Изобретение относитс к производству стеновой керамики, преимущественно к составам покрытий дл лицевых и облицовочных керамических изделий .The invention relates to the production of wall ceramics, mainly to compositions of coatings for facial and facing ceramic products.
Известна фритта дл глазуровани керамических изделий, включающа SiOi, , , TiOj, , CaO, MgO, K.O, I.A known frit for glazing of ceramic products, including SiOi,,, TiOj, CaO, MgO, K.O., I.
Недостатком данной фритты вл етс недостаточна термостойкость покрыти .The disadvantage of this frit is the insufficient heat resistance of the coating.
Целью изобретени вл етс повышение термостойкости покрыти .The aim of the invention is to increase the heat resistance of the coating.
Достигаетс это тем, что фритта дл глазуровани керамических изделий , включающа SiOj, , , TiO,, CaQ, MgO, K2O, Na2.O, дополнительно содержит FeO, MnO и следующем соотношении компонентов, вес.%:This is achieved by the fact that the frit for glazing of ceramic products, including SiOj,,, TiO, CaQ, MgO, K2O, Na2.O, also contains FeO, MnO and the following ratio of components, wt.%:
23,75-28,1923.75-28.19
13,85-16,6213.85-16.62
0,94-1,340.94-1.34
0,86-1,030.86-1.03
0,20-0,240.20-0.24
0,02-0,030.02-0.03
МпО MPO
0,84-1,10 СаО 0.84-1.10 CaO
0,25-0,30 MgO0.25-0.30 MgO
27,89-34,7927.89-34.79
PaOs PaOs
4,55-5,46 KjO 17,80-19,954.55-5.46 KjO 17.80-19.95
Фритту вар т при 1100-1200 С с выдержкой при максимальной температуре в течение 2-3 ч.The frit is boiled at 1100-1200 ° C and held at the maximum temperature for 2-3 hours.
Приготовленные на основе полученной фритты глазури методом пульверизации нанос на керамические образцы , которые обжигают при 870-970С. Глазури имеют хороший разлив, красивый блеск, небольшую в зкость. Глазурь хорошо согласовываетс с черепкбм , обладает хорс ей морозо- иPrepared on the basis of the obtained frit glaze by the method of spraying deposited on ceramic samples that are fired at 870-970C. Glazes have good spill, beautiful shine, low viscosity. The glaze is in good agreement with the skull; the frost has frost and
термостойкостью. При добавлении к глазур м различных красителей можно получить широкую гамму цветов. На основе фритты получают глазури дл одно- и двухкратного обжига лицевойheat resistance. When various dyes are added to the glazes, a wide range of colors can be obtained. Frit-based glazes are obtained for single and double firing of the face.
керамики.ceramics.
Состав и свойства фритты представлены в таблице.The composition and properties of the frit are presented in the table.
37 3537 35
4343
4141
Источники информации, прин тые во внимание при экспертизеSources of information taken into account in the examination
1. Авторское свидетельство СССР №201612, кл. С 03 С 5/00, 1965.1. USSR author's certificate №201612, cl. On 03 On 5/00, 1965.
Claims (1)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SU772521522A SU713851A1 (en) | 1977-08-24 | 1977-08-24 | Frit |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SU772521522A SU713851A1 (en) | 1977-08-24 | 1977-08-24 | Frit |
Publications (1)
Publication Number | Publication Date |
---|---|
SU713851A1 true SU713851A1 (en) | 1980-02-05 |
Family
ID=20723781
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
SU772521522A SU713851A1 (en) | 1977-08-24 | 1977-08-24 | Frit |
Country Status (1)
Country | Link |
---|---|
SU (1) | SU713851A1 (en) |
-
1977
- 1977-08-24 SU SU772521522A patent/SU713851A1/en active
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN1765836B (en) | Ceramic glaze with metal sense of reality | |
CA1138155A (en) | Cordierite crystal-containing glaze | |
DE59902632D1 (en) | Lead and cadmium free glass composition for glazing, enamelling and decorating glasses or glass ceramics as well as processes for the production of a glass ceramic coated with them | |
WO1999012857A1 (en) | Reflective porcelain enamel coating composition | |
HUP9602087A2 (en) | Glass composition | |
JPS59195551A (en) | Dental semitransparent glaze composition | |
SU713851A1 (en) | Frit | |
US5985473A (en) | Low-temperature barium/lead-free glaze for alumina ceramics | |
Dakhai et al. | Types and compositions of crystalline glazes: A review | |
SU1470685A1 (en) | Ground enamel for steel-coating | |
SU1000432A1 (en) | Slip for producing opacified glazing | |
RU1772101C (en) | Graze for chine articles | |
SU1315402A1 (en) | Matte glaze | |
SU697420A1 (en) | Black enamel | |
SU1413065A1 (en) | Enamel | |
SU1025671A1 (en) | Transparent glaze | |
SU1787964A1 (en) | Frit for enamel coating for steel | |
SU833639A1 (en) | Enamel | |
SU1217807A1 (en) | Primining enamel | |
SU1477702A1 (en) | Enamel | |
RU2399593C1 (en) | Reductive glase | |
CA1193619A (en) | Stain-resistant mica compositions for dental products and processes or the like | |
SU833629A1 (en) | Enamel | |
SU833622A1 (en) | Frit for primer enamel | |
SU1583400A1 (en) | Unfritted killed glaze |