SU549493A1 - Nickel based alloy - Google Patents

Nickel based alloy

Info

Publication number
SU549493A1
SU549493A1 SU2168333A SU2168333A SU549493A1 SU 549493 A1 SU549493 A1 SU 549493A1 SU 2168333 A SU2168333 A SU 2168333A SU 2168333 A SU2168333 A SU 2168333A SU 549493 A1 SU549493 A1 SU 549493A1
Authority
SU
USSR - Soviet Union
Prior art keywords
alloy
based alloy
nickel
nickel based
thermal expansion
Prior art date
Application number
SU2168333A
Other languages
Russian (ru)
Inventor
Виктор Иванович Леванов
Анатолий Сергеевич Смирнов
Мелитина Петровна Матвеева
Алевтина Михайловна Самарина
Ольга Петровна Забелина
Мария Александровна Казачкова
Original Assignee
Центральный научно-исследовательский институт стоматологии
Институт Металлургии Имени А.А.Байкова Ан Ссср
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Центральный научно-исследовательский институт стоматологии, Институт Металлургии Имени А.А.Байкова Ан Ссср filed Critical Центральный научно-исследовательский институт стоматологии
Priority to SU2168333A priority Critical patent/SU549493A1/en
Application granted granted Critical
Publication of SU549493A1 publication Critical patent/SU549493A1/en

Description

(54) СПЛАВ НА ОСНОВЕ НИКЕЛЯ(54) NICKEL-BASED ALLOY

Изобретение относитс  к металлургии, в частности, к литейным сплавам на основе никел , используемым дл  изготовлени  несъемных стоматологических протезов с фарфоровым покрытием, и может найти широкое применение в стоматологической практике. Известен сплав на основе никел  следующего химического состава (в вес. %): 8,0-20,0 Молибден 0,4-4,0 Алюминий 0,5-5,0 Бериллий 0,3-3,5 Углерод 0,03-0,3 Никель Остальное Сплав имеет коэффициент термического расширени  при 500° С 130-150- 10 /град. Недостатком сплава  вл етс  большой коэффициент термического расширени  по сравнению с фарфором (90-120- 0 /град), что приводит после охлаждени  к образованию трещин. Наиболее близким к изобретению по со ставу ингредиентов  вл етс  сплав на основе никел  следующего химического состава (в вес. %): 5,0-30,0 Хром Алюминий 0,1-9,0 0,1-6,5 0-15,0 Вольфрам Кремний 0,01-0,3 Углерод Л1арганец Остальное Никель Сплав может содержать кобальт, молибден , ниобий, гафний, тантал, ванадий, бор, железо, цирконий и другие элементы, обуславливающие растворное и дисперсионное упрочнение сплава. Данный сплав предназначен дл  изготовлени  газовых турбнн и имеет высокую прочность при высоких температурах. Недостатком известного сплава  вл етс  высокое значение коэффициента термического расширени  и низка  прочность сцеплени  с фарфором из-за отсутстви  в сплаве рени . Целью изобретени   вл етс  снижение коэффициента термического расширени  и повышение прочности сцеплени  сплава с фарфором . Зта цель достигаетс  тем, что- сплав на основе никел , содержащий хром, алюминий, титан, вольфрам, кремний, марганец, дополнительно содерл :ит рений при следующем соотношении комионентов (в вес. %):The invention relates to metallurgy, in particular, to nickel-based casting alloys used in the manufacture of non-removable dental prostheses with porcelain coating, and can be widely used in dental practice. Known nickel-based alloy of the following chemical composition (in wt.%): 8.0-20.0 Molybdenum 0.4-4.0 Aluminum 0.5-5.0 Beryllium 0.3-3.5 Carbon 0.03 -0.3 Nickel Else The alloy has a coefficient of thermal expansion at 500 ° C 130-150-10 / deg. The disadvantage of the alloy is a large coefficient of thermal expansion compared with porcelain (90-120-0 / degree), which, after cooling, leads to the formation of cracks. The closest to the invention in terms of the composition of ingredients is a nickel-based alloy of the following chemical composition (% by weight): 5.0-30.0 Chromium Aluminum 0.1-9.0 0.1-6.5 0-15 , 0 Tungsten Silicon 0.01-0.3 Carbon L1 manganese Else Nickel Alloy may contain cobalt, molybdenum, niobium, hafnium, tantalum, vanadium, boron, iron, zirconium and other elements causing the solution and dispersion hardening of the alloy. This alloy is intended for the manufacture of gas turbines and has high strength at high temperatures. A disadvantage of the known alloy is the high value of the thermal expansion coefficient and the low adhesion strength with porcelain due to the absence of rhenium in the alloy. The aim of the invention is to reduce the thermal expansion coefficient and increase the adhesion strength of the alloy with porcelain. This goal is achieved by the fact that a nickel-based alloy containing chromium, aluminum, titanium, tungsten, silicon, manganese, additionally containing: it rhenium in the following ratio of comonents (in wt.%):

SU2168333A 1975-08-21 1975-08-21 Nickel based alloy SU549493A1 (en)