TW201915519A - 透氣性眼用鏡片材料及透氣性眼用鏡片 - Google Patents
透氣性眼用鏡片材料及透氣性眼用鏡片 Download PDFInfo
- Publication number
- TW201915519A TW201915519A TW106132951A TW106132951A TW201915519A TW 201915519 A TW201915519 A TW 201915519A TW 106132951 A TW106132951 A TW 106132951A TW 106132951 A TW106132951 A TW 106132951A TW 201915519 A TW201915519 A TW 201915519A
- Authority
- TW
- Taiwan
- Prior art keywords
- ophthalmic lens
- breathable
- silane
- lens material
- patent application
- Prior art date
Abstract
一種透氣性眼用鏡片材料，其包含四乙氧基矽烷及離子型矽烷，該離子型矽烷包含正電荷及負電荷。另，本發明還涉及一種應用該透氣性眼用鏡片材料製成的透氣性眼用鏡片。
Description
本發明涉及一種眼用鏡片材料及應用該眼用鏡片材料製得的眼用鏡片，尤其涉及一種透氣性眼用鏡片材料及應用該透氣性眼用鏡片材料製得的透氣性眼用鏡片。
近年來，隨著近視人群的數量越來越多，隱形眼鏡因其便攜、美觀的特性而被廣泛使用。此外，對於高度近視者一般會藉由將透明晶（晶狀體）全摘除，然後植入眼內鏡片（人工晶狀體等），以使高度近視者可以看清物體。
透氣性眼用鏡片因為可以使佩戴者的角膜能夠與足夠的氧氣接觸，有利於角膜的健康，而受到使用者的青睞。習知的透氣性眼用鏡片中含有矽酮以使眼用具有透氣性，然而，矽酮的存在還可使眼用鏡片具有疏水性，而疏水性會導致眼用鏡片表面蛋白質沉積，使佩戴者有異物感，甚至滋生細菌。
有鑑於此，有必要提供一種新的透氣性眼用鏡片材料，以解決上述問題。
另，還有必要提供一種應用所述透氣性眼用鏡片材料製得的透氣性眼用鏡片。
一種透氣性眼用鏡片材料，其包含四乙氧基矽烷及離子型矽烷，該離子型矽烷包含正電荷及負電荷。
一種透氣性眼用鏡片，該透氣性眼用鏡片由上述透氣性眼用鏡片材料製得。
本發明的透氣性眼用鏡片材料中同時包含正電荷及負電荷兩種極性相反的電荷，使得透氣性眼用鏡片材料具有親水性，並且可以防止細菌污染。由該透氣性眼用鏡片材料製得的透氣性眼用鏡片中也同時包含正電荷及負電荷兩種極性相反的電荷，使得透氣性眼用鏡片具有親水性，並且可以防止細菌污染。
下面將結合本發明實施方式中的附圖，對本發明實施方式中的技術方案進行清楚、完整地描述，顯然，所描述的實施方式僅僅是本發明一部分實施方式，而不是全部的實施方式。
基於本發明中的實施方式，本領域普通技術人員在沒有做出創造性勞動前提下所獲得的所有其他實施方式，都屬於本發明保護的範圍。
本文所使用的所有的技術和科學術語與屬於本發明的技術領域的技術人員通常理解的含義相同。本文中在本發明的說明書中所使用的術語只是為了描述具體的實施方式的目的，不是旨在於限製本發明。
本發明較佳實施方式提供一種透氣性眼用鏡片材料，其用於製備透氣性眼用鏡片。該透氣性眼用鏡片材料包含四乙氧基矽烷（TEOS）及離子型矽烷。該離子型矽烷包含正電荷及負電荷。
在至少一實施例中，所述離子型矽烷為兩性離子型矽烷。在另一實施例中，所述離子型矽烷包括帶有正電荷的矽烷和帶有負電荷的矽烷。
當所述離子型矽烷為兩性離子型矽烷時，所述透氣性眼用鏡片材料中，四乙氧基矽烷的質量百分含量為68%~98.5%，兩性離子型矽烷的質量百分含量為1.5%~32%。
所述兩性離子型矽烷包括但不限於含有矽烷官能基的磺基甜菜鹼（Sulfobetainesilane）、含有矽烷官能基的羧基甜菜鹼（carboxybetainesilane）、及矽烷官能化磷酸膽鹼（phosphorylcholinesilane）中的一種或幾種。
所述含有矽烷官能基的磺基甜菜鹼的化學結構式為：。
所述含有矽烷官能基的羧基甜菜鹼的化學結構式為：。
所述矽烷官能化磷酸膽鹼的化學結構式為：。
所述兩性離子型矽烷中的總電荷為零，即兩性離子性矽烷的電荷總和為中性。同時帶有正電荷及負電荷兩種極性相反的電荷，使得兩性離子型矽烷具有親水性，並且可以防止細菌污染。從而使得透氣性眼用鏡片材料具有親水性，並且可以防止細菌污染。
當所述離子型矽烷包括帶有正電荷的矽烷和帶有負電荷的矽烷時，所述透氣性眼用鏡片材料中，四乙氧基矽烷的質量百分含量為67.2%~98%，帶有正電荷的矽烷的質量百分含量為0.8%~32%，帶有負電荷的矽烷的質量百分含量為0.8%~32%。
所述帶有正電荷的矽烷包括但不限於3-（三甲氧基矽基）丙基-N,N,N-三甲基（3-(trimethoxysilyl)propyl-N,N,N-trimethylammonium）、N-（三甲氧基甲矽烷基）乙二胺三乙酸三鈉（N-(trimethoxysilylpropyl) ethylenediaminetriacetate）、4-(三甲氧基矽基乙基)苄基三甲基氯化銨(4-(TRIMETHOXYSILYLETHYL)BENZYLTRIMETHYLAMMONIUM CHLORIDE)、及四乙酸二甲基(3-三甲氧基矽基丙基)銨(TETRADECYLDIMETHYL(3-TRIMETHOXYSILYLPROPYL)AMMONIUM CHLORIDE)中的一種或幾種。
所述帶有負電荷的矽烷包括但不限於羧乙基化矽烷三醇（carboxyethylsilanetriol）、3-(三羥基矽基)-丙烷磺酸(3-(TRIHYDROXYSILYL)-1-PROPANESULFONIC ACID)、三乙氧基矽基丙基馬來酸(TRIETHOXYSILYLPROPYLMALEAMIC ACID)、及3-(三羥基矽基)丙甲基磷酸酯(3-(TRIHYDROXYSILYL)PROPYL METHYLPHOSPHONATE) 中的一種或幾種。
所述離子型矽烷中帶有正電荷的矽烷和帶有負電荷的矽烷的總電荷為零，即離子型矽烷的電荷總和為中性。同時帶有正電荷及負電荷兩種極性相反的電荷，使得離子型矽烷具有親水性，並且可以防止細菌污染。從而使得透氣性眼用鏡片材料具有親水性，並且可以防止細菌污染。
一種透氣性眼用鏡片，其可為隱形眼鏡、眼內鏡片（AIOL）等，該眼內鏡片可為人工晶狀體（IOLs）等。該透氣性眼用鏡片由上述透氣性眼用鏡片材料製得。
當所述透氣性眼用鏡片材料中所包含的離子型矽烷為兩性離子型矽烷時，所述透氣性眼用鏡片中主要包含以下化學結構式：， 其中，R為磺基甜菜鹼基、羧基甜菜鹼基、或磷酸膽鹼基，n1
為大於等於1的自然數。上述化學結構式中，O-後連接Si，Si-後連接O，如此循環，形成一種連續的-Si-O-網路結構。
所述磺基甜菜鹼基的化學結構式為：， 其中，n2
可以為1、2或3。
所述羧基甜菜鹼基的化學結構式為：， 其中，n3
可以為1、2或3。
所述磷酸膽鹼基的化學結構式為：。
當所述透氣性眼用鏡片材料中所包含的離子型矽烷為正電荷的矽烷和帶有負電荷的矽烷時，所述眼用鏡片中主要包含一下化學結構式：， 其中，上述化學結構式中，O-後連接Si，Si-後連接O，如此循環，形成一種連續的-Si-O-網路結構；n4
為大於等於1的自然數；n5
為大於等於1的自然數； R1
為：； R2
為以下基團中的一種：（磺基）、（羧基）、（磷酸基）。
所述透氣性眼用鏡片中同時含有正電荷及負電荷兩種極性相反的電荷，使得該透氣性眼用鏡片具有親水性，並且可以防止細菌污染。
一種透氣性眼用鏡片的製造方法，其包括以下步驟：
步驟S1，提供所述四乙氧基矽烷及離子型矽烷，將該四乙氧基矽烷及離子型矽烷按照預設比例混合均勻，使四乙氧基矽烷與離子型矽烷共水解，得到前驅體溶液。
步驟S2，提供一眼用鏡片模具，將上述前驅體溶液置於眼用鏡片模具中，壓合，得到透氣性眼用鏡片片材。
步驟S3，對所述透氣性眼用鏡片片材的表面進行切削加工，以得到透氣性眼用鏡片。
下面藉由實施例來對本發明進行具體說明。
實施例1
本實施例的透氣性眼用鏡片材料包含四乙氧基矽烷及含有矽烷官能基的磺基甜菜鹼。
本實施例的透氣性眼用鏡片材料中四乙氧基矽烷的質量百分含量為94.8%，含有矽烷官能基的磺基甜菜鹼的質量百分含量為5.2%。
本實施例的透氣性眼用鏡片材料製得的透氣性眼用鏡片的表面的水接觸角為60℃。
本實施例的透氣性眼用鏡片材料製得的透氣性眼用鏡片的透氧值DK為100。
實施例2
本實施例的透氣性眼用鏡片材料包含四乙氧基矽烷及含有矽烷官能基的羧基甜菜鹼。
本實施例的透氣性眼用鏡片材料中四乙氧基矽烷的質量百分含量為90.2%，含有矽烷官能基的羧基甜菜鹼的質量百分含量為9.8%。
本實施例的透氣性眼用鏡片材料製得的透氣性眼用鏡片的表面的水接觸角為46℃。
本實施例的透氣性眼用鏡片材料製得的透氣性眼用鏡片的透氧值DK為100。
實施例3
本實施例的透氣性眼用鏡片材料包含四乙氧基矽烷、羧乙基化矽烷三醇及3-（三甲氧基矽基）丙基-N,N,N-三甲基。
本實施例的透氣性眼用鏡片材料中四乙氧基矽烷的質量百分含量為95%，羧乙基化矽烷三醇的質量百分含量為2.5%，3-（三甲氧基矽基）丙基-N,N,N-三甲基的質量百分含量為2.5%。
本實施例的透氣性眼用鏡片材料製得的透氣性眼用鏡片的表面的水接觸角為58℃。
本實施例的透氣性眼用鏡片材料製得的透氣性眼用鏡片的透氧值DK為100。
實施例4
本實施例的透氣性眼用鏡片材料包含四乙氧基矽烷、3-（三甲氧基矽基）丙基-N,N,N-三甲基、及N-（三甲氧基甲矽烷基）乙二胺三乙酸三鈉。
本實施例的透氣性眼用鏡片材料中四乙氧基矽烷的質量百分含量為90%，3-（三甲氧基矽基）丙基-N,N,N-三甲基的質量百分含量為7.5%，N-（三甲氧基甲矽烷基）乙二胺三乙酸三鈉的質量百分含量為2.5%。
本實施例的透氣性眼用鏡片材料製得的透氣性眼用鏡片的表面的水接觸角為52℃。
本實施例的透氣性眼用鏡片材料製得的透氣性眼用鏡片的透氧值DK為100。
本發明的透氣性眼用鏡片材料中同時包含正電荷及負電荷兩種極性相反的電荷，使得透氣性眼用鏡片材料具有親水性，並且可以防止細菌污染。由該透氣性眼用鏡片材料製得的透氣性眼用鏡片中也同時包含正電荷及負電荷兩種極性相反的電荷，使得透氣性眼用鏡片具有親水性，並且可以防止細菌污染。
另外，以上所述，僅是本發明的較佳實施方式而已，並非對本發明任何形式上的限製，雖然本發明已將較佳實施方式揭露如上，但並非用以限定本發明，任何熟悉本專業的技術人員，在不脫離本發明技術方案範圍內，當可利用上述揭示的技術內容做出些許更動或修飾為等同變化的等效實施方式，但凡是未脫離本發明技術方案內容，依據本發明的技術實質對以上實施方式所做的任何簡單修改、等同變化與修飾，均仍屬於本發明技術方案的範圍內。
無
無
Claims (10)
- 一種透氣性眼用鏡片材料，其改良在於，該透氣性眼用鏡片材料包含四乙氧基矽烷及離子型矽烷，該離子型矽烷包含正電荷及負電荷。
- 如申請專利範圍第1項所述的透氣性眼用鏡片材料，其中，所述離子型矽烷為兩性離子型矽烷。
- 如申請專利範圍第2項所述的透氣性眼用鏡片材料，其中，所述透氣性眼用鏡片材料中，所述四乙氧基矽烷的質量百分含量為68%~98.5%，所述兩性離子型矽烷的質量百分含量為1.5%~32%。
- 如申請專利範圍第2項所述的透氣性眼用鏡片材料，其中，所述兩性離子型矽烷包括含有矽烷官能基的磺基甜菜鹼、含有矽烷官能基的羧基甜菜鹼、及含有矽烷官能基的磷酸膽鹼中的一種或幾種。
- 如申請專利範圍第1項所述的透氣性眼用鏡片材料，其中，所述離子型矽烷包括帶有正電荷的矽烷和帶有負電荷的矽烷。
- 如申請專利範圍第5項所述的透氣性眼用鏡片材料，其中，所述透氣性眼用鏡片材料中，所述四乙氧基矽烷的質量百分含量為67.2%~98%，所述帶有正電荷的矽烷的質量百分含量為0.8%~32%，帶有負電荷的矽烷的質量百分含量為0.8%~32%。
- 如申請專利範圍第5項所述的透氣性眼用鏡片材料，其中，所述帶有正電荷的矽烷包括3-（三甲氧基矽基）丙基-N,N,N-三甲基、N-（三甲氧基甲矽烷基）乙二胺三乙酸三鈉、4-(三甲氧基矽基乙基)苄基三甲基氯化銨、及四乙酸二甲基(3-三甲氧基矽基丙基)銨中的一種或幾種，所述帶有負電荷的矽烷包括羧乙基化矽烷三醇、3-(三羥基矽基)-丙烷磺酸、三乙氧基矽基丙基馬來酸、及3-(三羥基矽基)丙甲基磷酸酯中的一種或幾種。
- 一種透氣性眼用鏡片，其改良在於，該透氣性眼用鏡片由申請專利範圍第1至7項中任意一項所述的透氣性眼用鏡片材料製得。
- 如申請專利範圍第8項所述的透氣性眼用鏡片，其中，所述透氣性眼用鏡片中主要包含以下化學結構式：， 其中，R為磺基甜菜鹼基、羧基甜菜鹼基、或磷酸膽鹼基，n1 為大於等於1的自然數。
- 如申請專利範圍第8項所述的透氣性眼用鏡片，其中，所述透氣性眼用鏡片中主要包含以下化學結構式：， 其中，n4 為大於等於1的自然數；n5 為大於等於1的自然數；R1 為；R2 為、、及中的一種。