TW202342644A - 矽橡膠黏土組合及成型體的製作方法 - Google Patents
矽橡膠黏土組合及成型體的製作方法 Download PDFInfo
- Publication number
- TW202342644A TW202342644A TW111116096A TW111116096A TW202342644A TW 202342644 A TW202342644 A TW 202342644A TW 111116096 A TW111116096 A TW 111116096A TW 111116096 A TW111116096 A TW 111116096A TW 202342644 A TW202342644 A TW 202342644A
- Authority
- TW
- Taiwan
- Prior art keywords
- silicone rubber
- essential oil
- component
- weight
- composition
- Prior art date
Abstract
一種矽橡膠黏土組合及成型體的製作方法，此矽橡膠黏土組合包含彼此分開儲存的第一組成物和第二組成物，第一組成物是由甲基乙烯基矽橡膠、乙烯基矽橡膠生膠、抗坍劑和白金催化劑所組成，第二組成物是由甲基乙烯基矽橡膠、乙烯基矽橡膠生膠、含氫聚矽氧烷以及可選的抗坍劑、顏料和芳香精油所組成，第一組成物和第二組成物本身可被重複捏塑，並可利用混合方式來製作定型之作品，作品在塑型後只要在常溫靜置一段時間即可完成固化得到矽橡膠黏土成型體，此矽橡膠黏土成型體仍保有材料的彈性，不易毀壞，易於永久保存。
Description
本發明係有關一種矽橡膠黏土材料，特別是指一種矽橡膠黏土組合及成型體的製作方法。
黏土因為材料的可塑性及價格便宜、容易取得的優點，是極受歡迎的創作媒材之一。市面上的黏土種類眾多，常見有超輕土、樹脂黏土、紙黏土、油土及兒童專用的安全黏土等等，而每一種黏土具有不同的特性，呈現出的效果也不盡相同，選擇上可根據使用需求及價格差異而定。
其中，超輕土的質感輕柔，延展性非常好，色彩也很鮮豔，其乾燥後不像樹脂黏土般堅硬，因為它的密度低且具有彈性，就算掉在地上也不易摔壞；但超輕土在使用上很容易沾手，製作動作要快，否則容易乾燥，而且一旦沾黏在其他物品或衣服上就很難清理，不適合重複捏玩使用。樹脂黏土的顏色相當多樣，韌性強，可塑性高且材質細緻，作品風乾後會呈透明感。樹脂黏土容易保存，可長期收藏也不會損壞，其延展性好，乾了之後質地硬，又不會像輕質土那樣容易黏手，可是樹脂黏土的土質容易乾燥，乾燥後則很難恢復軟度，其成品較重且容易龜裂，而且樹脂黏土主要是由澱粉和樹脂製成，易被蟲啃蝕，放在太潮濕的地方可能會發臭、發霉。紙黏土是由紙漿、石粉、樹脂等素材組成，由於紙黏土的纖維較粗，容易塑型，半乾燥後只需用水搓揉即可恢復軟度；然而，紙黏土的土質硬，易黏手，乾燥後容易有龜裂現象，也較難保存。另外，油土不會乾，但較為油膩，材質硬， 不容易塑型。而強調天然無毒的兒童用安全黏土通常成分包含麵粉、水及食用色素，其缺點為容易乾掉，塑型力差、容易散開，同時也較為沾手或沾黏其他物品，故不易清潔，善後比較麻煩，而且其保存期限短，容易有臭味。
故，如何對於黏土材料及其製作方法進行改良，以解決上述習知技術的不足，即為從事此行業相關業者所亟欲研發的課題。
有鑑於此，本發明的主要目的在於提供一種矽橡膠黏土組合及成型體的製作方法，此矽橡膠黏土組合包含彼此分開儲存的第一組成物和第二組成物，這兩種組成物本身可被重複捏塑，且進一步可直接混合來製作定型作品，作品在塑形後只要於常溫靜置一段時間即可完成固化，且仍保有材料的彈性，因而不易毀壞，容易保存。
本發明的另一目的在於提供一種矽橡膠黏土組合及成型體的製作方法，此矽橡膠黏土組合包含有彼此分開儲存的第一組成物和第二組成物，兩種組成物皆以甲基乙烯基矽橡膠和乙烯基矽橡膠生膠為主要原料，可達到操作不沾手、不掉屑、可重複捏塑等特性，且兩種組成物在混合為矽橡膠黏土組成物後才會產生固化反應來製作為矽橡膠黏土成型體，因而可根據需求選擇使產品可重複塑型或製作定型作品，使用上操作容易，更沒有惱人的善後及保存問題。
為達上述之目的，本發明提供一種矽橡膠黏土組合，其包含第一組成物和第二組成物。其中，第一組成物是由69-75重量%的甲基乙烯基矽橡膠、3-3.5重量%的乙烯基矽橡膠生膠、8-9重量%的抗坍劑和13-20重量%的白金催化劑所組成。第二組成物是由82-96重量%的甲基乙烯基矽橡膠、3.3-4.2重量%的乙烯基矽橡膠生膠、0-10重量%的抗坍劑、0.1-0.3重量%的含氫聚矽氧烷、0-5重量%的顏料和0-0.6重量%的芳香精油所組成。第一組成物和第二組成物彼此分開儲存，並容許第一組成物和第二組成物混合為一矽橡膠黏土組成物，此矽橡膠黏土組成物可於常溫下產生固化反應。
本發明也提供一種矽橡膠黏土成型體的製作方法，其步驟是先將69-75重量%的甲基乙烯基矽橡膠、3-3.5重量%的乙烯基矽橡膠生膠、8-9重量%的抗坍劑和13-20重量%的白金催化劑混合後形成第一組成物，再將82-96重量%的甲基乙烯基矽橡膠、3.3-4.2重量%的乙烯基矽橡膠生膠、0-10重量%的抗坍劑、0.1-0.3重量%的含氫聚矽氧烷、0-5重量%的顏料和0-0.6重量%的芳香精油混合後形成第二組成物，之後，將第一組成物和第二組成物彼此分開儲存，然後，將第一組成物和該第二組成物混合為矽橡膠黏土組成物，將矽橡膠黏土組成物捏塑成為預定成型之形狀，並置於常溫下產生固化反應，而得到矽橡膠黏土成型體。
根據本發明之實施例，前述第一組成物和第二組成物是以1：10的重量份比例存在，並容許第一組成物和第二組成物以1：10的重量份比例混合後於常溫下24小時固化成型。
根據本發明之實施例，前述抗坍劑為蓖麻油衍生物。
根據本發明之實施例，前述顏料包括無機顏料或有機顏料，該無機顏料為鎘紅、鎘檸檬黃、橘鎘黃、二氧化鈦、碳黑、黑色氧化鐵或黑色錯合無機顏料，該有機顏料為苯胺黑、苝黑、蒽醌黑、聯苯胺類黃色顏料、酞青藍或酞青綠。
根據本發明之實施例，前述芳香精油為香茅精油、樟腦精油、迷迭香精油、薰衣草精油、檜木精油、玫瑰精油、茉莉花精油、薄荷精油、茶樹精油、柑橘精油、檸檬草精油、鼠尾草精油、尤加利精油、葡萄柚精油、肉桂精油、檸檬草精油或是由上述物質所組成的混合物。
與先前技術相比，本發明具有以下優勢：
（1） 本發明提供的矽橡膠黏土組合可以方便使用者可以重複捏塑，不會有容易乾燥的情形，也不會產生臭味及發生掉屑、沾黏，易於清理及善後。
（2） 當使用者有定型需求時，本發明提供的矽橡膠黏土組合可以藉由混合在一起，即可使作品硬化定型但仍保有彈性，不會容易摔壞，而可方便永久保存。
（3） 本發明提供的矽橡膠黏土組合的組成和製作方法相當簡易、安全，能夠有效推廣至大眾成為理想的黏土材料。
底下藉由具體實施例詳加說明，當更容易瞭解本發明之目的、技術內容、特點及其所達成之功效。
下面結合具體實施例對本發明進行詳細說明，將有助於本發明所屬技術領域中具有通常知識者進一步理解本發明。
本發明中的實施例所採用的技術方案均僅作為示例，除非特別說明，不應用以限制本發明。在不衝突的情況下，本發明中的實施例及實施例中的特徵可以相互任意組合。除非特別說明，本發明使用的所有技術和科學術語具有與本發明所屬領域中具有通常知識者通常理解的相同含義。除非特別說明，本發明所列出的數值範圍值在包括範圍的端點，和該範圍之內的所有整數和分數。
本發明提供一種矽橡膠黏土組合，其包含有第一組成物和第二組成物。第一組成物和第二組成物彼此分開儲存，且第一組成物和第二組成物各自可供捏塑為任意形狀之作品，同時，第一組成物和第二組成物可兩者直接混合得到矽橡膠黏土組成物，此矽橡膠黏土組成物可於常溫下產生固化反應，以得到可永久保存之定型作品，也就是矽橡膠黏土成型體。
請參照第1圖，為本發明所提供的矽橡膠黏土組合中第一組成物的組成結構示意圖。本發明所提供的矽橡膠黏土組合中，以第一組成物的總重為基準，第一組成物是由以下成分所混合而得： 69-75重量%的甲基乙烯基矽橡膠；3-3.5重量%的乙烯基矽橡膠生膠；8-9重量%的抗坍劑；及13-20重量%的白金催化劑。
請參照第2圖，為本發明所提供的矽橡膠黏土組合中第二組成物的組成結構示意圖。本發明所提供的矽橡膠黏土組合中，以第二組成物的總重為基準，第二組成物是由以下成分所混合而得： 82-96重量%的甲基乙烯基矽橡膠；3.3-4.2重量%的乙烯基矽橡膠生膠；0-10重量%的抗坍劑；0.1-0.3重量%的含氫聚矽氧烷；0-5重量%的顏料；及0-0.6重量%的芳香精油。
第1、2圖中以重量百分比簡單表示，且圖中各成份所占面積比例並非實際比例。
本發明所使用的第一組成物和第二組成物皆具有不容易乾燥之特性，可供使用者重複捏塑，同時，這兩種組成物的配方簡單、安全，無臭無味，也不會發生掉屑、沾黏等情況，非常容易清理及方便善後，在混合為矽橡膠黏土組成物後只要靜置於常溫下即可進行固化，且固化後得到的矽橡膠黏土成型體仍保有彈性，不容易摔毀，可永久保存。
本發明所使用的第一組成物和第二組成物的比例不予以限制，而第一組成物所佔比例越高，則第一組成物和第二組成物混合為矽橡膠黏土組成物後會定型及固化得越快，可根據使用者需求來調整。為了提高作品的固化速度，第一組成物的用量可至少為第二組成物的十分之一，在第一組成物和第二組成物以1：10的重量份比例存在時，則第一組成物和第二組成物混合為矽橡膠黏土組成物後進行捏塑的作品可於常溫下24小時內固化成型。
本發明所使用的第一組成物和第二組成物中，適用於本發明的抗坍劑可以包括但不限於：蓖麻油衍生物，適用於本發明的顏料可為無機顏料或有機顏料，其中無機顏料可以包括但不限於：鎘紅、鎘檸檬黃、橘鎘黃、二氧化鈦、碳黑、黑色氧化鐵或黑色錯合無機顏料，有機顏料可以包括但不限於：苯胺黑、苝黑、蒽醌黑、聯苯胺類黃色顏料、酞青藍或酞青綠，芳香精油可以包括但不限於：香茅精油、樟腦精油、迷迭香精油、薰衣草精油、檜木精油、玫瑰精油、茉莉花精油、薄荷精油、茶樹精油、柑橘精油、檸檬草精油、鼠尾草精油、尤加利精油、葡萄柚精油、肉桂精油、檸檬草精油或是由上述物質所組成的混合物。上述所列舉之材料皆僅作為示例，實務上不限於此。
另外要說明的是，本發明所使用的抗坍劑、顏料和芳香精油的含量可以為0重量％，這表示在本發明的第一組成物和第二組成物的配方中也可以不包含抗坍劑、顏料或芳香精油。
以下請參照第3圖，詳細說明本發明所提供的矽橡膠黏土成型體的製作方法之流程步驟。
首先，如步驟S100，提供如前述第1圖之組成比例的第一組成物，其由69-75重量%的甲基乙烯基矽橡膠、3-3.5重量%的乙烯基矽橡膠生膠、8-9重量%的抗坍劑和13-20重量%的白金催化劑所混合而成。
然後，如步驟S110，提供如前述第2圖之組成比例的第二組成物，其由82-96重量%的甲基乙烯基矽橡膠、3.3-4.2重量%的乙烯基矽橡膠生膠、0-10重量%的抗坍劑、0.1-0.3重量%的含氫聚矽氧烷、0-5重量%的顏料和0-0.6重量%的芳香精油所混合而成。
如步驟S120，將第一組成物和第二組成物彼此分開儲存，這兩種組成物具有可塑性和彈性，不容易乾燥，不易沾手，使用者可以隨心所欲的用它來捏塑成任意形狀，亦可利用模具製成單一形狀的作品。
後續，若有成型需求，如步驟S130，再將第一組成物和第二組成物混合成為矽橡膠黏土組成物，再予以捏塑成為預定成型之形狀，並置於常溫下產生固化反應得到矽橡膠黏土成型體，此矽橡膠黏土成型體固化成型後仍保有彈性。
以下結合具體實施例對本發明作進一步詳細說明，但不應將其理解為對本發明保護範圍的限制。本發明實施例1〜3所提供之矽橡膠黏土組合中，第一組成物的具體組成列示於表一，第二組成物的具體組成列示於表二，表格中的單位為重量份。
表一
| 第一組成物的 組成成分 | 實施例1 | 實施例2 | 實施例3 |
| 甲基乙烯基矽橡膠 | 86 | 86 | 86 |
| 乙烯基矽橡膠生膠 | 4 | 4 | 4 |
| 抗坍劑 | 10 | 10 | 10 |
| 含氫聚矽氧烷 | 18 | 22 | 22 |
| 總重 | 118 | 120 | 122 |
表二
| 第二組成物的 組成成分 | 實施例1 | 實施例2 | 實施例3 |
| 甲基乙烯基矽橡膠 | 96 | 96 | 96 |
| 乙烯基矽橡膠生膠 | 4 | 4 | 4 |
| 抗坍劑 | 10 | 10 | 10 |
| 含氫聚矽氧烷 | 0.2 | 0.2 | 0.2 |
| 顏料 | 1 | 1 | 1 |
| 芳香精油 | 0 | 0 | 1 |
| 總重 | 111.2 | 111.2 | 112.2 |
在表二中，實施例1的顏料為二氧化鈦，實施例2的顏料為竹炭，實施例3的顏料為竹炭，並使用薄荷精油，且實施例1-3所使用的抗坍劑皆為蓖麻油衍生物。由上述可知，實施例1的第一組成物為透明無色，第二組成物為白色；實施例2的第一組成物為透明無色，第二組成物為黑色；實施例3的第一組成物為透明無色，第二組成物為黑色且具有薄荷香味。上述的第一組成物和第二組成物可以分開儲存起來，第一組成物和第二組成物本身都具有可塑性，可以被捏塑為任意形狀的作品，且可以重複使用；當製作定型作品時，只要將第一組成物和第二組成物以適當比例充分混合為矽橡膠黏土組成物，其中，實施例1的第一組成物和第二組成物混合後可獲得白色的矽橡膠黏土組成物，實施例2的第一組成物和第二組成物混合後可獲得黑色的矽橡膠黏土組成物，實施例3的第一組成物和第二組成物混合後可獲得黑色且具有薄荷香味的矽橡膠黏土組成物，使用者可將矽橡膠黏土組成物捏製成具有預定成型形狀之作品，此作品可於室溫一段時間固化成型後得到矽橡膠黏土成型體，以便於永久保存。
另一方面，上述實施例1-3的第一組成物和第二組成物可以任意組合方式以及任意比例來混合為矽橡膠黏土組成物，也就是說，實施例1的第一組成物可以分別和實施例2、3的第二組成物來混合，實施例2的第一組成物可以分別和實施例1、3的第二組成物來混合，實施例3的第一組成物可以分別和實施例1、3的第二組成物來混合；且第一組成物和第二組成物的搭配方式不限於此，具體而言，以固定使用透明無色的第一組成物為例，其可混入以各式顏料添加所形成之白色、黑色、紅色、藍色等各種顏色的一種或多種第二組成物，或者，可混入以各式芳香精油所形成之具有薄荷、綠茶、薰衣草等各種香味的一種或多種第二組成物，或者，可混入以各式顏料及各式芳香精油所形成之具有各種顏色和香味的一種或多種第二組成物。至於混合比例，全部的第一組成物的用量可至少為全部的第二組成物的十分之一為較佳，以提高作品的固化速度；在全部的第一組成物和全部的第二組成物以1：10的重量份比例存在時，則第一組成物和第二組成物混合為矽橡膠黏土組成物後進行捏塑的作品可於常溫下24小時內固化成型，而第一組成物所佔比例越高，則第一組成物和第二組成物混合為矽橡膠黏土組成物後會定型及固化得越快。
根據本發明所提供的矽橡膠黏土組合，藉由在第一組成物和第二組成物中以甲基乙烯基矽橡膠和乙烯基矽橡膠生膠作為基底原料，分別添加白金催化劑和含氫聚矽氧烷之交聯劑，並可於實務上搭配抗坍劑、顏料和芳香精油，使黏土的成份除了無臭無味之外，更是非常環保安全。再者，有別於習知黏土材料的缺點，比如容易乾燥、沾黏，而不利重複塑型，或是容易發臭、發霉，乾燥後容易龜裂，而難以保存，不易清潔及善後等等；本發明所提供的矽橡膠黏土組合的優勢在於，使第一組成物和第二組成物直到混合為矽橡膠黏土組成物後才會產生固化，而第一組成物和第二組成物本身具有不容易乾之特性，可重複捏塑，同時不會發出臭味，且使用上不易掉屑、不易沾手，更由於不會沾黏衣物或地板，相當容易清潔，也沒有惱人的善後問題，而矽橡膠黏土組成物固化後的矽橡膠黏土成型體仍具有彈性，不易龜裂或摔壞，有利於長期保存。
總的來說，本發明的矽橡膠黏土組合及成型體的製作方法，可以相當程度地提昇黏土的使用特性，方便使用者可以重複捏塑，不會有容易乾燥、掉屑及沾黏等問題，同時也易於清理、善後及保存。而當使用者有定型需求時，可以藉由將第一組成物和第二組成物以適當比例充分混合的簡單方式，即可使作品硬化定型但仍保有彈性，其組成及製作方法皆相當簡易、安全，能夠有效地推廣至大眾成為理想的黏土材料。
唯以上所述者，僅為本發明之較佳實施例而已，並非用來限定本發明實施之範圍。故即凡依本發明申請範圍所述之特徵及精神所為之均等變化或修飾，均應包括於本發明之申請專利範圍內。
無
第1圖為本發明所提供的矽橡膠黏土組合中第一組成物的組成結構示意圖。
第2圖為本發明所提供的矽橡膠黏土組合中第二組成物的組成結構示意圖。
第3圖為本發明所提供的矽橡膠黏土成型體的製作方法的流程圖。
Claims (10)
- 一種矽橡膠黏土組合，包含： 一第一組成物，該第一組成物係由69-75重量%的甲基乙烯基矽橡膠、3-3.5重量%的乙烯基矽橡膠生膠、8-9重量%的抗坍劑和13-20重量%的白金催化劑所組成；以及 一第二組成物，該第二組成物係由82-96重量%的甲基乙烯基矽橡膠、3.3-4.2重量%的乙烯基矽橡膠生膠、0-10重量%的抗坍劑、0.1-0.3重量%的含氫聚矽氧烷、0-5重量%的顏料和0-0.6重量%的芳香精油所組成； 其中，該第一組成物和該第二組成物彼此分開儲存，並容許該第一組成物和該第二組成物混合為一矽橡膠黏土組成物，此矽橡膠黏土組成物可於常溫下產生固化反應。
- 如請求項1所述之矽橡膠黏土組合，其中該第一組成物和該第二組成物以1：10的重量份比例存在，並容許該第一組成物和該第二組成物以1：10的重量份比例混合後所得到的該矽橡膠黏土組成物可於常溫下24小時固化成型。
- 如請求項1所述之矽橡膠黏土組合，其中該抗坍劑為蓖麻油衍生物。
- 如請求項1所述之矽橡膠黏土組合，其中該顏料包括無機顏料或有機顏料，該無機顏料為鎘紅、鎘檸檬黃、橘鎘黃、二氧化鈦、碳黑、黑色氧化鐵或黑色錯合無機顏料，該有機顏料為苯胺黑、苝黑、蒽醌黑、聯苯胺類黃色顏料、酞青藍或酞青綠。
- 如請求項1所述之矽橡膠黏土組合，其中該芳香精油為香茅精油、樟腦精油、迷迭香精油、薰衣草精油、檜木精油、玫瑰精油、茉莉花精油、薄荷精油、茶樹精油、柑橘精油、檸檬草精油、鼠尾草精油、尤加利精油、葡萄柚精油、肉桂精油、檸檬草精油或是由上述物質所組成的混合物。
- 一種矽橡膠黏土成型體的製作方法，包含下列步驟： 1） 將69-75重量%的甲基乙烯基矽橡膠、3-3.5重量%的乙烯基矽橡膠生膠、8-9重量%的抗坍劑和13-20重量%的白金催化劑混合後形成一第一組成物 ； 2） 將82-96重量%的甲基乙烯基矽橡膠、3.3-4.2重量%的乙烯基矽橡膠生膠、0-10重量%的抗坍劑、0.1-0.3重量%的含氫聚矽氧烷、0-5重量%的顏料和0-0.6重量%的芳香精油混合後形成一第二組成物； 3） 將該第一組成物和該第二組成物彼此分開儲存；以及 4） 將該第一組成物和該第二組成物混合為一矽橡膠黏土組成物，將該矽橡膠黏土組成物捏塑成為預定成型之形狀，並置於常溫下產生固化反應，而得到一矽橡膠黏土成型體。
- 如請求項6所述之矽橡膠黏土成型體的製作方法，其中該第一組成物和該第二組成物是以1：10的重量份比例混合並置於常溫下24小時固化成型。
- 如請求項6所述之矽橡膠黏土成型體的製作方法，其中該抗坍劑為蓖麻油衍生物。
- 如請求項6所述之矽橡膠黏土成型體的製作方法，其中該顏料包括無機顏料或有機顏料，該無機顏料為鎘紅、鎘檸檬黃、橘鎘黃、二氧化鈦、碳黑、黑色氧化鐵或黑色錯合無機顏料，該有機顏料為苯胺黑、苝黑、蒽醌黑、聯苯胺類黃色顏料、酞青藍或酞青綠。
- 如請求項6所述之矽橡膠黏土成型體的製作方法，其中該芳香精油為香茅精油、樟腦精油、迷迭香精油、薰衣草精油、檜木精油、玫瑰精油、茉莉花精油、薄荷精油、茶樹精油、柑橘精油、檸檬草精油、鼠尾草精油、尤加利精油、葡萄柚精油、肉桂精油、檸檬草精油或是由上述物質所組成的混合物。