TWI248355B - Cover sheet for personal care products - Google Patents
Cover sheet for personal care products Download PDFInfo
- Publication number
- TWI248355B TWI248355B TW091133231A TW91133231A TWI248355B TW I248355 B TWI248355 B TW I248355B TW 091133231 A TW091133231 A TW 091133231A TW 91133231 A TW91133231 A TW 91133231A TW I248355 B TWI248355 B TW I248355B
- Authority
- TW
- Taiwan
- Prior art keywords
- layer
- liner
- hydrophilic
- hydrophobic
- fibers
- Prior art date
Description
1248355 l、發明說明 (發明說明應敘明:發明所屬之技術領域、先前技術、內容、實施方式及圖式簡單說明) 發朗頷域 本發明爲關於個人看護用產品的襯墊、上薄層或罩板, 比如像婦女衛生產品、尿布、兒童訓練用褲等等。 襯墊設計成可滲透液體及不刺激肌膚,因爲有個人看護 用產品的最外層,並與穿戴者接觸。襯墊對肌膚而言觸感柔 軟,並允許尿液及月經相當輕易滲入。襯墊已由各種不同材 料製造,包括非織造織物、有孔薄膜、泡沫狀物質或其組合。 非織物及薄膜可由合成聚合物製造,包括聚烴,比如像聚乙 婦及聚丙婦。非織物也可由天然纖維或天然纖維及合成纖維 的組合製造。襯墊也可由起縐材料製造,比如起縐的非織造 織物。 發明瞀孑 襯墊已顯著提昇數年,雖然穿戴者肌膚的再濕及洩漏(尤 其在婦女衛生產品的情形下)剩下重要關鍵。因此,剩下需要 可迅速吸入像尿液及月經般的液體之襯墊,並阻止或預防液 體再次向上移至穿戴者。 發明极迷 爲響應先前技藝所遭遇的探討難題及問題,已發展出新 襯塾:其中婦具有親水性第—有孔非織物層,此層與疏水 性的第二有孔非織物層叠合在一起。這些孔排成一列。再 者,第一層可由耐久性的親水性纖維製造,第二層可由非耐 久性的親水性纖維製造(之後製成疏水性)。襯塾可由纺絲直 接編網法製造。襯塾可進一步具有運用於親水層的處理方 瓣噶註記並麵_ 1248355 發明說明β頁 式此處的處理方式爲麓薈、維他命Ε、礦物油、碳酸氯納 及其組合物。 本發明的另一實施例爲以短纖維、天然親水性纖維水糾 纏製造的第一非織物層,以形成與由疏水性纖維製造的第二 非織物層疊合,此處的疊合製品具有10〜50%區域有孔。襯 塾進一步具有由人造絲、紙漿、棉布、天然親水性纖維及其 混合物之親水性纖維製造的第一層。疏水性纖維可由聚合物 製造’比如像聚烴、聚g旨、丙烯酸及其混合物製造。 也提供具有可透液體襯墊、不透液體隔板及位於之同的 吸收芯之襯褲。根據紡絲直接編網法,襯墊具有親水性的第 一有孔之非織物層,此與疏水性的第二有孔之非織物層疊 合。第一層及第二層的孔排成一列。 此發明的襯墊可使用於其他個人看護用產品,比如像尿 布、兒重訓練用褲、可棄式泳衣、吸收性内褲、成人失禁用 品、繃帶、獸醫及埋葬用品以及婦女衛生用品(比如衛生棉)。 並揭發製造個人看護用產品的襯墊,此含有水糾纏一親 水性第一非織物層及疏水性第二非織物層,並將這些層開 孔。這些層可同時開孔,以製造出排成一列的孔。 圖式簡Μ 第一圖爲使用於試驗此發明試驗的速率模板之圖示。 可棄式”(disposable)包括單一使用後且不打算清洗 及再次使用的處置。 “親水性’’(hydrophilic)描述以水溶液與纖維接觸浸濕 1248355 發明說明_頁 =減維或纖維表面。材料的濕潤程度可依序以接觸角度及液 =材料含有的表面張力之説法來描述。適合測量特殊纖維 材料之可濕性的裝備及技術可由sfa一222表面力量分析器 系統或實質上相等系統提供。當以此系統測量時,具有接觸 角度小於90。的纖維設計成“可濕性”或親水性,同時具有 接觸角度等於或大# 9〇。的纖維設計成“非可濕性”或疏 水性。 ^ 如此處所使用“非織造織品或織物”(n〇nw〇ven of web) 一詞意指具有交又平行之個别纖維或細絲結構的織 物,但並非與編織織品視爲同一方式。非織造織品或織物已 由許多過程形成,比方舉例來説有熔吹過程、紡黏過程及黏 合柅機纖維網過程。非織造織品的基重通常以材料的盎司/ 平方英碼(osy)或克/平方公尺(gsm)表示,且有用的纖維質竟 通常以微米表示。(注意由osy轉換成gsm需乘上33 91) 如此處所使用熔吹式纖維”(meltblown fibers)—詞音 指由擠壓一熔解熱塑性材料經過多數纖細且通常爲圓形的 印模毛細管,儘管鑄造細絲或單纖維進入集中高速且通常爲 為的氣流(比如it氣),此減少缚造熱塑性材料的單纖維,以 降低本身直徑’此可爲微纖維直徑。之後,熔吹式纖維可由 高速氣流運送,並沉澱於一集合表面,以形成一任意分散之 炼吹式纖維的織物。舉例來説,此一過程由Butin等人揭發 於美國專利編號第3,849,241號。熔吹式纖維爲連續或間斷 纖維的微纖維’一般平均直徑小於10微米,且一般沉殿於 一集合表面時爲膠黏。 0續次頁(發明說明頁不敷使用時’請註記並使用續頁) r \wiKtQnPnntHrAPaff>nAPki)01 〇8-\0810^Κ-001-0810.Doc January 15, 2003 1248355 發明說明_胃 紡黏纖維’’(spunbonded fibers)意謂小直徑纖維,此由 擠壓鑄造熱塑性材料形成,此為來自多數纖細吐絲口的毛細 管。舉例來說,此一過程由Appe丨等人揭發於美國專利編號 第4,340,563號以及由Matsuki等人揭發於美國專利編號第 3/802,8 1 7號。這些纖維也可具有外形,比方舉例來說, 等人描述於美國專利編號第5,277,976號,此以非傳統外形 來描述纖維。 士此處所使用水糾纏(hydroentangling)—詞意指一 過程,其中非織造織物或非織造織物層在高能量及充分時間 下加入非壓縮流體(例如水)水流,以糾纏這些纖維。約使用 在200與5000 pwgG 4〜351公斤/平方公分間距)之間的壓力 則有利於此流體高過織物僅少數英吋(公分)距離,同時織物 由網狀結構支撐。此過程由Evans等人描述於美國專利編號 第3,486,168號,其合併於此作為參考。舉例來說,加入水 糾纏的非織造織物稱為“紡絲直接編網”織品。 “黏合梳機纖維網”(bonded carded web)引用由短纖維 製造,此傳送經過梳理裝置或梳機裝4,此分離或斷裂分 開,且在機械方向中將短纖維排成一歹,j,以形成一般機械方 向的纖維狀非織造織物。此材料可用點狀黏結;完全空氣黏 結、超音波黏結、黏性黏結等等的方法黏結在一起。 氣流成網”(airlaying)為形成纖維狀非織造層的著名 過程。在氣流成網過程中,分離具有一般長度(範圍約為3〜52 笔米(mm))的小纖維束,並於空氣供應中輸送,然後沉殿於 成形、、罔通㊉以真空供應幫助。然後任意沉澱的纖維彼此 10 1248355 赛〜在一起,舉例來說,使用的方 - 劑0泉仏丨步、、,γ 、丄 馬…工乳或噴灑黏著 舉例來况,氧流成網由Laursen等 4,_,m號中有指示。 ’人在美國專利編號第 出物的=看護用產品” (PerS〇nal⑽Pr〇duct)意謂身體滲 出的吸收屋品’比如尿布、兒童訓練用褲、可棄式泳衣、 :内襌、成人失禁用品、編帶、獸醫及埋葬用品以及像 術生棉及襯褲的婦女衛生用品。 “目標區域”(target area)爲穿戴者弄辨個人看護用產 品的區域或位置。 &M ^ it A ^ 蓋ϋ割3英忖(7·6公分)直徑的圓形樣本,並使用磅 秤秤重。記錄重量(克重)。重量除以樣本面積。測量五個樣 本並平均。 肢顧料的測徑器爲厚度的測量,並在 ^.05 ρ = 3·5克/平方公分)下以STARRET㊣體積試驗器測量, 單位爲毫米。樣本切成4英吋χ4英吋(1〇 2公分χ ι〇 2公分) 的四方形,且試驗五個樣本,並接結果平均之。 材料的密度以每平方公尺(gsm)之樣本的每單位 面積的重量(克)除以材料的測徑器(毫米)。測徑器可在上面 提及的〇.〇5pS1(3.5克/平方公分)下測量。結果爲乘上〇 〇〇1 以轉換成每乂方公分的克重(g/cc)。估計全部五個樣本,並 平均以得到密度數値。 試驗爲審查織品的流體處理特 性。使用下面程序及裝備: 用時’請註記並使用顯) 11 1248355 發明說明_頁 記錄每層的乾 1.摺疊非織物吸入絨毛襯墊上的試驗樣本 重、尺寸及厚度。 2·將速率模板置放於樣本上方。漏斗置於速率模板中的小上 方孔。 3·將吸量管尖端附著於Pipetman。以〜他⑽瓶將6 〇 μ 的流體送入速率模板上的漏斗。 4.使用Pipetman瓶模擬將吸收材料以6 〇…的弄 辨。使用馬錶測量流體分送至材料直到所有流體被吸收的 時間長短。記錄此時的吸收時間。 5 ·等待6 0秒。 6. 將速率模板自樣本及絨毛襯墊除去。 7. 將吸收材料樣本及絨毛襯墊置放於壓力臺的熱水瓶上。將 二片預先秤重的吸墨紙置放於樣本上方。然後壓下壓力間 距的試驗鈕,開始將製作將LO psi的壓力運用於系統3 分鐘的計劃。3分鐘後,壓力臺降低,壓力自吸收材料分 離。 8 ·再次將濕吸墨紙秤重。記錄重量。在吸墨紙中增加的水分 顯示自系統的紙張對流體的吸收(克)。 9·秤重且檢查浮凸絨毛及非織物試驗樣本的厚度。記錄結 果。
Gilson Pipetman P5000,使用RC-5000吸量管尖端及吸 量管過濾器 具有定時開關的ω工程壓力間距,模型HHP-70 1-20 12 1248355 . · 發明說明續頁 具有壓力凱的吸墨紙再濕壓力臺 馬錶 吸入織品樣本材料,大約5”X 5” 解吸材料-600 gSm正弦波浮凸絨毛 Z date /瓜體,獲自威斯康辛州Applet〇n的c〇nkey St.2901 號的 BASF Corp.。 耐熱有機玻璃速率模板(視第一圖)··襯墊(13)置於吸收 材料(14)上方,且將速率模板(1〇)置於該二物的上方。速率 杈板(10)為3英吋(76.2毫米)寬及2·87英吋(72 9亳米)深(進 入頁面),且總高為1.125英吋(28·6亳米),此包括在速率模 板(1〇)底部上的中央區域,此從速率模板(1〇)的主體遠離突 出,並具有0.125英吋(3.2毫米)的高度以及〇·886英吋(22 5 亳米)的寬度。速率模板(1〇)具有内側直徑為〇186英对(4.7 毫米)的毛細管,其從一側往下斜向延伸至中央線,此與水平 線的角度為21.8度。毛細管(12)可由自模板(1〇)側面鑽適當 大小的孔,一開始的適宜角度為速率模板(1〇)底部上方的點 0.726英吋(18.4耄米);無論如何,在側面中提供鑽孔的起點 之後必須塞住,因此試驗流體將不會漏出。上孔具有〇 · 32 英吋(7.9毫米)的直徑,以及〇·625英吋(15·9亳米)的深度, 因此與毛細管(12)相交。上孔與速率模板(1〇)的上方垂直, 亚自側面集中0.28英吋(7.1亳米)。上孔開孔以放置漏斗 (1 1)。中央孔乃是為了觀看試驗流體的漸進,且事實上為橢 圓形進入第一圖的平面。中央孔中央橫置於速率模板(1〇) 上,並自中央至形成橢圓形末端之O SH英对(8毫米)直徑半 Θ續次頁(發明說明頁不敷使用時,請註記並使用續頁)
Mavis-C:\Eunice 2005\PK-001-08\PK-00^08ί0\PK-00ί-08ί¢)-2-ίOri-Mav/sj.Doc November 14, 2005 〆 13 1248355 . 發明說明ft頁 圓形具有0.315英吋(8毫米)的下孔寬度以及ΐ·5〇英吋(3^ 宅米)的長度。為了方便觀看,自速率模板(1〇)底部,橢圓形 放大尺寸高於0.44英吋(11.2毫米),且長度為1.930英忖(4 9 毫米)。上孔及中央孔也可鑽孔形成。 較佳實施例詳細掘述 近代的個人看護用產品通常具有一外罩、>内芯部分及 僅靠穿戴者肌膚的襯裡。 外罩或“隔板”設計成不透液體,此乃是為了保護穿戴 者的衣物及被褥免弄髒。不透隔板最好由薄膜製造,且一般 由塑膠製造,雖然也可使用其他材料。也可使用非織造織 物、薄膜或覆蓋在非織物的薄膜。隔板的適當薄膜組成包括 聚乙烯薄膜,此最初厚度約為〇·5密爾(0.012毫米)至5.0密 爾(〇·12毫米)。隔板可任意為可透蒸氣或氣體的多微孔“可 吸入材料形成,此可透蒸氣或氣體實質上為不透液體。舉 例來說’吸入能力可藉由使用薄膜聚合物配方中的填料添 加’也可藉由將填料/聚合物配方擠入薄膜,然後將薄膜充分 拉伸’以在填料顆粒四周產生空隙,藉以製造可吸入的薄 膜。通常,使用更多填料,且更高度拉伸,更大吸入能力。 也可使用其他適當熱塑性材料(像烴、尼龍、聚酯、聚乙烯及 聚丙烯的共聚物)。 個人看護用產品的芯部分設計成吸收液體,其次含有固 體。芯(已知為吸收芯)、保留層等等可用紙漿與/或者超吸收 性材料製造。這些材料相當迅速吸收液體且有效,此乃為了 頁一 ’難記並使臓頁) 14 1248355 發明說明續頁 使洩漏減至最低。芯材料可根據一些過程製造,包括共形成 過程、氣流成網及黏結並機梳,且在50〜350 gsm之間。 一些個人看護用產品可包括各種不同其他層。這些包括 屬流層,通常位於襯裡與芯之間,並設計成含有大量湧流液 體,因此芯可超時吸收。許多個人看護用產品也包括分布 層。分布層通常位於芯隔壁,並採用湧流層或襯裡層的液 體,亚分布於芯的其他地區。在此方式中,與其大約在目標 區域内完全吸收液體,更可使用吸收芯。 、襯裡設計成可高滲透液體,且不刺激肌膚。襯裡可任意 i過層,或在中央區域中具有一層,此層在側面區域中具 有多層。相反形狀也可能再中央區域有二或更多層,且在側 面僅有一層。 更多先進類型的襯裡可結合洗劑或藥劑的處理方式,以 改善接近肌膚的環境,或實際上改善肌膚健康。此類處理方 式包括浮會、維他命E、礦物油、碳酸氫鈉及由精通技藝人 士熟知或發展的其他調配劑。這些處理方式運用於襯裡表 面,此將與穿戴者的肌膚接觸。 务明者已發現此對親水層彳冑助,可作為♦裡的最外體 〇。卩刀此處與穿戴者有接觸。結果使流體吸收非常迅速。 +無論如何,在許多狀況中,吸收芯上方的親水層允許液體自 芯朝穿戴者再次向上移動,並使穿戴者肌膚“再濕”。此也 將允許以體自目標區域蔓延至襯墊的側面,因此舉例來說, 玷污區域比薄冑覆蓋襯墊大很多。$些將視為纟可棄式個人 看護用產品中的負面因數,因為結果為弄髒衣物及被得,並 明頁不敷使用時,請註記並使用續頁) 15 1248355 發明說明 使穿戴者感到不舒適。 叙使疏水層位於親水性襯墊下方,液體從濕芯向上移動 的能力顯著降低。此結果為有較佳“再濕,,值、較小玷污大 小、減少玷污顏色強度,並有助於使穿戴者保持較乾燥。不 巧’低於親水層的疏水層也阻礙液體自穿戴者移動至吸收 芯,此引起在襯墊上液體積水。此最後引起流出並弄髒衣物 及被褥’就疏水層的問題乃嘗試解決。 發明者提出二方式以疏水層來解決此問題;藉由開孔以 及使用層壓過程連結,此牽涉化學及熱黏結過程。 親水層及疏水層的開孔提供迅速至吸收芯的通道,液體 來自襯塾表面。此解決問題提出疏水層阻礙液體通過。一旦 液體通過這些孔,有益於蔓延出疏水層下方,並進入吸收 芯。液體向上返回的數量顯然比液體向上通過單獨親水襯墊 的數量小。 將豐合製品開孔可發生於水糾纏之後、期間或之前,此 將在下面討論,雖然之後較佳。開孔可由任何熟知技藝的方 式完成,包括使用機械式木栓開孔、印模切割或於一方式中 形成材料,此由位置的孔產生。這些孔也可經由使用高壓水 喷射’同時發生水糾纏。可在襯墊的表面區域開孔,使產生 10〜50%的開口面積,尤其在2〇〜40%,且更特別約在25%。 水糾纏過程使用於連結這些層,此替代化學及熱黏結方 式,在這些交叉點,產生沒有熱溶解的纖維。此避免較大量 的熱塑性物質產生,此可阻礙流體移動。也可使用高壓水糾 纏’以在作用期間自疏水層除去不财久性的親水表面處理方 Θ續次頁(發明說明頁不敷使用時,請註記並使用續頁)
Mavis-C:\Eunice 200^KM1-08^K-Q01M1(J^K-001^810-2-(Ori-Mavis).Doc November 1, 2005 16 1248355 式 親水層的纖維製造包括天 龍)或已處理成親水性之天^ μ ^(tb如棉布及尼 處理成親水性的合成纖假使纖維為 双、鐵維,處理方式必須為耐 水糾纏的嚴酷。所有層的纖維不需為:抗 親水性。此層可由纖維混合物製造。 …多數為 疏水層的纖維製造包括天然疏水性纖維,比方 合物纖維。纖維層不需皆為 口成t 印不而自為疏水性,只要層多數為疏水性。 此層可由纖維混合物製造。如上面提及,在作用期間,水糾 纏也可使用於除去之前自疏水層運用不耐久性的親水性表 面處理方式,因此再次成為疏水性。 产此發明的纖維層可由已知技藝的非織造作用製造,包括 氣流成網、紡黏、炫吹及短纖維機梳。這些層的基重為每個 0.25〜3 osy(8.5〜102 gsm)。 合成纖維包括由聚烴、聚醯胺、聚酯、丙烯酸、 LYOCELL®改良纖維素、Lenzing's黏膠纖維,以及已知精通 技藝的任何其他適當疏水性合成纖維製造。許多聚烴可用於 纖維製造,舉例來說有聚乙烯,比如D〇w chemical、s ASPUN⑧6811A襯墊低密度聚乙烯、2553 LLDpE以及25355 及123 50兩密度聚乙烯為此適當的聚合物。聚乙烯有熔流速 率,約個別為26、40、25及12。纖維形成聚丙烯包括M〇ntell 化學公司的PF304。也可利用其他聚烴。也適合使用具有較 低溶解聚合物成分的纖維(比方像複合與雙成分纖維)。此類 纖維包括聚烴、聚醯胺及聚酯的複合纖維,比方像外勒芯複 E□續次頁(發明說明頁不敷使用時,請註記並使用續頁)
Mavis-C:\Eunice 2005^K-mimPK-0Q1-081(^PK-mM10-2-(Ori-Mavis).Doc November 1,2005 17 1248355 ___ 發明說明Mg 合纖維’此獲自名稱T-255及T-256下的KoSa Inc.(北卡羅 來納州的Charlotte)。 天然纖維包括羊毛、棉布、亞麻、大麻及木質紙漿。木 質紙漿包括標準軟木絨毛階級,比如CR-1 654(阿拉巴馬州 Coosa的US Alliance Pulp MiUs)。可變更紙漿,此乃為了提 高纖維固有特徵及作用能力。 此發明的體側層最好由具有少量疏水性纖維的親水纖 維混合物製造。親水性纖維的數量由50〜1〇〇 wt%,尤其是 70〜100 wt%,更特別的是8〇〜1〇〇 wt%。 遠離身體的層多數為疏水性纖維。對此類產品而言,低 價的聚丙烯纖維成為優良選擇,可使用差不多1〇〇 wt%數量 的聚丙烯纖維。具有像PET之其他纖維的聚丙烯混合物也有 效。 下面可用來幫助此發明。 範例 1 一層疊合製品製成有上方及體側面層及一底部或吸收 心面層。上層為〇·4〇 OSy(i3.5 gsm)的梳機纖維網,及具有 90 wt%的Ray0n、天然親水性纖維及wt%的聚乙烯對苯 二甲酸鹽(PET)纖維。底層為〇·47 osy(l 6.5 gsm)梳機纖維 網’此纖維網具有73 wt% PET及27 wt%聚丙烯(pp)纖維。 這些層在水壓為43 5〜725 ?8:1(3 0〜51]^^1112)下水糾纏,且之 後在密度大約50孔/平方公分下以580 psi(41 kgf/cm2)的水 糾纏作用開孔。這些孔的直徑約為〇 〇6毫米,面積約為〇·3 平方亳米。這些孔概略為菱形,因為疊合製品上的網孔被撐 酸記並麵續頁) 18 1248355 發明說明_頁 成菱形。具有其他形狀的支撐媒介物最後孔為其他形狀及大 λ|、〇 控制 單層襯墊具有親水性特性。襯墊由80 wt%的人造絲及 2〇%PET纖維。此襯墊的基重為〇·89 〇sy(3〇 gsm),且在相同 方式中開孔’且圖案如第一圖。 範例1及控制乃根據吸入速率及上面的再濕試驗試驗 之,結果如表所示。了解到此發明的襯墊的吸入速率比控制 襯墊快。再濕速率也更佳。進一步注意的是,與使用相等數 量的豬血比較試驗下,玷污大小與控制及範例丨不同。玷污 長度約與較寬的控制相同,但形狀及寬度不同,有更多橢圓 形及較窄的範例1及更多長方形。 1 -控制 -範例1 吸入速率(秒)爯逼 14.4 1.5 13.7 1.3 如精通技藝所了解,在那些精通技藝範圍内考慮對發明 的改變及變更。發明者對此類改變及變更乃意圖表現於發明 範圍内。 纖記鎌臓頁) 19 1248355 發明說明$賣Μ 圖式元件簡單說明 10 rate block 速率模板 11 funnel 漏斗 12 capillary 毛細管 13 liner 襯墊 14 absorbent 吸收材料 θ續次頁(發明說明頁不敷使用時,請註記並使用續頁)
Maw,s-C^unice 2005\PK-00[08\PKW1-0810\PK-001-0810-2-(Ori-Mavis).Doc November 14, 2005 20
Claims (1)
1248355 拾、申請專利範圍 1 · 一種個人看護用產品的襯墊,其包含一親水性的第一有 孔非織物層,此非織物層與疏水性的第二有孔非織物層 疊合,其中該第一層及第二層的孔排成一列,且將該聲 水性第二層置於該親水性第一層的下方,可降低該個人 看護用品之吸收芯中的液體向上回滲。
2. 如申請專利範圍第1項的襯墊,其中該第一層包含耐久 性的親水性纖維。 3. 如申請專利範圍第i項的襯墊,其中該第二層包含不耐 久性的親水性纖維。 4. 如申請專利範圍第i項的襯墊,其中該層根據紡絲直接 編網作用而層壓。 5.如申請專利範圍第1項的襯墊,進一步包含運用於該 水層的處理方式,該處理方式選自蘆薈、維他命 物油、碳酸氫納及其組合物的組成。
6· -種個人看護用產品,其包含第—非織物層此層為短 維、天然親水性纖維,水糾纏再一起形成具有第二非 物層的疊合製品’此第二非織物層包含疏水性纖維, 中該疊合製品具有10〜50%的孔。 7.如申請專利範圍第6項的襯墊,其中該第一層包含親 性纖維,其選自由人造絲、紙漿、 ’ 水铞I、天然親水性 維及其混合物組成。 8 ·如申請專利範圍第6項的襯墊,i中 ,、r忒弟二層包含由 鱗,請註記並醜_ 21 1248355 I-—π 申請專利範圍續頁 合物製造的疏水性纖維,此聚合物選自由聚烴、聚酯、 丙烯酸及其混合物組成。 9 ·如申請專利範圍第6項的襯墊,其中該疊合製品具有 10〜50%的孔。 10·如申請專利範圍第6項的襯墊,其中在該層中的孔排成 一列。 1 1 · 一種包含有申請專利範圍第1 0項之襯墊的個人看護用 產品。 12· —種包含可透液襯墊、不透液隔板及之間吸收芯的襯 褲,其中根據紡絲直接編網作用,該襯墊包含與疏水性 第二有孔非織物層疊合的親水性第一有孔非織物層。 1 3 ·如申清專利範圍第12項的襯褲,其中該第一層及第二層 的孔排成一列。 14. 一種製造個人看護用產品之襯墊的製造過程,其包含水 糾纏親水性弟一非織物層以及一疏水性第二非織物 層,並將這些層開孔。 15·如申請專利範圍第14項的製造過程,其中該層同時產生 排成一列的孔。