SU992554A1 - Method for removing coatings

Info

Publication number: SU992554A1
Application number: SU802973032A
Authority: SU
Inventors: Ольга Исаевна Гончарова; Юрий Николаевич Шлык
Original assignee: Камчатский Филиал Дальневосточного Технического Института Рыбной Промышленности И Хозяйства "Дальрыбвтуз"
Priority date: 1980-08-15
Filing date: 1980-08-15
Publication date: 1983-01-30

Description

Изобретение относитс к химии и может быть использовано в жест нобаночном производстве дл удалени лакокрасочного покрыти с отбракованной пищевой жести в цел х ее повторного использовани при изготовлении банно-тары.The invention relates to chemistry and can be used in the cans industry to remove the paint and varnish from the discarded food tin for the purpose of its reuse in the manufacture of bath containers.

Среди разнообразных материалов, используемых дл изготовлени тары в консервной промышленности, значительное место занимает пищева (белай ) жесть. Последнюю дл увеличени сроков хранени консервов подвергают лакированию. Ввиду сложности процесса лакировани незначительные отклонени от режимов его привод т к браку . Повторное использование бракованной жести требует удалени некачественного , покрыти .Among the various materials used for the manufacture of containers in the canning industry, food (bely) tin occupies a significant place. The latter is varnished to increase the shelf life of canned foods. Due to the complexity of the varnishing process, minor deviations from its modes lead to marriage. Reuse of defective tin requires removal of poor-quality coating.

Известен способ fl дл удалени лакокрасочного покрыти с металлических поверхностей путем обработки растворе, включающим-следующие компоненты при соотношении, вес.%There is a known method fl for removing paintwork from metal surfaces by treating a solution comprising the following components at a ratio, wt.%

Моноэтиловый эфир этиленгликол 20-.50Ethylene glycol monoethyl ether 20-.50

Едкий натрий10-20Caustic sodium 10-20

. Вторичный алкилсульфат0 ,05-0,5. Secondary alkyl sulfate0.05-0.5

ВодаОстальноеWaterEverything

Известен контрольный способ С2 удалени лаковой.пленкн с пищевой жести с целью определени толарсны сло лака.Согласно этому способу лакированную жесть обрабатывают составом: КаОН 100 г, растворитель 30400 мл, Н2О до ЮС О М71.A control method for removing lacquer film C2 from food tin is known in order to determine the tolarsny varnish layer. According to this method, the varnished tin is treated with the following composition: CaOH 100 g, solvent 30400 ml, H2O to JU O M71.

Общим недостатком известных способов вл етс присутствие щелочных A common disadvantage of the known methods is the presence of alkaline

10 компонентов, действие которых нарушает целостность олов нного пода что приводит к частичному сн тию сло олова. Даже если считать, что процент сноса олова и не велик, 10 components whose action violates the integrity of the tin hearth, which leads to a partial removal of the tin layer. Even if we assume that the percentage of demolition of tin and not great

15 тем не менее при толщине олов нного пода 10-14 мкр существует опасность местного нарушени олов нного покрыти , что способствует образованию гальванической пары олово-железо, 15 nevertheless, with a tin thickness of 10-14 microns, there is a danger of local disruption of the tin coating, which contributes to the formation of a tin-iron galvanic couple,

20 по влению окислов железа, быстрому протеканию электрохимической коррозии .20 the appearance of iron oxides, the rapid course of electrochemical corrosion.

Это исключает использование очищенной от лака пищевой жести дл пов This eliminates the use of peeled food tin for cooking.

25 торного лакировани .25 latex varnishing.

Наиболее близким к предлагаемому по технической сущности вл етс способ удалени покрытий с поверхности деталей путем обработки по30 верхности 10-15%-HtM аодньм раствором фенола при 70-80 0 в течение 1,5-2 ч. Далее детали промывают в холодной, а затем в гор чей воде и обезжиривают СЗЗ. Недостатком данного способа вл етс неполное (из-за присутстви воды) удаление лаков и эмалей, примен емых дл покрыти пищевой жести , например ФЛ-560, ФЛ-559, ЭП-527 ЭП-547, ЭП-947, ЭП-5147, ФЛ-5159. При обработке известньм растворе перечисленных покрытий имеет место только ограниченное набухание полимерной пленки. Дл полного удалени пленки с поверхности необходима жестка механическа обработка, при которой возникает опасность повреждени олов нного покрыти . Дальнейш повторное использование такой жести практически невозможно дл пищевых целей. Цель изобретени - возможность удалени покрытий с пищевой жести без повреждени поверхности же.сти и уменьшение времени удалени покрыти Поставленна цель достигаетс тем, что согласно способу удалени покрытий с поверхности изделий путе обработки их при нагревании смывкой на основе 10-15%-ного раствора фено ла в растворителе в качестве раство рител используют диметилсульфоксид С целью интенсификации процесса удалени покрытий в состав смывки ввод т поверхностно-активное вещест во, выбранное из группы, включающей стеарат натри , синтетическое моющее средство Лотос на основе алкилсульфатов и алкил.бензосульфонатов в когмчестзе 1,9-2,1 г на 100 г смывки. Кроме того, обработку изделий смывкой осуществл ют в присутствии ультразвука. Синтетическое моющее средство Ло тос представл ет собой (МРТУ 18-313 69) смесь, вес.%: Пав (алкилсульфаты, .алкилбензолсульфонаты, мыло,дне,неионогенные) Не менее Моноэтанола;миды Не более Карбоксиметилцеллюлоза1 Силикат натри в пересчете на SiO2 Не меt«ее 0,5 Триполифосфат нат- . Не мери нее 42,0 Оптический отбеливатель0 ,1-0,3 Отдушка 0,1 Не более Сульфат натри техническийДо 100 Использование интенсификаторов процесса повышает эффективность очистки: под действием омыл ющих добавок процесс набуха 1и протекает более активно, применение ультразвука ускор ет разрушение лакокрасочного покрыти вследствие вибрации раствора , причем эмалевые покрыти разрушаютс эффективней, чем лаковые. Способ осуществл етс следующим образом. Раствор приготовл ют при комнатной температуре 18-20 С путем растворени кристаллов фенола в диметилсульфоксиде . концентраци раствора берётс в пределах 10-15%. Дл повышени эффективности очистки примен ют интенсификаторы процессаj омыл ющие добавки или ультразвук. Метод обработки - окунание. Листы жести погружают в ванну с раствором и производ т подогрев до температуры, при которой происходит активное набухание и отслоение пленки. Температура зависит от марки покрыти . В случае использовани в качестве интенсификатора процесса ультразвука , подогрев раствора органической смывки не нужен, так как процесс Обработки ультразвуком (УЗК) сопровождаетс повышением температуры раствора. Пластины выдерживают в рабочем растворе, после чего их извлекают и удал ют оставшую от поверхности жести пленку. Врем выдержки в растворе зависит от марки, пленочного покрыти . Удаление достигаетс встр хиванием,струйной обработкой или легким протиранием поверхности жести м гкой щеткой. Затем жесть промывают последовательно холодной и гор чей водой. Перед повторным лакированием поверхность пищевой жести обезжиривают. Пример 1. Провод т обработку пищевой жести, покрытой лаком марки ФЛ-559. Основу лака составл ют ксиленоформальдегидна , эпоксифенольна и алкидноэпоксидна смолы. Раствор фенола в диметилсульфоксиде приготавливают при 18-20°С в i соотношении 1:10. Дл данной марки лака такое соотношение вл етс оптимальным, так как при большей концентрации эффект не улучшаетс , при меньшей концентрации набухание .пленки протекает медленнее и слабее. В ванну с раствором добавл ют , омыл ющие добавки в весовом соотношении 1:50. В качестве омыл ющих добавок используют стеарат натри или CMC Лотос. Пластину погружают в ванну с раствором и подогревают. Дл лака марки ФЛ-559 врем выдержки в растворе пропорционально температуре нагревани и составл ет:The closest to the proposed technical essence is the method of removing coatings from the surface of parts by treating the surface of 10-15% -HtM with an aqueous solution of phenol at 70-80 0 for 1.5-2 hours. Then the parts are washed in a cold and then in the hot water and degrease the SPZ. The disadvantage of this method is the incomplete (due to the presence of water) removal of varnishes and enamels used to cover foodstuffs, for example FL-560, FL-559, EP-527 EP-547, EP-947, EP-5147, FL -5159. When processing a limestone solution of the above coatings, only limited swelling of the polymer film takes place. To completely remove the film from the surface, a hard mechanical treatment is necessary, with which there is a risk of damage to the tin coating. Further reuse of such tin is practically impossible for food purposes. The purpose of the invention is the ability to remove coatings from food tin without damaging the surface of the same and reducing the removal time of the coating. The aim is achieved in that according to the method of removing coatings from the surface of products by treating them with a wash based on 10-15% solution of foil in a solvent, dimethyl sulfoxide is used as a solvent. In order to intensify the process of removing coatings, a surface-active substance selected from the group including sodium stearate, synth matic detergent Lotus based on alkyl sulphates and alkil.benzosulfonatov in kogmchestze 1.9-2.1 g per 100 g of washing. In addition, the processing of the products by washing is carried out in the presence of ultrasound. Synthetic detergent Lotos is (MRTU 18-313 69) mixture, wt.%: Pa (alkyl sulfates, alkyl benzene sulfonates, soap, bottoms, non-ionic) Not less than Monoethanol; mida No more than Carboxymethylcellulose 1 Sodium silicate in SiO2 Not more than "Its 0.5 Tripolyphosphate nat-. Not more than 42.0 Optical bleach0, 1-0.3 Perfume 0.1 Not more Technical sodium sulphate Up to 100 Using process intensifiers increases the cleaning efficiency: under the action of scrubbing additives, the process of swelling 1 and more active, the use of ultrasound accelerates the destruction of the paintwork due to the vibration of the solution, the enamel coating being destroyed more effectively than the lacquer. The method is carried out as follows. The solution is prepared at room temperature 18-20 ° C by dissolving phenol crystals in dimethyl sulfoxide. the concentration of the solution is taken in the range of 10-15%. Scrubbing agents or ultrasound are used to increase the cleaning efficiency. Processing method - dipping. Sheets of sheet metal are immersed in a bath with a solution and heated to the temperature at which active swelling and peeling of the film occurs. The temperature depends on the type of coating. In the case of using ultrasound as an intensifier, the heating of the organic wash solution is not necessary, since the Ultrasonic Treatment (UT) process is accompanied by an increase in the temperature of the solution. The plates are kept in the working solution, after which they are removed and the film remaining from the surface of the tin is removed. The exposure time in solution depends on the brand, film coating. Removal is achieved by shaking, blasting or lightly rubbing the surface of the tin with a soft brush. Then the tin is washed successively with cold and hot water. Before re-varnishing, the surface of food tin is degreased. Example 1. The treatment of food tin coated with FL-559 varnish. The lacquer base is composed of xylenformaldehyde, epoxyphenol and alkyd resin. A solution of phenol in dimethyl sulfoxide is prepared at 18–20 ° C in a ratio of 1:10. For this type of lacquer, this ratio is optimal, since at higher concentrations the effect does not improve, at lower concentrations the swelling of the film proceeds slower and weaker. Smearing additives are added to the bath with the solution in a weight ratio of 1:50. Sodium stearate or CMC Lotus is used as scrubbing agents. The plate is immersed in a bath with a solution and heated. For the FL-559 varnish, the exposure time in solution is proportional to the heating temperature and is:

Температура,с Врем выдержки,Temperature, with a holding time,

минmin

60206020

805-8805-8

iOO2-3iOO2-3

Если в качестве интенсификатора примен ют УЗК, подогрев раствора фенола в диметилсульфоксиде излишен так как. процесс обработки сопровождаетс повышением температуры раствора до . Обработку ультразвуком производ т с частотой 35 кГц. Врем выдержки в растворе 1,5-2 мин Отставшую пленку, удал ют встр хиванием .If ultrasonic testing is used as an intensifier, heating the phenol solution in dimethyl sulfoxide is superfluous since. The treatment process is accompanied by an increase in the temperature of the solution to. The sonication is performed at a frequency of 35 kHz. Holding time in the solution for 1.5-2 minutes. The backing film is removed by shaking.

Пример 2. Провод т обработ|Ку пищевой жести, покрытой эмалью марки ЭП-5147. Основу эмали составл ет лак ЭП-547, который включает эпоксидную смолу ЭД-5 и фенолформальдегидную ФПД-1. Усиленна адгези эмалевого покрыти требует повышени процентного содержани фенола в органической смывке. Дл работы используют 15%-ный раствор фенола в диметилсульфоксиде. В него добавл ют стеарат натри или CMC Лотос в весовом соотношении 1:50. Пластину погружают в ванну с раствором и нагревают до температуры кипени органической смывки. Врем выдержки в кип щем растворе дл эмали ЭП-5147Example 2. Conducted processed | Ku food tin, covered with enamel brand EP-5147. The basis of enamel is EP-547 lacquer, which includes ED-5 epoxy resin and phenol formaldehyde FPD-1. Enhanced adhesion of the enamel coating requires an increase in the percentage of phenol in the organic remover. For work using a 15% solution of phenol in dimethyl sulfoxide. Sodium stearate or CMC Lotus is added in a weight ratio of 1:50. The plate is immersed in a bath with a solution and heated to the boiling point of an organic wash. Exposure time in boiling solution for EP-5147 enamel

составл ет 15-20 мин.Затем пластину иэвл5екают. Отставшую пленку удал ют струйной обработкой или протиранием м гкой щеткой..is 15-20 minutes. Then the plate is 5 times. The loose film is removed by blasting or brushing with a soft brush.

Если в Ka4ectBe интенсификатора примен ют УЗК, то раствор не подогревают . При обработке УЗК частотой 35 КГЦ температура раствора от комнатной повышаетс до . Этой температуры при наличии вибрации If ultrasonic testing is used in Ka4ectBe intensifier, then the solution is not heated. When processing the ultrasonic frequency of 35 KHZ, the temperature of the solution from room temperature rises to. This temperature in the presence of vibration

o раствора достаточно дл отслоени полимерной пленки. Причем эффект отслоени эмалей в отличие от лаков при обработке УЗК значительно выие, чем при использовании омыл ющих до5 бавок.o the solution is enough to peel off the polymer film. Moreover, the effect of peeling enamels, in contrast to lacquers, when processing UT is much higher than with the use of washing up to 5 batches.

Врем выдержки составит 5-7 мин.Exposure time will be 5-7 minutes.

Пример 3. Провод т обработку пластин пищевой жести с эмалевьй (ФЛ-5159) и лаковым (ЭП-547) покрыти ми .Example 3. Conducting processing of plates of food tin with enamel (FL-5159) and lacquer (EP-547) coatings.

00

Эмаль ФЛ-5159 изготовлена на основе лака ФЛ-559, в состав которого вход т ксиленоформальдегидна , эпоксидна и алкидноэпоксидна смолы. 5 В основу лака ЭП-547 вход т эпоксидна и фенолформальдегидна смолы. Удаление пленочного покрыти провод т 12%-ным раствором фенола в диметилсульфоксиде . О&ш ющие добавки берутс в весовом соотношении It50.The enamel FL-5159 is made on the basis of the varnish FL-559, which includes xylene formaldehyde, epoxy, and alkyd-epoxy resins. 5 EP-547 lacquer is based on epoxy and phenol formaldehyde resins. Removal of the film coating is carried out with a 12% solution of phenol in dimethyl sulfoxide. O & supplements are taken in a It50 weight ratio.

Данные по очистке сведены в табл.1.Data cleaning are summarized in table 1.

Таблица 1Table 1

В табл.2 представлены режимы обработ1си лгисированной жести органической смывкой.в присутствии инбез . них до Table 2 presents the modes of processing of tinned sheet with an organic remover. In the presence of in-beam. them up

полполимерногоhalf polymer

6060

В приведенных примерах в качестве интенсификаторов процесса использованы: дл лака ФЛ-559 - стеарат нат ри , дл лака ЭП-547 - CMC Лотос.In the examples given, the following were used as process intensifiers: for varnish FL-559 — sodium stearate, for varnish EP-547 — CMC Lotus.

Из табл.2 видно, что процесс удалени лаковой пленки раствором феТаблица 2From Table 2 it can be seen that the process of removing a varnish film with a feTel 2 solution

нола в ДМС при протекает быстро и без эмульгаторов.Nola in LCA when flows quickly and without emulsifiers.

В табл.3 показано действи известно и предлагаемого способов на пластины лакированной белой жести.Table 3 shows the known effect and the proposed methods on plates of varnished tinplate.

гТаблицаЗTablespace

Claims

' Claim

1. The method of removing coatings from the surface of products by treating them when heated with a wash based on a 10-15% solution of phenol in a solvent, characterized in that, in order to be able to remove coatings from food sheet without damaging the surface of the sheet and reduce the time of removal of coatings, dimethyl sulfoxide is used as a solvent.

2. The method of pop, 1, characterized in that in order to intensify the process of removing coatings, a surfactant selected from the group consisting of sodium stearate, a synthetic detergent Lotus based on alkyl sulfates and alkylbenzenesulfonates in an amount of 1.92 is introduced into the wash composition, 1 g per 100 g of washing.

3, The method of π. 1, which is related to the fact that, in order to intensify the process of removing coatings, heating is carried out when the ultrasound is washed off.