TW201710101A - Hot melt adhesive film and a composite structure thereof - Google Patents
Hot melt adhesive film and a composite structure thereof Download PDFInfo
- Publication number
- TW201710101A TW201710101A TW104128783A TW104128783A TW201710101A TW 201710101 A TW201710101 A TW 201710101A TW 104128783 A TW104128783 A TW 104128783A TW 104128783 A TW104128783 A TW 104128783A TW 201710101 A TW201710101 A TW 201710101A
- Authority
- TW
- Taiwan
- Prior art keywords
- hot melt
- melt adhesive
- adhesive film
- film
- pores
- Prior art date
Abstract
Description
傳統鞋子其鞋面上花紋圖案等主要係採車縫方式縫設於鞋面，或直接於鞋面上以網版印刷印製有花紋圖案等；然，隨著人工車縫成本提高，將花紋圖案等車縫於鞋面方式，有製作成本過高缺失，另以網版印刷直接將花紋圖案印製於鞋面上，則有花紋圖案不易附著於鞋面上等缺失。於是，請參閱第五圖所示，乃有業者研發將具有花紋圖案之裝飾片體（６）黏貼於鞋面上，以期改善上述車縫成本過高及花紋圖案不易附著於鞋面等缺失，該裝飾片體（６）的製作主要係以網版印刷將油墨圖案（６２）印製於一膜材（６１）表面，再於該印刷有油墨圖案（６２）之膜材（６１）表面塗佈黏著層（６３），繼將保護膜（６４）藉由黏著層（６３）黏貼於膜材（６１）表面，以防止膜材（６１）上的油墨圖案被刮除，續將一熱熔膠膜（６５）及該具有油墨圖案之膜材（６１）依序設置於一基材（６６）上，而後以熱壓設備進行熱壓，使熱熔膠膜（６５）熱活化後，將該具有油墨圖案之膜材（６１）黏結於該基材（６６）上，依此，以完成該裝飾片體（６）的製作。Traditional shoes, such as the pattern on the upper, are mainly sewn on the upper of the shoe, or directly printed on the upper with a pattern printed on the screen; however, as the cost of the artificial sewing increases, the pattern The pattern is sewn to the upper, and the production cost is too high. The screen printing is directly printed on the upper by the screen printing, and the pattern is not easily attached to the upper. Therefore, as shown in the fifth figure, the manufacturer has developed a decorative sheet (6) with a pattern to adhere to the upper, in order to improve the cost of the above-mentioned sewing and the difficulty in attaching the pattern to the upper. The decorative sheet body (6) is mainly produced by screen printing an ink pattern (62) on the surface of a film (61), and then coating the surface of the film (61) on which the ink pattern (62) is printed. The adhesive layer (63) is adhered to the surface of the film (61) by the adhesive layer (63) to prevent the ink pattern on the film (61) from being scraped off, and a hot melt is continued. The film (65) and the film (61) having the ink pattern are sequentially disposed on a substrate (66), and then hot pressed by a hot pressing device to thermally activate the hot melt film (65). The film (61) having an ink pattern is adhered to the substrate (66), whereby the production of the decorative sheet (6) is completed.
由上述裝飾片體（６）的製作工序可知，該裝飾片體（１）係至少由膜材（６１）、黏著層（６３）、保護膜（６４）、熱熔膠膜（６５）及基材（６６）等五個層體所組成；然，此五個層體設置，不僅耗費材料成本，且將該五個層體依序黏結，更是繁瑣耗工費時，尤其該為強力膠、有機溶劑或水性膠水等黏著層（６３）於塗佈時，會揮發有毒氣體，造成作業人員呼吸道受損等情形，且易有塗佈不均勻，影響黏結牢固性，及黏著劑溢流於外乾燥後不美觀等缺失。因此，有鑑於該現有裝飾片體（６３）於製作上仍有上述工序繁複、製作成本高及層體間黏結不牢固等諸多缺失，乃藉其多年於相關領域的製造及設計經驗和知識的輔佐，並經多方巧思，研創出本發明。According to the manufacturing process of the decorative sheet body (6), the decorative sheet body (1) is composed of at least a film material (61), an adhesive layer (63), a protective film (64), a hot melt adhesive film (65), and a base. The material consists of five layers: (66); however, the five layers are not only costly, but also the five layers are sequentially bonded, which is cumbersome and time consuming, especially for super glue. When the adhesive layer (63) such as an organic solvent or an aqueous glue is applied, volatile gas is volatilized, causing damage to the respiratory tract of the operator, and uneven coating is likely to occur, affecting the firmness of adhesion, and the adhesive overflows. Missing after drying, etc. Therefore, in view of the fact that the conventional decorative sheet body (63) still has many defects such as the above-mentioned complicated steps, high production cost, and weak adhesion between the layers, it is the manufacturing and design experience and knowledge of the related fields for many years. Accomplished, and through many ingenuity, research and development of the present invention.
為了達到上述實施目的，本發明人乃研擬如下熱熔膠膜，係主要設有一呈片狀且具有厚度之膜體，並使該膜體由內而外成型有複數不規則細孔。In order to achieve the above-described object, the present inventors have developed a hot melt adhesive film which is mainly provided with a film body having a sheet shape and a thickness, and the film body is formed with a plurality of irregular pores from the inside to the outside.
如上所述之熱熔膠膜，其中，該複數細孔係包含有貫穿該膜體及非貫穿該膜體者。The hot melt adhesive film as described above, wherein the plurality of pores comprise a film that penetrates the film body and does not penetrate the film body.
如上所述之熱熔膠膜其組合結構，係於該熱熔膠膜一側端面對應設置有一保護膜，又使該熱熔膠膜相對其設置該保護膜之另側端面設有油墨圖案，且使該油墨圖案由該熱熔膠膜之細孔滲入該熱熔膠膜中，另設有一基材，乃使該基材對應設置於該熱熔膠膜相對其設置該保護膜之另側端面上，復使該熱熔膠膜與設置於其二側端面之保護膜及基材熱壓黏結，並使該熱熔膠膜之細孔密合。The hot melt adhesive film has a combined structure, and a protective film is disposed on one end surface of the hot melt adhesive film, and the hot melt adhesive film is provided with an ink pattern on the other end surface of the protective film. And inserting the ink pattern into the hot melt adhesive film from the pores of the hot melt adhesive film, and further providing a substrate, wherein the substrate is correspondingly disposed on the other side of the hot melt adhesive film opposite to the protective film On the end surface, the hot melt adhesive film is thermocompression bonded to the protective film and the substrate disposed on the both end faces thereof, and the pores of the hot melt adhesive film are adhered.
藉此，於將本發明之熱熔膠膜與保護膜及基材等組合實施時，係藉由熱熔膠膜上所設複數不規則細孔，以使印刷其上之油墨圖案由該熱熔膠膜之細孔滲入熱熔膠膜後，可使熱熔膠膜與設置於其二側面之保護膜及基材穩固黏結，以組成具有花紋圖案之裝飾片體，依此，即可有效簡化其組成該裝飾片體的層數及工序，達到節省材料成本及製作工時等實質效益。Therefore, when the hot melt adhesive film of the present invention is combined with the protective film and the substrate, the plurality of irregular pores are provided on the hot melt adhesive film so that the ink pattern printed thereon is heated by the heat. After the pores of the molten film penetrate into the hot melt adhesive film, the hot melt adhesive film can be firmly bonded to the protective film and the substrate disposed on the two sides thereof to form a decorative sheet having a pattern, thereby being effective Simplify the number of layers and processes that make up the decorative sheet, and achieve substantial benefits such as material cost savings and manufacturing hours.
首先，請參閱第一、二圖所示，為本發明之熱熔膠膜（１），本發明之熱熔膠膜（１）係主要設有一呈片狀且具有厚度之膜體（１１），並使該膜體（１１）由內而外成型有均勻分佈之複數不規則細孔（１２），該複數細孔（１２）係包含有貫穿膜體（１１）及非貫穿膜體（１１）者。First, referring to the first and second figures, the hot melt adhesive film (1) of the present invention, the hot melt adhesive film (1) of the present invention is mainly provided with a film body having a sheet shape and having a thickness (11). And forming the film body (11) from the inside to the outside with a plurality of irregular pores (12) uniformly distributed, the plurality of pores (12) comprising a penetrating membrane body (11) and a non-penetrating membrane body (11) )By.
據此，請一併參閱第三、四圖所示，當將本發明之熱熔膠膜（１）與保護膜（２）及基材（３）等組合實施時，係將一保護膜（２）對應設置於本發明之熱熔膠膜（１）一側端面，並使該熱熔膠膜（１）相對其設置該保護膜（２）之另側端面以網版印刷有油墨圖案（４），該油墨圖案（４）之油墨（４１）係會由該熱熔膠膜（１）其複數細孔（１２）滲入該熱熔膠膜（１）中，另設有一基材（３），乃使該基材（３）對應設置於該熱熔膠膜（１）相對其設置該保護膜（２）之另端面上［即該熱熔膠膜（１）印刷油墨圖案（４）之該端面］，並以熱壓設備熱壓，使熱熔膠膜（１）熱活化〔Heat Reactivity〕，而與設置於其二側端面之保護膜（２）及基材（３）相黏結，並使該熱熔膠膜（１）之細孔（１２）熱壓密合，以使由該熱熔膠膜（１）其複數細孔（１２）滲入該熱熔膠膜（１）內之油墨圖案（４）及其油墨（４１）封鎖於該熱熔膠膜（１）中，依此，以簡便組成一具有花紋圖案之裝飾片體（５）［請一併參照附件一所示］。Accordingly, as shown in the third and fourth figures, when the hot melt adhesive film (1) of the present invention is combined with the protective film (2) and the substrate (3), a protective film is used. 2) correspondingly disposed on one end surface of the hot melt adhesive film (1) of the present invention, and the inkjet printing film (1) is screen-printed with an ink pattern on the other end surface of the protective film (2) 4) The ink (41) of the ink pattern (4) is infiltrated into the hot melt adhesive film (1) by the plurality of fine pores (12) of the hot melt adhesive film (1), and a substrate (3) is further provided. ), the substrate (3) is correspondingly disposed on the other end surface of the hot melt adhesive film (1) opposite to the protective film (2) [ie, the hot melt adhesive film (1) printing ink pattern (4) The end surface] is heat-pressed by a hot pressing device to thermally activate the hot melt adhesive film (1), and is bonded to the protective film (2) and the substrate (3) provided on both end faces thereof. And the pores (12) of the hot melt adhesive film (1) are thermocompression bonded so that the hot melt adhesive film (1) is recovered The ink pattern (4) penetrating into the hot melt adhesive film (1) and the ink (41) thereof are sealed in the hot melt adhesive film (1), thereby facilitating the composition of a pattern having a pattern Decorative sheet (5) [please refer to Annex 1 together].
於此，當欲於運動鞋、休閒鞋…等鞋子之鞋面上設具花紋圖案，以增加鞋子造型美感時，即可將該裝飾片體（５）黏貼於鞋子之鞋面，於製作實施時，係可將該裝飾片體（５）裁切成與鞋面相對應形狀，另將黏著劑塗佈於鞋面上，而後將裝飾片體（５）黏貼於鞋面，以完成於鞋面上增設花紋圖案之製作，而於該將裝飾片體（５）與鞋面黏結之實施方式中，本發明係提供另一較佳實施方式，乃將一熱熔膠膜裁切成與鞋面相對應形狀後，再將該熱熔膠膜對應設置於該裝飾片體（５）及鞋面間，繼以熱壓設備進行熱壓，以使該熱熔膠膜熱活化後，將裝飾片體（５）與鞋面經該熱熔膠膜相互黏結，依此，即可將裝飾片體（５）與鞋面簡便黏結，以避免塗佈強力膠、有機溶劑或水性膠水等黏著劑，易造成作業人員呼吸道受損，與黏著劑溢流於外乾燥後不美觀性，或有塗佈不均勻、黏結不牢固等情形。Here, when a shoe pattern is to be provided on the upper surface of the shoes such as sports shoes, casual shoes, etc., in order to increase the beauty of the shoes, the decorative sheet body (5) can be adhered to the upper of the shoe, and the production is carried out. The decorative sheet body (5) can be cut into a shape corresponding to the upper, and an adhesive is applied to the upper, and then the decorative sheet (5) is adhered to the upper to complete the upper. In the embodiment in which the decorative sheet (5) is bonded to the upper, the present invention provides another preferred embodiment in which a hot melt adhesive film is cut into the upper surface. After corresponding shapes, the hot melt adhesive film is correspondingly disposed between the decorative sheet body (5) and the upper surface, and then hot pressed by a hot pressing device to thermally activate the hot melt adhesive film, and then the decorative sheet body is heated. (5) Bonding to the upper through the hot melt adhesive film, thereby, the decorative sheet body (5) can be easily bonded to the upper to avoid the application of adhesives such as super glue, organic solvent or water-based glue. Causes the operator's respiratory tract to be damaged, and the adhesive overflows after drying. Aesthetics, or uneven coating, and the like case is not strong bond.
前述之實施例或圖式並非限定本發明之熱熔膠膜及其組合結構實施樣態，本發明之熱熔膠膜（１）與保護膜（２）、基材（３）及油墨圖案（４）等組合形成之裝飾片體（５）亦可於裁切成所需形狀後黏貼於衣服或桌墊等，凡所屬技術領域中具有通常知識者所為之適當變化或修飾，皆應視為不脫離本發明之熱熔膠膜及其組合結構專利範疇。The foregoing embodiments or drawings do not limit the hot melt adhesive film of the present invention and the combination structure thereof, and the hot melt adhesive film (1) and the protective film (2), the substrate (3) and the ink pattern of the present invention ( 4) The decorative sheet (5) formed by the combination may be adhered to a garment or a table mat after being cut into a desired shape, and any change or modification made by a person having ordinary knowledge in the technical field shall be regarded as The patent range of the hot melt adhesive film and its combined structure of the present invention is not deviated.
由上述結構及實施方式可知，本發明係具有如下優點：As can be seen from the above structures and embodiments, the present invention has the following advantages:
1.本發明之熱熔膠膜及其組合結構係於熱熔膠膜上設有複數不規則細孔，藉此，以使印刷其上之油墨圖案由該熱熔膠膜之細孔滲入熱熔膠膜後，再使熱熔膠膜與設置於其二側面之保護膜及基材穩固黏結，以組成具有花紋圖案之裝飾片體，依此，即可有效簡化其組成該裝飾片體的層數及工序，達到節省材料成本及製作工時等效益。1. The hot melt adhesive film of the present invention and the combined structure thereof are provided with a plurality of irregular pores on the hot melt adhesive film, whereby the ink pattern printed thereon is infiltrated into the heat from the pores of the hot melt adhesive film. After the film is melted, the hot melt adhesive film is firmly bonded to the protective film and the substrate disposed on the two sides thereof to form a decorative sheet having a pattern, thereby effectively simplifying the composition of the decorative sheet. The number of layers and processes can save on material costs and manufacturing hours.
2.本發明之熱熔膠膜及其組合結構係藉其熱熔膠膜上設具複數細孔，以供油墨圖案滲入該熱熔膠膜中，而使熱熔膠膜二側面皆可與保護膜及基材進行穩固黏結，於此，即可避免使用強力膠、有機溶劑或水性膠水等為黏著劑，造成作業人員呼吸道受損，與黏著劑溢流於外乾燥後之不美觀性及黏結不牢固等情形者。2. The hot-melt adhesive film and the combined structure thereof of the present invention are provided with a plurality of fine holes on the hot-melt adhesive film for the ink pattern to penetrate into the hot melt adhesive film, so that both sides of the hot melt adhesive film can be combined with The protective film and the substrate are firmly bonded, thereby avoiding the use of superglue, organic solvent or water-based glue as an adhesive, causing damage to the respiratory tract of the operator, and the unsightly appearance of the adhesive overflowing outside and drying. If the bond is not strong, etc.
綜上所述，本發明之實施例確能達到所預期功效，又其所揭露之具體構造，不僅未曾見諸於同類產品中，亦未曾公開於申請前，誠已完全符合專利法之規定與要求，爰依法提出發明專利之申請，懇請惠予審查，並賜准專利，則實感德便。In summary, the embodiments of the present invention can achieve the expected functions, and the specific structures disclosed therein have not been seen in the same products, nor have they been disclosed before the application, and have fully complied with the provisions of the Patent Law. It is required that if an application for a patent for invention is filed in accordance with the law, and if the application is granted, the patent will be granted.
（１）‧‧‧熱熔膠膜(1)‧‧‧Hot melt film
（１１）‧‧‧膜體(11) ‧ ‧ membranous body
（１２）‧‧‧細孔(12)‧‧‧Pore
（２）‧‧‧保護膜(2) ‧ ‧ protective film
（３）‧‧‧基材(3) ‧‧‧Substrate
（４）‧‧‧油墨圖案(4) ‧ ‧ ink patterns
（４１）‧‧‧油墨(41) ‧ ‧ ink
（５）‧‧‧裝飾片體(5) ‧‧‧Decorative sheet
＜現有＞<existing>
（６）‧‧‧裝飾片體(6)‧‧‧Decorative sheet
（６１）‧‧‧膜材(61) ‧‧‧membrane
（６２）‧‧‧油墨圖案(62) ‧ ‧ ink patterns
（６３）‧‧‧黏著層(63) ‧‧‧Adhesive layer
（６４）‧‧‧保護膜(64) ‧ ‧ protective film
（６５）‧‧‧熱熔膠膜(65)‧‧‧Hot melt film
（６６）‧‧‧基材(66) ‧‧‧Substrate
第二圖：本發明之熱熔膠膜剖視圖Second: cross-sectional view of the hot melt adhesive film of the present invention
第三圖：本發明之熱熔膠膜實施組合狀態圖（一）The third figure: the combined state diagram of the hot melt adhesive film of the present invention (1)
第四圖：本發明之熱熔膠膜實施組合狀態圖（二）The fourth figure: the combined state diagram of the hot melt adhesive film of the present invention (2)
第五圖：現有之分解前視圖 【附件】Figure 5: Existing front view of the decomposition [Attachment]
附件一：本發明之熱熔膠膜及其組合形成之裝飾片體實物照片Annex I: Photograph of the decorative sheet formed by the hot melt adhesive film of the present invention and the combination thereof
(1)‧‧‧熱熔膠膜 (1)‧‧‧Hot melt film
(11)‧‧‧膜體 (11) ‧ ‧ membranous body
(12)‧‧‧細孔 (12)‧‧‧Pore
(2)‧‧‧保護膜 (2) ‧ ‧ protective film
(4)‧‧‧油墨圖案 (4) ‧ ‧ ink patterns
(41)‧‧‧油墨 (41) ‧ ‧ ink
Claims (4)