SU884790A1 - Filler for tube cold bending - Google Patents
Filler for tube cold bending Download PDFInfo
- Publication number
- SU884790A1 SU884790A1 SU802880384A SU2880384A SU884790A1 SU 884790 A1 SU884790 A1 SU 884790A1 SU 802880384 A SU802880384 A SU 802880384A SU 2880384 A SU2880384 A SU 2880384A SU 884790 A1 SU884790 A1 SU 884790A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- filler
- cold bending
- caustic soda
- pipes
- bending
- Prior art date
Description
(54) НАПОЛНИТЕЛЬ ДЛЯ ХОЛОДНОЙ ГИБКИ ТРУБ(54) FILLER FOR COLD PIPE BENDING
t.t.
Изобретение относитс к обработке металлов давлением, в частности к трубогибочному производству.The invention relates to the processing of metals by pressure, in particular to pipe bending production.
Известен наполнитель дл холодной гибки труб в виде сорбита с введенным в него гли-. церином. Известный наполнитель хорошо раствор етс в воде, обладает моющим свойством, не вызывает коррозии на стальных и алюминиевых трубах, после застывани обладает хорошими пластическими и смазывающими свойствами, нелетуч, нетоксичен, невзрывоопасен t.A known filler for cold bending of pipes in the form of sorbitol with gly- introduced into it. cerin. The known filler dissolves well in water, has detergent properties, does not cause corrosion on steel and aluminum pipes, after curing it has good plastic and lubricating properties, non-volatile, non-toxic, non-explosive.
Недостатком известного наполнешш вл етс то, что дл каждой гибки трубы требуетс нова порци наполнител , так как сорбит после его использовани из трубы вымываетс водой, т.е. требуетс большой расход наполнител .A disadvantage of the known filling is that a new portion of filler is required for each pipe bend, since after its use sorbitol is washed out of the pipe with water, i.e. high filler consumption required.
Цель изобретени - сокраще1ше расхода наполнител при гибке труб.The purpose of the invention is to reduce the consumption of filler during pipe bending.
Указанна цель достигаетс тем, что в качестве наполнител дл холодной гибки труб примен етс раствор едкого натра.This goal is achieved by using caustic soda solution as a filler for cold bending of pipes.
Применение едкого натра в качестве наполнител дл холодной гибки труб производитс следующим образом.The use of caustic soda as a filler for cold bending pipes is as follows.
Дл холодной гибки труб в зависимости от окружающей температуры примен ют раствор едкого натра необходимой концентрации. Предлагаетс примен ть раствор такой концентрации , температура затвердевани которого на 4-5°С выше температуры -окружающего воздуха, где производ т гибку труб. Наto пример, дл условий гибки труб с температурой окружающей среды 20°С примен етс . раствор едкого натра с концентрацией 113 г NaOH/100 мл воды, который затвердевает при 24° с.Depending on the ambient temperature, caustic soda solution of necessary concentration is used for cold bending of pipes. It is proposed to apply a solution of this concentration, the solidification temperature of which is 4-5 ° C higher than the temperature of the ambient air where the pipes are bent. In this example, for the conditions of bending pipes with an ambient temperature of 20 ° C is used. a solution of caustic soda with a concentration of 113 g of NaOH / 100 ml of water, which solidifies at 24 ° C.
ISIS
Подогретый на 3-4 С выше температуры затвердевани раствор едкого натра заливают в подготовленную дл гибки трубу, котора с одной стороны закрыта пробкой. Через несколько минут, благодар тЬплу,что темпераiO тура окружающего воздуха на 4-5° С ниже температуры затвердевани раствор NaOH превращаетс в твердое состо иие. После затвердевани раствора производитс гибка 3 fpy6bt. Затем труба подогреваетс на 3-4° С выше температуры затвердевани , раствор переходит в жидкое состо ние и используетс дл гибки следующих труб. При нахождении раствора едкого натра в трубах он хорошо очищает их внутреннюю поверхность, поэтому его особенно эффективно примен ть при гибке труб маслос стемы компрессорных холодильных, кислородных и воздушных агрегатов, которые об зательно надо очищать в период подготовки их к монтажу. После использовани раствора едкого натра дл холодной гибки труб на воздухоразд лительных станци х, где обычно устанавливаетс большое количество различных типов комнрессорных агрегатов, его направл ют в технолоA solution of caustic soda heated to 3-4 ° C above the solidification temperature is poured into a pipe prepared for bending, which is closed with a stopper on one side. After a few minutes, due to the fact that the ambient air temperature is 4-5 ° C below the solidification temperature, the NaOH solution turns into a solid state. After the solution has hardened, 3 fpy6bt is flexible. The pipe is then heated 3-4 ° C above the solidification temperature, the solution goes into a liquid state and is used to bend the next pipe. When a solution of caustic soda in pipes is found, it cleans their internal surface well; therefore, it is especially effective to use when bending pipes of the oil of compressor refrigeration, oxygen, and air units, which must be cleaned during their preparation for installation. After using caustic soda solution for cold bending pipes at air distribution stations, where a large number of different types of compressor units are usually installed, it is sent to
ГR
Claims (1)