TW332195B - Manufacturing method of ceramic face brick from recycled aluminum slag - Google Patents
Manufacturing method of ceramic face brick from recycled aluminum slagInfo
- Publication number
- TW332195B TW332195B TW083108981A TW83108981A TW332195B TW 332195 B TW332195 B TW 332195B TW 083108981 A TW083108981 A TW 083108981A TW 83108981 A TW83108981 A TW 83108981A TW 332195 B TW332195 B TW 332195B
- Authority
- TW
- Taiwan
- Prior art keywords
- aluminum
- pulp
- face brick
- slag
- recycled
- Prior art date
Abstract
A kind of manufacturing method of ceramic face brick from recycled aluminum slag which uses the aluminum slag from stabilizing procedures to produce the face brick, the steps include: a. mix the recycled aluminum slag with water and comminute to isolate the aluminum particles from non-metal material b. proceed the wet vibration process to bolt the coarse-grained with high aluminum density from fine particles with low aluminum density; the coarse-grained is recycled for aluminum production c. adjust the solid/liquid ratio for fine aluminum slag particles and water between 1:1 to 1:5, and proceed the heating and agitation for stabilization so that the active components, such as the aluminum, aluminum nitride and aluminum carbide, within the pulp can be hydrolyzed and erased. The temperature of aluminum pulp is kept at 80 to 100 degree in Celsius and proceeds the heating and agitation simultaneously for 12 to 48 hours d. after the stabilization, the aluminum pulp is proceeded the gravitating process to get rid of the chloride of clarified water layer. e. the stabilized aluminum pulp after step 4 is mixed with fixed ratio, 50%-90% for stabilized pulp and 10%-50% plasticizer and 0%-30% solutizer ; f. use the mixture for the forming process g. the burning process is at the temperature from 1100 to 1300 degrees in Celsius and the ceramic face brick is produced with hydrophilic rate greater than 6%.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
TW083108981A TW332195B (en) | 1994-09-29 | 1994-09-29 | Manufacturing method of ceramic face brick from recycled aluminum slag |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
TW083108981A TW332195B (en) | 1994-09-29 | 1994-09-29 | Manufacturing method of ceramic face brick from recycled aluminum slag |
Publications (1)
Publication Number | Publication Date |
---|---|
TW332195B true TW332195B (en) | 1998-05-21 |
Family
ID=58262737
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
TW083108981A TW332195B (en) | 1994-09-29 | 1994-09-29 | Manufacturing method of ceramic face brick from recycled aluminum slag |
Country Status (1)
Country | Link |
---|---|
TW (1) | TW332195B (en) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
TWI473671B (en) * | 2012-08-08 | 2015-02-21 | Sing Uang Environmental Co Ltd | A waste disposal methods of the renewable energy |
CN109678556A (en) * | 2019-02-26 | 2019-04-26 | 东北大学 | A method of light weight alumina insulating brick is prepared using aluminium ash |
-
1994
- 1994-09-29 TW TW083108981A patent/TW332195B/en not_active IP Right Cessation
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
TWI473671B (en) * | 2012-08-08 | 2015-02-21 | Sing Uang Environmental Co Ltd | A waste disposal methods of the renewable energy |
CN109678556A (en) * | 2019-02-26 | 2019-04-26 | 东北大学 | A method of light weight alumina insulating brick is prepared using aluminium ash |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
Cohen et al. | Mechanism of plastic shrinkage cracking in portland cement and portland cement-silica fume paste and mortar | |
US4529575A (en) | Process for producing ultrafine silicon carbide powder | |
JPH10507992A (en) | Method for preparing pazolanic material from paper residue and method for producing cement from pazolanic material | |
US4563432A (en) | Production of porous sintered ceramic material | |
JP2004131378A (en) | Process for manufacturing opaque quartz glass material | |
US4152281A (en) | Molten salt synthesis of lead zirconate titanate solid solution powder | |
Cano et al. | Effect of Dilution and Porosity on Self‐Propagating High‐Temperature Synthesis of Silicon Nitride | |
CA1313583C (en) | Process of producing plate-shaped calcium carbonate particles | |
BE904789A (en) | PROCESS FOR THE MANUFACTURE OF SILICON OR FERROSILICIUM IN AN ELECTRIC LOW TANK OVEN AND AGGLOMERATED FOR THIS PROCESS. | |
US4224073A (en) | Active silicon carbide powder containing a boron component and process for producing the same | |
CN106045558A (en) | Aerated concrete block preparation method | |
TW332195B (en) | Manufacturing method of ceramic face brick from recycled aluminum slag | |
FR2637906A1 (en) | PROCESS FOR THE PRODUCTION OF PENCIL MINES | |
JPH0151468B2 (en) | ||
JP2000226242A (en) | Production of lightweight aggregate for highly strong concrete | |
JPH06305854A (en) | Lightweight molded article of calcium silicate | |
US2209754A (en) | Self-set magnesium carbonate composition and method of effecting setting thereof | |
CN85108486A (en) | The production method of light fire brick | |
JP2001302238A (en) | Method for producing spindle-shaped calcium carbonate having small particle diameter | |
US4133693A (en) | Process for producing cement | |
RU2220928C1 (en) | Raw meal and a method for manufacturing granulated heat-insulation material | |
SU1231028A1 (en) | Method of producing granular heat-insulating material | |
US730778A (en) | Manufacture of tiles, slabs, or the like. | |
JP2002274902A (en) | Artificial lightweight aggregate | |
Gara et al. | Recipe-technological features of carbonization hardening of lightweight concrete |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
MM4A | Annulment or lapse of patent due to non-payment of fees |