SU916518A1 - Envelope for mineral fertilizer - Google Patents

Envelope for mineral fertilizer Download PDF

Info

Publication number
SU916518A1
SU916518A1 SU802972029A SU2972029A SU916518A1 SU 916518 A1 SU916518 A1 SU 916518A1 SU 802972029 A SU802972029 A SU 802972029A SU 2972029 A SU2972029 A SU 2972029A SU 916518 A1 SU916518 A1 SU 916518A1
Authority
SU
USSR - Soviet Union
Prior art keywords
coating
phosphoric acid
granules
mineral
polyvinyl acetate
Prior art date
Application number
SU802972029A
Other languages
Russian (ru)
Inventor
Leonid M Pozin
Evgeniya N Krupskaya
Elena A Fomina
Efim M Blyakhman
Renat Yu Zinyuk
Original Assignee
Le Gni Pi Osnovnoj Khim Promys
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Le Gni Pi Osnovnoj Khim Promys filed Critical Le Gni Pi Osnovnoj Khim Promys
Priority to SU802972029A priority Critical patent/SU916518A1/en
Application granted granted Critical
Publication of SU916518A1 publication Critical patent/SU916518A1/en

Description

(54) ПОКРЫТИЕ ДЛЯ МИНЕРАЛЬНОГО УДОБРЕНИЯ

I

Изобретение относится к производству минеральных удобрений, в частности, к получению удобрений с замедленным поступлением питательных элементов в почву.

Известно покрытие для минерального удобрения, состоящее из карбамидной смолы [11.

Недостатком этого покрытия является то, что оно обеспечивает уменьшение скорости растворения минеральной части удобрения в воде не более чем в 3-5 раз.

Наиболее близким к предлагаемому по составу и достигаемому результату является покрытие [2], состоящее из карбамидной смолы с добавками. При этом в качестве добавок используют фосфогипс. Состав покрытия, вес.%:

Карбамидная смола 31-68

Фосфогипс 32-69

Недостаток покрытия заключается в том, что оно не обеспечивает снижения скорости растворения минеральной массы удобрения более чем в 6 раз. Кроме того, фосфогипс, входящий в состав покрытия, содержит всего 0,8-1% Ρ3Οί и, таким образом, сумма пита2 тельных веществ самого покрытия (Ν+Ρ2Ο5) не превышает 12,7-27,9% от его веса.

Цель изобретения — уменьшение скорости растворения минеральной части удобрения и увеличение суммы питательных веществ в покрытии.

Поставленная цель достигается тем, что покрытие, состоящее из карбамидной смолы с добавками, в качестве добавок содержит поливинилацетат и фосфорную кислоту при следующем соотношении компонентов, вес%:

Поливинилацетат 15-20

Фосфорная кислота ,5 (100% РгО5) 0,3-0,5

Карбамидная смола Остальное

Предлагаемое покрытие позволяет уменьшить скорость растворения гранул минерального удобрения с покрытием (например, нктроаммофоски) в 40-60 раз по сравнению с исходными гранулами и в 10-15 раз по сравнению с известным и увеличить сумму питательных веществ в покрытии до 32.6-34,3% от веса покрытия.

Нанесение покрытия предлагаемого состава на гранулы минерального удобрения ведет из смеси раствора карбамидной смолы, поливинилацетатной дисперсии и фосфорной кислоты, что исключает наличие в растворе нанесения 5 твердой фазы, какой является в известном покрытии фосфогипс. Это позволяет получить однородный по всей поверхности гранул удобрения слой, что уменьшает скорость растворения минеральной части. Кроме того, вве- 10 дение в раствор для нанесения предлагаемого покрытия фосфорной кислоты увеличивает число поперечных сшивок в образующемся на поверхности гранул сополимере, что делает его менее проницаемым. 15

Содержание в покрытии фосфорной кислоты (100% Р2О5) в пределах 0,3-0,5% обусловлено тем, что при введении < 0,3% Р2О5 растворение гранул проходит со скоростью, приближающейся к скорости растворения гранул с м известным покрытием. При содержании в покрытии фосфорной кислоты (100% РгО5)>0,5% смесь для его получения имеет большую вязкость, вследствие чего не представляется возможным получить из нее при существующей 25 технологии равномерного покрытия.

Выход за количественный предел поливинилацетата (15-20 вес.%) приводит к увеличению скорости растворения минеральной части удобрения. ад

Пример 1. Для приготовления смеси берут: 35%-ный водный раствор карбамидной смолы 13,63 г, поливинилацетатную дисперсию (50%) 2,4 г, фосфорной кислоты (29% Р2О5)

0,134 г. Смесь распыляют на взвешенный слой нагретых до 70-90° С 100 г гранул нитроаммо- 35 фоски. Покрытие наносят в течение 3-5 мин. *

Полученное покрытие содержит» вес.%:

Карбамидная смола 79,6

Поливинилацетат 20

Фосфорная кислота (100% Р2О5) 0,5

Сумма питательных веществ покрытия (Ν+Ρ2Ο5) составляет 32,6% от веса покрытия. Пример 2. Для приготовления смеси берут 35%-ный раствор карбамидной смолы 14,51 г, поливинилацетатную дисперсию (50%)

1,8 г,фосфорную кислоту (29% Р2О5) 0,062 г. Покрытие на гранулы наносят аналогично примеру 1. Полученное покрытие содержи!, вес.%:

Карбамидная смола 84,7 Поливинилацетат 15 Фосфорная кислота (100% Р2О5) 0,3

Сумма питательных веществ (Ν + Р2О5) в покрытии составляет 34,3% к весу покрытия.

Использование предлагаемого покрытия в производстве медленно действующих удобрений может дать существенный экономический эффект.

Проведенные испытания на скорость растворения в среднесуглинистой почве (рН 4,6, влажность 60% от максимально возможной, которая составляет 50,98 г воды на 100 г почвы) гранул нитроаммофоски с покрытием предлагаемого состава показывают результаты, представленные в таблице. Эти результаты сопоставлены с результатами растворения гранул исходной нитроаммофоски и гранул с известным покрытием.

Из результатов видно, что за 10 дней (к моменту начала вегетащш) в гранулах с покрытием предлагаемого состава остается 16,5% от начальной минеральной массы, тогда как исходам нитроаммофоска растворяется полностью, а в нитроаммофоске с известным покрытием остается 5% от начальной минеральной массы. Это дает возможность увеличить коэффициент использования минерального удобрения на 15% при нанесении предлагаемого покрытия и лишь . на 3,6% при нанесении известного покрытия.

Пиело дней

(54) COVERING FOR MINERAL FERTILIZER

I

The invention relates to the production of mineral fertilizers, in particular, to the production of fertilizers with a slow entry of nutrients into the soil.

Known coating for mineral fertilizers, consisting of urea resin [11.

The disadvantage of this coating is that it reduces the rate of dissolution of the mineral part of the fertilizer in water by no more than 3-5 times.

The closest to the proposed composition and the achieved result is a coating [2], consisting of urea resin with additives. At the same time, phosphogypsum is used as additives. The composition of the coating, wt.%:

Urea Resin 31-68

Phosphogypsum 32-69

The disadvantage of the coating is that it does not reduce the dissolution rate of the fertilizer mineral mass by more than 6 times. In addition, phosphogypsum, which is part of the coating, contains only 0.8-1% Ρ 3 Ο ί and, therefore, the amount of nutrients of the coating itself (Ν + Ρ 2 Ο 5 ) does not exceed 12.7-27.9 % of its weight.

The purpose of the invention is to reduce the dissolution rate of the mineral part of the fertilizer and increase the amount of nutrients in the coating.

This goal is achieved in that the coating consisting of urea resin with additives, as additives contains polyvinyl acetate and phosphoric acid in the following ratio of components, weight%:

Polyvinyl Acetate 15-20

Phosphoric acid, 5 (100% PgO 5 ) 0.3-0.5

Carbamide Resin Else

The proposed coating allows you to reduce the dissolution rate of the granules of mineral fertilizers with a coating (for example, Nktroammofoski) 40-60 times compared with the original granules and 10-15 times compared with the known and increase the amount of nutrients in the coating to 32.6-34.3% by weight of the coating.

The coating of the proposed composition leads to granules of mineral fertilizer from a mixture of a solution of urea resin, polyvinyl acetate dispersion and phosphoric acid, which eliminates the presence in the solution of application5solid phase, which is in the known coating phosphogypsum. This allows you to get a layer homogeneous over the entire surface of the granules of the fertilizer, which reduces the rate of dissolution of the mineral part. In addition,10adding to the solution for applying the proposed coating of phosphoric acid increases the number of cross-links in the copolymer formed on the surface of the granules, which makes it less permeable.fifteen

The content in the coating of phosphoric acid (100% P 2 O 5 ) in the range of 0.3-0.5% is due to the fact that with the introduction of <0.3% P 2 O 5, the granules dissolve at a rate approaching the dissolution rate of the granules with m famous coating. When the content of phosphoric acid in the coating (100% P g O 5 )> 0.5%, the mixture for its preparation has a high viscosity, as a result of which it is not possible to obtain uniform coating from it with the existing 2 5 technology.

Going beyond the quantitative limit of polyvinyl acetate (15-20 wt.%) Leads to an increase in the dissolution rate of the mineral part of the fertilizer. hell

Example 1. To prepare the mixture take: 35% aqueous urea resin 13.63 g, polyvinyl acetate dispersion (50%) 2.4 g, phosphoric acid (29% P 2 O 5 )

0.134 g. The mixture is sprayed onto a suspended layer of 100 g of nitroammo- 35 granules heated to 70-90 ° C. The coating is applied for 3-5 minutes. *

The resulting coating contains "wt.%:

Urea resin 79.6

Polyvinyl Acetate 20

Phosphoric acid (100% P 2 O 5 ) 0.5

The amount of coating nutrients (Ν + Ρ 2 Ο 5 ) is 32.6% of the coating weight. Example 2. To prepare the mixture take a 35% solution of urea resin 14.51 g, polyvinyl acetate dispersion (50%)

1.8 g, phosphoric acid (29% P 2 O 5 ) 0.062 g. The coating on the granules is applied analogously to Example 1. The resulting coating contains !, wt.%:

Carbamide resin 84.7 Polyvinyl acetate fifteen Phosphoric acid (100% P 2 O 5 ) 0.3

The amount of nutrients (Ν + P 2 O 5 ) in the coating is 34.3% by weight of the coating.

The use of the proposed coating in the production of slow-acting fertilizers can give a significant economic effect.

The tests for dissolution rate in medium loamy soil (pH 4.6, humidity 60% of the maximum possible, which is 50.98 g of water per 100 g of soil) of nitroammophoska granules with the coating of the proposed composition show the results presented in the table. These results are compared with the results of dissolution of the granules of the original nitroammophos and granules with a known coating.

From the results it can be seen that in 10 days (by the time vegetation begins) 16.5% of the initial mineral mass remains in the granules with the coating of the proposed composition, while the outcome of the nitroammophosk completely dissolves, and in the nitroammophosk with the known coating, 5% of the initial mineral mass remains . This makes it possible to increase the utilization rate of mineral fertilizers by 15% when applying the proposed coating and more. 3.6% when applying a known coating.

Pielo days

Claims (1)

ФормулаиэобретенияFormulas and inventions Покрытие для минерального удобрения, состоящее из карбамидной смолы с добавках®, отличающееся тем, что, с целью $ снижения скорости растворения удобрения и повышения суммы питательных веществ в покрытия, в качестве добавок оно содержит поливияилацетат и фосфорную кислоту при следующем соотношении компонентов, вес.%:Coating for mineral fertilizers, consisting of urea resin with additives®, characterized in that, in order to reduce the dissolution rate of the fertilizer and increase the amount of nutrients in the coating, it contains polyvinyl acetate and phosphoric acid as additives in the following ratio of components, wt.% : Поливинилацетат 15-20Polyvinyl Acetate 15-20 Фосфорная кислота (100% Р2О5) 03-0,5Phosphoric acid (100% P 2 O 5 ) 03-0.5 Карбамидная смола ОстальноеCarbamide Resin Else
SU802972029A 1980-08-08 1980-08-08 Envelope for mineral fertilizer SU916518A1 (en)