Description
1one
Изобретение относитс к химической обработке древесины, в частиости к способу получени модифицированной древесины.The invention relates to the chemical treatment of wood, in part, to a method for producing modified wood.
Известен способ получени модифицированной древесины с введением в нее после предварительной ее вакуумизацши мономера с последуюи1 ,ей его нолимеризацней.A known method for producing modified wood with the introduction of a monomer with its subsequent vacuumization into it, followed by 1, is not polymerized.
Однако известный способ не обеспечивает высокого качества модифицированной древесиш: . и обладает продолжительным процессом полимеризации, который осуществл ют, например , радиационным облучением.However, the known method does not provide high quality modified wood:. and has a long polymerization process, which is carried out, for example, by radiation exposure.
С целью интенсификации процесса иолимеризации , повышени качества модифицированной древесины и расширени ассортимента пластифицирующих материалов по предложенному снособу древесину после вакуумизации в течение 1--Зчас обрабатывают в нарах хлороирена в течение 5-7 час при температуре 50-70°С с последующей технологической выдержкой до полной полимеризации хлоропрена .In order to intensify the imerization process, improve the quality of modified wood and expand the range of plasticizing materials, according to the proposed pulling-out wood, after evacuation for 1–3 hours, it is treated in chloroirene beds for 5-7 hours at a temperature of 50-70 ° C, followed by technological aging to complete polymerization of chloroprene.
Способ реализуетс следующим образом.The method is implemented as follows.
Предварительно вакуумированную древесину в течение 1-Зчас загружают в автоклав, Pre-evacuated wood is loaded into the autoclave for 1–3 hours,
УHave
В который направл етс хлоронрен, подвер нутый вакуумной лерегонке в атмосфере азота . Автоклав нагревают до температ}ры кнпени хлоропрена и выдерживают в течение 5-7 час при температуре 50-70°С. Иосле обработки в парах хлоропрена древесину оставл ют на несколько дней (5-10) при комнатной температуре дл завершени полнмернзации до полного отверждени .И ) е д м е г и 3 о б р е ген и Chlororrone is sent to it, subjected to vacuum distillation in a nitrogen atmosphere. The autoclave is heated to chloroprene pressure and maintained for 5-7 hours at 50-70 ° C. After the chloroprene vapor treatment, the wood is left for several days (5-10) at room temperature to complete the full merging until complete curing. And) e d me g and 3 o brie gene and
Способ нолучени модифицированной древесины путем введени в нее после предварительной ее вакуумнзании мономера с последующей его полимеризацией, or.ni4a/oii{iiuc. тем, что, с целью интенсификации процесса полимеризации, повьниени качества модифицированной древесины н раси1ире1ш ассортимента нластифнцнрующи.х материалов, древесину после вакуумизации в течение 1-3 час обрабатывают в парах хлоропрена в теченне 5-7 час при температуре 50-70°С с последующей технологической выдержкой до полной полимеризации хлоропрена.The method of obtaining modified wood by introducing monomer into it after its pre-vacuuming followed by polymerization, or.ni4a / oii {iiuc. By the fact that, in order to intensify the polymerization process, to improve the quality of the modified wood in a wide range of materials and materials, wood after vacuumization for 1-3 hours is treated in chloroprene vapors for 5-7 hours at 50-70 ° C, followed by technological exposure to the complete polymerization of chloroprene.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SU1757713A SU398391A1 (en) | 1972-03-17 | 1972-03-17 | METHOD OF OBTAINING MODIFIED WOOD |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SU1757713A SU398391A1 (en) | 1972-03-17 | 1972-03-17 | METHOD OF OBTAINING MODIFIED WOOD |
Publications (1)
Publication Number | Publication Date |
---|---|
SU398391A1 true SU398391A1 (en) | 1973-09-27 |
Family
ID=20506063
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
SU1757713A SU398391A1 (en) | 1972-03-17 | 1972-03-17 | METHOD OF OBTAINING MODIFIED WOOD |
Country Status (1)
Country | Link |
---|---|
SU (1) | SU398391A1 (en) |
-
1972
- 1972-03-17 SU SU1757713A patent/SU398391A1/en active
Similar Documents
Publication | Publication Date | Title |
---|---|---|
GB975279A (en) | A method of and apparatus for continuous freeze drying | |
SU398391A1 (en) | METHOD OF OBTAINING MODIFIED WOOD | |
IE35925L (en) | Process for treating tobacco. | |
GB871281A (en) | Improvements in and apparatus for purifying high pressure polyethylene | |
US3093560A (en) | Method of preparing polyformaldehyde material having improved characteristics | |
US1952116A (en) | Polymerization of unsaturated organic materials | |
ATE3259T1 (en) | MANUFACTURING SHAPED NETWORKED MATERIALS. | |
US3228865A (en) | Process for polymerizing tetrafluoroethylene | |
SU439159A1 (en) | ||
JPH058202A (en) | Processing method and processing device of bent wood | |
DE2500765C3 (en) | Process for reducing the content of monomeric vinyl chloride in polyvinyl chloride produced by bulk polymerization | |
US676350A (en) | Process of vulcanizing. | |
SU614110A1 (en) | Method of obtaining aminoethoxysilica | |
US2867675A (en) | Process for the polymerization of monoolefin and acetylene hydrocarbons | |
SU713852A1 (en) | Method of thermal moist treatment of concrete articles | |
US1374403A (en) | Process of curing cement | |
US661177A (en) | Process of vulcanization. | |
SU405919A1 (en) | Method of producing crosslinked polybenzoxazole | |
SU977163A1 (en) | Method of chemical modification of wood | |
SU390972A1 (en) | ||
SU670433A1 (en) | Timber-working method | |
US4117220A (en) | Removal of vinyl chloride from pvc resins using microwave radiation | |
DE2503308A1 (en) | Polycaprolactam melt of low monomer content - by treatment of melt in vacuum appts. (BE280776) | |
SU783872A1 (en) | Method of drying capacitors | |
SU24129A1 (en) | Method for simultaneous drying and formalization of various plastics |