SU678113A1 - Method of treating pulp after digesting - Google Patents
Method of treating pulp after digestingInfo
- Publication number
- SU678113A1 SU678113A1 SU772532289A SU2532289A SU678113A1 SU 678113 A1 SU678113 A1 SU 678113A1 SU 772532289 A SU772532289 A SU 772532289A SU 2532289 A SU2532289 A SU 2532289A SU 678113 A1 SU678113 A1 SU 678113A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- liquor
- pulp
- cellulose
- monosulfite
- spent
- Prior art date
Description
(54) СПОСОБ ОБРАБОТКИ ЦЕЛЛЮЛОЗЫ ПОСЛЕ ВАРКИ(54) METHOD FOR PROCESSING PULP PULSE
мывают на многоступенчатой промывной установке. Полученную после промьюки смесь моносульфитного и варочного щелока направл ют на совместную регенерацию .washed in a multistage washing installation. The mixture of monosulfite and cooking liquor obtained after the run is sent for joint regeneration.
Сокращение расхода свежей воды на промьшку и повышение концентрации сухих веществ в сМесИ щёлоков по сравнению с известным способом достигаетс за счет того, что целйюлО:зупромывают только 1 раз. V- .A reduction in the consumption of fresh water per flush and an increase in the concentration of solids in the mixture of liquors in comparison with the known method is achieved due to the fact that OI: only once is stored. V-.
При м е р 1. Сульфатную небеленую цалшлозу Архангельского ЦБК, вз туюпосле выдувного резервуара до про678113Example 1. Unbleached sulphate granulose of the Arkhangelsk pulp and paper mill, taken after the blown tank to 67,8113
.мывки, отжимали от свободно стекающего щелока, который имел плотность 1,06 г/сма затем добавл ли на 1 г целлюлозы 4,6 мл отработанного моносульфитного щелока Архангельского ЦБК плотностью 1,048 при 21с и выдерживали при 7р-80 С в течение 1 часа. рН среди при обработке был 9,7. После обработки массу промывали на воронке Бюхнера водой и определ ли выход целлюлозь ,содержание пентрзанов по ГОСТ 10820-75 и механические показатели отлибок7 Полученные результаты представлёйы Б таблице (1 строка). . .The washes were squeezed out of the free flowing liquor, which had a density of 1.06 g / cm2, and then 4.6 ml of the spent monosulfite liquor of the Arkhangelsk PPM with a density of 1.048 at 21 s were added to 1 g of cellulose and kept at 7 p-80 C for 1 hour. pH among the treatment was 9.7. After treatment, the mass was washed on a Büchner funnel with water and the cellulose yield was determined, the content of pentrzans according to GOST 10820-75, and the mechanical parameters of the pulp 7 The obtained results are presented in table B (1 row). . .
Судафатна целлюлоза, обработанна по пред1Юб ,1 11,8 лагаемому способуSudafatna cellulose, processed according to pred1yub, 1 11.8 lagged method
Сульфатна целлюлоза, „„ обработанна по из- . , вестному способу 103,0 12,4Sulphate pulp, “„ processed by iz. the known method 103.0 12.4
.- ,ts Сульфатна целлюлоза, - , промыта водой 100,0 9,1.-, ts Sulphate cellulose, -, washed with water 100.0 9.1
Сульфитна целлюлоз, обработайна по пред105 ,9 лагаемому способуSulphite pulp, processed according to the previous 105, 9 lagged process
iСульфитна целлюлоза, ОгГ ,Sulfite pulp, OGG,
100,0 промыта водой100.0 washed with water
П р и м е р 2. Сульфатную нёбеле ную целлюлоз промывали водой ни Во ронке Бюхнера до бесцветных промывных вод и затем подвергали обработке с моносульфитным щелоком в уй лйви х примера 1. Дальнейшую обработку наполн ли аналогично примеру 1. Полу гёйные результаты представлены в таблй11е (2 строка) . .ч EXAMPLE 2 Sulfate pulp and cellulose was washed with Buchner water to colorless wash water and then subjected to treatment with monosulfite liquor in the formula of Example 1. Further processing was filled in the same way as in Example 1. Semi-henary results are presented in Table 11. (2 line). .h
Пример 3. Дл сравнени сульфатную небеленую целлюлозу, промытую водой до бесцветны: npO viafffi °SS2, анализировали, как в примере 1. Полученные результаты представлены в таблице (3 строка). -.Г,,,Example 3. For comparison, unbleached sulphate pulp, washed with water to colorless: npO viaffffi ° SS2, was analyzed as in example 1. The results obtained are presented in the table (3rd row). -.Г ,,,
Пример 4. Промытую суль(11итную небеленую целлюлозу ApxaJirejtbCKOго ЦБК смешивали с сульфитным отработанньм щелоком (5 мл/г целлюлозы) плотностью 1,048 при 20°С и нагревали за 10. мин до 70-80С. Затем добавл ли моносульфйтный щелок в количестве 4,5 мл/г целлюлозы и обрабатывали как в примере 1. Промывку целлюлозы после обработки и определение выхода и механических СВОЙСТВ осуществл ли аналогично примеру IV Полученные Е 1 ЭуЛьтаты представлены в таблице (4 строка ) . -- - ---Example 4. Washed Sul (11x Unbleached Cellulose ApxaJirejtbCKO pulp and paper mill was mixed with sulphite waste liquor (5 ml / g cellulose) with a density of 1.048 at 20 ° C and heated in 10 minutes to 70-80 ° C. Then 4.5% monosulfite liquor was added. ml / g of cellulose and treated as in Example 1. The washing of the cellulose after treatment and the determination of yield and mechanical PROPERTIES was carried out analogously to Example IV. The obtained E 1 values are presented in the table (4th row). - - ---
88008800
6,46.4
19nineteen
6493 6493
1818
6,0 6.0
19 8490 6,319 8490 6.3
4,0 4.0
76507650
3131
6990 3,76990 3.7
3636
Пример 5. Дл сравнени проМытую сульфитную небеленую целлюлозу Example 5. For comparison, washed washed sulphite unbleached pulp.
анализировали как в примере 4 (5 строка ) . ..-...-. analyzed as in example 4 (line 5). ..-...-.
Как ййдно из таблицы выход сульфатной цёлЛюлОзы увеличилс на 6,1%, а сульфитной целлюлозы на 5,9%. По сравнению с известным способом выход сульфатной Небеленой Целлюлозы вьйае на 3,1%, тМкак содержание пентозанов в целлюлозах примерно одинаковое, увеличение выхода целлюлозы по предлагаеиому способу может быть объ снено осаждением в услови хобработки мрносулЬфитным щелоком некоторого количества лигнина из сульфаТногр щелрка. Механические показатели:отливокAs shown in the table, the yield of sulfate cellulose increased by 6.1%, and sulfite pulp increased by 5.9%. Compared with the known method, the yield of sulphate unbleached pulp is 3.1%, the tM as the content of pentosans in cellulose is about the same, the increase in the yield of cellulose in the proposed method can be explained by precipitation of some lignin from sulphate under monogrammed lye. Mechanical performance: castings
сульфатной целлюлозы остались на прежнем уровне, у сульфитной - увеличились на 8-10%.sulphate pulp remained at the same level, at sulphite pulp - increased by 8-10%.
Claims (2)