛化妝料係實質不含有複合樹脂核殼型高分子乳液。此處,所謂上述複合樹脂核殼型高分子乳液,係指依序施行以下步驟(1)~(4):(1)在屬於含有具酯基之(甲基)丙烯酸單體的聚合性單體、且使其進行聚合而獲得之聚合體之玻璃轉移溫度成為95℃以上且105℃以下的聚合性單體((b)成分)存在下,使聚丙二醇、二羥甲基丙酸及脂肪族或脂環式多元異氰酸酯進行反應,而生成含有異氰酸酯基與羧基的胺基甲酸乙酯預聚物((a)成分),獲得(a)成分與(b)成分的混合液之步驟;(2)將(1)所獲得之(a)成分及(b)成分的混合液中(a)成分所含有之羧基使用當量之三乙醇胺進行中和,獲得(a)成分中和物與(b)成分的混合液之步驟;(3)使(2)所獲得之(a)成分中和物與(b)成分的混合液,在水性介質中進行乳化分散而獲得乳化液的步驟;(4)使(3)所獲得之乳化液中的(b)成分進行聚合,而獲得複合樹脂核殼型高分子乳液的步驟;等各步驟而獲得者,在步驟(1)中,作為聚丙二醇係依94:6~92:8(質量比)比例使用數量平均分子量1000之聚丙二醇、與數量平均分子量2000之聚丙二醇之2種;混合液中的(a)成分與(b)成分之比例係(a)成 分:(b)成分(純分質量比)=50:50~60:40的複合樹脂核殼型高分子乳液。 In one aspect of the present invention, the eyelash cosmetic of the present invention does not substantially contain a composite resin core-shell polymer emulsion. Here, the so-called composite resin core-shell polymer emulsion refers to the following steps (1) to (4) are sequentially performed: (1) In a polymerizable monomer containing a (meth)acrylic monomer having an ester group, In the presence of a polymerizable monomer (component (b)) having a glass transition temperature of 95°C or more and 105°C or less of a polymer obtained by polymerizing it, polypropylene glycol, dimethylolpropionic acid and aliphatic aliphatic or alicyclic polyisocyanate reacts, and generates the urethane prepolymer ((a) component) containing isocyanate group and carboxyl group, and obtains the step of the mixed solution of (a) component and (b) component; ( 2) Neutralize the carboxyl group contained in the component (a) in the mixed solution of the component (a) and the component (b) obtained in (1) with an equivalent of triethanolamine to obtain a neutralized product of the component (a) and (b) ) the step of the mixed solution of the component; (3) the step of emulsifying and dispersing the mixed solution of the (a) component neutralized product and (b) component obtained in (2) in an aqueous medium to obtain an emulsion; (4) ) The step of polymerizing the component (b) in the emulsion obtained in (3) to obtain a composite resin core-shell type polymer emulsion; for those obtained in each step, in step (1), as a polypropylene glycol-based polymer emulsion Two kinds of polypropylene glycol with a number average molecular weight of 1000 and a number average molecular weight of 2000 are used according to the ratio of 94:6~92:8 (mass ratio); the ratio of (a) component and (b) component in the mixed solution is (a) Component: (b) Component (pure mass ratio) = 50:50~60:40 composite resin core-shell polymer emulsion.
所謂「實質不含有」係指例如不含有固形份換算計超過1質量%的量(或1質量%以上),更佳係不含有固形份換算計超過0.5質量%的量(或0.5質量%以上)。 The term "substantially not contained" means that, for example, an amount exceeding 1 mass % (or 1 mass % or more) in terms of solid content is not contained, and more preferably an amount exceeding 0.5 mass % (or 0.5 mass % or more) in terms of solid content is not contained. ).
本發明一態樣中,本發明之睫毛化妝料係實質不含有從磺基聚酯、聚醯胺、聚胺基甲酸酯及聚丙烯酸聚合物及該等混合物中選擇的高分子染料。 In one aspect of the present invention, the eyelash cosmetic of the present invention does not substantially contain polymer dyes selected from sulfopolyester, polyamide, polyurethane and polyacrylic acid polymers and mixtures thereof.
所謂「實質不含有」係指例如不含有超過1質量%的量(或1質量%以上)、更佳係不含有超過0.5質量%的量(或0.5質量%以上)。 The term "substantially not contained" means that, for example, it does not contain an amount exceeding 1 mass % (or 1 mass % or more), and more preferably does not contain an amount exceeding 0.5 mass % (or 0.5 mass % or more).
本發明之睫毛化妝料係依照熟習此技術者的技術常識並依照慣用處方例便可製造。各成分的摻合方法、順序等可依照熟習此技術者的技術常識而為任意。 The eyelash cosmetic of the present invention can be produced in accordance with the technical common sense of those skilled in the art and in accordance with customary prescriptions. The blending method, order, etc. of each component can be arbitrary according to the technical common sense of those skilled in the art.
以下,列舉具體例針對本發明進行更詳細之說明,惟該等實施例並未對本發明技術範圍構成任何限定。可配合熟習此技術者所要求的耐水性、溫水洗淨容易性、捲翹力、其他條件而適當調配。另外,以下實施例及比較例中的摻合量(含有量)均為「質量%」。 Hereinafter, specific examples are given to describe the present invention in more detail, but these embodiments do not constitute any limitation to the technical scope of the present invention. It can be appropriately prepared according to the water resistance, ease of washing with warm water, curling force, and other conditions required by those skilled in the art. In addition, the compounding amount (content) in the following Examples and Comparative Examples is all "mass %".
作為皮膜劑係使用聚胺基甲酸酯-35(BAYCUSAN C1010(含有聚胺基甲酸酯-35約40%)、Covestro Deutschland AG製)。 As the coating agent system, polyurethane-35 (BAYCUSAN C1010 (containing about 40% of polyurethane-35), manufactured by Covestro Deutschland AG) was used.
各實施例中,依各極性溶劑相對於皮膜劑總量成為10%的方式添加各極性溶劑。 In each example, each polar solvent was added so that each polar solvent was 10% of the total amount of the coating agent.
相關耐皮脂性、耐水性、溫水洗淨容易性、乾燥性、安定性、斷裂強度(浸水時),係使用將皮膜劑與極性溶劑的混合物利用刮漿刀在玻璃板上塗抹擴展60μm,並經乾燥2小時者作為試料。 Regarding sebum resistance, water resistance, ease of washing with warm water, drying, stability, and breaking strength (when immersed in water), a mixture of coating agent and polar solvent is used to spread on a glass plate by 60 μm with a doctor blade. And dried for 2 hours as a sample.
相關伸縮性,係使用在聚矽氧模具中流入由皮膜劑與極性溶劑混合者2g,利用45℃恆溫槽進行乾燥3小時以上,形成均勻厚膜,將從模具中取出的皮膜切取0.2cm×5cm,載放5kg錘並放置平坦,使用經放冷後者作為試料。 For stretchability, use 2g of a mixture of film agent and polar solvent poured into a polysiloxane mold, and dry it in a 45°C thermostat for more than 3 hours to form a uniform thick film. The film taken out from the mold is cut out 0.2cm× 5cm, place a 5kg hammer and place it flat, and use the latter as a sample after letting it cool.
將人工皮脂(三(辛酸/癸酸)甘油酯(O.D.O、日清Oillio Group(股)製))滴垂2滴在試料上,靜置1分鐘後拭除,然後觀察其表面狀態,由5位審查人員依照以下基準進行評價。全員一致而成為表1所示評價。 2 drops of artificial sebum (tri(caprylic/capric) glycerides (O.D.O, manufactured by Nissin Oilio Group)) were dropped on the sample, left to stand for 1 minute and then wiped off, and then the surface state was observed. A reviewer evaluated according to the following criteria. The evaluations shown in Table 1 were obtained in unanimous agreement.
○:‧‧‧皮膜沒有變化 ○:‧‧‧Film does not change
△:‧‧‧皮膜些微沾黏 △:‧‧‧The film is slightly sticky
×:‧‧‧皮膜明顯沾黏、脫落 ×: ‧‧‧The film is obviously sticking and falling off
將試料在室溫下浸漬於水中24小時,於經5秒、10分、30分、 60分、24小時的時候拍攝試料。圖1係僅由皮膜劑作成試料之例子(例1)。圖2~8分別係使用乙氧基二甘醇(例2)、碳酸丙烯酯(例3)、二丙酮醇(例4)、檸檬酸三乙酯(例5)、乙氧乙醇(圖6)、丁氧基二甘醇(圖7)、或羥丙酮(圖8)作為極性溶劑製成試料的例子。 The sample was immersed in water at room temperature for 24 hours, and the sample was photographed when 5 seconds, 10 minutes, 30 minutes, 60 minutes, and 24 hours elapsed. Fig. 1 shows an example (Example 1) in which a sample was prepared from only the coating agent. Figures 2 to 8 respectively use ethoxydiglycol (Example 2), propylene carbonate (Example 3), diacetone alcohol (Example 4), triethyl citrate (Example 5), and ethoxyethanol (Figure 6). ), butoxydiglycol ( FIG. 7 ), or hydroxyacetone ( FIG. 8 ) as examples of polar solvents prepared as samples.
皮膜呈現白濁的原因可認為係因為水膨潤所致。例1、5在經60分鐘之後,試料分散於所浸漬的水中。 The reason why the film appears cloudy is considered to be due to water swelling. In Examples 1 and 5, the samples were dispersed in the immersed water after 60 minutes.
拍攝結果由5位審查人員依照以下基準進行2階段評價,結果全員一致而成為表1所示評價。 The imaging results were evaluated in two stages by five examiners according to the following criteria, and the results were all agreed and the evaluations shown in Table 1 were obtained.
○:耐水性佳 ○: Good water resistance
×:耐水性差 ×: Poor water resistance
將試料在約40℃溫水中浸漬10秒鐘,由5位審查人員利用手指搓拭10次左右,並依照以下基準進行評價。全員一致而成為表1所示評價。 The samples were immersed in warm water of about 40° C. for 10 seconds, rubbed with their fingers about 10 times by five examiners, and evaluated according to the following criteria. The evaluations shown in Table 1 were obtained in unanimous agreement.
○:‧‧‧完全脫落 ○: ‧‧‧completely fall off
△:‧‧‧5成~9成左右脫落 △: ‧‧‧about 50% ~ 90% fall off
×:‧‧‧沒有脫落 ×: ‧‧‧ not falling off
另外,所謂「脫落」係指溶解或剝離。 In addition, "exfoliation" means dissolution or peeling.
由5位審查人員測量從將試料塗抹於玻璃板後的瞬間起、直到皮膜色成為透明為止的時間,求取其平均值,並依照以下基準進行評價。 Five examiners measured the time from the moment after applying the sample to the glass plate until the color of the film became transparent, obtained the average value, and evaluated according to the following criteria.
○:未滿7分鐘 ○: Less than 7 minutes
△:7分鐘以上、且未滿9分鐘 △: 7 minutes or more and less than 9 minutes
×:達9分鐘以上 ×: Up to 9 minutes or more
將各試料裝入至玻璃瓶中,於45℃下靜置1週~1個月後,針對各試料的狀態利用目視、黏度計測,由5位審查人員依照以下基準進行評價。全員一致而成為表1所示評價。 Each sample was put into a glass bottle and left to stand at 45° C. for 1 week to 1 month. The state of each sample was measured visually and by a viscosity measurement, and evaluated by five examiners according to the following criteria. The evaluations shown in Table 1 were obtained in unanimous agreement.
○:‧‧‧沒有變化 ○:‧‧‧No change
△:‧‧‧略增黏/減黏 △:‧‧‧Slight increase/decrease in viscosity
×:‧‧‧明顯增黏/減黏、出現凝聚物、或產生氣體。 ×: ‧‧‧Viscosity increase/decrease, agglomeration occurs, or gas is generated.
將試料浸漬於約40℃溫水中,由5位審查人員以手拉扯,斷裂強度的官能評價係依1(非常弱)~5(非常強)進行判定,依照以下基準評價其平均值。 The sample was immersed in warm water at about 40°C and pulled by hand by five examiners. The sensory evaluation of breaking strength was determined on a scale of 1 (very weak) to 5 (very strong), and the average value was evaluated according to the following criteria.
○:達3.5以上 ○: 3.5 or more
△:1.5以上、且未滿3.5 △: 1.5 or more and less than 3.5
×:未滿1.5 ×: Less than 1.5
由5位審查人員以手拉扯試料,依1(完全沒有延伸)~5(良好延伸)判定伸縮性的官能評價,依照以下基準評價其平均值。 The sample was pulled by hand by five examiners, and the sensory evaluation of stretchability was judged on a scale of 1 (no stretching at all) to 5 (good stretching), and the average value was evaluated according to the following criteria.
○:達4.0以上 ○: 4.0 or more
△:2.5以上、且未滿4.0 △: 2.5 or more and less than 4.0
×:未滿2.5 ×: Less than 2.5
評價結果如表1所示。例1、3及5係比較例。例2、4及6~8係實施例。 The evaluation results are shown in Table 1. Examples 1, 3 and 5 are comparative examples. Examples 2, 4 and 6-8 are examples.
由試驗結果得知,相較於使用碳酸丙烯酯作為極性溶劑的比較例,本發明的安定性獲得改善。此外,乾燥性亦確認到獲得提升。又,數個例子亦確認到伸縮性提升、或浸水時的斷裂強度提升。 From the test results, it was found that the stability of the present invention was improved compared to the comparative example using propylene carbonate as the polar solvent. In addition, an improvement in dryness was also confirmed. In addition, improvement in stretchability and improvement in breaking strength at the time of immersion in water were also confirmed in several examples.
依照表2,調配2種睫毛化妝料。 According to Table 2, 2 kinds of eyelash cosmetics were prepared.
準備假睫毛(Girl's Secret 01、販售商Elizabeth(股)),將每1束解體。將其中1束依睫毛垂直朝下狀態,將假睫毛根部黏於直立塑膠板上(參照圖9、10),利用睫毛夾使其捲翹,塗抹上述處方(例9~13)之睫毛化妝料30次。在塗抹前及塗抹經5分鐘後,測定捲翹底面至睫毛尾的角度(參照圖9、10)。測定結果如表3所示。 False eyelashes (Girl's Secret 01, sold by Elizabeth Co., Ltd.) were prepared, and each bundle was disintegrated. Place one of the bundles with the eyelashes vertically downward, stick the roots of the false eyelashes on the upright plastic plate (refer to Figures 9 and 10), use an eyelash curler to curl them, and apply the eyelash cosmetic of the above prescription (Examples 9 to 13). 30 times. Before application and after 5 minutes of application, the angle from the bottom surface of the curl to the end of the eyelashes was measured (see FIGS. 9 and 10 ). The measurement results are shown in Table 3.
由試驗的結果得知,相較於比較例(例9),例10的處方係捲翹力獲得提升。此現象可認為因乾燥性與伸縮性提升所致。即,可認為乾燥時皮膜更強地收縮,而提升捲翹力。若相對於皮膜劑與極性溶劑之和,將乙氧基二甘醇從10%(例10)改變為0.1%(例11)時,例11的處方並未觀察到如例10的處方般之高捲翹力,但可獲得較例9(無極性溶劑)更高的捲翹力。又,此效果係在皮膜劑濃度較低時(將皮膜劑與極性溶劑之和從30%(例10)變更為1%(例12))仍可確認到。 From the results of the test, it was found that the curling force of the prescription system of Example 10 was improved compared with that of the comparative example (Example 9). This phenomenon is considered to be due to the improvement in drying properties and stretchability. That is, it is considered that the film shrinks more strongly during drying, and the curling force is improved. When the ethoxydiglycol was changed from 10% (Example 10) to 0.1% (Example 11) relative to the sum of the coating agent and the polar solvent, the formulation of Example 11 did not observe the same effect as the formulation of Example 10. High curling force, but higher curling force than Example 9 (non-polar solvent) can be obtained. In addition, this effect was confirmed even when the concentration of the coating agent was low (the sum of the coating agent and the polar solvent was changed from 30% (Example 10) to 1% (Example 12)).
Claims (2)