SU558085A1 - Bumjana mass for the manufacture of packaging material - Google Patents
Bumjana mass for the manufacture of packaging materialInfo
- Publication number
- SU558085A1 SU558085A1 SU2141978A SU2141978A SU558085A1 SU 558085 A1 SU558085 A1 SU 558085A1 SU 2141978 A SU2141978 A SU 2141978A SU 2141978 A SU2141978 A SU 2141978A SU 558085 A1 SU558085 A1 SU 558085A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- semi
- finished product
- pulp
- cooking
- fibrous
- Prior art date
Description
лабораторном ролле. При этом фиксируют врем размола и степень помола массы, определ ют прочность полотна во влажном состо нии по Брехту и межволоконные силы св зи по Иванову.laboratory roll. At the same time, the grinding time and the degree of grinding of the mass are recorded, the strength of the web in the wet state according to Brecht and the interfiber bonding forces according to Ivanov are determined.
Р1звестна бумажна масса имеет следующий состав, вес. %:Known pulp has the following composition, weight. %:
Полуфабрикат, сваренный нейтрально-сульфитным сиособом 83,5 Целлюлоза сульфатна небелена 15 ,0 Проклеивающее вещество0,5 Осадитель1,0 Предлагаема бумажна масса имеет следующий состав, вес. %:Prefabricated, welded with neutral sulphite method 83.5 Cellulose sulphate unbleached 15, 0 Sizing agent 0.5 Precipitant1.0 The offered paper pulp has the following composition, weight. %:
Полуфабрикат, полученный с использованием в качестве варочного раствора смеси мопосульфита и черного сульфатного щелока84,0 Целлюлоза сульфатна небелена 15 ,0 Осадитель1,0 Из полученных бумажных масс отливают образцы бумаги дл гофрировани .The semi-finished product obtained using a mixture of mosposulfite and black sulphate liquor as a cooking solution84.0 Cellulose sulphate unbleached 15, 0 Precipitant1.0 Samples of corrugated paper are cast from the resulting paper masses.
Сопоставление параметров размола и результатов анализа образцов бумаги представлено в табл. 1.Comparison of grinding parameters and results of analysis of paper samples are presented in Table. one.
Таблица 1Table 1
влажном состо нии повыщаетс . Также исключаетс надобность добавки ироклеивающего вещества.the wet state rises. It also eliminates the need for the addition of a glue agent.
П р и м е р 2. В производственных услови х получают бумагу дл гофрировани из пейтрально-сульфнтной полуцеллюлозы и волокнистого иолуфабриката, полученного с использованием смеси моносульфита и черного сульфатного щелока.PRI mme R 2. Under production conditions, paper for corrugating is produced from peutral sulfonic hemicellulose and fibrous iolufabrikaat obtained using a mixture of monosulfite and black sulfate lye.
Полученные полуфабрикаты размалывают в две ступени на участке полумассного размола, сортпруют, промывают и подают на двухступенчатый массный раз1мол до 25-27°ШР. Известна бумажна масса имеет следующий состав, вес. % :The obtained semi-finished products are milled in two steps on the site of semi-mass grinding, sorted, washed and served on a two-stage mass of 1 mol to 25-27 ° ShR. Known pulp has the following composition, weight. %:
Полуфабрикат, сваренный нейтрально-сульфитным способом 73,5 Целлюлоза сульфатна небелена 25 ,0 Проклеивающее вещество0,5 Осадитель1,0 Предлагаема бумажна масса имеет следующий состав, вес. %:Prefabricated, brewed by neutral sulphite method 73.5 Cellulose sulphate unbleached 25, 0 Sizing agent 0.5 Precipitant1.0 The offered paper pulp has the following composition, weight. %:
Полуфабрикат, полученный с использованием в качествеThe semifinished product obtained using as
варочиого раствора смеси моносульфита и черного сульфатного щелока89,0 Целлюлоза сульфатна небелепа 10 ,0 Осадптель1,0 Основные параметры процесса и показатели бумаги дл гофрировани иредставлены в табл. 2. Т а б л и ц а 2a mixture of monosulphite and black sulphate liquor 89,0 Cellulose sulphate non-whitewash 10, 0 Osadptel1,0 The main process parameters and indicators of paper for corrugation are presented in Table. 2. T a b e c i a 2
Таким образом, при использовании полуфабриката , полученного с использованием смеси моносульфцта и черного сульфатного щелока, физико-механические показатели бумаги дл гофрировани новыщаютс , а расход энергии на размол бумажной массы из этого полуфабриката снижаетс .Thus, when using a semi-finished product obtained using a mixture of monosulphate and black sulphate liquor, the physicomechanical indicators of corrugated paper are increased, and the energy consumption for grinding the pulp from this semi-finished product is reduced.
Следовательно, при нспользовании дешевого волокнистого полуфабриката, получаемого с применением дл варкн смеси моносульфита и черного сульфатного щелока, ири получеиим высоких физико-механических иоказателей бумаги дл гофрировани , расход энергии на размол снижаетс и прочность иолотна воConsequently, when using cheap fiber semi-finished product obtained using a mixture of monosulfite and black sulphate liquor for warn, and the resultant high physicomechanical corrugation paper indicators, the grinding energy consumption decreases and
Как видно из представленных данных при использовании более дещевого полуфабриката , иолученного с использованием на варку смеси моносульфита и черного сульфатного щелока, физико-механические показатели бумаги дл гофрировани иовыщаютс , снижены расход эиергии на размол на 160 квтч/т и содержаиие сульфатиой целлюлозы в комгозиции массы.As can be seen from the presented data, when using a more benign semi-finished product obtained using a mixture of monosulfite and black sulphate liquor for cooking, the physicomechanical indicators of corrugated paper are increased, the energy consumption for grinding is reduced by 160 kwh / ton and the cellulose sulphate content is reduced.
Следовательно, предлагаема бумажна масса дл изготовлени тароупаковочного материала дает возможность получить качественную бумагу дл гофрировани из более дешевого волокнистого сырь при снижении расхода энерг П1 иа размол и исключении проклеивающего вещества.Consequently, the proposed paper pulp for the manufacture of packaging material makes it possible to obtain high-quality corrugated paper from cheaper fiber raw materials while reducing the consumption of energy P1 and grinding and exclusion of the sizing agent.
Пример 3. В лабораторных услови х полуфабрикат, полученный пейтральпо-сульфитным способом и волокнистый полуфабрикат , сваренный с использованием смеси моносульфпта и черного сульфатного щелока, размалывают в две ступени на лабораторной дисковой мельнице и лабораторном ролле. При этом фиксируют врем размола, степень помола массы, определ ют прочность полотна во влажном состо нии по Брехту и межволоконпые силы св зи по Иванову. Известна бумажна масса имеет следующий состав, вес. %: Полуфабрикат, сваренный нейтрально-сульфитным способом 50,0 Целлюлоза сульфатна небелена 48 ,5 Проклеивающее вещество0,5 Осадитель1,0 Предлагаема бумажна масса пмеет следующий состав, вес. %:Example 3. In laboratory conditions, the semi-finished product obtained by the glass-sulfite method and the semi-finished fibrous material, welded using a mixture of monosulfft and black sulfate liquor, are milled in two steps on a laboratory disk mill and a laboratory roll. At the same time, the grinding time, the degree of grinding of the mass are recorded, the durability of the web is determined in the wet state according to Brecht, and the intervolume bonding forces in Ivanov. Known pulp has the following composition, weight. %: Prefabricated, brewed by neutral-sulfite method 50.0 Cellulose sulphate unbleached 48, 5 Sizing agent 0.5 Precipitant1.0 The proposed paper pulp has the following composition, weight. %:
Полуфабрикат, полученный с использованием в качестве варочного раствора смеси моносульфита и черного сульфатного щелока50,0 Целлюлоза сульфатна пебелена 49 ,0Semi-finished product obtained using a mixture of monosulfite and black sulphate liquor as a cooking solution 50.0 Cellulose sulphate pebelin 49, 0
Осадитель1,0.The precipitator1.0.
Из иолученпых бумажных масс отливают образцы картона дл гладких слоев гофрированного картона.Samples of cardboard for smooth layers of corrugated cardboard are cast from molded paper masses.
Сопоставление параметров размола и результатов анализа образцов картона представлено в табл. 3.Comparison of grinding parameters and results of the analysis of samples of cardboard are presented in Table. 3
Таблица 3Table 3
Прп использовании полуфабрпката, свареиного со смесью моносульфита п черного сульфатного щелока, физико-механические показатели картона повышаютс , а расход энергии на размол бумажной массы с использованием этого полуфабрпката сппжаетс , о чем свидетельствует сокращение продолжительности размола до конечной степени разработки массы с 42-46 MiiH до 13-16 мин, также исключаетс надобность в введении проклеиваюпдего Benj,ecTBa.Using a semi-finished product, which is welded with a mixture of monosulfite and black sulphate liquor, the physical and mechanical properties of the paperboard increase, and the energy consumption for grinding paper pulp using this semi-finished product is reduced, which is indicated by a reduction in the duration of grinding to a final mass development from 42-46 MiiH to 13-16 min, also eliminating the need for the introduction of a sizing Benj, ecTBa.
Следует отметить, что содержание полуфабрпката высокого выхода в картоне марки К-1 и К-2 ГОСТ 7420-69 не нормируетс .It should be noted that the content of the high-yield semi-finished product in cardboard grade K-1 and K-2 GOST 7420-69 is not standardized.
При м е р 4. В производственных услови х иолучают картон дл гладких слоев гофрированного картона из бумажных масс, композици которых состоит из сульфатной целлюлозы и полуфабрпката высокого выхода, иолучеппого либо нейтрально-сульфитным способом , либо сваренного с использованием смеси моиосульфита и чериого сульфатного щелока .Example 4. Under production conditions, cardboard is produced for smooth layers of corrugated cardboard made from paper pulp, the composition of which consists of sulphate pulp and a high-yield semi-finished product, either with a finite or neutral sulphite method, or welded using a mixture of myosulphite and black sulfate liquor.
Р1звестна бумажна масса пмеет следующий состав, вес. %:Known paper pulp has the following composition, weight. %:
Полуфабрнкат, сваренный нейтрально-сульфитным способом Целлюлоза сульфатна небеле45 0,5 1,0 на Neutral sulfite brewed semifabrnat pulp method Cellulose sulphate nebele45 0.5 1.0 on
Проклеивающее вепдество ОсадительSizing Warrior Osaditel
Предлагаема бумажна масса пмеет следующий состав, вес. %:We offer pulp dough the following composition, weight. %:
Полуфабрикат, получеппый с использованием в качестве варочиого раствора смеси моносульфита п черного суль54 .0 фатного щелока Целлюлоза сульфатна небеле45 .0 1,0 на ОсадительSemi-finished product, obtained using black monosulfite and black sul54 .0 fatty liquor cellulose sulphate oil 45 .0 1.0 per precipitator as a boiling solution.
Основные параметры процесса п показатели картона представлены в табл. 4.The main parameters of the process and cardboard indicators are presented in Table. four.
Таблица 4Table 4
Claims (1)