507031 五、發明說明(1) 本發明係有關於一種複合纖維紗線之製造方法,尤其 ^ 指於内層之外部包覆一由膠料壓出成型之外層,且外層表 . 面藉由表面切割機之二組反向斜刀輪進行切割,其產生之 菱形切割痕可使紗線之外層硬度降低者。 按,習用複合纖維紗線為使成品具有適當之柔軟度, 特將包覆内層(高強度纖維)之外層(低熔點纖維),採 沾黏之方式與内層組成紗線連結〔請參閱附件一〕,但該 由長度不一之纖維組成之紗線外層,卻存在包覆内層分佈 不均、外層直徑無法同一及生產製造流程費時之缺失〔請 參閱附件一〕,其直徑不一之外層,將造成紗線以經、緯 穿梭織造之布面強度不佳者。 〇 本發明人有鑑於此,特以其參予相關產品製造生產多 年之實務經驗及其一貫秉持具有之優良設計理念,針對習 用品之外層直徑無法一致、紗線產製之布面強度不佳及生 產製造流程費時之弊端進行研究開發,期使紗線之製造充 γ 份符合產業利用性者。 ’ 本發明之主要目的,在提供一種可使紗線之生產製造 · 效率提昇且增進紗線產製的布面強度之「複合纖維紗線之 製造方法」,其於内層外部包覆一採壓出方式成型之外層 ,且外層表面藉由表面切割機之二組反向斜刀輪進行切割 ,其產生之菱形割痕可使紗線之外層硬度降低者。 φ 本發明另一主要目的,在提供一種製造流程可以縮短 產製時間進而節省生產成本之「複合纖維紗線之製造方法 」,其採壓出方式成型之外層具有外徑處處同一及包覆内507031 V. Description of the invention (1) The present invention relates to a method for manufacturing a composite fiber yarn, especially ^ refers to an outer layer covered with an outer layer extruded from a rubber compound, and the outer layer surface. The surface is cut by the surface The two sets of reverse inclined knife wheels of the machine are used for cutting, and the diamond-shaped cutting marks generated by it can reduce the hardness of the outer layer of the yarn. According to the conventional composite fiber yarn, in order to make the finished product have appropriate softness, the inner layer (high-strength fiber) is covered with the outer layer (low-melting fiber), which is connected to the inner layer to form a yarn (see attachment 1) 】 However, the outer layer of the yarn composed of fibers of different lengths has the disadvantages of uneven distribution of the inner layer of the coating, different outer layer diameters, and time-consuming manufacturing processes [see Annex 1]. The outer layers of different diameters, Will cause the yarn to weave the warp and weft of the fabric strength is not good. 〇In view of this, the inventor especially uses his many years of practical experience in participating in the production and production of related products and has always adhered to the excellent design concept. The diameter of the outer layer of the custom product cannot be consistent, and the fabric strength of the yarn is not good. And the research and development of the time-consuming disadvantages of the production and manufacturing process, in order to make the production of yarn γ content in line with industrial applicability. '' The main object of the present invention is to provide a "composite fiber yarn manufacturing method" which can improve the production and efficiency of yarn production and increase the fabric strength of the yarn production. The outer layer is formed out of the way, and the surface of the outer layer is cut by two sets of reverse slash cutter wheels on the surface cutter. The diamond-shaped cuts produced by it can reduce the hardness of the outer layer of the yarn. φ Another main object of the present invention is to provide a "composite fiber yarn manufacturing method" which can shorten the production time and save the production cost. Its production method is the same as the outer layer with the outer diameter and the inside of the coating.
第4頁 507031 五、發明說明(2) 層之程序快速之產業利用性,係為符合發明要件之紗線製 造方法者。 本發明複 依序為原絲絡 D、二次冷卻 原絲絡集 絡為條束狀之 壓出包覆 方式包覆於内 第二 複合 請參 進行 痕( (1 軸捲 (1 )因 梭織 圖 次 纖維 切割 閱第 切割13 二次 )再 捲取 取者 本發 2 ) 材質 造成 冷卻 紗線 D : 三圖 ,致 )者 冷卻 次送 F : 〇 明製 接近 產生 布面 合纖維 集成束 E及捲 成束A 内層( B :將 層(1 C :將 (1 ) 利用表 〕,對 使外層 〔請參 E :將 入冷卻 製造完 造生產 於菱形 之硬度 時,可 紗線之製造流程〔請參閱第一圖〕, A、壓出包覆B 、一次冷卻C 、切割 取F所共同完成;其中: :將多數高強度纖維原絲或者紗線,11); 預熱完成之低熔點纖維採壓出成型之 1 )外部成為外層(1 2 )〔請參閱 具有内層(11)與外層(12)之 送入冷卻槽中進行降溫程序; 面切割機之二組反向斜刀輪(2 )〔 複合纖維紗線(1 )之外層(1 2 ) (1 2 )表面產生菱形(◊形)切割 閱第四圖〕, 具有切割痕(1 3 )之複合纖維紗線 槽中進行降溫程序; 成之複合纖維紗線(1 )成品,以線 之複合纖維紗線(1 ),可藉由外層 之切割痕(1 3 ),降低外層(1 2 •,當複合纖維紗線(1 )以經、緯穿 針對布面加熱致使線之經、緯交錯結Page 4 507031 V. Description of the invention (2) The fast industrial applicability of the procedure is for the yarn manufacturing method that meets the requirements of the invention. In the present invention, the original filament network D and the secondary cooling original filament network are arranged in a stripe-shaped extrusion coating method. The second compound is covered with a trace ((1 shaft roll (1) due to shuttle Weaving pattern, the fiber is cut and read 13 times, the second time) the rewinder's hair 2) the material causes the cooling yarn D: three pictures, the) the person who cools down and sends F: 〇 the Ming system is close to produce the cloth surface fiber integrated bundle E and coiled bundle A. Inner layer (B: layer (1 C: (1) using table), and outer layer [see E: When finished in cooling and manufactured in rhombic hardness, yarn can be manufactured. The process [please refer to the first figure], A, pressing and covering B, cooling once, and cutting F are completed together; of which: most high-strength fiber strands or yarns, 11); low preheating completion The melting point fiber is produced by pressing and pressing. 1) The outer layer becomes the outer layer (1 2). [Refer to the cooling tank with the inner layer (11) and the outer layer (12) for the cooling process. (2) [The outer layer of the composite fiber yarn (1) (1 2) (1 2) produces a diamond shape (◊ shape) (See the fourth figure), the cooling process is performed in the composite fiber yarn groove with cutting marks (1 3); the finished composite fiber yarn (1) is finished, and the composite fiber yarn (1) is threaded. The cut marks on the outer layer (1 3), lower the outer layer (1 2 •, when the composite fiber yarn (1) is heated by warp and weft through the cloth surface, the warp and weft of the thread are intertwined.
第5頁 507031 五、發明說明(3) 點,因線之外層(1 2 )熔合(化學變化)而增進布面結 構強度者;由本發明複合纖維紗線(1 )織造之布面,極 適合建築工程内胚及砂土攔阻工程使用者。 本發明採壓出成型方式於内層(1 1 )外部包覆之塑 料外層(1 2 ),俾以產製複合纖維紗線(1 )之方法, 可改善習用複合纖維紗線之外層,因低熔點纖維包覆内層 之分佈不均〔請參閱附件一〕,造成外層之直徑無法同一 ,致使紗線以經、緯穿梭織造之布面強度不佳者。 綜上所述,本發明實施例確能達到所預期之產品價值 ,又其所揭露之具體構造,不僅未曾見諸於同類產品中, 亦未曾公開於申請前,誠已完全符合發明專利法之規定與 要求,爰依法提出發明專利之申請,懇請惠予審查,並早 曰賜准專利,則實感德便。 附件一:習用複合纖維紗線外層直徑不一之實物樣品Page 5 507031 V. Description of the invention (3) Point, because the outer layer (12) of the thread is fused (chemically changed) to increase the strength of the structure of the cloth surface; the cloth surface woven by the composite fiber yarn (1) of the present invention is extremely suitable End users of construction works and sand retaining works. The present invention adopts a pressure-extrusion molding method to cover a plastic outer layer (1 2) on the inner layer (1 1) and use a method for producing a composite fiber yarn (1), which can improve the outer layer of a conventional composite fiber yarn because of low The distribution of the inner layer covered by the melting point fiber is uneven [see Annex I], which causes the outer layer diameters to be different, which results in poor yarn strength of the fabric woven by warp and weft shuttles. In summary, the embodiments of the present invention can indeed achieve the expected product value, and the specific structure disclosed has not only been found in similar products, nor has it been disclosed before the application. It has fully complied with the invention patent law. Regulations and requirements, applying for an invention patent in accordance with the law, and begging for approval, and granting the patent as early as possible, it is a matter of convenience. Attachment 1: Samples of different outer diameters of conventional composite fiber yarns
第6頁 507031 圖式簡單說明 第一圖:本發明複合纖維紗線之製造流程圖 第二圖:本發明複合纖維紗線之剖視圖 第三圖:本發明複合纖維紗線之外層切割示意圖 第四圖:本發明複合纖維紗線之外觀圖 本創作圖中參照號數: 1 複合纖維紗線 12 外層 2 斜刀輪 内層 切割痕Page 6 507031 Brief description of the drawings First diagram: The manufacturing flowchart of the composite fiber yarn of the present invention Second diagram: The sectional view of the composite fiber yarn of the present invention Third diagram: The schematic diagram of the outer layer cutting of the composite fiber yarn of the present invention Fourth Figure: Appearance of the composite fiber yarn of the present invention Reference numbers in the creative drawing: 1 Composite fiber yarn 12 Outer layer 2 Inner layer cutting marks on the inclined knife wheel
第7頁Page 7