TW593671B - Method for producing waxy decoration and product therefrom - Google Patents

Abstract

The present invention relates to a method for producing a waxy decoration and a product therefrom. The invented method comprises: preparing a polyethylene wax (PE wax), a hydrogenated polymer, and a paraffin oil at a suitable ratio; melting and throughly mixing the PE wax, hydrogenated polymer, and paraffin oil; pouring the resulting liquid into at least a mold having a specified shape; cooling the molding(s) to form at least a waxy decoration, the external surface of the waxy decoration having a specified shape; preparing at least a clear colloidal component; melting the colloidal component into liquid; coating the external surface of the waxy decoration with the liquid colloidal component without melting the wax on the external surface of the waxy decoration; and performing a cooling procedure for the liquid colloidal component to coagulate and tightly adhered to the external surface of the waxy decoration. A product according to the invention is made by melting a polyethylene wax (PE wax), a hydrogenated polymer, and a paraffin oil at a suitable ratio; and cooling the molten liquid to form a waxy decoration, where the external surface of the waxy decoration has a specified shape. The waxy decoration can be formed into an arbitrary configuration according to the shape of a specified mold. The waxy decoration can include at least a colloidal component coagulated and tightly adhered to the external surface thereof, where the melting point and the solidification point of the colloidal component are lower than those of the waxy decoration.

Description

593671 _ Case No. 90127402 V. Description of the invention (1) [Background of the invention] With the widespread use of electricity and electric lamps, it has become the main and indispensable source of lighting for modern people. Lighting sources in early societies, such as coal lamps, candles, etc. Etc., are not the lighting tools used in everyday life; among them, the earthen candle can be used for emergency lighting only in the event of a power failure, except for the special use of religious beliefs. Features are decorative items. The conventional decorative candle products only change the color and appearance shape, or force t in the wax raw material; the general flavor is added so that the candle can generate a scent when it is burned; these appearance-modified candles Or wax costumes can't be manufactured and preserved because of their low strength and poor elasticity due to the quality enhancement. Moreover, their appearance and shape are easily deformed by the local temperature increase, and they are often caused by collisions and falls. It is damaged by falling to the ground; for example, various factors have caused the design limitation of the decorative articles made of fiber materials, and the decorative efficacy of the decorative articles is reduced. Conventional case 1, as shown in the first figure, when a pigment is added to the raw material of the gelatinous component (50) or the waxy decoration (51), the gelatinous component (50) or the gelatinous decoration The color of (5 1) will cause the condition of mutual pigment penetration (5 2), which destroys the original design and the colors made by it, and can not exert the original beauty on the visual. In the second case, as shown in the second figure, during the manufacturing process, the glue component (50) and the surface of the waxy decoration (52) were melted, and a paste mixed with each other was generated around the contact surface. In the state of waxy (53), the finished product completely destroys the original design of the waxy decoration (51). 1 shape and 2 colors, which cannot produce the visual originality of the product: 5936671

Based on the limitation and research on the use of soil to make the city, the manufacturing method of a kind of cormorant ornament and its production ... = to > A colloidal component is coagulated and fixed and tightly wrapped and connected to at least one The external surface allows the waxy decoration to be formed into any shape according to the shape of a preset mold. [Summary of the Invention] The present invention is a method for manufacturing a waxy decorative object and its products. The steps of the method are as follows: preparing an appropriate ratio of polyethylene wax (PE Wax), hydrogenated polymer, and white wax oil. Material; Polyethylene Wax, hydrogenated polymer and white wax are melted to form a liquid and fully mixed; the liquid is poured into at least one mold having a defined shape, and cooled to cool to make at least A waxy decoration, the outer surface of the at least one waxy decoration has a defined shape; at least one gum component is prepared, the gum component is transparent, and the gum component is heated to melt into a liquid state to make the liquid state The gelatinous component is filled and covered on the outer surface of the waxy decorative object, but it is not fused in the waxiness of the outer surface of the sacrificial decorative object. The outer surface of the iron shell is thinly covered with germanium. # # 番 的 聚乙 The product of the present invention is Huanli at an appropriate ratio ^ κ aa »White wax oil material Mixed warming (Polyethylene Wax), hydrogenated polymer and > missing decorations' The 4 argon decoration is melted into a liquid state, and the wax is made after cooling. Preset mold 1 _ • The shape of arsenic wax decoration can be used, can be formed into any plastic body, ^ ---

The outer surface has a defined shape. The wax is cold w ^ 593671 _ Case No. 90127402__ Year Month-Amendment ___ V. Description of the invention (3) At least one colloidal component is coagulated, fixed and tightly wrapped and connected to the external surface, and the gelatinous component has a low melting point and freezing point To the waxy ornament. A first object of the present invention is to provide a method for producing a waxy decorative object and a product thereof, which are polyethylene wax (P ο 1 yethy 1 ene W a X), hydrogenated polymer, and white oil in an appropriate ratio. The materials are mixed and heated to melt into a liquid state, and then cooled to cool to form a waxy ornament. The outer surface of the waxy ornament has a limited shape, and can be formed into any shape according to the shape of a preset mold. The ingredients are coagulated, fixed and tightly covered and connected to the outer surface of the waxy decoration. The gum component is transparent and soft, which can protect the outer surface of the waxy decoration. The waxy ornament. 2. The second object of the present invention is to provide a method for manufacturing waxy decorative objects and products thereof. The natural inorganic pigments suitable for the gelatinous ingredients or the original waxy decorative objects can be used to make the gums The composition or the butterfly-shaped object = has any color, and the colors of the gum component or the waxy decoration will not penetrate each other, and it can maintain the original design, manufacturing color, and perceived original beauty. The third purpose of the excellent method is to provide a 14-item product that can be made of qualitative packaging. 'The gelatinous ingredients or the waxy decorative objects of the manufacturing process can be produced. Soluble / flavor will not disappear because the product is placed in open space. [Detailed description] The features and functions of the present invention 2 will make your reviewing committee understand the purpose of the present invention. The following specific examples and the accompanying drawings 593671 ——__ Case No. 90127402_ year month day amendment ______ five 2. Description of the invention (4) A detailed description is as follows: As shown in the third figure, it is a flowchart of the manufacturing method of the present invention; the present invention is a manufacturing method of a quality decoration and its product The steps are as follows: (a) Prepare polyethylene wax (PE Wax, Polyethylene Wax), hydrogenated polymer and wax oil material in appropriate ratios; (b) Polyethylene Wax, hydrogenated polymer and wax The oil is heated to melt into a liquid state and fully mixed; (c) the liquid is poured into at least one mold having a defined shape, and cooled to cool to form at least one waxy decoration, the waxy decoration The outer surface has a defined shape; (d) preparing at least one gum component, the gum component is transparent, and the gum component is heated to melt into a liquid state; the temperature of the liquid gum component is adjusted to match the wax content The decoration will not melt or melt the surface of the waxy decoration when it comes into contact; (e) Fill the liquid gelatinous component and cover the outer surface of the waxy decoration, but not fuse with the waxy decoration In the waxy surface of the waxy surface; (f) cooling and cooling to condense and fix the liquid colloidal component and tightly cover the outer surface of the waxy decoration. According to the manufacturing method of the present invention, the hydrogenated polymer is: "a styrene cross-linked polymer containing hydrogenated 2methyl 1,3 butadiene and 1,3 butadiene" (English chemical name "Styrene block polymer with 2-methyl-l, 3-butadiene and 1, 3-butadiene,

593671 I--1 柳 27402 _Year Month Day Amendment V. Description of Invention (5) hydrogenated "). In the steps (a) and (b), the weight ratio of the polyethylene wax (hydrolyzed polymer: white wax) is about 3 to 6%: 7 to 11 ° / 〇: 85 to 88% At this weight ratio, its melting point and freezing point are about 80 ~ 170 ° C. The preferred weight ratio of the polyethylene wax (hydrolylated polymer: white wax) in steps (a) and (b) is 4.5%: 9 0 / 〇: 8 6 · 5%. At this weight I ratio, its melting point and freezing point are approximately 1 2 5 ° C. The preset test tool is not 'the 塩 is in the step material,%: 89-93 ° C, which is lower than that in the step material' 〇 / 0: 910 / 〇 The waxy material is thin and hydrogen, so that According to the shape of the step machine pigment, step (c), the waxy decorative object (丨 〇) can be formed into any shape body, as shown in the fourth and fifth figures :: decorative object (10) Shape the lotus mist or flowers. Step (d) The rubber & parts are hydrogenated polymer and white oil mixed with the hydrocyanated polymer: the weight ratio of white wax oil is about 7 ~ n%, and its dazzling point and freezing point are about 1%. It is the melting point and freezing point of this waxy decoration. In step (d), the colloidal components are each "°" ##-A 咿 %% a also oxidized polymer and white wax mixed with the broadening compound :, the preferred weight ratio is about 9 Π points and The freezing point is about 120 ° C, and the melting point and freezing point of the decorative object are low. Yiming's manufacturing method, in the step (a, ten ~, halogenated polymer, white wax oil material force: ⑨Polyethylene wax in 5 Hai In the natural inorganic color of the decorative object, the colloidal component can be added to the colloidal component to have any color ...

Page 9 593671 Amended J No. 90127402 5th, Description of the invention (6) Chemical polymerization step (a) or (b) and / or step (b), in the polyethylene wax, hydrogen bran helmet II, Add appropriate days to the white wax oil material and / or the gum component =: the color of the waxy decoration and / or gum component when the material is used = permeate 'can maintain the original design, manufacturing color, and visual See original beauty above. You can use the appropriate fragrance in step U) or (b) and / or step (d) to add the appropriate fragrance to the polyethylene wax, hydrogen = 5, wax oil material and / or the gum ingredients. It emits fragrance and the fragrance does not dissolve in water. According to the manufacturing method of the invention, in step (e), a container for accommodating the waxy decoration ^ ^ may be provided, and the container may have any shape appearance, which is clear or non-transparent. In step e, during the specific implementation, the liquid gum component is controlled to a temperature of 120 degrees c, and the liquid gum component of 20 degrees C is slowly added to the solid waxy decoration. The appearance of the 120 ° C liquid colloidal component is in contact with air at normal temperature during the slow filling process. The liquid colloidal component has been cooled to below 2 ° C by normal temperature air before it has condensed into a knee shape. For example, it becomes a fluid of about 80 to 90 degrees C, and the liquid colloidal component of 80 to 90 degrees C is used to contact the coating melting point. The solid waxy decoration of 25 degrees C, the temperature difference between the interface between the two reaches Above 3 5 ~ 4 5 ° C, the surface of the solid waxy decorative object will of course not have a state where the interface is partially fused, and even in the thin and thin part of the waxy ornament, there is no state where the interface is locally fused. In step e, another specific embodiment is that the liquid colloidal component at 120 degrees c is slowly filled in a container, and the liquid colloidal component at 120 degrees c is slowly added to the container at room temperature. The temperature of the air and the container contacted, before it was condensed into a gel, the temperature had dropped below 20 ° C, and became about 80 ~ 90 ° C.

P. 10 593671

V. Description of the invention (7) Fluid, and then put the solid waxy decoration into the liquid colloidal component of 80 ~ 90 degrees c, and contact the coating melting point with the liquid colloidal component of 80 ~ 90 degrees C. 125 The solid waxy decorative object with a degree C has a temperature difference of 35 to 45 degrees C or more at the interface between the two. Of course, the surface of the solid fibrous decorative object will not produce a state where the interface is partially fused. In the manufacturing method of the present invention, in step (e), a layer of Cainan warm film can be laid in a molding mold, and then the electric decoration is placed therein, and the outer surface of the loam decoration is filled with the gum component. After the cooling is completed, remove the film from the molding mold and remove the film. Referring to the seventh figure, the molding mold (31) is cylindrical. A layer of high temperature resistant film (32) is laid in the molding mold (31). The waxy decoration An object (10) is placed therein, and the waxy decoration (10) is filled with the gelatinous component (20), and after cooling, the thin mold (32) is taken out of the molding mold (31). Then remove the film (32). In the manufacturing method of the present invention, in step (e), referring to the sixth figure, a candle wick (40) can be placed beside the waxy decorative object (10) to be made, and the wax The decorative material (10) is filled with the gum component (20) on the surface, and the top of the candle wick (40) is exposed on the top surface of the waxy decoration (100) and the gum component (20). After the cooling is completed, a decorative wax scorpion is formed. The invention relates to a waxy decorative article, which is made of polyethylene wax (hydrogen polymer) and white wax oil in an appropriate ratio. Among them, the polyethylene wax (hydrogen polymer) And wax oil materials are mixed, heated to melt into a liquid state, and then made into a waxy decoration after cooling. The external surface of the bad decoration has a limited shape.

Page 11 593671 SE_90127402 V. Description of the invention (8) The δ-hydrogenated polymer is: "a styrene-linked polymer containing hydrogenated 2methyl 1,3 butadiene and ι, 3 butadiene" (English Chemistry (Named "styrene block polymer with 2iethyl-l, 3-butadiene and 1, 3-butadiene, hydrogenated"). The weight ratio of this polyethylene x (Polyethylene Wax): hydrogenated polymer: white wax material is about 3 ~ 6. %: 7 ~ 11%: 85 ~ 88%, at this weight ratio, its melting point and freezing point are about 80 ~ 1 70 ° C; where the Polyethylene Wax: hydrogenated polymer: white wax The preferred weight ratio is 4.5%: 9%: 86.5%. At this weight ratio, its melting point and freezing point are about 125 ° C. The waxy decoration (10) can be formed into any shape according to the shape of a preset mold. Referring to the fourth and fifth figures, the waxy decoration (10) is a lotus mist or a flower shape. . The waxy decoration (10) 'can be fixed with at least one gum component (20) and tightly covered and connected to the external surface' The melting point and freezing point of the gum component (20) are lower than the waxy decoration (10) ) ° The melting volume of the gel cyanide weight compound, and the hydrogen polymerization ratio (10)

The quality component (20) is a mixed material of hydrocyanated polymer and white wax oil. The weight ratio of polymer: white wax oil is about 7 ~ 11%: 8 9 ~ 9 3%. 7 5 ~ 1 4 0 C; wherein the preferred weight ratio of hydrogen and white gland oil is about 9%: 9 1% 'At this weight, the melting point and freezing point are about 1 20 ° C, which is lower than the waxy decoration Point and freezing point. The waxy decoration (10) and the gum component (20) are placed in a container (30). The container (30) can be transparent or non-transparent in any shape.

593671 ___ grade _ 90127402__ year, month, day and year ___ five. Description of the invention (9) The product of the present invention, such as the sixth (4 0), the top of the wick (4 0) is exposed to the component (1 0) The top surface can be used as a wax product of the present invention, and the outer surface of the gummy ornament (1 0) is intact (20) to watch the wax coated product of the present invention, which can be used on the polyethylene of the gum (1 0). Wax and hydrocyanation are natural inorganic pigments, so that the gum (10) can have any color, and the color of (10) does not penetrate each other, and the product with the original visual beauty of the present invention can be maintained. The polyethylene wax and hydrocyanated perfume in the gum (10) can naturally scent. It is sown in the countryside. The weir of the present invention has the practicality of creation and the application of the invention patent in the industrial patent law. The invention has been described in detail as a preferred embodiment of the invention. That is, where the scope of application according to the present invention should still be within the scope of the patent coverage of the present invention, it may include a candle wick for the waxy decoration (10) and the colloidal candle to ignite. The component (20) covers and protects the mask, so that the user can see through the gum component decoration (1 0). The waxy decorative polymer (20) and / or the waxy decorative polymer and white wax oil material are added with a suitable component (20) or the butterfly-like decorative substance (20) or the waxy decorative object can maintain the original design, The look of manufacture. (20) and / or the base decorative polymer and white wax oil material are suitable, and the fragrance will not dissolve in water. The manufacturing method of the decorative object and its products are worthwhile and have never been seen before. They have actually met the requirements and applied in accordance with the law and documents. Detailed explanation, but the above are only within the scope of equivalent changes and modifications made when the scope of the present invention can not be limited.

Page 13 593671 _Case No. 90127402_ Year Month Revision _ Brief description of the diagram: The first diagram is a schematic diagram of the three-dimensional appearance of the conventional case one; the second diagram is the schematic diagram of the three-dimensional appearance of the conventional case two; the third diagram is It is a flowchart of the manufacturing method of the present invention; the fourth figure is a schematic diagram of the three-dimensional appearance of the embodiment of the present invention; the fifth figure is a schematic diagram of the three-dimensional appearance of the second embodiment of the present invention; Appearance diagram; The seventh diagram is an embodiment of the manufacturing method of the present invention, and illustrates the operation of manufacturing the present invention by using a mold and a film.

Figure number description:

1 0 waxy decoration 20 gel composition 3 0 container 31 modeling mold 32 film 40 candle wick 50 gel composition 5 1 waxy decoration 5 2 pigment penetration 53 gelatinized wax

Page 14

Claims (1)

593671 Case No. 90127402 6. Scope of patent application 1. A method for manufacturing waxy decorative objects, the main steps are: (a) preparing polyethylene wax (PE Wax), hydrogenated polymer and white wax Materials; (b) melting the polyethylene wax (hydrogenated polymer) and tar wax into a liquid form and mixing them thoroughly; (c) pouring the liquid into at least one mold having a defined shape, After cooling and cooling, at least one kind of waxy decoration is made, and the outer surface of the at least one kind of creeping decoration has a defined shape; Λ (d) preparing at least one gum component, the gum component is transparent, and the faulty component Melt it into a liquid when heated; adjust the level of the liquid colloidal ingredients' so that it will not melt or surface when it comes into contact with the waxy decoration; fresh a the waxy decoration (e) so that the liquid colloidal ingredients are full and wrapped; The outer surface, but not fused with the "(g)" of the "decorative object", is cooled and cooled, so that the liquid gum is densely covered and connected to the outer surface of the waxy decorative object. The polyethylene wax in steps (a) and (b): weight ratio of hydrogenated polymer: white wax oil = (p ^ yethylene 〇 / 0. 6 / .: 7 ~ 11 〇 / 〇: 85 ~ 88 2 · The waxy product as described in item 1 of the scope of the patent application, wherein the nitrided polymer is: "Manufacturing method containing hydrogenated 2 clothing 4, butadiene styrenic polymer" (English / / ,, 3 Butylene and 丨, 3 + named "Styrene Page 15593671 _ Case No. 90127402 6. Scope of patent application block polymer with 2-methy1-1, 3-butadiene and 1,3-butadiene, hydrogenated ") ° 3 · Manufacture of waxy decoration as described in item 1 of the scope of patent application The method, wherein the melting point and freezing point of the gum component are lower than the waxy decoration. 4. The method for manufacturing a waxy decorative object as described in item 1 of the scope of application for a patent, wherein the butterfly decorative object can be formed into an arbitrary shaped body according to the shape of a preset mold. ^ 5 The method for manufacturing a waxy decorative object as described in item 1 of the scope of patent application, wherein the polyethylene soil (hydrogenated polymer) in steps (a) and (b), hydrogenated polymer: and white wax The oil mixture has a melting point and a freezing point of 80 to 1700C. "6. The method for manufacturing a waxy decoration according to item 丨 of the scope of the patent application, wherein in the steps (a) and (b) the polyethylene wax (polyol Wax): lice polymer: The preferred weight ratio of white wax oil is 4.5%: 9%: 86%. Under the reset ratio, its melting point and freezing point are 丨 2 5. / V, 嗲 n I „^ Injury is The oxidized polymer is mixed with white wax oil, and it is a glutamate polymer. The weight of white fat oil is 〇 /, which is better than the weight of Huangdinggan. The preferred weight ratio of guanidine is 9%: 91. Its melting point and freezing point are 12. . 〇, below the wax 593671 0 — Said amendment _ Case No. 90127402 __---- 6. Scope of patent application Melting point and freezing point of high-quality decorative objects. # ^ Manufacture method of W's decoration, 9 · Can as described in item 1 of the scope of patent application, wherein in step u) or (b), in the polywax, hydrogenated polymer, A suitable natural inorganic pigment is added to the white wax oil material department, so that the waxy decorative object has any one-member color II. The method for manufacturing wax-free and decorative objects as described in item 1 of the scope of patent application, wherein In step (d), an appropriate natural inorganic pigment is added to the colloidal component, so that the colloidal component has an arbitrary member color ° t < II. The method for manufacturing a wax garnish according to item g or 10 of the scope of patent application, wherein in step (a) or (b) and / or step (d), 'the polyethylene butterfly (Polyethylene Wax), hydrogenated polymer, white oil material, and / or the colloidal component, when the appropriate natural inorganic pigment is added, the colors of the decorate and / or the colloidal component do not penetrate each other. 1 2 · The method for manufacturing a waxy decorative object as described in item 1 of the scope of the patent application, wherein in step (a) or (b) and / or step (d), the polyethylene wax (Polyethylene Wax), The hydrogenated polymer, tar oil material, and / or the gum ingredients are added with appropriate fragrances, which can naturally emit fragrances, and the fragrances will not dissolve in water. , 1 3. The method for manufacturing a waxy decoration as described in item 1 of the scope of patent application, wherein in step (e), a container is provided for containing the waxy decoration. The appearance of the container is not limited, and it is transparent or Not transparent. σ = · The method for manufacturing a waxy decoration as described in item 1 of the scope of the patent application 'In the film: In step (e), a layer of a high-temperature-resistant film is laid in the -moulding mold' and the waxy decoration is placed therein , Irrigation on the surface of the waxy decoration $ ΠPage 593671 Case No. 90127402 6. Scope of patent application After cooling the gelatin component, remove it from the mold and remove the thin film. 15 · The method for manufacturing a waxy decoration as described in item 1 of the scope of patent application, wherein in step (e), a candle wick is placed beside the waxy decoration to be manufactured, and the wax is placed on the wax After the outer surface of the decorative material is coated with the gelatinous component and cooled, the top of the candle wick is exposed on the top surface of the waxy decorative material and the gelatinous component to form a decoration. 16 · The waxy decorative object manufacturing method as described in item 1 of the scope of the patent application, wherein the waxy decorative product made is a polyethylene wax (Polyethylene Wax), hydrogenated polymer and Made of white wax oil material; wherein, the polyethylene wax (Polyethylene Wax), hydrogenated polymer and white wax oil material are mixed, melted to form a liquid after heating, and then made into a waxy decoration after cooling. The outer surface has a defined shape; the weight ratio of the polyethylene wax (Polyethylene Wax): hydrogenated polymer: white wax is 3 to 6%: 7 to 11%: 85 to 88%; the hydrogenated polymer is: "contained with Styrene block polymer with 2-methyl-1,3-butadiene and 1,3-butadiene "(English name is" Styrene block polymer with 2-methyl-1, 3-butadiene and 1,3-butadiene , Hydrogenated ”). 1 7. The method for manufacturing a waxy decoration according to item 16 of the scope of application for a patent, the waxy decoration made of the product, wherein the waxy decoration is formed into a pattern according to the shape of a preset mold. body. 1 8. The manufacturer of the waxy decoration as described in item 16 of the scope of patent application Page 18 593671 _Case number 90? 7 cents? 6. The scope of patent application method, the waxy decorative products made by it, wherein the melting point and freezing point of the mixture of polyethylene wax, hydrogenated polymer and white wax oil are 80-170 ° C . 1 9 · The method for manufacturing a waxy decorative object as described in item 16 of the scope of patent application, and the waxy decorative product made thereof, wherein the polyethylene wax (Polyethylene Wax): hydrogenated polymer The preferred weight ratio of the oil is 4.5%. 9%. 86. 5%. At this weight ratio, its melting point and freezing point are 20. The fiber described in item 16 of the patent scope of Shenyan Method for manufacturing decorative objects' products made of butterfly decorative objects, wherein the earthy decorative objects are fixed with at least one gum component and tightly covered and connected to an external surface, and the melting point and freezing point of the gum component are lower than the Wax ornament. 2 1 · The method for manufacturing a waxy decorative object as described in Item 20 of the scope of the patent application, the waxy decorative product made by it, wherein the gum component is a mixed material of vaporized polymer and white wax, the Hydrogenated polymer: White wax oil has a weight ratio of 7 ~ 11%: 89 ~ 93%. At this weight ratio, its melting point and freezing point are 75 ~ 1 40 ° C, which is lower than the melting point of the waxy decoration. And freezing point. 2 2 · According to the method for manufacturing a quality decorative item described in item 21 of the scope of the patent application, the waxy decorative product made by it, wherein the preferred weight ratio of the cyanated polymer and wax oil is 9% : 91%, at this weight ratio, the freezing point is 1 20 ° C, which is lower than the melting point and solidification point 4 of the waxy decoration. ",, 23. The waxy decorative object as described in item 20 of the scope of the patent application, the waxy decorative product made by the method, wherein the wax coat & gelatinous ingredients are contained in the whole body. In the case, the face was crying, the clothes and accessories and the 1% ua were made transparent or non-transparent. Page 19 593671 SS_9〇l27402 __ ^ ___ 3--§— ^ i% if__ VI. Application for Patent Scope 2 4 · The manufacturer of waxy decorations as described in Item 20 of the scope of patent application ti Wax made by him A decorative product, wherein the waxy decoration and the capsule component include a candle wick, and the top end of the candle wick is exposed on the top surface of the waxy decoration and gum component, and is used as a candle as a whole. 25. The method for manufacturing a waxy decoration according to item 16 or 20 of the scope of application for a patent, wherein the waxy decoration is made of a product 'wherein the waxy decoration is a polyethylene butterfly (polyethylene Wax), hydrogen cyanide A suitable natural inorganic pigment is added to the polymer and the tar oil material and / or the gum component, and the colors of the waxy decorative object and the natural inorganic pigment in the gum component will not penetrate each other. 26. The method for manufacturing a waxy decoration according to item 16 or 20 of the scope of application for a patent, wherein the waxy decoration is made of a product 'wherein the waxy decoration is a polyethylene wax (Polyethylene Wax), cyanidation Appropriate fragrances can be added to the polymer and tar oil material and / or the gum component, and the fragrance will not dissolve in water. Page 20