SU515822A1 - Structural steel - Google Patents
Structural steelInfo
- Publication number
- SU515822A1 SU515822A1 SU1809949A SU1809949A SU515822A1 SU 515822 A1 SU515822 A1 SU 515822A1 SU 1809949 A SU1809949 A SU 1809949A SU 1809949 A SU1809949 A SU 1809949A SU 515822 A1 SU515822 A1 SU 515822A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- structural steel
- temperatures
- steel
- structural
- toughness
- Prior art date
Description
1one
Изобретение относитс к области изыскани хладостойких конструкционных сталей, предназначенных дл работы при температурах от (-|-20°С) до (-80°С).The invention relates to the field of research on cold-resistant structural steels intended for operation at temperatures ranging from (- | -20 ° C) to (-80 ° C).
Известна конструкционна сталь, содержаща углерод, кремний, марганец, никель и железо.Structural steel containing carbon, silicon, manganese, nickel and iron is known.
Предлагаема сталь отличаетс от известной тем, что, с целью повышени прочности и ударной в зкости при температурах от -(-20°С до -80°С, в нее введен вольфрам при следующем соотношении компонентов, %: Углерод0,37-0,43The proposed steel differs from the known one in that, in order to increase strength and toughness at temperatures from - (-20 ° C to -80 ° C, tungsten is introduced into it in the following ratio of components,%: Carbon0.37-0.43
Кремний0,17-0,37Silicon0.17-0.37
Марганец0,4-0,8Manganese0.4-0.8
Пикель0,7-1,0Pickel0.7-1.0
Вольфрам0,4-0,6Tungsten0.4-0.6
ХромПе более 0,3ChromePe more than 0.3
СераНе более 0,03Sulfur Not more than 0.03
ФосфорНе более 0,03Phosphorus not more than 0.03
ЖелезоОстальноеIronErest
Механические свойства стали после термической обработки по режиму (закалка в масле от 820-830°С и отпуск при 600°С с последующим охлаждением в масле или с печью) следующие:The mechanical properties of the steel after heat treatment according to the mode (oil hardening from 820-830 ° C and tempering at 600 ° C, followed by cooling in oil or with a furnace) are as follows:
Предел прочности, кг/мм 95-105Strength, kg / mm 95-105
Предел текучести, кт/мм-85-90Yield point, kt / mm-85-90
Относительное удлинение, %17-19Relative lengthening,% 17-19
Относительное сужение, %58-61Relative narrowing,% 58-61
3 Предмет изобретени 3 Subject of the invention
Конструкционна сталь, содержаща углерод , кремний, марганец, никель и железо, отличающа с тем, что, с целью повышени прочности и ударной в зкости при температурах от +20°С до -80°С, в нее введен вольфрам при следующем соотношении компонентов , %:Structural steel containing carbon, silicon, manganese, nickel and iron, characterized in that, in order to increase strength and toughness at temperatures from + 20 ° C to -80 ° C, tungsten is introduced into it in the following ratio of components, %:
0,37-0,430.37-0.43
0,17-0,370.17-0.37
0,4-0,80.4-0.8
0,7-1,00.7-1.0
0,4-0,60.4-0.6
ОстальноеRest