SU916582A1 - High speed steel composition - Google Patents

High speed steel composition Download PDF

Info

Publication number
SU916582A1
SU916582A1 SU802971561A SU2971561A SU916582A1 SU 916582 A1 SU916582 A1 SU 916582A1 SU 802971561 A SU802971561 A SU 802971561A SU 2971561 A SU2971561 A SU 2971561A SU 916582 A1 SU916582 A1 SU 916582A1
Authority
SU
USSR - Soviet Union
Prior art keywords
vanadium
high speed
titanium
carbon
speed steel
Prior art date
Application number
SU802971561A
Other languages
Russian (ru)
Inventor
Avenir N Popandopulo
Vladimir P Alferov
Yurij V Vinogradov
Vladimir N Zhuchin
Mikhail M Klyuev
Svetlana D Popova
Aleksandr A Smirnov
Original Assignee
Avenir N Popandopulo
Vladimir P Alferov
Yurij V Vinogradov
Vladimir N Zhuchin
Mikhail M Klyuev
Svetlana D Popova
Aleksandr A Smirnov
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Avenir N Popandopulo, Vladimir P Alferov, Yurij V Vinogradov, Vladimir N Zhuchin, Mikhail M Klyuev, Svetlana D Popova, Aleksandr A Smirnov filed Critical Avenir N Popandopulo
Priority to SU802971561A priority Critical patent/SU916582A1/en
Application granted granted Critical
Publication of SU916582A1 publication Critical patent/SU916582A1/en

Description

Изобретение относится к металлургии, а именно к изысканию сталей для металлорежущего инструмента.The invention relates to metallurgy, in particular to finding steels for metal-cutting tools.

Наиболее близкой к предлагаемой по технической сущности и достигаемому результату является быстроре· жущая сталь Р6М5 состава, вес.%: . Углерод 0,8-0,88Closest to the proposed technical essence and the achieved result is a fast-cutting steel R6M5 composition, wt.%:. Carbon 0.8-0.88

Вольфрам 5,5-6,5Tungsten 5.5-6.5

Молибден 5,0-5,5Molybdenum 5,0-5,5

Хром 3,8-4,4Chrome 3.8-4.4

Ванадий 1,7-2,1Vanadium 1.7-2.1

Железо Остальное [(],Iron Else [(],

Недостатком известной стали является склонность к структурной наследственности, в том числе к образованию нафталинистого излома, а также относительно невысокие режущие свойства.A disadvantage of the known steel is the tendency to structural heredity, including the formation of naphthalene fracture, as well as relatively low cutting properties.

Цель изобретения - уменьшение склонности к структурной наследственности и повышение режущих свойствThe purpose of the invention is to reduce the tendency to structural heredity and increase the cutting properties

Это достигается тем, что быстро- " режущая сталь, содержащая углерод,This is achieved by the fact that fast-cutting carbon-containing steel

10ten

Г 15G 15

вольфрам, молибден, хром, ванадий, железо, дополнительно содержит титан и кальций при следующем соотношении компонентов, вес.%:tungsten, molybdenum, chromium, vanadium, iron, additionally contains titanium and calcium in the following ratio of components, wt.%:

Углерод 0,84-0,92Carbon 0.84-0.92

Вольфрам 4,5-5,4Tungsten 4.5-5.4

Молибден 4,8-5,3Molybdenum 4.8-5.3

Хром 3,8-4,4Chrome 3.8-4.4

Ванадий 0,9-1,3Vanadium 0.9-1.3

Титан 0,01-0,03Titanium 0.01-0.03

Кальций 0,01-0,05Calcium 0.01-0.05

Железо ОстальноеIron Else

Отношение суммарного содержания ванадия и титана к содержанию углерода составляет 1,1-1,4. 'The ratio of the total content of vanadium and titanium to the carbon content is 1.1-1.4. '

Химический состав исследованных плавок предлагаемой и известной сталей и соответствующие им свойства приведены в табл. 1 и 2.The chemical composition of the investigated bottoms of the proposed and known steels and the corresponding properties are given in Table. 1 and 2.

Предлагаемая сталь подвергается закалке с 1160-1180°С и отпуску при 560°С 3 раза ήο 1 часу,The proposed steel undergoes quenching from 1160-1180 ° С and tempering at 560 ° С 3 times for 1 hour,

После термической обработки предел прочности при изгибе и ударнаяAfter heat treatment, flexural strength and impact strength

2020

3 916562 43 916562 4

'Вязкость предлагаемой стали составляют .соответственно 320-350 кгс/мм2 и 3-4 кгс·м/см*. При точении и фрезеровании стали 12Х18Н9Т стойкостьThe viscosity of the proposed steel is respectively 320-350 kgf / mm 2 and 3-4 kgf · m / cm *. When turning and milling steel 12X18H9T resistance

инструмента из предлагаемой стали выше стойкоцти инструмента из стали Р6М5 соответственно в 1,2 и 1,4 1,6 раза.tools of the proposed steel are higher than the resistance of tools made of steel R6M5, 1.2 and 1.4, respectively, 1.6 times.

Т а б л и ц а IT a b l and c a I

Содержание, мае,XContent, May, X

Плавка 1 ίMelting 1 ί С WITH Сг Cr V V Мо Moe V V Со With Т1 T1 Са Sa 1 one 0,84 0.84 3,80 3.80 4,5 4.5 4,8 4.8 0,9 0.9 - - 0,01 0.01 0,0! 0,0! 2 2 0,88 0.88 4,10 4,10 4,95 4.95 5,1 5.1 1,1 1.1 0,02 0.02 0,03 0.03 з 1 h 1 0,92 0.92 4,40 4.40 5,4 5.4 5,3 5.3 1,3 1,3 - - 0,03 0.03 0,05 0.05

Плавка Melting 1-—-ή Твердость вторичная ИКС 1 ——- ή Hardness secondary X --и Красностойкость для ИКС 58, »С --and Redness for X 58, "WITH Балл зерна Grain Score После первой закалки After the first quenching После второй закалки After second quenching Предлагаемая Offered 1 one 65 65 625 625 10-11 10-11 8-9 8-9 2 2 65 65 630 630 10-11 10-11 8-10 8-10 3 3 66 66 630 630 10-11 10-11 9-10 9-10 Известная Known 4 · four · 63-65 63-65 625 625 10-11 10-11 4-5 4-5

Claims (1)

Формула изобретенияClaim 1, Быстрорежущая ст аль, содержа· щая углерод, вольфрам, молибден, хром, ванадий, железо, о т л и ча ю щ а я с я тем, что, с целью уменьшения склонности к структурной наследственности и повышения режущих свойств, она дополнительно содержит титан и кальций при следующе соотношении компонентов, вес.%51, High-speed al, containing carbon, tungsten, molybdenum, chromium, vanadium, iron, and it is due to the fact that, in order to reduce the tendency to structural heredity and increase the cutting properties, it additionally contains titanium and calcium in the following ratio of components, wt.% 5 Углерод 0,84-0,92Carbon 0.84-0.92 Вольфрам 4,5-5,4Tungsten 4.5-5.4 Молибден 4., 8-5,3Molybdenum 4., 8-5,3 Хром Chromium 3,8-4,4 3.8-4.4 Ванадий Vanadium 0,9-1,3 0.9-1.3 Титан Titanium 0,01-0,03 0.01-0.03 Кальций Calcium 0,01-0,05 0.01-0.05 Железо Iron Остальное Rest 2. Сталь по п. 2. Steel according to claim. 1, отлич 1, excellent ί а я с я тем, ί and I'm with that что отношение what's the attitude
марного содержания ванадия и титана к содержанию углерода составляет 1,1-1,4.the content of vanadium and titanium to the carbon content is 1.1-1.4.
SU802971561A 1980-08-11 1980-08-11 High speed steel composition SU916582A1 (en)