SU979476A1 - Adhesive - Google Patents
Adhesive Download PDFInfo
- Publication number
- SU979476A1 SU979476A1 SU813305373A SU3305373A SU979476A1 SU 979476 A1 SU979476 A1 SU 979476A1 SU 813305373 A SU813305373 A SU 813305373A SU 3305373 A SU3305373 A SU 3305373A SU 979476 A1 SU979476 A1 SU 979476A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- glue
- adhesive
- fraction
- polyethylene glycol
- water
- Prior art date
Description
изобретение относитс к производству клеев и может найти применение в химической промышленности при производстве клеев дл нанесени на бумажную основу при изготовлении клеевых лент, этикеток, марок, обоев .The invention relates to the production of adhesives and can be used in the chemical industry in the production of adhesives for application to paper base in the manufacture of adhesive tapes, labels, brands, wallpaper.
Известна клеева композици , включающа Костный клей, глицерин, карбамид и водуС .A known adhesive composition comprising Bone glue, glycerin, urea and water.
Композици после высушивани на бумаге-основе и при последующем увлажнении обладает, длительным временем схватывани с субстратом.The composition, after drying on a base paper and upon subsequent moistening, has a long setting time with the substrate.
Наиболее близким к изобретению по технической сущности и достигаемому результату вл етс клей, включающий декстрин, костный клей, глицерин/ .пропанол и J.The closest to the invention to the technical essence and the achieved result is glue, including dextrin, bone glue, glycerin / propanol and J.
Известный клей после увлажнени обладает длительным временем схватывани , в св зи с чем его невозможно примен ть на высокопроизводительных обандероливающих автоматах.The known glue after moistening has a long setting time, and therefore it cannot be used on high-performance wrapping machines.
Целью изобретени вл етс уменьшение времени схватывани с субстратом .The aim of the invention is to reduce the setting time for the substrate.
Поставленна цель достигаетс тем, что клей, включающий костный клей и воду, дополнительно содержит высшие спирты фракции Ц,-С и полиэтилен гликоль при следующем соотношении компонентов, вес.%:The goal is achieved by the fact that the glue, including bone glue and water, additionally contains higher alcohols of the C, -C fraction and polyethylene glycol in the following ratio of components, wt.%:
Костный клейBone glue
(на сухое вещество) 25-60(dry basis) 25-60
Высшие спирты фракцииHigher alcohols fraction
С о-С-гб0,05-8,0С о-С-гб0,05-8,0
Полиэтиленгликоль 0,10-15,0Polyethylene glycol 0.10-15.0
ВодаОстальноеWaterEverything
10ten
Клей готов т следующим образом.The adhesive is prepared as follows.
В реактор загружают воду и костный клей, нагревают до 50-70°С и перемешивают в течение 2-4 ч до получени однородной массы. Затем снижают температуру до 35-45°С и при перемешивании добавл ют высшие спирты фракции ,и Полиэтиленгликоль в виде 60%-ного водного раствора. Клей перемешивают 10-100 мин в эави20 скглост от количества добавки.Water and bone glue are loaded into the reactor, heated to 50-70 ° C and stirred for 2-4 hours until a homogeneous mass is obtained. Then the temperature is reduced to 35-45 ° C and the higher alcohols of the fraction are added with stirring, and polyethylene glycol in the form of a 60% aqueous solution. The glue is mixed for 10-100 minutes in a 20 skglost on the amount of additive.
Состав кле по примерам 1-3 представлен в табл.1.The composition of the glue in examples 1-3 are presented in table.1.
Свойства кле приведены в табл.2.The properties of the adhesive are given in table 2.
2525
Из табл.2 видно, что клей по примерам 1-3 обладает уменьшенным временем схватывани .From table 2 it can be seen that the glue in examples 1-3 has a reduced setting time.
Применение кле позвол ет повысить производительность труда, ме30 ханизировать процесс склеивани .The use of glue allows to increase labor productivity, to mechanize the process of gluing.
Таблица 1Table 1
Claims (1)