SU90542A1 - The method of increasing the strength and water resistance of glass fabrics - Google Patents
The method of increasing the strength and water resistance of glass fabricsInfo
- Publication number
- SU90542A1 SU90542A1 SU407463A SU407463A SU90542A1 SU 90542 A1 SU90542 A1 SU 90542A1 SU 407463 A SU407463 A SU 407463A SU 407463 A SU407463 A SU 407463A SU 90542 A1 SU90542 A1 SU 90542A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- strength
- water resistance
- increasing
- fabrics
- glass
- Prior art date
Description
Как известно, издели из .стекл нных тканей резко тер ют прочность от воздействи влаги. Поэтому стекл нное волокно в процессе его Обработки замасливают путем нанесени на него парафина или парафина в смеси со склеивающими веществами. Така обработка стекл нного волокна предохран ет его от истирани и способствует процессу ;изготовлени стекл нных тканей, но не позвол ет их более щироко использовать .As is known, articles made of glass fabrics drastically lose their strength due to moisture. Therefore, in the process of its processing, the glass fiber is oiled by applying paraffin or paraffin on it in a mixture with adhesive substances. Such processing of glass fibers protects it from abrasion and contributes to the process, the manufacture of glass fabrics, but does not allow them to be used more widely.
Предложенный способ повыщени прочности и водоустойчивости стекл нных тканей основан также на изготовлении их из покрытых замасливател ми стекл нных волокон, но отличаетс тем, что полученную из таких волокон ткань обрабатывают водным или неводным раствором поверхностно-активный веществ, примен в качестве последних органические кислоты или соли поливалентных металлов, или смеси этих веществ. Така обработка стекл нных тканей повышает адгезию стекл нных волокон к замасливателю и делает их более прочными и водоустойчивыми .The proposed method of enhancing the strength and water resistance of glass fabrics is also based on their fabrication from coated with lubricant glass fibers, but is characterized in that the fabric obtained from such fibers is treated with an aqueous or non-aqueous solution of surfactant polyvalent metals, or mixtures of these substances. Such treatment of glass fabrics increases the adhesion of glass fibers to the sizing agent and makes them more durable and waterproof.
Пример 1. Ткань, приготовленную из стекл нных волокон, покрытых парафином в количестве 2-3% от веса ткани, обрабатывают водным раствором, содержащим 0,5% уксусной кислоты и 0,3%крезола. Обработку ведут в течение 20 мин при температуре 50-60°С. Затем ткань высушивают и прогревают при температуре 70-100°С.Example 1: A fabric prepared from glass fibers coated with paraffin in an amount of 2-3% by weight of the fabric is treated with an aqueous solution containing 0.5% acetic acid and 0.3% cresol. The treatment is carried out for 20 minutes at a temperature of 50-60 ° C. Then the fabric is dried and heated at a temperature of 70-100 ° C.
Пример 2. Стекл нную ткань пропитывают 3%-ным раствором каучука в бензине, вл ющимс замасливателем. В бензин ввод т 0,1 - 0,2% крезолоксиленольной смеси и 0,2% уксусной кислоты.Example 2 A glass cloth was impregnated with a 3% rubber solution in gasoline, which is a lubricant. 0.1 - 0.2% cresoloxylene mixture and 0.2% acetic acid are introduced into gasoline.
№ 90542- 2 -No. 90542-2 -
Предмет изобретени Subject invention
Claims (2)