CN201814368U - Aluminium-steel composite pot - Google Patents
Aluminium-steel composite pot Download PDFInfo
- Publication number
- CN201814368U CN201814368U CN2010205644892U CN201020564489U CN201814368U CN 201814368 U CN201814368 U CN 201814368U CN 2010205644892 U CN2010205644892 U CN 2010205644892U CN 201020564489 U CN201020564489 U CN 201020564489U CN 201814368 U CN201814368 U CN 201814368U
- Authority
- CN
- China
- Prior art keywords
- steel
- pot
- aluminium
- pot body
- pan
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model relates to an aluminium-steel composite pot which comprises an aluminium pot body and a steel pot bottom piece, and is characterized in that a contact surface between the aluminium pot body and the steel pot bottom piece is provided with a steel and aluminum penetration fusion layer. The aluminium-steel composite pot has the beneficial effects that the aluminium pot body and the steel pot bottom are firmly compounded with each other, and the technique process is simple, so that the aluminium-steel composite pot is suitable for large batch production; and the production process has the advantages of energy conversation and emission reduction, so that the aluminium-steel composite pot is better in accordance with the requirements of environmental protection.
Description
Technical field
The utility model relates to a kind of cooker pot field, and particularly a kind of pot bottom has the pot of steel aluminium infiltration fused layer.
Background technology
As everyone knows, the pot of metal is as the main tool of heated food, and the thermal conducting function of aluminum pot is far longer than the steel pot, but aluminium cooker body intensity is limited, and the method for the inapplicable electrical induction of generally using now, so everybody hankers after designing at the bottom of the various aluminum steel compound pot very much.For example Chinese patent CN201227154Y relates to be a kind of aluminum pot compound pot at the bottom of, be compositely fixed with permeability magnetic material on the bottom of a pan of aluminum pot, it is characterized in that: the bottom of a pan of described aluminum pot is provided with convex tendon, and convex tendon is with zoning territory, the bottom of a pan, and permeability magnetic material is fixed in each zone by the high-temperature metal spraying.Owing to be compositely fixed with permeability magnetic material on the bottom of a pan, it can be implemented in electromagnetic stove and use.The disadvantage of this structure is that permeability magnetic material is a convex tendon, is not the structure of full wafer, therefore exists to be subjected to the long-pending little and dispersion of magnetic surface, causes the problem of heating efficiency difference.
Disclosed a kind of method of making composite-bottom steel-aluminum pot of Chinese patent CN101028668A and products thereof and for example.Earlier make steel-aluminum pot by steel-aluminum composite plate, inwall simultaneously is a steel disc; Superimposed superimposed with the aluminium flake in the bottom of a pan again with aluminium-magnetic conductive metal sheet, spot welding links into an integrated entity, and the high temperature heating is placed on the pressure welding of carrying out HTHP on the large-tonnage friction press, obtain steel-aluminium-four layers of compound composite-bottom steel-aluminum pot of aluminium-magnetic conductive metal, its base thickness is greater than the pot wall thickness.Be characterized in the complex welding synthermal heating in back with various metals, carry out the high temperature pressure welding again, this patent has solved the little problem of heating surface area, but because aluminium is different with the thermal expansion factor of steel, may cause each layer metal not fuse effectively after the compacting cooling, influence the problem of compound pot body firmness.
Also have Chinese patent CN101352305A utility model to relate to a kind of aluminium alloy compression casting pan with compound bottom.It comprises aluminium alloy compression casting pan pot body, stainless iron compound bottom sheet, is characterized in the direct and smooth compound one that is of bottom of pot body of stainless iron compound bottom sheet.The utility model also relates to the combination process of above-mentioned aluminium alloy compression casting pan with compound bottom.This combination process is to make aluminium alloy compression casting pan with compound bottom through steps such as die casting, cleaning surfaces, coating complexing agent, paster, precompressed, compound, pressurize cooling, surperficial subsequent treatment.This technology is more reasonable, and it is to pass through induction coil in compound process, and aluminium is heated to 450-630 ℃, and the duration is 40-45s, makes aluminium combine with the stainless iron compound bottom sheet, and such process time is oversize, is unfavorable for producing in enormous quantities; Because each part pot body all is independent heating, so the energy resource consumption height, is unfavorable for environmental protection, and the equipment complexity; The melt temperature of aluminium is 660 ℃ as you know, and therefore heat influences aluminum ions diffusion velocity to 450-630 ℃ of aluminum ions active deficiency, and the firmness of product is not high enough.
Summary of the invention
The utility model will solve the not high problem of traditional handicraft steel aluminium multiplicity, and a kind of aluminum steel compound pot is provided, and its steel aluminium composite surface steel aluminium ion can fully fuse, and firmness is stronger.
The technical scheme that its technical problem that solves the utility model adopts is: the aluminum steel compound pot that a kind of aluminium matter the bottom of a pan is provided: comprise pot body, the steel the bottom of a pan sheet of aluminium matter, it is characterized in that: the pot body of described aluminium matter and the contact-making surface of steel the bottom of a pan sheet have steel aluminium infiltration fused layers.Aluminium matter pot body is heated to 400~500 ℃, and steel the bottom of a pan sheet is heated to 780-820 ℃, with both rolling combinations on friction press or hydraulic press, and cooling naturally after the rolling end.780-820 ℃ steel the bottom of a pan sheet contacts under forcing press with the surface of 400~500 ℃ aluminium matter pot body, because the two has the temperature difference of 300-400 ℃ of degree, and the heat conductivility of aluminium is fine, be raised to more than the melting temperature of 660 ℃ of degree and 800 ℃ rapid combination of active steel ion in the aluminum ions temperature of contact-making surface so at once, formed the steel aluminium infiltration alloy film of contact-making surface; Because steel the bottom of a pan sheet thinner thickness, thermal capacity is limited, adds the perfect heat-dissipating of aluminium, and the aluminium surface surpasses 660 ℃ high temperature, just form in the part, and the time of effect is very short, therefore can not exert an influence to aluminium matter pot body; The cooling naturally of rolling end back because the temperature height of steel can reduce pot cooling velocity of body aluminum component, reduces contraction distortion; Through at the bottom of the steel aluminium compound pot of this processing technology moulding, its firmness is higher, because process velocity is fast, is more suitable for producing in enormous quantities.
For stretched aluminium matter pot body, described heating-up temperature is 450-500 ℃.Because aluminium matter pot body is stretched, its rigidity increases, so heating-up temperature selects the upper limit relatively good.
For the aluminium matter pot body through die casting, described heating-up temperature is 400-450 ℃.Because the aluminium matter pot body rigidity of die casting is relatively low, so be limited to good under the heating-up temperature selection.
As preferably, the upper surface of steel the bottom of a pan sheet is shot-peening or frosted.Coarse steel surface more helps aluminum ions infiltration combination.
As preferably, the lower surface of aluminium matter pot body adopts shot-peening or frosted or is processed into annular corrugated or spiral lamination.The aluminium ion of rough surface more helps fusion.
As preferably, steel the bottom of a pan sheet is a basin shape stage body.The compound egative film of steel can be fully around the aluminium matter the bottom of a pan that encases easy deformation in pressing process like this, thereby has guaranteed the shape of rolling back pot body, has improved the rigidity and the intensity of the bottom of a pan appearance.
As preferably, the pot body of aluminium matter is a flat bottom cooker.
As preferably, the pot body of aluminium matter is a digester.
The beneficial effect that the utlity model has is: the bottom of a pan of pot body and the steel of aluminium matter compound firmly and technical process simple, be suitable for production in enormous quantities; Production process energy-saving and emission-reduction, more compliance with environmental protection requirements.
Description of drawings
Fig. 1 is a kind of pot of body cutaway view of the utility model;
Fig. 2 is the partial view of a kind of bottom of pot body of the utility model;
Fig. 3 is a kind of steel of the utility model the bottom of a pan sheet cutaway view;
Fig. 4 is the cutaway view of flat bottom cooker at the bottom of a kind of aluminum steel compound pot of the utility model;
Fig. 5 is the vertical view of flat bottom cooker at the bottom of a kind of aluminum steel compound pot of the utility model;
Fig. 6 is the cutaway view of digester at the bottom of a kind of aluminum steel compound pot of the utility model;
Fig. 7 is the partial view of digester bottom of pot body at the bottom of a kind of aluminum steel compound pot of the utility model;
The specific embodiment
Below in conjunction with specific embodiment, further set forth the utility model.
Embodiment 1
A kind of frying pan of the compound end of aluminum steel of aluminium matter pot, comprise aluminium matter pot body 10 and steel the bottom of a pan sheet 20 compositions, aluminium matter pot body 10 is for having the square stretching pot body of fillet, the bottom is outstanding Rotary-table, the outer surface of Rotary-table has tiny helical ripple 11, the inner surface in aluminium matter pot body 10 thes bottom of a pan has wavy projection, and the lateral surface of aluminium matter pot body 10 is equipped with handle; Steel the bottom of a pan sheet 20 is a spill stretching Rotary-table, the Rotary-table coupling of the interior shape of Rotary-table and aluminium matter pot body 10, and the inner surface of Rotary-table is through frosted processing layer 21, referring to accompanying drawing 1,2,3;
The aluminum steel combination process in a kind of aluminium matter the bottom of a pan comprises:
1) aluminium matter pot body 10 is preheated to 480 ℃;
2) steel the bottom of a pan sheet 20 is preheated to 810 ℃;
3) the steel the bottom of a pan sheet 20 of heating is placed on the bottom of aluminium matter pot body 10, rolling combination on 1000 tons friction press, the inner surface that patrix suppresses the bottom of a pan simultaneously has wavy projection, improves the density of the bottom of a pan aluminium alloy, cools off naturally in room temperature after the rolling end.Aluminium matter pot body 10 and the fusion of steel the bottom of a pan sheet 20 surface seepages form infiltration fused layers 30 under HTHP, reach aluminium matter pot body 10 and steel the bottom of a pan sheet 20 adeciduate effects, referring to accompanying drawing 4,5.
Embodiment 2
A kind of digester of the compound end of aluminum steel of aluminium matter pot comprises that aluminium matter pot body 40 and steel the bottom of a pan sheet 20 form, and aluminium matter pot body 40 is a column tubular compression casting pan body, and the outer surface of bottom has tiny by annular corrugated 13; Steel the bottom of a pan sheet 20 is a spill stretching Rotary-table, the column tubular compression casting pan body coupling of the interior shape of Rotary-table and aluminium matter pot body 40, and the inner surface of Rotary-table is through bead layer 21, referring to accompanying drawing 6,7;
The aluminum steel combination process in a kind of aluminium matter the bottom of a pan comprises:
1) the aluminium matter pot body 40 to die casting is preheated to 430 ℃;
Other operation is identical with embodiment 1, repeats no more here.
The product that this processes is come out, can be by cold and hot test: the frying pan of the compound end that will process burns 200 ℃ of degree on naked light, the cold water of putting into 20 ℃ of degree of water temperature at once cools off, and does not come off for 25 times repeatedly.
Specific embodiment described herein only is that the utility model spirit is illustrated, the utility model person of ordinary skill in the field can make various modifications or replenishes or adopt similar mode to substitute described specific embodiment, but can't depart from spirit of the present utility model or surmount the defined scope of appended claims.
Claims (6)
1. aluminum steel compound pot comprises pot body, the steel the bottom of a pan sheet of aluminium matter, and it is characterized in that: the pot body of described aluminium matter and the contact-making surface of steel the bottom of a pan sheet have steel aluminium infiltration fused layers.
2. a kind of aluminum steel compound pot according to claim 1 is characterized in that: the lower surface of described aluminium matter pot body is shot-peening or frosted or annular corrugated or spiral lamination structure.
3. a kind of aluminum steel compound pot according to claim 1 is characterized in that: the upper surface of described steel the bottom of a pan sheet adopts shot-peening or frosted to handle.
4. a kind of aluminum steel compound pot according to claim 1 is characterized in that: described steel the bottom of a pan sheet is a basin shape stage body.
5. according to claim 1 or 2 or 3 or 4 described a kind of aluminum steel compound pot, it is characterized in that: the pot body of described aluminium matter is a flat bottom cooker.
6. according to claim 1 or 2 or 3 or 4 described a kind of aluminum steel compound pot, it is characterized in that: the pot body of described aluminium matter is a digester.