200539834 五、發明說明(1) 【發明所屬之技術々員g 本發明係有關」種;吏用, 法,尤指一種於金屬容器沖墨成h 處理方 易因微波分子造成火花之尖 ς茭:孟Μ合益'表面容 r中塵成型裁切時於裁切部之金屬容 去除,並於前述表面毛 斤產之穴銳毛邊予以 進而將金屬容器之全屬>面夕,,再進行表面皮骐處理, 金屬表面形成-層皮:表最細孔予以填補平滑,並於 層耐胍材枓,進而可使經處理後之土佈— 爐中以微波加埶(每、4 〃离σ口除7置入微波 燐、兩沪;5 #二 熱)1文用外,其亦可使用於瓦斯 [私爐及烤相加熱使用之目的者。 九斯 【先前技術】 、按、’邑大夕數使用過微波爐之人皆知道,目前 所銷售可使用於微波煻六 〜市面上 料製成.,ι包括:以:二:;大都為陶£及塑勝類材 盧衣k業者在内,均知道金屬定200539834 V. Description of the invention (1) [Technical staff g to which the invention belongs] The present invention is related to "species; method and method, especially a method of processing ink into a metal container to form a h. It is easy to cause sparks due to microwave molecules." : Meng M Heyi's surface volume r The metal content in the cutting part is removed during the shaping and cutting, and the sharp edges of the holes produced by the aforementioned surface hairs are used to further all the metal container's face> Surface skin treatment is performed, metal surface is formed-layer skin: the finest pores on the surface are filled and smoothed, and the layer is made of guanidine-resistant material, so that the treated soil cloth — microwave oven can be used to add water (each, 4 hours) In addition to 7 microwave ovens, Lianghu; 5 # 2 heat) 1 away from the σ mouth, it can also be used for gas [private furnace and baking phase heating purposes. Jiusi [previous technology], press, 'Yi Daxi number anyone who has used a microwave oven knows that the current sale can be used for microwave 煻 26 ~ made of materials on the market., Ι include: to: two :; most are pottery Both the £ and plastic industry players know that metal
^於微波爐中會發生危險,㈣對於-般消費者Γ不 :田,僅知金屬容器不可使用於微波爐中,但卻不知: :之.岛:i匕問題則係因金屬容器於金屬材料經沖壓成型J 屬材料之表面則形成了無數由肉眼,於金 同時金屬容器㈣成型裁切時於裁;;祭之^毛邊, 尖銳毛邊’而此些尖銳毛邊則係為遍C處亦將產生 危險之主要原因,因此,至目前為:波造成火钯而引起 此-問題’且,目前大多數糕餅之穿作尚決 衣作,其均採金屬容器^ Dangers occur in microwave ovens. For ordinary consumers, I do n’t know that metal containers ca n’t be used in microwave ovens, but I do n’t know that:: 之 .Island: The problem is because metal containers are used in metal materials. The surface of the stamping J-shaped material is formed by the naked eye, and it is cut at the same time when the metal container is formed and cut ;; sacrifice burrs, sharp burrs', and these sharp burrs are generated all over C. The main reason for the danger, therefore, until now: the wave caused fire-palladium to cause this problem-and most of the pastry dresses are still made in metal containers.
第5頁 200539834_ 五、發明說明(2) 之外模,而於製造糕餅如蛋糕類食品之前,大都均需將所 使用之金屬容器外模予以預熱至一定温度後,方倒入蛋糕 麵料,因此,此些預熱均需置於烤箱内加以預熱,但此種 預熱方式均因時間較長而造成於製做糕餅時花費較長之時 間,而微波爐之預熱時間短及溫度提升快,因此,若可將 金屬容器置於微波爐中使用,將可解決前述之問題。 【内容】 <所欲解決之技術問題> 本發明人有鑑於上述習知之金屬容器無法使用於微波 爐實周困難及有待改善之缺失,盼能提供一突破性之設 計,以增進實用效果,乃潛心研思、設計組製,綜集其多 年從事相關產品設計產銷之專業技術知識與實務經驗及研 思設計所得之成果,終研究出本發明一種使用於微波爐金 屬容器之處理方法,以使金屬容器亦可使用於微波爐中 者。 <解決問題之技術手段> 為了達到前述之目的,本發明係於金屬容器沖壓成型 後,將金屬容器表面容易因微波分子造成火花之尖銳毛 邊、尖銳凹陷部及金屬容器沖壓成型裁切時於裁切部之斷 面所產生之尖銳毛邊予以去除,並於前述表面毛邊處理 後,再進行表面皮膜處理,進而將金屬容器之金屬表面之 毛钿孔予以填補平滑,並於金屬表面形成一層皮膜,最後 再於金屬容器之表面塗佈一層耐溫材料,進而可使經處理 後之金屬容器除可置入微波爐中以微波加熱(或預熱)使Page 5 200539834_ V. Description of the invention (2) Outer molds. Before manufacturing cakes such as cakes, most of the metal container outer molds need to be preheated to a certain temperature before being poured into the cake fabric. Therefore, all of these preheating needs to be preheated in the oven, but this preheating method takes a long time to make pastry because of the long time, while the microwave oven has a short preheating time and temperature rise Fast, therefore, if the metal container can be used in a microwave oven, the aforementioned problems can be solved. [Content] < Technical problem to be solved > In view of the above-mentioned conventional metal container cannot be used in microwave ovens and the lack of improvement, we hope to provide a breakthrough design to improve the practical effect. It is an intensive research and design system that integrates its many years of professional technical knowledge and practical experience in the design, production and sales of related products, and the results of research and design. Finally, it has developed a method for processing metal containers for microwave ovens in the present invention, so that Metal containers can also be used in microwave ovens. < Technical means to solve the problem > In order to achieve the foregoing object, the present invention is to cut and sharpen the burrs, sharp recesses and sharp recesses of metal containers which are liable to cause sparks due to microwave molecules after the metal containers are press-formed. The sharp burrs generated in the section of the cutting section are removed, and after the aforementioned surface burrs are processed, the surface film treatment is performed to further fill and smooth the burr holes on the metal surface of the metal container, and form a layer on the metal surface. Coating, and finally coating a layer of temperature-resistant material on the surface of the metal container, so that the treated metal container can be placed in a microwave oven for microwave heating (or pre-heating) so that
200539834_ 五'發明說明(3) 闬外,其亦可使用於瓦斯爐、電爐及烤箱加熱使用之目的 者。 <對先前技術之功效> 本發明之主要目的係藉本發明之方法使金屬材料之金 屬容器可於微波爐使用,進而藉由金屬容器具熱傳導性佳 之特性,可達縮短加熱時間之目的者。 為使 貴審查委員能更了解本發明之結構特徵及其功效, 茲配合圖式並詳細說明於后。 【實施方式】 請參閱第一圖、第二圖、第三圖及第四圖所示,本發 明之處理方法其主要於金屬容器(1 )(如第五圖所示) 沖壓成型後,金屬容器(1 )於金屬材料(1 1 )經沖壓 成型(2 )加工之過程中,其金屬材料(1 1 )被外力沖 壓及拉伸展延後,於金屬材料(1 1 )之表面則形成了無 數由肉眼無法觀察之尖銳毛邊(1 2 )及尖銳凹陷部(1 3 ),同時金屬容器(1 )沖壓成型裁切時於裁切部之斷 面將產生之尖銳毛邊(1 2 ),則再將金屬容器(1 )進 行表面毛邊處理(3 ),進而將容易因微波分子造成火花 之金屬表面尖銳毛邊(1 2 )及尖銳凹陷部(1 3 )予以 去除,於表面毛邊處理(3 )後,再進行表面皮膜處理 (4.),進而將金屬容器(1)之金·屬材料(1 1 )表面 之毛細孔予以填補平滑,並於金屬材料(1 1 )表面形成 一層皮膜(1 4 ),最後步驟塗佈耐溫絕緣材料(5 )則 係於金屬容器(1 )之金屬材料(1 1 )表面塗佈一層耐200539834_ Five 'invention description (3) In addition, it can also be used for gas stoves, electric stoves and oven heating purposes. < Effects of the prior art > The main purpose of the present invention is to make the metal container of metal material available in a microwave oven by the method of the present invention, and then the metal container has the characteristics of good thermal conductivity and can shorten the heating time. . In order to make your reviewers better understand the structural features and effects of the present invention, the drawings are described in detail below. [Embodiment] Please refer to the first diagram, the second diagram, the third diagram, and the fourth diagram. The processing method of the present invention is mainly applied to the metal container (1) (as shown in the fifth diagram). When the container (1) is stamped and formed (2) during the processing of the metal material (1 1), the metal material (1 1) is stamped and stretched by external force, and is formed on the surface of the metal material (1 1). Innumerable sharp burrs (1 2) and sharp depressions (1 3) that cannot be observed by the naked eye, and at the same time, the metal container (1) is punched and formed on the cross section of the cutting section during cutting and cutting, Then, the metal container (1) is subjected to surface burr treatment (3), and then the sharp burr (1 2) and sharp depression (1 3) on the metal surface that are easy to cause sparks due to microwave molecules are removed, and the surface burr treatment (3) is performed. ), And then perform a surface film treatment (4.) to further fill and smooth the pores on the surface of the metal container (1) of the metal material (1 1), and form a film on the surface of the metal material (1 1) ( 1 4), the last step is to apply a temperature-resistant insulating material (5) Metal container (1) of metallic material (11) coated with a layer resistant surface
200539834 五、發明說明(4) 溫絕緣材料(1 5 )後即完成,經前述方法處理後之金屬 容器(1 ),除可置入微波爐中以微波加熱(或預熱)使 用外,其亦可使用於瓦斯爐、電爐及烤箱加熱使用,其用 途廣泛,而前述成型後金屬容器(1 )之表面毛邊處理 (3 ) 7其主要係以纟亞瑣酸納將金屬材料(1 1 )表面經 沖壓展延所產生之尖銳毛邊(1 2 )及尖銳凹陷部(1 3 )之尖銳部份予以溶解去除,而表面皮膜處理(4 )之程 序係採用磷鋅皮膜劑將金屬容器(1 )之金屬材料(1 1 )表面之毛細孔予以填補並於其表面形成一皮膜(1 4 ),而最後步驟所塗佈之耐溫絕緣材料(1 5 ),除塗佈 該耐溫絕緣材料(1 5 )外,亦可依所需於每1 0 0 %之 鐵弗龍中加入2 5 %〜3 5 %之耐溫絕緣材料(1 5 ), 除使金屬容器(1 )具耐溫絕緣之特性外,亦兼具不沾鍋 之特性者。 综上所述,本發明方法具提供使金屬材料之金屬容器 可於微波爐使用,進而藉由金屬容器具熱傳導性佳之特 性,可達縮短加熱時間之目的者,為一甚具新I員性及可供 產業上應用之發明,實已符合發明專利之給與要件,爰依 法提出專利申請,尚祈 貴審查委員能詳予審查,並早曰 賜准本案專利,實為德便。200539834 V. Description of the invention (4) The temperature insulation material (1 5) will be completed immediately. The metal container (1) treated by the aforementioned method can be placed in a microwave oven for microwave heating (or preheating) and it can also be used. It can be used for heating gas stoves, electric furnaces and ovens. It has a wide range of uses, and the surface burr treatment of the metal container (1) after forming (3) 7 is mainly based on the surface of metal materials (1 1) with sodium oxalate. The sharp burrs (1 2) and sharp recesses (1 3) produced by stamping and extension are dissolved and removed, and the surface coating process (4) uses a phosphorous zinc coating to place the metal container (1) The pores on the surface of the metal material (1 1) are filled and a film (1 4) is formed on the surface, and the temperature-resistant insulating material (1 5) applied in the last step is not coated with the temperature-resistant insulating material ( 15) In addition, you can also add 25% ~ 35% of temperature-resistant insulation material (1 5) to 100% of Teflon, in addition to making the metal container (1) with temperature-resistant insulation. In addition to its characteristics, it also has the characteristics of non-stick. In summary, the method of the present invention provides a metal container that can be used in a microwave oven, and furthermore, the metal container has good thermal conductivity and can shorten the heating time. The inventions that can be used in the industry have already met the requirements for granting patents for inventions. They have filed patent applications in accordance with the law, and they still pray that the examiners can examine them in detail and grant the patents in this case as soon as possible.
第8頁 200539834 圖式簡單說明 (一) 圖式部份 第一圖係金屬容器於沖壓成型後於其金屬材料表面形成多 數尖銳毛邊及尖銳凹陷部之放大剖示圖。 第二圖係本發明將金屬容器表面之尖銳毛邊及尖銳凹陷部 予以去除後之實施例放大剖示圖。 第三圖係本發明於金屬容器之金屬材料表面以表面皮膜處 理後再塗佈一層耐溫材料之放大剖示圖。 第四圖係本發明處理方法之步驟方塊圖。 第五圖係本發明試舉其中一種沖壓成型之金屬容器之立體 圖。 (二) 圖號部份 (1 )金屬容器 (1 1 )金屬材料 (1 2 )尖銳毛邊 (1 3 )尖銳凹陷部 (14)皮膜 (1 5 )耐溫絕緣材料 (2 )沖壓成型 (3)表面毛邊處理 (4 )表面皮膜處理· (5 )塗佈耐溫絕緣材料Page 8 200539834 Brief description of the drawings (1) Schematic part The first drawing is an enlarged cross-sectional view of a metal container that has formed a number of sharp burrs and sharp depressions on the surface of its metal material after stamping. The second figure is an enlarged sectional view of an embodiment of the present invention after removing sharp burrs and sharp recesses on the surface of a metal container. The third figure is an enlarged cross-sectional view of the surface of the metal container of the present invention after the surface of the metal material is treated with a surface film and then coated with a layer of a temperature-resistant material. The fourth figure is a block diagram of the steps of the processing method of the present invention. The fifth figure is a perspective view of one of the press-molded metal containers of the present invention. (2) Part of the drawing (1) Metal container (1 1) Metal material (1 2) Sharp burr (1 3) Sharp recess (14) Film (1 5) Temperature-resistant insulation material (2) Stamping (3) ) Surface burr treatment (4) Surface coating treatment (5) Coating of heat-resistant insulation material
第9頁Page 9