SU298950A1 - PIEZOCERAMIC MATERIAL - Google Patents
PIEZOCERAMIC MATERIALInfo
- Publication number
- SU298950A1 SU298950A1 SU1383972A SU1383972A SU298950A1 SU 298950 A1 SU298950 A1 SU 298950A1 SU 1383972 A SU1383972 A SU 1383972A SU 1383972 A SU1383972 A SU 1383972A SU 298950 A1 SU298950 A1 SU 298950A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- mol
- piezoceramic material
- hours
- materials
- b12oz
- Prior art date
Description
Изобретение относитс к материалам, йспользуемым в радиоэлектронике.This invention relates to materials used in electronics.
Известны пьезокерамические материалы на основе твердых растворов цирконата-титаната свинца, .содержащие добавки.Piezoceramic materials based on solid solutions of lead zirconate-titanate, containing additives are known.
Однако эти материалы имеют сравнительно йизкие температуры спекани и электрофизические характеристики.However, these materials have relatively low sintering temperatures and electrophysical characteristics.
Предлагаемый материал отличаетс от известных тем, что он дополнительно содержит окись двухвалентного элемента Са, Ва, Sr, Си, Ln, Cd в количестве 0,5-5 мол. %. Это позвол ет повысить электрофизические характеристики матер.иала.The proposed material differs from the known ones in that it additionally contains an oxide of the divalent element Ca, Ba, Sr, Cu, Ln, Cd in an amount of 0.5-5 mol. % This allows to improve the electrical characteristics of the material.
Дл приготовлени 100 г материала состава РЬ (Zro,53Tio,47) Оз с добавками Li2O 2 мол. %, Bi2O3 1 мол. %, СаО 1 мол. % готов т шихту, состо щую .из следующих компонентов, г: РЬСОз 81,31, ТЮ2 11,55, ZrO2 19,87, В12Оз 1,45, LiaCOs 0,45, СаСОз 0,31. После помола исходных веществ из .полученной шихты изготовл ют брикеты. Брикеты обжигают при 700- 800°С в течение 2 час и затем тщательно .измельчают в порошок с размером частиц 3-5 м,, после чего добавл ют раствор поливинилового спирта в качестве св зки и прессуют издели заданной формы .и величины.To prepare 100 g of the material of composition Pb (Zro, 53Tio, 47) Oz with the addition of Li2O 2 mol. % Bi2O3 1 mol. % Cao 1 mol. % of the prepared mixture consisting of the following components, g: PzCOz 81.31, TiO2 11.55, ZrO2 19.87, B12Oz 1.45, LiaCOs 0.45, CaCOz 0.31. After grinding the raw materials, briquettes are made from the obtained mixture. The briquettes are calcined at 700-800 ° C for 2 hours and then thoroughly crushed into powder with a particle size of 3-5 m, after which the solution of polyvinyl alcohol is added as a binder and pressed into articles of a given shape and size.
Спрессованные издели помещают в печь и спекают при 1050°С в течение 1,5-2 час. Скорость подъема температуры 200-300°С/час, скорость охлаждени 100-200°С/час.Compressed products are placed in an oven and sintered at 1050 ° C for 1.5-2 hours. The rate of temperature rise is 200-300 ° C / hour, the cooling rate is 100-200 ° C / hour.
Пол ризаци изделий осуществл етс в силиконовом масле при 140-160°С в течение 1-1,5 час, в посто нном поле с напр женностью 3-4 кв/мм. Ниже приведены свойства полученного материала:The polarization of the products is carried out in silicone oil at 140-160 ° C for 1-1.5 hours, in a constant field with a strength of 3-4 kV / mm. Below are the properties of the material obtained:
Гспек, °С1060Hsek, ° С1060
р, г/сл(37,5p, g / sl (37.5
2119021190
tg60,030tg60,030
Гн, °С330GN ° C330
d.,iX10e ед. CGSE4,6d., iX10e units CGSE4,6
/(р0,54/ (p0,54
QM54QM54
Пред мет изобретени Present Invention
Пьезокерамическ.ий материал на основе твердых растворов РЬ (ZrxTii x) Оз при х 0,4-0,6 с добавкой в мол. % В12Оз 0,5-5 и Li2O 0,25-10, отличающийс те:м, что, с .целью повышени электрофизических характеристик, он дополнительно содержит окись двухвалентного элемента в количестве 0,5-5 мол. %.Piezoceramics material based on Pb (ZrxTii x) Oz solid solutions at x 0.4-0.6 with addition to mol. % B12Oz 0.5-5 and Li2O 0.25-10, characterized by those: m that, in order to improve the electrical characteristics, it additionally contains an oxide of the divalent element in the amount of 0.5-5 mol. %