Description
Изобретение относитс к электроламповой области промышленности и предназначено дл использовани в производстве газоразр дных источников света, в частности натриевых ламп высокого давлени .The invention relates to the electric lamp industry and is intended for use in the manufacture of gas-discharge light sources, in particular high-pressure sodium lamps.
Известны металлические припои, примен ющиес дл соединени металла с керамикойMetal solders are known that are used to join metal to ceramics.
1 Недостатком спаев, полученных ири использовании данных припоев, вл етс их низка надежность в эксплуатации из-за различи значений температурных коэффициентов линейного расширени керамики и металла.1 The disadvantage of solders obtained using these solders is their low operational reliability due to the difference in the temperature coefficients of linear expansion of ceramics and metal.
Наиболее близким техническим решением к изобретению вл етс стеклокерамический Ириной, включающий окислы алюмини , кальци магни , циркони 2J.The closest technical solution to the invention is a glass-ceramic Irina, including oxides of aluminum, calcium magnesium, zirconium 2J.
Однако такие стеклокерамические цементы имеют иедостаточное адгезионное сцепление с керамикой и с металлом, что приводит к ухудшению качества спа , число термоударов, которое выдерживает спай, не тер вакуумной плотности, невелико.However, such glass-ceramic cements have an inadequate adhesive adhesion to ceramics and metal, which leads to a deterioration in the quality of the spa, the number of thermal shocks that the junction can withstand, without losing vacuum density, is small.
Цель изобретени - иовышение прочности сцеплени .The purpose of the invention is to increase the adhesion strength.
Достигаетс это тем, что предлагаемый стеклокерамическнй припой, включающий двуокись циркоии , скись кальци и соединени алюл:;П1:; и магни , содержит два последних соединапьч в в де оксисолей iijv.i следующем соотноиюнии колиюнснтов, вес.%:This is achieved by the fact that the proposed glass-ceramic solder, including zirconium dioxide, calcium oxide and aluyl compounds:; P1 :; and magnesium, contains the last two compounds in de oxysols iijv.i of the following coloint ratio, wt.%:
Дв окнсь циркони Окись кальци Оксисоль алюмини Оксисоль магни Twin Zirconia Calcium Oxide Aluminum Oxysol Magnesium Oxisol
Оксисоли ири высыхании и выжигани из суспензии образуют соединени , обладающие значительно, адгезионно-когезионной прочностью , при термообработке разлагаютс до соответствующих окислов.Oxides and salts, after drying and burning out of the suspension, form compounds that possess significant adhesive and cohesive strength; during thermal treatment, they decompose to the corresponding oxides.
Суспензию стеклоцемеита готов т по обычной технологии, прин той на производстве. Пайку производ т в вакууме или же в инертHoii среде при 1500° С.The steklocemeite suspension is prepared according to the usual technology adopted in production. Soldering is carried out in vacuum or in inertHoii medium at 1500 ° C.
Результаты иенытаний ламп, горелки которых изготовлены с применением предлагаемого стеклокерамического припо приведены в таблице.The results of the lamps of which the burners are manufactured using the proposed glass-ceramic solder are shown in the table.
При использовании вместо оксисолей окислов алюмини и магни лампы выдерживают Е среднем только 936 включений.When aluminum oxides and magnesium are used instead of oxysols, the lamps withstand an E average of only 936 inclusions.
Claims (2)
Priority Applications (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| SU762439762A SU600124A1 (en) | 1976-11-09 | 1976-11-09 | Glass-ceramic fusing compound |
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| SU762439762A SU600124A1 (en) | 1976-11-09 | 1976-11-09 | Glass-ceramic fusing compound |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| SU600124A1 true SU600124A1 (en) | 1978-03-30 |
Family
ID=20690488
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| SU762439762A SU600124A1 (en) | 1976-11-09 | 1976-11-09 | Glass-ceramic fusing compound |
Country Status (1)
| Country | Link |
|---|---|
| SU (1) | SU600124A1 (en) |
Cited By (2)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| GB2231524A (en) * | 1989-02-15 | 1990-11-21 | English Electric Co Ltd | Metal and ceramic-substrate bonding |
| RU2487000C2 (en) * | 2011-09-07 | 2013-07-10 | Юрий Петрович Петренко | Cermet solder |
-
1976
- 1976-11-09 SU SU762439762A patent/SU600124A1/en active
Cited By (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| GB2231524A (en) * | 1989-02-15 | 1990-11-21 | English Electric Co Ltd | Metal and ceramic-substrate bonding |
| GB2231524B (en) * | 1989-02-15 | 1993-09-01 | English Electric Co Ltd | Metal-ceramic-substrate bonding |
| RU2487000C2 (en) * | 2011-09-07 | 2013-07-10 | Юрий Петрович Петренко | Cermet solder |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| ES446625A1 (en) | Anti-inflammatory methods using 2-amino-3-(5- and 6-)benzoylphenylacetic acids, esters and metal salts thereof and the compounds | |
| SU600124A1 (en) | Glass-ceramic fusing compound | |
| GB1231517A (en) | ||
| GB1457627A (en) | Glass soldering mixture | |
| SU654584A1 (en) | Ceramic solder | |
| SU767866A1 (en) | Protective coating for burners of lithium gas discharge lamps | |
| SU643473A1 (en) | Frit | |
| ES8502983A1 (en) | 5-(4-Chloro-3-sulfamoylbenzoyl)-2,3-dihydro-2-benzofuran-carboxylic acids and process for their preparation. | |
| SU1206269A1 (en) | Slip for manufacturing refractory articles | |
| SU977419A1 (en) | Glass | |
| SU633835A1 (en) | Glaze | |
| GB2010242A (en) | Alumina, calcia, baria sealing composition and article of manufacture | |
| SU1091929A1 (en) | Coating for dentures | |
| FR433131A (en) | Improvements in the preparation of refractory metal bodies used in the manufacture of incandescent lamps | |
| US2098811A (en) | Composite body | |
| SU1638135A1 (en) | Composition of refractory oxidation-protective coating | |
| SU546576A1 (en) | Glass | |
| FI821583L (en) | NYA 1-PYRROLINTIOLAKTIMETRAR OCH FOERFARANDE FOER DERAS FRAMSTAELLNING | |
| SU729694A1 (en) | Composition of reflective coating for electric lamps | |
| SU1413094A1 (en) | Refractory mixture | |
| SU1172895A1 (en) | Black glass | |
| SU409976A1 (en) | ||
| SU890485A1 (en) | Amalgam for luminescent lamps | |
| SU633832A1 (en) | Glass cement for soldering metal with ceramics | |
| SU996499A1 (en) | Cermet material based on nickel for soldering metal with glass |