200840649 九、發明說明: 【發明所屬之技術領域】 物體. 裝置 H聽㈣於—種熱炫轉粉末用於黏著非金屬 •械理嫩編.椒峨電荷神 r用於黏著非金屬物體表面處理方法及其處理 i光别技術】200840649 IX. Description of the invention: [Technical field of invention] Object. Device H (4) in a kind of hot-spinning powder for adhesion to non-metal, mechanical and tender. The scorpion is used to adhere to the surface treatment of non-metallic objects. Method and its processing i-light technology]
欠用3ΓΓ _岐行黏合時,都_將液態膠 2蛛或鮮在雜合部位後再進行黏合,由於待 贺塗區域的形狀不確定性,因此其作業均為勞動密集型的 手工作業,例如好料_合,錄底料的黏合或鞋 底與鞋底以上部分_合,它包含了先_賴型溶劑塗 覆於鞋子部件上辭n崎再·_水或者黏ς 翻炼劑塗覆的手工應用,其後還要消耗高度能量,用以 =發水或其他_黏合嫩體成分。由於__合劑型炫 有一些有毒成份,如苯,甲轉,長期處於這種惡劣 的手工作#環财,會對人體產錄大的危害,尤其是女 性’可能還會影_下—代的舰出生。 、 【發明内容】 本發明的目的在於提供一種熱熔膠粉末噴塗在非金 200840649 聽體表崎齡編方奴4轉置,該處理方 — 娜粉禾噴塗及⑽b過程在作章 至裏進行並達到自動化程度,可 ,、 Η 又了以即名能源,減少工作空 3,降低勞動強度,並改善作業環境。 為了達到上述目的,本發日月提供了 _種 :於非金屬物體表面的處理方法,該處理心If you use 3ΓΓ _ 岐 黏 黏 , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , For example, the material is _, the bottom of the material is bonded or the sole is combined with the upper part of the sole. It contains the first solvent to be applied to the shoe parts, or the water is coated with the retort. Manually applied, and then consumes a high amount of energy, used to = water or other _ adhesive body composition. Because __ mixture type Hyun has some toxic ingredients, such as benzene, A turn, long-term in this kind of bad hand work #环财, will cause great harm to the human body, especially women 'may be shadow _ lower - generation The ship was born. SUMMARY OF THE INVENTION [The present invention] It is an object of the present invention to provide a hot-melt adhesive powder sprayed on a non-gold 200840649 listener table Sakizawa Noun 4 transposition, the treatment side - Na powder and spray and (10) b process in the chapter to the inside And to achieve the degree of automation, can,, and 以, with the name of energy, reduce work space 3, reduce labor intensity, and improve the working environment. In order to achieve the above objectives, the present day and the moon provide _ kinds of: treatment methods on the surface of non-metallic objects, the treatment heart
區域; a·塗抹清潔劑:將清潔劑塗抹在待黏 著物體的待黏著 b.塗抹導電液體:將導電液體塗抹在相同區域; 咖處理:在一輻射室,在足夠的輻射時間内,對 w者物縣面细料線結合臭氧進行輻射處理丨 d.唷塗熱難膠粉末n室中Area; a. Applying cleaning agent: Apply cleaning agent to the object to be adhered. b. Apply conductive liquid: Apply conductive liquid to the same area; Coffee treatment: in a radiation room, in sufficient radiation time, for w The material line of the county is combined with ozone for radiation treatment. 丨d.
面噴塗帶電_熔_於碎物體表 熔站骖叔末,使该熱熔黏膠粉末在靜電力 作用下附著於待黏著區域;及 =猶理··在—加熱㈣,料__膠粉末 輪者區域進行加熱,使熱雜膠粉末炫融。 本發明還提供了一種供完成上述處理方法的處理裝 …’錄置包括-傳送帶,一輻射室,—喷塗室及—加熱 著物體傳 該傳送贡,位於各室的下方,可依序將待黏 6 200840649 送到輪射室,噴塗室及加熱室; 壯該輻射室,位於該傳送帶的上方,該輻射室的上部安 衣有至少—紫外線放射源,其錢上還結合有—臭氧發生 -’精由紫外線結合臭氧對絲著健進行輻射處理; 、該噴塗室,位於該傳送帶的上方,在該噴塗室的上部The surface is sprayed with electricity _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ _ The wheel area is heated to melt the hot glue powder. The invention also provides a processing device for performing the above processing method... 'recording includes-conveyor belt, a radiation chamber, a spraying chamber and a heating object to transmit the transfer tribute, which is located below each chamber, and can be sequentially To be bonded 6 200840649 to the shooting room, spraying room and heating room; strong radiation room, located above the conveyor belt, the upper part of the radiation room is equipped with at least - ultraviolet radiation source, the money is also combined with - ozone generation - 'fine radiation treatment by wire with ultraviolet light combined with ozone; the spray booth is located above the conveyor belt, at the upper part of the spray booth
=—_,該噴輯塗帶電絲_粉末到待黏 者物體表面,在該噴室合適部位安裝有至少一吹風壯置 Γ欠風裝置可麟轉物縣面多餘之__4吹 該加熱室,位於該傳送帶的上方,在該加熱室内設置 置’籍由該加熱裝置產生的熱能使細轉粉末 _^^_理方法及其處理裝置’可以使得熱溶黏 二直=能_喻塗,自動,而不需要作業 了 _業,提高了作軸化程度,降低 力動域,保護了作業人員的人身健康。 【實施方式】 術 針對上述本翻的處理方法及處理裝置所採用的技 ,手段和效果_—錄實_並結合圖式詳細說明如 .一鋪溶轉粉末轉非金屬物縣面的處理方法, 其步驟包括如下,如第1_示: 7 200840649 a•塗抹清潔劑:將清潔劑(市面上可以買到)用刷子 或贺搶等塗抹在絲著非金屬物體,本實施㈣鞋子部件 1表面的待黏著區域11上; b•塗抹導電液體··用刷子或喷槍等將導電液體(市面 上可以買到)塗抹在上述待黏著區域n上,並將該塗袜 好導電液體的鞋子部件〗放置在網格狀傳送帶2上,該傳=—_, the spray coated with wire _ powder to the surface of the object to be glued, at least one blower is installed in the appropriate part of the spray chamber, and the wind is sturdy. Located above the conveyor belt, in the heating chamber, the heat generated by the heating device can be set to enable the finely-turned powder _^^ method and its treatment device to make the heat-melt-adhesive Automatic, without the need for homework, improve the degree of shafting, reduce the force field, and protect the personal health of the workers. [Embodiment] The techniques, means and effects of the above-mentioned processing method and processing apparatus of the present invention are described in detail, and the processing method of the powder-to-non-metallic material county surface is described in detail. The steps include the following, as shown in the first paragraph: 7 200840649 a• Applying a cleaning agent: Applying a cleaning agent (commercially available on the market) with a brush or a rush to a non-metallic object, this embodiment (4) shoe parts 1 The surface of the surface to be adhered to the surface 11; b. Applying a conductive liquid. · Applying a conductive liquid (commercially available on the market) to the area to be adhered by a brush or a spray gun, and the shoes are coated with a conductive liquid. The part is placed on the grid conveyor 2, the pass
2的傳送速度可通過一調速馬達(或驅動 f 調節; °° ^ • C•輻射處理:一輻射室3位於該傳送帶2上方,籍由 該傳送^將鞋子部件1送到輻射室3内,在該輕射^ 3 的上方安裝有至少—料線(uv)放射燈管 例錢設有三個),透過謂賺懷子部件 射處理’為了制更好魄紐果,更可 UV-C紫外 線麵射燈管,在輻射室3還安裝有—臭氧發m,、透 3臭赠生器32為輕射室3提供臭氧,使得爪輕射 六氧環境下餅,叫加鋪縣,躲量可 ;:32進行調整,該鞋卿的待黏著區域η由於經 7=理,其較之未清潔部位,受_輻射效果更顯 鞋以傳运帶2的速細_室3的長度選擇,以保證 t子部件1有足夠的照射時間; h塗熱、雜膠粉末:該熱熔轉粉末可以在一定溫 8 200840649 子聚合物,優選為聚氨酯熱溶轉 仰末’一贺塗室4位於該傳送帶2的上方,籍 2將經過_處理雜子部件1送到該喷塗室 該貝頭41㈣特殊設計能夠使鱗轉粉末粒 作上靜電荷,其可__造,比_Nord膽The conveying speed of 2 can be adjusted by a speed control motor (or drive f; ° ° ^ • C • radiation treatment: a radiation chamber 3 is located above the conveyor belt 2, and the shoe component 1 is sent to the radiation chamber 3 by the transmission At least above the light beam ^ 3 is installed with at least the material line (uv) radiation lamp. There are three kinds of money, and it is processed by the means of making a piece of the baby's parts. Ultraviolet spotlight tube, in the radiation chamber 3 is also installed - ozone hair m, 3 through the smell device 32 to provide ozone for the light shot room 3, so that the claw lightly shot the six oxygen environment cake, called Jiapu County, hiding The amount can be adjusted: 32, the shoe to be adhered to the area η due to 7 = rational, compared with the uncleaned part, the _radiation effect is more obvious, the length of the transport belt 2 is selected as the length of the transport belt 2 To ensure that the t sub-assembly 1 has sufficient irradiation time; h heat-coated, miscellaneous rubber powder: the hot-melt-transferred powder can be at a certain temperature 8 200840649 sub-polymer, preferably polyurethane hot-melt transfer end of the end of a coating chamber 4 Located above the conveyor belt 2, the _ processed miscellaneous component 1 is sent to the spray booth by the 2, and the special design energy of the bead head 41 (4) The powder particles so as scales transferred to the electrostatic charge, which can be made __, gall than _Nord
么司’該噴頭41可連接1氣壓力粉末槽(圖上未示), 2 Γ祕力作用下,該空氣麗力粉末槽可以將熱熔黏膠 4粒子送到該喷頭4卜經該喷頭41充以靜電荷後喷射 到鞋子部件1的表面,由於待黏魏域U塗有導電液體, 在靜電引力作用下,熱_膠粉末牢_黏著在待黏著區 或11上’ 5㈣頭41的噴概速和數量可依轉送帶2的 逮度選擇,以確保齡轉粉末充分覆魏鞋子部件 1表面,在該室4内沿著傳送帶2還設置有至少一吹 氣裝置’本實施例__空氣対42,在雜黏膠粉 ,噴灑到鞋子部件1的表面後,沿傳送帶2通過時,該空 =嘴42可以將鞋子部件丨表面待黏著區域η以外區域 覆蓋的熱溶黏膠粉末吹掉,該空氣噴嘴42通過輸氣管道 421與室外的空氣泵422 (或空壓機)連接,該空氣噴嘴 42的氣流速和數量可依據傳送帶2的速度選擇,其方向 可依據鞋子部件1的位置來調節,以嫁保鞋子部件i的待 200840649 J著區域11 外的區域的熱溶黏膠粉末被徹底清除;為 了使人落到傳送帶2上的熱溶黏膠粉末回收,在該喷塗室 4及雜思帶2的下方設置-粉末回收室43,該回收室 43可通過官道431與空氣壓力粉末槽(圖上未示)連接, 藉真空作用將鱗轉粉末回㈣空氣壓力粉末槽中再 利用;及司司' The nozzle 41 can be connected to a gas pressure powder tank (not shown). Under the action of 2 Γ secret force, the air Lili powder tank can send the hot melt adhesive 4 particles to the nozzle 4 The nozzle 41 is charged with an electrostatic charge and then sprayed onto the surface of the shoe component 1. Since the conductive layer U is coated with a conductive liquid, under the action of electrostatic attraction, the heat-gel powder is firmly adhered to the head to be adhered or the '5 (four) head The speed and number of sprays of 41 can be selected according to the degree of catch of the transfer belt 2 to ensure that the age-transferred powder sufficiently covers the surface of the shoe component 1, and at least one air blowing device is disposed along the conveyor belt 2 in the chamber 4. Example __Air 対42, after the adhesive powder is sprayed onto the surface of the shoe component 1, when passing along the conveyor belt 2, the air=mouth 42 can heat the surface of the shoe component 丨 surface to be adhered to the area η The rubber powder is blown off, and the air nozzle 42 is connected to the outdoor air pump 422 (or air compressor) through the gas transmission pipe 421. The gas flow rate and the number of the air nozzles 42 can be selected according to the speed of the conveyor belt 2, and the direction can be determined according to the shoes. The position of the part 1 is adjusted to marry the shoe part i 200840649 J The hot-melt adhesive powder in the area outside the area 11 is completely removed; in order to recover the hot-melt adhesive powder falling on the conveyor belt 2, a powder is disposed under the spraying chamber 4 and the thought strip 2 a recovery chamber 43 which can be connected to an air pressure powder tank (not shown) through the official passage 431 to transfer the scale powder back to the (IV) air pressure powder tank by vacuum; and
一加熱室5,其位於傳送帶2的上方, 透過該傳送帶2將靜過鱗轉粉末魄子部件〗送到 s六、至5 $ °亥加熱冑5透過紅外線光,直接熱空氣流 或微波加_加熱方法對錄子部件1上的待黏著區域 1曰 1的熱轉膠粉末進行加熱,直錄辆融,本實施例 是在該加熱室5的上方織有紅外線投娜51進行加 熱,該紅外線投射燈51的數量可依據溶融轉粉末所需 的温度及傳送帶2的賴選擇,該加熱室5的溫度可透過 控制紅外概51财_溫度控彻52調整,該溫 度控制器52可絲在該加熱室5 _也抑絲在加教 室5之外’最好錢在加熱室5外,且其與—設置在加執 室5内的溫度感魅53連接來感知溫度,透過該加熱室 5的加熱’該鞋子部件i上的待轉區域u上的熱溶黏膠 财吸收熱能後熔融’成為可用於黏著的一層液體點合割 溥膜。 10 200840649 寺該鞋子部件1的待黏著區域η上的熱溶黏膠粉末 熔融後’該鞋子部件1就可以被傳送帶送去與其他鞋子部 件進行黏合。 /的b步驟也可以通過使用清潔劑和導電液體 的混合物結合在—起成為—個步驟,這樣可以縮短作業過 程’節省作業時間。 透過上述具體的處理方法及其處理装置,可以使得熱 1 _膠縣在各作業室裏自動噴塗,自_:融,而不需要 作業人員直接去手工噴塗作業,提高了作業自動化程度, 降低了勞動強度,也節省了能源;各個健室再加之該處 _ 歧置奴杨錄核_粉相收室,提高了粉末利 用卞’避免了環境受到污染,也保護了作業人員的人身健 康。 Φ 【圖式簡單說明】 第1圖本發明處理裝置之立體示意圖。 11待黏著區域 21馬達 31 UV燈管 4噴塗室 【主要元件符號說明】 1 鞋子部件 2傳送帶 3 輻射室 32臭氧發生器 11 200840649 41喷頭 421輸氣管道 43粉末回收室 5 加熱室 52溫度控制器 42空氣喷嘴 422空氣泵 431管道 51紅外線投射燈 53溫度感應器a heating chamber 5, which is located above the conveyor belt 2, through which the static scale-turned powder tweezers are sent to the s six, to 5 $ ° heating 胄 5 through the infrared light, direct hot air flow or microwave plus The heating method heats the hot-transfer powder of the area to be adhered 1曰1 on the recording unit 1 to directly record the melt. In this embodiment, the infrared ray 51 is woven on the heating chamber 5 for heating. The number of infrared projection lamps 51 can be adjusted according to the temperature required for melting the powder and the temperature of the conveyor belt 2. The temperature of the heating chamber 5 can be adjusted by controlling the infrared temperature, and the temperature controller 52 can be The heating chamber 5_ is also suppressed from being outside the classroom 5, and the best money is outside the heating chamber 5, and it is connected to the temperature sensor 53 disposed in the chamber 5 to sense the temperature through the heating chamber 5. The heating 'the hot-melt adhesive on the part u to be transferred on the shoe part i absorbs the heat energy and then melts' into a layer of liquid-bonded cutting film which can be used for adhesion. 10 200840649 Temple After the hot-melt adhesive powder on the to-be-adhered area η of the shoe component 1 is melted, the shoe component 1 can be sent by the conveyor belt to be bonded to other shoe parts. The step b can also be combined by using a mixture of a cleaning agent and a conductive liquid, which can shorten the work process and save time. Through the above specific treatment methods and processing devices, it is possible to automatically spray the hot 1_Jiao County in each working room, and it does not require the operator to directly go to the manual spraying operation, thereby improving the automation of the operation and reducing the degree of automation. Labor intensity, but also save energy; each health room plus the _ 置 奴 杨 录 录 _ _ powder collection room, improve the use of powder 卞 'to avoid environmental pollution, but also protect the personal health of workers. Φ [Simplified description of the drawings] Fig. 1 is a schematic perspective view of the processing apparatus of the present invention. 11 to be adhered to area 21 motor 31 UV lamp tube 4 spray booth [main component symbol description] 1 shoe component 2 conveyor belt 3 radiation chamber 32 ozone generator 11 200840649 41 nozzle 421 gas pipeline 43 powder recovery chamber 5 heating chamber 52 temperature control 42 air nozzle 422 air pump 431 pipe 51 infrared projection lamp 53 temperature sensor
1212