SU1798338A1 - Additive for preparing building waterproofing solution - Google Patents

Additive for preparing building waterproofing solution Download PDF

Info

Publication number
SU1798338A1
SU1798338A1 SU904827959A SU4827959A SU1798338A1 SU 1798338 A1 SU1798338 A1 SU 1798338A1 SU 904827959 A SU904827959 A SU 904827959A SU 4827959 A SU4827959 A SU 4827959A SU 1798338 A1 SU1798338 A1 SU 1798338A1
Authority
SU
USSR - Soviet Union
Prior art keywords
water
molecular weight
prototype
low molecular
weight polyethylene
Prior art date
Application number
SU904827959A
Other languages
Russian (ru)
Inventor
Aleksej E Antipov
Farkhat I Azimov
Vladimir R Yashin
Evgenij P Pushkov
Yurij S Orevkov
Vladimir A Beloborodov
Gulnara F Abdullina
Original Assignee
Kz Inzh Str Inst
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kz Inzh Str Inst filed Critical Kz Inzh Str Inst
Priority to SU904827959A priority Critical patent/SU1798338A1/en
Application granted granted Critical
Publication of SU1798338A1 publication Critical patent/SU1798338A1/en

Description

Изобретение относится к строительным материалам,для растворной гидроизоляции полов, кровли и стен промышленных гражданских зданий и сооружений.The invention relates to building materials for mortar waterproofing of floors, roofs and walls of industrial civil buildings and structures.

Цель изобретения - снижение пенообразования и повышение ее стабильности при хранении.The purpose of the invention is to reduce foaming and increase its stability during storage.

Изобретение иллюстрируется примерами конкретного выполнения, приведенными в табл. 1,2,3, 4.The invention is illustrated by examples of specific implementation given in table. 1,2,3, 4.

Добавку - водную эмульсию низкомолекулярного полиэтилена готовят по следующей технологии: в горячую воду (Т = =90...100°С) при интенсивном перемешивании лопастной мешалкой (п = 80010ОО об/мин в течение 3-5 мин) вводят соду и олеиновую кислоту, а затем - расплавленный полиэтилен - отход производства при Т = 100~120°С и жидкое стекло с. непрерывным перемешиванием в течение 5-6 минут при тех же оборотах лопастного вала. Эмульсия имеет продолжительный срок хранения (до 18 месяцев) и малое пенообразование при приготовлении (15-25%), готовится заранее в цехах, хранится в расходных емкостях из древесины, стекла или полимерного материала. Добавка - эмульсия имеет сметанообразную консистенцию и обладает свойством растворяться в воде без распада (порог водоразбавления до 160%) и поэтому для равномерного распределения полимера в строительном растворе, добавка растворяется в воде до 150% и вводится в цементно-песчаный раствор в качестве уплотняющей добавки.The additive - an aqueous emulsion of low molecular weight polyethylene is prepared according to the following technology: soda and oleic acid are introduced into hot water (T = 90 ... 100 ° C) with vigorous stirring with a paddle mixer (n = 80010OO rpm for 3-5 minutes) , and then - molten polyethylene - production waste at T = 100 ~ 120 ° C and liquid glass with. continuous stirring for 5-6 minutes at the same speed of the blade shaft. The emulsion has a long shelf life (up to 18 months) and low foaming during preparation (15-25%), is prepared in advance in workshops, stored in consumable containers made of wood, glass or polymer material. Additive - the emulsion has a creamy consistency and has the property of dissolving in water without disintegration (the threshold of water dilution is up to 160%) and therefore, for uniform distribution of the polymer in the mortar, the additive is dissolved in water up to 150% and is introduced into the cement-sand mortar as a sealing additive.

Гидроизоляционные растворы готовят в лабораторной растворомешалке путем перемешивания цемента, песка и воды с эмульсией. Из приготовленного раствора готовили образцы - кубики размерами 7,07х юWaterproofing solutions are prepared in a laboratory mortar mixer by mixing cement, sand and water with an emulsion. Samples were prepared from the prepared solution - cubes measuring 7.07 x 10

ω ω оо >ω ω oo>

х 7,07 х 7,07 см, балочки размерами 4 х 4 х х 16 см, цилиндры диаметром 15 см и высотой 15см и пластины размерами 15х 15x3 см. Образцы подвергают термовлажностной обработке в пропарочной камере в течение 12 ч с максимальной температурой 70°С.x 7.07 x 7.07 cm, beams measuring 4 x 4 x x 16 cm, cylinders with a diameter of 15 cm and a height of 15 cm and plates measuring 15 x 15x3 cm.The samples are subjected to thermal and humidity treatment in a steam chamber for 12 hours with a maximum temperature of 70 ° WITH.

Низкомолекулярный полиэтилен, входящий в водную эмульсию, является крупнотоннажным отходом ПО Оргсинтез. Применение предложенной добавки-эмульсии позволяет утилизировать отходы производства.Low molecular weight polyethylene included in the water emulsion is a large-tonnage waste of PO Orgsintez. The use of the proposed additive-emulsion allows you to dispose of production waste.

Claims (1)

Формула изобретенияClaim Добавка для приготовления строительного гидроизоляционного раствора, вклю чающая низкомолекулярный полиэтилен с мол, м. до 2780, олеиновую кислоту, кальцинированную соду и воду, отличающаяс я тем, что, с целью снижения пенообразо5 вания и повышения ее стабильности при хранении, она содержит дополнительно си-. ликат натрия с модулем 2,6-3,0, при следующем соотношении компонентов, мае. %: Низкомолекулярный поли10 этилен с мол.м. 2780 25,0-28,0An additive for the preparation of a building waterproofing mortar, including low molecular weight polyethylene with a molecular weight of up to 2780, oleic acid, soda ash and water, characterized in that, in order to reduce foaming and increase its stability during storage, it additionally contains ... sodium licate with a modulus of 2.6-3.0, with the following ratio of components, May. %: Low molecular weight poly10 ethylene mol.m. 2780 25.0-28.0 Олеиновая кислота 6,0-7,0 Кальцинированная сода 1,5-2,0 Силикат натрия с модулем 2,6-3,0 0,4-0,6Oleic acid 6.0-7.0 Soda ash 1.5-2.0 Sodium silicate with a modulus of 2.6-3.0 0.4-0.6 15 Вода Остальное.15 Water Rest. Составы полимерной добавкиPolymer additive compositions Таблица 1Table 1 Компонент Состав, мас.%Component Composition, wt% 1 прототип 2 3 41 prototype 2 3 4 Низкомолекулярный полиэтилен с молекулярной массой до 2780 26,5 25,0 28,0 26,5Low molecular weight polyethylene with molecular weight up to 2780 26.5 25.0 28.0 26.5 Олеиновая кислота 6,5 7,0 6.0 6,5Oleic acid 6.5 7.0 6.0 6.5 Сода кальцинированная 1,75 1,5 2,0 1,75Soda ash 1.75 1.5 2.0 1.75 Силикат натрия с модулем 2,6-3,0 - 0,4 0,6 0,5Sodium silicate with modulus 2.6-3.0 - 0,4 0.6 0.5 Вода 65,25 66,1 63,4 64,75Water 65.25 66.1 63.4 64.75 Таблица 2table 2 Свойства предложенной полимерной добавки и прототипаProperties of the proposed polymer additive and prototype Показатель СоставIndex Composition 1 прототип 2 3 41 prototype 2 3 4 Порог водоразбавления, % 128 145 145 160Water dilution threshold,% 128 145 145 160 Дисперсность частиц, мкм 0,21 0,15 0,20 0,18Dispersion of particles, microns 0.21 0.15 0.20 0.18 Стабильность, мес 12 . 15 16 18Stability, months 12 . 15 16 eighteen Пенообразование при при- готовлении,% 60 25 20 18Foaming during cooking,% 60 25 twenty eighteen Консистенция Молокообразная СметанообразнаяConsistency Milky Creamy Составы гидроизоляционных растворовCompositions of waterproofing solutions Таблица 3Table 3 Компонент Состав, мас.%Component Composition, wt% 1 прототип 2 3 41 prototype 2 3 4 Портландцемент М-400 23,0 20,0 26,0 23,0Portland cement M-400 23.0 20.0 26.0 23.0 Песок кварцевый Мкр=1,5-2,0 62,5 65,0 60,0 62,5Quartz sand Mkr = 1.5-2.0 62.5 65.0 60.0 62.5 Водная эмульсия низкомолекуляр- ного полиэтилена, согласно изобре- тения (в пересчете на сухой остаток) - 1,0 1,5 1,25Water emulsion of low molecular weight polyethylene, according to the invention (in terms of dry residue) - 1.0 1.5 1.25 Вода 13,25 14,0 12,5 13,25Water 13.25 14.0 12.5 13.25 Водная эмульсия низкомолекуляр- ного полиэтилена по прототипу 1,25 -г- . —Aqueous emulsion of low molecular weight polyethylene according to the prototype 1.25 -G- . - 5 1798338 65 1798338 6 Свойства гидроизоляционных растворовProperties of waterproofing mortars Таблица 4Table 4 Показатель СоставIndex Composition 1 прототип 2 3 41 prototype 2 3 4 Предел прочности на изгиб. МПа 3.5 2,85 3.2 3,65Flexural strength. MPa 3.5 2.85 3.2 3.65 Предел прочности на сжатие. МПа 12,5 12,5 11,3 12,7Compressive strength. MPa 12.5 12.5 11.3 12.7 Водопоглощение за 24 часа, % 4,1 6,0 5,6 4.1Water absorption in 24 hours,% 4.1 6.0 5.6 4.1 Водонепроницаемость, МПа 0,6 0,4 0,5 0,6Water tightness, MPa 0.6 0,4 0.5 0.6 Подвижность, см 3,0 3,0 2,5 3,5Mobility, cm 3.0 3.0 2.5 3.5
SU904827959A 1990-05-22 1990-05-22 Additive for preparing building waterproofing solution SU1798338A1 (en)