SU860906A1 - Plugging composition - Google Patents
Plugging composition Download PDFInfo
- Publication number
- SU860906A1 SU860906A1 SU792758716A SU2758716A SU860906A1 SU 860906 A1 SU860906 A1 SU 860906A1 SU 792758716 A SU792758716 A SU 792758716A SU 2758716 A SU2758716 A SU 2758716A SU 860906 A1 SU860906 A1 SU 860906A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- composition
- cement
- setting time
- silicic acid
- potassium
- Prior art date
Description
Изобретение относитс к области бурени , а именно к тампонажным составам дл ликвидации поглощений промывочной жидкости . Известен тампонажный состав, содержащий цементную смесь с раз 1ичными ускорител ми схватывани 1. Недостатком этого состава вл етс низка прочность тампонажного камн . Наиболее близким по технической сущности и достигаемому результату вл етс тампонажный состав, содержащий цемент, воду и ускоритель сроков схватывани 2. Недостатками его вл ютс низка прочность цементного камн на сжатие в ранние сроки твердени и большие сроки схватывани . Целью изобретени вл етс повышение прочности цементного камн на сжатие в ранние сроки твердени при одновременном уменьшении сроков схватывани составаЭто достигаетс тем, что в качестве ускорител сроков схватывани состав содержит свежеприготовленный раствор из кремневой кислоты и едкого натри или кали , причем соотношение ингредиентов следующее , вес. %: Цемент53-61 ; Вода27-31 Кремниева кислота4-10 Едкий натрий или калий4-10 Данный состав имеет следующую харакеристику: Плотность, 1,65 г/см Растекаемость по конусу Азнии, см16-17 Начало схватывани , мин1,5-12 Конец схватывани , мин19-26 Прочность камн на сжатие, кгс/см : через 1 ч40-80 через 3 ч100-130 через 24 ч130-160 Дл получени данной тампонажиой меси были-приготовлены несколько состаВОВ , представленных в таблице. ТамПонажный состав включает цементный расрвор (в/ц 0,45) и отвердитель. Последний готов т следующим образом. Отдельно в части воды раствор ют едкий натрий (калий), затем кремниевую кислоту . После полного растворени смесь добавл ют в цементный раствор. При этом на растворение едкого натра (кали ) и кремневой кислоты необходимо 6-8% воды от количества, указанного в составе, например: цементный раствор (в/ц 0,45) - 450 г цемента, 200 мл воды, а отвердитель - 7 мл воды, 40 г едкого натра, 40 г кремниевой кислоты. Лабораторные исследовани предложенного состава 11оказа„1И, что врем схватывани цементного камрг сокращаетс : начало схватывани 1,5-12 мин, конец схватывани 19-26 мин, а црочность его возрастает. Экономический эффект составл ет 300- 350 руб, на одну онерацию.The invention relates to the field of drilling, namely to cement slurries to eliminate the absorption of washing liquid. A grouting composition containing a cement mixture with primary setting accelerators 1 is known. A disadvantage of this composition is the low strength of the grouting stone. The closest in technical essence and the achieved result is a grouting composition containing cement, water and accelerator setting time 2. Its disadvantages are the low compressive strength of the cement stone in the early periods of hardening and long setting times. The aim of the invention is to increase the compressive strength of cement stone in the early periods of hardening while simultaneously reducing the setting time of the composition. This is achieved by providing the composition with a freshly prepared solution of silicic acid and caustic sodium or potassium, as an accelerator of setting time, and %: Cement 53-61; Water27-31 Silicic acid 4-10 Caustic sodium or potassium 4-10 This composition has the following characteristics: Density, 1.65 g / cm. Flowability along the cone of Aznia, cm 16-17 Start of setting, min 1.5-12 End of setting, min 19-26 Durability stone in compression, kgf / cm: after 1 h40-80 after 3 h100-130 after 24 h130-160 To prepare this tamponage mixture, several compositions were prepared as presented in the table. There, the composition of the composition includes a cement mortar (w / c 0.45) and a hardener. The latter is prepared as follows. Separately, sodium hydroxide (potassium) is dissolved in a portion of the water, then silicic acid. After complete dissolution, the mixture is added to the cement mortar. At the same time, 6-8% of water is needed to dissolve caustic soda (potassium) and silicic acid, based on the amount specified in the composition, for example: cement mortar (w / c 0.45) - 450 g of cement, 200 ml of water, and hardener - 7 ml of water, 40 g of sodium hydroxide, 40 g of silicic acid. The laboratory studies of the proposed composition of the 11 "1" show that the setting time of the cement block is reduced: the beginning of the setting is 1.5-12 minutes, the end of the setting is 19-26 minutes, and its degree of increase increases. The economic effect is 300-350 rubles per operation.
Формула и 3 о б р е т е н и Formula and 3 optics
Тампонажный состав, содержа1ций цемент , воду и ускоритель сроков схватывани , отличающийс тем, что, с целью цовыщени прочности цементного камн на сжатие в ранние сроки твердени атри одновремеином уменьшении сроков схватывани соста-ва, в качестве ускорител сроков схва .тывани состав содержит свеженриготовленный раствор из кремниевой кислоты н едкого натри или кали , нричем соотношение ингредиентов следующее, вес. %:The cement composition, cement, water and accelerator setting time, characterized in that, in order to compress the strength of cement stone in the early periods of hardening, while simultaneously reducing the setting time of the composition, the composition contains freshly prepared mortar from silicic acid and sodium hydroxide or potassium, and the ratio of ingredients is the following, wt. %:
Цемент53-61Cement53-61
Вода27-31Water27-31
Кремниева кислота4-10Silicic acid 4-10
Едкий натрий или калий4-10.Caustic Sodium or Potassium4-10.
Источники информании, прин тые во внимание нри экснертнзеSources of information taken into account by experts
1. Данюшевский В. С. н др. Справочное руководство цо тамнонажным материалам. М., «Недра, 1973, с. 130-144. 2- Тишков Н. И. и др. Изол ци поглощающих горизонтов нри бурении скважнн. М., 1960, с. 161.1. Danyushevsky V.S.N. Dr. Reference Guide for Standard Materials. M., "Nedra, 1973, p. 130-144. 2- N. I. Tishkov et al. Isolation of absorbing horizons while drilling boreholes. M., 1960, p. 161.
Claims (1)