TW202007718A - 植物纖維發泡板結構及其製造方法 - Google Patents

植物纖維發泡板結構及其製造方法 Download PDF

Info

Publication number
TW202007718A
TW202007718A TW107126776A TW107126776A TW202007718A TW 202007718 A TW202007718 A TW 202007718A TW 107126776 A TW107126776 A TW 107126776A TW 107126776 A TW107126776 A TW 107126776A TW 202007718 A TW202007718 A TW 202007718A
Authority
TW
Taiwan
Prior art keywords
plant fiber
patent application
board structure
item
application scope
Prior art date
Application number
TW107126776A
Other languages
English (en)
Inventor
高智暉
Original Assignee
欣瑤企業股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 欣瑤企業股份有限公司 filed Critical 欣瑤企業股份有限公司
Priority to TW107126776A priority Critical patent/TW202007718A/zh
Priority to US16/413,198 priority patent/US20200040148A1/en
Publication of TW202007718A publication Critical patent/TW202007718A/zh

Abstract

本發明提供一種植物纖維發泡板結構及其製造方法，該植物纖維發泡板係由包含植物纖維、乙烯醋酸乙烯共聚物及碳酸鈣混合發泡劑後加溫加壓模塑成型板片形狀，該植物纖維發泡板的結構中具有許多發泡氣泡孔，該些發泡氣泡孔為彼此之間不連通的獨立氣泡孔。製造方法包含以下步驟：將植物纖維、乙烯醋酸乙烯共聚物、碳酸鈣、發泡劑與架橋劑放入一攪拌機混合攪拌形成半成品；將該半成品放到熱壓發泡機的模具進行加熱加壓成型。藉此使本發明之植物纖維發泡板具有良好的彈性與隔音效果佳，而且不吸水份不易產生霉菌。

Description

植物纖維發泡板結構及其製造方法
本發明係關於一種發泡板結構及其製造方法，特別是關於一種植物纖維發泡板結構及其製造方法。
我們的生活中大量使用發泡板材，例如：拼接地墊、睡墊、瑜珈墊、餐墊、軟地板、隔音板、車用腳踏墊…等發泡產品，這些習知的發泡產品通常使用塑料或橡膠添加發泡劑後製成，該些塑料發泡材料不可分解，容易造成環境污染，對環境造成巨大的負荷。
為了改良上述習知技術的缺點，另一種習知技術，例如：中華民國公告第M470129號建築板材結構新型專利，其揭示一種植物纖維複合瑜珈墊，該植物纖維複合瑜珈墊利用植物纖維複合材料(Fiber Particulate Composite，簡稱FPC)與橡膠相互混合發泡成型所製成。該專利技術使用植物纖維混合天然橡膠製成發泡墊，其產品仍然具有些許橡膠，發出的令人不悅的味道，而且習用的發泡方法通常只加溫而不加壓發泡，發泡墊體內的氣泡孔為相互連通的氣泡孔，空氣會在氣泡孔間流動而無法具有單獨的氣室，使得彈性比較差，而且連通的氣泡孔使水分容易進入內部，以致容易產生霉菌。
有鑑於此，確實有必要提供一種發泡板結構以及製造方法，以改善上述習知發泡板之各項缺點。
本發明之一目的在提供一種能在自然界中分解的植物纖維發泡板結構及其製造方法。
本發明之另一目的在提供一種具有更大彈性以及更佳隔音效果的植物纖維發泡板結構及其製造方法。
本發明之另一目的在提供一種能大幅減少乙烯醋酸乙烯共聚物使用量的植物纖維發泡板結構及其製造方法。
為達成上述目的，本發明之植物纖維發泡板結構在一個實施例中，該植物纖維發泡板較佳係由包含植物纖維、乙烯醋酸乙烯共聚物及碳酸鈣混合發泡劑後加溫加壓模塑成型板片形狀，該植物纖維發泡板的結構中具有許多發泡氣泡孔，該些發泡氣泡孔為彼此之間不連通的獨立氣泡孔，藉此提供一種具有更大彈性以及更佳隔音效果的植物纖維發泡板結構。
在本發明的一些實施例中，其中，該植物纖維之重量百分比為30~65%，該乙烯醋酸乙烯共聚物之重量百分比為15~70%，該碳酸鈣之重量百分比為15~35%，藉此能大幅減少乙烯醋酸乙烯共聚物使用量。
在本發明的一些實施例中，其中，更佳的比例為該植物纖維之重量百分比為60%，該乙烯醋酸乙烯共聚物之重量百分比為15%，該碳酸鈣之重量百分比為15%，藉此能大幅減少乙烯醋酸乙烯共聚物使用量而且具有較佳的比例。
在本發明的一些實施例中，所述發泡劑之重量百分比為5~15%，藉此使發泡的發泡氣泡孔數量與孔徑獲得良好的控制。
在本發明的一些實施例中，所述發泡劑之重量百分比較佳為7%，藉此獲得更佳的發泡氣泡孔數量與孔徑。
在本發明的一些實施例中，該些發泡氣泡孔的孔徑為20~100μm，使本發明之植物纖維發泡板具有良好的彈性與抗濕性。
為達成上述目的，本發明製造植物纖維發泡板結構的方法在一個實施例中，包含以下步驟：將植物纖維、乙烯醋酸乙烯共聚物、碳酸鈣、發泡劑與架橋劑放入一攪拌機混合攪拌形成半成品；將該半成品放到熱壓發泡機的模具進行加熱加壓成型。
在本發明的一些實施例中，所述攪拌機為一密閉式捏合機，該攪拌時間為10~14分鐘，該攪拌溫度為120~140度C。
在本發明的一些實施例中，所述半成品放到熱壓發泡機的模具進行加熱加壓成型之前放入一雙軸滾輪機進行再次攪拌。
在本發明的一些實施例中，所述架橋劑為有機過氧化物BIPB，利有機過氧化物BIPB的特性使本發明之植物纖維發泡板不會產生刺激性臭味。
在本發明的一些實施例中，其中，該植物纖維為稻殼、小麥殼、甘蔗渣、玉米梗或水稻梗，經粉碎後取得之粉狀纖維，藉此能大幅減少乙烯醋酸乙烯共聚物使用量。
為讓本發明之上述及其他目的、特徵及優點能更明顯易懂，下文特舉本發明之較佳實施例，並配合所附圖式作詳細說明，文中實施例僅說明本發明可能之實施態樣，然並非用以限制本發明所欲保護之範疇。
參照圖1及圖2，圖1顯示本發明之植物纖維發泡板結構發泡成為大面積基材的示意圖，圖2顯示本發明將大面積基材裁切為所需形狀的示意圖。本發明之植物纖維發泡板10可以在模具中加壓發泡成為大面積基材，再將大面積基材裁切為所需形狀後成為成品。可以理解的是，本發明之植物纖維發泡板10也可以在模具中直接加壓發泡形成所需的尺寸與形狀。
將大面積基材裁切為所需形狀後的成品可以是如圖所示的拼接地墊11形狀，也可以裁切形成睡墊、瑜珈墊、餐墊、軟地板、隔音板、車用腳踏墊…等等的各種發泡產品。
同時參照圖3至圖5，圖3顯示本發明之植物纖維發泡板結構之製造過程的說明圖，圖4顯示本發明之植物纖維發泡板結構製造方法的製造流程圖，圖5顯示本發明之植物纖維發泡板結構的剖面示意圖。本發明之植物纖維發泡板結構製造方法在一個實施例中，該植物纖維發泡板10較佳係由包含植物纖維20、乙烯醋酸乙烯共聚物30及碳酸鈣40混合發泡劑50與架橋劑60後加溫加壓模塑成型之板片，該植物纖維發泡板的結構中具有許多發泡氣泡孔12，該些發泡氣泡孔12為彼此之間不連通的獨立氣泡孔，使本發明能提供一種具有更大彈性以及更佳隔音效果的植物纖維發泡板結構及其製造方法。
本較佳實施例之植物纖維發泡板10係以植物纖維20、乙烯醋酸乙烯共聚物30及碳酸鈣40作為基礎，上述的組成中，較佳地，植物纖維20之重量百分比為30~65%，該乙烯醋酸乙烯共聚物30之重量百分比為15~70%，該碳酸鈣40之重量百分比為15~35%，藉此能大幅減少乙烯醋酸乙烯共聚物30的使用量。其中，更佳的比例為該植物纖維20之重量百分比為60%，該乙烯醋酸乙烯共聚物30之重量百分比為15%，該碳酸鈣40之重量百分比為15%，藉此能大幅減少乙烯醋酸乙烯共聚物30使用量，而且該比例使本發明的彈性與抗水性等各項特性優良。
其中，該植物纖維20可以是稻殼、小麥殼、甘蔗渣、玉米梗或水稻梗等農業廢棄物，經粉碎後取得之粉狀纖維，利用上述農業的廢棄物作為本發明的主要構造，使本發明的植物纖維發泡板結構及其製造方法能在自然界中分解，也可以藉此大幅減少乙烯醋酸乙烯共聚物30的使用量。
其中，該乙烯醋酸乙烯共聚物30（又稱乙烯／乙酸乙烯酯共聚物，是由乙烯和乙酸乙烯酯共聚而製成，英文名稱為Ethylene Vinyl Acetate，簡稱為EVA），該乙烯醋酸乙烯共聚物30具有良好的柔軟性和彈性，化學穩定性良好，抗老化和耐臭氧強度良好，並且無毒性。
其中，該碳酸鈣40可以促進發泡並減緩熔體變形和移動能力，從而可以抑制發泡孔過快膨脹，使本發明的發泡氣泡孔12的氣泡孔徑更細。
較佳地，本發明植物纖維發泡板結構及其製造方法於製造過程使用的發泡劑50為偶氮二甲醯胺，藉此使本發明之植物纖維發泡板10具有良好的柔軟性及彈性，並且無毒性。偶氮二甲醯胺(發泡劑 AC，英文名稱為Azodicarbonamide，ADCA)，發泡劑50使用偶氮二甲醯胺，可以使本發明的植物纖維發泡板結構及其製造方法具有孔徑為20~100μm的發泡氣泡孔12，使本發明之植物纖維發泡板具有良好的彈性與抗濕性。
較佳地，所述發泡劑50之重量百分比為5~15%，藉此使發泡的發泡氣泡孔12的數量與孔徑獲得良好的控制。更佳地，所述發泡劑50之重量百分比較佳為7%，藉此獲得更佳的發泡氣泡孔12的數量與孔徑。
較佳地，本發明植物纖維發泡板結構及其製造方法於製造過程另包含重量百分比為1~3%的架橋劑60，藉此強化各個界面的結合作用。較佳地，所述架橋劑60使用有機過氧化物BIPB，利有機過氧化物BIPB的特性使本發明之植物纖維發泡板不會產生刺激性臭味。
續參照圖3，將上述植物纖維20、乙烯醋酸乙烯共聚物30及碳酸鈣40、發泡劑50以及架橋劑60一同放入一密閉式捏合機70中進行攪拌，攪拌時間大約為10~20分鐘，攪拌溫度大約為120~140∘C。
植物纖維20、乙烯醋酸乙烯共聚物30、碳酸鈣40、發泡劑50以及架橋劑60經過密閉式捏合機70攪拌後，可以直接放進一熱壓發泡機80的模具中同時加熱加壓發泡，通過熱壓發泡機80同時加熱及加壓發泡，可以使每一個發泡氣泡孔12形成獨立氣泡孔。
續參照圖4，本發明之植物纖維發泡板結構製造方法較佳係包含以下步驟：
S01步驟，將植物纖維20、乙烯醋酸乙烯共聚物30、碳酸鈣40、發泡劑50與架橋劑60放入一攪拌機混合攪拌形成半成品。該攪拌機較佳但不限於使用密閉式捏合機70。該密閉式捏合機70通常由缸體、漿軸、牆板、缸蓋等構成，藉由一對互相配合和旋轉的葉片產生強烈剪切作用，使材料能獲得均勻混合攪拌，可通過PLC控制及記錄生產中的溫度、時間與黏度。本發明較佳但不限於可以使用密閉式捏合機70進行上述材料的攪拌，使攪拌的溫度、時間與黏度都容易獲得較精確的控制。以上所述攪拌時間較佳為10~14分鐘，攪拌溫度為120~140度C，使該些混合物可以充分混合。
S02步驟，將上述混合物放入雙軸滾輪機(未繪示)反覆滾動。植物纖維20、乙烯醋酸乙烯共聚物30、碳酸鈣40、發泡劑50以及架橋劑60經過密閉式捏合機70攪拌後，也可以再放到一雙軸滾輪機(未繪示)反覆滾壓攪拌配方，使分散效果更佳。此步驟的目的是可以使混合物的分散效果更佳，但可以理解的是，此步驟亦可以省略。
S03步驟，出片冷卻機壓成片狀半成品。上述混合物通過雙軸滾輪機再次滾壓攪拌後，可以再通過一出片冷卻機(未繪示)壓成所需規格的片狀半成品後冷卻，該片狀半成品具有設定的厚度、形狀與重量，使後續的步驟可以順利製成規範的產品。此步驟的目的是可以使半成品符合規範的形狀與尺寸，但可以理解的是，此步驟亦可以省略。
S04步驟，將半成品放到熱壓發泡機的模具進行加熱加壓成型。將前一步驟冷卻出片機壓成所需規格的片狀體接著再放到熱壓發泡機80進行加熱及加壓發泡，藉此，可以使本發明的植物纖維發泡板10的每一個發泡氣泡孔12形成獨立氣泡孔。
S05步驟，冷卻後進行裁切。將上述步驟取得的植物纖維發泡板10進行裁切成所需的拼接地墊、睡墊、瑜珈墊、餐墊、軟地板、隔音板、車用腳踏墊…等發泡產品，即可以進行包裝出貨。
通過以上說明，本發明藉由包含植物纖維20、乙烯醋酸乙烯共聚物30及碳酸鈣40等材料，混合發泡劑50與架橋劑60後放到密閉式捏合機70進行攪拌，再放進熱壓發泡機80的模具中加溫加壓模塑形成板片材料，該植物纖維發泡板10的結構中具有許多發泡氣泡孔12，該些發泡氣泡孔12為彼此之間不連通的獨立氣泡孔，使本發明能提供一種能自然分解、能具有更大彈性以及更佳隔音效果的植物纖維發泡板結構及其製造方法。
以上所述之實施例僅係為說明本發明之技術思想及特徵，其目的在使熟習此項技藝之人士均能了解本發明之內容並據以實施，當不能以此限定本發明之專利範圍，凡依本發明之精神及說明書內容所作之均等變化或修飾，皆應涵蓋於本發明專利範圍內。
10‧‧‧植物纖維發泡板11‧‧‧拼接地墊12‧‧‧發泡氣泡孔20‧‧‧植物纖維30‧‧‧乙烯醋酸乙烯共聚物40‧‧‧碳酸鈣50‧‧‧發泡劑60‧‧‧架橋劑70‧‧‧密閉式捏合機80‧‧‧熱壓發泡機S01~S05‧‧‧步驟S01~S05
圖1顯示本發明之植物纖維發泡板結構發泡成為大面積基材的示意圖。 圖2顯示本發明將大面積基材裁切為所需形狀的示意圖。 圖3顯示本發明之植物纖維發泡板結構之製造過程的說明圖。 圖4顯示本發明之植物纖維發泡板結構製造方法的製造流程圖。 圖5顯示本發明之植物纖維發泡板結構的剖面示意圖。
S01~S05‧‧‧步驟S01~S05

Claims (10)

  1. 一種植物纖維發泡板結構，該植物纖維發泡板係由包含植物纖維、乙烯醋酸乙烯共聚物及碳酸鈣混合發泡劑與架橋劑後加溫加壓模塑成型板片形狀，該植物纖維發泡板結構具有許多發泡氣泡孔，該些發泡氣泡孔為彼此之間不連通的獨立氣泡孔。
  2. 如申請專利範圍第1項所述之植物纖維發泡板結構，其中，該植物纖維之重量百分比為30~65%，該乙烯醋酸乙烯共聚物之重量百分比為15~70%，該碳酸鈣之重量百分比為15~35%。
  3. 如申請專利範圍第2項所述之植物纖維發泡板結構，其中，該植物纖維之重量百分比為60%，該乙烯醋酸乙烯共聚物之重量百分比為15%，該碳酸鈣之重量百分比為15%。
  4. 如申請專利範圍第1項所述之植物纖維發泡板結構，其中，該些發泡氣泡孔的孔徑為20~100μm。
  5. 如申請專利範圍第1項所述之植物纖維發泡板結構，其中，該植物纖維為稻殼、小麥殼、甘蔗渣、玉米梗或水稻梗，經粉碎後取得之粉狀纖維。
  6. 如申請專利範圍第1項所述方法，其中，該發泡劑為偶氮二甲醯胺。
  7. 如申請專利範圍第1項所述方法，其中，該架橋劑為有機過氧化物BIPB。
  8. 一種製造如申請專利範圍第1至7項其中任一項所述之植物纖維發泡板結構的方法，包含以下步驟：將植物纖維、乙烯醋酸乙烯共聚物、碳酸鈣、發泡劑與架橋劑放入一攪拌機混合攪拌形成半成品；將該半成品放到熱壓發泡機的模具進行加熱加壓成型。
  9. 如申請專利範圍第8項所述之方法，其中，該半成品放到熱壓發泡機的模具進行加熱加壓成型之前放入一雙軸滾輪機進行再次攪拌。
  10. 如申請專利範圍第8項所述之方法，其中，如申請專利範圍第6項所述方法，其中，該攪拌機為一密閉式捏合機，該攪拌時間為10~14分鐘，該攪拌溫度為120~140度C。
TW107126776A 2018-08-01 2018-08-01 植物纖維發泡板結構及其製造方法 TW202007718A (zh)