Description

The invention relates to household chemicals, in particular, to polishing emulsion compositions intended for the care of leather footwear. A composition for imparting skin shine and softening, containing montan wax, mineral spirits, indene coumarin resin, turpentine and primary product alcohols of synthetic fatty acids C-CjjjflJ Specified, the composition does not give sufficient footwear. A leather shoe polishing compound that is known to contain a film-forming substance — montan-wax bleached, polyethylene oxidized wax, paraffin, diethylethanolamine, a dye, white spirit, and water 12. However, this composition is characterized by a relatively low gloss of the shoe and insufficient storage stability. The aim of the invention is to increase the shine of the shoe and increase the stability of the polishing composition. The goal is achieved by the fact that a known composition containing a film-forming substance, oxidized polyethylene wax, paraffin, diethylethanolamine, a dye, white alcohol and WNE, as a film-forming substance contains a product of etherifying high molecular weight fatty acid monoethanol amides of synthetic fatty acids of the fraction additionally contains a fragrance The following ratio of components, wt.%: Film-forming substance6-18 Polyethylene oxidized wax1-4 Paraffin 5-13 Diethylethanolamine 1-4 Dye 0.05-2.0 W.t-spirit 20-45 From abalone 0.1-1.0 Water the rest as oxidized polyethylene wax polishing composition co. keeps wax grade GShO-200. When it is necessary to obtain a colored polishing composition, known dyes are added to its composition. Synthetic wax has the following characteristics: acid number 14.0 mg KOH / G, deposit number 114.8 mg. (Jg) H / r, dropping temperature 70 ° C, penetration 100 g / 5 s. The invention is confirmed by examples of specific performance.

The polishing composition is prepared as follows.

In the reactor, equipped with a stirrer and heated, load the prescription amount of wax and wax-like substances. i The mixture is melted at 110IIS C. After the molten mixture, the calculated amount of solvent and

incubated for 10 minutes, add diethypethanolamine and mix for 20 minutes. Then, water heated to 90-95 ° C is added in small portions, stirred for 15-20 minutes and the dye is added. The mixture is cooled to 40-4 ° C, perfume is added and poured into molds.

The formulations of polishing compounds of examples 1-3 are given in table 1.

Table 1

The properties of the proposed polishing, 35 th composition for each recipe in

Known (prototype) 12

0.7

Offered by example 1

12.5 0.7

lfi.5 0.7

2 3 16.0 0.7 The results of the tests of polishing compositions show that 65

: T а .6 л и ц and 2

80

Partial

stratification

emulsions

60

Emulsin stratification no

80 80

Claims (2)

The same comparison with the prototype are given in table 2. in appearance, the main characteristics .. and consumer properties. to you (the ability to apply and the ease of polishing the proposed polishing compound is not inferior to its weight, but surpasses in some characteristics. For example, the gloss of the film in the prototype is 12/0 unit head and in the proposed formulation (example 21 it). , is 16.5.. Use of synthetic wax in a mixture with polyethylene oxidized wax as a film-forming substance improves the stability of the polishing composition. During storage for 10 months, a partial separation of the emulsion is observed, no polishing composition of the bundle is not observed. The formula of the invention, the polishing composition of leather shoes, containing a film-forming substance, oxidized polyethylene wax, paraffin, .. ethyl ethanol, crush, mineral spirits and water, because In order to increase the shoe shine and increase the stability of the composition during storage, it contains the product of etherifying high molecular weight fatty acids with monoethanolamides of synthetic fatty acids as a film-forming substance; the fraction additionally contains a perfume and the following ratio of components, wt.%: The specified film-forming material that breaks out in v. “e.stvo - 6-18 Polyethylene oxidized work1-4 Paraffin5-13 di ethylethan6lamin 1-t4 Beautified White spirit 20-45 Otduyky 0.1-1 Water Else Sources of information taken into account during the examination 1. Author's certificate of the USSR 317694, cl. From 09 G 1/10, 1972. 2. TU 6-15-277-76 Shoe cream emulsion Shevro-2 (prototype 1.