1one
Изобретение относитс к изысканию хромистых сталей мартенситного класса, работающих при температурах до и предназначенных дл изготовлени сварной химической аппаратуры.The invention relates to the search for chromium steels of the martensitic class, operating at temperatures up to and intended for the manufacture of chemical welded apparatus.
Известна сталь Х5М этого класса и назначени состава, вес.%:Known steel H5M of this class and the composition, wt.%:
До 0,15 До 0,5 До 0,5 4,5-6 0,45-0,6 ОстальноеUp to 0.15 To 0.5 To 0.5 4.5-6-6 0.45-0.6 Else
После закалки с 90О-1200°С сталь имеет твердость НВ 363-472 и ударную в зкость 0,3-4,9 кгм/см.After quenching from 90 ° –1200 ° C, the steel has a hardness of HB 363–472 and a impact strength of 0.3–4.9 kgm / cm.
Однако известна сталь имеет повышенную твердость и низкую ударную в зкость после закалки, у нее наблюдаетс образование трещин при изготовлении сложных деталей методом гор чего деформировани , склонность к образованию трешин в околощовной зоне сварных соединений при охлаждении со скоростью более .However, steel is known to have increased hardness and low toughness after quenching, it has the formation of cracks in the manufacture of complex parts by hot deformation, a tendency to the formation of cracks in the near-weld zone of welded joints during cooling at a rate higher.
Цель изобретени - уменьшить склонность к закалке.The purpose of the invention is to reduce the tendency to quench.
Дл этого предлагаема сталь дополн{1тельно легирована ниобием, цирконием и кальцием.For this, the proposed steel is additionally {1 alloyed with niobium, zirconium and calcium.
Сталь имеет следующий состав, вес.%:Steel has the following composition, wt.%:
0,09-0,150.09-0.15
0,1-0,80.1-0.8
0,1-О,50,1-O, 5
4,5-64.5-6
0,45-0,60.45-0.6
0,4-0,80.4-0.8
О,О5-0,1Oh, O5-0,1
О,О1-0,О-1O, O1-0, O-1
ОстальноеRest
Сталь имеет следующие свойсSteel has the following properties.
Температура испытани , °СTest Temperature, ° C
Предел прочности, кг/мм Strength, kg / mm
Предел текучести, кг/мм2.Yield point, kg / mm2.
Ударна в зкость, кгм/см Impact viscosity, kgm / cm
Относительное удлинение,%Relative extension,%
После закалки в воду с температурой 25 9ОО-120О°С твердость стали составл ет НВ 143-312, а ударна в зкость 6-16 кгм/см. Сталь не склонна к образованию трешин в околошоБной зоне сварных соединений при охлаждении со скоростью не выш 20-230/сек. Ударна в зкость металла участков околошовной зоны не ниже 10 кгм/см2. зобретени Формул Теплоустойчива сталь, содержаща уг лерод, кремний, марганец, хром, молибде железо, отличающа с тем, что, с целью уменьшени склонности к за повышени деформируемости при выих температурах и улучшени сваривае-, сти, она дополнительно содержит ниобий, . коний ,и кальций при следуюшем соотении компонентов, вес.%: О,О 9-0-,15 Углерод 0,1-4Э,8 Кремний 0,1-0,5 Марганец 0,45-0,6 Молибден 0,4-0,8 Ниобий Цирконий 0,О5-О,1 Кальций 0,01-0,04 Железо ОстальноеAfter quenching in water with a temperature of 25 9OO-120 ° C, the hardness of the steel is HB 143-312, and the impact strength is 6-16 kgm / cm. Steel is not prone to the formation of cracks in the near-weld zone of welded joints when cooled at a rate not exceeding 20-230 / s. The impact viscosity of the metal of the heat-affected zone is not lower than 10 kgm / cm2. The invention of heat resistant steel containing carbon, silicon, manganese, chromium, molybdenum iron, characterized in that, in order to reduce the tendency to increase deformability at high temperatures and to improve weldability, it additionally contains niobium,. horse and calcium, with the following ratio of components, wt.%: O, O 9-0-, 15 Carbon 0.1-4E, 8 Silicon 0.1-0.5 Manganese 0.45-0.6 Molybdenum 0.4 -0.8 Niobium Zirconium 0, O5-O, 1 Calcium 0.01-0.04 Iron Rest
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SU2116995A SU511381A1 (en) | 1975-01-15 | 1975-01-15 | Heat resistant steel |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SU2116995A SU511381A1 (en) | 1975-01-15 | 1975-01-15 | Heat resistant steel |
Publications (1)
Publication Number | Publication Date |
---|---|
SU511381A1 true SU511381A1 (en) | 1976-04-25 |
Family
ID=20613825
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
SU2116995A SU511381A1 (en) | 1975-01-15 | 1975-01-15 | Heat resistant steel |
Country Status (1)
Country | Link |
---|---|
SU (1) | SU511381A1 (en) |
-
1975
- 1975-01-15 SU SU2116995A patent/SU511381A1/en active
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JPS61130462A (en) | High-touchness extra high tension steel having superior stress corrosion cracking resistance as well as yield stress of 110kgf/mm2 and above | |
KR20070091368A (en) | High tensile and fire-resistant steel excellent in weldability and gas cutting property and method for production thereof | |
US4740255A (en) | High strength weldable seamless tube of low alloy steel | |
JPH02254120A (en) | Production of high tension strength steel having excellent weldability and low temperature toughness | |
SU511381A1 (en) | Heat resistant steel | |
US3463677A (en) | Weldable high strength steel | |
WO1986007096A1 (en) | Process for producing high-strength seamless steel pipes excellent in sulfide stress corrosion cracking resistance | |
JP2000178697A (en) | Martensitic stainless steel excellent in corrosion resistance and weldability | |
JPS6216250B2 (en) | ||
JPS6112849A (en) | Reinforced steel bar having excellent low-temperature toughness and sea water resistance | |
JPS6148521A (en) | Manufacture of reinforcing bar steel superior in low temperature toughness and strength | |
JPH0219175B2 (en) | ||
CN114196880B (en) | High-strength low-yield-ratio austenitic stainless steel and preparation method thereof | |
CA1276893C (en) | High strength weldable seamless tube of low alloy steel | |
JP2005307313A (en) | Method for producing steel plate excellent in earthquake-proof and weldability | |
SU569648A1 (en) | Refractory chromium steel | |
JPH0225969B2 (en) | ||
JPS6358892B2 (en) | ||
SU865963A1 (en) | Steel | |
JPS62263922A (en) | Production of forged steel | |
JPS62149814A (en) | Production of low-carbon high-strength seamless steel pipe by direct hardening method | |
JPS60243250A (en) | High-hardness wear-resistant steel having superior weldability | |
SU855060A1 (en) | Steel | |
SU1749307A1 (en) | Steel | |
JPWO2006064553A1 (en) | 655 MPa grade martensitic stainless steel excellent in toughness and method for producing the same |